Patent Application
20130333521
The present invention relates to a method of controlling the rotational speed of an impeller, and particularly, to a novel improvement that prevents an impeller from being unnecessarily abraded and improves the cycle life of the impeller by increasing the rotational speed of the impeller when a load current value I of a motor rotationally driving the impeller is smaller than a predetermined threshold value I0.
In general, in an iron foundry and a steel foundry, a desulfurization treatment is performed between a pig iron making process and a steel making process so as to remove sulfur content (impurity element) causing embrittlement from molten iron. In the desulfurization treatment, a desulfurizing agent such as calcined lime, calcined soda, carbide, caustic soda, and hydrated lime is supplied to a container such as a ladle in which the molten iron is received and is mixed by an impeller (mixing blade) immersed in the molten iron in the container so as to promote the desulfurization reaction therein.
As a structure for performing the desulfurization treatment, for example, a structure disclosed in the Patent Document 1 below and the like may be exemplified. That is, in the structure of the related art, an overload reserve amount as a ratio between a heating amount of a current operation and a heating amount when the motor is operated at 100% is estimated from the load current value of the motor rotationally driving the impeller. Then, when the estimated overload reserve amount is smaller than a predetermined threshold value, the rotational speed of the impeller is decreased, so that the impeller is rotated at the maximum rotational speed in which the operation is not stopped due to the overload of the motor. This control is used to prevent the occurrence of defective desulfurization as much as possible by setting the rotational speed of the impeller 3 to a large value.
Further, determination of the rotational speed of the impeller based on an abrasion state empirically estimated from the usage count of the impeller is also carried out although this is a company technique not disclosed as a Patent Document.
Patent Document 1: JP 2003-82409 A
In the structure disclosed in Patent Document 1, since the impeller is rotated at the maximum rotational speed in which the operation is not stopped due to an overload of the motor, the impeller is rotated at the rotational speed greater than the necessary speed in accordance with the performance of the impeller. Further, even when the rotational speed of the impeller is determined based on the empirically estimated abrasion state, there is a tendency that the rotational speed is set to a large value in order to prevent the occurrence of defective desulfurization. Accordingly, in the above-described structures of the related art, the impeller may be unnecessarily abraded, so that the cycle life of the impeller is degraded.
The invention was devised to solve the above-described problems, and it is an object of the invention to provide a method of controlling the rotational speed of an impeller capable of preventing the impeller from being unnecessarily abraded and improving the cycle life of the impeller.
According to the invention, there is provided a method of controlling the rotational speed of an impeller which is used to control the rotational speed of an impeller when molten metal and a desulfurizing agent added to the molten metal are mixed by the impeller immersed in the molten metal, the method including: reading out a load current value I of a motor rotationally driving the impeller when the impeller is rotated at a predetermined set rotational speed X0; and increasing the rotational speed of the impeller so that the load current value I becomes equal to or larger than a threshold value I0 when it is determined that the load current value I is smaller than the predetermined threshold value I0.
According to the method of controlling the rotational speed of the impeller of the invention, a load current value I of a motor rotationally driving the impeller is read out when the impeller is rotated at a predetermined set rotational speed X0, and the rotational speed of the impeller is increased so that the load current value I becomes equal to or larger than a threshold value I0 when it is determined that the load current value I is smaller than the predetermined threshold value I0. Accordingly, since there is no need to set the rotational speed of the impeller to a large value from the first, operation at the appropriate rotational speed may be realized. Therefore, since it is possible to prevent the impeller from being unnecessarily abraded, the cycle life of the impeller may be improved.
Hereinafter, an embodiment of the invention will be described by referring to the drawings.
An impeller 3 (mixing blade) which is made of a refractory is immersed into the molten iron 2. A rotary shaft 3a is integrated with the impeller 3, and a motor 4 is connected to the end portion of the rotary shaft 3a. That is, the impeller 3 is rotationally driven by the operation of the motor 4. When the impeller 3 is rotationally driven, the molten iron 2 and the desulfurizing agent are mixed with each other, so that the desulfurization reaction is promoted.
