Method for steel pin manufacture

Abstract

A steel pin is disclosed of a type to be forcibly driven into a steel substrate by using a powder-actuated tool. The steel pin has a substantially cylindrical shank and a substantially sharp point which extends from one end of the substantially cylindrical shank, which conforms substantially to a tangent or secant ogive except for a substantially spherical tip having a radius in a range of approximately 0.02 inch (approximately 5 millimeters) to approximately 0.03 inch (approximately 7.5 millimeters), which has substantially true concentricity, which has surface-texture irregularities with a roughness-height index value in a range from approximately 10 microinches (approximately 0.25 micrometers) to approximately 15 microinches (approximately 0.38 micrometers), and which appears to be substantially free of other surface imperfections when viewed under 60.times. magnification. The substantially cylindrical shank is joined to the substantially sharp point at a transition having a substantially smooth, continuously curved surface, and is knurled near the transition. The steel pin is made by deforming a length of steel wire as by forging or swaging, so as to form the steel pin with the substantially cylindrical shank and with the substantially sharp point, and reshaping the substantially pointed end as by barrel finishing the steel pin in a finishing medium.

Description

TECHNICAL FIELD OF THE INVENTION

This invention pertains to a steel pin of a type to be forcibly driven through a workpiece into a steel substrate, by means of a powder-actuated tool. The steel pin has a substantially sharp point which is reshaped so that such point has substantially true concentricity, so that surface-texture irregularities on such point are reduced, and so that such point appears under high magnification to be substantially free of other surface imperfections. This invention also pertains to a method for the manufacture of the steel pin.

BACKGROUND OF THE INVENTION

Frequently, powder-actuated tools are employed to drive steel pins or fasteners through workpieces into steel, concrete, or masonry substrates. A powder-actuated tool employs a powder charge which undergoes explosive combustion.

High velocity tools, those without pistons, are no longer produced in the industry. Current low velocity, powder-actuated tools drive the steel pins or fasteners by means of a piston disposed between the charge and the steel pin. These current low velocity tools result in a lower velocity for the steel pin and thus lower energy imparted to the pin. Without proper design and manufacture of the steel pin or fastener, these tools could result in inadequate penetration of the steel substrate and a lower level of holding power in some instances. Without a properly designed pin, some would-be powder-actuated tool users may opt for other methods of holding articles to steel or concrete, such as inserting a fastener into a drilled hole.

Typically, such a pin is manufactured by drawing a steel wire to a desired diameter, cutting the drawn wire to a predetermined length while deforming one end of the length of wire to form a head, and deforming the other end of the length of wire to form a point. Typically, the steel pin is then heat-treated, as by austempering which produces a ductile core in combination with surface decarburization, and then plated with zinc, as by electrogalvanizing. Various additional coatings may also be applied to further improve corrosion resistance.

Commonly, the point is formed either by swaging the wire end or by pinch pointing, which refers to forging the wire end between two matched dies. Each point-forming process, as practiced heretofore, has its own shortcomings.

Swaging is a slower process. Swaging tends to form a protuberance at the point. The protuberance tends to bend over, to deflect the steel pin, and to increase resistance to penetration, particularly as the steel pin is driven initially against a steel surface, whereby it may be unduly difficult to maintain perpendicularity of the steel pin relative to the steel surface.

Pinch pointing is a faster process. Pinch pointing tends to form a cleft where the matched dies come together at the tip. Because of its striking appearance under high magnification (for example 60.times. magnification) the cleft that is formed is known as a "fish mouth" to persons involved with the manufacture of steel pins.

In addition to resulting in a tip having either a protuberance or a "fish mouth", both swaging and pinch pointing processes make it difficult to produce a smooth transition, which is required, where the pointed end of the steel pin meets the cylindrical shank of the steel pin.

Generally, a "fish mouth" cleft does not seem to unduly interfere with the driving of a steel pin having such a cleft into a concrete or masonry substrate by means of a powder-actuated tool, even if the steel pin must be initially driven through a thin-walled steel workpiece. However, such a cleft tends to increase resistance to penetration to such a high level that a steel pin having such a cleft cannot be effectively driven by means of a low velocity powder-actuated tool so as to deeply penetrate into a steel substrate. Although a larger powder charge aids penetration of a steel pin into a steel substrate, such penetration is not always successful even if such a charge is employed.

When a low velocity tool is employed, penetration of a steel pin having such a cleft into a steel substrate tends to be arrested before all energy from the powder charge that has been employed has been spent, whereupon the steel pin may break along its shank. It may be similarly difficult to drive a steel pin having such a cleft through a thick-walled steel workpiece by means of a powder-actuated tool.

