Patent Application
20240426029
The present invention relates to a method of treating a fibrous raw material containing cellulosic and polyester fibres.
Currently almost all postconsumer textile waste is sent to incineration or landfills despite approximately 95% of textiles being recyclable. Only a small portion of pre-consumer waste is mechanically recycled. Since the beginning of 2016 disposing of used textiles as landfill has been prohibited in the European Union (EU). Thus, in EU countries, textiles and their raw materials that cannot be reused or recycled are typically burnt in energy production plants.
Naturally, recycling would be preferred. The clothing textile market is predominantly based on either cotton or polyester, both of which have an environmental impact. Cotton growing, for example, requires huge amounts of water as well as pesticides and artificial fertilizers. The global demand for cotton has seriously outgrown the planet's resources for producing virgin material. Therefore, it is essential that postconsumer textile waste is recycled. Processing textile materials to obtain reusable fibres is known, e.g. from WO2013/124265A1, which describes the regeneration of a cellulose containing material by dispersing and precipitation.
One process used in the recycling of cotton-based textile waste materials is described in WO2018/197756 in which the textile material is treated in an alkaline extraction and then further treated with an acid to cause at least a partial dissolution of the textile-based material.
Another known technique utilized in recycling is the hydrolysis of the fibres. Typically, it is preceded by a mechanical removal of metals and hard polymer pieces, such as buttons and zippers. For example, WO2010/124944A1 discloses a process for the hydrolysis of cellulose.
The Lyocell process is a process in which cellulose is regenerated by dissolving a cellulosic starting material in a first generation ionic liquid, NMMO. Ioncell-F, developed from the lyocell process, is a regeneration process including a dissolution of the starting material using a recently developed ionic liquid as solvent (WO2014/162062A1). The BioCelSol process, in turn, utilizes an enzymatic treatment of the starting material. Both of these processes, however, focus on preparing textiles from wood.
The chemically separated fraction of cellulose fibres can subsequently be used for various purposes, including carbamation or spinning.
It is known from U.S. Pat. No. 7,662,953 how carbamate cellulose is manufactured from high quality virgin cellulose raw materials such as dissolving pulp. A multi-phase dissolution technique for carbamate cellulose is presented in U.S. Pat. No. 8,066,903, where it is taught how a low temperature is applied in the dissolution and how the solution is prepared by first wetting the mass in low diluted alkali and then in highly concentrated and strongly chilled alkali.
A separation method involving a combination of mechanical and chemical processes for the separation of cellulose fibres from a textile material comprising cellulose fibres and other fibre and non-fibre elements is described in EP 3 511 448 A1. In such a process, the textile materials are first shredded in order to remove larger non-fibre foreign bodies. The remaining fibre components are then mechanically treated to separate cellulose fibres from non-cellulose fibres before the cellulose fibres undergo a chemical treatment to remove any non-cellulose fibres still remaining on the cellulose fibres.
A process for the separation of the cellulosic part from a polyester and cellulose composition is described in international patent application publication WO 2020 013755 A1. The application describes a process for separation of the cellulosic part from a raw material composition comprising polyester and cellulose containing composition, a cellulosic composition obtainable from the process for separation, a mixture comprising polyester hydrolysis products obtainable from the process for separation, a pulp, a dissolving pulp, a paper pulp, a regenerated cellulosic fibres product, and a paper product. In the separation process a polyester/cellulose composition is contacted with a hydrolyzing liquor comprising an alkaline solution. Polyester hydrolysis products form as a part of the separation process and build up in the alkaline solution.
U.S. Pat. No. 4,345,039 discloses a method of recovering polyester fibres from polyester/cotton textile waste. In the method the mixed textile is treated with anhydrous HCl gas, which while not damaging to the polyester, degrades the cellulosic material to cellulosic powder and results in chlorinated hydrocarbons.
It is an aim of the present invention to overcome at least some of the problems associated with the prior art and provide a method of treating a fibrous raw material containing cellulosic and polyester fibres
The invention is defined by the features of the independent claim. Some specific embodiments are defined in the dependent claims.
