Patent Application
20110023965
This application claims priority to Japanese Patent Application No. 2006-111598 filed on Apr. 14, 2006, the entire disclosure of which is incorporated herein by reference in its entirety.
The present invention relates to a method of controlling a regulating hole for regulating an amount of light, a flow rate of fluid, or a pressure of the fluid passing through tubular passage and a device of controlling the regulating hole.
Conventionally, as a method of controlling a flow rate fluid passing through a tubular passage, a mechanical control method, such as, e.g., a control method using a needle valve, has been typically used.
In this method, however, there are drawbacks that the mechanical slide movements cause wear of the valve, varying control characteristics thereof across the ages, which in turn may result in loss of control.
the meantime, magnetic fluid containing magnetic particles is used as a damper for damping vibrations of a CD player (see, e.g., Patent Documents 1 and 2).
[Patent Document 1] Japanese Unexamined Laid-open Patent Publication No. 2005-180612
[Patent Document 2] Japanese Unexamined Laid-open Patent Publication No 2001-291609
Magnetic fluid containing magnetic particles, however, has fluidity which is inconvenience in handling, and vaporizes/volatilizes by the prolonged use, resulting in gradual volume decrease. By these reasons, the control device for dampers using magnetic fluid varies control characteristics thereof across the ages, which in turn may result in loss of control.
The present invention was made in view of the aforementioned technical background, and the purpose of the invention is to provide a method of controlling a regulating hole for regulating an amount of light, a flow rate of fluid, or a pressure of the fluid passing through a tubular passage, a device for controlling a regulating hole for use in the aforementioned control method, and a production method of a partition wall used in the control device.
The other purposes and advantages of the present invention will be apparent from the following preferred embodiments.
[1] A method of controlling a regulating hole, wherein a partition wall formed by a viscoelastic solid containing magnetic particles is transversely disposed in a tubular passage through which light or fluid passes, the partition wall being provided with a regulating hole for regulating an amount of the light, a flow rate of the fluid, or a pressure of the fluid so that the regulating hole penetrates the partition wall in an axial direction, and
wherein magnetic field gradient is generated in a radial direction in the tubular passage to thereby change an opening degree of the regulating hole.
[2] The method of controlling a regulating hole as recited in the aforementioned Item 1, wherein the magnetic particle is set to 500 μm or less in particle size.
[3] The method of controlling a regulating hole as recited in the aforementioned Item 1 or 2, wherein the viscoelastic solid is one type or two or more types of rubbers selected from the group consisting of silicone rubber, urethane rubber, propylene rubber, polyethylene rubber, neoprene rubber, and natural rubber.
[4] The method of controlling a regulating hole as recited in any one of the aforementioned Items 1 to 3, wherein the magnetic particle is one type or two or more types of particles selected from the group consisting of carbonyl iron particles, ferrite particles, and magnetite particles.
[5] The method of controlling a regulating hole as recited in any one of the aforementioned Items 1 to 4, wherein, when a value obtained by dividing a volume of the magnetic particles by a total volume of the magnetic particles and the viscoelastic solid is defined as a rate of content of the magnetic particles in the partition wall, the rate of content is set so as to fall within the range of 15 to 52 volume %.
[6] The method of controlling a regulating hole as recited in any one of the aforementioned Items 1 to 5, wherein the partition wall is formed by a silicone rubber containing carbonyl iron particles obtained by mixing mother liquid of the silicone rubber, its hardening solution, and carbonyl iron particles falling within the range of 1:0.1-1.5:1.3-8 in mass ratio and then heat hardening the mixture.
[7] The method of controlling a regulating hole as recited in any one of the aforementioned Items 1 to 6, wherein the magnetic field gradient is generated by a coil disposed at an outside of the tubular passage so as to surround the partition wall in a circumferential direction.
