This invention relates to the processing of lignin and related phenolic polymers into their constituent monomers and oligomers to provide commercially useful small molecules.
Lignin is a class of naturally-occurring phenolic polymers that form structural materials in the supporting tissues of plants and algae. The degree of polymerisation is difficult to measure, since the material is heterogeneous. The polymers are made up of cross-linked coumaryl alcohol, coniferyl alcohol and sinapyl alcohol monomers, among other components. Lignin also contains large quantities of the commercially important compound, vanillin. Around 12,000 tons of vanillin are consumed globally per annum, 80% of which is obtained from petrochemical sources, and the remaining 20% produced from lignosulphonates.
Lignin is an attractive source of functionalised aromatic chemicals because it is relatively abundant, renewable, environmentally benign, and is currently produced in large quantities as part of agroforestry and agricultural waste. Its valorisation through depolymerisation has attracted significant attention as this offers a solution to the growing global demands for fuels and chemicals, which are currently being met through the utilisation of non-renewable petroleum feedstocks.
Structurally lignin is a complex crosslinked phenolic polymer with robust C—C and C—O bonds, which makes its depolymerisation into low molar mass aromatic monomers and oligomers a challenge. Harsh reaction conditions including extreme pH, temperature and pressure conditions, which require complicated experimental setups are thus often implemented. These extreme conditions pose severe challenges in lignin depolymerisation, which include poor selectivity and low yield. In addition, reaction media tend to be highly corrosive which poses significant waste disposal challenges.
Milder alternatives include depolymerisation using nitrobenzene, oxygen and metal oxide oxidising agents. These are widely referred to as mild oxidising agents because they can depolymerise lignin while preserving the aromatic structures of its constituent monomers to produce aldehyde functionalised aromatic compounds. While nitrobenzene can be an effective oxidant, its use often results in the formation of toxic nitrobenzene side-products such as azobenzene, 4-(phenylazo)-phenol and azoxybenzene. Nitrobenzene is also known to be carcinogenic and is therefore undesirable to handle.
Oxygen is a relatively inexpensive oxidant that is known to convert lignin to aldehydes. An advantage of using oxygen as an oxidant is that it does not require additional toxic chemicals for the reaction to proceed. However, yields tend to be low and elevated temperatures and pressure may be required to obtain satisfactory results. Furthermore, the use of oxygen without a catalyst frequently causes over oxidation, poor selectivity towards aromatic monomers and a significantly reduced level of conversion to desired products. Over oxidation leads to repolymerisation and/or the formation of undesirable gaseous compounds.
There is therefore a need for an efficient and selective method of depolymerising phenolic polymers and, more specifically, lignin in a manner which is environmentally benign and addresses some of the aforementioned challenges, at least to some extent.
The preceding discussion of the background to the invention is intended only to facilitate an understanding of the present invention. It should be appreciated that the discussion is not an acknowledgment or admission that any of the material referred to was part of the common general knowledge in the art as at the priority date of this application.
In accordance with a first aspect of this invention, there is provided a method for depolymerising a phenolic polymer, the method comprising reacting the phenolic polymer with dimethylsulphoxide (DMSO) and a hydrogen halide.
The phenolic polymer may be selected from the group consisting of lignin and derivatives thereof.
The hydrogen halide may be selected from the group consisting of HF, HCl, HBr and HI. The hydrogen halide may be HBr. The quantity of hydrogen halide per gram of phenolic polymer may be from 0.001 mmoles to 10,000 mmoles, from 0.01 mmoles to 1,000 mmoles, from 0.1 mmoles to 500 mmoles, from 1 mmole to 200 mmoles, from 10 mmoles to 100 mmoles, or from 30 mmoles to 70 mmoles.
The quantity of DMSO per gram of phenolic polymer may be from 0.001 mmoles to 10 moles, from 0.01 mmoles to 5 moles, from 0.01 mmoles to 1 mole, from 0.1 mmoles to 1 mole, from 1 mmole to 1 mole, from 10 mmoles to 1 mole, or from 0.1 mole to 1 mole.