According to a first aspect of the present invention, there is provided a method of treating a fibrous raw-material, comprising the steps of providing a fibrous raw-material containing cellulosic fibres and polyester fibres, subjecting the raw-material to acid treatment at a pH of less than 5 in an aqueous acid medium to obtain a first modified raw-material, subjecting the first modified raw-material to a washing operation carried out with water, subjecting the washed first modified fibrous raw-material to a an alkaline treatment at a pH of more than 7 in an alkaline cooking liquor to dissolve at least a portion of the polyester fibres and to form a second modified fibrous raw-material, subjecting the second modified fibrous raw-material to separation to separate solid matter from an aqueous liquid phase comprising dissolved material, recovering the solid matter of the separation, subjecting the recovered second modified raw-material, i.e. the solid material of the separation, to a washing operation carried out with water or an aqueous liquid, subjecting the liquid phase, i.e. the aqueous liquid phase from the separation and/or previous washing step, to a first membrane filtration step using a micromembrane to obtain a first reject fraction and a first aqueous permeate, subjecting the first permeate to a second membrane filtration step using a nanomembrane to obtain a second reject fraction and a second permeate, recovering the second aqueous permeate and recycling the second aqueous permeate to an alkaline treatment step.
As mentioned above it is an aim of the present invention to provide a method of treating a fibrous raw material. By means of the present invention it has surprisingly been found that hydrolysis products arising from polyester depolymerisation can be removed from an alkaline cooking liquor by membrane filtration, providing a permeate that can be recycled to an alkaline treatment step, thereby improving the economy in terms of the amount of alkaline needed to treat a fibrous raw material.
According to an example aspect of the present invention, there is provided a method of treating a fibrous raw-material containing cellulosic fibres and polyester fibres, comprising the steps of subjecting the raw-material to acid treatment in an aqueous acid medium to obtain a first modified raw-material, subjecting the first modified raw-material to a washing operation carried out with water, subjecting the washed first modified fibrous raw-material to an alkaline treatment in an alkaline cooking liquor to dissolve at least a portion of the polyester fibres and to form a second modified fibrous raw-material, subjecting the second modified fibrous raw-material to separation to separate solid matter from an aqueous liquid phase comprising dissolved material, recovering the solid matter of the separation, subjecting the recovered second modified raw-material, i.e. the solid material of the separation, to a washing operation carried out with water or an aqueous liquid, wherein a washed solid material and liquid phase comprising the washing solution are obtained, subjecting the liquid phase(s) to a first membrane filtration step using a micromembrane to obtain a first reject fraction and a first aqueous permeate, subjecting the first permeate to a second membrane filtration step using a nanomembrane to obtain a second reject fraction and a second permeate, recovering the second aqueous permeate and recycling the second aqueous permeate to an alkaline treatment step.
Thus, embodiments relate to a method of treating a fibrous raw-material. In an embodiment the method comprises the steps of providing a fibrous raw-material containing cellulosic fibres and polyester fibres, subjecting the raw-material to acid treatment at a pH of less than 5 in an aqueous acid medium to obtain a first modified raw-material, subjecting the first modified raw-material to a washing operation carried out with water, subjecting the washed first modified fibrous raw-material to a an alkaline treatment at a pH of more than 7 in an alkaline cooking liquor to dissolve at least a portion of the polyester fibres and to form a second modified fibrous raw-material, subjecting the second modified fibrous raw-material to separation to separate solid matter from an aqueous liquid phase comprising dissolved material, recovering the solid matter of the separation, subjecting the recovered second modified raw-material to a washing operation carried out with water or an aqueous liquid, subjecting the liquid phase to a first membrane filtration step using a micromembrane to obtain a first reject fraction and a first aqueous permeate, subjecting the first permeate to a second membrane filtration step using a nanomembrane to obtain a second reject fraction and a second permeate, recovering the second aqueous permeate and recycling the second aqueous permeate to an alkaline treatment step.
In an embodiment the method comprises the steps of providing a fibrous raw-material containing cellulosic fibres and polyester fibres, and optionally colours, pigments, dyes, organics and/or inorganics. In a preferred embodiment the fibrous raw-material contains at least 0.1% by weight, in particular at least 1% by weight, most suitably 2-8% by weight, suitably 2-15% by weight of polyester fibres, and up to 25% of polyester fibres by weight of dry weight of the raw-material.
