The present invention relates to a method for preparing pure cross-linked hyaluronic acid nanoparticles, which have biocompatibility without a cross-linking agent, nanoparticles prepared by the same method, and a use of the nanoparticles.
Hyaluronic acid is an ingredient that constitutes skin cells with elastin and collagen, is called a moisture storage capable of storing 1000 ml of moisture per 1 g, and has been widely used as a cosmetic material.
Nanoparticles such as pure hyaluronic acid hydration gels which are usable in vivo and biocompatible are required for being used as a contrast agent thereof and in vivo. A study of using hyaluronic acid to be cross-linked and converted into a nanoparticle form is still in an early stage and a study of synthesizing nanoparticles without using a cross-linking agent is hardly reported.
Meanwhile, there is provided a method for preparing nanoparticles by irradiating a hyaluronic acid aqueous solution with an electron beam (Korean Patent Registration No. 10-1893549). However, since the hyaluronic acid concentration is high in conditions in which the nanoparticles are prepared, it is not economic, and only nanoparticles having a diameter of more than 100 nm are prepared, and thus, there is a limit to be used in various fields.
Accordingly, the present invention provides a new method for preparing biocompatible and pure hyaluronic acid nanoparticles or nanogels by recognizing the conventional problems and needs.
The present invention provides a method capable of forming cross-linked hyaluronic acid nanoparticles on an aqueous solution other than an organic solvent without a separate cross-linking agent and provides a method capable of controlling sizes of nanoparticles.
As one aspect, the present invention provides a method for preparing cross-linked hyaluronic acid nanoparticles, comprising forming intermolecular or intramolecular cross-linking of hyaluronic acid by irradiating a hyaluronic acid aqueous solution with an electron beam.
In the present invention, the nanoparticles refer to particles having sizes of several to hundreds of nanometers (nm, material with one billionth of a meter). In the present invention, the nanoparticles are characterized to have particle sizes of 1 to 100 nm, but are not limited thereto. In the present invention, the nanoparticle is a concept including a nanogel or nanohydrogel, and hereinafter, the nanoparticle, and the nanogel or nanohydrogel are all used to mean the nanoparticle according to the present invention.
The hyaluronic acid aqueous solution is acidic, and may further include HClO4 in the hyaluronic acid-containing solution for an acidic aqueous solution. As described in detail and proved below, when the hyaluronic acid aqueous solution is acidic or the acid is added to the hyaluronic acid aqueous solution, it is newly provided that as compared with if not, high nanoparticle synthesis efficiency is increased. It is also provided that the sizes of the nanoparticles may be unexpectedly controlled due to adjustment of pH and adjustment of an added concentration of an acidic compound.
In the present invention, the hyaluronic acid is widely distributed in the cell-matrix in the connective tissue to form an adhesive and elastic solution under a physiological condition and is a main component of the extracellular matrix which is known to physically protect tissues such as iris and retina, vascular endothelial cells and epithelial cells, etc. and provide a buffer role. In the present invention, the hyaluronic acid is not limited to physical properties, shapes, size, and the like, and is preferably sterilized. In addition, the hyaluronic acid may have a average molecular weight of 5 to 5000 kDa, preferably a average molecular weight of 5 to 3000 kDa. In addition, the hyaluronic acid may be used in the form of a pharmaceutically acceptable salt, wherein the pharmaceutically acceptable salt includes a sodium salt, a potassium salt, a calcium salt, etc., and preferably a sodium salt. Further, derivatives of hyaluronic acid may also be used, and these derivatives may be specifically hyaluronic acids chemically modified by cross-linking, sulfuration, esterification or amino acid binding.
In the present invention, the pH of the hyaluronic acid aqueous solution may be 1 to 6,more preferably pH 1 to 5, much more preferably pH 1 to 4, and most preferably pH 1.5 to 3.5.
In the preparation method of the hyaluronic acid nanoparticles provided in the present invention, the concentration of the hyaluronic acid aqueous solution may be 0.05 to 7% (w/v), preferably 0.1 to 5% (w/v).
The aqueous solution does not include a cross-linking agent and an organic solvent. After irradiating the electron beam, dialysis and freeze-drying steps are further included.
The sizes of the hyaluronic acid nanoparticles are controlled by changing an irradiation dose of the electron beam and the sizes of the hyaluronic acid nanoparticles are reduced by increasing the irradiation dose of the electron beam.
