Patent Grant
10780644
Field of the Invention
The invention is in the field of mechanical engineering and construction and concerns a method for joining two objects. A first one of the object includes an insert portion and the other object includes an opening, and, for the two objects to be joined, the insert portion is anchored in the opening, wherein, in the anchoring area, one of the objects includes a solid material having thermoplastic properties, and the other object includes a solid material that is penetrable by the material having thermoplastic properties when liquefied. The penetrable material of the second object is, e.g., fibrous or porous. Especially, it may be a wood-based material such as wood, chipboard, etc. The second object may be a board, and the opening may be an opening in the narrow side face of the board.
Description of the Related Art
From e.g. the publications WO 96/01377 (Createc), WO 98/042988 (Woodwelding) and WO 2006/002569 (Woodwelding) or WO 2008/080239 a first approach is known to anchor inserts including materials having thermoplastic properties in fibrous or porous materials such as e.g. chipboard or wood. For such anchoring, the insert is positioned relative to the opening, and then mechanical vibration, in particular ultrasonic vibration, and a force directed for pressing the insert into the opening are simultaneously applied to the insert. In the step of positioning the insert, no relevant force is used, i.e., on application of the vibratory energy, the positioned insert will vibrate freely, or will, due to the named force pressing it against the fibrous or porous material, transmit the vibratory energy to the latter. In the step of applying vibration and force, the material having thermoplastic properties is liquefied due to friction heat at least where in contact with the fibrous or porous material and it penetrates into the fibrous or porous material of the walls of the opening and forms on re-solidification a positive fit connection with the porous or fibrous material.
According to a second, alternative approach, the second object (including a second material penetrable by a thermoplastic material) may be chosen to include an opening having a depth and the first object (including a first material being a solid material having thermoplastic properties) to include an insert portion having a length, wherein the opening and the insert portion are adapted to each other for the insert portion to be positioned in the opening with an interference fit. In this, the first and second materials constitute at least part of opposite surface areas of insert portion and opening pressed against each other in the interference fit. The interference fit may then be established by placing the insert portion in the opening and applying an interference force, and only thereafter, the insert portion is anchored in the opening by transferring energy suitable for liquefaction of the first material to the vicinity of said opposite surface areas in an amount and for a time sufficient, for liquefaction of the first material and interpenetration of the first and second materials in the vicinity of the opposite surface areas and stopping the transfer of energy for a time sufficient for the first material liquefied during the step of anchoring to re-solidify. The energy may be mechanical vibration energy, in particular ultrasonic vibration.
Especially if the second, alternative approach (with establishing an interference fit prior to the anchoring step) but also on certain embodiments of the first approach in which during the step of applying vibration and force, for example described in WO 2008/080239, a slightly oversized portion of the insert is pressed into the opening, the second object may be subject to a considerable mechanical load due to the interference force. Depending to the composition of the penetrable material or possibly other materials of the anvil object, there may be a risk of cracks or other damages (such as portions flaking off) being caused by the introduction of the insert portion into the opening prior to the step of anchoring. This risk of such damages is particularly high if the second object is board shaped at least in sections and if the opening is an opening in the narrow side face of the board, in particular if the dimensions of the opening are of a same order of magnitude as the thickness of the board (board section) so that there is not too much of the penetrable material between the opening and the broad surfaces. The same applies to objects that are not necessarily board shaped if a distance between the opening and a side surface is comparably small, for example not larger than one or two times an opening diameter.
An object of the present invention is to provide a method for joining two objects based on the above-mentioned first or second approach where the risk of damages to the second object caused by inserting the insert portion in the opening if the insert portion has a slightly oversized cross section is minimized.