[8] A control device for a regulating hole, comprising:
a tubular passage through which light or fluid passes;
a partition wall formed by a viscoelastic solid containing magnetic particles transversely disposed in the tubular passage and provided with a regulating hole for regulating an amount of the light, a flow rate of the fluid, or a pressure of the fluid so that the regulating hole penetrates the partition wall in an axial direction; and
a magnetic field gradient generating means for generating magnetic field gradient in a radial direction in the tubular passage.
[9] The control device for a regulating hole as recited in the aforementioned Item 8, wherein the magnetic particle is set to be 500 μm or less in particle size.
[10] The control device for a regulating hole as recited in the aforementioned Item 8 or 9, wherein the viscoelastic solid is one type or two or more types of rubbers selected from the group consisting of silicone rubber, urethane rubber, propylene rubber, polyethylene rubber, neoprene rubber, and natural rubber.
[11] The control device for a regulating hole as recited in any one of the aforementioned Items 8 to 10, wherein the magnetic particle is one type or two or more types of particles selected from the group consisting of carbonyl iron particles, ferrite particles, and magnetite particles.
[12] The control device for a regulating hole as recited in any one of the aforementioned Items 8 to 11, wherein, when a value obtained by dividing a volume of the magnetic particles by a total volume of the magnetic particles and the viscoelastic solid is defined as a rate of content of the magnetic particles in the partition wall, the rate of content is set so as to fall within the range of 15 to 52 volume %.
[13] The control device for a regulating hole as recited in any one of the aforementioned Items 8 to 12, wherein the partition wall is formed by a silicone rubber containing carbonyl iron particles obtained by mixing mother liquid of the silicone rubber, its hardening solution, and carbonyl iron particles falling within the range of 1:0.1-1.5:1.3-8 in mass ratio and then heat hardening the mixture.
[14] The control device for a regulating hole as recited in any one of the aforementioned Items 8 to 13, wherein the magnetic field gradient generating means is configured to generate magnetic field gradient by a coil disposed at an outside of the tubular passage so as to surround the partition wall in a circumferential direction.
[15] A method of producing a partition wall for use in a control device for a regulating hole, the control device comprising:
a tubular passage through which light or fluid passes;
a partition wall transversely disposed in the tubular passage and provided with a regulating hole for regulating an amount of the light, a flow rate of the fluid, or a pressure of the fluid so that the regulating hole penetrates the partition wall in an axial direction; and
a magnetic field gradient generating means for generating magnetic field gradient in a radial direction in the tubular passage,
wherein the partition wall is formed by silicone rubber containing carbonyl iron particles obtained by mixing mother liquid of the silicone rubber, its hardening solution, and carbonyl iron particles falling within the range of 1:0.1-1.5:1.3-8 in mass ratio and then heat hardening the mixture.
The present invention exerts the following effects.
In the invention [1], by generating the magnetic field gradient in the radial direction in the tubular passage, the opening degree of the regulating hole can be changed. Therefore, even in the case of repeatedly changing the opening degree of the regulating hole, almost no wear of the partition wall occurs. Furthermore, the partition wall is formed by a viscoelastic solid, which does not cause volatilization or vaporization. Therefore, the regulating hole can be controlled over a long period of time.
Furthermore, the partition wall formed by a viscoelastic solid is easy to handle as compared with a partition wall formed by magnetic fluid, and the installation work of the partition wall in the tubular passage can be easily performed.
In the invention [2], at the time of producing the partition wall, the magnetic particles can be evenly dispersed in the viscoelastic solid. Therefore, a partition wall in which magnetic particles are evenly dispersed can be produced. By using this partition wall, the control of the regulating hole can be performed assuredly.
In the invention [3], the partition wall can be assuredly set to have elasticity appropriate for changing the opening degree of the regulating hole. Thus, the control of the regulating hole can be performed assuredly.
In the invention [4], the partition wall can be assuredly set to have magnetism appropriate for changing the opening degree of the regulating hole. Thus, the control of the regulating hole can be performed assuredly.
In the invention [5], the partition wall can be assuredly set to have elasticity and magnetism appropriate for changing the opening degree of the regulating hole. Thus, the control of the regulating hole can be performed more assuredly.
