1. Field of the Invention
The invention relates to methods of controlled remelting of or laser metal forming on the surface of articles.
2. Brief Description of the Related Art
In the last years laser metal forming (LMF) has been introduced in industrial manufacturing. Laser metal forming is a process where a high power laser locally melts a focused stream of metal powder or a metal wire 20 onto a substrate. In this way material can be added to the underlying part. The method is suitable for controlled material build-up and the laser generated parts are characterized by a dense microstructure which is usually free of pores.
Laser metal forming has been recently used for commercial manufacturing of superalloys due to its attractive potential for repair of locally damaged or worn parts. Indeed, it is possible to selectively add material at desired locations and to re-establish the full functionality of a component. It is clear that laser repair technology is particularly attractive for the refurbishment of expensive parts that are affected by local damage or local mechanical wear. Turbine blades and vanes are typical examples.
However, the process is complicated when single-crystal components have to be refurbished. Single crystal blades and vanes can be found in the most heavily loaded rows of modern gas turbines (first or high pressure row). Their mechanical integrity relies on the particular properties due to single-crystal microstructure and the absence of grain boundaries. Reconditioning of such components is only feasible if the single crystal microstructure can be maintained during the repair process.
During laser metal forming substrate material is locally molten and powder (or wire 20) is injected into the melt pool with a suitable powder (or wire 20) feeder mechanism. After a certain interaction time (which is determined by the laser spot size and the relative movement between laser and substrate) the molten material resolidifies leading to material build-up on the substrate.
However, during the solidification of the molten material new grains may form in the melt pool due to constitutional undercooling of the liquid melt. The growth of these newly formed grains leads to undesired build-up of equiaxed material, i.e. material that is oriented in a random manner. As the thermomechanical properties of superalloys greatly depend on the crystallographic orientation and as SX crystal components rely on the benefit of preferable orientation it is obvious that the consequence of equiaxed growth is a serious degradation of the mechanical properties. Moreover, superalloys which do not contain grain boundary stabilizing elements exhibit excessive creep when unwanted grain boundaries are formed. For epitaxial laser metal forming it is therefore crucial to ensure a completely SX microstructure of a part by avoiding the so-called columnar to equiaxed transition (CET).
One strategy for ensuring epitaxial growth, i.e. growth with orientation matched to the substrate and without formation of new grains, is to use special process conditions. Laser parameters have to be adjusted in a manner that a specific ratio between temperature gradient G and the solidification speed Vs is maintained. Both quantities depend not only on laser parameters such as power, power density, advance speed but also on the properties of the substrate and powder (or wire 20) material.
Those skilled in the art of laser metal forming are also aware that the onset of (marangoni) convection in the melt pool is one of the main reasons for the undesired CET. Initiation of convection processes in the melt pool leads to fragmentation of the fragile dendrites that form during the solidification of the molten material. By the effect of convective transport dendrite fragments are distributed all over the melt pool where they acts as nucleation sites and promote the formation of equiaxed material.
Unfortunately melt pool convection is also affected by other process parameters like mass feed rate, protection gas stream, injection angle. In addition, marangoni convection is not readily detectable without melt pool monitoring.
So far, several patents have been issued for the laser metal forming process. The basic principle is described in EP-A1-0 558 870, DE-C1-199 49 972, U.S. Pat. No. 5,873,960, U.S. Pat. No. 5,622,638 or U.S. Pat. No. 4,323,756.
The application of epitaxial material build-up for protective coatings is covered by U.S. Pat. No. 6,277,500, applications for generation or refurbishment of single crystal components are described in U.S. Pat. No. 6,024,792, EP-A1-0 740 977, WO95/35396 or U.S. Pat. No. 5,914,059. Except U.S. Pat. No. 6,024,792 none of these patents mentions the significance of the G, Vs parameters in order to obtain the desired single crystal microstructure. U.S. Pat. No. 6,024,792 states that the laser power has to be set in a way to obtain adequate values for G and Vs, however, does not suggest a method for automatic laser power control or for avoiding melt pool convections.
Another patent application, WO95/06540 suggests the use of a pyrometer for interactive laser welding of super alloy articles measuring the substrate preheating temperature.
The collection of optical signals from the melt pool is also depicted in U.S. Pat. No. 6,122,564. In this patent, an optical monitoring system is connected to a feedback controller in order to adjust the material deposition rate depending on the indicated height of previously deposited material.
