Patent Application
20120213911
The invention regards a method for the realization of biologically compatible prosthesis, particularly suitable for obtaining elements implantable in human and animal body.
Prosthesis, such as for example acetabular cups, femoral and tibial implants, glenoids and other components of the like, are used for implants into human or animal bodies so as to replace bone parts or joints which have been irremediably damaged by trauma or diseases such as arthritis and arthrosis.
There are various production techniques. It could be reminded machining for removing chips, casting, Selective Laser Sintering (SLS) and Electron Beam Melting (EBM). The latter two techniques are used to produce prosthesis through deposition and sintering of successive layers of powder.
Some of the external surfaces of the prosthesis are then usually treated to confer porosity and/or roughness features thereto, so as to facilitate or accelerate the osteointegration process.
A particular method, of the subtractive type, is described in the patent application WO2009/004444. A given amount of powder material containing a second removable granular material (also called spacer) having a melting temperature that is higher than the sintering temperature of the former, is placed in a mold. The two materials are first mixed homogeneously, and subsequently subjected to a sintering and solidification process. The obtained object, concave and/or convex, is submerged in water or in an acid or basic solution. Submersion into the solution allows dissolving the spacer material, which leaves the volume it had occupied in the pressing and sintering step empty. After completing dissolution, the piece, which is made up of only the first material, is characterized by the presence of pits and pores on the surface.
This method has limited degrees of freedom regarding the realization of the prosthesis, especially due to the fact that the porous surface and the layer on which it lies are made of the same material. However—consider an acetabulum for example—the ideal choice would be that of having a porous surface made up of a biocompatible material with high osteointegration capacity on an underlying base with high mechanical resistance and resistant to wear. Systems with these two characteristics are not frequent and however do not entirely meet the aforementioned characteristics.
The main object of the invention is defining a method for the realization of biologically compatible prosthesis having greater degrees of freedom in the realization of the prosthesis themselves.
Another object is that of providing biologically compatible prosthesis with improved resistance, duration and compatibility with the body that receives them.
Such object is attained through a method for the realization of a biologically compatible prosthesis component, characterized in that it comprises the steps of having at least two materials with different physical/chemical features, defining in forming means the component—which may be concave and/or convex and/or flat-shaped—as a composition of at least two volumes of said at least two materials, and sintering the component in said forming means and at a preset sintering temperature.
The use of two or more materials allows designing the component with less structural constraints, alongside allowing obtaining a porous surface for osteointegration on a base resistant to wear.
Preferably one or each of the two or more materials is initially available in form of powder, so as to best exploit the sintering techniques. In particular, a porous part may be obtained starting from a first powder material, possibly adding thereto a material called a spacer, having a melting temperature that is greater than the sintering temperature of the first material. Subsequently, the spacer material is removed from the finished component hence creating corresponding empty spaces (pores) on the finished component. However, there are other techniques for forming the porous parts, see for example U.S. Pat. No. 6,849,230. Thus, after sintering, the piece may be entirely dense, given that the spacer is yet to be removed.
It may be provided for that one or each of these two or more materials may be a material initially available in sintered or pre-sintered form. This opens the field to numerous new products, which may exploit the physical/mechanical features of portions of the prosthesis realized or prepared before sintering. Same case applies should one or each of these two or more materials be a material already having a porous structure, which may be associated to the rest of the component sintered in the method described herein, but be produced previously, with the advantage of, for example, disregarding the parameters or requirements of the described sintering method.
Preferably, for production economy, the component is defined by overlapping the two or more materials in layers.
Preferably the sintering method is the SPS (Spark Plasma Sintering) method.
One or more of said materials may be made up of alloys of the same metal and/or different metals and/or pure metals.
The metals may be selected from among: Ti, Cr, Co, Mo, Fe, Zr, Nb, Ta, Mg.
The metal alloys may be selected from among groups that consist of: Cobalt-Chromium, Cobalt-Chromium-Molybdenum, Magnesium, Titanium-Aluminium, Titanium-Nickel, Zirconium-Niobium and Tantalum, Iron-Carbon and any combination therebetween.
Another variant is that one or each of said one or more materials is a ceramic material or a ceramic composite. The ceramic material may be selected from the group consisting of: Alumina, Zirconia, Zirconia stabilized with oxides such as for example Yttria, Ceria, Magnesia, etc., Zirconia Toughened Alumina (ZTA), Alumina Toughened Zirconia (ATZ), Chromium nitride, Silicon Carbide, Silicon Nitride, Titanium Carbide, Titanium Nitride, Zirconium Carbide, Zirconium Nitride, Tantalum Carbide, Tungsten Carbide, Hydroxyapatite, Calcium Phosphate, Magnesia, and any other combination therebetween.
In addition, one or each of said one or more materials may be a material made up of mixture of metal and/or ceramic powders or by a metal or ceramic or polymer matrix or a polymer matrix reinforced by fibrous or particle materials.