Furthermore, the impeller 3 is used for plural charges, and is abraded with an increase in the number of times of use. Further, the impeller 3 and the motor 4 are supported by an elevation device (not illustrated) so as to be capable of moving up and down, and are moved down to a position where the impeller 3 is immersed in the molten iron 2 when performing the desulfurization treatment of the molten iron 2.
A control device 5 is connected to the motor 4. The control device 5 includes, for example, an inverter, a calculation device (computer), and the like, and controls the rotational speed of the impeller 3 by controlling the operation of the motor 4.
A current measuring device 6 and a storage device 7 are connected to the control device 5. The current measuring device 6 is used to measure the value of a current supplied to the motor 4, that is, a load current value I of the motor 4. The load current value I corresponds to the energy which is consumed to rotate the impeller 3 (the energy which is used by the impeller 3 to mix the molten iron 2 and the desulfurizing agent with each other), and is proportional to the resistance related to the rotation of the impeller 3 inside the molten iron 2 and the rotational speed of the impeller 3. The resistance related to the rotation of the impeller 3 decreases as the impeller 3 is abraded, that is, the mixing capability of the impeller 3 decreases. That is, the mixing capability of the impeller 3 can be checked by comparing the load current value I at the rotational speed serving as a set reference with a predetermined reference value.
The storage device 7 stores a predetermined set number X0 of rotations and a threshold value I0.
The control device 5 reads out a load current value I which is measured by the current measuring device 6 when the impeller 3 is rotated at the set rotational speed X0 stored in the storage device 7. In addition, the load current value I which is read out at this time is an average current value for a predetermined time.
Further, the control device 5 determines whether or not the read load current value I is smaller than the threshold value I0 stored in the storage device 7.
Furthermore, when the control device 5 determines that the load current value I is smaller than the threshold value I0, the control device 5 increases the rotational speed of the impeller 3 so that the load current value I becomes equal to or larger than the threshold value I0.
That is, when the control device 5 detects that the mixing capability of the impeller 3 does not reach a predetermined reference by the comparison between the load current value I and the threshold value I0, the control device 5 makes up for a decline in the mixing capability by increasing the rotational speed of the impeller 3. Accordingly, since there is no need to set the rotational speed of the impeller 3 to a large value from the first, the operation at the appropriate rotational speed may be realized. Therefore, since it is possible to prevent the impeller 3 from being unnecessarily abraded, the cycle life of the impeller 3 may be improved.
Here, the threshold value I0 is set to the lower limit value of the load current value I in which the defective desulfurization does not occur. That is, as described above, when the rotational speed of the impeller 3 is increased so that the load current value I becomes equal to or larger than the threshold value I0, the rotational speed of the impeller 3 may be set to the minimum rotational speed in which the defective desulfurization does not occur. Accordingly, the operation at the low rotational speed may be further reliably performed. In addition, such lower limit value depends on the desulfurization condition including the inner diameter of the ladle 1, the amount of the molten iron 2, the immersion depth of the impeller 3, and the capacity of the motor 4, but may be obtained by the comparison with the desulfurization efficiency while measuring the load current value I of the motor 4.
The control device 5 reads out the load current value I after a predetermined standby time elapses from the time when the rotational speed of the impeller 3 reaches the set rotational speed X0. This is because the determination precision of the mixing capability is improved by using the load current value I when the mixing state is stabilized at the set rotational speed X0.
Further, when the control device 5 determines that the load current value I is smaller than the threshold value I0, the control device 5 increases the rotational speed of the impeller 3 by a predetermined fixed value ΔX. This is because the abrasion of the impeller 3 is a gentle shift and the amount by which the load current value I is smaller than the threshold value I0 may be estimated in advance. In this way, since it is possible to simplify the calculation program by setting the increase amount to the fixed value ΔX, the equipment costs may be reduced.