According to an aspect of the invention, a method of anchoring a first object in a second object is provided, the method including the steps of:
providing the first object including a first material and providing the second object including a second material, wherein the first material is solid and includes thermoplastic properties and wherein the second material is solid and is penetrable by the first material when in a liquefied state, the second object having an end face with an opening with an opening axis and the first object further including an insert portion,
wherein the opening and the insert portion are adapted to each other for the insert portion to be positioned in the opening, and wherein said first and second materials constitute at least part of opposite surface areas of insert portion and opening pressed against each other,
applying a clamping force to the second object while the insert portion is at least partially inserted in the opening, the clamping force acting between two opposing clamping elements arranged so that the opening is between the surfaces on which the clamping elements act when the clamping force is applied, the clamping force acting in a direction non-parallel to the opening axis,
anchoring the insert portion of the first object in the opening by transferring energy suitable for liquefaction of the first material to the vicinity of said opposite surface areas in an amount and for a time sufficient, for at least partial liquefaction of the first material and interpenetration of the first and second materials in the vicinity of said opposite surface areas;
stopping the transfer of energy for a time sufficient for the first material liquefied during the step of anchoring to re-solidify.
In this, the clamping force may be applied during the step of anchoring or before the step of anchoring (for example, during the step of establishing an interference fit, especially by inserting the insert portion in the opening) or both.
The application of the clamping force reduces the risk that cracks are formed in the second object, since the second object is supported by the clamping force during at least a portion of the time during which the interference fit exerts a mechanical load on the second object. Also, the clamping force reduces the risk of visible bulges of the second object.
Whereas in the prior art, clamping is used for holding an object, for example for transport thereof, the present invention thus suggests applying a clamping force specifically—and for example locally—for keeping an object intact. Due to this, especially the clamping force may be applied in temporal and spatial correlation with the anchoring and/or the insertion of the insert portion in the opening.
In embodiments, the opening and the insert portion are adapted to each other for the insert portion to be inserted with an interference fit.
The fact that the opening and the insert portion are dimensionally adapted to each other for an interference fit (press-fit) implies that the insert portion is oversized at least locally compared with the opening, resulting in at least local pressure between insert portion and opening wall when the insert has a desired position within the opening, i.e. resulting in elastic compression of the insert portion and/or the wall of the opening. Therein the named first and second materials are arranged opposing each other at least in parts of areas of such compression.
This feature that the insert portion and the opening are adapted to each other for the insert portion to be positioned in the opening with an interference fit may, but does not need to be, used for establishing an interference fit before the step of anchoring, in accordance with the above-mentioned second approach. Then, the method includes the further step of establishing the interference fit by placing the insert portion in the opening and applying an interference force, and the step of anchoring the insert portion is carried out after the step of establishing the interference fit.
In such an optional method step of establishing the interference fit first, the insert portion is positioned in the desired position within the opening where it is retained by the above named interference fit. For achieving the interference fit, i.e. for generating the compression between insert portion and opening wall an interference force is necessary either for forcing the insert portion into the undersized opening or for clamping wall sections of the opening against the insert portion. The magnitude of the interference force corresponds substantially with the strength and area of the interference fit and it is mainly dependent on and limited by the relative dimensions of insert portion and opening and on the compressibility of either one or both of the two materials.
In alternative embodiments, no interference fit is established prior to the anchoring step, but the fact that the insert portion and the opening are adapted to each other for the insert portion to be positioned in the opening with an interference fit merely implies that an interference could be established if the insert portion was pressed further into the opening. In these embodiments, the insert portion prior to the anchoring step is placed relative to the opening only to an extent that no substantial force is necessary. During the step of anchoring, the insert portion is further moved relative to the opening, for example by being pressed further into the opening, until the opposite surface areas of the insert portion and the opening are in contact with each other, while at the same time parts of the first material are liquefied. These alternative embodiments are based on the above-mentioned first approach.
In an even further group of embodiments, the insert portion is not oversized compared to the opening, i.e. insert portion and opening are not adapted to each other for an interference fit. In these embodiments, the anchoring is carried out by a distally facing end face of the insert portion being pressed against a bottom and/or shoulder and/or taper of the opening, i.e. the opposite surface areas are the bottom/shoulder/taper of the opening and the according section of the insert portion pressed thereagainst.
Also in embodiments of this even further group, the approach according to the invention may be advantageous because due to the pressing of the insert portion into the opening and simultaneous liquefaction, a hydrostatic pressure may be built up in the opening, and the clamping force may counteract adverse effects of this hydrostatic pressure on the first object.