In the preparation method of the hyaluronic acid nanoparticles provided in the present invention, the electron beam may be irradiated at the irradiation dose of 0.5 to 300 kGy, preferably 1 to 250 kGy, most preferably 1 to 200 kGy.
In the present invention, a total irradiation energy intensity of the electron beam may be 0.1 MeV to 5 MeV. The total irradiation energy intensity of the electron beam may be preferably 0.5 MeV to 3 MeV, and most preferably 1.0 MeV to 2.5 MeV.
The sizes of the hyaluronic acid nanoparticles are controlled by adjusting pH of the aqueous solution and the sizes of the hyaluronic acid nanoparticles are increased by decreasing pH of the aqueous solution.
The preparation method of the hyaluronic acid nanoparticles provided in the present invention may be a preparation method of hyaluronic acid nanoparticles having a diameter of 100 nm or less, preferably hyaluronic acid nanoparticles having a diameter of 50 nm or less, most preferably hyaluronic acid nanoparticles having a diameter of 30 nm or less.
As another aspect, the present invention provides intermolecular or intramolecular cross-linked nanoparticles of hyaluronic acid prepared by the method.
The nanoparticles are characterized as hydrogels with a swelling property.
The nanoparticles are characterized by having tumor selectivity. In particular, the nanoparticles are characterized to have colon cancer or melanoma selectivity.
The nanoparticles are characterized to have a tumor-to-muscle ratio of higher than 8times and a tumor-to-blood ratio of 1.5 times for the colon cancer tumor. The nanoparticles are characterized to have the tumor-to-muscle ratio of higher than 14 times and the tumor-to-blood ratio of higher than 3 times for the melanoma.
As another aspect, the present invention provides a contrast agent including the hyaluronic acid nanoparticles which are labeled with at least one labeling material selected from the group consisting of radioactive isotopes, organic fluorescent materials, quantum dots as inorganic materials, a magnetic resonance image contrast agent, a computed tomography contrast agent, a positron tomography contrast agent, an ultrasonic contrast agent, a fluorescent contrast agent, and a shape shift material.
A ligand compound conjugated to the nanoparticles and a radioactive isotope coordinately bonded to the ligand compound are included.
The ligand compound is characterized as at least one of NODA—GA—NH2, DOTA—GA, DOTA, TETA, and NOTA.
The radioactive isotope is characterized as at least one of 11C, 13N, 15O, 18F, 38K, 62Cu, 64Cu, 68Ga, 82Rb, 124I, 89Zr, 99mTc, 123I, 111 In, 67Ga, 177Lu, 201Tl, 117mSn, 1251, 131I, 166Ho, 188Re, 67Cu, 89Sr, 90Y, 225Ac, 213Bi, and 211At.
As another aspect, the present invention provides a conjugate of ascorbic acid and hyaluronic acid nanogels.
In the present invention, the “conjugate” refers to a compound having two or more compounds linked to each other. The linkage may be achieved by a non-covalent or covalent bond. That is, the conjugate of the present invention means that ascorbic acid and hyaluronic acid are directly or indirectly linked to each other by a non-covalent bond or covalent bond. Preferably, the conjugate of the present invention may mean that a hydroxyl group of ascorbic acid forms a bond to a carboxylic group of hyaluronic acid through an alkyl group of C1 to C5 to be firmly linked by a covalent bond.
In the present invention, the “ascorbic acid” is a material having an antioxidant effect represented by the following Chemical Formula 1 and called Vitamin C as a water-soluble vitamin and has been used in various industrial applications including pharmaceutical preparations, feed, inhibition of accumulation of melanin pigments, medical drugs, and cosmetics. However, the ascorbic acid as a very unstable compound is unstable under an oxidation condition and a thermal condition to lose the activity when exposed to heat, air, and light in the preparation process, and the activity thereof is lost in a distribution process, and thus, there is a large limit on utilization.
In the present invention, unless otherwise stated, the term “hyaluronic acid nanogel” refers to hyaluronic acid having various chain lengths and charge states as well as various chemical modifications including cross-linking, all variants of hyaluronate or hyaluronan, and hydrogels having a nano-meter size by cross-linking the variants. That is, the hyaluronic acid nanogel collectively includes various hyaluronate-derived nanogels of hyaluronic acid having various opposite ions, such as sodium hyaluronate. For example, various derivative-derived nanogels of hyaluronic acid are collectively included by the term, such as oxidation, such as oxidation to —CHO and/or —COOH of a —CH2OH group; periodate oxidation of adjacent hydroxyl groups selectively involving reduction, such as reduction of forming imine by reduction to —CH2OH of —CHO and involving reduction to amine: sulphation: selectively deamidation or deamidation involving formation of amide together with a new acid: esterification; cross-linking: substitution with various compounds, using binding by assistance of a cross-linking agent or carbodiimide, including binding of hyaluronic acid with various molecules such as proteins, peptides, and active medical ingredients; and deacetylation.
