The invention described and claimed hereinbelow is also described in German Patent Application DE 10 2005 024 563.3-45, filed May 28, 2005. This German Patent Application, whose subject matter is incorporated here by reference, provides the basis for a claim of priority of invention under 35 U.S.C. 119 (a)-(d).
1. Field of the Invention
The present invention relates to methods of dividing glass into separate pieces using a cutting liquid and to cutting liquids used for that purpose.
2. Related Art
That division of glass into separate pieces is made easier by wetting the crack formed in the glass, e.g. with water, during scribing and breaking of the glass has been known for many years in the glass blowing arts. At the same time water acts as a cooling medium for producing breaking stresses in a glass surface during scribing of the glass by means of a laser, e.g. as described in U.S. Pat. No. 6,252,197. It is already known to add a surfactant to the water, e.g. during laser cutting, (US 2003/0052098 A1) to provide a cooling liquid with improved power to penetrate the scribed line or crack formed by the laser beam. All known classes of wetting agents, i.e. anionic, cationic and nonionic wetting agents, are suitable (WO 2004/018144 A1).
It is especially important to maintain as constant as possible conditions during the dividing of the glass after scribing, when cutting extremely thin glass, e.g. for LCD applications, by means of a laser.
The glass to be divided along the scribed line is heated very rapidly by means of a laser beam during laser cutting in contrast to the scribing methods in which diamond or cutting wheels are used. The heated spots are quenched immediately after heating with the laser beam, generally by spraying the spots with a gas-water mixture. As a result, a crack is formed in the glass because of the large thermal stresses produced during quenching. The glass is broken or divided along the scribed line or crack by application of a force. The force can be applied mechanically, but it is possible to produce still more thermal stresses along the scribed line or crack by additional treatments of the glass with the laser, so that the glass breaks along the scribed line.
It is an object of the present invention to provide a method of dividing glass using a cutting liquid and also a suitable cutting liquid, in and with which further reductions of the applied breaking force and breaking force fluctuations are possible in an industrial operation.
According to the invention the method of dividing glass comprises the steps of:
a) producing a linear crack in the glass;
b) during or immediately after the producing of the linear crack, applying an aqueous liquid to the linear crack so that the aqueous liquid acts on or attacks the linear crack, the aqueous liquid containing an ionic organic compound, which comprises a cation with a positively charged nitrogen atom and a hydroxyl anion; and
c) dividing or separating the glass along the scribed line by application of a force to the glass.
According to the invention the cutting liquid is an aqueous liquid, which contains an ionic organic compound, which comprises a cation with a positively charged nitrogen atom and a hydroxyl anion.
Lower and more uniform, reproducible breaking forces divide the glass into separate pieces in the method according to the invention, in which an aqueous cutting liquid, which comprises an ionic organic compound with a cation including a positively charged nitrogen atom and a hydroxyl anion, acts on a crack in the glass during or immediately after producing the crack.
A plausible scientific explanation for the outstanding effect of the compounds that were discovered is that the OH− reacts with the broken siloxane bonds in the crack and prevents the spontaneous reaction of the broken bonds with each other (self-healing).
The method and the new cutting liquid used in it are especially suitable for laser cutting methods, in which the crack is formed or the scribing occurs by heating of the glass along the dividing line and immediately after that the heated glass is acted on or attacked by the aqueous liquid (cutting liquid). The crack or gap produced during laser cutting is especially narrow so that self-healing could otherwise be especially great.
The application of the cutting liquid to the crack can occur by all known techniques, e.g. spraying, spraying of a cutting liquid/water mixture, application of a wick, sponge, immersing the crack in the liquid, etc.
Quaternary ammonium hydroxide compounds are especially suitable as the active ingredient of the cutting liquid.
Those quaternary ammonium hydroxide compounds, which are especially suitable, have a cation of the following formula I:
wherein two to three of the R groups each, independently of each other, represent a straight-chained or branched aliphatic group with 1 to 2 carbon atoms, but one to two others of the R groups each independently represent a respective straight-chained or branched aliphatic group with 8 to 18 carbon atoms.
Especially suitable quaternary ammonium hydroxide compounds include dialkyldimethyl ammonium hydroxide compounds, such as distearyldimethylammonium hydroxide, didecyldimethylammonium hydroxide, dimethyldioctylammonium hydroxide, dilauryidimethylammonium hydroxide. Quaternary ammonium hydroxide compounds with three short-chained and one long-chained alkyl group, for example trimethylhexadecylammonium hydroxide, octadecyltrimethylammonium hydroxide and trimethyloctylammonium hydroxide are also especially preferred.
Alkyldimethylbenzylammonium hydroxides with a cation of the following formula II:
in which R represents a straight-chained or branched alkyl group with 7 to 17 carbon atom, are also suitable.
Quaternary ammonium compounds with cations of the following generally formula III:
in which R represents a straight-chained or branched alkyl group with 8 to 18 carbon atoms, are also suitable.
