Method of bonding vulcanized rubber to resin

Abstract

A composite composed of vulcanized rubber and thermoplastic resin which adheres tightly to the rubber can be obtained by treating the surface of the vulcanized rubber with at least one of halogen, halogen generating compound and halogenoid, and bonding melted polyamide resin, polyester resin, styrene series resin or acrylic resin to the above treated rubber surface region by the injection or extrusion molding.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a method of bonding vulcanized rubber to resin. 2. Description of the Prior Art

Among recently developed various thermoplastic resins, resins called as engineering plastics are known. These resins are polyamide resin, polyester resin, polycarbonate resin, polyacetal resin, polysulfone resin, silicone resin, polyphenylene oxide resin, polyimide resin, ABS resin, methacrylic resin and the like, and many of them are excellent in mechanical strength, heat resistance, creep resistance, chemical resistance, electrical property, dimensional stability and the like, and can be widely used in place of metals, such as iron, zinc, aluminum and the like, under various use conditions.

In general, industrial rubber products are composites composed of rubber and metal; rubber and plastics; and rubber and inorganic substance, but major part of the rubber products are composites composed of rubber and metal. However, in recent industrial rubber products, the rubber-metal composite tends to be replaced by a rubber-resin composite. Industrial rubber composites are now required to have a light weight, excellent corrosion resistance, chemical resistance, wear resistance and electrical property, and a low friction coefficient.

When the composites of rubber and plastics are produced, the rubber must be tightly bonded to the plastics. In the conventional method for bonding rubber to plastics, a chlorine-containing adhesive is applied on the surface of a resin molded article obtained by the extrusion molding and the resin molded article is bonded to an unvulcanized rubber through the adhesive layer by vulcanization. However, this method of bonding resin molded article to rubber through vulcanization has the following drawbacks. That is, the adhesion strength between the resin molded article and the rubber lowers or the resin molded article cracks due to the repeating cooling and heating cycles or to the heat aging during the vulcanization step, and further the adhesion strength varies depending upon the kind of the resin. Moreover, when thermoplastic resins having a low melting point are used among thermoplastic resins, the resin molded article deforms due to the high temperature and pressure during the vulcanization.

SUMMARY OF THE INVENTION

In order to obviate the above described drawbacks, the inventors have made various investigations with respect to treating agents for the surface of a vulcanized rubber in a method of bonding a vulcanized rubber to a resin. The surface of the vulcanized rubber is treated with a treating agent to form a treated rubber surface region, and a previously melted polyamide resin, polyester resin, styrene series resin or acrylic resin is bonded to the above treated rubber surface region through an injection molding or extrusion molding. The inventors found a method of bonding tightly the vulcanized rubber to the resin to produce rubber products having a high dimensional accuracy, and accomplished the present invention.

That is, the feature of the present invention is a method of bonding vulcanized rubber to resin, comprising treating the surface of a vulcanized rubber with at least one member selected from the group consisting of halogen, halogen generating compound and halogenoid to form a treated rubber surface region, and bonding a heated and melted resin selected from the group consisting of polyamide resin, polyester resin, styrene series resin and acrylic resin to the above treated rubber surface region by the injection or extrusion molding.

According to the present invention, a vulcanized rubber having an optional shape is previously prepared, the rubber is treated with at least one of halogen, halogen generating compound and halogenoid at the surface to be bonded to a resin, the thus treated vulcanized rubber is placed in a metal mold, and the above described specifically limited resin previously heated and melted is bonded to the above treated rubber surface region by injection or extrusion molding to produce a composite composed of the rubber and the resin bonded tightly thereto at the interface. Moreover, in the present invention, vulcanized rubber is treated with a solution or the like at the surface to be bonded to resin without subjecting the surface to mechanical treatment, such as buffing by means of emery paper, grinder and the like, and therefore composites having a precise and complicated shape can be produced.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1a and 1b are a plan view and a sectional view respectively of a test piece used for evaluating the bonding method of the present invention; and

FIGS. 2a and 2b are a side view and a sectional view respectively of another test piece used for evaluating the bonding method of the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENT

The present invention will be explained in more detail.

