Method of decomposing flow

Abstract

An excellent method of decomposing flon is provided which can decompose flon economically with high decomposition efficiency without necessitating high temperature and high pressure by contacting a gas containing a flon with a catalyst at a condition of a temperature of not less than 200.degree. C. and space velocity of not over than 50,000 (hr.sup.-1).

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a method of treating flon, more particularly a method of decomposing flon.

2. Related Art Statement

Heretofore, flon is said to be a cause of worsening of the environment of the earth, because if it is discharged in the air it flows into the ozone layer and is decomposed by the ultraviolet ray from the sun to generate active chlorine atoms which destruct the ozone layer. Therefore, development of a technique of decomposing flon is earnestly desired, in addition to development of a substitute of flon.

Heretofore known techniques of decomposing flon are a pressurized combustion method of combusting and decomposing flon under pressure in a sealed vessel and a super critical water method of mixing an aqueous solution of flon with super pure water and reacting the same under a condition of a temperature of about 400.degree. C. and a pressure of about 360 atm.

In the pressurized combustion method, there is a problem in that the temperature and the pressure for the combustion have to be elevated above an usual condition of a temperature of about 800-900.degree. C. and an ambient pressure required for combusting usual substances, in order to improve decomposition efficiency. Meanwhile, in the super critical water method, there is a problem in that a very high investment cost is required for maintaining the high pressure condition.

SUMMARY OF THE INVENTION

An object of the present invention is to solve the above problems.

Another object of the present invention is to provide a method of decomposing flon which can decompose flon economically with a high decomposition efficiency at around the usual condition required for combusting usual substances.

In an effort of achieving the above objects, the inventors made man researches and experiments to accomplish the present invention.

The present invention is characterized by decomposing flon by contacting a gas containing a flon with a catalyst at a condition of a temperature of not less than 200.degree. C. and a space velocity of not over than 50,000 (hr.sup.-1).

The reason why the temperature is limited to not less than 200.degree. C. or higher is that the decomposition of flon by oxidation becomes insufficient at a temperature of less than 200.degree. C., as shown in the later described Example 1. Preferably, the decomposition is effected at a temperature of 400-600.degree. C. In this temperature range, the efficiency of decomposition of flon by oxidation reaches a peak. At temperatures above 600.degree. C., good decomposition efficiency can be obtained, however, improvement of the decomposition efficiency can not be expected and the cost of energy for elevating the decomposition temperature is vainly increased.

The reason why the space velocity (SV) is limited to not over than 50,000 (hr.sup.-1) is because the contacting time of the catalyst and the gas containing flon becomes insufficient, so that the decomposition efficiency is decreased, if the SV is over 50,000 (hr.sup.-1). Though the space velocity has no lower limit with no particular problem as regard the efficiency, the amount of the catalyst is vainly increased to increase the catalyst cost, if the space velocity is below 2,000 (hr.sup.-1). Therefore, the space velocity is preferably within a range of 2,000-20,000 (hr.sup.-1).

Types and shapes of the catalyst are not restricted to specific ones. However, the catalyst is preferably selected and used from the oxides of metals consisting of Pt, Rh, Pd, Ru, Mn, Cu, Cr, Fe, and mixtures thereof. In addition, use of a catalyst consisting of components A and B is effective, the component A being a single oxide of a metal selected from the group consisting of Zr, Ti, Al, W and Si or a complexed multi oxide of at least two metals selected from the group consisting of Zr, Ti, Al, W and Si, and the component B being a metal or metals selected from the group consisting of Pt, Rh, Pd, Ru, Mn, Cu, Cr and Fe, an oxide or oxides thereof. Especially, the use of the latter catalyst is preferable in that the catalyst per se has acidic property and exhibits a remarkable resistance to acid and can decompose and remove flon gas efficiently for a long period in the presence of Hf, HCl, etc., which are produced by decomposition of the flon gas.

