Method for the Synthesis of Ferric Oraganic Compounds

Information

  • Patent Application
  • 20190047934
  • Publication Number
    20190047934
  • Date Filed
    December 17, 2015
    8 years ago
  • Date Published
    February 14, 2019
    5 years ago
Abstract
The present invention relates to an improved method for the synthesis of Ferric Citrate and also to provide an amorphous form of Ferric Citrate having an active surface area less than 14 sq.m/g.
Description
FIELD OF INVENTION

The present invention describes a novel process for the preparation of pharmaceutical grade Ferric Citrate (I) used for the treatment of a various disorders such as hyperphosphatemia and metabolic acidosis. Ferric Citrate is also a common nutritional supplement against iron deficiency.




embedded image


BACKGROUND OF THE INVENTION

Ferric Citrate or Iron (III) citrate is chemically known as Iron (III) 2-hydroxypropane-1,2,3-tricarboxylate. Ferric Citrate was approved by the U.S. Food and Drug Administration on Sep. 5, 2014 for the control of serum phosphorous levels in patients with treatment of chronic kidney disease (CKD) on dialysis. Ferric Citrate is garnet red or pale brown odorless powder.


The following patents and applications describe the synthesis of Ferric Citrate.


PL 69800 describes the general synthetic approach for the production of Ferric Citrate and involves the reaction of ferric hydroxide with citric acid under heating for 120 min after complete dissolution; the resulting solution was filtered to remove undissolved ferric hydroxide and evaporated at 35° and 20-30 mm Hg to a thick syrup. The obtained crude was treated with methanol to precipitate methanol.


IT529984 describes another process for the preparation of Ferric Citrate using Iron filings by heating a mixture of Iron filings and aqueous citric acid at 80° C. for 14-16 hrs followed by oxidation with nitric acid.


JP 18/79861 application discloses a process for the production of Iron complex from alkali citrate and iron carbonate followed by reaction with sodium citrate to obtain Ferric Citrate consisting of 60% of iron.


U.S. Pat. No. 5, 206,265 discloses a process for the preparation of Ferric Citrate, which involves the reaction of ferric chloride hexahydrate with sodium bicarbonate followed by addition of trisodium citrate. The resulting solution was dialyzed to remove low molecular weight compounds and freeze dried.


U.S. Pat. No. 7,767,851 B2 describes a process for the synthesis of Ferric Citrate by adding an alkaline metal hydroxide solution to a ferric chloride solution and isolating a ferric hydroxide precipitate. Adding citric acid to the ferric hydroxide in water suspension followed by heating, precipitates the solid form of Ferric Citrate.


U.S. Pat. No. 6,903,235 B2 describes another method for the synthesis of Ferric Citrate by mixing solid citric acid with a solid ferric salt to form a mixture followed by addition of alcohol to the mixture and filtering the solid Ferric Citrate.


Most of the reported procedures in the prior art processes are associated with one or other drawbacks and the Ferric Citrate produced by most of the prior art processes was not suitable in the pharmaceutical applications. Moreover, some of the reported processes are very tedious and not suitable for an industrial scale production. In order to overcome the problems associated with prior art, there is a need to develop an efficient and cost effective method for the commercial scale production of pharmaceutical grade Ferric Citrate, which meets all the required specification as a drug.


SUMMARY OF THE INVENTION

In light of the forgoing deficiencies in the prior art, one of the object of the invention is to provide pharmaceutical grade Ferric Citrate.


Another object of the invention is to develop an improved process for the synthesis of pharmaceutical grade Ferric Citrate having an active surface area less than 14 sq.m/g.


Yet another object of the invention is to provide alternate method for the preparation of amorphous form of Ferric Citrate with BET less than 14 sq.m/g.


Another object of the present invention is to provide Ferric Citrate which has intrinsic dissolution rate of about 0.1-1.5 mg/cm2/min.


