BRIEF DESCRIPTION OF THE DRAWINGS
The present invention will become more fully understood from the detailed description given here below, the appended claims, and the accompanying drawings in which:
FIG. 1 is a simplified cross-sectional view of an exemplary glow plug installation in the pre-combustion chamber of a diesel engine;
FIG. 2 is a cross-sectional view of a glow plug assembly in accordance with an embodiment of the invention;
FIG. 3 is a fragmentary, cross-sectional view of the high temperature tip region of a glow plug according to one embodiment of the invention; and
FIG. 4 is a flowchart illustrating the method for manufacturing the heating device, in accordance with an embodiment of the present invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT
Referring to the Figures, wherein like numerals indicate like or corresponding parts throughout the several views, a diesel engine is generally shown at 10 in FIG. 1. The engine 10 includes a piston 12 reciprocating in a cylinder. The cylinder is formed in a block 14. A cylinder head 16 covers the block 14 to enclose a combustion chamber. An intake manifold routes through the cylinder head 16 and includes a fuel injector 18 which, at timed intervals, delivers a charge of atomized fuel into the combustion chamber. A glow plug, generally indicated at 20, includes a high temperature tip 22 positioned, in this example, within a pre-combustion chamber 24. The arrangement of components as illustrated in FIG. 1 is typical of one configuration style for a diesel engine. However, there are many other diesel engine types for which a glow plug 20 according to the invention is equally applicable. Furthermore, many other types of devices can utilize the subject glow plug 20, such as space heaters, industrial furnaces, fuel cells, exhaust systems, and the like. Accordingly, the subject glow plug 20 is not limited to use in diesel engine applications.
Referring now to FIG. 2, a cross-sectional view of the glow plug 20 is depicted. Here, the high-temperature tip 22 is shown forming the distal end of a heating element, generally indicated at 26. The heating element 26 is a composite structure which protrudes from the end of a hollow shell 28, such as by a copper ring 30 and a brazed joint 32. By these means, the heating element 26 is both securely fixed in position relative to the shell 28 and held in electrically conductive relationship therewith. A proximal end of the heating element 26 is affixed to a conductive center wire 34, such as via a tapered and brazed joint. The proximal end of the center wire 34 holds a terminal 36 used to join an electrical lead (not shown) from the ignition system. The center wire 34 and terminal 36 are held in electrical isolation from the conductive shell 28 by way of an insulating layer of alumina powder 38, epoxide resin 40 and plastic gasket 42. Of course, alternative materials may be suitable to hold the center wire 34 and terminal 36 in position and in electrical isolation from the shell 28. The exterior of the shell 28 is provided with a tool fitting 44 and threads 46. Of course, the glow plug 20 can take numerous other forms and constructions, depending upon the materials used and its intended application.
Generally stated, the heating element 26 operates by passing an electrical current through a resistive material. The current is introduced to the heating element 26 through the center wire 34. Current flows through the heating element 26 and into the shell 28 which is typically metallic and grounded through the cylinder head 16 or other component of the device.
A fragmentary, cross-sectional view taken through the lower end of the heating element 26 is depicted in FIG. 3. Here, the heating element 26 is shown including a starter substrate 48. Starter substrate 48 is used as a foundation for forming a layered structure. Substrate 48 may be a fired or unfired ceramic, ceramic composite or metal form that will become a part of the final structure. The present invention also contemplates that substrate 48 may be a form that can be removed from the multilayer structure before it is fired. For example, substrate 48 may be a metal mandrel.
Alternatively, substrate 48 may be a pre-form that is configured to be removable by pyrolosis during heat treatment of the layered resistive core. In an embodiment of the invention, the substrate 48 has a surface treatment or a configuration that promotes the adhesion of subsequent layers as described here below.