In the invention [6], the partition wall can be assuredly set to have elasticity and magnetism appropriate for changing the opening degree of the regulating hole. Thus, the control of the regulating hole can be performed assuredly.
In the invention [7], the opening degree of the regulating hole can be changed assuredly.
In the inventions [8] to [14], a control device for a regulating hole preferably used in a control method of regulating hole according to the present invention can be provided.
In the invention [15], a partition wall used in the control device for a regulating hole according to the present invention can be produced assuredly.
Next, some preferred embodiments of the present invention will be explained with reference to the attached drawings.
This control device 1A is, as shown in
In detail, the tubular member 2 is a tubular member round in cross-section. Therefore, the tubular passage 3 of this tubular member 2 is round in cross-section. Through this tubular passage 3, fluid G, such as, liquid (e.g., water, oil, or liquid fuel) or gas (e.g., air, or gaseous fuel) passes along the axial direction. It should be noted that the present invention does not limit the type of the fluid G passing through the tubular passage 3.
The tubular member 2 is made of a magnetic field permeable material. Specifically, it is made of, for example, plastics (e.g., acrylic resin, vinyl chloride resin, or polytetrafluoroethylene resin) or a non-magnetic substance, such as e.g., ceramics.
The inner diameter of the tubular member 2, i.e., the diameter D (see
In
The partition wall 5 has a columnar shape as shown in
The length L (see
As shown in
In this embodiment, the cross-sectional shape of the regulating hole 6 is circular, and the diameter d and the opening area S of the regulating hole 6 are each set to be constant along the axial direction of the tubular passage 3.
The diameter d of the regulating hole 6 is set so as to fall within the range of, for example, from 0.1 to 1 mm. The present invention, however, does not require that the diameter d falls within this range.
The partition wall 5 is made of a viscoelastic solid containing magnetic particles, and therefore is elastically deformable. The magnetic particles are dispersed evenly or generally evenly in the viscoelastic solid and contained in the viscoelastic solid in a fixed manner. The partition wall 5 is configured such that it can be deformed elastically when magnetic field gradient is generated in the tubular passage 3 in the radial direction (i.e., in the r-direction).
As shown in
It is preferable that the viscoelastic solid is one type or two or more types of rubbers selected from the group consisting of silicone rubber, urethane rubber, propylene rubber, polyethylene rubber, neoprene rubber, and natural rubber. In detail, it is preferable that the viscoelastic solid is a rubber made of one of the rubbers selected from the group or made by mixing two or more types of the rubbers selected from the group. The use of such viscoelastic solid as the structural material of the partition wall 5 assuredly enables the partition wall 5 to have elasticity suitable for changing the opening degree of the regulating hole 6, which in turn enables assured control of the regulating hole S. Each rubber can be used in a gel state.
It is preferable that the tearing strength of the viscoelastic solid at 100° C. falls within the range of, for example, from 10 to 30 kN/m2. It should be noted, however, that the present invention does not require that the tearing strength falls within the aforementioned range.
The use of viscoelastic solid as the structural material of the partition wall 5 enables minute changes of the opening degree of the regulating hole 6, which in turn enables assured control of the regulating hole 6.
As the magnetic particles, it is preferable to use, for example, one or two or more particles selected from the group consisting of ferromagnetic particles, diamagnetic particles, antiferromagnetic particles and paramagnetic particles. In detail, it is preferable that the magnetic particles are one type of the particles selected from the group or a mixture of two or more types of the particles selected from the group.
Furthermore, it is preferable that the magnetic particle is one type or two or more types of particles selected from the group consisting of carbonyl iron particles, ferrite particles, and magnetite particles. In detail, the magnetic particles are preferably one type of particles or particles obtained by mixing two or more types of particles selected from the group.
The magnetic particle is preferably set to be 500 μm or less in particle size. The particle size denotes an average particle size of the magnetic particles. The particle size of 500 μm or less enables uniform dispersion of the magnetic particles in the viscoelastic solid at the time of producing the partition wall 5. As a result, a partition wall 5 in which magnetic particles are uniformly dispersed can be produced. The use of such a partition wall 5 enables assured control of the regulating hole 6. It is more preferable that the particle size is set to be 10 μm or less.