In an embodiment the method comprises subjecting the raw-material to acid treatment at a pH of less than 5 in an aqueous acid medium. Preferably, the method comprises carrying out the acid treatment in an aqueous inorganic or organic acid, in particular in aqueous mineral acid, such as sulphuric acid, in particular at a temperature in the range of 50 to 100° C., preferably 60 to 95° C., suitably >70° C., preferably at temperature below 100° C., suitably at atmospheric pressure to obtain a first modified raw-material. In a typical embodiment the aqueous acid medium comprises 3-6 g acid per litre of water. After the acid treatment, the first modified raw material preferably has a consistency of 6-15%. Suitably, the acid treatment hydrolyses cellulose, reduces its molecular weight and polydispersity, and dissolves at least a portion of, preferably the majority of acid soluble metals and acid soluble nitrogen, phosphorus and chlorine containing compounds and acidic water soluble organics e.g. textile finishes present in the fibrous raw material. For the purposes of embodiments the majority of acid soluble metals typically amounts to <0.3% by weight of dry weight of the raw material. For the purposes of embodiments the majority of acid soluble nitrogen, phosphorus and chlorine containing compounds typically amounts to <0.05% by weight of dry weight of the raw material. For the purpose of embodiments the majority of acidic water soluble organics typically amounts to <1.0% by weight of dry weight of the raw material.
In an embodiment the first modified raw-material is subjected to a washing operation carried out with water. Preferably the method comprises carrying out the washing operation such that the first modified raw-material has a residual acid content of less than 5% by weight of dry weight pulp, in particular less than 1% by weight of dry weight pulp, for example less than 0.5% by weight of dry weight pulp, typically the washing step is carried out to minimise carrying acid (and optional dissolved cellulose derived impurities as total dissolved organic carbon (TOC) less than 1.5% by weight of dry weight pulp, non-cellulose derived dissolved organics less than 0.5% by weight of dry weight pulp and inorganics less than 0.2% by weight of dry weight pulp) over into a subsequent step. In an embodiment carry-over of inorganics and organic carbon is also reduced in the washing operation, further improving the performance of alkali recycling process. After washing, the first modified raw-material is preferably dewatered, suitably to a consistency of 30-60%. After acidic treatment the pulp dry weight is the dry weight of cellulose and polyester (PES). Residues of non-cellulose or non-polyester fibres can be present.
In an embodiment, after the washing operation the method further comprises subjecting the washed first modified fibrous raw-material to an alkaline treatment at a pH of more than 7 in an alkaline cooking liquor, preferably at a temperature in the range of 50 to 200° C., preferably 95 to 140° C., typically 100 to 120° C., suitably 110° C., suitably for a period of 30 minutes to 240 minutes, typically 60 minutes to 180 minutes, preferably 60 minutes to 120 minutes, typically at a pressure in the range of 0.1 to 3 bar (g) to dissolve at least a portion of the polyester fibres and to form a second modified fibrous raw-material, particularly in a consistency of 6-15%. In a preferred embodiment the method comprises carrying out the alkaline treatment in an aqueous alkaline medium with at least one alkaline agent selected from inorganic and organic bases, such as amines, alkali metal hydroxides, alkali metal carbonates, alkali metal sulphides, ammonium sulphide, alkaline earth metal hydroxides, alkaline earth metal carbonates, alkaline earth metal sulphides and a mixture thereof, said alkaline agent being present in an amount which gives an alkalinity corresponding to at least 20 g/l, for example 25 to 100 g/l of NaOH, suitably 60 to 90 g/l NaOH and said alkaline treatment in particular being carried out at a temperature of 100 to 150° C. In one embodiment the method comprises carrying out the alkaline treatment using at least partially white liquor of a pulping process.
According to an embodiment the method further comprises subjecting the second modified fibrous raw-material to separation to separate solid matter from an aqueous liquid phase comprising dissolved material, undissolved microparticulates and residual fibres. In a preferred embodiment the method comprises subjecting the second modified fibrous raw-material to separation to separate solid matter from an aqueous phase in a filter, such as a filter press, screw press or drum filter, or centrifuge.
In an embodiment the method further comprises recovering the solid matter of the separation. In a preferred embodiment the method comprises subjecting the recovered second modified raw-material to a washing operation carried out with water or an aqueous liquid, particularly at a temperature of up to 100° C. Suitably the washing takes place in displacement washing and pressing equipment.
