The disclosure relates to a method for butt-welding of workpieces, especially tailored welded blanks used in the manufacture of bodywork in the car industry.
At least two flat workpieces are positioned in relation to one another and secured there in a first sub-process in such a way that a minimal gap is formed between the two edges to be welded together. In another sub-process, the position and the width of the gap are measured continuously directly before welding together. These measurements are then used to control a laser welding device, where at least the welding rod feed and the processing lens are controlled on the basis of the measurements.
Tailored Blanks (TB) or also Tailor Welded Blanks (TWB) were developed in order to manufacture sheet-metal blanks that were broader than those that could be produced using the rolling technology available at the time. Nowadays, manufacturers mainly make use of the advantage that blanks can be made up of different material grades or sheet thicknesses, also with less scrap. This makes it possible to adapt various parts of the subsequent workpiece to the loads occurring locally in the future, which would otherwise require additional reinforcing parts. The advantages are savings in weight and manufacturing costs. TWBS are used widely in the car industry for the manufacture of car bodies, where welded parts are made from single metal sheets—after preparation of the sheet edges if necessary. There are two welding methods known, especially for laser welding: In a first method, metal sheets are positioned exactly, clamped in place and welded together by a movable welding head. With the other method, metal sheets coming from parallel tracks are fed to a stationary welding tool and welded together. Both methods require a high degree of mechanical precision in order to process a maximum gap width that is currently in the region of 0.3 mm.
A method and a device for performing the process is described in patent specification U.S. Pat. No. 5,328,083, which does not however disclose how the welding tool is positioned exactly in relation to the current part of the seam. Inaccuracies in the blanks and shifts in the position of the seam can lead to faulty welds.
The European patent specification EP 0450349 relates to a method for continuous welding of butted strip or sheets by means of a laser beam, without additional materials being added, where the material to be welded is cooled in the area of the weld directly behind the welding focus in strip running direction—depending on the width of the gap formed by the abutting edges. The present publication also proposes a device for continuous welding of abutting sheets or strips by means of a stationary laser beam, with straightener rolls arranged vertically to their running direction in pairs on both sides of the strips to be welded together and which form a minimal gap in the area where the strips abut and which the stationary laser beam hits when welding the abutting edges together.
In European patent specification EP 0817698 B1, a method is described for continuous butt-seam welding of metal plates, where the relative position of the metal plates and thus the precision of the seam is maintained within a specified tolerance range. This method deliberately does without mechanically precise alignment of the metal plates to be welded together; instead, the laser tool follows the path of the two abutting metal plates by means of sensor equipment to determine the gap width and position continuously. Hereafter, a control loop can be used to permanently adjust the performance of the weld beam and the required cooling performance for the welding process (gas, water). A system of this kind requires a great deal of maintenance.
In industrial manufacturing technology, laser is gaining more and more importance due to the large number of technological advantages. These advantages result primarily from the targeted application of energy to the workpiece, for a limited time and over a limited area, and the resulting high machining speed. Lightweight car body production opens up considerable potential in terms of manufacturing engineering for laser welding.
Scenarios in which the gap situation can vary from workpiece to workpiece, where A-shaped, V-shaped, parallel and zero gaps, or mixed combinations thereof occur, are challenging in laser welding. Large gap dimensions result in a loss of absorbed laser energy through the gap. It is possible to reduce this loss to a certain extent by defocusing the monofocus. However, this inevitably also reduces the maximum intensity of the laser beam. Whereas the root penetration ability, that is to say full penetration of the workpiece by means of the metal vapour capillary during laser welding, is also reduced with a technical zero-gap. This can be compensated to a certain extent either by a lower welding speed or a higher laser output. In summary, it is true to say that an area of tension forms in the application between gap bridging capability and root penetration. In order to guarantee optimum productivity, the laser beam sources are operated at the design limit of the laser output. A change in the welding speed during welding work is not possible in many plant concepts due to the reaction time. This leads generally to reduced productivity.
In the car industry nowadays, door rings are made of tailored welded blanks (TWB). Such door rings typically comprise up to eight individual parts, but a larger number is also conceivable. The sheet thickness of the individual parts can also vary here. Due to the shape and manufacturing tolerances for the individual parts, there is normally unfavourable gap formation, at least at one of the welds in the finished part, as a result of the ring being closed. Subsequently, the fact that the gap situation can differ from door ring to door ring, where different types of gap situation can occur, makes efficient production more complicated. Proficiency with V-shaped welds is the biggest challenge here.