In the present invention, the preparation method of the hyaluronic acid nanogel is not particularly limited so long as the nanogel is a hydrogel of a nano-meter size formed by a hyaluronic acid molecule as a basic unit. In the art, the method for preparing the hyaluronic acid hydrogel having the nano-meter size is well known, and for example, a preparation method using a cross-linking agent, a preparation method using an electron beam, etc. may be referred to, but most preferably, the hyaluronic acid nanogel may be prepared by irradiating an electron beam to the aforementioned hyaluronic acid aqueous solution.
In the present invention, the conjugate of the ascorbic acid and the hyaluronic acid nanogels may be represented by the following Chemical Formula 2.
Wherein, m is 1 to 5.
In the conjugate provided by the present invention, a ratio of an ascorbic acid molecule to a carboxyl acid group of the hyaluronic acid molecule may be 1 to 5:1, preferably 1 to 4:1,much more preferably 2 to 4:1, and most preferably 2 to 3:1.
In the present invention, the conjugate of the ascorbic acid and the hyaluronic acid nanogels may be sequentially prepared according to the following Reaction Formulas 1 to 3.
Wherein, m is 1 to 5.
In Reaction Formulas 2 and 3 of the present invention, the hyaluronic acid may be induced by cross-linking after Reaction Formulas 2 and 3 to form nanogels, and after the hyaluronic acid is prepared in a nanogel form according to a known method or a preparation method of hyaluronic acid nanogels provided by the present invention, Reaction Formulas 2and 3 may also be applied.
Preferably, in Reaction Formulas 2 and 3 of the present invention, after the hyaluronic acid is prepared in a nanogel form according to a known method or a preparation method of hyaluronic acid nanogels provided by the present invention, Reaction Formulas 2 and 3 may be applied.
According to an embodiment of the present invention, it was confirmed that the ascorbic acid included in the conjugate has significantly improved stability and then the physiological activity of ascorbic acid is equally exhibited even after the ascorbic acid is left under a very harsh condition. Accordingly, the conjugate provided by the present invention is characterized in that the storage stability of ascorbic acid is improved.
In another aspect, the present invention provides a cosmetic composition for antioxidation, skin whitening, wrinkle improvement or skin anti-aging comprising the ascorbic acid and the hyaluronic acid nanogels as active ingredients.
Further, the present invention provides a cosmetic composition for antioxidation, skin whitening, wrinkle improvement or skin anti-aging (essentially) consisting of the ascorbic acid and the hyaluronic acid nanogels as active ingredients.
The ingredients included in the cosmetic composition of the present invention include ingredients which are generally used in the cosmetic composition as active ingredients in addition to the active ingredients, and for example, include general adjuvants such as antioxidants, stabilizers, solublizers, vitamins, pigments, and fragrances, and carriers.
The cosmetic composition of the present invention may be prepared even in any formulation commonly prepared in the art, and may be formulated by, for example, a solution, a suspension, an emulsion, a paste, a gel, a cream, a lotion, a powder, a soap, a surfactant-containing cleansing, oil, a powder foundation, an emulsion foundation, a wax foundation, a spray, and the like, but is not limited thereto. More specifically, the cosmetic composition of the present invention may be prepared by softener (skin), nourishing toner (milk lotion), nourishing cream, massage cream, essence, eye cream, cleansing cream, cleansing foam, cleansing water, pack, spray or powder formulations.
Preferably, the cosmetic composition of the present invention may be W/O cream, O/W cream, O/W essence and hydrogel formulations, and most preferably a hydrogel formulation, but is not limited thereto.
When the formulation of the present invention is the paste, cream, or gel, as a carrier ingredient, animal oils, vegetable oils, wax, paraffin, starch, tragacanth, cellulose derivatives, polyethylene glycol, silicone, bentonite, silica, talc, zinc oxide or the like may be used.
When the formulation of the present invention is the powder or spray, as the carrier ingredient, lactose, talc, silica, aluminum hydroxide, calcium silicate or polyamide powder may be used, and particularly, in the case of the spray, additionally, a propellant such as chlorofluorohydrocarbon, propane/butane or dimethyl ether may be included.