In U.S. Pat. No. 6,311,099 an apparatus for regulating laser welding parameters is suggested that uses optical signals from the interaction zone. In this patent the optical signal is generated by near infrared radiation originating from the weld pool. The radiation is detected by a CCD camera and processed in order to obtain information about the physical dimensions of the melt pool.
According to an aspect of the invention, an advanced method for controlled deposition or remelting of material on substrates avoids hot tearing defects, the columnar to equiaxed transition (CET) and melt pool convection. With material it should be possible to deposit material on single crystal substrates epitaxial with the base material or to transform a previously polycrystalline surface layer into single crystal material.
In accordance with another aspect of the invention, a method can include remelting of the surface of an article and can also include laser metal forming on the surface of an article.
The method can be used for remelting substrate material in order to re-establish a single crystal microstructure in the surface zones of the substrate, to transform a previously polycrystalline surface layer into single crystal material, to coat single crystal articles with a single crystal coating or for the repair of single crystal turbine components. Due to matched thermo-physical properties of solidified and base material the method leads to reduced stress and therefore to greater lifetime of the components.
With the online monitoring system and using automatic feed-back control of at least one process parameter such as laser power it is possible to establish and maintain optimum process conditions. In this favorable case the columnar to equiaxed transition (CET) and melt pool convection are avoided and a temperature field is created in the melt pool which leads to defect-free, epitaxial growth of the deposited material. Thus, it is possible to add new material without creation of grain boundaries. Beside the laser power process parameters like the relative speed between laser beam and the substrate, the carrier gas flow and mass feed rate of added material can be controlled.
Preferably a fibre coupled high power diode laser is used as a light source. The inventive method combines laser power delivery, material supply and process monitoring in a dedicated laser/powder head. With this device the powder injection can be concentric with respect to the cone of captured optical signals from the melt pool or the cone of captured optical signals from the melt pool concentric with respect to the light source focusing cone. With the help of a dichroitic mirror infrared (IR) radiation from the melt pool is collected through the same optics which is used for laser focusing. The dichroitic mirror transmits laser light and reflects process light or vice versa.
The process signal from the melt pool can be coupled to a pyrometer or another fiber-coupled detector. For this purpose the optical properties of the monitoring system are chosen such that the measurement spot is smaller than the melt pool and located at the center of the melt pool. In a preferred embodiment according to the invention the optical signal is captured from the center and vicinity of the laser focal spot using a single optical fiber, an imaging fiber bundle or a charged coupled device (CCD) camera that is equipped with suitable optical filters. This information is used to determine the temperature a single spot or simultaneously at several locations in the center and in the vicinity of the melt pool. In a second case temperature gradients in the laser interaction zone can be analyzed.
The online feed back control of the laser power is decoupled from the main process control by means of a separate microprocessor. This allows faster parallel processing in real-time, i.e. independent from the operating system.
In another embodiment post-processing of the optical signal from the melt pool is used for quality control: The analysis of the measured data allows optimizing process parameters such that a desired microstructure is obtained. Recording of monitoring signals serves also for documentation purposes and for ensuring consistent product quality.
Moreover, dedicated commercially available software tools with enhanced functionality can be used for the realization of the control system. As a consequence short loop times and advanced PID control features such as gain scheduling can be realized.
Still other objects, features, and attendant advantages of the present invention will become apparent to those skilled in the art from a reading of the following detailed description of embodiments constructed in accordance therewith, taken in conjunction with the accompanying drawings.
The invention of the present application will now be described in more detail with reference to preferred embodiments of the apparatus and method, given only by way of example, and with reference to the accompanying drawings, in which:
Referring to the drawing figures, like reference numerals designate identical or corresponding elements throughout the several figures.
The herein disclosed method can be used for remelting substrate material of the article I in order to re-establish a single crystal (SX) microstructure in the surface zones of the substrate or to transform a previously polycrystalline surface layer into SX material. In addition this method can be used for SX-coating application on SX-articles 1 or for the repair of single crystal (SX) turbine components. The underlying single crystal bulk material will act as a crystal seed for the remolten material. Due to matched thermo-physical properties the method leads to reduced stress and therefore to greater lifetime of the components.
It can be seen from the previous paragraph that high thermal gradients with the melt pool 7 are crucial for single crystal solidification. For this reason high power lasers such as CO2, (fibre coupled) Nd—YAG or (fibre coupled) high power diode lasers offer a particularly attractive choice as a light source. Laser radiation can be focussed to small spots and generate thermal gradients in excess of 106 K/m. It is beneficial if the laser intensity is uniform over the heated area, which can be achieved by fiberoptic beam delivery. As laser power is very easily controlled, it is ensured that the criterion for single crystal solidification is maintained during the whole operation.
