Patent Application
20090003124
The present invention relates to a method of adding a low-pressure gas which serves as a reaction auxiliary continuously to a supercritical fluid, and to an apparatus therefor. The method and apparatus are usable, for example, in a process of dissolving a reaction auxiliary and a metal precursor into a supercritical fluid or a subcritical fluid and forming a thin film on a substrate.
In recent years, a technology to synthesize substances without using substances having much effects on environment such as organic solvents is required. When a gas such as CO2 is maintained at a point higher than a critical point, it is converted into a supercritical state in which there is no boundary between gas and liquid. A substance in the supercritical state is a fluid which is neither liquid nor gas, and is referred to as a supercritical fluid.
Downsizing of integrated circuits is in steady progress. In the related art, a super-micro-fabrication process such as manufacture of the integrated circuits is generally performed with a dry process (vacuum process) in vacuo, a rarefied gas environment, or a plasma discharge environment.
The dry process has been developed as an extremely effective measure because independent atomic elements or molecules, or ions thereof can be used directly for processing. However, in the vacuum process, maintenance of vacuum and generation of plasma increase the cost. In a wet process in which a liquid is used for plating or cleaning, a large quantity of waste liquid is generated, which presents a serious environmental problem.
The supercritical fluid using CO2 as a medium has a property between liquid and gas, and has peculiar properties such that surface tension is zero and the capability to dissolve other substances (solvation capability) is high. In addition, it also has advantages such as chemical stability, inexpensiveness, harmless, and low cost. In addition, there are many characteristics such that recycling of CO2 in itself and substances dissolved in CO2 fluid by vaporization and reliquefaction.
In an integrated circuit manufacturing process, study and development of using the supercritical CO2 are in progress mainly in a wafer cleaning process. For example, in a cleaning process, a process aiming at the salvation energy, the safety and recycling capability of the supercritical CO2 has been developed. The study and development of a micro-fabrication process for forming a nano-level wiring are also in progress taking advantage of the fact that the surface tension is zero in the supercritical CO2.
For example, a main function in manufacture of semiconductor devices is the formation of a thin film, and Rapid Expansion of Supercritical Solution is known as a method of forming a thin film using a supercritical fluid. D. Matson et al disclose a technology of expanding a supercritical fluid containing a source material dissolved therein and forming a supersaturated raw material. A further developed technology is a method of obtaining a thin film of a metal oxide by dissolving an oxide complex in a supercritical fluid and blowing the same onto a heated substrate (see Patent Document 1: JP 2003-213425 A)
The inventors have uniquely developed a method of forming a thin film by dissolving a thin film forming raw material such as an organic metal in a supercritical CO2 and allowing it to undergo a film forming reaction in that state (E. Kondoh and H. Kato, Microelectron. Eng. Vol. 64 (2002), pp. 495), and applies the method to the manufacture of integrated circuit wirings such as filling Cu into via holes or trenches, and the formation of a Cu diffusion barrier layer (Japanese Patent Application No. 2003-17948, “Method of manufacturing semiconductor devices”, and Japanese Patent Application No. 2003-17949 “Method of manufacturing semiconductor devices”) The similar method is disclosed also in JP 2003-514115 T.
In the processing in a supercritical fluid, addition of a gas as a source material is frequently performed. For example, when decomposing a harmful organic substance such as dioxin using oxidative reaction in a supercritical water instead of burning, an oxidizing gas such as oxygen or air as an oxidizer is used in addition to the supercritical water. It is pointed out that addition of the gas to a supercritical CO2 is necessary when performing coating of fine particles efficiently by the Rapid Expansion of Supercritical Solution (see Patent Document 1: JP 11-197494 A).
When depositing a thin film using a reaction in a supercritical fluid, addition of a gas is further important. For example, the inventors have developed a technology of dissolving Cu (hfac)2, a metal complex, in a supercritical fluid, adding H2 thereto to produce a reduction reaction to obtain a Cu thin film, and proved that when H2 is not added, only the particles are produced, and a thin film is not formed (Report introduced above). In order to deposit a thin film, it is necessary that a heterogeneous reaction occurs continuously on the substrate surface and developing surfaces. In order to cause the reaction to occur on the substrate surface by priority, the substrate surface is required to act catalytically. In the case of precipitation of Cu, the substrate metal aids dissociation of H2.