Heretofore, it has been known to remove slight imperfections and small burrs from such steel pins by tumbling the steel pins upon themselves, with or without media. As practiced heretofore, tumbling only is not entirely satisfactory, as tumbling tends to distort the clefts or protuberances on the points of the tumbled pins. Because of the distorted points, it can be more difficult to maintain perpendicularity of such pins relative to steel substrates, and resistance to penetration of such pins into steel substrates tends to also be increased.

The purpose of tumbling practiced heretofore was to remove flash or upstanding thin-walled protuberances on the steel pin, a process commonly known as deburring. The purpose was not to remove steel from most of the surface of the tip of the pin.

Terms Used Herein

References are made hereinafter to an ogive, which is the curved or tapered front portion of a projectile having a cylindrical body, or equivalently, of a steel pin having a cylindrical shank. An ogive is generated by a circular arc or a straight taper, which arc or taper is rotated 360.degree. about a central axis. A tangent or true ogive is generated by a circular arc tangent to the generator of the cylindrical surface of the cylindrical body, or equivalently of the cylindrical shank. A secant ogive is generated by a circular arc not tangent to, but intersecting at a small angle, the cylindrical surface thereof. A conical ogive is generated by a straight taper intersecting the cylindrical surface thereof.

References are made hereinafter to a roughness-height index value, which is a number that equals the arithmetical average deviation of minute surface irregularities from a hypothetical perfect surface, as expressed either in microinches (.mu.in) or micrometers (.mu.m). Surface-texture measurements expressed as roughness-height index values and related topics are explained in Broadston, "Surface-Texture Designation, Production, and Control", which is a chapter in Baumeister et al., Marks' Standard Handbook for Mechanical Engineers, Eighth Edition, McGraw-Hill Book Company, New York (1978) at pages 13-73 et seq.

As explained in Broadston, supra, flaws in a surface are not considered in surface-texture measurements. Accordingly, references made herein to other surface imperfections refer to clefts, protuberances, and other flaws that are not considered in surface-texture measurements.

Also, tip radius is defined as the radius at the very tip of the pin.

SUMMARY OF THE INVENTION

This invention has resulted from efforts to reduce resistance to penetration of a steel pin into a steel substrate, particularly a steel pin having a forged point having a "fish mouth" cleft, as described above.

This invention provides a steel pin having a substantially sharp point which is reshaped so as to provide substantially true point concentricity, so as to reduce surface-texture irregularities, and to eliminate other surface imperfections apparent under high magnification. This invention also provides a method for the manufacture of the steel pin.

Broadly, the substantially sharp point has surface-texture irregularities with a roughness-height index not greater than approximately 15 microinches (approximately 0.38 micrometers) and appears to be substantially free of other surface imperfections when viewed under high magnification, specifically when viewed under 60.times. magnification. Preferably, the substantially sharp point has surface-texture irregularities with a roughness-height index value in a range from approximately 10 microinches (approximately 0.25 micrometers) to about 15 microinches (approximately 0.38 micrometers).

Desirably, the substantially sharp point conforms substantially to an ogive except that the substantially sharp point has a substantially spherical tip. Desirably, the substantially spherical tip has a radius in a range from approximately 0.02 inch (approximately 5 millimeters) to approximately 0.03 inch (approximately 7.5 millimeters).

Preferably, the steel pin has a substantially cylindrical shank joined to the substantially sharp point at a transition having a substantially smooth, continuously curved surface. In one contemplated embodiment, the substantially cylindrical shank is knurled near the transition.

When a steel pin is made by the method provided by this invention, a length of steel wire is deformed so as to form a steel pin with a substantially cylindrical shank, and with a substantially sharp point which extends from one end of the substantially cylindrical shank. The substantially sharp point is reshaped so that the substantially sharp point has substantially true concentricity, so that surface-texture irregularities on the substantially sharp point have a roughness-height index value not greater than approximately 15 microinches, and so that the substantially sharp point appears to be substantially free of other surface imperfections when viewed under 60.times. magnification.

Preferably, the substantially sharp point is reshaped so that surface-texture irregularities on the substantially sharp point have a roughness-height index value in a range from approximately 10 microinches (approximately 0.25 micrometers) to approximately 15 microinches (approximately 0.38 micrometers). Desirably, the substantially sharp point is reshaped so as to have a substantially spherical tip and so as to conform substantially to an ogive except for the substantially spherical tip. Desirably, the substantially sharp point is reshaped so that the substantially spherical tip has a radius in a range from approximately 0.02 inch (approximately 5 millimeters) to approximately 0.03 inch (approximately 7.5 millimeters).