On the other hand, the lower limit of the particle size of the magnetic particle is not specifically limited, and can be any size as long as it exceeds 0 μm. Specifically, it is preferable that the particle size is 1 μm or more since it is possible to produce and obtain magnetic particles at low cost.
In cases where the magnetic particle is 10 nm or less in particle size, e.g., in the case of the magnetite particle having a particle size of 10 nm or less, there is a possibility that it can be used as a superparamagnetic particle. The use of the superparamagnetic particle has the following advantages. That is, in cases where the partition wall 5 is formed by a viscoelastic solid containing ferromagnetic particles, repeated applications of magnetic fields to the partition wall 5 may generate heat. On the other hand, in cases where the partition wall 5 is formed by a viscoelastic solid containing superparamagnetic particles, there is an advantage that no such heat will be generated. Since the ferromagnetic particles cause remnant magnetization, the former partition wall 5 using ferromagnetic particles has somewhat problems in response. On the other hand, since superparamagnetic particles does not almost or not at all cause remnant magnetization, the latter partition wall 5 using superparamagnetic particles has advantages that the response is superior to the former partition wall 5.
The present invention, however, does not require that the particle size of the magnetic particle falls within the aforementioned range.
The magnetic particle can have a spherical shape, a bar-shape, a needle-shape, or any other shape.
In this partition wall 5, when the value obtained by dividing the volume of the magnetic particles by the total volume of the magnetic particles and the viscoelastic solid is defined as the rate of content (volume content) of the magnetic particles in the partition wall 5, it is preferable that the rate of content falls within the range of 15 to 52 volume %. This rate of content can be calculated by [A/(A+B)]×100, where the volume of the magnetic particles is A and the volume of the viscoelastic solid is B.
By setting the rate of content within the aforementioned range, the elasticity and magnetism of the partition wall 5 each can be assuredly set to a value appropriate for changing the opening degree of the regulating hole 6. In detail, if the content is less than 15 volume %, the amount of the magnetic particles is too small, resulting in small deformation of the partition wall 5, which in turn may make it difficult to change the opening degree of the regulating hole 6. On the other hand, if the content exceeds 52 volume %, there is a possibility that the deformability of the partition wall 5 cannot follow the intensity of the magnetic field. This may cause breakage of the partition wall 5. The more preferable content range is 25 to 30 volume %. In the present invention, however, does not require that the rate of content falls within the aforementioned range.
In cases where the partition wall 5 is formed by silicone rubber (more specifically, silicone gel) containing carbonyl iron particles as the magnetic particles, an example of the preferable production method of the partition wall 5 will be as follows.
A mother liquid of silicone rubber, its hardening solution, and carbonyl iron particles falling within the rang of 1:0.1-1.5:1.3-8 in mass ratio are uniformly agitated and mixed with an agitation means, such as, e.g., an agitation mixer, while defoaming under reduced pressure. Thereafter, this mixture is poured into a molding cavity of a predetermined forming die. At this time, in the molding cavity, a thin rod-shaped core for forming a regulating hole disposed along the axial direction. As the material for the molding die, plastic, such as, e.g., acrylic resin, can be preferably used. It is especially preferable that the mixture ratio (i.e., compounding ratio) of the mother liquid of the silicone rubber, its hardening solution, and carbonyl iron particles falls within the range of 1:1:1.3-8 in mass ratio.
Next, the mixture in the molding cavity is heated to be hardened in the temperature range of, e.g., 30 to 70° C. with a heating means, such as, e.g., a hot-air heater. Thereafter, the hardened material is taken out from the molding cavity, and further subjected to a trimming work if needed. Thus, a partition wall 5 formed by silicone rubber containing carbonyl iron particles can be produced.