Further, if the control device 5 increases the rotational speed of the impeller 3, the control device 5 updates the set rotational speed X0 stored in the storage device 7 to the increased rotational speed. If the set rotational speed X0 is fixed, there is a case where the mixing capability is determined by the rotational speed largely deviated from the appropriate rotational speed in response to the abrasion state at the time point when the impeller 3 is abraded. In this case, sufficient mixing may not be performed until the rotational speed reaches the appropriate rotational speed, which causes insufficient desulfurization. That is, since the set rotational speed X0 is updated, the effective mixing may be performed until the determination of the mixing capability ends, and hence the occurrence of insufficient desulfurization may be prevented.
In addition, when the impeller 3 is replaced, a reset signal is input to the control device 5 in response to, for example, the operation and the like of the operator. When the control device 5 detects the replacement of the impeller 3 based on the reset signal, the control device 5 resets the set rotational speed X0. In other words, the updated set rotational speed X0 is continuously used until the impeller 3 is replaced.
Next,
Next, the control device 5 determines whether or not the load current value I is smaller than the threshold value I0 stored in the storage device 7 (step S4). At this time, when it is determined that the load current value I is smaller than the threshold value I0, it is detected that the mixing capability of the impeller 3 is degraded due to the abrasion, and the rotational speed of the impeller 3 is increased so that the load current value I becomes equal to or larger than the threshold value I0 (step S5). In addition, since the amount by which the load current value I is smaller than the threshold value I0 may be estimated in advance, the increase amount in the rotational speed of the impeller 3 is set to a predetermined fixed value ΔX. Further, the threshold value I0 is set to the lower limit value of the load current value I in which the defective desulfurization does not occur, and the increased rotational speed becomes the small rotational speed in which the defective desulfurization does not occur in response to the abrasion state of the impeller 3 at the time point. When the rotational speed of the impeller 3 increases, the set rotational speed X0 stored in the storage device 7 is updated to the increased rotational speed by the control device 5 (step S6).
Here, when it is determined that the load current value I is equal to or larger than the threshold value I0, it is detected that the mixing capability of the impeller 3 reaches a predetermined reference, so that the mixing operation is maintained at the set rotational speed X0 (step S7). That is, the increasing of the rotational speed of the impeller 3 (step S5) and the updating of the set rotational speed X0 (step S6) are not performed.
This operation of controlling the rotational speed is repeatedly performed until a predetermined mixing time elapses from the time when the mixing using the impeller 3 starts. Further, the operation of controlling the rotational speed ends at the time point when the mixing time has elapsed. In addition, even when the operation of controlling the rotational speed ends, the set rotational speed X0 stored in the storage device 7 is maintained. That is, when the set rotational speed X0 is updated, the rotational speed of the impeller 3 is increased to the updated set rotational speed X0 immediately after the start of the mixing at the subsequent charge. The set rotational speed X0 is reset when the impeller 3 is replaced.
Next, an example will be described. The applicant performed a desulfurization treatment using a mechanical desulfurization device having the specification illustrated in Table 1 before the converter charging after ejecting stainless hot metal obtained by an electric furnace. The stainless hot metal was composed of iron and impurities and included Cr of 10 wt % to 30 wt %, Ni of 0 wt % to 20 wt %, carbon of 2 wt % to 4 wt %, and the remainder including Si, Cu, and Mo.
In addition, the respective setting values used in the control of the rotational speed of the impeller 3 of the embodiment were as below.
Initial value of set rotational speed X0: 70 rpm
Threshold value I0: 150 A
Fixed value ΔX: 10 rpm
Standby time: 3 minutes
Current measuring time: 10 seconds
Further, the applicant also performed a conventional desulfurization operation (desulfurization operation with empirically set rotational speed) as a comparative example. Then, the applicant respectively examined the transition of the rotational speed of the impeller 3, the desulfurization rate ((sulfur amount [wt %] before desulfurization−sulfur amount [wt %] after desulfurization)/sulfur amount [wt %] before desulfurization×100 [%]), and the cycle life of the impeller were examined in cases where the control of the rotational speed of the embodiment was performed and where the conventional desulfurization operation was performed.