When the formulation of the present invention is the solution or emulsion, as the carrier ingredient, a solvent, a solubilizing agent or an emulsifying agent may be used. For example, the carrier ingredient includes water, ethanol, isopropanol, ethyl carbonate, ethyl acetate, benzyl alcohol, benzyl benzoate, propylene glycol, 1,3-butyl glycol oil, glycerol aliphatic ester, polyethylene glycol or fatty acid ester of sorbitan.
When the formulation of the present invention is the suspension, as the carrier ingredient, a liquid diluent such as water, ethanol or propylene glycol, a suspension such as ethoxylated isostearyl alcohol, polyoxyethylene sorbitol ester and polyoxyethylene sorbitan ester, microcrystalline cellulose, aluminum metahydroxide, bentonite, agar, tragacanth, or the like may be used.
When the formulation of the present invention is the surfactant-containing cleansing, as the carrier ingredient, aliphatic alcohol sulfate, aliphatic alcohol ether sulfate, sulfosuccinic acid monoester, isethionate, imidazolinium derivatives, methyltaurate, sarcosinate, fatty acid amide ether sulfate, alkylamido betaine, aliphatic alcohol, fatty acid glyceride, fatty acid diethanolamide, vegetable oil, lanolin derivatives, ethoxylated glycerol fatty acid ester, or the like may be used.
In the present invention, the composition may have an antioxidant activity. The antioxidation means an effect of suppressing oxidation, and in the human body, a prooxidant and an antioxidant are balanced, but when this balanced state is imbalanced by various factors and biased toward the promotion of oxidation, oxidative stress is induced to cause potential cell damage and pathological diseases.
In one embodiment of the present invention, it was confirmed that the composition exhibited an excellent DPPH free radical scavenging activity.
The term “whitening” used herein means whitening the skin, and means all actions of inhibiting or preventing the skin pigmentation of melanin by inhibiting the synthesis of melanin. In the present invention, the composition may inhibit the activity of tyrosinase. The tyrosinase is a metal-containing protein containing a pair of copper ions in an active site and refers to an enzyme involved in a process in which in a production path of melanin, L-tyrosine is converted to 3,4-dihydroxyphenyl alanine (L-DOPA) through a hydroxylated reaction, oxidized to phenylalanine-3,4-quinen (dapaquinone) again, and then synthesized to melanin through various intermediates such as dopachrome, indole-5,6-quinen, etc.
In one embodiment of the present invention, it was confirmed that the composition had a tyrosinase inhibitory activity in a concentration-dependent manner and thus, it can be seen that the composition had a whitening activity.
In the present invention, the composition may be characterized by inhibiting the production of melanin. The melanin is made by a dye of black brown granules and is made by a cell organelle called melanosomes in melanocytes. The melanin is present in skin, hair, eye, and the like, and a skin color is determined according to the amount of melanin, and the more the amount of melanin, the darker the skin color.
In one embodiment of the present invention, it was confirmed that the composition had a melanin production inhibitory effect in a concentration-dependent manner and thus, it can be seen that the composition had a whitening activity.
The term “wrinkles” used herein refers to fine lines occurring by declining in the skin, and may be caused by genetic factors, reduction in collagen existing in the skin dermis, external environments, etc. In the present invention, the composition may be characterized by promoting collagen biosynthesis. The collagen is present in a collective tissue such as bone, cartilage, skin, and tendon. When the skin is continuously exposed to external stimuli, such as ultraviolet rays, collagen fibers involved in skin elasticity are damaged, resulting in the aging of the skin.
In one embodiment of the present invention, it was found that the composition may exhibit a wrinkle improvement effect by increasing the collagen biosynthesis in a concentration-dependent manner.
The term “skin aging” used herein shows symptoms such as reduction in elasticity of the skin, reduction in shine, generation of wrinkles, decreased regeneration, or severe drying, and may be caused by the passage of time, external environments, etc.
In one embodiment of the present invention, it was found that the composition may promote the proliferation of fibroblasts to improve regeneration and elasticity of damaged skin.
In another aspect, the present invention provides a food composition for antioxidation, skin whitening, wrinkle improvement or skin anti-aging comprising the conjugate of the ascorbic acid and the hyaluronic acid nanogels as active ingredients.
Further, the present invention provides a food composition for antioxidation, skin whitening, wrinkle improvement or skin anti-aging (essentially) consisting of the conjugate of the ascorbic acid and the hyaluronic acid nanogels as active ingredients.