The reaction may be performed at a temperature of from 20° C. to 200° C., from 80° C. to 150° C., or from 100° C. to 120° C. The reaction may be carried out for between 1 h and 120 h, for between 2 h and 24 h, for between 6 h and 18 h, or for between 10 h and 14 h.
The reaction may be carried out at a pressure within a range from about 101 kPa to about 500 kPa. The reaction may be carried out at atmospheric pressure.
The method may include isolating a product of the reaction. The product may be isolated at least in part by vacuum distillation. The vacuum distillation may be performed at one or more temperatures between 60° C. and 250° C., or between 100° C. and 180° C. The vacuum distillation may be performed at a pressure approximating a substantially complete vacuum, at least for practical purposes. The distillation pressure may be between 0 kPa and 50 kPa.
The product of the reaction may comprise at least one compound selected from the group consisting of monomeric and oligomeric forms of vanillin, syringaldehyde, benzaldehyde, p-hydroxybenzaldehyde, eugenol, phenol, guaiacol, phloroglucinol, 2,4-dihydroxybenzaldehyde, and aromatic hydrocarbons. The aromatic hydrocarbons may be selected from the group consisting of benzene, toluene, xylenes, and other aryl alkanes.
The product of the reaction may comprise vanillin.
In accordance with a second aspect of this invention, there is provided a method of producing an aromatic compound from a phenolic polymer, the method comprising reacting the phenolic polymer with dimethylsulphoxide (DMSO) and a hydrogen halide to form a reaction mixture, and isolating the aromatic compound from the reaction mixture.
The phenolic polymer may be selected from the group consisting of lignin and derivatives thereof.
The aromatic compound may be selected from the group consisting of monomeric and oligomeric forms of vanillin, syringaldehyde, benzaldehyde, p-hydroxybenzaldehyde, eugenol, phenol, guaiacol, phloroglucinol, 2,4-dihydroxybenzaldehyde, and aromatic hydrocarbons. The aromatic hydrocarbons may be selected from the group consisting of benzene, toluene, xylenes, and other aryl alkanes.
The aromatic compound may comprise vanillin.
The hydrogen halide may be selected from the group consisting of HF, HCl, HBr and HI. The hydrogen halide may be HBr.
The quantity of hydrogen halide per gram of phenolic polymer may be from 0.001 mmoles to 10,000 mmoles, from 0.01 mmoles to 1,000 mmoles, from 0.1 mmoles to 500 mmoles, from 1 mmole to 200 mmoles, from 10 mmoles to 100 mmoles, or from 30 mmoles to 70 mmoles.
The quantity of DMSO per gram of phenolic polymer may be from 0.001 mmoles to 10 moles, from 0.01 mmoles to 5 moles, from 0.01 mmoles to 1 mole, from 0.1 mmoles to 1 mole, from 1 mmole to 1 mole, from 10 mmoles to 1 mole, or from 0.1 mole to 1 mole.
The reaction may be performed at a temperature of from 20° C. to 200° C., from 80° C. to 150° C., or from 100° C. to 120° C. The reaction may be carried out for between 1 h and 120 h, for between 2 h and 24 h, for between 6 h and 18 h, or for between 10 h and 14 h.
The reaction may be carried out at a pressure within a range from about 101 kPa to about 500 kPa. The reaction may be carried out at atmospheric pressure.
The compound may be isolated at least in part by vacuum distillation. The vacuum distillation may be performed at one or more temperatures between 60° C. and 250° C., or between 100° C. and 180° C. The vacuum distillation may be performed at a pressure approximating a substantially complete vacuum, at least for practical purposes. The distillation pressure may be between 0 kPa and 50 kPa.
In accordance with a third aspect of this invention, there is provided a method of producing vanillin from lignin, the method comprising reacting the lignin with dimethylsulphoxide (DMSO) and a hydrogen halide to form a reaction mixture, and isolating vanillin from the reaction mixture.