The inventors developed a technology to obtain a ruthenium oxide (RuO2) thin film by dissolving bis(cyclopentadienyl)ruthenium (RuCp2) as a metal complex in a supercritical fluid and causing an oxidative reaction with ozone gas (O3) added simultaneously (Japanese Patent Application No. 2004-167782). Ozone, being unstable and dissociating on the substrate surface by priority to liberate oxygen atom, reacts easily with the metal precursor, so that the ruthenium oxide is deposited.
Patent Document 1: JP 2003-213425 A
Non-Patent Document 1: J. Mater. Sci. Soc. Vol. 22, No. 6, 1918 (1987)
Patent Document 2: JP 2003-514115 T
Patent Document 3: JP 11-197494 A
However, in order to add a gas to a high-pressure supercritical fluid, it is necessary to compress the gas to a pressure equal to or higher than the supercritical fluid. For example, in the supercritical hydroxylation reaction, air is brought into a high pressure using a compressor, and is added to a supercritical water. Compression of a gas as such requires a large scale apparatus which costs much and, in addition, it is extremely dangerous especially when a highly reactive gas or a combustible gas is added. Examples of the above-described gas includes O2, air, H2, O3 as well as N2O, NH3, H2S in JP 2003-514115 T described above for example and other almost all types of gases which are required for synthesis.
Another method of adding a gas in a reaction process using a supercritical fluid is a batch method. That is, the additive gas is encapsulated in a reaction vessel, and then a medium fluid is supplied in a gas or liquid state. Subsequently, when the temperature of the reaction vessel is raised or the pressure is raised by further supplying the medium fluid, the interior exceeds the critical point, and hence is brought into a supercritical flow state.
Although the batch method is used quite generally, the amount of composition that can be achieved in one operation is limited since all the materials are encapsulated. This causes an upper limit in film thickness in the case of deposition of a thin film. In addition, the condition of processing such as the concentrations of the materials in the reaction vessel change continuously. For example, as the synthesis proceeds, by-products of the reaction are condensed, whereby impurities caused thereby may be contained easily therein.
The problems described above may be solved by dissolving a metal complex and a low-pressure additional gas in a supercritical fluid and supplying them continuously into a reaction vessel. However, such a method has not been developed thus far.
The present invention is for dissolving a metal complex and a low-pressure additive gas in a supercritical fluid and supplying the same continuously to a reaction vessel, aiming to provide a method and an apparatus for adding a low-pressure gas to a high-pressure supercritical fluid continuously, so that a gas which should be handled with care, such as a combustible gas, can be added to a supercritical fluid without compression.
That is, the method of adding a low-pressure gas continuously to a supercritical fluid according to the present invention comprises supplying a reactant gas to a supercritical fluid or a subcritical fluid by repeating, in an alternate manner, a step of storing the reactant gas midway through a piping in a low-pressure state and a step of carrying the reaction gas toward a reaction vessel with the supercritical fluid or the subcritical fluid, so that the reactant gas is continuously charged in the reaction vessel.
In one embodiment, the method of adding a low-pressure gas continuously to a supercritical fluid according to the present invention is characterized in that the step of storing the reactant gas in a low-pressure state is performed at a temperature being maintained at a supercritical or subcritical temperature or higher.
The apparatus for adding a low-pressure gas continuously to a supercritical fluid according to the present invention comprises; a piping system for transporting a supercritical fluid or a subcritical fluid to a reaction vessel and a piping system for adding and mixing a reactant gas at an adding and mixing portion midway through the piping system, wherein the adding and mixing portion comprises a means for storing the reactant gas in a low-pressure state, a means for carrying the stored reactant gas toward the reaction vessel with the supercritical fluid or the subcritical fluid, and a switch valve for switching the respective means.
In one embodiment, the apparatus for adding a low-pressure gas continuously to a supercritical fluid according to the present invention is characterized in that the means for storing the reactant gas in a low-pressure state has a stirring means.
In another embodiment, the apparatus for adding a low-pressure gas continuously to a supercritical fluid according to the claimed invention is characterized in that the switch valve for switching the means for storing the reactant gas in a low-pressure state and the means for carrying the stored reactant gas toward the reaction vessel with the supercritical fluid or the subcritical fluid is a hexagonal valve.
In another embodiment, the apparatus for adding a low-pressure gas continuously to a supercritical fluid according to the present invention is characterized in that the switch valve integrates therein the means for storing the reaction gas in a low-pressure state.