If a carrier of ZrO.sub.2 -TiO.sub.2 or ZrO.sub.2 -TiO.sub.2 -Al.sub.2 O.sub.3 system of a large specific surface area of at least 10 m.sup.2 /g is used as a catalyst carrier, a high catalytic activity can be exhibited even at low temperatures as shown in the later described Examples, and a good property of decomposing and removing flon can be exhibited even at high space velocities. In addition, the catalyst carrier can be prepared so easily that it can be formed into any shape, such as, pellet, plate, cylinder, lattice, honeycomb or the like. Moreover, the catalyst carrier has distinguished mechanical and physical properties, such as crush strength, wear resistance, shutter strength and the like, so that it can be used stably for a long time.

Zr source material for preparing the catalyst carriers, such as, ZrO.sub.2 -TiO.sub.2 system carrier, can be selected from inorganic Zr compounds and organic Zr compounds. Preferable inorganic Zr compounds are, for example, zirconyl nitrate, zirconyl sulfate, zirconyl oxalate. Ti source material for preparing the catalyst carriers ZrO.sub.2 -TiO.sub.2, etc., can be selected from inorganic titanium compounds, such as, titanium chloride, titanium sulfate, and the like, and organic titanium compounds, such as, titanium oxalate, tetraisopropyl titanate, and the like.

Shape of the catalyst carrier is not restricted to specific ones. Integral honeycomb structural bodies having an equivalent diameter of throughholes of not over than 30 mm and an open porosity of not less than 50%, are particularly preferable. This is because the honeycomb structural bodies can decrease the pressure loss of the catalyst carriers and achieve high decomposition efficiencies even at high space velocities. However, if the equivalent diameter of the throughholes exceeds 30 mm, the efficiency of removing flon is decreased. Also, if the open porosity is less than 50%, the pressure loss of the catalyst carriers becomes high.

As a decomposing aid, use of CH.sub.4 or H.sub.2 O is effective. The present invention is not especially restricted to the use and the type of the decomposing aid. However, if the content of flon in the flon containing gas is high, injection of CH.sub.4, H.sub.2 O, or C.sub.6 H.sub.6, etc., is effective in decomposing flon.

BRIEF DESCRIPTION OF THE DRAWINGS

For a better understanding of the present invention, reference is made to the accompanying drawings, in which:

FIG. 1 is a flow sheet of an embodiment of the process for carrying out the present invention into effect;

FIG. 2 is a graph of characteristic curves showing relations between treating temperature and decomposition percentage of flon taking space velocity as a parameter; and

FIG. 3 is a graph showing relations between use time of various catalysts and decomposition percentage.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Hereinafter, the present invention will be explained in more detail with reference Examples.

EXAMPLE 1

Using an experimental apparatus of the flow sheet as shown in FIG. 1 and a finished catalyst prepared by supporting Pt on a honeycomb shaped carrier composed of a complexed oxides of Zr:Ti=8.5:1.5 (mole ratio) and having a pore opening of 2.0 mm and a partition wall thickness of 0.4 mm in an amount of 1.5 g of Pt per 1 l of the carrier, decomposition of an exhaust gas containing flon R113 is effected under the conditions as shown in the following Table 1 to obtain the results as shown in Table 1.

Relation between the treating temperature and the decomposition percentage is shown in FIG. 2.

As seen from Table 1 and FIG. 2, good decomposition percentage can be obtained, if the treating temperature is not less than 200.degree. C. and the space velocity SV is not over 50,000 (hr.sup.-).