The hydrogen halide may be selected from the group consisting of HF, HCl, HBr and HI. The hydrogen halide may be HBr. The quantity of hydrogen halide per gram of lignin may be from 0.001 mmole to 10,000 mmoles, from 0.01 mmoles to 1,000 mmoles, from 0.1 mmoles to 500 mmoles, from 1 mmole to 200 mmoles, from 10 mmoles to 100 mmoles, or from 30 mmoles to 70 mmoles.
The quantity of DMSO per gram of lignin may be from 0.001 mmoles to 10 moles, from 0.01 mmoles to 5 moles, from 0.01 mmoles to 1 mole, from 0.1 mmoles to 1 mole, from 1 mmole to 1 mole, from 10 mmoles to 1 mole, or from 0.1 mole to 1 mole.
The reaction may be performed at a temperature of from 20° C. to 200° C., from 80° C. to 150° C., or from 100° C. to 120° C. The reaction may be carried out for between 1 h and 120 h, for between 2 h and 24 h, for between 6 h and 18 h, or for between 10 h and 14 h.
The reaction may be carried out at a pressure within a range from about 101 kPa to about 500 kPa. The reaction may be carried out at atmospheric pressure.
The vanillin may be isolated at least in part by vacuum distillation. The vacuum distillation may be performed at a temperature of between 170° C. and 200° C., or between 175° C. and 185° C. The vacuum distillation may be performed at a pressure approximating a substantially complete vacuum, at least for practical purposes. The distillation pressure may be between 0 kPa and 50 kPa.
Certain modes of performing the invention will now be described, by way of example only, with reference to the accompanying figures.
In the figures:
The invention provides a method of depolymerising a phenolic polymer, such as lignin, into its constituent monomers and/or oligomers under mild oxidising conditions using a combination of DMSO and hydrogen halide. The method provides a means of obtaining these compounds from lignocellulosic biomass, technical lignins, lignin residue, agricultural waste and/or agroforestry waste, instead of from petrochemicals from which they are traditionally obtained.
The term “lignin” as used herein refers to any lignin or lignin derivative including but not limited to technical lignins such as kraft lignin, softwood kraft lignin, hardwood kraft lignin, Brauns' lignin, cellulolytic enzyme lignin, dioxane acidolysis lignin, Klason lignin, milled wood lignin, periodate lignin, lignosulphates, lignosulphonates, organosolv lignin, steam explosion lignin, lignocellulosic biomass, and lignin residue. It also refers to any substances made in whole or in part from lignin or subunits of lignin.
As used herein, the term “lignosulphonate” refers to a sulphonated lignin, which is a water-soluble anionic polyelectrolyte polymer typically produced as a byproduct of the sulphite process used in wood pulp manufacturing. Sulphite pulping removes lignin from wood particles to form lignosulphonate and substantially pure cellulose wood pulp.
“Kraft lignin” refers to lignin produced as a byproduct of the Kraft process for producing wood pulp. The Kraft process involves treating wood chips with a hot mixture of water, sodium hydroxide (NaOH) and sodium sulphide (Na2S), which breaks the bonds that link lignin, hemicellulose and cellulose.
“Lignin residue” refers to lignin that is produced as a by-product from biomass, agricultural and/or agroforestry waste processing or any lignin depolymerisation process. The production of the lignin residue may include but is not limited to enzymatic, oxidative or acid/base catalyzed protocols.
The term “oligomer” will be understood to refer to a molecule of intermediate relative molar mass, the structure of which essentially comprises a small plurality of units derived, actually or conceptually, from molecules of lower relative molar mass. A molecule is regarded as having an intermediate relative molar mass if it has properties which do vary significantly with the removal of one or a few of the units. If a part or the whole of the molecule has an intermediate relative molar mass and essentially comprises a small plurality of units derived, actually or conceptually, from molecules of lower relative molar mass, it may be described as oligomeric, or as an oligomer. An oligomer is essentially a molecular complex that includes a limited number of monomer units, such as from 2 to 8 or from 2 to 5 monomer units. In the case of lignin, these monomers tend to be derivatives of phenol. The molar mass of these oligomers may be less than 2000 g/mol as determined from techniques usually used in the field, e.g. size exclusion chromatography.