As the rubber component of the vulcanized rubbers to be used in the present invention, there can be used natural rubber (NR) and synthetic rubber having carbon-carbon double bonds in the structural formula alone or in admixture of at least two of the rubbers. The synthetic rubbers include polyisoprene rubber (IR), polybutadiene rubber (BR), polychloroprene rubber and the like, which are homopolymers of conjugated diene compounds, such as isoprene, butadiene, chloroprene and the like; styrene-butadiene copolymer rubber (SBR), vinylpyridine-butadiene-styrene copolymer rubber, acrylonitrile-butadiene copolymer rubber, acrylic acid-butadiene copolymer rubber, methacrylic acid-butadiene copolymer rubber, methyl acrylate-butadiene copolymer rubber, methyl methacrylate-butadiene copolymer rubber and the like, which are copolymers of the above described conjufated diene compounds with vinyl compounds, such as styrene, acrylonitrile, vinylpyridiene, acrylic acid, methacrylic acid, alkyl arcylates, alkyl methacrylates and the like; copolymers of olefins, such as ethylene, propylene, isobutylene and the like, with diene compounds, for example, isobutylene-isoprene copolymer rubber (IIR); copolymers (EPDM) of olefins with nonconjugated diene, for example, ethylene-propylene-cyclopentadiene terpolymer, ethylene-propylene-5-ethyldiene-2-norbornane terpolymer, ethylene-propylene-1,4-hexadiene terpolymer; polyalkenamer obtained by the ring opening polymerization of cycloolefin, for example, polypentanamer; rubber obtained by the ring opening polymerization of oxirane ring, for example, sulfur-vulcanizable polyepichlorohydrin rubber and polypropylene oxide rubber; and the like. The rubber components of the vulcanized rubber of the present invention further include halogenides of the above described rubbers, for example, chlorinated isobutylene-isoprene copolymer rubber (Cl-IIR), broninated isobutylene-isoprene copolymer rubber (Br-IIR), polynorbornane rubber and the like.

The vulcanized rubber to be used in the present invention is obtained in the following manner. The above described rubber is fully kneaded together with fillers, such as carbon black, silica, calcium carbonate, calcium sulfate, clay, diatomaceous earth, mica and the like; softeners, such as mineral oil, vegetable oil, synthetic plasticizer and the like; vulcanization accelerators, such as stearic acid and the like; antioxidant, crosslinking agent and promoter and the like in a kneader, and the resulting homogeneous mixture is vulcanized under a proper vulcanization condition.

The vulcanized rubbers to be used in the present invention include not only vulcanized rubbers obtained by the commonly known and most important sulfur vulcanization, but also all vulcanized rubbers obtained by the thiurum vulcanization, peroxide vulcanization, quinoide vulcanization, resin vulcanization, metal salt vulcanization, metal oxide vulcanization, polyamine vulcanization, radiation vulcanization, hexamethylenetetramine vulcanization and the like.

The halogens to be used in the treatment of the vulcanized rubber surface include chlorine, bromine and iodine. These halogens are used in the form of molecule and an aqueous solution thereof. The halogen generating compounds include hypochlorous acid and hypobromous acid, and are used as such or in the form of an aqueous solution thereof.

The halogenoids include halogenated isocyanate, N-monohaloalkylurethane, N,N-dihaloalkylurethane, N,N-dihaloarylsulfonamide, sulfur halide, sulfenyl halide, halomethyl ether, thiocyanogen, iodine azide, bromine azide, iodine chloride, iodine bromide, trichloroacetic acid iodide, acetic acid bromide, iodine nitrate, alkyl hypohalite, alkyl thionylchloride, aryl thionylchloride, nitrosyl chloride, nitrosyl bromide, halogenated isocyanuric acid, halogenated methylhydantoin and the like.

Among the above described treating agents, the use of halogenoids, particularly the use of halogenated isocyanate, N,N-dihaloalkylurethane, N,N-dihaloarylsulfonamide, alkyl hypohalite, halogenated isocyanuric acid, halogenated methylhydantoin and the like is suitable for attaining the object of the present invention in view of the performance, treating processability and safety treatment.

The halogenoids are concretely iodine isocyanate, N,N-dichloroethylurethane, N,N-dibromoethylurethane, N,N-dichloropropylurethane, N,N-dibromopropylurethane, N,N-dichlorodibenzylurethane, N,N-dibromobenzylurethane, N,N-dichloro-p-toluenesulfonamide, N,N-dibromotoluenesulfonamide, N,N-dichlorobenzenesulfonamide, N,N-dibromobenzenesulfonamide, tertiary-butyl hypohalite, trichloroisocyanuric acid, dichloroisocyanuric acid, dibromo-dimethylhydantoin, dichloro-dimethylhydantoin, dichloro-methyl-isobutylhydantoin, dichloro-methylhexylhydantoin and the like.