Preferably, the substantially pointed end is reshaped by barrel finishing the steel pin in finishing media. Another term for barrel finishing, as employed for purposes of this invention, is tumble pointing. Tumbling or deburring, as practiced in the prior art, was not intended to change the tip radius or the overall shape of a pin point. According to this invention, however, the substantially sharp point is reshaped so as to have a substantially spherical tip which desirably has a radius in the range noted above.

Preferably, deforming the length of steel wire includes forging one end of the length of steel wire so as to cause the forged end to become the substantially sharp point of the steel pin. Alternatively, deforming the length of steel wire includes swaging one end of the length of steel wire so as to cause the swaged end to become the substantially sharp point of the steel pin.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other objects, features, and advantages of this invention will become evident from the following description of a preferred mode for carrying out this invention with reference to the accompanying drawings in which like reference characters designate like or corresponding parts throughout the several views, and wherein:

FIG. 1 is an elevational view of a steel pin embodying this invention, in a larger size, with a head, a shank having a knurled portion, and a substantially sharp point.

FIG. 2 is an elevational view of a steel pin embodying this invention, in a smaller size, with head, a shank that is not knurled, and a substantially sharp point.

FIG. 3 is a flow chart of preferred major steps in the manufacture of the steel pin shown in FIG. 1. Preferred major steps in the manufacture of the steel pin shown in FIG. 2 are similar to those steps employed in connection with the manufacture of the pin shown in FIG. 1 except that the knurling step is omitted.

FIG. 4 is a microphotograph (at 60.times. magnification) of a substantially sharp point formed on a steel pin by a pinch pointing process after the substantially sharp point has been reshaped by barrel finishing in finishing media for a prescribed time for the purposes of this invention.

FIG. 5 is a microphotograph (at 60.times. magnification) of a substantially sharp point formed on a steel pin by a pinch pointing process before the substantially sharp point is reshaped for the purposes of this invention. A pronounced "fish mouth" cleft is visible. FIG. 5 exemplifies the prior art.

FIG. 6 is a microphotograph (at 60.times. magnification) of a substantially sharp point formed on a steel pin by a pinch pointing process after the substantially sharp point has been reshaped by barrel finishing in finishing media for 28 hours for the purposes of this invention.

FIG. 7 is a microphotograph (at 60.times. magnification) of a substantially sharp point formed on a steel pin by a swaging process before the substantially sharp point is reshaped for the purposes of this invention. A small protuberance at the substantially sharp point is visible. FIG. 7 exemplifies the prior art.

FIG. 8 is a microphotograph (at 100.times. magnification) of a cross-section through the substantially pointed end of a steel pin and through a steel plate after the steel pin has been driven into the steel plate. The substantially pointed end was formed by a pinch-pointing process and the steel pin was reshaped as described below. Geometric shapes in FIG. 8 are artifacts due to hardness tests.

FIG. 9 is a microphotograph (at 100.times. magnification) of a cross-section through the substantially pointed end of a steel pin and through a steel plate after the steel pin has been driven into the steel plate. The substantially pointed end was formed by a swaging process and was not reshaped as described below. Geometric shapes in FIG. 9 are artifacts due to hardness tests. FIG. 9 exemplifies the prior art.

FIG. 10 is a microphotograph (at 50.times. magnification) of a cross-section through the substantially cylindrical shank of a steel pin and through a steel plate after the steel pin has been driven into the steel plate. The steel pin, which has a substantially pointed end formed by a pinch-pointing process, was reshaped as described below.

FIG. 11 is a microphotograph (at 50.times. magnification) of a cross-section through the substantially cylindrical shank of a steel pin and through a steel plate after the steel pin has been driven into the steel plate. The steel pin, which had a substantially pointed end formed by a swaging process, was not reshaped as described below. FIG. 11 exemplifies the prior art.

DETAILED DESCRIPTION OF PREFERRED MODE

As shown in FIG. 1, a steel pin 10 of a larger size constitutes a first embodiment of this invention. The pin 10 has a relatively long, substantially cylindrical shank 12 having a given diameter, a head 14 having a larger diameter than that of the shank 12 and formed at one end of the shank 12, and a substantially sharp point 16 formed at and extending from the other end of the shank 12. The point 16 conforms substantially to an ogive, particularly to a secant ogive, except that the point 16 has a substantially spherical tip 18. The point 16 is joined to the shank 12 at a transition 20. The shank 12 has a knurled portion 22 near the transition 20.