The term “phenolic” is understood to refer to molecules which include phenol or a derivative thereof in their molecular structure, or which are derived from phenol-containing molecules. Examples of phenolic compounds include lignin, vanillin, syringaldehyde, p-hydroxybenzaldehyde, eugenol, phenol, guaiacol, phloroglucinol and 2,4-dihydroxybenzaldehyde.
Throughout this specification, certain embodiments are described in a range format. It should be understood that the description in range format should not be construed as an inflexible limitation on the scope of the disclosed ranges. Accordingly, ranges are to be interpreted as disclosing all possible sub-ranges and individual numerical values within the range, and to be inclusive of the stated lower and upper bounds of the range. A description of a range of from 1 to 6 should be considered as specifically disclosing sub-ranges such as from 1 to 3, from 1 to 4, from 1 to 5, from 2 to 4, from 2 to 6, from 3 to 6, etc., as well as individual numbers within that range, i.e. 1, 2, 3, 4, 5, and 6. A description of a range of temperatures between 170° C. and 200° C. should be considered as specifically disclosing the upper and lower bounding temperatures (i.e. 170° C. and 200° C.) as well as all possible sub-ranges and individual numerical values within that range.
Throughout the specification and claims unless the context requires otherwise the word “comprise” or variations such as “comprises” or “comprising” will be understood to imply the inclusion of a stated integer or group of integers but not the exclusion of any other integer or group of integers.
The method includes reacting the phenolic polymer with dimethylsulphoxide (DMSO) and a hydrogen halide. The polymer, DMSO and hydrogen halide form a reaction mixture which is typically heated for a defined period of time at a specific temperature or temperature range. The DMSO acts as a mild oxidising agent and solvent, while the hydrogen halide acts as a Brønsted acid catalyst for the reaction. There are several advantages of using this DMSO-based oxidation system which include (1) DMSO is a selective reagent, (2) it is a mild reagent, (3) there is no over oxidation of primary alcohols to carboxylic acids i.e. the oxidation of primary alcohols gives aldehydes, (4) it is a very good solvent for lignin, (5) it is commercially available as well as relatively inexpensive, and (6) it is relatively non-toxic and environmentally friendly in comparison to some other metal-based oxidation systems.
The quantity of DMSO per gram of phenolic polymer in the reaction can be from 0.001 mmoles to 10 moles, from 0.01 mmoles to 5 moles, from 0.01 mmoles to 1 mole, from 0.1 mmoles to 1 mole, from 1 mmole to 1 mole, from 10 mmoles to 1 mole, or from 0.1 mole to 1 mole.
The hydrogen halide can be selected from hydrogen fluoride (HF), hydrogen chloride (HCl), hydrogen bromide (HBr) and hydrogen iodide (HI). In some embodiments, the hydrogen halide is HBr. The quantity of the hydrogen halide per gram of phenolic polymer in the reaction can be from 0.001 mmoles to 10,000 mmoles, from 0.01 mmoles to 1,000 mmoles, from 0.1 mmoles to 500 mmoles, from 1 mmole to 200 mmoles, from 10 mmoles to 100 mmoles, or from 30 mmoles to 70 mmoles.
The reaction is typically carried out at a moderately elevated temperature and can be performed at a temperature of from 20° C. to 200° C., from 50° C. to 150° C., from 80° C. to 140° C., or from 100° C. to 120° C. The length of the reaction can vary depending on the temperature. Longer reaction times at higher temperatures result in greater conversion but can cause an increase in side product formation. Typically the reaction can be carried out for between 1 h and 120 h, for between 2 h and 48 h, for between 6 h and 24 h, or for between 10 h and 14 h. The pressure at which the depolymerisation is carried out may be in a range of between 101 kPa and 500 kPa. Said pressure may be atmospheric pressure.