The magnetic field gradient generating means 7 is configured to generate magnetic field gradient in the radial direction (i.e., in the r-direction) in the tubular passage 3, and includes a coil (more specifically, an electromagnetic coil) 8 and a power source 9. This magnetic field gradient generating means 7 is configured to generate magnetic field gradient in the tubular passage 3 by the coil 8.
The coil 8 is formed into, e.g., a round shape. More specifically, the coil 8 is formed by, e.g., a finite-length solenoid coil. The coil 8 is disposed coaxially with the central axis of the tubular passage 3 so that the coil 8 circumferentially surrounds the partition wall 5 at the outside of the tubular passage 3 (i.e., at the outside of the tubular member 2). In other words, the tubular passage 3 and the partition wall 5 is disposed at the inside of the coil 8. The length of this coil 8 (more specifically, the axial direction of the coil 8) is set so as to fall within the range of, for example, 4 L to 8 L (L: the length of the partition wall 5). It should be noted, however, that the present invention does not require that the length of the coil 8 falls within this range.
The power supply 9 is configured to supply current to the coil 8, more specifically to supply direct current to the coil 8, and is connected to the coil 8. This power supply 9 is provided with a current regulating means 10, such as, e.g., a variable resistor, for regulating supply current to the coil 8. For example, it can supply direct current I falling within the range of 0 to 30 A. This current regulating means 10 can be considered as a means for changing the magnitude of the magnetic field gradient in the radial direction in the tubular passage 3.
Furthermore, the magnetic field gradient generating means is equipped with a copper coil holder 12 for holding the coil 8 and a cooling jacket 11 as a means for cooling the coil 8 and the coil holder 12.
The cooling jacket 11 has a cooling pipe 11a mounted on the outer periphery of the coil 8 and the outer periphery of the coil holder 12. It is configured to cool the coil 8 and the coil holder 12 by passing a cooling liquid, such as, e.g., water, through the cooling pipe 11a.
Next, the control method of the regulating hole 6 using the control device 1A for a regulating hole according to the first embodiment and the control principle will be explained.
Initially, direct current I is supplied to the coil 8 of the magnetic field gradient generating means 7 by the power supply 9. Then, as shown in
When the magnetic field gradient is generated, the force will work on a number of magnetic particles in the partition wall 5 in the direction of the magnetic field gradient (this force is called “Kelvin force”). This causes elastic deformation of the partition wall 5, which in turn causes accumulation of elastic restoring force in the partition wall 5. The deformation of the partition wall 5 will continue until the Kelvin force working on the magnetic particles and the elastic restoring force accumulated in the partition wall balance out. In accordance with the deformation of the partition wall 5, the opening degree (i.e., the opening area) of the regulating hole 6 changes.
The magnitude of the magnetic field gradient generated in the radial direction in the tubular passage 3 can be easily changed by increasing/decreasing the supply current I to the coil 8.
Now, the change of the opening degree of the regulating hole 6 will be explained with reference to
In the control device 1A shown in
On the other hand, in the control device 1A shown in
On the other hand, in the control device 1A shown in
As explained above, in the regulating hole control device 1A of the first embodiment, changing the magnitude of the magnetic field gradient in the radial direction in the tubular passage 3 by increasing/decreasing the supply current I to the coil 8 with the current regulating means 10 causes increase/decrease of the opening degree (opening area) of the regulating hole 6. This enables regulation of the flow rate or pressure of the fluid G passing through the tubular passage 3.
In the control method of the regulating hole 6 using the regulating hole control device 1A of the first embodiment, the opening degree of the regulating hole 6 is changed by generating the magnetic field gradient in the radial direction in the tubular passage 3. Therefore, even if the opening degree of the regulating hole 6 is changed repeatedly, almost no friction of the partition wall 5 will occur. Furthermore, the partition wall 5 is formed by a viscoelastic solid, which does not cause volatilization or vaporization. Therefore, the regulating hole 6 can be controlled over a long period of time.
Furthermore, the partition wall 5 formed by viscoelastic solid is easy to handle as compared with a partition wall formed by fluid, and the installation work of the partition wall 5 in the tubular passage 3 can be easily performed.