As shown in FIG. 2, a steel pin 10' of a smaller size constitutes a second embodiment of this invention. The pin 10' has a relatively short, substantially cylindrical shank 12' having a given diameter, a head 14' having a larger diameter than that of the shank 12 and formed at one end of the shank 12', and a substantially sharp point 16' formed at and extending from the other end of the shank 12'. The point 16' conforms substantially to an ogive, particularly to a secant ogive, except that the point 16' has a substantially spherical tip 18'. The point 16' is joined to the shank 12' at a transition 20'. The shank 12' does not have a knurled portion.

Although the points 16, 16', conform substantially to a secant ogive, this invention may also be embodied in a steel pin having a substantially sharp point conforming substantially to a tangent ogive.

The substantially sharp point of each one of the steel pins 10, 10', has surface-texture irregularities with a roughness-height index value in a range from approximately 10 microinches (approximately 0.25 micrometers) to approximately 15 microinches (approximately 0.38 micrometers). Further, the substantially sharp point of each one of the steel pins 10, 10', appears to be substantially free of other surface imperfections when viewed under high magnification, specifically when viewed under 60.times. magnification.

The substantially sharp point of each one of the steel pins 10, 10', has substantially true concentricity. The substantially spherical tip of the substantially sharp point of each one of the steel pins 10, 10', has a radius in a range from approximately 0.02 inch (approximately 5 millimeters) to approximately 0.03 inch (approximately 7.5 millimeters). Also, on each one of the steel pins 10, 10', the transition between the substantially sharp point and the substantially cylindrical shank comprises a substantially smooth, continuously curved surface. In each one of the illustrated embodiments, except for the substantially spherical tip, the substantially sharp point conforms substantially to a secant ogive.

Having a substantially sharp point that has substantially true concentricity and a roughness-height index value not greater than approximately 15 microinches (approximately 0.25 micrometers) and that appears to be substantially free of other surface imperfections when viewed under high magnification, specifically when viewed under 60.times. magnification, are characteristics which distinguish each of the steel pins 10, 10', from steel pins sold and used previously. Having a point that conforms substantially to an ogive except that the point has a substantially spherical tip is another characteristic which distinguishes each one of the steel pins 10, 10' from steel pins sold and used previously.

A steel pin having these characteristics offers significant advantages over a steel pin lacking these characteristics. Because the point of a steel pin having these characteristics has substantially true concentricity, the point does not interfere with maintaining perpendicularity between the steel pin and a steel substrate. Outward flow of the steel that is displaced as a steel pin having these characteristics penetrates a steel substrate tends to be uniformly concentric, whereby initial frictional forces imparted to the steel pin and to the steel substrate as the steel pin begins to penetrate the steel substrate are minimized.

Preferably, as explained below, a steel pin having these characteristics is made so that surface-texture irregularities on its shank are similar to surface-texture irregularities on its point. Advantageously, therefore, resistance of the steel pin to withdrawal from the steel substrate is maximized.

Preferred major steps in the manufacture of the steel pin 10 are charted in FIG. 3. Preferred major steps in the manufacture of the steel pin 10' are similar except that the knurling step described below is omitted.

Initially, in the manufacture of a steel pin, a steel wire is drawn from an initial diameter to a desired diameter. Conventional equipment is employed in this step.

Thereupon, a length wire is cut from the drawn wire, the head is formed on one end of the cut length wire, and the head is stamped with a manufacturer's mark. Conventional equipment is employed in these steps.

Thereupon, conventional pinch pointing equipment is employed to form the point on the other end of the same length wire, which between the head and the point becomes the shank of the steel pin. Thus, as exemplified in the microphotograph that is FIG. 5, the point has a pronounced "fish mouth" cleft.

Presently, it is preferred to employ a Hartford High Speed Point Former (Model 5-700) which is available commercially from The Hartford Special Machinery Co. of Simsbury, Conn., to form the point of the pin.

If the shank of the steel pin is to have a knurled portion near the transition between the shank and the point, conventional equipment is employed to knurl the shank portion. Preferably, as shown in FIG. 3, this knurling step is performed between the point-forming step and the next step. Alternatively, this knurling step is performed between the wire-cutting, head-forming, and head-stamping steps and the point-forming step. This knurling step is employed in the manufacture of the steel pin 10 but is omitted in the manufacture of the steel pin 10'.

The next step is a degreasing step, in which conventional solvents are employed in conventional equipment to degrease the steel pin, as formed in the prior steps.