First, the rotational speed of the impeller 3 will be illustrated.
Next, the examination results of the desulfurization rate and the cycle life of the impeller are illustrated in the following Table 2.
As illustrated in Table 2, compared to the average desulfurization rate of the desulfurization operation of the related art, the average desulfurization rate increases by 12.6% when performing the control of the rotational speed of the embodiment. This is because the satisfactory shape of the impeller 3 was maintained until the large usage count by setting the set rotational speed X0 of the impeller 3 to the minimum rotational speed in which the defective desulfurization does not occur. In addition, the average specific consumption of the desulfurizing agent illustrated in Table 2 indicates the average value of the used amount of the desulfurizing agent (kg—desulfurizing agent/Ton—hot metal) used in the desulfurization operation during a period in which one impeller is continuously used. Here, the desulfurization performance may be also changed in accordance with the amount of the desulfurizing agent used. However, since the average specific consumption of the desulfurizing agent in the operation of the present invention and the operation of the related art are the same, it is found that the improvement in the average desulfurization rate is not caused by the used amount of the desulfurizing agent.
Further, in the desulfurization operation of the related art, the impeller 3 needs to be replaced when the impeller 3 is used up to 184 CH. However, in the case of the control of the rotational speed of the present embodiment, the impeller 3 may be continuously used up to 271 CH. From this result, it is found that the desulfurization rate and the cycle life of the impeller may be improved by performing the control of the rotational speed of the present embodiment and hence an economic and effective desulfurization operation may be realized.
In the method of controlling the rotational speed of the impeller 3, the load current value I of the motor 4 rotationally driving the impeller 3 is read out when the impeller 3 rotates at the predetermined set rotational speed X0, and when it is determined that the load current value I is smaller than the predetermined threshold value I0, the rotational speed of the impeller 3 is increased so that the load current value I becomes equal to or larger than the threshold value I0. Accordingly, since there is no need to set the rotational speed of the impeller 3 to a large value from the first, operation at the appropriate rotational speed may be realized. Therefore, the impeller 3 may be prevented from being unnecessarily abraded, and the cycle life of the impeller 3 may be improved.
Further, since the threshold value I0 is the lower limit value of the load current value I in which the defective desulfurization does not occur, the rotational speed of the impeller 3 may be set to the minimum rotational speed in which the defective desulfurization does not occur, and hence operation at the smaller rotational speed may be further reliably performed.
Furthermore, since the load current value I is read out after it is determined that the predetermined standby time has elapsed from the time when the rotational speed of the impeller 3 reaches the set rotational speed X0, the load current value I when the mixing state is stabilized at the set rotational speed X0 may be used, and hence the determination precision of the mixing capability may be improved.
Further, since the amount of increase of the rotational speed is the predetermined fixed value ΔX, the calculation program may be simplified, and hence the equipment costs may be reduced.
Furthermore, the set rotational speed X0 is updated to the increased rotational speed when the rotational speed of the impeller 3 increases, the effective mixing may be performed until the determination of the mixing capability ends, and hence the occurrence of insufficient desulfurization may be prevented.
In addition, in the first embodiment, a case has been described in which the rotational speed of the impeller 3 is increased by the predetermined fixed value ΔX when it is determined that the load current value I is smaller than the threshold value I0, but the amount by which the rotational speed of the impeller 3 is increased may be determined based on the difference value between the load current value I and the threshold value I0. Specifically, the rotational speed of the impeller 3 is increased so that the difference value becomes 0. In this way, when the amount of increase is determined based on the difference value, the control of the rotational speed may be performed even more finely.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011-049827 | Mar 2011 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2012/055084 | 2/29/2012 | WO | 00 | 2/8/2013 |