In a further embodiment the method comprises subjecting the liquid phase to
a first membrane filtration step, particularly to filter solid particles, using a micromembrane, suitably one or more membranes, to obtain a first reject fraction and a first aqueous permeate. In an embodiment prior to the first membrane filtration step, preferably a part, particularly the majority of fibrous material remaining in the liquid phase from the solid matter separation step is removed from the liquid in an optional screening stage. In a typical embodiment, the first membrane filtration step takes place at a temperature in the range of 10-99° C., for example 10-90° C., suitably at a temperature in the range of 50-95° C. or 35-60° C. The higher the temperature is during the filtration step, the higher is the viscosity, which results in better flux values. Permeate obtained from filtering is a high-energy fraction from which heat can be recovered. The micromembrane is typically comprised of membrane unit having a suitable pore size to remove of major part of undissolved microparticulates focusing to protect the subsequent nanomembrane unit. The filter type is preferable of a cross flow tubular type or a dynamic crossflow filter or a combination thereof. Other possible types include capillary and spiral types of filters. The filter materials can be polymeric membranes, ceramic or steel with ceramic coating. In a preferred embodiment the first membrane filtration step, typically a microfiltration step, is carried out using a membrane, suitably one or more membranes, having an average pore size (pore diameter) of 0.025 to 10 μm or a molecular weight cut-off of 50 to 500 kDa. The pressure used in the microfiltration step is preferably in the range of 2-6 barg, typically in the range of 3-5 barg. The flux is typically in the range 10-400 dm3/m2·h, more typically in the range of 100-350 dm3/m2·h. According to one embodiment, weight reduction in the microfiltration step is 80-99%, typically 90-97%. Microfiltration is preferably performed at an elevated temperature of about 50-95° C. The first reject fraction typically contains undissolved particles with a mean size higher than the resolution of the micro filtration membrane (>0.025-10 μm), for example the first reject fraction may contain residual undissolved cellulose and cellulose derived particles, residual undissolved non-cellulosic particles present in feedstock, colour pigments and their agglomerates, alkaline earth metal hydroxide, alkaline earth metal carbonate, alkaline earth metal sulphide alkaline earth metal phosphate alkaline earth metal silicate precipitates and suitably transition metal hydroxide, transition metal carbonate, transition metal sulphide, transition metal phosphate, transition metal silicate precipitates, and mixtures thereof. The first aqueous permeate typically contains dissolved organic molecules or their undissolved microparticulates, e.g. colour pigments, terephthalate in the form of a sodium salt, alcohols such as ethylene glycol, resins, waxes, carboxylic and hydroxy acids and free fatty acids in the form of their sodium salts, and inorganic ions, such as small amounts of two and/or three valent cations mainly in the form of dissolved hydroxides, carbonates, sulphides, phosphates or silicates, or anions such as sulphates, chlorides, silicates, carbonates, phosphates dissolved and/or in the form of microparticulates and undissolved micro or nanoparticles such as cellulose or cellulose derived microparticulates or non-cellulosic microparticulates with mean size smaller than the resolution of the microfiltration membrane (<0.025-10 μm). In an embodiment the first reject fraction, typically comprising the above described composition is directed to effluent recovery and treatment, preferably to be utilized in a Kraft pulp mill integrated chemical recovery process or alternatively is directed to a chemical and or a biological wastewater treatment process.
In an embodiment, the method comprises subjecting the first permeate to a second membrane filtration step, particularly to filter dissolved molecules, using a nanomembrane, suitably one or more membranes, to obtain a second reject fraction and a second permeate. Preferably, the second membrane filtration step takes place at a temperature in the range of 10-70° C., suitably at a temperature in the range of 35-60° C., especially in the range of 50-60° C. The nanomembrane is typically comprised of a membrane unit having a suitable molecular weight cut-off to remove the remaining undissolved microparticulates and at least a portion of, preferably the majority of dissolved impurities focusing to chemically purify the second permeate for recycling back to an alkaline treatment e.g. of the first modified raw material. The type of nanomembrane is preferable a spiral type membrane made of alkali stable materials. In a typical embodiment the second membrane filtration step is carried out using a membrane, suitably one or more membranes, having an average molecular weight cut-off of 50 to 1000 Da, preferably 50-500 Da, suitably 50-300 Da. The pressure used in the nanofiltration step is preferably in the range of 10-60 barg, typically in the range of 15-35 barg. The flux is typically in the range 2-90 dm3/m2·h, more typically in the range of 4-35 dm3/m2·h. According to one embodiment, weight reduction in the nanofiltration step is 40-85%, typically 60-80%. The second permeate typically contains the same composition of impurities as the first permeate but in reduced concentration. The main purpose of nanofiltration is to reduce the amounts of colour pigments alkali extracted from a mixed colour raw material feedstock (colour reduction) and to reduce the amount of polyester derived hydrolysis product (terephthalate reduction) and cellulose derived organic compounds (organic carbon reduction, TOC reduction), simultaneously reducing the amount of dissolved inorganics such as silicates, whereby the yield of recyclable active alkali species, such as sodium hydroxide, is maximised. The total recovery rate of the active alkali species, sodium hydroxide, is preferably at least 80%. In an embodiment the second reject fraction, typically comprising terephthalate, colour pigments and their agglomerates and other cellulose derived or polyester derived hydrolysis products such as polyethylene terephthalate derived, or non-cellulose or non-polyester derived impurities or inorganics such as sodium silicate, is directed to effluent recovery and treatment preferably to be utilized in a Kraft pulp mill integrated chemical recovery process or alternatively directed to a chemical and or a biological wastewater treatment process, optionally terephthalate and selected organics such as organic acids can be separated and commercially utilized).