The method may further include isolating one or more products of the reaction from the reaction mixture after the reaction is complete. The product may be a monomeric or oligomeric aromatic phenolic compound, such as vanillin, syringaldehyde, benzaldehyde, p-hydroxybenzaldehyde, eugenol, phenol, guaiacol or 2,4-dihydroxybenzaldehyde. The one or more products of the reaction may also comprise an aromatic hydrocarbon, e.g. benzene, toluene or xylenes. The product or products may be isolated by solvent extraction, chromatography (e.g. size exclusion chromatography, column chromatography, ion exchange chromatography, reversed phase chromatography, or normal phase chromatography), and/or distillation (e.g. simple distillation, fractional distillation or vacuum distillation).
Since the boiling point of the monomers and/or oligomers of phenolic polymers is relatively high (e.g. >180° C. for phenol), the product is preferably isolated at least in part by vacuum distillation so that the distillation temperature can be reduced. Vacuum distillation refers to distillation of a liquid under reduced pressure enabling it to boil at a lower temperature than at atmospheric pressure. This technique is capable of separating different compounds based on differences in their boiling points and can be used when the boiling point of a desired compound is difficult to achieve or will cause the compound to decompose. Lower distillation temperatures reduce the likelihood of degradation of the product. The vacuum distillation can be performed at one or more different temperatures, depending on how many products are isolated. Products having different boiling points can be collected at different temperatures, under vacuum (at approximately 0 kPa for example).
While the vacuum distillation can be performed at any suitable temperature, it is preferably done at a temperature of between 60° C. and 250° C., or between 100° C. and 180° C. For example, the product(s) can be distilled under vacuum at 100° C. to 130° C., 140° C. to 150° C., approximately 160° C. and/or approximately 180° C., and at a pressure ranging from approximately 0 kPa to 50kPa. Syringaldehyde and benzaldehyde can be collected at between 140° C. and 150° C.; eugenol can be collected at between 155° C. and 165° C., preferably at about 160° C.; and vanillin and/or p-hydroxybenzaldehyde can be collected at between 170° C. and 200° C., preferably between 175° C. and 185° C., or at about 180° C. Phloroglucinol, 2,4-dihydroxybenzaldehyde, phenol and guaiacol can be collected from an undistilled, high boiling point fraction of the reaction product. Aromatic hydrocarbons such as benzene, toluene, xylenes and aryl alkanes, can also be collected from the undistilled high boiling point fraction.
The phenolic polymer, DMSO or hydrogen halide may be at least partially dissolved in a solvent. The solvent may be selected from dimethyl acetamide (DMAC), dimethyl formamide (DMF), n-alkyl pyrrolidone (such as N-methyl-2-pyrrolidone (NMP)), acetone, acetonitrile, tetrahydrofuran, water, ethyl acetate, alkyl alcohols (such as methanol and ethanol), 2-pyrrolidone, ethylene carbonate, propylene carbonate, y-butyrolactone, caprolactam, y-valerolactone, dimethylbenzamide, diethylbenzamide, other dialkylacetamides, N-methyl-2-piperidone, 2-piperidone, other N-alkyl piperidones, the aforementioned solvents in combination with water e.g. water/methanol, water/DMSO, water/acetonitrile, water/THF in varying quantities and varying ratios.
The invention will now be described in further detail by way of the following non-limiting examples.
Alkaline lignin (Kraft lignin) with low sulphonate content and lignosulphonate were dried overnight in an oven at 105° C. to a constant mass, before depolymerisation. Dimethyl sulphoxide (DMSO, HPLC grade, 99.7%, Sigma-Aldrich, Poznan, Poland), hydrogen bromide (HBr, 48%, Sigma-Aldrich, St. Louis, USA), and hydrochloric acid (HCl, 32%, Merck, Darmstadt, Germany) were used as received.
