Patent Application
20150337064
This disclosure relates to polymer electrolyte materials, such as those used in proton exchange membrane (PEM) fuel cells.
Fuel cells are commonly used for generating electric current. A single fuel cell typically includes an anode electrode, a cathode electrode, and an electrolyte between the anode and cathode electrodes for generating an electric current in a known electrochemical reaction between a fuel and an oxidant. The electrolyte may be a polymer membrane, which is also known as a proton exchange membrane or “PEM.”
One common type of polymer exchange membranes is per-fluorinated sulfonic acid (PFSA) polymer membrane, such as NAFION® (E. I. du Pont de Nemours and Company). PFSA polymer consists of a perfluorinated carbon-carbon backbone, to which are attached perfluorinated side chains. Each side chain terminates in a sulfonic acid group that works as a proton exchange site to transfer or conduct protons between the anode and cathode electrodes.
The proton conductivity of PFSA polymers varies in relation to relative humidity (RH) and temperature. The relation between conductivity and level of hydration is based on two different mechanisms of proton transport. One is the vehicular mechanism, where the proton transport is assisted by the water in the membrane, and the other is the hopping mechanism, where the proton hops along the sulfonic acid sites. While vehicular mechanism is dominant at high relative humidity conditions, the hopping mechanism becomes important at low relative humidity conditions.
PEM fuel cells, especially for automobile applications, are required to be able to operate at high temperature (≧100° C.) and low RH (≦25% RH) conditions, in order to reduce the radiator size, simplify the system construction and improve overall system efficiency. Consequently, PEM materials with high proton conductivity at high temperature and low RH conditions are needed.
PFSA polymer is usually prepared by free radical copolymerization of tetrafluoroethylene (TFE) and per-fluorinated (per-F) vinyl ether monomer (such as perfluoro-2-(2-fluorosulfonylethoxy) propyl vinyl ether, or “PSEPVE”, for Nafion®). One approach to produce a PFSA polymer with improved proton conductivity is to decrease the TFE content in the product polymer. An indicator of conductivity of an electrolyte material is equivalent weight (EW), or grams of polymer required to neutralize 1 mol of base. The most common equivalent weights of commercially available PFSA polymers (such as NAFION®) are between ˜800 and ˜1100 g/mol, which provide a balance between conductivity and mechanical properties. While PFSA polymer with EW in this range is needed, increasing conductivity below a certain EW threshold, saying ˜700 g/mol, renders the electrolyte water soluble and not suitable for PEM applications.
Per-F sulfonimide (SI) acids (such as Bis (trifluoromethane) sulfonimide, CF3—SO2—NH—SO2—CF3) show favorable properties, including strong acidity, excellent chemical and electrochemical stability, for PEM fuel cell applications. Linear per-F sulfonimide polymers (PFSI), prepared by copolymerization of TFE and SI-containing per-F vinyl ether monomer, were first reported by DesMarteau, et al. (U.S. Pat. No. 5,463,005). Such type of linear PFSI polymers with the EW in the range of 1175-1261 g/mol for PEM application was reported by Creager, et al. (Polymeric materials: science and engineering—WASHINGTON— 80, 1999: 600). Per-F vinyl ether monomer that contains two SI groups was also synthesized, and the corresponding linear PFSI polymer with the EW of 1175 g/mol was prepared and demonstrated to have high thermal and chemical stability in PEM fuel cell operating conditions (Zhou, Ph.D. thesis 2002, Clemson University). Reducing TFE content in the PFSI polymers is an efficient way to increase the proton conductivity of the product polymers. Linear PFSI polymer with the EW of 970 g/mol was reported in the literature (Xue, thesis 1996, Clemson University). However, such type of linear PFSI polymers with even lower EW is difficult to synthesis through free-radical copolymerization process and also renders the polymer water soluble below a certain EW threshold.