In embodiments, the second object has a board shaped section defining two broad surfaces and a narrow side face between the broad surfaces, wherein the above-mentioned end face with the opening(s) is the narrow side face of the board shaped section. Especially, the second object may be a board of a wood-based material, such as chipboard, fiber board, such as High Density Fiber board (HDF) and Medium Density Fiber board (MDF), or wood. In this text “chipboard” is used to refer to any composite materials manufactured by mixing wood particles of any shape with adhesives, independent of the product's shape, including, for example, oriented strand board.
In embodiments, the clamping force is perpendicular to the opening axis, i.e., the opening extends along a plane perpendicular to the clamping force. This plane in which the opening axis extends may especially be parallel to the broad surfaces of the board, i.e. to the board plane.
The clamping force may be a force that is constant or follows a controlled (pre-determined or dependent on measured parameters) time dependent profile, for example by being applied by a pressurized air based mechanism driven by a suitable compressor and possibly a regulator (including valves etc.). These embodiments feature the advantage of making a precise control and an easy adaptation to changing requirements—for example due to changing material compositions or element dimensions—possible.
In embodiments, applying the clamping force is coordinated with transferring energy and/or with inserting. In many embodiments, the clamping force is maintained until the energy input is sufficient for liquefying at least a part of the insert portion so that the pressure generated by the interference fit (if any) is substantially released.
Alternatively, the clamping force may be applied by holding the clamping elements at a fixed position relative to one another during the clamping step, for example by a mechanical locking mechanism. An embodiment of a suitable mechanical locking mechanism includes a knee lever or similar.
Embodiments that feature holding the clamping elements at a fixed position relative to one another have the advantage that they may be particularly simple to set up, with no additional energy input for the clamping force required, and that the clamping force is automatically adapted to the circumstances. In configurations with larger expanding forces on the second object (for example, of the insert portion is particularly strongly oversized compared to the opening), the tendency to bulge will be larger, but as the clamping elements are at a fixed distance, the clamping force will if necessary automatically be higher.
The clamping elements may be opposing jaws of a clamp. Alternatively, one of the clamping elements may be a support (such as a panel/table of a manufacturing machine) and the other one may equipped for being pressed/held relative to the support.
In a group of embodiments, a clamping surface area (i.e. the area of an interface between the respective clamping element and the surface portion against which it is pressed during clamping) of at least one of the clamping elements may be comparably small, for example smaller than the surface against which it is pressed (the broad surface in case of a board shaped second object) by at least a factor 5 or 10.
It has been found that the clamping surface only needs to approximately cover the insert portion, i.e. in a projection along the direction of the clamping force the dimension of the clamping surface does not need to be much larger than the according dimension of the insert portion. In embodiments, the clamping surface is slightly larger than the according dimensions of the insert portion, for example a lateral extension (extension perpendicular to the opening axis) maybe 1.5 to 8 or 2 to 5 times a diameter of the insert portion, whereas a longitudinal extension (extension parallel to the opening axis) may correspond to about 1.2 to 3 or 1.5 to 2.5 times the length of the insert portion. The condition may apply that for at least one of the clamping elements a clamping surface area corresponds to at most 40 times, preferably at most 20 times, and for example at most 15 times, and at least 1.5 times or at least 2.5 times an area of the insert portion as seen in a projection on a plane being perpendicular to the direction of the clamping force.
It has been found by the inventors that not necessarily the pressing force needs to be the decisive quantity for the prevention of damages but the mechanical pressure. By keeping the area of the clamping surface area comparably small, the pressing force required to upheld a certain mechanical pressure is kept comparably small. In embodiments with a chipboard board (panel) as the second object and with an insert portion of a diameter of about 10 mm, it has been found that the pressure should preferably be at least about 0.3 or 0.4 N/mm2.
Further, the comparably small clamping surface areas make possible that the movable mass of clamping elements is comparably small, which may be a further advantage in a high speed process. The handling may be accelerated while the board remains protected from overly high impact due to too high clamping element momenta.