When the vulcanized rubber surface is treated with the halogenoid in the present invention, the halogenoid is dissolved in a proper solvent and used in a concentration of 0.1-20% by weight, preferably, 1-15% by weight. As the solvent, mention may be made of halogenated hydrocarbons, such as carbon tetrachloride, chloroform, dichloromethane and the like; aromatic hydrocarbons, such as benzene, nitrobenzene, halogenated benzene, toluene, xylene and the like; chain or cyclic ethers, such as dimethyl ether, diethyl ether, tetrahydrofuran (THF), dioxane and the like; esters, such as ethyl acetate and the like; aliphatic hydroxarbons, such as pentane, hexane, heptane, octane, cyclohexane and the like; ketones, such as acetone, cyclohexanone, methyl ethyl ketone and the like; alcohols, such as tertiary butyl alcohol and the like. Among them, tetrahydrofuran, dioxane, acetone, benzene, toluene, carbon tetrachloride, chloroform, methyl ethyl ketone and ethyl acetate are preferably used.

As a method of forming a treated rubber surface region by treating a rubber surface with the above described treating agent, any industrial technique capable of making the rubber surface in contact with the treating agent can be adopted. This includes brushing, spraying, dipping and the like.

The resin to be bonded to the vulcanized rubber in the present invention is selected from polyamide resin, polyester resin, styrene series resin and acrylic resin.

As the polyamide resin, there can be used nylon-6, nylon-11, nylon-12, nylon-66, nylon-610 and their copolymers and blends, and their modified polymers obtained by modifying a part of the functional groups of the polyamides.

As the polyester resin, there can advantageously be used polyethylene terephthalate, polybutylene terephthalate and their copolymers and blends, and their modified polymers obtained by modifying a part of the functional groups of the polyesters. Of course, other polyester resins can be used as well.

As the styrene series resin, there can be used polystyrene resin, styrene copolymer resins, such as ethylene propylene nonconjugated diene-styrene-acrylonitrile copolymer resin (EPSAN resin), acrylonitrile-acrylic-styrene copolymer resin (AAS resin), acrylonitrile-styrene copolymer resin (AS resin), acrylonitrile-butadiene-styrene copolymer resin (ABS resin), butadiene-methyl methacrylate copolymer resin (MBS resin) and the like, and blends thereof, and their modified polymers obtained by modifying a part of the functional groups or carbon-carbon double bonds of the polystyrene or styrene copolymers.

As the acrylic resin, there can be used polyacrylic acid resin, polymethacrylic acid resin, polyacrylamide resin, polyacrylonitrile resin, and their copolymers and blends, and their modified polymers obtained by modifying a part of the functional groups of the acrylic polymers.

The above described resins can be mixed with inorganic fillers, such as glass fibers, calcium carbonate, talc and the like, coloring agent, ultraviolet ray absorber and the like, which are commonly added to plastics.

Further, the above described resins can be mixed with other thermoplastic resins in order to improve the processability and adhesion of the resins.

The above described resins are bonded to the treated surface region of a vulcanized rubber in the following manner. A previously melted resin is injected or extruded on the treated rubber surface region, and the resulting assembly is cooled to cure the resins.

The following examples are given for the purpose of illustration of this invention and are not intended as limitations thereof.

EXAMPLE 1

A rubber composition having a compounding recipe shown in the following Table 1 was vulcanized under a condition shown in Table 1 to produce a vulcanized rubber. From the vulcanized rubber were cut out rubber pieces 2 for test pieces shown in FIGS. 1a and 1b, which would be used for the 90.degree. peeling test described in ASTM D429, Method B, and conical rubber pieces 2 for test pieces shown in FIGS. 2a and 2b, which would be used for the tensile test described in ASTM D429, Method C. In FIGS. 1a, 1b and 2a, 2b, the numeral 1 represents resin and the unit of the dimension of the test pieces is mm.

As rubber surface treating solutions, acetone solutions containing 2, 5, 10 or 20% by weight of each halogenoid of DCTS (N,N-dichloro-p-toluenesulfonamide) and TCCA (trichloroisocyanuric acid) were prepared, and each of the acetone solutions was applied by means of a brush to the vulcanized rubber pieces 2 shown in FIGS. 1a, 1b, or FIGS. 2a, 2b at the surface to be adhered to a resin.

As polyamide resins, nylon-6 (CM 1001 made by Toray Co.), nylon-66 (CM 3001N made by Toray Co.) and nylon-12 (Daiamid made by Daicel Co.) were used, and each of the polyamides was dried for 8 hours under a condition of 120.degree. C. and 5 mmHg.