After the steel pin has been degreased, the steel pin is reshaped by barrel finishing or tumble pointing the steel pin in finishing media over an extended period of time, whereby the steel pin is provided with the characteristics which distinguish the steel pins 10, 10' from steel pins known and used previously. Barrel finishing in finishing media is known also as media finishing.

Conventional finishing media may be suitably used, such as Ceratech Ceramic Media (5/8".times.1/4"). Conventional barrel finishing or media finishing equipment may be suitably employed, along with a magnetic separator with a demagnetizer, a spin dryer, and a wire spin basket. Alternatively, vibratory finishing equipment with appropriate media may also be used.

In successive steps after the steel pin has been barrel finished in finishing media for the extended period of time, the steel pin is heat treated by austempering which produces a ductile core in combination with surface decarburization, plated with zinc by electrogalvanizing, coated with a protective chromate, and packaged.

The extended period of time, over which the steel pin must be barrel finished in finishing media to provide the steel pin with the characteristics noted above, is determined empirically with due regard to the finishing media that are employed and the finishing equipment that is employed.

It is informative to compare the microphotographs that comprise FIGS. 4, 5, and 6. FIG. 4 illustrates the substantially pointed end provided on a steel pin by pinch pointing, after barrel finishing of the steel pin in finishing media for 40 hours, whereby the substantially pointed end has no apparent "fish mouth" cleft.

FIG. 5 illustrates the substantially pointed end provided on a steel pin by pinch pointing, before barrel finishing of the steel pin has begun, the substantially pointed end having a very pronounced "fish mouth" cleft. FIG. 6 illustrates the substantially pointed end provided on a steel pin by pinch pointing, after barrel finishing of the steel pin in finishing media for 28 hours, whereby the "fish mouth" cleft appears to be substantially reduced but not entirely eradicated.

As seen in FIG. 5, the point tip radius of a prior art pinch-pointed pin is difficult to ascertain due to the "fish Mouth" cleft. The point tip radius of a pin substantially similar to this pin was determined, as noted in Table I, by looking at the pin from the side so that the "fish mouth" cleft was not seen. The tip radius was measured on one of the two sides of the "fish mouth" cleft. As shown in FIG. 4, after barrel finishing or tumble pointing for 40 hours, the tip radius can be taken at any rotational angle because the tip is truly concentric.

Moreover, as seen in Table I, the tip radius after barrel finishing or tumble pointing is larger than the tip radius of the original pinch-pointed pin. It can be appreciated that this would also apply to a pin point originally made by swaging.

Barrel finishing or tumble pointing of a steel pin reduces all of its exterior dimensions, not merely its substantially pointed end, as exemplified by the following data obtained from three specimen pins reshaped as described herein. The following data also shows from shortening of various dimensions, that barrel finishing or tumble pointing not only removes upstanding flash or protuberances but also removes metal from the steel pin in its entirety.

TABLE I__________________________________________________________________________ After After Before Reshaping Reshaping Change (%) Change (%)Specimen Dimension Reshaping 28 Hours 40 Hours 28 Hours 40 Hours__________________________________________________________________________Specimen A Knurl 0.154 inch 0.150 inch knurl not 2.6% Diameter measured Shank 0.615 inch 0.592 inch 0.575 inch 3.7% 6.5% Length Head 0.298 inch 0.297 inch 0.295 inch 0.3% 1% Diameter Ogive 0.237 inch 0.220 inch 0.212 inch 7% 11% Length Point Tip 0.010 inch 0.018 inch 0.022 inch 180% 220% Radius Fish Mouth 0.009 inch nil nil Shank 0.150 inch 0.150 inch 0.146 inch nil 2.6% DiameterSpecimen B Knurl 0.152 inch 0.149 inch knurl not 2% Diameter measured Shank 0.739 inch 0.718 inch 0.696 inch 2.9% 6% Length Head 0.298 inch 0.297 inch 0.295 inch 0.3% 1% Diameter Ogive 0.231 inch 0.209 inch 0.191 inch 9.5% 17% Length Point Tip 0.010 inch 0.020 inch 0.024 inch 200% 240% Radius Fish Mouth 0.007 inch nil nil Shank 0.150 inch 0.150 inch 0.146 inch nil 2.6% DiameterSpecimen C Knurl 0.154 inch 0.149 inch knurl not 3% Diameter measured Shank 0.866 inch 0.832 inch 0.814 inch 4% 6% Length Head 0.298 inch 0.297 inch 0.294 inch 0.3% 1% Diameter Ogive 0.228 inch 0.199 inch 0.190 inch 13% 17% Length Point Tip 0.012 inch 0.023 inch 0.028 inch 192% 233% Radius Fish Mouth 0.017 inch nil nil Shank 0.150 inch 0.150 inch 0.146 inch nil 2.6% Diameter__________________________________________________________________________