The food composition according to the present invention includes all forms such as functional foods, nutritional supplements, health foods, and food additives. The types thereof may be prepared in various forms according to a general method known in the art.
For example, as the health food, the food composition itself of the present invention may be prepared in the form of tea, juice, and drinks, to be drunk, or taken in by granulation, encapsulation and powder. Further, the food composition of the present invention may be prepared in the form of a composition mixed with a known material or active ingredient known as an effect of antioxidation, skin whitening, wrinkle improvement or skin anti-aging.
Further, the functional food may be prepared by adding the food composition of the present invention to beverages (including alcoholic beverages), fruits and processed foods thereof (e.g., canned fruit, bottled food, jam, marmalade, etc.), fish, meat and processed foods thereof (e.g., ham, sausage, corned beef, etc.), bread and noodles (e.g., udon, buckwheat noodles, ramen, spaghetti, macaroni, etc.), fruit juice, various drinks, cookies, sweets, dairy products (e.g., butter, cheese, etc.), edible vegetable oil, margarine, vegetable protein, retort food, frozen food, various seasonings (e.g., soybean paste, soy sauce, sauce, etc.), etc.
The preferred content of the food composition according to the present invention is not limited thereto, but is preferably 0.01 to 50 wt % of the total weight of the finally prepared food. In order to use the food composition of the present invention in the form of food additives, the food composition may be used in the form of powder or concentrate.
Further, the present invention also provides a use of a conjugate of the ascorbic acid and the hyaluronic acid nanogels for preparing a preparation for antioxidation, skin whitening, wrinkle improvement, or skin anti-aging.
Further, the present invention provides a method for antioxidation, skin whitening, wrinkle improvement, or skin anti-aging comprising administering an effective dose of the composition comprising the conjugate of the ascorbic acid and the hyaluronic acid nanogels as active ingredients, to a subject in need thereof
The term ‘effective dose’ of the present invention means an amount which exhibits effects of improving, treating, preventing, detecting, and diagnosing of diseases associated with antioxidation, skin whitening, wrinkle improvement, or skin anti-aging, or inhibiting or alleviating diseases associated with antioxidation, skin whitening, wrinkle improvement, or skin anti-aging when administered to the subject. The ‘subject’ may be animals, preferably, mammals, particularly animals including humans and may also be cells, tissues, and organs derived from animals. The subject may be a patient requiring the effects.
The term ‘treatment’ of the present invention comprehensively refers to improving diseases associated with antioxidation, skin whitening, wrinkle improvement, or skin anti-aging or symptoms of the diseases associated with antioxidation, skin whitening, wrinkle improvement, or skin anti-aging. The treatment may include treating or substantially preventing these diseases, or improving the conditions thereof and include alleviating, treating or preventing a symptom or most of symptoms derived from the diseases, but is not limited thereto.
In the present invention, the term ‘comprising’ is used in the same manner as ‘containing’ or ‘characterizing’, and does not exclude additional ingredients or steps of the method which are not mentioned in the composition or the method. The term ‘consisting of’ is used in the same as ‘comprising’ and means excluding additional elements, steps or ingredients, etc., unless otherwise noted. The term ‘essentially consisting of’ or ‘essentially comprising’ means including ingredients or steps that do not substantially affect basic properties thereof in addition to the described ingredients or steps within the range of the composition or the method.
According to the present invention, there is provided a method for preparing pure hyaluronic acid nanoparticles on an aqueous solution without a cross-linking agent and an organic solvent. According to the present invention, there are provided uses as a contrast agent for tumor diagnosis and a therapeutic agent of synthesized hyaluronic acid nanoparticles through the skin permeability confirmed by fluorescence labeling and the radioactive labeling by uniformly synthesizing various nano-meter sizes of hyaluronic acid nanoparticles reproducibly under an optimized electron beam condition.
Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings. The present invention can apply various modifications and may have various forms, and specific embodiments will be illustrated in the drawings and will be described in detail in the specification. However, this does not limit the present invention to specific embodiments, and it should be understood that the present invention covers all the modifications, equivalents and replacements included within the idea and technical scope of the present invention. In describing each drawing, like reference numerals were used for like components.
Terms used in the present application are used only to describe specific embodiments, and are not intended to limit the present invention. A singular form may include a plural form unless otherwise clearly indicated in the context. In the present application, it should be understood that term “including” or “having” indicates that a feature, a number, a step, an operation, a component, a part or a combination thereof described in the specification is present, but does not exclude a possibility of presence or addition of one or more other features, numbers, steps, operations, components, parts or combinations thereof, in advance.