Especially, the second object may be provided with a plurality of openings at an according plurality of sites (for example spaced from each other on the narrow side face if the second object has a board shaped section) for anchoring a plurality of first objects therein, wherein the clamping force is applied individually for each site instead of by a large clamp extending over more than one of the sites. Especially, a device for applying the clamping force may include for at least one of the broad surfaces a plurality of clamping elements arranged side by side. A machine for carrying out the method may include the possibility of adjusting the distance between the clamping elements.
In the approach according to the invention, the first material is solid (at ambient temperature) and includes thermoplastic properties (i.e., it is liquefiable with the aid of thermal energy; in the following this material is called “thermoplastic material”),
The second material is also solid and it is penetrable by the first material when the latter is in a liquefied state (i.e. the second material is fibrous or porous, it includes penetrable surface structures or it cannot resist such penetration under pressure). The penetrable material especially is rigid, substantially not elastically flexible (no elastomer characteristics) and not substantially plastically deformable. It further includes (actual or potential) spaces into which the liquefied material can flow or be pressed for the anchoring. It is, e.g., fibrous or porous or includes penetrable surface structures which are e.g. manufactured by suitable machining or by coating (actual spaces for penetration). Alternatively the penetrable material is capable of developing such spaces under the hydrostatic pressure of the liquefied thermoplastic material, which means that it may not be penetrable or only to a very small degree when under ambient conditions. This property (having potential spaces for penetration) implies e.g. inhomogeneity in terms of mechanical resistance. An example of a material that has this property is a porous material whose pores are filled with a material that can be forced out of the pores, a composite of a soft material and a hard material or a heterogeneous material (such as wood) in which the interfacial adhesion between the constituents is smaller than the force exerted by the penetrating liquefied material. Thus, in general, the penetrable material includes an inhomogeneity in terms of structure (“empty” spaces such as pores, cavities etc.) or in terms of material composition (displaceable material or separable materials).
Especially, the second material is not only solid at ambient temperature, but is such that it does not melt under the conditions that apply when the first material penetrates the surface structures. For example, the second material may be of a material that does not have thermoplastic properties, i.e. a material different from a thermoplastic material. The second material may further be such that it does not undergo a reversible liquefaction process or that it has a melting temperature substantially above a temperature at which the first material becomes flowable. For example, if the second material is meltable, for example if it is a metallic foam, its melting temperature or glass transition temperature may be higher than a glass transition temperature or melting temperature of the first material by at least 50° C. or at least 80° C. or at least 100° C.
In the anchoring step, energy is applied to one or the other of the objects, wherein the energy is to act as heat, in particular in areas (anchoring areas) in which, in embodiments due to the interference fit, surface areas of insert portion and opening wall are pressed against each other and include one each of the thermoplastic and the penetrable material. The heat causes the thermoplastic material to liquefy and the pressure of the interference fit and/or the pressure due to the pressing force causes interpenetration of the two materials, wherein, if applicable, the interference fit is at least partly relaxed.
In the last of the above-mentioned method steps, the supply of energy is stopped until the thermoplastic material liquefied and dislocated in the anchoring step is re-solidified, whereby in the interpenetration area a sort of composite material is formed, which connects the two objects in a positive fit connection.
The energy necessary for liquefying the thermoplastic material in the anchoring step may be supplied, as above discussed, to either one of the two objects. In embodiments, this is done in the form of mechanical vibration, in particular ultrasonic vibration, to be transformed into friction heat at the interface between the insert portion and the wall of the opening. The vibration, for example, has a main vibration direction parallel to the named opposite surfaces of insert portion and opening wall. Preferred therefore are, for achieving lateral anchorage, longitudinal vibrations substantially parallel to the depth of the opening or rotary vibrations with an axis substantially parallel to the depth of the opening.
In embodiments that include establishing an interference fit prior to anchoring, for overcoming the interference fit, it is necessary to apply a shearing load between the insert portion and the opening wall, wherein this shearing load may be caused by strong enough vibration of the one of insert portion or opening wall relative to the other one, or by the vibration and an additional shearing force acting between the two objects. For preventing undesired movement, in particular translational movement of the two objects relative to each other due to the shearing force, it may be necessary to counteract the latter in a suitable manner.