TABLE 1______________________________________ Flon R113 Decompo- Tem- concen- sition per- Cata- tration percent- ature lyst SV at inlet age Evalu-No. .degree.C. type (hr.sup.-1) (ppm) (%) ation______________________________________ 1 200 metal 2,500 500 84 .largecircle. 2 300 metal 2,500 500 93 .circleincircle. 3 400 metal 2,500 500 98 .circleincircle. 4 500 metal 2,500 500 99 .circleincircle. 5 600 metal 2,500 500 99+ .circleincircle. 6 700 metal 2,500 500 99+ .circleincircle. 7 200 metal 15,000 500 74 .DELTA. 8 300 metal 15,000 500 89 .largecircle. 9 400 metal 15,000 500 94 .circleincircle.10 500 metal 15,000 500 97 .circleincircle.11 600 metal 15,000 500 98 .circleincircle.12 700 metal 15,000 500 99 .circleincircle.13 200 metal 45,000 500 70 .DELTA.14 300 metal 45,000 500 78 .DELTA.15 400 metal 45,000 500 83 .largecircle.16 500 metal 45,000 500 87 .largecircle.17 600 metal 45,000 500 89 .largecircle.18 700 metal 45,000 500 90 .circleincircle.19 200 metal 60,000 500 30 X20 300 metal 60,000 500 44 X21 400 metal 60,000 500 54 X22 500 metal 60,000 500 61 X23 600 metal 60,000 500 67 X24 700 metal 60,000 500 72 .DELTA.25 500 metal 2,500 2,000 99+ .circleincircle.26 500 metal 15,000 2,000 99+ .circleincircle.27 500 metal 2,500 5,000 99+ .circleincircle.28 500 metal 15,000 5,000 99+ .circleincircle.______________________________________[Decomposition percentage] [Evaluation]90% + .circleincircle.80.about.89% .largecircle.70.about.79% .DELTA.69% - X

EXAMPLE 2

Decomposition tests of an exhaust gas containing flon R113 are effected under the following condition to obtain the results as shown in Table 2 below.

(Condition) Gas composition: 500 ppm of flon R113, the rest of air Space velocity: 2,500 hr.sup.-1 Temperature: 500.degree. C. Catalyst type:

Catalyst A: Pt

Catalyst B: Pt+Rh+Pd

Catalyst C: Pt+Rh+Pd+Ru+Mn+Cu

Catalyst D: Pt+Rh+Pd+Ru+Mn+Cu+Cr+Fe

Catalyst E: Ni

Catalyst F: Ce

Catalyst G: V

Amount of the catalyst total 1.5 g/carrier 1 l

TABLE 2______________________________________ Temper- Decomposition ature Catalyst SV percentage Evalu-No. .degree.C. type (hr.sup.-1) (%) ation______________________________________1 500 A 2,500 99 .circleincircle.2 500 B 2,500 99+ .circleincircle.3 500 C 2,500 99+ .circleincircle.4 500 D 2,500 99+ .circleincircle.5 500 E 2,500 10 X6 500 F 2,500 14 X7 500 G 2,500 8 X______________________________________

As seen from Table 2, good decomposition percentages can be obtained by the use of the catalyst selected from Pt, Rh, Pd, Ru, Mn, Cu, Cr and Fe.

EXAMPLE 3

Using a honeycomb shaped body supporting Pt (1.5 g/1 l of carrier), decomposition tests of an exhaust gas containing flon R113 are effected under the following condition to obtain the results as shown in FIG. 3.

(Condition) Gas composition: 500 ppm of flon R113, the rest of air Space velocity: 2,500 hr.sup.-1 Temperature: 500.degree. C. Carrier

Carrier A: Zr: Ti=7:3 (mole ratio)

Carrier B: Ti: Si=7:3 (mole ratio)

Carrier C: mullite type

Carrier D: cordierite type

Carrier E: zeolite

As seen from FIG. 3, the catalyst can withstand use for a long period, if a carrier is used which is not deteriorated easily by fluoric acid, hydrochloric acid, and the like which are generated after the decomposition of the flon substance.

EXAMPLE 4

Using a honeycomb shaped body as the carrier for the catalyst, decomposition tests of an exhaust gas are effected under the following conditions to obtain the results as shown in FIG. 3.