Kraft lignin (0.2 g) was dissolved in DMSO (8 mL, 1.13×10−1 moles) in a round bottom flask, and a catalytic amount of HBr (1 mL, 8.8×10−3 moles) was added to the reaction mixture. The reaction flask was immersed in an oil bath set at 110° C., and the reaction mixture heated for 12 hrs. The reaction was then stopped by cooling to room temperature. The reaction was repeated using a lignosulphonate instead of Kraft lignin following the same procedure and under the same experimental conditions.
Kraft lignin (0.2 g) was dissolved in DMSO (8 mL, 1.13×10−1 moles) in a round bottom flask, and a catalytic amount of HCl (1 mL, 1.06×10−2 moles) was added to the reaction mixture. The reaction flask was immersed into an oil bath thermostated at 110° C., and the reaction mixture heated for 12 hrs. The reaction was then stopped by cooling to room temperature.
The extent of depolymerisation was determined gravimetrically using the equations below:
% of native lignin=(Weight of precipitated lignin/Initial weight of lignin)×100%
Conversion=100−% native lignin
An Agilent 1200 HPLC instrument (Agilent Technologies, Waldbronn, Germany) was used, comprising the following: autosampler, on-line degasser, quaternary pump unit and a thermostated column compartment set to 55° C. The detector used was an Agilent ultraviolet (UV) detector at a wavelength of 277 nm. Two 10 μm PSS GRAM columns (PSS Polymer Standards Service GmbH, Mainz, Germany) (with polyester copolymer as a stationary phase) with porosities of 100 Å and 1000 Å and a 10 μm guard column were used. The sample solvent and mobile phase was DMSO/H2O/LiBr (90:10:0.05 M respectively), and a flowrate of 0.4 mL/min was used. Calibration was carried out using narrow poly(styrene sulphonate) sodium salt (PSS Polymer Standards Service GmbH, Mainz, Germany) with peak maximum molar masses (Mp) ranging from 891 to 1 000 000 g/mol. PSS WinGPC Unichrom software (8.2) was used to acquire and process the data.
An Agilent 1100 refractive index (RI) detector was later added to the HPLC instrument because pullulan standards (PSS Polymer Standards Service GmbH, Mainz, Germany, having a peak molar mass (Mp) between 342 and 1 220 000 g/mol) which did not have UV chromophore were used to calibrate the columns. The pullulan standards were used because the lignosulphonate and most depolymerised products were eluting after the lowest poly(styrene sulphonate) sodium salt standard with peak molar mass (Mp) of 891 g/mol. All molar mass values are, therefore, calculated and reported as pullulan equivalents.
SEC analysis was used to investigate the oxidative depolymerisation of lignin. The following parameters that ensure optimum separation were considered: mobile phase composition, choice of stationary phase, operating temperature, and use of an electrolyte to disrupt non-covalent polymer-polymer and polymer-stationary phase interactions.
When solubility studies were carried out, it was found that Kraft lignin (with low sulphonate content) and lignosulphonate (with high sulphonate content) together with their respective products of depolymerisation, dissolved completely in a DMSO/H2O/LiBr (90:10% (v/v):0.05M) mobile phase, without the need for derivatisation. PSS GRAM columns were selected due to their compatibility with the mobile phase and polymer. Porosities of 100 Å and 1000 Å were selected for the columns in order to cover a wider separation range taking into account that depolymerisation of lignin would result in low molar mass compounds. All SEC measurements were carried out at a UV wavelength of 277 nm.
A comparison of the molar masses of the products of the DMSO/HBr and DMSO/HCl reactions shows that DMSO/HBr is a more effective system for depolymerising lignin than DMSO/HCl. The molar mass dispersity for the two systems decreased significantly after depolymerisation. Table 1 below provides a summary of the respective molar masses of the reaction products.
a Mn (g/mol)
b Mw (g/mol)
c Mp (g/mol)
d Ð
a Number average molar mass (Mn),
b weight average molar mass (Mw),
c peak molar mass (Mp),
d molar mass dispersity (Ð), measured using the SEC method described previously.
Table 2 tabulates the percentage conversions obtained for the DMSO/HBr system with lignin. The DMSO/HBr oxidation was also performed at a scaled-up quantity of 10 g lignin and showed a similar conversion rate to the 0.2 g reaction, indicating that the reaction is scalable.