Tables II, III, and IV report hardness data taken at cross-sections after steel pin D was driven into steel plate D, after steel pin E was driven into steel plate E, and after steel pin F was driven into steel plate F, respectively. Steel pin D, which embodied this invention, was a steel pin having a substantially pointed end formed by a pinch-pointing process and reshaped as described above. Steel pins E and F, which did not embody this invention, were commercially available pins having substantially pointed ends formed by a swaging process but not reshaped as described above.

If there is a phase change from martensite to ferrite near the surface of a steel pin, as a result of high frictional heating when the steel pin is driven into a steel plate, the surface hardness of the steel pin and its shear strength near its surface are reduced markedly. In view of the available data including the data in Tables II, III, and IV, it has been concluded that there is less frictional heating and less resultant deterioration in pin surface hardness when a steel pin embodying this invention is driven into a steel plate.

TABLE II______________________________________ Core or Hardness Hardness Converted Depth from Measured on to RockwellSpecimen Surface Knoop Scale Scale Noted______________________________________Steel Pin D Core 635.4 59 C Core 642.1 59 C Core 652.4 60 C 0.040 inch 612.7 58 C 0.020 inch 487.8 50 C 0.010 inch 422.4 45 C 0.005 inch 390.1 42 C 0.002 inch 400.8 43 CSteel Plate D Core 167.3 86 B Core 169.1 86 B Core 161.2 84 B 0.060 inch 201.7 93 B 0.040 inch 214.2 96 B 0.020 inch 256.3 26 C 0.010 inch 257.1 26 C 0.005 inch 269.5 28 C 0.002 inch 237.0 36 C______________________________________ TABLE III______________________________________ Core or Hardness Hardness Converted Depth from Measured on to RockwellSpecimen Surface Knoop Scale Scale Noted______________________________________Steel Pin E Core 642.1 57 CPrior Art Core 608.0 56 C Core 603.4 55 C 0.040 inch 517.0 50 C 0.020 inch 419.7 43 C 0.010 inch 264.6 25 C 0.005 inch 185.5 90 B 0.002 inch Hardness not measured due to distortionSteel Plate E Core 136.9 75 BPrior Art Core 147.1 79 B Core 148.9 80 B 0.060 inch 231.0 99 B 0.040 inch 229.6 98 B 0.020 inch 238.1 100 B 0.010 inch 195.9 92 B 0.005 inch 179.1 89 B 0.002 inch 118.0 (?) 67 B______________________________________ TABLE IV______________________________________ Core or Hardness Hardness Converted Depth from Measured on to RockwellSpecimen Surface Knoop Scale Scale Noted______________________________________Steel Pin F Core 592.8 55 CPrior Art Core 581.0 54 C Core 606.5 56 C 0.040 inch 597.3 55 C 0.020 inch 550.2 52 C 0.010 inch 469.3 47 C 0.005 inch 275.6 26 C 0.002 inch 208.1 95 BSteel Plate F Core 150.5 80 BPrior Art Core 153.4 81 B Core 160.3 83 B 0.060 inch 198.5 93 B 0.040 inch 223.9 97 B 0.020 inch 252.9 23 C 0.010 inch 272.3 26 C 0.005 inch 265.0 25 C 0.002 inch 269.1 26 C______________________________________

Hardness data in Tables II, III, and IV also indicates that ferrite is not formed from martensite near the surface of a steel pin made in accordance with this invention and driven into a steel plate but that ferrite is formed from martensite near the surface of a steel pin made in accordance with the prior art and driven into a steel plate. In Tables II, III, and IV, higher hardness values (for example Rockwell 42 C to Rockwell 60 C) are indicative of martensite being present, whereas lower hardness values (for example Rockwell 25 C, Rockwell 26 C, Rockwell 90 B, and Rockwell 95 B) are indicative of ferrite being present.

Further evidence that there is less frictional heating during driving of the pin into the substrate is available from microphotographic studies of changes of martensitic structures to ferritic structures when steel pins are driven into steel plates. It is informative to compare FIGS. 8 and 9.

In FIG. 8, which illustrates a steel pin made in accordance with this invention and driven into a steel plate, the steel pin does not exhibit a significant number of large grains, which are indicative of ferrite being present. In FIG. 9, which illustrates a steel pin made in accordance with the prior art and driven into a steel plate, a significant number of large grains appear, which are indicative of ferrite being present.