The preparation of PFSI polymer with calculated EW of 1040 by chemical modification of PFSA polymer resin (in —SO2—F form) was reported in a Japanese patent (Publication No: 2002212234). Furthermore, a more efficient chemical modification process was reported by Hamrock et al. (Publication No. WO 2011/129967). In this process, a linear PFSA polymer resin (in —SO2—F form) was treated with ammonia in acetonitrile (ACN) to convert the —SO2—F groups to sulfonamide (—SO2—NH2) groups, which then reacted with a per-F disulfonyl difluoride compound (such as F—SO2—(CF2)3—SO2—F) to convert to —SO2—NH—SO2—(CF2)3—SO3H in the final product. By starting with a 3M's PFSA (in —SO2—F form) with EW of ˜800 g/mol, water-insoluble polymer electrolyte with EW as low as ˜625 g/mol was reported. However, polymer electrolyte with even lower EW (<625 g/mol) resulted in a water soluble polymer and hence is not suitable for PEM applications.
Cross-linking is known as an effective strategy to prevent polymers from being soluble in water and organic solvents. This step is known to improve polymers' mechanical strength. Cross-linking PFSA polymer (in SO2—F form) can be achieved by a coupling reaction of a sulfonyl fluoride (—SO2—F) group and a sulfonamide (NH2—SO2—) group to form a sulfonimide acid (—SO2—NH—SO2—). The resulting sulfonimide group also works as a proton conducting site.
Uematsu et al. (Journal of Fluorine Chemistry 127 (2006) 1087-1095) reported using thermal treatment (270° C.) to couple sulfonyl fluoride groups and sulfonamide groups in terpolymers of TFE, PSEPVE and sulfonamide-containing per-F vinyl ether monomer to form sulfonimide groups as cross-linking sites in the polymer matrix. An improvement in mechanical strength of polymer matrix was shown, without reduction in equivalent weight.
Hamrock et al. (US2009/041614, US2006/0160958, US2005/0113528, U.S. Pat. No. 7,060,756, EP1690314) proposed to use aromatic cross-linking agents to react with PFSA polymer (in —SO2—F and/or —SO2—Cl form) to generate aromatic sulfone-containing cross-links in the polymer matrix. The proposed reaction conditions include thermal treatment at high temperature (160° C. or higher) and with a Lewis acid as catalyst. The proposed product polymer may have EW lower than 900 g/mol. The even lower EW (≦700 g/mol) cross-linked polymer products were not mentioned in these patents. In addition, the introduction of aromatic ring structures into the polymer matrix compromised chemical stability and could lead to inferior durability of product polymer membranes in highly acidic and highly oxidizing conditions in PEM fuel cells.
A method of fabricating water insoluble, low EW perfluorinated polymer electrolyte materials includes providing a low EW perfluorinated polymer resin that includes perfluorinated carbon-carbon backbone and perfluorinated side chains that extend from the perfluorinated carbon-carbon backbone chain and terminate in a sulfonyl fluoride, —SO2—F. The perfluorinated polymer resin is exposed to ammonia gas to convert the sulfonyl fluoride groups to sulfonamide groups, —SO2—NH2. The perfluorinated polymer in sulfonamide form is contacted with chemical agent(s) to convert sulfonamide to sulfonimide, —SO2—NH—SO2—, in a 3-dimensional cross-linked, low EW, water-insoluble perfluorinated polymer electrolyte material.
The disclosed example proton exchange materials may be used as proton exchange membranes for PEM fuel cells or other applications where proton exchange is desirable. As will be described, the disclosed proton exchange material provides the ability to increase the density of proton exchange sites while maintaining resistance to solvents, such as water. As a comparison, an increase in the density of proton exchange sites by simply decreasing TFE content in PFSA polymers increases proton conductivity but also increases the polymer solubility in water, which is detrimental in PEM fuel cell applications. Conversely, a decrease in the density of proton exchange sites by simply increasing TFE content in PFSA polymers enhances polymers' water stability but decreases proton conductivity and debits PEM fuel cell performance.