The oxidative depolymerisation reaction was applied to a sample of lignosulphonate and the resulting SEC elution profile of the reaction product is illustrated in
a Mn (g/mol)
b Mw (g/mol)
c Mp (g/mol)
d Ð
a Number average molar mass (Mn),
b weight average molar mass (Mw),
c peak molar mass (Mp),
d molar mass dispersity (Ð)
In one example of the described DMSO/HBr reaction, the pH of the starting reaction and of the resultant crude product mixture were measured. The starting reagents had a pH of approximately 4 whilst the products of the reaction had a pH of between 6 and 8.
Gas chromatography-mass spectrometry (GC-MS) using electron impact (EI) ionisation was used to identify products of the oxidative depolymerisation reaction of lignin with DMSO/HBr of Example 1. These compounds are presented in Table 4 below:
Gas chromatography-mass spectrometry (GC-MS) and electrospray ionisation-mass spectrometry (ESI-MS) analyses were also performed to identify the products of the lignosulphonate depolymerisation reaction from Example IV. The products included guaiacol (E2), hydroxybenzaldehyde (E1), 1-(2-hydroxyphenyl)ethanone (E3), 2-methoxy-4-methylphenol (4-methylguaiacol) (E4), (E)-3-(4-hydroxyphenyl)prop-2-enal (4-hydroxyacinnamaldehyde (E8)), 4-hydroxy-3-methoxybenzaldehyde (vanillin) (E10), 3-phenylpropanal (E11), 3-methoxybenzaldehyde (E12), (E)-3-(4-hydroxy-3-methoxyphenyl)prop-2-enal (coniferaldehyde) (E14), 2-formyl-5-methoxyphenyl acetate (E16), ethyl 2-(4-hydroxy-3-methoxyphenyl)acetate (ethyl homovanillate) (E17), (Z)-3-(3,4,5-trimethoxyphenyl)prop-2-enal (3,5-trimethoxycinnamaldehyde) (E19), 2-hydroxy-4,4′-diethoxybenzophenone (E23), ethyl 4-methoxyphenyl isophthalate (E24) and 1-(4-(1-(4-hydroxy-3-methoxyphenyl)prop-1-en-2-yloxy)-3,5-dimethoxyphenyl)ethanone (E25). The chemical structures of these compounds as well as their characteristic m/z ratios and theoretical masses are shown in Table 5 below.
bM
am/z
am/z observed, [M + H]+ or [M + Na]+ or [M + K]+, Theoretical mass (M) b. The letter E before a number is used to denote structures obtained from ESI-MS
A summary of the products and their relative abundances are provided in Table 6 below.
The influence of the concentration of HBr catalyst used was investigated by varying the amount of catalyst added as follows: 0.001 moles, 0.003 moles, 0.009 moles, 0.020 moles, 0.050 moles and 0.100 moles, with the other reaction parameters having been kept constant as in Example 1, i.e. the amounts of DMSO and lignin, and the reaction time and temperature. Table 7 tabulates a selection of the parameters and conditions used for the study.
Size exclusion chromatography (SEC) was used to monitor the success of the depolymerisation reaction. A shift from lower to higher elution volumes would indicate that the chemical linkages in the high molar mass lignin were cleaved, and lower molar mass oligomeric and monomeric species formed. On the other hand, a shift towards lower elution volumes would indicate that unwanted recombination (condensation) reactions had occurred.
The results obtained indicated that the molar amount of 0.009 per 2 g of lignin and 0.113 moles of DMSO would be most suitable to effectively cleave lignin to its monomeric and/or oligomeric compounds.
While maintaining the quantities of reagents and other reaction conditions used in Example V of Table 7 above, the depolymerisation temperature was systematically varied as tabulated in Table 8.