In another embodiment, the apparatus for adding a low-pressure gas continuously to a supercritical fluid according to the present invention is characterized in that the means for storing the reactant gas in a low-pressure state integrated in the switch valve includes a loop piping, so that a fluid comprising the supercritical fluid or the subcritical fluid and the reactant gas is stirred to accelerate mixing thereof while passing through the loop piping.
In another embodiment, the apparatus for adding a low-pressure gas continuously to a supercritical fluid according to the present invention is characterized in that the means for storing the reactant gas in a low-pressure state integrated in the switch valve includes a pressure-resistant container having a stirring means, so that a fluid comprising the supercritical fluid or the subcritical fluid and the reactant gas is stirred in the pressure-resistant container to accelerate mixing.
In another embodiment, the apparatus for adding a low-pressure gas continuously to a supercritical fluid according to the present invention is characterized in that a check valve for the supercritical fluid or the subcritical fluid is provided in the piping system for adding and mixing the reactant gas.
In another embodiment, the apparatus for adding a low-pressure gas continuously to a supercritical fluid according to the present invention is characterized in that a shut-off valve for the reaction gas is provided in the piping system for adding and mixing the reactant gas.
Herein, a supercritical fluid means a state of being fluid, which is obtained by maintaining a gas such as CO2 at its critical point or higher to eliminate the boundary between gas and liquid, and is neither liquid nor gas.
A subcritical fluid is a state of a fluid immediately under the critical values.
A metal precursor is a generic designation indicating an organic metallic compound, an organic metal complex, a metal halide, and a complex halide.
Since the method of adding a low-pressure gas continuously to a supercritical fluid and the apparatus therefor according to the present invention are configured as shown above, a gas which should be treated carefully, such as flammable gas which is dangerous when being accompanied with compression or temperature increase, can be added to and mixed with a supercritical fluid or a subcritical fluid at a low pressure without compression.
Therefore, high-security is achieved and, in addition, the reactant gases can be added and mixed to a supercritical fluid or a subcritical fluid with high efficiency.
Referring now to the drawings, embodiments of the method of adding a low-pressure gas continuously to a supercritical fluid and the apparatus therefor according to the present invention will be described hereinafter.
The hexagonal valve 11 has two piping connecting states, which are referred to as State A and State B. Hydrogen is connected to a connecting port 1, and carbon dioxide is connected to a connecting port 5. A connecting port 2 is connected to an discharge line, and a connecting port 4 is connected to a reaction vessel. A stainless steel pipe of 1/16 inches in outer diameter is used for the piping of this example. Between a connecting port 3 and a connecting port 6, the piping is formed into a loop having an interior capacity of 500 μL, which is a capacity significantly larger than that of the piping in the interior of the hexagonal valve 11. The supply pressure of hydrogen is 0.3 MPa, and the supply pressure of carbon dioxide is 100 MPa. Since the entire hexagonal valve 11 and the piping are heated to 40° C., carbon dioxide is in a supercritical state (the critical point is 7.4 MPa, 31° C.).
In State A, the piping is shunted to connect between the connecting ports 1 and 6, 2 and 3, and 4 and 5, hydrogen is charged in the above-described loop piping 7 and then is discharged, while carbon oxide is supplied to a reaction vessel 8.
When the state is switched to State B after elapse of a predetermined period, the piping is shunted to connect between the connecting ports 1 and 2, 3 and 4, and 5 and 6, and hence hydrogen is directly discharged, while carbon dioxide is connected to the reaction vessel 8 via the loop piping 7. In other words, the passage of the loop piping 7 is switched from the hydrogen side to the carbon dioxide side. Hydrogen charged in the loop piping 7 is pushed into the reaction vessel 8 while being dissolved in carbon dioxide, and only carbon dioxide flows into the loop piping 7.
The above-described loop piping 7 may be of a spiral or coil shape (eddy shape)as a whole, or partly of a loop-shape (ring-shape). When a fluid including a supercritical fluid or a subcritical fluid (for example, carbon dioxide) and a reactant gas (for example, hydrogen) pas therethrough, a rotational force is applied thereto to accelerate stirring and mixing thereof is accelerated.
The stirring performance depends on the number of loops, the diameter of loop, the diameter of the pipe, and the flow velocity. Therefore, the shape of the loop or the like needs to be determined experimentally. In this example, the loop diameter is about 1 cm.