The present invention provides an improved process for the preparation of Ferric Citrate of formula I. The below process also provides Ferric Citrate having an active surface area less than 14 sq.m/g,




embedded image


which comprises:


a)adding alkali metal carbonate to an aqueous solution of ferric chloride at 25-30° C.;


b)isolating a solid ferric hydroxide (various forms of ferric hydroxides such as hydrated ferric oxide, ferric oxyhydroxide, polymeric ferric hydroxide, ferric hydroxide gel) at pH ranging from 6.8.0 to 8.5;


c) adding ferric hydroxide to an aqueous solution of citric acid monohydrate and heating at 80 to 120° C.;


d) reducing the volume of water to 60% to 30% followed by precipitation of Ferric Citrate by adding it to water miscible organic solvent at 25-30° C. or adding water miscible organic solvent to it;


e) optional purification of Ferric Citrate from a water miscible organic solvent, alternatively from a mixture of water and water miscible organic solvent.


In another embodiment, the present invention relates to a process for the preparation of amorphous form of Ferric Citrate with defined water content, which comprises


a) Purification of Ferric Citrate from water miscible organic solvent


b) drying the product under vacuum at 25-30° C.


The present invention is schematically represented as follows.




embedded image





DRAWINGS

In drawings which illustrate specific embodiments of the invention, but which should not be construed as restricting the scope of the invention in any way:



FIG. 1 is an X-ray diffraction spectrum of the Ferric Citrate.



FIG. 2 is a thermo gravimetric analysis of Ferric Citrate.





DETAILED DESCRIPTION OF THE INVENTION

In one embodiment, this invention provides an alternate method for the synthesis of ferric organic compounds such as Ferric Citrate having an active surface area less than 14 sq.m/g, which comprises the reaction of ferric chloride with alkali metal carbonate to form a colloidal suspension of ferric hydroxide (III), which is further treated with aqueous solution of citric acid or citric acid monohydrate to form Ferric Citrate. Finally the Ferric Citrate was precipitated from aqueous solution by reducing the volume of water and mixing water miscible organic solvent, which is optionally further purified from water miscible organic solvent, alternatively from a mixture of water and water miscible organic solvent.


In another embodiment, the preparation of colloidal suspension of ferric hydroxide of formula III involves the addition of alkali metal carbonate to an aqueous solution of ferric chloride hexahydrate with the liberation of carbon dioxide gas at 25-30° C.


Alternatively, the preparation of ferric hydroxide involves the formation of ferric carbonate by reaction of ferric chloride hexahydrate with sodium carbonate, which is further converted into ferric hydroxide by removal of excess carbon dioxide gas by purging of nitrogen gas in the reaction at a temperature ranging from 15 to 40° C.


In another aspect of the invention, the alkali metal carbonate used was selected from carbonates such as sodium carbonate, potassium carbonate, calcium carbonate or the like.


In an aspect of the invention, the process comprises the addition of 20 to 50% aqueous solution of sodium carbonate to an aqueous solution of ferric chloride hexahydrate and adjusting the pH of the solution to 6.8 to 8.5 at a temperature ranging from 15 to 40° C.


The precipitated ferric hydroxide was filtered and washed with excess water to remove the excess chloride content or to maintain less than 100ppm or to the non-detectable level.


In the next step, the ferric hydroxide isolated was treated with citric acid, more preferably citric acid monohydrate and heated the suspension to 80 to 150° C. depending up on the reaction volume. The quantity of citric acid can vary from 0.9 to 2 equivalents and in one aspect the quantity used ranges from 1.25 to 1.5 equiv.


In one aspect, the reaction temperature ranges from 100 to 130° C. and the reaction was maintained for 3 to 24 h, more preferably the reaction was carried for 12 to 16 h.


Ferric Citrate was isolated by reducing the water volume to 60% to 30% and precipitating the product by adding water miscible organic solvent.


Finally the precipitated Ferric Citrate was purified from a water miscible organic solvent or from a mixture of water and water miscible organic solvent to obtain the pharmaceutical grade Ferric Citrate, which meets all the standard specification.


In another aspect, the water miscible organic solvent used in the present invention for the precipitation of Ferric Citrate is selected from the group of protic and aprotic solvents. The preferred protic solvents are alcohols like methanol, ethanol, and isopropyl alcohol; Aprotic solvent is selected from the group comprising carbonyl compounds like acetone, 2-butanone, methyl tertiary butyl ketone; ethers like THF, 1,4-dioxane;amides like dimethyl formamide, dimethyl acetamide; other solvents like dimethyl sulfoxide, acetonitrile.