Other sorts of energy such as, e.g., irradiation with electromagnetic energy for which suitable absorbing means are to be provided at the locations where the interference fit is active, or corresponding heating (e.g., inductive or resistive heating) are applicable also.
The thermoplastic material and the penetrable material taking part in the anchorage may be present only on selected surfaces of the insert portion and on walls of the opening. For example, the insert portion may include a core of a not thermoplastic material and a coating thereof made of the thermoplastic material. However, they may also constitute larger portions of the two objects, which may include further portions of different materials or may fully consist of either the thermoplastic material or the penetrable material.
In the regions of the opposite surface areas either one of the two surfaces being pressed together may include structures functioning as energy directors, i.e. point-shaped or line-shaped elements protruding from a principal surface.
In addition or as an alternative to the approach according to this invention that includes applying a clamping force, the method of anchoring the first object may include using the thermoplastic material of the first object that has flown during the anchoring step for healing possible cracks in the second object. This may especially be combined with an insert portion design that favors in-plane (along the board plane) material flow. Examples of such designs are for example described in the Swiss patent application 01 539/14 in FIGS. 28 and 29 and their description.
Examples of second materials (penetrable materials) are wood-based materials such as chipboard (“chipboard” in this text includes any composite materials manufactured by mixing wood particles of any shape with adhesives, independent of the product's shape, including for example oriented strand board) or wood, or metallic or ceramic foams or possibly open porous structures of a material based on a not thermoplastic (thermosetting) polymer. Specific examples of penetrable materials applicable in the method according to the invention are solid materials such as wood, plywood, chipboard, cardboard, concrete brick material, porous glass, foams of metal, ceramic, or polymer materials, or sintered ceramic, glass or metal materials, wherein such materials include spaces into which the thermoplastic material can penetrate, which spaces are originally filled with air or with another displaceable or compressible material. Further examples are composite materials, which have the above stated properties, or materials with surfaces including a suitable roughness, suitable machined surface structures or suitable surface coatings (e.g. consisting of particles). If the penetrable material has thermoplastic properties it is necessary that it maintains its mechanical strength during the anchoring step either by further including a mechanically stable phase or by having a considerably higher melting temperature than the thermoplastic material to be liquefied in the anchoring step.
A thermoplastic material suitable for the method according to the invention is, under the conditions of the step of establishing the interference fit, also solid in the sense as above described for the penetrable material. It preferably includes a polymeric phase (especially C, P, S or Si chain based) that transforms from solid into liquid or flowable above a critical temperature range, for example by melting, and re-transforms into a solid material when again cooled below the critical temperature range, for example by crystallization, whereby the viscosity of the solid phase is several orders of magnitude (at least three orders of magnitude) higher than of the liquid phase. The thermoplastic material will generally include a polymeric component that is not cross-linked covalently or cross-linked in a manner that the cross-linking bonds open reversibly upon heating to or above a melting temperature range. The polymer material may further include a filler, e.g. fibers or particles of material that has no thermoplastic properties or has thermoplastic properties including a melting temperature range that is considerably higher than the melting temperature range of the basic polymer.
Examples for the thermoplastic material applicable in the method according to the invention are thermoplastic polymers, co-polymers or filled polymers, wherein the basic polymer or co-polymer is e.g. polyethylene, polypropylene, polyamides (in particular Polyamide 12, Polyamide 11, Polyamide 6, or Polyamide 66), Polyoxymethylene, polycarbonateurethane, polycarbonates or polyester carbonates, acrylonitrile butadiene styrene (ABS), Acrylester-Styrol-Acrylnitril (ASA), Styrene-acrylonitrile, polyvinyl chloride, polystyrene, or Polyetherketone (PEEK), Polyetherimide (PEI), Polysulfon (PSU), Poly(p-phenylene sulfide) (PPS), Liquid crystall polymers (LCP) etc. LCPs are of particular interest since their sharp drop in viscosity during melting enables them to penetrate in very fine spaces in the penetrable material.