Besides the quaternary ammonium hydroxide compounds imidazoline derivatives with cations of the following general formula IV:
in which R1 represents an alkyl or alkylene group with 4 to 20 carbon atoms and R2 represents —CH2OH or —CH2NH—COR3, wherein R3 denotes an alkyl group with 8 to 18 carbon atoms, are also suitable.
An especially suitable example of an imidazoline derivative is 1-(octylaminoethyl)-2-decyl-3-methyl-imidazolonium hydroxide.
These compounds are contained in the cutting liquid in amounts of from 0.005 to 1 percent by weight. Below 0.005 percent by weight the solution acts like water; above 1% by weight the additive is no longer effective or has a reduced effect. These compounds are preferably contained in the cutting liquid in amounts of from 0.02 to 0.1 percent by weight, since good action is combined with reduced chemical consumption when amounts in this concentration range are employed. Mixtures of these compounds can understandably also be employed.
In the event that it is necessary the cutting liquid can contain still other solvating agents for the compounds used. These solvating agents can include low molecular weight alcohols, such as methanol, ethanol, propanol and butanol in amounts of up to 80% by volume of the cutting liquid. Other additives, such as thickeners, corrosion inhibitors, bactericides can be added as needed.
The cutting liquid not only makes the dividing of the glass into pieces by laser action easier, but also makes conventional glass cutting, for example by scribing with a diamond or by cutting with a cutting wheel easier. It is especially suitable for cutting of sensitive objects, e.g. thin glass substrates for TFT display screens, and makes the breaking forces used in these methods smaller and more uniform.
A special advantage of the method and discovered cutting liquids of the present invention is that scarcely any troublesome anions are present, which could interfere with further processing of the separated glass pieces in later working steps.
The objects, features and advantages of the invention will now be illustrated in more detail with the aid of the following examples, with reference to the accompanying figures in which:
The breaking forces and their reproducibility for embodiments of the method of dividing glass into separate pieces according to the invention and according to the prior art were tested. The cutting liquids of the invention were used to divide glass plates by means of the method according to the invention, while the cutting liquids of the prior art were used to divide equivalent glass plates using a comparable test method.
Glass plates of dimensions of 25 mm×150 mm with a thickness of 0.7 mm were manufactured by means of a laser cutting machine, Type DLC 1200/Blue of Schott Advanced Processing. A transverse crack, which had a depth of about 115 μm, was centrally scribed at 75 mm on each of the glass plates to be broken during testing. During the laser scribing to form a crack the glass plates were acted on with a mixture of 6 ml/min cutting liquid and 40 l/min of air, immediately following behind the laser focal spot. The plates were dried after the scribing or crack formation. The glass plates were supported over a 10 mm section on both small sides, with the crack facing downward. Subsequently the glass plates were loaded from above until they broke along their cracks.
About 30 equivalent test plates were broken in this manner for each cutting fluid tested. The cutting liquid used in comparative example 1 was water. The cutting liquids of the invention used in examples 2 to 5 were aqueous solutions of hexadecyltrimethylammonium hydroxide in different concentrations, as stated on
The diamond points shown in the figures give the individual measured breaking force (in kg read off the Y axis) for a particular test sample (designated by probe no. on the X axis). The square point on each figure gives the average value of the breaking force for all test samples. A line is shown on each figure drawn through the diamond points.
The test results shown in the figures clearly show that the methods using the cutting liquids according to the invention clearly have superior properties to those using the cutting liquids according to the prior art. Particularly they show that the breaking forces required to break the test plates along their cracks are considerably smaller and fluctuate or vary much less when the cutting liquids according to the invention are used instead of those of the prior art. Thus the cutting forces are more reproducible using the cutting liquids of the invention.
While the invention has been illustrated and described as embodied in a method of dividing glass into separate pieces using a cutting liquid and an improved cutting liquid for use in the method, it is not intended to be limited to the details shown, since various modifications and changes may be made without departing in any way from the spirit of the present invention.
Without further analysis, the foregoing will so fully reveal the gist of the present invention that others can, by applying current knowledge, readily adapt it for various applications without omitting features that, from the standpoint of prior art, fairly constitute essential characteristics of the generic or specific aspects of this invention.
What is claimed is new and is set forth in the following appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2005 024 563 | May 2005 | DE | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3138610 | Buc et al. | Jun 1964 | A |
| 3634243 | Wessels et al. | Jan 1972 | A |
| 3819647 | Foley | Jun 1974 | A |
| 3827874 | Adams | Aug 1974 | A |
| 5259888 | McCoy | Nov 1993 | A |
| 6086736 | Dasgupta et al. | Jul 2000 | A |
| 6252197 | Hoekstra et al. | Jun 2001 | B1 |
| 6807824 | Miwa | Oct 2004 | B1 |
| 20030052098 | Kim et al. | Mar 2003 | A1 |
| 20040219372 | Ogihara et al. | Nov 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| 2 809 318 | Nov 2001 | FR |
| 2004018144 | Mar 2004 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20060266195 A1 | Nov 2006 | US |