As in the case of the study relating to HBr concentration, SEC was also used in the temperature study to monitor the success of the depolymerisation reaction, and the results are illustrated in
Although reaction temperatures of 80° C. and 90° C. already resulted in a shift towards lower molar mass species, the shift became enhanced at higher temperatures of 110° C. and 120° C. However, depolymerising lignin at even higher temperatures such 150° C. became less suitable owing to the bulk formation of char (solid carbonised material), which is insoluble in the mobile phase used for SEC.
The reaction products of the oxidative depolymerisation of lignin were distilled under vacuum and fractions collected at the following temperatures: 100-130° C., 140-150° C., 160° C. and 180° C. After all the fractions were collected they were quantified gravimetrically. The fraction that contained the undistilled product was also quantified gravimetrically. The percentage of recovered sample was calculated according to the following equation:
% of recovered sample=(weight of fraction/weight of crude product mixture)×100%
The quantity of material recovered at each temperature is shown in Table 9 below:
Syringaldehyde and benzaldehyde were isolated from the 140-150° C. fraction in an amount of 31.1% syringaldehyde and 6.4% benzaldehyde (based on single point calibration) and identified by LC-MS mass spectrometry.
Eugenol is the compound that was quantified and identified from the 160° C. fraction (phase 2) by LC-MS in positive SIM mode and was quantified at 21.8% (by mass of injected sample) using single point calibration.
Vanillin (Ve: 17.5 mL) and p-hydroxybenzaldehyde (Ve: 16.4 mL) were identified from the 180° C. (phase 1) fraction by LC-MS in positive SIM mode.
Vacuum distillation was carried up to 180° C. and the high boiling point fraction was isolated by decanting from the undistilled fraction. Increasing temperature beyond 180° C. on the undistilled bulk sample led to formation of solid char. The high boiling point fraction was also characterized by LC-MS in SIM mode only. Phloroglucinol (Ve: 10.96 mL, 5.5% by mass of injected sample) and 2,4-dihydroxybenzaldehyde (Ve: 17.15 mL, 12.3% by mass of injected sample) were identified and quantified in this fraction by single point calibration.
The method described above, and illustrated by the Examples, results in a conversion of approximately 50% of lignin to low molar mass value added compounds, a value which is comparable to other previously reported oxidative depolymerisation procedures (ChemSusChem. 2010; 3:719-23, Chemical Reviews. 2018; 118:614-78). With the current conditions, approximately 91% of the depolymerised product could be quantitatively recovered through vacuum distillation and approximately 20% to 25% identified as phenolic-type compounds which included vanillin, syringaldehyde, benzaldehyde, p-hydroxybenzaldehyde, eugenol, phenol, guaiacol, phloroglucinol and 2,4 dihydroxybenzaldehyde. The remaining quantity of recovered product was unidentified but could be other aromatic/non-aromatic compounds that were also formed from the depolymerisation process. Solid char was quantified at approximately 9%. Table 10 below summarises the quantities of selected aromatic compounds from an exemplary run of the depolymerisation process.
Some advantages of the present invention may include alleviation of overoxidation of primary alcohols to carboxylic acids as means of forming aldehyde functionalised chemicals from lignin and other polyphenolic polymers, lessening repolymerisation of reaction products to high molar mass polymers, which is prevalent in some oxidative depolymerisation methods. The method may be cheaper and requires a less complicated experimental setup. In certain conditions depolymerisation may use mild pH, temperature and pressure conditions; and larger amounts of aromatic functionalised compounds may be produced, including vanillin, syringaldehyde, benzaldehyde, p-hydroxybenzaldehyde, eugenol, 2,4-dihydroxybenzaldehyde, phenol, guaiacol and phlorogucinol, the latter being a compound that is not widely reported as a product of oxidative depolymerisation.
Furthermore, it will be appreciated that the lignin-derived monomers manufactured by the disclosed methods may be suitable for downstream processing such as polymerisation and/or incorporation into advanced materials or resins. The disclosed methods may accordingly find application in the manufacture of substitutes for certain crude-oil based products.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019/02602 | Apr 2019 | ZA | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2020/053859 | 4/23/2020 | WO | 00 |