In an embodiment the method comprises recovering the second aqueous permeate. In a preferred embodiment the second aqueous permeate is recovered and concentrated by removing of excess of water to adjust the suitable level of active alkali concentration, e.g. sodium hydroxide concentration, for internal recycling. In one embodiment the method comprises the step of recycling the second aqueous permeate having a suitable concentration of active alkali, such as sodium hydroxide, to an alkaline treatment step.
In a further embodiment, the method comprises subjecting at least one, preferably one or more of the following aqueous streams to wet air oxidation:
In an embodiment the method comprises recycling, optionally after wet air oxidation, in addition to the second aqueous permeate at least one, preferably one or more, of the following aqueous streams to an alkaline treatment step:
By carrying out the wet-oxidation, preferably for the first aqueous permeate prior to nanomembrane it increases the capacity of the nanomembrane as purification pre-treatment.
In a particular embodiment the method comprises recycling the second aqueous permeate to the alkaline treatment step of the first modified fibrous raw-material Colour reduction and organic carbon reduction enable the recycling of recovered alkali. Without the reduction in colour pigments and organic carbon said contaminants accumulated in the process resulting in a higher carry-over from one process stage to subsequent stages. Contaminants may precipitate or otherwise disturb a particular process stage e.g. too much colour pigment or organic load carry-over into bleaching stage either increases consumption of active bleaching chemicals or reduces the whiteness of the bleached product. The second aqueous permeate typically comprises a purified active alkali species, such as sodium hydroxide, with the reduced amount of dissolved organic molecules or their undissolved microparticulates, e.g. colour pigments, terephthalate in the form of a sodium salt, alcohols such as ethylene glycol, carboxylic and hydroxy acids in the form of their sodium salts, and inorganic ions, such as small amounts of two and/or three valent cations mainly in the form of dissolved hydroxides, carbonates, sulphides, phosphates or silicates, or anions such as sulphates, chlorides, silicates, carbonates, phosphates dissolved and/or in the form of microparticulates and undissolved micro or nanoparticles such as cellulose or cellulose derived microparticulates or non-cellulosic microparticulates with mean size smaller than the resolution of the nanofiltration membrane (50-1000 Da).
In a further embodiment, the method comprises concentrating, in particular by evaporation, one or more aqueous streams selected from the washing water of the washing operation, the aqueous filtrate of the filtration step, the first aqueous permeate of the first membrane filtration step and the second aqueous permeate of the second membrane filtration step, to an effective alkalinity corresponding to at least 20 g/l, for example 25 to 100 g/l of NaOH, suitably 60 to 90 g/l NaOH content before recycling of said stream to the alkaline treatment step. In an embodiment one or more of the aqueous streams are recovered, mixed together and concentrated by evaporation to remove excess water.
In an embodiment the method comprises subjecting at least a part of the second reject fraction to diafiltering in the second nanomembrane filtration step, said diafiltering for example being carried out using water or an aqueous stream of a process step, such as an effluent, filtrate or supernatant. Diafiltering is typically carried out in order to maximise the recovery of alkali from the second reject fraction.
In one embodiment the method comprises recovering at least one, preferably both of, the first and the second reject fraction(s), containing at least one of terephthalate, colour pigments, and other organic carbon, and optionally subjecting it to further treatment, for example using biological purification or wet air oxidation or in a pulp mill integrate. Further treatment of one or more fractions containing terephthalate In an embodiment the first and/or second reject fractions is/are directed to effluent recovery and treatment preferably to be utilized in a Kraft pulp mill integrated chemical recovery process or alternatively directed to a chemical and/or biological wastewater treatment process.
In a particular embodiment the method comprises providing a fibrous raw-material containing a mixed-colour textiles. In a preferred embodiment, the method comprises recovering the solid matter of the separation to bleaching, for example to bleaching carried out with an oxidizing agent or a combination of oxidizing agents, for example selected from the group of ozone, peroxide and peroxo compounds, or a reducing agent, such as sodium dithionite, or a combination thereof. The bleaching is particularly preferred to remove colour in embodiments in which the fibrous-raw material contains mixed-colour textiles.
