Patent Application
20160340244
The present invention relates to a method of conditioning a gypsum calcination product, and particularly to a method for increasing the hemihydrate content of the calcination product.
Gypsum (calcium sulphate dihydrate) is available as a naturally-occurring raw material or as a synthetic by-product of flue gas desulphurisation. The manufacture of gypsum-containing products, such as plasterboard, typically comprises the following steps:
In general, the stucco formed through calcination comprises other phases in addition to calcium sulphate hemihydrate. In particular, the stucco may contain calcium sulphate anhydrite (CaSO4). This form of calcium sulphate has no chemically bound water molecules, and is undesirable because of its adverse effect on the setting time and/or water demand of the stucco slurry.
Therefore, it is desirable to reduce the level of calcium sulphate anhydrite in stucco.
Therefore, at its most general, the present invention may provide a conditioning treatment to increase the proportion of hemihydrate phase within a calcined stucco product. More particularly, the conditioning treatment comprises heat-treating a calcined product in a humid environment at a temperature below the calcination temperature.
It has been found that such a conditioning treatment may help to decrease the water demand of the stucco. Additionally, it has been found that the treatment may result in a reduced specific surface area of the stucco, which may help to decrease the overall setting time of the stucco slurry, while retaining the fluidity of the slurry in the early stages of the hydration process.
It has further been found that the presence of dihydrate particles within the stucco during the conditioning treatment may assist in reducing the levels of anhydrite particles. This is considered to be due to the release of chemically-bound water molecules from the dihydrate particles, these water molecules then being available to promote the transformation of anhydrite particles to hemihydrate particles. The presence of dihydrate particles within the stucco during the conditioning process is considered to promote a better distribution of humidity than other methods such as the introduction of steam into the stucco.
In particular, it has been found that the conversion of the anhydrite phase to hemihydrate may be promoted by maintaining a high bulk density of stucco particles during the conditioning treatment. This high degree of compaction is considered to help to promote the exchange of water molecules between particles.
Therefore, in a first aspect, the present invention may provide a method of conditioning stucco comprising the steps of:
Preferably, the bulk density of the stucco particles within the reaction vessel is at least 1.5 g/cm3, more preferably at least 2 g/cm3.
The high bulk density of the stucco particles is achieved by holding the particles statically within the reaction vessel. Previous methods of conditioning stucco (such as described in e.g. US2012/0060723 and US2011/0150750) required the stucco to be entrained in process gas, e.g. fluidised. Thus, the bulk density of the stucco was much lower than for the present invention e.g. around 0.7-0.9 g/cm3.
Typically, the conditioning time is at least 30 minutes, preferably at least one hour.
Typically, the treatment temperature is at least 130° C. In general, the pressure within the reaction vessel during the step of treating the stucco particles is less than 2 bar.
In general, the stucco particles supplied to the reaction vessel comprise calcium sulphate anhydrite. Typically, this is in the form of calcium sulphate anhydrite III, which is a soluble form of calcium sulphate anhydrite. Calcium sulphate anhydrite III may be present in an amount of up to 70 wt %. However, the calcium sulphate anhydrite III amount is preferably lower than 15 wt %. Typically, the calcium sulphate anhydrite amount is greater than 10 wt %.
Typically, the stucco particles supplied to the reaction vessel comprise calcium sulphate dihydrate in an amount greater than 3 wt %, preferably greater than 5 wt %. Typically, the amount of calcium sulphate dihydrate is less than 20 wt %, preferably less than 10 wt %.
The calcium sulphate dihydrate particles present in the stucco may result from incomplete calcination of the gypsum material (for example, through lower calcination times or temperatures). In an alternative example of the method of the invention, calcium sulphate dihydrate may be added separately to the calcined stucco.
Typically, the stucco is supplied to the reaction vessel in an amount to fill at least 80%, preferably 85% of the internal volume of the vessel. That is, the bulk volume of the stucco within the reaction vessel (including gaps between adjacent stucco particles) is at least 80% and preferably at least 85% of the internal volume of the vessel.
The invention will now be described by way of example only.
Gypsum (calcium sulphate dihydrate) was calcined in a calcination kettle at a temperature of 190° C. for about 1 hour. After calcining, further gypsum (calcium sulphate dihydrate) was added to the calcination product to provide a gypsum-enriched calcination product. This mixture was then transferred to a steam pressure vessel. The steam pressure vessel was sealed and placed in an oven at 130° C. for 4 hours to condition the stucco. After this treatment, the conditioned stucco was immediately placed into a metallic bucket and allowed to cool.