Then, the above treated vulcanized rubber piece is placed in a metal mold, and each of the above described polyamide resins was bonded to the treated surface of the rubber piece through an injection molding by means of an injection molding machine under an injection condition of 230.degree. C. in the case of nylon-6, 250.degree. C. in the case of nylon-66 or 180.degree. C. in the case of nylon-12 to produce a test piece of a composite composed of the rubber and the resin as shown in FIGS. 1a, 1b, or 2a, 2b. In FIGS. 1 and 2, the numeral 1 represents the resin, and the numeral 2 represents the rubber.

Then, the test piece shown in FIGS. 1a, 1b or 2a, 2b was subjected to an adhesion test according to Method B or Method C in ASTM D429, respectively. The obtained results are shown in the following Table 2. It can be seen from Table 2 that nontreated vulcanized rubber does not adhere to polyamide resin, but vulcanized rubber treated according to the method of the present invention adheres tightly to polyamide resin.

TABLE 1______________________________________ (parts by weight)______________________________________Natural rubber 70SBR 1500 30Carbon black 50Aromatic process oil 5Stearic acid 1.5Antioxidant *1 1Paraffin wax 1Zinc white 5Sulfur 2Vulcanization accelerator *2 1Vulcanization condition: 160.degree. C. .times. 20 minutes______________________________________ *1 Nphenyl-Nisopropyl-p-phenylenediamine *2 Dibenzothiazyl sulfide TABLE 2__________________________________________________________________________ Halogenoid Not treated Poly- DCTS TCCA (Compara- amide (N,N-Dichloro-p-toluenesulfonamide) (Trichloroisocyanuric tive) resin 2% 5% 10% 20% 2% 5% 10% 20% example)__________________________________________________________________________ASTM D429, Nylon-6 5kg/25mm 20kg/25mm 30kg/ 40kg/ 21kg/25mm 37kg/25mm 45kg/ 42kg/ 0kg/25mmMethod B (Toray, 25mm 25mm 25mm 25mm CM 1001) (25R) (80R) (100R) (100R) (80R) (100R) (100R) (100R) (R/P) Nylon-66 4kg/25mm 12kg/25mm 20kg/ 29kg/ 8kg/25mm 35kg/25mm 40kg/ 29kg/ 0kg/25mm (Toray, 25mm 25mm 25mm 25mm CM 3001N) (25R) (50R) (70R) (85R) (40R) (100R) (100R) (100R) (R/P) Nylon-12 5kg/25mm 10kg/25mm 25kg/ 30kg/ 15kg/25mm 30kg/25mm 50kg/ 50kg/ 1kg/25mm (Daicel, 25mm 25mm 25mm 25mm Daiamid) (20R) (40R) (80R) (60R) (60R) (100R) (100R) (100R) (R/P)ASTM D429, Nylon-6 52kg 76kg 86kg 90kg 87kg 92kg 90kg 90kg 0kgMethod C (Toray, CM 1001) (80R) (95R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P) Nylon-66 78kg 70kg 86kg 92kg 92kg 62kg 86kg 89kg 0kg (Toray, CM 3001N) (100R) (100R) (100R) (100R) (100R) (80R) (100R) (100R) (R/P) Nylon-12 58kg 94kg 96kg 99kg 87kg 78kg 78kg 70kg 0kg (Daicel, Daiamid) (80R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P)__________________________________________________________________________ Note: R: Cohesion of rubber is broken (numerical value is % of broken area of rubber). R/P: Rubber is peeled from plastics at the interface.

EXAMPLE 2

Adhesion of polyester resin was evaluated in the same procedure as described in Example 1.

As polyester resins, polyethylene terephthalate (FR-PET, B-3030 made by Teijin Co.), polybutylene terephthalate (Tufpet N 1000 made by Mitsubishi Rayon Co.), Hitrel 7246 made by DuPont Co. and Pelprene 150B made by Toyobo Co. were used. The polyester resins were dried for 8 hours under a condition of 120.degree. C. and 5 mmHg.

Then, test pieces were produced by means of an injection molding machine under an injection condition of 265.degree. C. in the case of FR-PET, 260.degree. C. in the case of Tufpet N 1000, 250.degree. C. in the case of Hitrel 7246, and 240.degree. C. in the case of Pelprene 150B.

The obtained results are shown in the following Table 3.