In an embodiment the method comprises subjecting the solid matter of the separation to dissolution, preferably the method comprises subjecting the solid matter of the separation to dissolution using a cellulose solvent and/or in the presence of a derivatizing agent. Suitable cellulose solvents include NMMO (N-Methylmorpholine N-oxide) used in traditional Lyocell process or ionic liquid based cellulose solvents suitable for use in processes producing Lyocell type fibres or modified Lyocell type fibres; metal ammine complexes e.g. copper ammine complex used in Cupro process or Schweitzer's Reagent, iron tartrate complex, or Zincoxen reagent ((tri (ethylenediamine) zinc hydroxide solution); sodium hydroxide or sodium zincate. Each of the mentioned solvents may be used either with or without organic surface active agents and/or urea and/or thiourea. Suitable derivatizing agents include e.g. carbon disulphide in viscose or modal processes or urea in the cellulose carbamate process.
In a further embodiment the method comprises using the solid matter of the separation as a starting material in the preparation of cellulose carbamate dope. In one embodiment the solid matter of the separation contains less than 1% by weight, in particular less than 0.5% by weight of terephthalate. In an embodiment, a part of the terephthalate may be present in the form of its polymers, e.g. in the polymeric form of the corresponding polyester, e.g. due to channeling of cooking liquor in a digester of due to incomplete contact between the feedstock and cooking reagents. Typically solid matter containing less than 0.5% by weight of terephthalate is suitable as a starting material in the preparation of cellulose carbamate polymer and subsequent preparation of cellulose carbamate dope and cellulose carbamate spinning dope from the cellulose carbamate polymer. In an embodiment the evaporated liquor originating from aqueous liquid phase of the separation step recycled back to the alkaline treatment exhibits a colour reduction of at least 90%, preferably at least 95%, of the absorbance at 430 nm. The lower is the colour pigment content in the spin bath circulation, the smaller is the amount of the carry-over carried by the mass into following washing steps and further to following bleaching. Thus, low content of colour pigments, for example, decreases consumption of bleaching chemicals. Some colour pigments may be soluble into the spin bath at high temperatures, wherein those can not be necessary removed with water while the lye content decreases.
In an embodiment, the concentrated liquor provided by concentrating, in particular by evaporating one or more aqueous streams selected from the washing water of the washing operation, the aqueous filtrate of the filtration step, the first aqueous permeate of the first membrane filtration step and the second aqueous permeate of the second membrane filtration step before recycling of said stream to the alkaline treatment step exhibits a reduction of total organic carbon based on the colour pigments and cellulosic degradation products of 90% by weight. Thus, in an embodiment the evaporated liquor exhibits a reduction of total organic carbon based on the colour pigments and cellulosic and polyester degradation products of at least 60% by weight, suitably at least 65% by weight, preferably about 70% by weight.
Further embodiments relate to solid material obtainable by a method of above-described embodiments. In one embodiment solid matter obtainable by the method comprises less than 1% terephthalate and its polymers by dry weight of the raw material, in particular less than 0.5% terephthalate and its polymers by dry weight of the material and at least 95% cellulosic fibers by dry weight of the raw material. In a further embodiment the cellulosic fibers are preferably cotton fibers. In a particular embodiment the cellulosic fibers have a final viscosity after both the acid step and the alkaline step in range of 200 to 500 ml/g, preferably 250 to 500 ml/g, suitably 250 to 450 ml/g, particularly 300 to 350 ml/g (based on the CED viscosity measurement according to the ISO 5351, modified).
The following non-limiting example illustrates at least some embodiments of the invention:
Recycled mixed colour sorted cotton textile waste with CED viscosity of 750 ml/g (modified ISO 5351) containing 8.8% of non-cellulosic fibres (mainly polyester and traces of nylon) were mechanically shredded to disintegrate the fabric structure into the form of pieces having fibres of an average size of 6 mm. The shredded material (batch size of 295 kg of air dry shredded textile waste) was acid pre-treated in a digester with a medium consistency loop designed for processing of medium consistency wood fibre based pulp. The main part of the loop consisted of a standpipe and a related medium consistency pump. In the first acidic stage, the shredded material was treated with sulphuric acid at 95 degrees Celsius for 70 min; a liquid to solid ratio of 10 to 1 was applied, the initial acid charge was 5.0 g/l, and the final acid concentration in the end of cooking was 4.3 g/l. The pH value of the final washing liquid was 3.2 measured in wash filtrate corresponding to 0.6 g of free sulphuric acid per kilogram of dry acid treated material. The medium consistency pulp slurry in the acidic cooking liquor was circulated through a chemical mixer and returned to the top of the feed pipe. The flow in the loop was controlled by adjusting the speed of the pump and by bypassing the loop by directing part of the flow back to the lower part of the standpipe. The bypass was adjusted with a control valve suitable for fibre suspension. The viscosity of the acid treated material was 315 ml/g (based on the CED viscosity measurement according to the ISO 5351, modified). The average yield through acid stage was 89% solids on oven-dried material in.