The process further comprises the drying of the purified Ferric Citrate, more preferably the purified Ferric Citrate is dried under vacuum at a temperature less than 30° C. The moisture content of the product produced by this method contains about less than 25% (w/w) as determined by general KF method after drying.


According to one embodiment of the invention Ferric Citrate produced by the method described above is having an active surface area less than 14.0 sq.m/g


According to another embodiment of the invention, Ferric Citrate produced by any known or unknown methods having an active surface area (BET) greater than 14.0 sq.m/g can be converted to Ferric Citrate with active surface area (BET) less than 14.0 sq.m/g by spraying the active with a mixture of water and water miscible organic solvent or by dissolving the active with water miscible organic solvent, wherein the water miscible organic solvent is as described herein.


According to another embodiment of the invention, Ferric Citrate produced by any known or unknown methods having an active surface area (BET) greater than 14.0 sq.m/g can be converted into Ferric Citrate with active surface are (BET) less than 14 sq.m/g by treating the active with a mixture of water and water miscible organic solvent. ‘Treating the active’ involves spraying the ferric citrate with a mixture of water and water miscible organic solvent or by dissolving in a mixture of water and water miscible organic solvent, wherein the water miscible organic solvent is as described herein.


Ferric Citrate prepared by any known method having (BET) surface area greater than 14 sq.m/g can be taken in a tray, to that 1 volume of 10% of water in acetone solution was added over the solid and blended the sample for uniformity. The obtained solid was dried under vacuum at 50-55° C. until MC (moisture content) complies. If the surface area of sample is still greater than 14 sq.m/g, then the same process repeated until (BET) surface area is below the 14 sq.m/g.


The analysis of BET is according to the method described as: out gassing a portion of the test sample, about 100 mg at 90° C. for 1 hour at ambient pressure using nitrogen as the adsorbate gas.


In one aspect of the invention Ferric Citrate or Iron (III) citrate produced by this method is amorphous powder, which is characterized by X-Ray powder diffraction method as shown in FIG. 1 and TGA as shown in FIG. 2.


In yet another aspect of the invention the Ferric Citrate obtained from the present invention have the intrinsic dissolution rate of about 0.1-1.5 mg/cm2/min


In conclusion, the authors have disclosed an improved industrial scale process for the synthesis of Ferric Citrate.


The following examples further illustrate the present invention, but should not be construed in anyway as to limit its scope.


EXAMPLE I

Preparation of Ferric Citrate of Formula I


100 g of Ferric chloride hexahydrate was dissolved in water, adjusted pH of the solution to 8.0-8.5 with 1200 ml of 20% Sodium carbonate solution and stirred the solution for 90 minutes at 25-30° C. Filtered the precipitated solid and slurred in water to remove excess chloride (less than 100 ppm). The obtained solid was added to a solution containing 1.5 eq. of Citric acid monohydrate dissolved in water at 25-30° C., heated the solution to 100-120° C. for 15-16 hrs and filtered through hiflo bed. The resulting filtrate was passed through micron filter and reduced the volume of solvent to 30% of its volume under vacuum at below 50° C. and precipitated final product by adding 2000 ml of acetone. The obtained Ferric Citrate was purified by suspending in 300 ml of acetone, filtered and dried under vacuum at 25-30° C. The final product obtained as an amorphous powder with BET active surface area less than 14 sq.m/g


Yield: 55-65%


Moisture content: 18%


Specific surface area: 12.36 sq.m/g


Chloride content: less than 20 ppm


EXAMPLE II

Preparation of Ferric Citrate of Formula I


100 g of Ferric chloride hexahydrate was dissolved in water, adjusted pH of the solution to 8.0-8.5 with 1000 ml of 20% potassium carbonate solution and stirred the solution for 90 minutes at 25-30° C. Filtered the precipitated solid and slurred in water to remove excess chloride (less than 100 ppm). The obtained solid was added to a solution containing 1.5 eq. of Citric acid monohydrate dissolved in water at 25-30° C., heated the solution to 100-120° C. for 15-16 hrs and filtered through hiflo bed. The resulting filtrate was passed through micron filter and reduced the volume of solvent to 30% of its volume under vacuum at below 50° C. and precipitated final product by adding 1500 ml of Isopropyl alcohol. The obtained Ferric Citrate was purified by suspending in 300 ml of Isopropyl alcohol, filtered and dried under vacuum at 25-30° C. The final product obtained as an amorphous powder with BET active surface area less than 14 sq.m/g