Unless otherwise contrarily defined, all terms used herein including technological or scientific terms have the same meanings as those generally understood by a person with ordinary skill in the art. Terms which are defined in a generally used dictionary should be interpreted to have the same meaning as the meaning in the context of the related art, and are not interpreted as an ideal meaning or excessively formal meanings unless clearly defined in the present application.
In the case of an electron-beam irradiation experiment using hyaluronic acid, three types of hyaluronic acids having different molecular weights below were used and the experiment was performed in an acidic aqueous solution condition.
For reference, through the prior study (Korean Patent Registration No. 1893549), the present inventors confirmed that nanogels of 380 nm were generated when an electron beam of 50 kGy was irradiated to 10 kDa of a hyaluronic acid 1% (w/v) aqueous solution, and nanogels of 108 nm were generated when an electron beam of 200 kGy was irradiated to a hyaluronic acid 5% (w/v) aqueous solution. However, in other conditions, the nanogels were not formed, and even in the case of the nanoparticles prepared under the conditions, it was found that there was a limit to the industrial utilization because the size was relatively large.
Accordingly, the present inventors attempted a method of irradiating an electron beam to a hyaluronic acid aqueous solution under an acidic condition to provide nanogels having very small particle sizes as well as capable of being prepared with economical costs under a lower concentration condition of the hyaluronic acid aqueous solution while using hyaluronic acid (HA1) of a molecular weight (8 kDa) similar to the prior study.
Specifically, HC104 was added to the HA1 aqueous solution of a concentration (w/v %) shown in Table 2 below to adjust pH to 1.6 to 2.1, and then the electron beam was irradiated at energy of 1 MeV with an irradiation dose (kGy) shown in Table 2 below.
The result thereof was shown in Table 2 below.
As shown in Table 2 below, in various electron beam irradiation energy, when hyaluronic acid (HA1) at various concentrations was used and additional acid was added, conditions capable of synthesizing small nanoparticles having a size of 3 to 4 nm with a low polydispersity index were confirmed.
Next, in the case of HA2, it was confirmed that when acid A (HClO4) was added to lower pH to 1.8 to 2.2 and the electron beam was irradiated, the nanoparticles were generated well, and it was confirmed that as the concentration of the added acid was increased, the size of the particles tended to be increased.
Next, even in an experiment using HA3, it was confirmed that nanoparticles were generated when an acid was added. The result thereof was illustrated in
As shown in
The hyaluronic acid nanoparticles showing the result were synthesized in large quantities, and a sample was obtained in a powder form after a freeze-drying process, as shown a photograph of
In the following experiment, nanoparticles were prepared and used by irradiating 100 kGy of an electron beam (irradiation energy of 2.5 MeV) in a 1% (w/v) HA3 aqueous solution at pH 2.0.
(1) Structural analysis of nanoparticles
The study of the synthesized hyaluronic acid nanoparticles was conducted not only to measure the size of the nanoparticles through DLS, but also to directly confirm a morphological shape of the actually synthesized nanoparticles through a transmission electron microscope (TEM).
The nanoparticles were dropped to 2 to 3 drops on a copper grid coated with carbon, subjected to a dying process using uranyl acetate, and then analyzed using TEM illustrated in
Like the results of DLS, it was confirmed that the nanoparticles had small sizes of approximately 10 nm or less, and it was confirmed that the shape of the particle was not clear, but kept an approximately round shape.
(2) Characteristic Analysis of Hydrogel
An experiment of confirming whether the synthesize nanoparticle had a substantially swelling characteristic of a hydrogel was conducted, and the experiment was conducted using pure water and hyaluronic acid without irradiating an electron beam as a control.
The same amounts of hyaluronic acid nanoparticles and control were dissolved in 500 μL of water, respectively, and then centrifuged using a centrifugal filter with a separation membrane to check an amount of water dropped on each tube bottom, and in order to see a difference thereof well, the water dropped below the tube was dyed with green ink and then captured. It was illustrated in
When confirmed the results, it can be confirmed that the amount of water dropped to the bottom of the tube after a centrifuging process is smaller in the nanoparticle sample obtained by irradiating the electron beam and a more solution is left in a supernatant portion. Through such a result, it can be confirmed that hyaluronic acid nanoparticles synthesized through the electron beam irradiation are further swelled than the control and have a characteristic as a hydrogel.