With reference to both FIGS. 3 and 4, a method 90 for forming the multi-layered structure will now be described, in accordance with an embodiment of the present invention. In an initial step, as represented by block 100, a starting substrate or pre-form 48 is provided upon which the multi-layered structure will be built. At step 102, substrate 48 is immersed in a suspension of particles in a fluid medium to produce a first coating 50 (shown in FIG. 3) on substrate 48. First coating 50 is caused to set into a non-fluid layer, as represented by block 104. First coating 50 is transformed into a non-fluid layer by chemical or physical means. At block 106, second coating 52 is applied over first coating 50 in a similar manner. The present invention contemplates that second coating 52 has the same composition or a different composition relative to first coating 50. Additional coatings such as third coating 54 are sequentially applied until the desired multi-layer structure is completed, as represented by block 108. There may be additional coatings or layers over the third coating 54. In some applications, it may be desirable to modify one or more of the coating layers 50, 52, 54 to provide for an electrical interconnect. For example, as illustrated in FIG. 3, the tip of the second coating 52 may be ground flat so that the first 50 and third 54 coating layers can establish an electrical connection therebetween. Once any such optional modifications have been made, and all desired layers built, the assembly is fired to consolidate the multilayered structure, as represented by block 110. The multi-layered structure may be further treated before or after firing to provide electrical contacts with one or more of the various layers, as represented by block 112. As shown in FIG. 3, this electrical contact may be established between the first 50 and third 54 coatings. The fired structure may be further combined with other components to form a device such as a glow plug 20 to be used in a diesel engine 10, as represented by block 114.
In an embodiment of the present invention, first coating 50 is a suspension of ceramic particles in a water that also contains a gelling binder such as alginate. After the layer is formed, the alginate-containing suspension can be caused to set by immersing the coated pre-form in a solution containing dissolved calcium ions. The calcium ions chemically interact with the alginate causing the suspension to gel. Once the coating has gelled it may be desirable to wash the surface to remove excess gelling agent before forming the next layer. Alternatively, the substrate might be first coated with a calcium-containing solution and then subsequently dipped into alginate-containing slurry to form a gelled layer. The thickness of the layer is controlled by the amount of calcium in the calcium-containing solution.
In yet another embodiment of the present invention, other gellation reactions as an alternative to alginate and calcium may be used. For example, a slurry containing polyacrylic acid can be gelled by changing the pH or the temperature of the slurry. In operation, the substrate 48 is coated by dipping the substrate 48 into a slurry of particles that contain polyacrylic acid. The coating is then gelled either by dipping the coated substrate 48 into an acidic or basic solution depending on the type of polyacrylic acid used or by dipping it into a bath containing an immiscible liquid. The immiscible liquid is held at an elevated temperature, which causes gellation.
Alternatively, an organic monomer may be used as a gelling agent in a suspension of ceramic particles. The organic monomer is coated on substrate 48 and gelled by polymerization initiated by a chemical initiator. Other types of binders could be gelled by ultraviolet radiation. A large number of gellation binder systems are known in the ceramic art and any of these could be used in this method.
Any one of the layers might also be modified in such a way as to form interconnects between layers. For example, in a three layer structure a first conductive layer might be formed followed by an insulating layer and finally a resistive layer. After the insulating layer is formed, a portion of the insulating layer is removed exposing the conductive layer and forming an electrical contact between the conductive layer and the resistive layer during a final coating operation.
In a manufacturing setting the method of the present invention is performed, for example, by setting up a series of slurry tanks and solution tanks in a line with the substrates suspended above the tanks on a moving conveyor. Alternately, the substrates may be dipped and then set or hung on draining racks to drain and then moved to the next tank to be dipped and drained. This process is repeated until the desired coatings have been built up on the substrate 48.
In yet another embodiment of the invention, a method is provided whereby the substrate 48 is sprayed to create the coating layers prior to the gellation step. The gellation of these coating layers may also be accomplished by spraying any of the gelling solutions described above instead of dipping the substrate. The addition of subsequent coatings allows individual conductors, resistors and insulators to be merged into one another gradually to reduce thermal shock and delamination. More specifically, the layers may be designed by slurry rheology to produce thicknesses of 0.001 inch (i.e., about 25 microns) after dipping. Thus, the difficulty of injection molding plaster casting (and other methods) is eliminated and makes the process easy to semi-automate into high volume production.
The foregoing discussion discloses and describes an exemplary embodiment of the present invention. One skilled in the art will readily recognize from such discussion, and from the accompanying drawings and claims that various changes, modifications and variations can be made therein without departing from the true spirit and fair scope of the invention as defined by the following claims.
Patent Application
20080095943