TABLE 3(a)__________________________________________________________________________ Halogenoid Not treated Poly- DCTS TCCA (Compara- ester (N,N-Dichloro-p-toluenesulfonamide) (Trichloroisocyanuric tive) resin 2% 5% 10% 20% 2% 5% 10% 20% example)__________________________________________________________________________ASTM D429, 12kg/25mm --kg/25mm 36kg/ 38kg/ 28kg/ --kg/ 40kg/25mm 39kg/25mm 0kg/25mmMethod B PET 25mm 25mm 25mm 25mm (FR-PET) (50R) (--) (100R) (100R) (70R) (--) (100R) (100R) (R/P) PBT 38kg/25mm 42kg/25mm 48kg/ 45kg/ 40kg/ 42kg/ 41kg/25mm 32kg/25mm 0kg/25mm (Tufpet 25mm 25mm 25mm 25mm N1000) (90R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P) Copolymer 39kg/25mm 50kg/25mm 46kg/ 43kg/ 51kg/ 42kg/ 35kg/25mm 28kg/25mm 1kg/25mm (Hitrel 25mm 25mm 25mm 25mm 7246) (90R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P) Copolymer 25kg/25mm 21kg/25mm 45kg/ 40kg/ 48kg/ 48kg/ 44kg/25mm 36kg/25mm 0kg/25mm (Pelprene 25mm 25mm 25mm 25mm 150B) (70R) (60R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P)__________________________________________________________________________ TABLE 3(b)__________________________________________________________________________ Halogenoid Not treated Poly- DCTS TCCA (Compara- ester (N,N-Dichloro-p-toluenesulfonamide) (Trichloroisocyanuric tive) resin 2% 5% 10% 20% 2% 5% 10% 20% example)__________________________________________________________________________ASTM D429, PET 98kg 120kg 109kg 120kg 105kg 129kg 120kg 126kg 0kgMethod C (FR-PET) (80R) (100R) (95R) (100R) (90R) (100R) (100R) (100R) (R/P) PBT 112kg 128kg 129kg 129kg 129kg 108kg 110kg 105kg 0kg (Tufpet N1000) (90R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P) Copolymer 108kg 126kg 120kg 115kg 130kg 108kg 102kg 101kg 0kg (Hitrel 7246) (95R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P) Copolymer 128kg 131kg 105kg 103kg 126kg 108kg 106kg 100kg 0kg (Pelprene 150B) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P)__________________________________________________________________________

EXAMPLE 3

Adhesion of another polyester resin (polyarylate resin, AX 1500 produced by Unichika Co. and called as U polymer) was evaluated in the same procedure as described in Example 1. The injection molding was carried out at a temperature of 230.degree. C.

The obtained results are shown in the following Table 4.

TABLE 4__________________________________________________________________________ Halogenoid Not treated DCTS TCCA (Compara- (N,N-Dichloro-p-toluenesulfonamide) (Trichloroisocyanuric acid) tiveMethod 2% 5% 10% 20% 2% 5% 10% 20% example)__________________________________________________________________________ASTM D429, 15kg/25mm 18kg/25mm 50kg/25mm 48kg/25mm 10kg/25mm 46kg/25mm 52kg/25mm 49kg/25mm 0kg/25mmMethod B (R/P) (20R) (100R) (100R) (20R) (90R) (P) (100R) (R/P)ASTM D429, 26kg 69kg 112kg 108kg 48kg 102kg 121kg 105kg 0kgMethod C (R/P) (50R) (100R) (100R) (40R) (90R) (100R) (100R) (R/P)__________________________________________________________________________ Note: P: Cohesion of plastics is broken.

EXAMPLE 4

Adhesion of styrene series resins was evaluated in the same procedure as described in Example 1.

The kind of used styrene series resins and the injection molding condition are as follows. Polystyrene resin (Styron 683 made by Asahi Dow Co.) was injection molded at 260.degree. C., acrylonitrile-butadiene-styrene copolymer resin (Cevian SER 20 made by Daicel Co.) was injection molded at 200.degree. C., and glass fiber-reinforced acrylonitrile-styrene copolymer resin (Cevian N 080 FS made by Daicel Co.) was injection molded at 235.degree. C.

The obtained results are shown in the following Table 5.