Usually either one of the two objects to be joined needs to be able to transfer the vibration energy, preferably with a minimum of energy loss, from a proximal object side, where a vibrating tool is applied, to a distal side, where the insert portion or the opening is arranged. If this object is fully made of the thermoplastic material the latter will need an elasticity coefficient (at ambient temperature) of at least 0.5.GPa or preferably of at least 1.0 GPa.
Mechanical vibration or oscillation suitable for the method according to the invention has preferably a frequency between 2 and 200 kHz (even more preferably between 10 and 100 kHz, or between 20 and 40 kHz) and a vibration energy of 0.2 to 20 W per square millimeter of active surface. The vibrating tool (e.g., sonotrode) is, for example, designed such that its contact face oscillates predominantly in the direction of the tool axis (longitudinal vibration) and with an amplitude of between 1 and 100 μm, preferably around 30 to 60 μm. Such preferred vibrations are, e.g., produced by ultrasonic devices as known from ultrasonic welding.
The invention also concerns a machine for carrying out the method. Such a machine includes an insertion mechanism capable of inserting the insert portion at least partially in the opening, an anchoring tool capable of transferring the energy suitable for liquefaction of the first material to the first object or the second object, or both, for the anchoring step, and further includes a clamping mechanism capable of applying the clamping force to the second object during insertion or anchoring or both.
The machine may include an insertion station and an anchoring station separate therefrom, wherein the clamping mechanism is capable of applying the clamping force at least in the anchoring station.
Alternatively, it may be equipped for carrying out the steps of inserting and of anchoring at a same station. In such embodiments, the machine may include a gripping arrangement adapted for holding the first object in place for insertion, for example without substantial force, wherein the anchoring tool is adapted for contacting the first object adjacent to the gripping arrangement and for inserting the insertion portion into the opening.
For carrying out the process simultaneously for different first objects (for example, fittings) at different anchoring sites of a same (or possibly different) second object, the machine may include a plurality of clamping elements defining an according number of clamping sites that correspond to the anchoring sites. For carrying out the method for different second objects, a distance between the clamping sites may be adjustable.
At least one of the clamping elements of the machine may include a non-sticking arrangement adapted for facilitating release of the clamping element from the second object after release of the clamping force. In embodiments, said non-sticking arrangement includes a non-sticking pad, for example made from low friction material, and/or a gas supply for supplying release gas to a position between the clamping element and the second object.
In a group of embodiments, the machine further includes a pressurized fluid cylinder, such as a pressurized gas (for example, pressurized air) cylinder or a hydraulic cylinder, for applying the clamping force on the clamping element.
A pressurized gas cylinder may also be present for attenuating/leveling the clamping force, especially in case of mechanical locking arrangements if otherwise damages to the surface of the second object are to be expected caused by too high pressures.
Applications of the concepts described in this text and illustrated in the figures include the furniture industry, especially furniture designed for self-assembly by the customer. In this, the first object may be a fitting, and the second object may be a furniture part with a board-shaped section.
Further applications include other branches of mechanical engineering and constructions, including the automotive, aviation and shipbuilding industries where the method may be suitable of anchoring an anchor in a lightweight board of any composition, building industry, etc.
The invention and embodiments thereof are described in further detail in connection with the appended drawings that are all schematical. Same reference numbers refer to same or analogous elements. In the drawings:
The insert portion 6 has a slightly oversized cross section compared to the opening 2 so that the insert portion is held in an interference fit in the opening 2 after the insert portion 6 has been introduced, for example by a pressing force acting in a direction of an axis 20 of the opening. Due to the interference fit, opposite surface areas 18, 19 of the insert portion 6 and the opening 2 are pressed against each other. In the subsequent anchoring step, a vibrating tool, namely a sonotrode 11 is used to couple mechanical vibration energy into the fitting element 5 to liquefy portions of the thermoplastic material of the fitting element 5, and preferably of the insert portion 6, that then penetrate into structures of the board 1 and yield, after the energy input stops, the above-described anchoring.