(1) Evaluation of stability of hyaluronic acid nanogels conjugated with contrast agent
As shown in a schematic diagram of
As shown in a schematic diagram of
As a result, as confirmed in
In the case of the stability of radiolabeled nanoparticles, the experiment was performed by checking radiolysis, and the stability of the nanoparticles was confirmed by time-dependent radio-TLC analysis using phosphate buffer saline (PBS) and fetal bovine serum (FBS).
As a result, like the result of
(2) In vivo distribution verifying experiment in normal mouse
An in vivo distribution verifying experiment for a normal mouse was performed by using the hyaluronic acid (HA) nanogels labeled with Cu-64 and a study to verify distribution for organs and in vitro release paths was conducted.
Thereafter, since the synthesized nanoparticles will be used for development and research of a nanogel-based tumor contrast agent, the experiment was planned with a time when the nanogels sufficiently targeted the tumor, and accordingly, the nanogels were injected and then experimented by a method of verifying a distribution for each organ after 24 hours.
When confirming the results thereof, as illustrated in
Thereafter, in a process of synthesizing HA nanogels using an electron beam, a specific acid (HClO4) was added to a beam-irradiated sample to change pH, and then an in vivo distribution verifying experiment was performed in a normal mouse (
Further, even for HA nanogels obtained by a method of precipitating with an organic solvent other than a freeze-drying process of generally obtaining synthesized HA nanogels as a final sample, the in vivo distribution verifying experiment was performed, and as confirmed in
Using nanoparticles made by the labeling reaction with Cu-64, the in vivo distribution verifying experiment was performed in a tumor model, and after 24 hours of injection, the distribution for each organ was confirmed and the intake level for the tumor was confirmed.
First, when a tumor model was prepared using colon tumor cells (CT26) and tumors grew in an appropriate size of 6 to 8 mm, the in vivo distribution verifying experiment was performed in the tumor model. As a result, as confirmed in
In addition, the tumor model was prepared using skin cancer cells (melanoma/B16f10) and the in vivo distribution verifying experiment was performed after 24 hours when the tumor grew at an appropriate size. As confirmed in FIG. 16, high intake was shown in the liver, kidneys and spleen, but it was confirmed that the nanogels were released in vitro through the liver and kidneys, and the tendency to be released through the liver other than the kidneys was higher, and it was confirmed that the high intake was shown even in the spleen due to characteristic of the nanoparticles. Next, in tumor (0.62% ID/g) and lymph node (0.89% ID/g), it was confirmed that high intake was shown, and it was confirmed that the tumor to muscle ratio was 14.2 times and the tumor to blood ratio was 3.2 times to excellently diagnose the tumor.
A nuclear medicine imaging study for a tumor model was conducted by using hyaluronic acid nanogels labeled with radioisotope Cu-64, and the intake of detailed organs and the distribution and release for organs which have not been confirmed in the in vivo distribution verifying experiment performed above, and the target ability for tumor were confirmed.
In the nuclear medicine imaging experiment, colon tumor cells (CT26) were used. As confirmed in
(1) Synthesis of hyaluronic acid nanoparticles bound with ascorbic acid
1) Synthesis of ascorbic acid derivative
As a method for effectively binding hyaluronic acid and ascorbic acid, a strategy to synthesize an ascorbic acid derivative by an ester bond to a carboxylic group of hyaluronic acid was established.
An alkylation condition (1-chloro-3-iodopropane, NaHCO3, DMSO) capable of selectively binding to a hydroxyl group at position 3 of ascorbic acid protected in an acetal form was found and a protective group was removed to synthesize an ascorbic acid derivative in a form capable of binding to hyaluronic acid (
Specifically, an ascorbic acid derivative was synthesized by binding 1-chloro-3-iodopropane to an OH group at position 3 of ascorbic acid protected in an acetal form, substituting a chloro group (Cl) with an iodo group (I), and removing an acetal group as a protective group (
(2) Synthesis of hyaluronic acid nanoparticles bound with ascorbic acid
The prepared ascorbic acid derivative was to bind to the hyaluronic acid nanoparticles prepared in Example 1.