When the state is switched from State B to State A again after elapse of a predetermined period, carbon dioxide charged in the loop piping 7 is rapidly expanded. However, since there is provided a check valve 9 in the piping on the hydrogen side, the carbon dioxide is discharged without flowing in the reverse direction, and hence the inside of the loop piping 7 is replaced by hydrogen.
As a result of the operation shown above, the fluids flowing in the piping are schematically shown in
The mixture ratio between hydrogen and carbon dioxide is preferably set to a value not more than an explosion limit (lower than 4%) of hydrogen, to keep safety without a risk of explosion.
Carbon dioxide supplied from a carbon dioxide cylinder 21 is liquidized by a cooling unit 22. The carbon dioxide is supplied to a pump 23 at about 6 MPa, is compressed to 10 MPa, and is connected to a mixer 24. Hydrogen supplied from a hydrogen cylinder 25 is reduced to 0.3 MPa by a depressurizing valve 26, and is connected to the mixer 24. The piping connections of the mixer 24 (State A and State B) are switched at certain intervals by a valve controller 27.
Preferably, a flow rate adjusting valve 28 for limiting the flow rate of hydrogen is provided between the above-described depressurizing valve 26 and the mixer 24. If there is no flow rate adjusting valve 28, excessive hydrogen flows into the discharge line in above-described State B, which is uneconomic, and is also unfavorable in terms of safety. It is also possible to provide a flow meter (not shown). Alternatively, the object of the present invention is also achieved with a configuration to fully close the valve or limit the flow rate in State B synchronously with the state of the hexagonal valve 11.
It is preferable to provide a post-mixer 29 for accelerating mixing of hydrogen and carbon dioxide in downstream of the mixer 24. It may be a spiral mixer or a mechanically stirring device. It is further preferable to provide a shock absorber (damper) 30 for preventing fluctuations of the pressure.
A metal complex as a raw material is stored in a dissolving container 31, and is dissolved and mixed when circulating a supercritical fluid therein. The amount of dissolution is adjusted by changing the temperature or the pressure in the dissolving container 31 or the grain size of the metal complex.
The components are entirely stored in a thermostat 32 maintained at 40° C. The reason why the components are heated entirely is to maintain the fluid in the supercritical state, and the temperature must simply be a temperature equal to or higher than the critical point of the fluid. In this example, the dissolving container 31 is also maintained at the same temperature.
In the configuration as described above, the resulting fluid comprises a supercritical carbon dioxide, hydrogen and the metal complex, and is supplied to the reaction vessel 33. The configuration of the reaction vessel 33 shown in Japanese Patent Application No. 2004-167782 may also be employed (however, members 18, 19 in the drawing in the document are not used, and a discharge port is additionally provided).
The fluid flowing out from the reaction vessel 33 passes through a pressure adjusting valve 34 and reaches a separator 35. The separator 35 evaporates carbon dioxide and hydrogen, and unreacted raw material and low-boiling by-products are collected. The evaporated components are discharged to the outside with the exhaust from the piping system of the above-described hydrogen mixing means. The reaction vessel 33 and the piping extending to the reaction vessel 33 may also be heated to 40° C. and stored in the same thermostat.
Reference numeral 36 in the drawing designates a pressure gauge.
Hereinafter, a process of mixing H2 when H2 is added to CO2 and carried to the reaction vessel using the apparatus shown in
A supercritical CO2 of 10 MPa was supplied from a carbon dioxide side piping system at a rate of 10 mL/min. (conversion at 40° C.), and H2 gas of 0.3 MPa was supplied from the hydrogen side piping system to the loop piping 7 at 0.3 L/min. Since the apparatus and the piping were maintained at 40° C., CO2 was in a supercritical state. The flow rates shown above are values at the respective pressure and temperature.
The capacity of the loop piping 7 was 500*. The state of the hexagonal valve 11 was switched intermittently between State A and State B. The period required for switching the valve was not more than 1 second, which was ignorable. The periods of connection were 10 to 50 seconds for CO2 (State A) and 10 second for H2 (State B), which were repeated alternately.
At this time, the density of the supercritical CO2 is 0.63 g/ML. The number of moles of a fluid flowing for T seconds was as Formula 1 shown below.
T(sec.)× 1/60×0.63(g/ML)×10(ML/min.)× 1/44=0.00239T Formula 1
The number of moles of H2 to be dissolved was as shown by Formula 2 shown below, where R designates a gas constant.