The invention also has the aim of providing a biocompatible prosthesis obtained according to the aforedescribed method.
Further characteristics and advantages of the invention shall be clearer from the exemplifying description of the method, alongside the attached drawings wherein:
The present invention is suitable for obtaining orthopaedic prosthesis in general.
In general, the method is suitable for obtaining components, such as orthopaedic prosthesis and the like, made up of two or more materials 20, 22 having different physical/chemical characteristics and which may be in different form in the finished piece depending on the specific application needs, for example dense, or porous, or a combination of both forms, as clarified hereinafter.
By way of non-limiting example, it is specified that the method described in an embodiment thereof is ideal for obtaining a hip prosthesis, for example an acetabulum cup 50 (
More generally, it is specified that the present method may be applied to obtain objects, such as prosthesis and the like, of any shape, without any limitations whatsoever.
The materials 20, 22 preferably have different chemical/physical features and they are selected to maximize a different function with the properties thereof: maximum biointegration for the material 22, maximum resistance to wear and mechanical resistance for the material 20.
The cup 50 may be obtained through sintering methods that use pulsating currents such as for example the Spark Plasma Sintering (SPS), or, generally, through any sintering method (
The spacer material 26 has, suitably, a melting temperature T2 that is greater than the sintering temperature T1.
More in detail, the first material 22, intended for obtaining the porous part of the object to be obtained, is first mixed in a substantially homogeneous manner with the third spacer material 26, for example in form of granules, so as to obtain a mixture containing a spacer percentage equivalent to that of the porosity that is intended to be obtained on the final piece. The mixing step may be performed both manually and with more or less energetic mixing instruments, such as for example, ball milling, high energy milling, etc. The mixing of the first material 22 and the spacer 26 may also include the use of mixing additives such as water or volatile organic solvents which allow creating a slurry. The percentage in volume of the spacer material may generally range between 1% and 99% of the layer provided for. More preferably, the percentage in volume of the spacer material may generally vary between 10% and 80% of the layer provided for and even more preferably between 50% and 80%. The dimensions of the spacer material, for example in form of granules, may range between 5 and 3000 μm. More preferably the dimensions of the spacer material, for example in form of granules, may range between 100 and 1500 μm and even more preferably between 200 and 400 μm or between 400 and 600 μm or between 800 and 1000 μm.
Several layers of the same mixture with percentages of spacer material 26, for example, progressively decreasing, may be provided for to obtain a progressively decreasing porosity so as to provide greater support to the porous layer in the coupling thereof with the second material 20.
Subsequently, the first material 22, mixed with the third spacer material 26 according to the described methods, is arranged inside the die 18 in a manner such that the thickness of the layer is uniform over the entire profile of the die. This operation may be performed both manually and using instruments to facilitate the operation.
Then, a layer of the second material 20 is deposited on the layer of the first material 22. Two materials are considered in the example but the method may provide for even more, depending on the type and structure designed for the prosthesis to be obtained. Even the final structure may be considered as a multilayer, having for example an n number of materials for forming an n number of layers.
However, it should be observed that in other embodiments of the method according to the invention, the order of depositing the materials 20, 22 in the die 18 may be inverted, depending on the type of component to be obtained.
A voltage generator 16 is connected between the punch 12 and the die 18 with the aim of inducing a current between the two pieces. Such current also flows in the materials (conductors) 20, 22 and locally generates plasmas between the particles thereof, optimizing the densification of the powders. After completing sintering, during which the third spacer material 26 has not melted, the object made up of the three materials 20, 22, 26 is taken from the mold 10 and submerged in water or a suitable solution (acid or basic), so as to dissolve the material 26, remove it from the host material 22 leaving it partly porous. The space emptied by the material 26 constitutes the empty spaces or pores of the porous part 52.
An embodiment of the method according to the invention comprises, at this point, a further step of optimizing the densification of the component obtained through thermal treatments, performed at a temperature lower than the lowest among the melting temperatures of the materials that constitute the component, with or without using a given treatment pressure (for example methods such as Hot Isostatic Pressing).
Another embodiment of the method according to the invention comprises, at this point, a further step of performing mechanical post-machining operations on the obtained component to modify the surface quality of a part or the entire component, for example in terms of surface roughness.
Another embodiment of the method according to the invention comprises, at this point, a further step of depositing, on a part of the component or on the entire component, a single or multi-layer coating, through the Plasma Spray technique, a biologically compatible material which helps the osteointegration of Titanium and/or Hydroxyapatite and/or a material belonging to the class of Calcium-Phosphates.
Another embodiment of the method according to the invention comprises, at this point, a further step of depositing, on a part of the component or on the entire component, a single or multi-layer coating, through chemical or electrochemical means, a biologically compatible material which helps the osteointegration of Hydroxyapatite and/or a material belonging to the class of Calcium-Phosphates.