In a second, alkaline stage the washed, acid treated fibrous raw-material was chemically treated in a pressure reactor equipped with a medium consistency pump with sodium hydroxide at 110° C. for 120 min, liquid to solid ratio of 13 to 1 was applied, initial alkali charge was 71.7 g/l, final alkali concentration at the end of cooking was 63.7 g/l. The average yield through alkaline stage was 86% solids on oven dried material in.
The alkali treated fibrous raw-material was subjected to separation to separate solid matter from an aqueous liquid phase comprising dissolved material and undissolved particles. The recovered raw-material was further subjected to a washing operation carried out with water. The separated solid matter was dewatered to a dry matter content of 55% by weight using a screw press. The separated and recovered aqueous liquid phase had the following composition: pH value of 13.4, conductivity of 250 mS/cm, total concentration of solids substances of 740 mg/l (by gravimetry using a membrane with a porosity of 1 μm), turbidity of 210 NTU, absorbance of 8.8 (colour determined as absorbance of solution at the wavelength of 430 nm measured by VIS spectrophotometer), TOC of 15000 mg/l, total effective alkali as sodium hydroxide of 63.7 g/l (based on acid-base titration with hydrochloric acid and potentiometric detection of the end-point), formic acid concentration of 2.4 g/l, lactic acid concentration of 1.0 g/l, 3,4-Dideoxypentonic acid concentration of 1.3 g/l, terephthalic acid concentration of 4.5 g/l, β-(gluco)isosaccharinic acid concentration of 7.6 g/l, α-(gluco)isosaccharinic acid concentration of 2.8 g/l, calcium (Ca) concentration of 53 ppm, magnesium (Mg) concentration of <20 ppm iron (Fe) concentration of <30 ppm, phosphorus (P) concentration of <20 ppm, copper (Cu) concentration <2 ppm, silicon (Si) concentration of <50 ppm, aluminium (Al) concentration of <100 ppm and manganese (Mn) concentration of <5 mg.
The recovered aqueous liquid phase with the above mentioned composition was directed to the first filtration with micromembrane. Optifilter CR-250 served as apparatus for the micromembrane. Optifilter CR-250 had two flat sheet membranes with a rotor between membranes to enhance cross flow velocity on the surface of the membranes. Membrane with a pore size of 0.05 μm and total filtration area of 0.09 m2 was used. The permeate of Optifilter CR-250 was directed to the second filtration process with a nanomembrane. The filtration pressure used in Optifilter CR-250 was 2 bar with target flux of 200 LMH (litre per m2 per hour). Filtration temperature was 52-60 degrees Celsius and feed volume was 50 L. Filtration was carried out up to as high WR (weight reduction %) as possible. Average flux at pressure 2 bar up to WR 84% was 230 LMH. The permeate passed through the micromembrane had the following composition: pH value of 13.4, conductivity of 240 mS/cm, absorbance of 6.4 (colour determined as absorbance of solution at the wavelength of 430 nm measured by VIS spectrophotometer), TOC of 13760mg/l, total effective alkali as sodium hydroxide of 63.0 g/l (based on acid-base titration with hydrochloric acid and potentiometric detection of the end-point), formic acid concentration of 2.4 g/l, lactic acid concentration of 1.0 g/l, 3,4-Dideoxypentonic acid concentration of 1.3 g/l, terephthalic acid concentration of 4.5 g/l, β-(gluco)isosaccharinic acid concentration of 7.6 g/l, α-(gluco)isosaccharinic acid concentration of 2.8 g/l, calcium (Ca) concentration of <50 ppm, magnesium (Mg) concentration of <20 ppm iron (Fe) concentration of <30 ppm, phosphorus (P) concentration of <20 ppm, copper (Cu) concentration <2 ppm, silicon (Si) concentration of <50 ppm, aluminium (Al) concentration of <100 ppm and manganese (Mn) concentration of <5 mg.