If during this operation the ratio Gn/Vs (where G is the temperature gradient in the melt pool, n is a material constant and Vs is the solidification speed) is kept above a material dependent threshold value, the subsequent solidification will occur epitaxially, i.e. without creating new grain boundaries.
In a typical application the laser will be focussed to a spot size of 1-3 mm diameter. Preferably the laser would be either of the Nd—YAG or high power diode laser type. These lasers operate in the near infrared and about 30-40% of the incident radiation is absorbed by typical super alloys. The laser beam will move at relatively slow speeds (approx. 1-10 mm/s) over the affected zones and operate in the conduction welding mode. Laser intensities of 1*103 W/cm2 to 5*104 W/cm2 will remelt a zone reaching up to 500 □m below the surface. Larger penetration depths can be achieved by further reducing the processing speed or by preheating the article 1 prior to the melting of the surface 5 to a desired temperature in the range of 500-1000° C., e.g. with a high frequency generator. On preheated articles, however, thermal gradients are smaller and it is more difficult to meet the Gn/Vs criterion. On the other hand the risk of hot tearing defects during the whole operation is reduced. The area on the substrate which is directly heated by the light source is known as a light source interaction zone.
As seen from the
The method uses a combination of a concentric feeder 10, a fiber coupled laser and an on-line monitoring system with real time capability. With the help of the online monitoring system optimum process conditions are established and maintained where the columnar to equiaxed transition (CET) and melt pool convection are avoided. Hence, defect-free, epitaxial growth of the deposited material is observed. It is thus possible to add new material without creation of grain boundaries.
The method combines laser power delivery, material supply and process monitoring in a dedicated laser/powder head as shown in
The optical signal 13 from the melt pool 7 is coupled to a pyrometer 15 or another fiber-coupled detector which allows the online determination of the melt pool temperature. For this purpose the optical properties of the monitoring system are chosen such that the measurement spot is smaller than the melt pool and located at the center of the melt pool 7. In another embodiment according to the invention the optical signal 13 is captured from the center and vicinity of the laser focal spot using an imaging fibre bundle or a charged coupled device (CCD) camera that is equipped with suitable optical filters. This information is used to determine the temperature a single spot or simultaneously at several locations in the center and in the vicinity of the melt pool. In a second case temperature gradients in the laser interaction zone can be analyzed.
The cone of captured optical signals 13 from the melt pool 7 can be concentric with respect to the laser focusing cone. The symmetry of this arrangement ensures that laser-powder interaction does not change during movements on complex shaped components. This leads to consistent high quality of the process.
As seen in
In another embodiment postprocessing of the optical signal 13 from the melt pool 7 is used for quality control: The analysis of the measured data allows optimizing process parameters such that a desired microstructure is obtained. Recording of monitoring signals serves also for documentation purposes and for ensuring consistent product quality.
Moreover, dedicated commercially available software tools (e.g. LabView RT) with enhanced functionality can be used for the realization of the control system 16. As a consequence loop times <10 ms and advanced PID control features such as gain scheduling, which means the use of different sets of PID parameters in predefined temperature intervals can be realized.
An example of a structure treated in accordance with an embodiment of the invention is shown in
Another example of a structure treated in accordance with an embodiment of the invention is shown in
Reference Numbers
1 Article, e.g. blades or vanes for gas turbines
2 Root portion
3 Platform
4 Blade
5 Surface of article 1
6 Laser beam
7 Melt pool
8 Powder
9 Carrier gas
10 Feeder
11 Direction of movement
12 Solidified material
13 Optical signal
14 Dichroitic mirror
15 Pyrometer
16 Control system
17 Main process control
18 Controller for feeder 10
19 Controller for laser
20 Wire
While the invention has been described in detail with reference to preferred embodiments thereof, it will be apparent to one skilled in the art that various changes can be made, and equivalents employed, without departing from the scope of the invention. Each of the aforementioned documents is incorporated by reference herein in its entirety.
Number | Date | Country | Kind |
---|---|---|---|
02405126.0 | Feb 2002 | EP | regional |
This application is a Continuation of, and claims priority under 35 U.S.C. §120 to, International application number PCT/CH03/00098, filed 10 Feb. 2003, and claims priority under 35 U.S.C. §119 to European application number 024 05 126.0, filed 20 Feb. 2002, the entireties of which are incorporated by reference herein.
Number | Date | Country | |
---|---|---|---|
Parent | PCT/CH03/00098 | Feb 2003 | US |
Child | 10920715 | Aug 2004 | US |