Another embodiment of the method according to the invention comprises, at this point, a further step of depositing, on a part of the component or on the entire component, a single or multi-layer coating, through the Physical Vapor Deposition (PVD) or Chemical Vapor Deposition (CVD) techniques, of a biologically compatible material capable of facilitating osteointegration.
Another embodiment of the method according to the invention comprises, at this point, at least one further step of performing surface treatments on a part or on the entire component suitable to modify the surface roughness of the same components. Examples of such treatments may be sanding, or other treatments both mechanical and chemical.
Depending on the type and number of materials and layers present in the sintering method, the final components provided according to the invention may, for example, be made up of or comprise:
The following may be used as ceramic materials for such purpose: Zirconium Oxide (Zirconia), Y-TZP (Yttria Stabilized Zirconia), PSZ (Zirconia stabilized for example using MgO, CeO2, etc.), Alumina, ZTA (Zirconia Toughened Alumina), ATZ (Alumina Toughened Zirconia). The matrix may contain carbon fibers;
MgO may be used as the spacer material 26 but even for example sodium chloride or hydroxyapatite may also be used.
The sintering temperatures and the other parameters of the method depend on many variables, among which the type of object to be produced, the shape thereof, the constituting materials and the materials with which the mold is made. For example, should one want to obtain a prosthesis component having a Co-Cr alloy as a constituent of the dense part and Titanium grade 4 as the constituent of the porous part, the sintering temperature may range between 500-2000° C., the pressure may range between 5-100 MPa and the duration of the sintering may vary between 1-20 minutes.
These values, just like for the currents circulating in the mold, should be optimized from time to time. They strongly depend on the materials, the shape of the mold and the geometry of the object to be sintered.
Regarding, in particular, objects made using the first material 22 and the second material 20 of different type and thus with different characteristics, it is hereby also pointed out the following.
Should the two or more materials 20, 22 have a different coefficient of thermal dilation, as it for example occurs in cases whereby the second material 20 is a material of the ceramic type of materials, while the first material 22 is a metal material, at the end of the sintering method, the cooling of the produced piece determines a considerable contraction of the first metal material 22, such contraction instead being lower in the second material 20, considerably lower or absent in case of ceramic material.
This effect, particularly but not exclusively if the produced piece has a substantially acetabular form or the like, but also in the substantially flat pieces, allows obtaining a better quality coupling between the two materials 20, 22, for example better than the traditional conical coupling used in this type of objects. Actually, it is known in the field that the interface area between the two materials 20, 22 constitutes a weak link for this type of objects: a conventional conical coupling, for example, may detach easily and inadvertently.
It should thus be observed that the contraction of the first metal material 22 determines the occurrence of a given internal “lock” tension between the two materials 20, 22, which in particular withholds the second material 20 within the first material 22 in a considerably firm, rigid and precise manner with respect to what occurs in the pieces produced through conventional methods. Furthermore, due to this effect, thinner metal layers may be obtained, increasing the thickness of the ceramic layer.
Another embodiment of the method according to the invention provides for the realization of a component made up of two materials 20, 22, with different physical/chemical features, which define two respective volumes both dense, i.e. without any porous area, so as to meet the needs of some specific applications which require this solution, for example applications which provide for a subsequent step of creating a porous coating through the Plasma Spray technique or the like.
The method, thus comprises at least the steps of defining the component, in the forming means 10, as a composition of two volumes of different materials 20, 22, followed by a step of sintering, in the forming means 10, the two volumes of materials 20, 22, which in particular acquire the form, in the obtained component, of two respective adjacent or coupled layers.
In the case of association between ceramic and metal material, the previously described improvement of coupling quality effects may be obtained.
At this point, possible further steps, such as surface treatments, mechanical machinings, deposition of coating layers (for example through Plasma Spray), etc., may be carried out as described previously to obtain a component having the desired characteristics.
In another embodiment of the method according to the invention, the component is defined, in the forming means 10, as the composition of volumes of materials 20, 22 of different physical/chemical features, and at least one volume of a third spacer material 26.
More in detail, the component to be obtained is defined as a succession of volumes of the above-mentioned materials 20, 22, 26. For example, it is possible to define, in the forming means 10, the component 50, 60, 90 as made up of at least one layer of the second material 20, coupled to at least one layer of the first material 22, to which at least one layer of the third spacer material 26, for example in form of granules, however not mixed to any other material in this case is associated in turn (the order of the layers may obviously be inverted depending on the type of component to be obtained).
Thus, at the end of the sintering step provided for, the third spacer material 26 is removed, through the aforementioned techniques, so as to create a rough surface on the component 50, 60, 90. The roughness of the surface may be defined, for example, by the size of the granules of the third spacer material 26.
At the end of the latter step, further steps, such as surface treatment, mechanical machinings, deposition of coating layers, etc., may be performed as described previously to obtain a component of the desired characteristics.
| Number | Date | Country | Kind |
|---|---|---|---|
| VR2009A000154 | Sep 2009 | IT | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/IB10/54401 | 9/29/2010 | WO | 00 | 3/29/2012 |