500×10−9(m3)×0.3×106×1/R×1/313=5.76×10−5 Formula 2
Therefore, the H2 concentration is as shown by Formula 3.
0.0244/T×100(%) Formula 3
A stirrer was provided at the exit of the apparatus, and a carburetor was used to vaporize at the exit thereof for analysis, and H2 in CO2 was analyzed with a gas chromatograph device. Ar was used as the carrier gas for the analysis.
The result is shown in
This is another example in which the present invention is applied to deposit a thin film of Cu usable in the internal wiring of integrated circuits. Hexafluoroacetylacetonate (Cu(hfac)2) was used as a metal complex. A Si substrate coated with tantalum nitride (TaN) by 20 nm was used as a substrate.
Firstly, 150 mg of Cu(hfac)2 was encapsulated in the dissolving container and the substrate was installed and sealed in the reaction vessel. Then a carbon dioxide cylinder was semi-opened to circulate carbon dioxide gas entirely in the flow channel to replace the inside air by carbon dioxide. The state of the hexagonal valve is A.
Then the carbon dioxide cylinder was fully opened, so that 10 mL/min. of liquid carbon dioxide was delivered and was increased in pressure by a pump to 10 MPa as a whole. Inlet-outlet port valves at two positions on the raw material dissolving container were closed once to allow the fluid to pass through a bypass valve. This was for preventing the raw material to flow out before starting the film formation. The operation of the hexagonal valve was started, hydrogen was delivered at 0.3 L/min., and the switching cycle of the valve was State A:State B=30 seconds:10 seconds. In
The reaction vessel having an inner capacity of 10 mL was heated to 250° C., the bypass valve of the raw material dissolving container was closed and, simultaneously, the inlet-outlet port valves at two positions were opened to supply the raw material and the hydrogen to the reaction vessel. The inventors proved the fact that the concentration of the Cu complex is a supercritical carbon dioxide under the same condition as described above was substantially constant (0.2 mg/mLCO2) by an absorptiometric analysis.
When deposition was performed for 30 minutes, a Cu thin film having metallic gloss was deposited. The thickness was 2 μm. The result of depth analysis by X-ray photoelectron spectroscopy is shown in
Cu deposition was performed with a batch method. Another substrate was installed in the reaction vessel, the exit of the reaction vessel was sealed, and hydrogen of 0.1 MPa and the Cu complex were encapsulated therein. The amount of the Cu complex was 110 mg, and the molar ratio of Cu complex:hydrogen was the same as Examples shown above. Subsequently, liquid CO2 was encapsulated, and processed at 230° C. for 30 minutes, to obtain a thin film of red copper color. The thickness was about 700 nm, and was about ⅓ of Examples shown above. I is presumed that the reaction could hardly proceed due to the accumulation of by-products in association of the deposition reaction of Cu in the closed system (see Formula 4).
Cu(hfac)2+H2→Cu+2Hhfac Formula 4
As a result of depth analysis (
Referring now to
In this configuration, the same function as the hexagonal valve is realized by combining eight valves. In
The pipings (a), (a′), (b) and (b′) are opened, and (d), (d′), (c) and (c′) are closed. The supercritical CO2 is charged in a pressure-resistant container 1, and discharged portion is supplied to the reaction vessel. On the other hand, H2 is charged in a pressure-resistant container 2. This state corresponds to State A described above (State A in
The mixture ratio is adjustable by changing the capacities of the pressure-resistant container 1 and the pressure-resistant container 2 and the switching intervals, but needs to be determined experimentally since excessively large volume of the containers may cause fluctuations of the pressure.
Preferably, a stirring and mixing means for internal fluid are provided in the above-described pressure-resistant container 1 and the pressure-resistant container 2. For example, a magnetic stirrer or a propeller-type stirrer may be applied.
In the configuration described above, one of the pressure-resistant container 1 and the pressure-resistant container 2 may be omitted to connect directly by piping. In this case, in the configuration using the hexagonal valve, it is needless to say that the loop piping corresponds to the pressure-resistant container, and the operation is the same in principle.
However, in the Example shown in
Therefore, in the Example shown in
In this manner, when the connecting port 2 is adapted to be closable and the connecting port 1 is adapted to be dischargeable, hydrogen is reliably charged in the above-described loop piping 7, which serves as a closed container, in State C.