(Condition) Gas composition: 500 ppm of flon R113, the rest of air Space velocity: 2,500 hr.sup.-1 Temperature: 500.degree. C. TABLE 3______________________________________ Equivalent Decompo- diameter of sition through Open Pressure percent- holes porosity loss age Evalu-No. (mm) (%) (mmH.sub.2 O) (%) ation______________________________________1 1.6 64 15 99 .largecircle.2 2.0 69 18 99 .largecircle.3 2.0 51 34 87 .largecircle.4 2.0 44 293 71 X5 5.0 67 16 91 .largecircle.6 5.0 51 74 82 .largecircle.7 5.0 39 240 63 X8 15 62 13 83 .largecircle.9 15 51 64 74 .largecircle.10 15 42 163 61 X11 30 73 11 78 .largecircle.12 30 56 95 70 .largecircle.13 50 69 8 52 X______________________________________ [Evaluation]- X Decomposition percentage is less than 70% or pressure loss is 150 mmH.sub.2 O or higher .largecircle. Decomposition percentage is 79% or higher and the pressure loss is less than 150 mmH.sub.2 O

As seen from Table 3, if a honeycomb shaped body having an equivalent diameter of throughholes of not over than 30 mm and an open porosity of not less than 50% is used as the catalyst carrier, good decomposition percentages can be obtained with low pressure loss.

As clearly apparent from the foregoing explanations, the present invention does not necessitate the condition of high temperature and high pressure and can decompose flon economically with high decomposition efficiency at around a condition of combusting usual substances, so that the energy cost can be reduced considerably and a high cost expensive apparatus can be dispensed with.

Accordingly, the present invention obviates the prior problems and contributes in a great deal to the development of the industry.

Although the present invention has been explained with specific examples and numeral values, it is of course apparent to those skilled in the art that various changes and modifications thereof are possible without departing from the broad spirit and aspect of the present invention as defined in the appended claims.

Claims

1. A method of decomposing flon, comprising contacting a gas containing flon with a catalyst at a temperature of 200-700.degree. C. and a space velocity of 2,000 to 50,000 (hr.sup.-1), the catalyst being selected from the group consisting of Rh, Pd, Mn, and Cu and an oxide or oxides thereof.

2. The method of claim 1, wherein the catalyst uses a carrier of an integral honeycomb type structural body having an equivalent diameter of throughholes of 30 mm or less and an open porosity of not less than 50% .

3. The method of claim 1, wherein the temperature is 400-600.degree. C.

4. The method of claim 1, wherein the space velocity is 2,000-20,000 (hr.sup.-1).

5. The method of claim 1, wherein the catalyst uses a carrier of a specific surface area of at least 10 m.sup.2 /g selected from the group consisting of ZrO.sub.2 -TiO.sub.2 and ZrO.sub.2 -TiO.sub.2 -Al.sub.2 O.sub.3.

6. A method of decomposing flon, comprising contracting a gas containing flon with a catalyst at a temperature of 200-700.degree. C. and a space velocity of 2,000-50,000 (hr.sup.-1), the catalyst consisting of components A and B, the component A being a single oxide of a metal selected from the group consisting of Zr, Ti, and W or a complexed multi oxide of at least two metals selected from the group consisting of Zr, Ti, Al, W and Si, and the component B being a metal or metals selected from the group consisting of Pt, Rh, Pd, Ru, Mn, Cu, Cr, and Fe, and an oxide or oxides thereof.

7. The method of claim 6, wherein the catalyst uses a carrier of a specific surface area of at least 10 m.sup.2 /g selected from the group consisting of ZrO.sub.2 -TiO.sub.2 and ZrO.sub.2 -TiO.sub.2 -Al.sub.2 O.sub.3.

8. The method of claim 6, wherein the catalyst uses a carrier of an integral honeycomb type structural body having an equivalent diameter of throughholes of 30 mm or less and an open porosity of not less than 50%.

9. The method of claim 6, wherein the temperature is 400-600.degree. C.