During the step of inserting and/or during the step of anchoring a clamping force is applied to the site where the anchoring takes place. In the depicted configuration, the clamping force is applied between a movable clamping element 21 and a support 22 serving as a second clamping element.
In embodiments that include establishing an interference fit, and in which the clamping force is applied during both steps, the clamping force serves for strengthening the second object 1 including the opening 2 (or a plurality of openings) and the penetrable material for better withstanding the establishment of the interference fit and the anchoring step. Also in embodiments that do not include the step of establishing the interference fit prior to the step of anchoring but in which the oversized section of the insert portion is only introduced during the application of the mechanical vibration, a similar strengthening results.
The clamping force to be applied may, for example, be achieved by connecting the movable clamping element 21 to, for example, a pressurized gas or air cylinder 16, as schematically sketched, a hydraulic cylinder, or a mechanic screw. In particular air cylinders and hydraulic cylinders are convenient in that the clamping pressure may be controlled by controlling the air- or hydraulic pressure.
The depicted configuration of
As shown in
As the clamping elements are to exert a considerable pressure on the board 1 (in an example with chipboard as the penetrable material and with fittings 5 having an insert portion 6 of a diameter of about 7 mm, the necessary clamping pressure has been found to exceed 0.4 N/mm2), depending on the surface properties of the board 1 there may be a certain risk of the clamping elements 21, 25 sticking to the broad surfaces when the clamping pressure is to be released. To this end, the clamping elements 21, 25 may be provided with a non-sticking pad 32 or surface coating, as schematically illustrated in
A further possibility of dealing with the risk of sticking is shown in
Whereas in
As sketched in
As shown, the interference force can initially be higher than the clamping force as long as the crossover of both curves is below the damage threshold of the board material.
Furthermore, since the board material has an certain initial resistance against splitting—the clamping force does not need to be higher than the interference force, actually, only the sum of clamping force, damage threshold and some safety margin has to be higher than the interference force.
Instead of applying a constant pressure or a pressing force/pressure profile, the clamping force may be applied by holding the clamping elements at a fixed position relative to one another during the clamping step. Then, the clamping force may be zero or very small until the insertion of the insert portion starts exerting an expanding force on the board.
Other locking mechanisms locking a distance between two clamping elements are possible.
As previously mentioned, a machine for carrying out the method may include means for inserting the insert portion in the opening and means for carrying out the anchoring step at a same station or at different stations.
A gripper 71 is used for holding the first object (fitting element 5) in place for insertion, substantially without exerting pressure. The sonotrode 11 exerts the pushing force for the insertion step until the insert portion 6 is inserted in the opening 2 to a sufficient depth for the fitting element 5 being held therein. If applicable, the pressing force is exerted until the interference fit is established.
The gripper 71 is then removed, and, for the anchoring step, the sonotrode 11 starts coupling mechanical energy into the fitting element 5 while still or again exerting a pressing force. The clamping force is exerted by means of the clamping element 21 and the support 22 during the anchoring step and/or during the insertion step, preferably during both the insertion step and the anchoring step.
| Number | Date | Country | Kind |
|---|---|---|---|
| 824/14 | May 2014 | CH | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2015/061855 | 5/28/2015 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2015/181301 | 12/3/2015 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4784591 | Ackermann | Nov 1988 | A |
| 5879115 | Medal | Mar 1999 | A |
| 5902657 | Hanson | May 1999 | A |
| 20090104399 | Field | Apr 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 2004-316901 | Nov 2004 | JP |
| 2012-513552 | Jun 2012 | JP |
| 2014-77345 | May 2014 | JP |
| 9842988 | Oct 1998 | WO |
| 2006002569 | Jan 2006 | WO |
| 2008080238 | Jul 2008 | WO |
| 2008080239 | Jul 2008 | WO |
| 2016054751 | Apr 2016 | WO |
| Entry |
|---|
| International Preliminary Report on Patentability dated Nov. 29, 2016, Application No. PCT/EP2015/061855. |
| Indian Office Action dated Jan. 31, 2020, Application No. 201637040583, 5 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20170144367 A1 | May 2017 | US |