In the example shown
In the example shown in
In the example shown in
In the example shown in
In the example shown in
In the example shown in
In the example shown in
In this control device 1B, light passes through the tubular passage 3 of the tubular member 2 in the axial direction. Specifically, the tubular member 2 is a tubular member round in cross-section. The partition wall 5 is a round plate-shaped member transversely disposed in the tubular Passage 3. At the central portion of the partition wall 5, a regulating hole 6 for regulating the amount of light passing through the tubular passage 3 is formed so that it straightly penetrates in the axial direction. The cross-sectional shape of this regulating hole 6 is round. The control device 1B of the second embodiment controls the regulating hole 6. This regulating hole 6 functions as, for examples, an iris.
This control device 13 used as, for example, an aperture device of an image-taking apparatus, such as, e.g., camera. “20” denotes an object, and “21” denotes a screen, such as, e.g., a light-sensitive surface.
The control method of the regulating hole 6 using this control device 13 is the same as in the aforementioned first embodiment. The following is a brief explanation thereof.
Direct current is supplied to the coil 8 of the magnetic field gradient generating means 7 by the power source 9 to thereby generate the magnetic field gradient in the radial direction in the tubular passage 3. With this, the opening degree (opening area) of the regulating hole 6 of the partition wall 5 is increased, which in turn increases the amount of light which reaches the screen 21. On the other hand, when the supply current to the coil 8 is decreased, the opening degree of the regulating hole 6 will decrease, which in turn decreases the amount of light which reaches the screen 21.
As explained above, in this control device 13, the magnitude of the magnetic field gradient in the radial direction in the tubular passage 3 is changed by regulating the supply current to the coil 8 to thereby increase/decrease the opening degree of the regulating hole 6. Thus, the amount of light passing through the tubular passage 3 can be regulated.
Although several embodiments of the present invention were explained, the present invention is not limited to the aforementioned embodiments and allows various modifications.
For example, in the present invention, the current I to be supplied to the coil 8 of the magnetic field gradient generating means 7 can be, for example, alternating current (e.g., low frequency alternating current) or pulsating current, as well as direct current.
In the present invention, the method of controlling the supply current I to the coil 8 can be a method in which the control is performed by repeating On and Off operations of the current supply switch provided at the power source 9, etc., in a predetermined cycle, i.e., an on-off control method. Alternatively, the method can be a method in which the supply current I to the coil 8 is gradually increased or decreased in terms of time while alternatively repeating the increase and the decrease in a predetermined cycle, or any other methods.
In the present invention, the magnetic field gradient generating means 7 can be constituted by, other than the coil 8, for example, a permanent magnet or an electric magnet disposed at the outside of the tubular passage 3 (i.e., at the outside of the tubular member 2) which generates magnetic field gradient in the radial direction in the tubular passage 3. In this case, by approaching the permanent magnet or the electric magnet to, for example, the tubular passage 3, moving in the axial direction of the tubular passage 3, moving in the circumferential direction, or rotating, the opening degree of the regulating hole 6 can be increased/decreased.
Furthermore, in the present invention, the cross-sectional shape of the tubular passage 3 can be, other than a circular shape, for example, a polygonal shape, such as, e.g., a square shape or a hexagonal shape, or any other shape.
In the present invention, the magnetic particles can be contained in the viscoelastic solid in an evenly dispersed manner or unevenly dispersed manner.
Next, examples (experimental examples) performed experiments on whether the regulating hole control device according to the present invention can regulate the flow rate of fluid will be explained. It should be noted, however, that the present invention is not limited to these examples.
In this control device 1C, “51” denotes an electric motor, “52” denotes a speed controller, “53” denotes a ball screw, “54” denotes a piston rod, “55” denotes a connection plate, “56” denotes a cylinder, “57” denotes a supply tank, “58” denotes a flow regulating valve, “59” denotes a storage tank, “60” denotes an air compressor, “61” denotes a pressure indicator, “62” denotes a video camera, “63” denotes a monitor, “64” denotes a differential pressure sensor, and “65” denotes a controller for a cooling means for cooling the coil 8. The unit of the numerals shown in
The partition wall 5 was formed by a viscoelastic solid containing ferromagnetic particles having the following materials.