Yield: 55-65%


Moisture content: 18.6%


Specific surface area: 10.6 sq.m/g


Chloride content: less than 20 ppm


EXAMPLE III

Preparation of Ferric Citrate of Formula I


100 g of Ferric chloride hexahydrate was dissolved in water, adjusted pH of the solution to 8.0-8.5 with 1500 ml of 20% Calcium carbonate solution and stirred the solution for 90 minutes at 25-30° C. Filtered the precipitated solid and slurred in water to remove excess chloride (less than 100 ppm). The obtained solid was added to a solution containing 1.5 eq. of Citric acid monohydrate dissolved in water at 25-30° C., heated the solution to 100-120° C. for 15-16 hrs and filtered through hiflo bed. The resulting filtrate was passed through micron filter and reduced the volume of solvent to 30% of its volume under vacuum at below 50° C. and precipitated final product by adding 2500 ml of methanol. The obtained Ferric Citrate was purified by suspending in 300 ml of methanol, filtered and dried under vacuum at 25-30° C. The final product obtained as an amorphous powder and specific surface area is less than 14 sq.m/g


Yield: 55-65%


Moisture content: 9.3%


Specific surface area: 12.0 sq.m/g


Chloride content: less than 20 ppm


EXAMPLE IV

Preparation of Ferric Citrate of Formula I


100 g of Ferric chloride hexahydrate was dissolved in water, adjusted pH of the solution to 7.0-8.0 with 1400 ml of 20% Sodium carbonate solution and stirred the solution for 90 minutes at 25-30° C. Filtered the precipitated solid and slurred in water to remove excess chloride (less than 100 ppm). The obtained solid was added to a solution containing 1.5 eq. of Citric acid monohydrate dissolved in water at 25-30° C., heated the solution to 100-120° C. for 15-16 hrs and filtered through hiflo bed. The resulting filtrate was passed through micron filter and reduced the volume of solvent to 30% of its volume under vacuum at below 50° C. and precipitated final product by adding 2000 ml of Isopropyl alcohol. The obtained Ferric Citrate was purified by suspending in 300 ml of acetone, filtered and dried under vacuum at 25-30° C. The final product obtained as an amorphous powder with BET active surface area less than 14 sq.m/g


Yield: 55-60%


Moisture content: 17.5%


Specific surface area: 11.0 sq.m/g


Intrinsic dissolution rate: 0.231 mg/sq.cm/min


Chloride content: less than 20 ppm


EXAMPLE V

Preparation of Ferric Citrate of Formula I


100 g of Ferric chloride hexahydrate was dissolved in water, adjusted pH of the solution to 6.8-8.0 with 400 ml of 20% Sodium carbonate solution and stirred the solution for 60-70 minutes at 10-15° C. Filtered the precipitated solid and slurred in water to remove excess chloride (less than 100 ppm). The obtained solid was added to a solution containing 1.5 eq. of Citric acid monohydrate dissolved in water at 25-30° C., heated the solution to 80-85° C. for 1-2 hrs until and filtered through hiflo bed. The resulting filtrate was passed through micron filter and reduced the volume of solvent to 30% of its volume under vacuum at below 50° C. andthe filtrate is then added to 1000 ml of acetone. The obtained Ferric Citrate solid was purified by suspending in 300 ml of acetone and stirred the reaction mass for 5-60 minutes. The final product was washed with acetone, filtered and dried under vacuum at 25-30° C. The final product obtained washed with acetone and as an amorphous powder with BET active surface area less than 14 sq.m/g


Yield: 55-65%


Moisture content: 18%


Chloride content: less than 20 ppm


Specific surface area: 7.8 sq.m/g


Intrinsic dissolution rate is 0.31 mg/sq.cm/min


EXAMPLE VI

100 g of Ferric Citrate (surface area is 28.6. Sq.m/g) was taken in a rotocone vacuum dryer (rcvd), to this 150 ml of water and acetone mixture prepared by mixing 15 ml of water in 135 ml of acetone was added and blended the mixture for 1-2 hrs at 25-30° C. The obtained solid was dried under vacuum at 50-55° C. until MC complies (MC limit NMT 15). Surface area of the sample is 10.3 sq.m/g.