When the state is switched to State D, carbon dioxide is connected from the connecting port 4 to the reaction vessel (not shown) via the above-described loop piping 7. In other words, hydrogen charged in the loop piping 7 is pushed out toward the reaction vessel by carbon dioxide being in a supercritical state while being dissolved in the carbon dioxide, and only carbon dioxide flows in the loop piping 7.
Hydrogen in the piping system which continues to the connecting port 2 flows back and is released from the shut-off valve 11 from the discharge valve 10.
When the state is switched to State E, carbon dioxide in the above-described loop piping 7 flows back and is released from the discharge valve 10 and is brought into a standby state.
In the Example shown in
In this manner, when the connecting port 2 is adapted to be closable and the discharge from the connecting port 1 is adapted to be adjustable, hydrogen is reliably charged in the above-described loop piping 7 which serves as a closed container in State C.
Subsequently, when the state is switched to State D, carbon dioxide is connected from the connecting port 4 to the reaction vessel (not shown) via the above-described loop piping 7. In other words, hydrogen charged in the loop piping 7 is pushed out toward the reaction vessel by carbon dioxide being in a supercritical state while being dissolved in the carbon dioxide, and hence only carbon dioxide flows in the loop piping 7.
Hydrogen in the piping system connected to the connecting port 2 is still held in the piping system by the check valve 12.
When the state is switched to State E, carbon dioxide in the above-described loop piping 7 flows back and is released from the check valve 12, and is brought into a standby state.
In the configuration of the storage container and the switch valves, the switch valve A-1 of the flow channel of fluid A and the switch valve B-1 of the flow channel of fluid B are opened to store hydrogen in the storage container 13 in State (1).
In State (2), the switch valve A-1 of the flow channel of fluid A and the switch valve B-1 of the flow channel of fluid B are closed, and the switch valve B-2 of the bypass piping and the switch valve B-2 of the flow channel of the fluid B are opened to pump carbon dioxide, so that hydrogen stored in the storage container 13 is delivered to a pressure container together with carbon dioxide.
In the state (3), when the switch valve B-2 of the bypass pipe 14 and the switch valve A-2 of the flow channel of the fluid A are closed, and the discharge valve 15 and the switch valve B-1 of the flow channel of the fluid B are opened, carbon dioxide in the storage container 13 is released from the discharge valve 15.
In the Example in
In the configuration of the loop piping and the switch valves, in the state (1), the switch valve A-1 of the flow channel of the fluid A and the switch valve B-1 of the flow channel of the fluid B are opened to store hydrogen in the loop piping 7.
In the state (2), the switch valve A-1 of the flow channel of the fluid A and the switch valve B-1 of the flow channel of the fluid B are closed and the switch valve B-2 of the bypass pipe 14 and the switch valve A-2 of the flow channel of the fluid A are opened to pump carbon dioxide, and hydrogen stored in the loop piping 7 is delivered to a pressure container together with carbon dioxide.
In the state (3), when the switch valve B-2 of the bypass pipe 14 and the switch valve A-2 of the flow channel of the fluid A are closed and the discharge valve 15 and the switch valve B-1 of the flow channel of the fluid B are opened, carbon dioxide in the loop piping 7 is released from the discharge valve 15.
In the Examples shown in
The supercritical fluid in the present invention may be widely selected from the group of water, alcohols, ketones, carbon halide, flons, ammonia, rare gases, nitrogen, which are known by those skilled in the art, in addition to carbon dioxide.
The additive gas is not limited to hydrogen, and any gas necessary for synthesis may be used, such as oxygen, air, nitrogen monoxide, ozone, ammonia, carbon monoxide, sulfides such as hydrogen sulfide, and hydrocarbons such as methane.
The present invention may be utilized not only in a film forming process for forming a thin film on a substrate by dissolving a reaction auxiliary and a metal precursor in a supercritical fluid or a subcritical fluid but also in the micro-fabrication process represented by various integrated circuit processes or MEMS.
7 loop piping
8 reaction vessel
9 check valve
11 hexagonal valve
21 carbon dioxide cylinder
22 cooling unit
23 pump
24 mixer
25 hydrogen cylinder
26 depressurizing valve
27 valve controller
28 flow rate adjusting valve
29 post-mixer
30 shock absorber (damper)
31 dissolving container
32 thermostat
34 pressure adjusting valve
35 separator
36 pressure gauge
| Number | Date | Country | Kind |
|---|---|---|---|
| 2004-249487 | Aug 2004 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP05/15660 | 8/29/2005 | WO | 00 | 2/28/2007 |