Magnetic particle: carbonyl iron particle (made by BASF, the brand name: “CM”)
Particle size of the magnetic particle: see Table 1
Particle density of the magnetic particles: 3.7×103 kg/m3
Magnetism of the magnetic particle: ferromagnetism
Shape of the magnetic particle: spherical shape
Viscoelastic solid: silicone gel (made by Dow Corning Toray Co., Ltd., the brand name: “SE1885A&B”)
Viscosity of the viscoelastic solid: 0.5 Pa·s
Density of the viscoelastic solid: 1.0×103 kg/m3
The aforementioned characteristics of the magnetic particle and the viscoelastic solid were measured at 25° C.
The partition wall 5 was produced by the following production method.
A mother liquid of silicone gel (brand name: “SE1885A”), its hardening solution (brand name: “SE1885B”), and carbonyl iron particles were uniformly agitated and mixed at the compounding ratio shown in Table 1 with an agitation mixer while defoaming under reduced pressure. Thereafter, this mixture was poured into a molding cavity of an acrylic forming die. At this time, in the molding cavity, a thin rod-shaped core for forming a regulating hole was disposed along the axial direction. Next, the mixture in the molding cavity was heated to be hardened in the temperature range of 30 to 70° C. with a hot-air heater. Thereafter, the hardened material was taken out from the molding cavity to thereby produce the desired partition wall 5.
In the partition wall 5 produced as mentioned above, the rate of content of carbonyl iron particles (unit: volume %) was shown in Table 1. The rate of content was calculated by [A/(A+B)]×100, where the volume of the carbonyl iron particles is A and the volume of silicone gel is B.
Partition walls 5 of Examples 1 to 7 shown in Table 1 were prepared. Each partition wall 5 was disposed in the tubular passage 3 of the control device 1C. Next, direct current I was supplied to the coil 8 of the magnetic field gradient generating means 7 within the range of 0 to 30 A, and the relationship between the representative magnetic field strength Hz* in the tubular passage 3 and the opening area S of the regulating hole 6 was measured. An example of the result is shown by a graph in
In
As shown in
Actually, while supplying air as fluid from the upstream side into the tubular passage 3 of the control device 1C, the supply current I to the coil 8 was increased and decreased. As a result, in each partition wall of all Examples shown in Table 1, the flow rate of air could be regulated, and further the pressure of the air could also be regulated. Also in the case of using water in place of air as fluid, in the same manner, the flow rate of water could be regulated and further the water pressure could also be regulated.
It should be understood that the terms and expressions used herein are used for explanation and have no intention to be used to construe in a limited manner, do not eliminate any equivalents of features shown and mentioned herein, and allow various modifications falling within the claimed scope of the present invention.
While the present invention may be embodied in many different forms, a number of illustrative embodiments are described herein with the understanding that the present disclosure is to be considered as providing examples of the principles of the invention and such examples are not intended to limit the invention to preferred embodiments described herein and/or illustrated herein.
While illustrative embodiments of the invention have been described herein, the present invention is not limited to the various preferred embodiments described herein, but includes any and all embodiments having equivalent elements, modifications, omissions, combinations (e.g., of aspects across various embodiments), adaptations and/or alterations as would be appreciated by those in the art based on the present disclosure. The limitations in the claims are to be interpreted broadly based on the language employed in the claims and not limited to examples described in the present specification or during the prosecution of the application, which examples are to be construed as non-exclusive.
The present invention can be applied to a control method for a regulating hole and a control device for a regulating hole for regulating the amount of light, the flow rate of fluid and the pressure of fluid passing through a tubular passage.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2006-111598 | Apr 2006 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2007/058380 | 4/11/2007 | WO | 00 | 10/21/2010 |