Since the hyaluronic acid nanoparticles having a carboxylic group were not dissolved in DMSO as a reaction solvent, a method of substituting to a tetrabutyl ammonium (TBA) group was used. Specifically, the hyaluronic acid nanoparticles containing the carboxylic group were dissolved in water and gradually added with TBAOH to adjust pH=9 to 10, and then freeze-dried to prepare hyaluronic acid nanogels in TBA forms (
Thereafter, a hyaluronic acid nanogel derivative bound with ascorbic acid in a powder form was obtained by stirring the prepared ascorbic acid derivative substituted with an iodo group with hyaluronic acid nanogels obtained in a TBA form under a DMSO solvent for about 12 hours and adding acetone to a reaction solution (
Whether the hyaluronic acid nanogel derivative bound with ascorbic acid was prepared was confirmed by NMR and HPLC chromatogram, which was shown in
According to the NMR analysis result, it was confirmed that a ratio of ascorbic acid to carboxylic acid of a hyaluronic acid molecule was 2.5:1. That is, it was confirmed that one ascorbic acid per 2.5 carboxylic groups of the hyaluronic acid molecule was bound.
(2) Evaluation of stability and efficacy of hyaluronic acid-ascorbic acid nanoparticles (HA-VitC)
Thermal stability evaluation was analyzed using HPLC after leaving ascorbic acid (AA, 100 uM) and the prepared hyaluronic acid-ascorbic acid nanogels (HA-VitC, 0.5 mg/mL) aqueous solution at 50° C. for 48 hours, respectively.
The result thereof was illustrated in
As illustrated in
(3) Evaluation of efficacy of whitening, antioxidation, and wrinkle improvement of hyaluronic acid-ascorbic acid nanoparticles (HA-VitC)
Whitening efficacy evaluation was measured by melanin contents assay and cellular tyrosinase activity assay after treating each experimental substance to a B16F10 mouse melanoma cell line and incubating the each experimental substance for 48 hours. As a control, ascorbic acid, ascorbic acid-2-glucoside (AA2G) and HAI (Oligo-HA) used in Example 2 were used.
The substances used in the experiment were all left for 24 hours at −20° C. or 50° C. and then used in the experiment.
The result thereof was illustrated in
As illustrated in
Then, the free radical scavenging ability of HA-VitC was evaluated using DPPH assay. Specifically, ascorbic acid, oligo-HA and HA-VitC were treated for each concentration shown in
Referring to
Particularly, when considering that vitamin C is very vulnerable to oxidation after exposure to air and then quickly decomposed, in the case of HA-VitC according to the present invention, it is determined that utilization is very high by improving the storage stability of vitamin C and having the effect of Vit C as it is at the same time.
Next, the cellular tyrosinase inhibitory activity of HA-VitC was evaluated according to a known method:
Cell line: B16F10 mouse melanoma (Passage 10), 6 well plate, 4×105 cells/well
Evaluation method: Cellular tyrosinase activity assay
Experimental substance treatment time: 48 hours
Experimental substance treatment concentration: See
The result thereof was illustrated in
As illustrated in
Next, the fibroblast proliferation effect was evaluated according to a conventional known method.
Briefly, experimental conditions are as follows, and a type of experimental substance and a treatment concentration of each substance are shown in
Cell line: HDF-neo, Human primary dermal fibroblast-neonatal (passage 15), 24 well plate, 1×104 cells/well
Evaluation method: WST-8 assay (Ez-cytox) and Procollagen ELISA (Takara #MK101)
Experimental substance treatment time: 3 day, 1 day fasting, serum free condition
The result thereof was illustrated in
As illustrated in
Next, the effect of HA-VitC on collagen biosynthesis was evaluated according to a conventional known method. Briefly, experimental conditions are as follows, and a type of experimental substance and a treatment concentration of each substance are shown in
Cell line: HDF-neo, Human primary dermal fibroblast-neonatal (passage 11), 96 well plate, 3×103 cells/well
Evaluation method: Procollagen ELISA (Takara #MK101)
Experimental substance treatment time: 3 day, 1 day fasting, serum free condition
The result thereof was illustrated in
As illustrated in
The present invention provides a method for preparing pure hyaluronic acid nanoparticles on an aqueous solution without a cross-linking agent and an organic solvent. The present invention may be very usefully used for developing a contrast agent for tumor diagnosis and a therapeutic agent of synthesized hyaluronic acid nanoparticles through the skin permeability confirmed by fluorescence labeling and the radioactive labeling by uniformly synthesizing various nano-meter sizes of hyaluronic acid nanoparticles reproducibly under an optimized electronic beam condition, and therefore, industrial applicability is very excellent.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2019-0003966 | Jan 2019 | KR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2020/000612 | 1/13/2020 | WO |