An example proton exchange material includes perfluorinated carbon-carbon backbone chains and perfluorinated side chains extending off of the perfluorinated carbon-carbon backbone chains via an ether linkage. The perfluorinated side chains that have one or more sulfonimide (SI) groups, —SO2—NH—SO2—.
In embodiments, the perfluorinated carbon-carbon backbone chains have a structure of —(CF2CF2)N—CF2—CF(—O—RA—RB)—, where N on average is greater than or equal to zero, RA is a linear or branched perfluorinated chain, which includes a general structure of —CXF2XOZ—, where X is greater than or equal to two and Z is greater than or equal to zero. RB is a linear or branched perfluorinated chain, which contains one or more SI groups and ends with a —CF3 group or a —SO3H group, or covalently links to another RA.
In embodiments, the side chains that extend off of the backbone chains may be end-capped chains, cross-link chains, or both. The end-capped chains may have at least one SI group, —SO2—NH—SO2—, and may include between two and five of SI groups or even greater than five SI groups. Additionally, the end-capped chains may be ending with a —CF3 group or a —SO3H group. The portion of end-capped chains that are ended with —CF3 may include multiple SI groups and the portion of end-capped chains that are ended with —SO3H may include at least one SI group. The cross-link chains may contain at least two SI groups and covalently link to the same or different polymer backbone chains.
In the proton exchange material, 20-99% of the perfluorinated side chains may be the end-capped chains and 80-1% of the side chains may be the cross-link chains. In other examples, 50-99% of the perfluorinated side chains are the end-capped chains and 50-1% of the side chains are the cross-link chains.
In one example, the proton exchange material has Structure 1 shown below, where N on average is greater than or equal to zero, RA is a linear or branched perfluorinated chains, which includes a general structure of —CXF2XOZ—, where X is greater than or equal to two and Z is greater than or equal to zero. SI is sulfonimide group, RC1, RC2 and RC3 are independently selected from —(CF2)y— where y is 1-6 and —(CF2)y′—O—(CF2)y′— where y′ is 1-4, m, m′, n and n′ are greater than or equal to 1. m, m′, n and n′ may be equal to or different than each other, z is greater than or equal to zero. It is also understood that the end-capped chains and cross-link chains may occur randomly on the perfluorinated carbon-carbon backbone chains. The amounts of end-capped chains and cross-link chains may be as described above.
A user may design the proton exchange material of the disclosed examples with a selected number of SI groups, backbone structure and side chain structure to provide a desired EW of proton exchange sites.
The EW of the proton exchange material may generally be less than 850. In further examples, the equivalent weight is less than 700. In further examples, the equivalent weight is less than 625. The disclosed range provides relatively high proton conductivity and a suitable rheology for membranes and electrode ionomers desired for a PEM fuel cell or other applications.
A method of fabricating such an electrolyte material, or proton exchange material, includes
The disclosed SI chemistry creates cross-links that prevent the low EW polymer from being water soluble and thus permit the usage in electrochemical applications. In prior known linear PFSA polymers with low EW are water soluble and unusable for PEM fuel cells.
The electrolyte material produced according to the exemplary method could have EW of less than 700 and provide excellent proton conductivity in high temperature and low relative humidity conditions, while maintaining good chemical and mechanical stability in comparison to prior electrolyte materials.