If the surface area of the sample is still greater than 14 sq.m/g, then repeat the same process until surface is less than 14 sq.m/g.


EXAMPLE VII

100 g of Ferric Citrate (surface area is 30.0 Sq.m/g) was taken in a rotocone vacuum dryer (rcvd), to this 100 ml of water and acetone mixture prepared by mixing 10 ml of water in 100 ml of acetone was added and blended the mixture for 1-2 hrs at 25-30° C. The obtained solid was dried under vacuum at 50-55° C. until MC complies (MC limit NMT 15). Surface area of the sample is 20.0 sq.m/g. Repeated the same process to get the surface area 12.5 sq.m/g.

Claims
  • 1. A process for preparing Ferric Citrate having (BET) surface area less than 14 sq.m/g and with intrinsic dissolution rate of about 0.1-1.5 mg/cm2/min, the process comprising: a) adding alkali metal carbonate to an aqueous solution of ferric chloride in the range of 25-30° C.;b) isolating solid ferric hydroxide at a pH in the range of 6.8 to 8.5;c) adding ferric hydroxide to an aqueous solution of citric acid monohydrate and heating in the range of 80 to 120° C.;d) reducing the volume of water to 60% to 30% followed by precipitation of Ferric Citrate by one of adding it to water miscible organic solvent in the range of 25-30° C. and adding water miscible organic solvent to it.
  • 2. The process as claimed in claim 1, wherein the alkali metal carbonate comprises at least one of the following: sodium carbonate, potassium carbonate, and calcium carbonate.
  • 3. The process as claimed in claim 1, wherein the water miscible organic solvent is protic solvent or aprotic solvent.
  • 4. The process as claimed in claim 3, wherein the protic solvent comprises at least one of the following: alcohol, methanol, ethanol, and isopropyl alcohol.
  • 5. The process as claimed in claim 3, wherein the aprotic solvent comprises at least one of the following: a carbonyl compound, acetone, 2-butanone, methyl tertiary butyl ketone; ethers like THF, 1,4-dioxane, an amide, dimethyl formamide, dimethyl acetamide, a solvent, dimethyl sulfoxide, and acetonitrile.
  • 6. A process for preparing Ferric Citrate having (BET) active surface area of less than 14 sq.m/g which, comprising: a) treating 1 volume of 10% of water in water miscible organic solvent to Ferric Citrate having (BET) surface area greater than 14 sq.m/g;b) and optionally blending the sample for uniformity.
  • 7. The process as claimed in claim 6, wherein the water miscible organic solvent is protic solvent or aprotic solvent.
  • 8. The process as claimed in claim 6, wherein the protic solvent comprises at least one of the following: alcohols, methanol, ethanol, and isopropyl alcohol.
  • 9. The process as claimed in claim 6, wherein the aprotic solvent comprises at least one of the following: a carbonyl compound, acetone, 2-butanone, methyl tertiary butyl ketone; ethers like THF, 1,4-dioxane, an amide, dimethyl formamide, dimethyl acetamide, a solvent, dimethyl sulfoxide, and acetonitrile.
  • 10. A process for reducing (BET) active surface area of Ferric Citrate to less than 14 sq.m/g, comprising: a) treating 1 volume of 10% of water in water miscible organic solvent to Ferric Citrate having (BET) surface area greater than 14 sq.m/g;b) and optionally blending the sample for uniformity.
  • 11. The process as claimed in claim 10, wherein the water miscible organic solvent is protic solvent or aprotic solvent.
  • 12. The process as claimed in claim 10, wherein the protic solvent comprises at least one of the following: alcohols, methanol, ethanol, and isopropyl alcohol.
  • 13. The process as claimed in claim 10, wherein the aprotic solvent comprises at least one of the following: carbonyl compound, acetone, 2-butanone, methyl tertiary butyl ketone; ethers like THF, 1,4-dioxane, an amide, dimethyl formamide, dimethyl acetamide, a solvent, dimethyl sulfoxide, and acetonitrile.
Priority Claims (1)
Number Date Country Kind
6352/CHE/2014 Dec 2014 IN national
PCT Information
Filing Document Filing Date Country Kind
PCT/IN2015/050208 12/17/2015 WO 00