Because a steel pin that has been reshaped as described above has surface-texture irregularities with a roughness-height index value not greater than approximately 15 microinches and appears to be substantially free of other surface imperfections when viewed under 60.times. magnification, better surface-to-surface contact is achieved not only at the substantially pointed end but also along the substantially cylindrical shank when the steel pin is driven into a steel plate, as compared to steel pins known and used heretofore. The fact that better surface-to-surface contact is achieved is illustrated by FIGS. 8 through 11. A dark region leading to the upper edge of FIG. 8 is believed to be an entrapment of zinc that had been used to coat the steel pin.

When FIGS. 10 and 11 are compared, it is evident that the surface of the steel pin shown in FIG. 10 and made in accordance with this invention appears to have surface-to-surface contact over approximately 55% of the surface area between the steel pin and the steel plate and to be substantially smooth, after the steel pin has been driven into a steel plate. A dark region shown between the pin surface and the plate surface, along the surface area therebetween, is believed to be a portion of the zinc that had been used to coat the steel pin. Furthermore, it is evident that the surface of the steel pin shown in FIG. 11 and made in accordance with the prior art appears to have surface-to-surface contact over approximately 55% of the surface area between the steel pin and the steel plate and to have large voids, which are believed to have resulted from an irregular flow of the substrate steel of the steel plate over the pin surface.

As described above, this invention alleviates two problems, that have been attributed to surface irregularities on the pin point, when a steel pin is driven into a steel plate. One such problem is that surface irregularities cause high frictional resistance which produces high heat and causes a phase change of martensite to ferrite near the surface. Ferrite is weaker than martensite in shear strength. The other problem is that surface irregularities produce surface voids which are attributable to an irregular flow of the substrate steel over the pin surface.

Although this invention has been described primarily in connection with a steel pin having a forged point, as exemplified in FIG. 5, this invention may be alternatively used in connection with a steel pin having a swaged point, as exemplified in FIG. 7.

Various other modifications may be made without departing from the scope and spirit of this invention. It is therefore to be understood that within the scope of the appended claims, the present invention may be practiced otherwise than as specifically described herein.

Claims

1. A method of manufacturing a steel pin, comprising the steps of:

forming a steel pin from a length of steel wire such that said steel pin has a substantially cylindrical shank;

forming a substantially sharp point upon one end of said substantially cylindrical shank such that said substantially sharp end of said steel pin has surface imperfections; and

reshaping said substantially sharp point end of said steel pin so that said surface imperfections of said substantially sharp point end of said steel pin are eliminated and a substantially sharp point end of said steel pin, without said surface imperfections, is achieved.

2. The method as set forth in claim 1, wherein:

said forming of said substantially sharp point upon said one end of said substantially cylindrical shank comprises forging of said one end of said substantially cylindrical shank such that said surface imperfections of said substantially sharp point end of said steel pin comprise a cleft portion having a substantially fish-mouth configuration.

3. The method as set forth in claim 1, wherein:

said forming of said substantially sharp point upon said one end of said substantially cylindrical shank comprises swaging of said one end of said substantially cylindrical shank such that said surface imperfections of said substantially sharp point end of said steel pin comprise a protuberance portion which is disposed at an angle with respect to a longitudinal axis of said steel pin.

4. The method as set forth in claim 1, wherein:

said reshaping of said substantially sharp point end of said steel pin comprises barrel finishing said steel pin within a finishing medium.

5. The method as set forth in claim 1, wherein:

said reshaping of said substantially sharp point end of said steel pin is performed so that said substantially sharp point end of said steel pin has surface-texture irregularities which have a roughness-height index value not greater than approximately 15 microinches so as to thereby reduce high frictional resistance and high frictional heating of said steel pin as said steel pin is driven into a steel substrate so as to prevent the transformation of martensite steel to ferrite steel within surface portions of said steel pin.

6. A method of manufacturing a steel pin, comprising the steps of:

forming a steel pin from a length of steel wire such that said steel pin has a substantially cylindrical shank;

forming a substantially sharp point upon one end of said substantially cylindrical shank such that said substantially sharp end of said steel pin has surface imperfections; and

reshaping said substantially sharp point end of said steel pin so that said substantially sharp point end of said steel pin has substantially true concentricity, so that surface-texture irregularities upon said substantially sharp point end of said steel pin have a roughness-height index value not greater than approximately 15 microinches, and so that said surface imperfections of said substantially sharp point end of said steel pin are eliminated and a substantially sharp point end of said steel pin, without said surface imperfections, is achieved.