TABLE 5__________________________________________________________________________ Halogenoid Not treated DCTS TCAA (Compara- (N,N-Dichloro-p-toluenesulfonamide) (Trichloroisocyanuric tive) Styrene 2% 5% 10% 20% 2% 5% 10% 20% example)__________________________________________________________________________ASTM D429, Polystyrene 0kg/25mm 1kg/ 4kg/ 5kg/ 1kg/25mm 2kg/25mm 5kg/ 6kg/ 0kg/25mmMethod B resin 25mm 25mm 25mm 25mm 25mm (Styron 683) (R/P) (R/P) (5R) (10R) (R/P) (R/P) (10R) (10R) (R/P) ABS resin 5kg/25mm 32kg/ 45kg/ 40kg/ 40kg/25mm 45kg/25mm 36kg/ 40kg/ 0kg/25mm (Cevian 25mm 25mm 25mm 25mm 25mm SER20) (10R) (90R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P) FR-AS resin 30kg/25mm 42kg/ 48kg/ 42kg/ 45kg/25mm 43kg/25mm 38kg/ 39kg/ 0kg/25mm (Cevian 25mm 25mm 25mm 25mm 25mm N 080FS) (85R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P)ASTM D429, Polystyrene 25kg 50kg 2kgMethod C resin (Styron 683) (20R) (30R) (R/P) ABS resin 102kg 128kg 138kg 140kg 139kg 124kg 110kg 108kg 5kg (Cevian SER20) (90R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P) FR-AS resin 124kg 129kg 136kg 130kg 139kg 120kg 111kg 106kg 1kg (Cevian N 080FS) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P)__________________________________________________________________________

EXAMPLE 5

Adhesion of acrylic resins was evaluated in the same procedure as described in Example 1.

The kind of used acrylic resins and the injection molding condition are as follows. Methacrylic resin (Acrypet MD made by Mitsubishi Rayon Co.) was injection molded at 220.degree. C., and a blend (Metamarble made by Teijin Co.) of methacrylic resin and polycarbonate resin was injection molded at 260.degree. C.

The obtained results are shown in the following Table 6.

TABLE 6__________________________________________________________________________ Halogenoid Not treated DCTS TCCA (Compara- Acrylic (N,N-Dichloro-p-toluenesulfonamide) (Trichloroisocyanuric tive) resin 2% 5% 10% 20% 2% 5% 10% 20% example)__________________________________________________________________________ASTM D429, Methacrylic 8kg/25mm 52kg/ 48kg/ 50kg/ 45kg/ 53kg/ 41kg/ 48kg/25mm 0kg/25mmMethod B resin 25mm 25mm 25mm 25mm 25mm 25mm (Acrypet MD) (20R) (100R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P) Metacrylic resin + poly- 5kg/25mm 12kg/ 49kg/ 42kg/ 45kg/ 40kg/ 42kg/ 42kg/25mm 0kg/25mm carbonate 25mm 25mm 25mm 25mm 25mm 25mm (Metamarble) (10R) (25R) (100R) (100R) (100R) (100R) (100R) (100R) (R/P)ASTM D429, Methacrylic 96kg 128kg 138kg 140kg 130kg 124kg 113kg 108kg 5kgMethod C resin (Acrypet MD) (20R) (50R) (100R) (P) (100R) (100R) (100R) (100R) (R/P) Metacrylic resin + poly- 68kg 108kg 120kg 132kg 122kg 128kg 120kg 119kg 8kg carbonate (Metamarble) (30R) (80R) (100R) (100R) (80R) (100R) (100R) (100R) (R/P)__________________________________________________________________________

Claims

1. A method of bonding vulcanized rubber to resin, comprising treating the surface of a vulcanized rubber with at least one member selected from the group consisting of halogen, halogen generating compound, and halogenoid to form a treated rubber surface region, and bonding a heated and melted resin selected from the group consisting of polyamide resin, polyester resin, styrene series resin and acrylic resin to the above treated rubber surface region by the injection or extrusion molding.

2. A method according to claim 1, wherein said halogen is at least one member selected from the group consisting of chlorine, bromine and iodine.

3. A method according to claim 1, wherein said halogen generating compound is hypochlorous acid.

4. A method according to claim 1, wherein said halogenoid is at least one member selected from the group consisting of N,N-dichloro-p-toluenesulfonamide and trichloroisocyanuric acid.

5. A method according to claim 1, wherein said resin is polyamide resin.

6. A method according to claim 5, wherein said polyamide resin consists mainly of polyamide resin having amide groups in the main chain.

7. A method according to claim 1, wherein said resin is polyester resin.

8. A method according to claim 7, wherein said polyester resin is thermoplastic resin consisting mainly of polyethylene terephthalate or polybutylene terephthalate.

9. A method according to claim 1, wherein said resin is styrene series resin.

10. A method according to claim 1, wherein said resin is acrylic resin.