The perfluorinated polymer resin of step (A) can be synthesized through a free radical polymerization step. Step (B) may be referred to as an amidification step, step (C) may be referred to as a gelation step and optional step (D) is a post-treatment step. The following illustrate non-limiting examples of steps (A), (B), (C) and (D). Where appropriate, the following abbreviations are used herein:
° C.: degrees Celsius
3P: bis(pentafluoropropionyl) peroxide
4P: bis(heptafluorobutyryl) peroxide
ACN: acetonitrile
atm: atmosphere
DSC: differential scanning calorimetry
EW: equivalent weight
g: grams
HFC 43-10: 2,3-dihydrodecafluoropentane
M: molarity
mtorr: millitorr
PSEPVE: perfluoro-2-(2-fluorosulfonylethoxy) propyl vinyl ether
POPS: perfluoro 3-oxa-4-pentene-sulfonylfluoride, CF2═CF—O—CF2CF2—SO2—F
psig: pounds per square inch gauge
RH: relative humidity
rpm: rotations per minute
TFE: tetrafluoroethylene
TGA: thermal gravimetric analysis
The perfluorinated polymer resin is produced by free radical polymerization of TFE and per-F vinyl ether monomer (such as PSEPVE or POPS). In one example of the polymerization, a molar ratio of TFE to per-F vinyl ether monomer is approximately 3:1 or less, resulting in polymer resins of low EW (less than ˜750). In a further example, the polymerization is carried out with per-F vinyl ether monomer only, which produces the homopolymer of the monomer with the lowest EW (as low as ˜280).
The following examples illustrate further details of the polymer resin synthesis.
A typical run involves adding 200 g of HFC 43-10 and 550 g of PSEPVE to a 600-mL autoclave and degassing the solution by freeze-pump-thawing 5 times to remove all oxygen. The autoclave is then filled with nitrogen to 0 psig and heated to 40° C. with stifling at a rate of 200 rpm. At the same time, the initiator feed line is cooled to −30° C.
The autoclave is pressurized to 105 psig using an equimolar mixture of TFE and CO2. A 5.26 weight percent solution of 4P in HFC 43-10 is added by a high pressure pump to the autoclave at the flow rate of 10 mL/min for one minute, then reducing the flow rate to 0.0167 mL/min for the remainder of the polymerization. As TFE is consumed during the polymerization, the equimolar mixture of TFE and CO2 is continuously added to keep the pressure of TFE constant throughout. After 5 hours, the initiator feed and TFE feed are stopped, and the autoclave is allowed to sit overnight so the remaining TFE is consumed.
The remaining CO2 is then vented from the autoclave, and the solvent and excess monomer are removed by vacuum distillation at 120° C. and 20 mtorr, yielding 95 g of polymer resin with an equivalent weight of 775 g/mol.
A typical run involves adding 525 g of HFC 43-10 and 200 g of POPS to a 600-mL autoclave and degassing the solution by freeze-pump-thawing 5 times to remove all oxygen. The autoclave is then filled with nitrogen to 0 psig and heated to 35° C. with stifling at a rate of 200 rpm. Meanwhile, the initiator feed line is cooled to −30° C.
The autoclave is pressurized to 105 psig using equimolar mixture of TFE and CO2. A 2.03 weight percent solution of 3P in HFC 43-10 is added by a high pressure pump to the autoclave at the flow rate of 14 mL/min for one minute, then reducing the flow rate to 0.0389 mL/min for the remainder of the polymerization. As TFE is consumed during the polymerization, the equimolar mixture of TFE and CO2 is continuously added to keep the pressure of TFE constant throughout. After 5 hours the initiator feed and TFE feed are stopped, and the autoclave is allowed to sit overnight so the remaining TFE is consumed.
The remaining CO2 is then vented from the autoclave. The solvent and excess monomer are removed by vacuum distillation at 120° C. and 20 mtorr, yielding 60 g of polymer with an equivalent weight of 700 g/mol.
124.25 g of degassed PSEPVE is added to a sealed glass reaction vessel which has previously been pacified with 3P initiator. 2.4 mL of a 3.38 weight percent solution of 3P in HFC 43-10 is added every 5 days, with the polymerization being carried out at 20° C. Five days after the fifth addition, the excess monomer is removed by vacuum distillation, yielding 36 g of PSEPVE homopolymer.