Table 1 shows the anhydrite and dihydrate contents, water demand and specific surface area of the gypsum-enriched calcination product before and after conditioning in the steam pressure vessel. Each example was prepared from a different grade of gypsum, the d50 value of each gypsum grade being indicated in the Table.
The specific surface area was measured through BET.
As shown by Table 1, the conditioning treatment decreases the levels of anhydrite and dihydrate in the stucco, and additionally decreases the water demand and the specific surface area.
Gypsum (calcium sulphate dihydrate) was calcined in a calcination kettle at a temperature of 190° C. for about 1 hour, to provide a calcination product. After calcining, further gypsum (calcium sulphate dihydrate) was added to the calcination product in an amount corresponding to 5 wt % of the calcination product, to provide a gypsum-enriched calcination product. This mixture was then transferred to a steam pressure vessel. The steam pressure vessel was sealed and placed in an oven for 2 hours to condition the stucco. After this treatment, the conditioned stucco was immediately placed into a metallic bucket and allowed to cool.
Table 2 shows the anhydrite and dihydrite contents, water demand and specific surface area of the conditioned stucco as a function of oven temperature. Corresponding parameters for the direct calcination product (that is, without gypsum enrichment) are also given, for reference.
The specific surface area was measured through BET.
Gypsum (calcium sulphate dihydrate) was calcined in a calcination kettle at a temperature of 190° C. for about 1 hour, to provide a calcination product. After calcining, further gypsum (calcium sulphate dihydrate) was added to the calcination product in an amount corresponding to 8 wt % of the direct calcination product, to provide a gypsum-enriched calcination product. This mixture was then transferred to a steam pressure vessel. The steam pressure vessel was sealed and placed in an oven at 130° C. to condition the stucco.
After this treatment, the conditioned stucco was immediately placed into a metallic bucket and allowed to cool.
Table 3 shows the anhydrite and dihydrite contents, water demand and specific surface area of the conditioned stucco as a function of conditioning time. Corresponding parameters for the direct calcination product (that is, without gypsum enrichment) are also given, for reference.
Gypsum (calcium sulphate dihydrate) was calcined in a calcination kettle at a temperature of 190° C. for about 1 hour, to provide a calcination product. After calcining, further gypsum (calcium sulphate dihydrate) was added to the calcination product to provide a gypsum-enriched calcination product. This mixture was then transferred to a steam pressure vessel. The steam pressure vessel was sealed and placed in an oven at 130° C. for 2 hours to condition the stucco. After this treatment, the conditioned stucco was immediately placed into a metallic bucket and allowed to cool.
Table 4 shows the anhydrite and dihydrite contents, water demand and specific surface area of the conditioned stucco as a function of the level of gypsum enrichment. Corresponding parameters for the direct calcination product (that is, without gypsum enrichment) are also given, for reference.
Gypsum (calcium sulphate dihydrate) was calcined in a calcination kettle at a temperature of 190° C. for about 1 hour, to provide a calcination product. After calcining, further gypsum (calcium sulphate dihydrate) was added to the calcination product to provide a gypsum-enriched calcination product. This mixture was then transferred to a steam pressure vessel. The steam pressure vessel was sealed and placed in an oven at 130° C. for 4 hours to condition the stucco. After this treatment, the conditioned stucco was immediately placed into a metallic bucket and allowed to cool.
Table 5 shows the anhydrite and dihydrite contents, water demand and specific surface area of the conditioned stucco as a function of extent to which the stream pressure vessel was filled with the gypsum-enriched calcination product. Corresponding parameters for the direct calcination product (that is, without gypsum enrichment) are also given, for reference.
Gypsum (calcium sulphate dihydrate) was calcined in a calcination kettle at a temperature of 190° C. for about 1 hour, to provide a calcination product. After calcining, further gypsum (calcium sulphate dihydrate) was added to the calcination product to provide a gypsum-enriched calcination product. This mixture was then transferred to a steam pressure vessel. The steam pressure vessel was sealed and placed in an oven at 130° C. for 1 hour to condition the stucco. After this treatment, the conditioned stucco was immediately placed into a metallic bucket and allowed to cool.
Table 6 shows the anhydrite and dihydrite contents, water demand and specific surface area of the conditioned stucco as a function of the pressure within the steam vessel. Corresponding parameters for the direct calcination product (that is, without gypsum enrichment) are also given, for reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| 14368008.0 | Jan 2014 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2015/050267 | 1/8/2015 | WO | 00 |