Poor welding quality means that undesirable cracks can occur in the weld seams during door ring crash tests. Due to safety considerations, this risk is not acceptable in the production of door rings.
Currently, three methods are known for closing variable gaps of up to a maximum of 0.3 mm by adding flux-cored wire.
Several approaches have been pursued so far to solve the problem of processing wide welding gaps. For example, the idea of a scan tracker with monofocus pursues the idea that a laser beam with a small focus diameter (0.2 mm to 0.3 mm) and high intensity oscillates at right angles across the welding assignment. The amplitude and the laser output is varied depending on the gap width. However, trials with the system technology available on the market for welding blanks show that, due to the frequencies achievable, the period length of the oscillating motion does not guarantee full coverage of the remelted material at high welding speeds of approximately 10 m/minute. In order to generate acceptable weld seams, the welding speed would have to be reduced significantly, which would lead to a loss of productivity regardless of whether there is a gap or a zero-gap.
The idea of the trifocal laser with at least three monofocuses pursues the approach of adapting the intensity distribution through three fibre-coupled laser beam sources according to the gap width by means of beam forming and thus filling larger gaps without any loss of productivity. Two spots with a small diameter are used here at the front and one spot with a large diameter at the rear. The geometrical arrangement of the spots cannot be changed and is only suitable for one area of application. The change is made via the output of the individual laser sources. However, in practical use the intensity of the small spots cannot be reduced enough to ensure that they do not generate any unwanted notches in the welding material. Due to the geometrical consistency, this concept only permits very little margin for adapting on the basis of the variable gap width during the production process.
Patent specification DE 101 13 471 B4 discloses a laser hybrid welding method in which a conventional welding process is combined with a laser. Two laser focal points are generated here. According to the disclosed embodiments, the spacing between the two focal points are varied constantly based on measurement of the individual parameters of the welding process, particularly the welding speed and the welding quality.
When welding tailored blanks, it is possible to weld variable gaps of up to a maximum of 0.3 mm with filler metal using the technology currently available. It is a challenge to close variable gaps up to approximately 1 mm dynamically with additional material (filler rod) and high welding quality.
Important criteria in a process for welding tailored blanks are the throughput of the overall plant on the one hand, i.e. how many parts can be produced per hour at an acceptable reject rate, and on the other hand the effort required to ensure both the quality of the overall machining process as well as the desired quality of the welded blanks.
A disadvantage in the aforementioned solutions and processes are the considerable technical effort for cooling the weld seam, for clamping the plates in a safe way for the process, for discharging the welding fumes and spatters from the plant, as well as the capacity and thus also the productivity of the overall plant. In general, either the welding lens is designed to be movable and the blanks to be welded are stationary in such plants, or the welding material is fed in continuously and the welding lens is stationary during the welding process. A subsequent disadvantage is the substantial effort required to load and unload the conveyor belts.
The inventive embodiments disclosed herein are based on the task of describing a method by which the above mentioned disadvantages are eliminated.
In one embodiment, a laser welding device is designed as a laser with rotatable twin-spot lens, comprising one main and one auxiliary spot. The relative alignment of the main spot and the auxiliary spot to one another is controlled during the welding process depending on the absolute position of the gap and the gap width by rotating the processing lens of the laser welding device around the axis of the laser beam at the angle of rotation alpha.
With this structure, the position of the laser spots can be changed in relation to the welding gap and adapted to different gap widths simply by rotating the processing lens.
Surprisingly it was noted that the system is particularly effective as from gap widths larger than 0.2 mm and that it is not absolutely necessary to rotate the processing lens at gap widths smaller than 0.2 mm. Hence, it is an advantage if the relative alignment of the main spot and the auxiliary spot is controlled as from a measured gap width of more than 0.2 mm.
At gap widths of less than 0.2 mm, the main spot can then be at the front when viewed in welding direction and the auxiliary spot behind it, where the connecting line between the centres of the two spots runs in parallel to the welding direction. This is equal to an angle of rotation alpha of 0 degrees.