The recovered aqueous liquid permeate obtained from microfiltration by micromembrane with the above mentioned composition was directed to the second filtration with the nanomembrane. The nanofiltration was performed with a SEPA filtration module equipped with a flow circulation measurement unit and a spiral wound membrane having a molecular cut-off of 100 Da and 1.6 m2 membrane area was selected. Average flux at WR 50%, WR 60%, WR 70% and WR 80% was ˜14 LMH, ˜13 LMH, ˜11 LMH and ˜7 LMH respectively. Filtration pressure was 20 bar with target flux of 15 LMH (litre per m2 per hour). Filtration temperature was 50 degrees Celsius. The permeate passed through the nanomembrane at WR 70% had the following composition: pH value of 13.6, conductivity of 260 mS/cm, absorbance of 0.37 (colour determined as absorbance of solution at the wavelength of 430 nm measured by VIS spectrophotometer), TOC of 3450 mg/l, total effective alkali as sodium hydroxide of 58.6 g/l (based on acid-base titration with hydrochloric acid and potentiometric detection of the end-point), formic acid concentration of 2.7 g/l, lactic acid concentration of 1.3 g/l, 3,4-Dideoxypentonic acid concentration of 0.9 g/l, terephthalic acid concentration of 0.6 g/l, β-(gluco)isosaccharinic acid concentration of 2.1 g/l, α-(gluco)isosaccharinic acid concentration of 0.8 g/l, calcium (Ca) concentration of <50 ppm, magnesium (Mg) concentration of <20 ppm iron (Fe) concentration of <30 ppm, phosphorus (P) concentration of <20 ppm, copper (Cu) concentration <2 ppm, silicon (Si) concentration of <50 ppm, aluminium (Al) concentration of <100 ppm and manganese (Mn) concentration of <5 mg. Permeate obtained through the filtration with micromembrane at the first stage and nanomembrane at the second stage at WR 70% had the calculated TOC reduction of 77% and colour reduction of >95%.
It is to be understood that the embodiments of the invention disclosed are not limited to the particular structures, process steps, or materials disclosed herein, but are extended to equivalents thereof as would be recognized by those ordinarily skilled in the relevant arts. It should also be understood that terminology employed herein is used for the purpose of describing particular embodiments only and is not intended to be limiting.
Reference throughout this specification to one embodiment or an embodiment means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment of the present invention. Thus, appearances of the phrases “in one embodiment” or “in an embodiment” in various places throughout this specification are not necessarily all referring to the same embodiment. Where reference is made to a numerical value using a term such as, for example, about or substantially, the exact numerical value is also disclosed.
As used herein, a plurality of items, structural elements, compositional elements, and/or materials may be presented in a common list for convenience. However, these lists should be construed as though each member of the list is individually identified as a separate and unique member. Thus, no individual member of such list should be construed as a de facto equivalent of any other member of the same list solely based on their presentation in a common group without indications to the contrary. In addition, various embodiments and example of the present invention may be referred to herein along with alternatives for the various components thereof. It is understood that such embodiments, examples, and alternatives are not to be construed as de facto equivalents of one another, but are to be considered as separate and autonomous representations of the present invention.
Furthermore, the described features, structures, or characteristics may be combined in any suitable manner in one or more embodiments. In the following description, numerous specific details are provided, such as examples of lengths, widths, shapes, etc., to provide a thorough understanding of embodiments of the invention. One skilled in the relevant art will recognize, however, that the invention can be practiced without one or more of the specific details, or with other methods, components, materials, etc. In other instances, well-known structures, materials, or operations are not shown or described in detail to avoid obscuring aspects of the invention.
While the forgoing examples are illustrative of the principles of the present invention in one or more particular applications, it will be apparent to those of ordinary skill in the art that numerous modifications in form, usage and details of implementation can be made without the exercise of inventive faculty, and without departing from the principles and concepts of the invention. Accordingly, it is not intended that the invention be limited, except as by the claims set forth below.
The verbs “to comprise” and “to include” are used in this document as open limitations that neither exclude nor require the existence of also un-recited features. The features recited in depending claims are mutually freely combinable unless otherwise explicitly stated. Furthermore, it is to be understood that the use of “a” or “an”, that is, a singular form, throughout this document does not exclude a plurality.
At least some embodiments of the present invention find industrial application in recycling fibrous materials, particularly in the recycling of garments and textiles in which new fibres from cellulose carbamate dopes after the mechanical and chemical treatment of raw fibrous materials comprising cellulosic and polyester fibres.
| Number | Date | Country | Kind |
|---|---|---|---|
| 20215949 | Sep 2021 | FI | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/FI2022/050588 | 9/6/2022 | WO |