7. The method of claim 6 wherein the substantially sharp point end is reshaped so that surface-texture irregularities on the substantially sharp point end have a roughness-height index value in a range from approximately 10 microinches to approximately 15 microinches.

8. The method of claim 7 wherein the substantially sharp point end is reshaped so as to have a substantially spherical tip and so as to conform substantially to an ogive except for the substantially spherical tip.

9. The method of claim 8 wherein the substantially sharp point end is reshaped so that the substantially spherical tip has a radius in a range from approximately 0.02 inch to approximately 0.03 inch.

10. The method of claim 7 wherein the substantially sharp point end is reshaped by barrel finishing the steel pin in a finishing medium.

11. The method of claim 10 wherein the substantially sharp point end is reshaped so as to have a substantially spherical tip and so as to conform substantially to an ogive except for the substantially spherical tip.

12. The method of claim 11 wherein the substantially spherical tip has a radius in a range from approximately 0.02 inch to approximately 0.03 inch.

13. The method of claim 7, wherein:

said forming of said substantially sharp point upon said one end of said substantially cylindrical shank comprises forging said one end of said substantially cylindrical shank so as to cause said forged end of said substantially cylindrical shank, defining said substantially sharp point end of said steel pin, to have a cleft portion, defining said surface imperfections, to be incorporated therein.

14. The method of claim 7, wherein:

said forming of said substantially sharp point upon said one end of said substantially cylindrical shank comprises swaging said one end of said substantially cylindrical shank so as to cause said swaged end of said substantially cylindrical shank, defining said substantially sharp point end of said steel pin, to have a protuberance portion, defining said surface imperfections, to be incorporated therein.

15. A method of manufacturing a steel pin, comprising the steps of:

forming a steel pin from a length of steel wire such that said steel pin has a substantially cylindrical shank;

forming a substantially sharp point upon one end of said substantially cylindrical shank such that said substantially sharp end of said steel pin has a cleft portion; and

reshaping said substantially sharp point end of said steel pin so that said cleft portion of said substantially sharp point end of said steel pin is eliminated and a substantially sharp point end of said steel pin, without said cleft portion, is achieved.

16. The method as set forth in claim 15, wherein:

said forming of said substantially sharp point upon said one end of said substantially cylindrical shank comprises forging of said one end of said substantially cylindrical shank such that said cleft portion of said substantially sharp point end of said steel pin has a substantially fish-mouth configuration.

17. The method as set forth in claim 15, wherein:

said reshaping of said substantially sharp point end of said steel pin comprises barrel finishing said steel pin within a finishing medium.

18. The method as set forth in claim 15, wherein:

said reshaping of said substantially sharp point end of said steel pin is performed so that said substantially sharp point end of said steel pin has surface-texture irregularities which have a roughness-height index value not greater than approximately 15 microinches so as to thereby reduce high frictional resistance and high frictional heating of said steel pin as said steel pin is driven into a steel substrate so as to prevent the transformation of martensite steel to ferrite steel within surface portions of said steel pin.

19. A method of manufacturing a steel pin, comprising the steps of:

forming a steel pin from a length of steel wire such that said steel pin has a substantially cylindrical shank;

forming a substantially sharp point upon one end of said substantially cylindrical shank such that said substantially sharp end of said steel pin has a protuberance portion; and

reshaping said substantially sharp point end of said steel pin so that said protuberance portion of said substantially sharp point end of said steel pin is eliminated and a substantially sharp point end of said steel pin, without said protuberance portion, is achieved.

20. A method as set forth in claim 19, wherein:

said forming of said substantially sharp point upon said one end of said substantially cylindrical shank comprises swaging of said one end of said substantially cylindrical shank such that said protuberance portion of said substantially sharp point end of said steel pin is disposed at an angle with respect to a longitudinal axis of said steel pin.

21. A method as set forth in claim 19, wherein:

said reshaping of said substantially sharp point end of said steel pin comprises barrel finishing said steel pin within a finishing medium.

22. The method as set forth in claim 19, wherein:

said reshaping of said substantially sharp point end of said steel pin is performed so that said substantially sharp point end of said steel pin has surface-texture irregularities which have a roughness-height index value not greater than approximately 15 microinches so as to thereby reduce high frictional resistance and high frictional heating of said steel pin as said steel pin is driven into a steel substrate so as to prevent the transformation of martensite steel to ferrite steel within surface portions of said steel pin.