It is also an advantage if not only the gap width and the gap position, but also the shape of the gap edges are determined or measured and the relative alignment of the main spot and the auxiliary spot to each other is controlled during the welding process, also depending on the shape of the edges. Different edge or gap shapes are shown in
It has been noted that additional offset (Y-offset) of the laser spots in a direction perpendicular to the transport direction of the workpieces can have a positive effect on the welding result, depending on the shape of the edges (rounded, sharp, with burr). This means it was also established that the central point between the main spot and the auxiliary spot must not always be in the centre of the gap in order to achieve optimum welding results. Cases in which this central point has a certain amount of offset to the centre of the gap are also conceivable. Thus, it is an advantage if the process lens is also moved in a direction perpendicular to the transport direction of the workpieces so that the central point between the two spots is offset in relation to the centre of the gap.
It is preferable if the spacing between the two spots remains constant.
For example, the auxiliary spot can be rotated around the main spot at the back when viewed in welding direction.
However, it is also conceivable that the axis of rotation around which the two laser spots are rotated as a single unit lies between the main spot and the auxiliary spot and on the rear spot, respectively.
It is favourable if the processing lens is movable in relation to the workpieces to be welded together, preferably in a direction perpendicular to the transport direction of the workpieces (on the plane of the workpiece). The relative speed between the workpieces to be joined together and the processing lens is equal to the welding speed (vMatFlow).
The welding speed (vMatFlow) can be constant during the welding process, but can also be controlled depending on the gap width, the plate thickness or the plate edge quality.
The same applies to the laser output during the welding process.
The laser output can also be controlled depending on the position of the twin-spot lens.
This disclosed method enables efficient and reliable industrial manufacture of tailored welded blank (TWB) parts, especially door rings for the car industry. Here, the blanks are secured on a conveyor belt from below using magnetic forces so that the machine is guaranteed to be accessible from above. Workpieces can be reliably joined in a TWB arrangement without losses in productivity and results in an enlarged process window in terms of gap width and edge quality of the input material compared to the state of the art. In particular, the solution proposed also makes it possible to master the large challenges in closing V-shaped gap situations reliably. Due to enlargement of the process window, the overall reject rate is reduced, thus significantly increasing productivity overall. In addition, the welding quality can be improved.
As the blanks can be secured reliably for the process over a longer transport distance, a movable or “flying” lens can also be used, as described in European Patent Specification EP 3038789 A1, which means that the capacity of the machine in comparison with other machines using conventional concepts can be increased by up to 20%. Hereafter, the magnetic retaining principle has a positive effect on maintaining the smallest possible gap between the blanks to be welded together, meaning that a better quality of weld seam can be achieved.
The present invention is further explained in the following on the basis of example embodiments and referring to drawings. In the drawings,
In a cross-sectional view,
In a first sectional view A-A according to
In a second sectional view A′-A′ according to
In a third sectional view A′-A′ according to
These descriptions are merely illustrative examples of the types of adaptations in the positioning of the main spot 8 and auxiliary spot 9 that are possible to accommodate the virtually countless sizes, shapes and configurations of gaps between adjacent workpieces.
Within the graphical representations shown in the drawings, reference numerals represent elements of the inventive embodiments, as follows:
Number | Date | Country | Kind |
---|---|---|---|
18173891 | May 2018 | EP | regional |
Number | Name | Date | Kind |
---|---|---|---|
4824007 | Depaoli | Apr 1989 | A |
5023427 | Neiheisel | Jun 1991 | A |
5204505 | Prange et al. | Apr 1993 | A |
5328083 | Peru | Jul 1994 | A |
5814786 | Johnson | Sep 1998 | A |
6034347 | Alber | Mar 2000 | A |
6339207 | Bishop | Jan 2002 | B1 |
10052707 | Henry et al. | Aug 2018 | B2 |
20060261045 | Wang et al. | Nov 2006 | A1 |
20160184929 | Staubli | Jun 2016 | A1 |
20200156185 | Vila I Ferrer et al. | May 2020 | A1 |
Number | Date | Country |
---|---|---|
10113471 | Oct 2002 | DE |
0823304 | Feb 1998 | EP |
2947612 | Sep 1999 | JP |
2004298964 | Oct 2004 | JP |
2016078075 | May 2016 | JP |
0000320 | Jan 2000 | WO |
Number | Date | Country | |
---|---|---|---|
20190358735 A1 | Nov 2019 | US |