This polymer has been characterized by IR and TGA, showing 10% weight loss at 375° C. and 50% weight loss at 406° C. DSC shows a Tg of 20.11° C. and a Tm of 184° C.
140 g of degassed POPS is added to a sealed glass reaction vessel which has previously been pacified with 3P initiator. 4.3 mL of a 3.38 weight percent solution of 3P in HFC 43-10 is added every 5 days, with the polymerization being carried out at 20° C. Five days after the fifth addition, the excess monomer is removed by vacuum distillation, yielding 33 g of the homopolymer.
This polymer has been characterized by IR and TGA, showing 10% weight loss at 365° C. and 50% weight loss at 402° C. DSC shows a Tg of 44.02° C.
To a 100-mL stainless steel autoclave is added 149.42 g of degassed PSEPVE. The autoclave is heated to 45° C. at a stirring rate of 200 rpm. Using a pump, 2.3 mL of a 0.2324 M solution of 4P in perfluorohexane is added to the autoclave over 1 minute before pressurizing the autoclave to 55 psig with an equimolar mixture of TFE and CO2. The polymerization is then allowed to react overnight as the TFE is consumed and the pressure drops. The resulting polymer had an EW of 500 g/mol by infrared spectroscopy.
128 g of degassed PSEPVE is added to the 100-mL stainless steel autoclave. With the CO2 scrubber installed, the TFE and CO2 mixture is slowly added with the temperature on the six point thermocouple located in the scrubber being always below 50° C. The neat TFE is added to the autoclave and the pressure of neat TFE inside the autoclave head space is kept at 55 psig throughout the reaction with a stirring rate of 200 rpm. Using a pump, 4.0 mL of a 0.106 M solution of 3P in perfluorohexane is added to the autoclave over 1 minute followed by 5 hours of a 0.00667 mL/min addition rate. Resulting polymer had an EW of approximately 550 g/mol by infrared spectroscopy.
The amidification includes exposing the perfluorinated polymer resin (in —SO2—F form) to ammonia to convert all —SO2—F groups to sulfonamide groups, —SO2—NH2. The use of ammonia gas permits the amidification to be conducted in a solvent-free process where the perfluorinated polymer resin is processed in a solid state rather than being dissolved in a liquid solvent solution. Prior to the exposing of the perfluorinated polymer resin to ammonia gas, decreasing the particle size of the polymer resin by technologies, including but not limited to cryogrinding, increases polymer's contact surface area with ammonia gas, and therefore, reduces the reaction time and improves the reaction yield. The elimination of the solvent provides (i) a relatively clean reaction that reduces undesired by-products from side reactions with the solvent, (ii) easier collection of the product by simplifying product work-up. The following illustrate further examples of the amidification using ammonia gas, which can also be conducted in a solution (solvent) process.
For the preparation of sulfonimide form of homopolymer, the substrate was placed in a round bottom flask and heated slowly under vacuum until the polymer started to flow. Then the flask was rotated to form thin film of the homopolymer on an internal flask surface. The reaction flask cooled down and ammonia gas was added to reach 1 atm pressure. The ammonia was added from time to time to keep constant pressure of 1 atm in the reaction flask.
For the work-up, one of two methods below were applied:
1) Product was extracted by dry ACN, the solvent was evaporated and the product was dried at 100-120° C. under vacuum; and
2) Product was dissolved in an organic solvent, including but not limited to ethyl acetate or diethyl ether, and washed with water. The solution was dried over MgSO4, the solvent was evaporated and the product was dried at 100-120° C. under vacuum.
The second method allowed for the removal of all NH4F from the polymer product. Starting from 3.5 g of PSEPVE homopolymer (7.85 mmol, in —SO2—F form), 2.91 g of polymer product (in —SO2—NH2 form) was obtained with 84% yield.
6.67 g of PSEPVE homopolymer (in —SO2—F form) was added to a flask and gaseous ammonia was added at 20° C. As ammonia was consumed, more was added to keep the pressure constant at 15 psig for 3 days. NH4F was removed at 100° C. and 20 mtorr. ACN was added to the resulting polymer and heated at 80° C. for 12 hours to dissolve the polymer. The solution was decanted off and the ACN was removed by distillation to yield 5.78 g of polymer product (in —SO2—NH2 form). This polymer product is well soluble in polar organic solvents, with a solubility of 100 mg/mL in ACN.
4.00 g of the copolymer of PSEPVE and TFE with an EW of 775 was added to a Ni autoclave and NH3 was added and maintained at 30 psig and 20° C. for 12 hours. The NH4F produced was removed by vacuum distillation at 100° C. and 20 mtorr. Two aliquots of 150 mL ACN was added and heated to 80° C. to dissolve the sulfonamide polymer product. The solution was decanted off and the ACN was removed by distillation to yield 3.46 g of polymer product (in —SO2—NH2 form). This polymer is soluble in polar organic solvents, with a solubility of 10 mg/mL in ACN and 25 mg/mL in N-methyl-2-pyrrolidinone.
An amount of 6.52 g of the copolymer of TFE and PSEPVE is dissolved in refluxing perfluorohexane. Ammonia is bubbled through the solution to maintain a high reflux rate for several hours at room temperature. The ammonia is allowed to boil away and the volatiles, including ammonium fluoride, are all removed by heating to 110° C. at 50 mtorr. Dry ACN is then added to the flask and heated to refluxing. After three extractions with ACN, 5.67 g of white product is obtained in 87% yield.
In the gelation step, the perfluorinated polymer in sulfonamide form from the amidification step (B) reacts with a first chemical agent to convert at least a portion of the sulfonamide groups to SI groups and generate cross-linking side chains at the same time. As an example, the first chemical agent includes F—SO2-Rf—SO2—F and, optionally, NH2—SO2-Rf′—SO2—NH2, where Rf and Rf′ are independently selected from —(CF2)n— where n is 1-6, or —(CF2)n′—O—(CF2)n′— where n′ is 1-4. In further examples n is equal to or different than n′.
In embodiments, the gelation step can be conducted in either one or two step reactions. The one-step reaction includes co-adding F—SO2-Rf—SO2—F, NH2—SO2-Rf′—SO2—NH2 and the perfluorinated polymer in sulfonamide form into a reaction vessel with at least one polar solvent and at least one amine as catalyst. In examples, the polar solvent includes but not limited to ACN, 1,4-Dioxane, DMF, NMP and combinations thereof. The amine catalyst includes but not limited to trimethylamine (TMA), triethylamine (TEA), N,N-Diisopropylethylamine (DIPEA), 1,4-diazabicyclo[2.2.2]octane (DABCO) and combinations thereof. The reaction temperature can be approximately 25° C. to 100° C. or higher. In one example, the temperature is 50-80° C. The reaction time is several hours to up to one month, depending on the reaction reagents, ratio and reaction temperature.
The two-step reaction includes combining F—SO2-Rf—SO2—F and NH2—SO2-Rf′—SO2—NH2 first in a reaction vessel with at least one polar solvent and at least one amine as catalyst (as described above), to cause a reaction to produce linear SI-containing oligomers that terminate in a —SO2—F at both ends. Then the perfluorinated polymer in sulfonamide form from the amidification step is added in the reaction solution to react with the linear SI-containing oligomers. In examples, F—SO2-Rf—SO2—F, NH2—SO2-Rf′—SO2—NH2 and TEA are combined in a reaction vessel with ACN and TEA. The mixture is stirred under 50-80° C. for one hour to one week, producing a linear SI-containing oligomers with —SO2—F groups on both ends. The perfluorinated polymer in sulfonamide form from the amidification step (optionally in ACN) is then added into the above reaction mixture. The reaction time is several hours to one month, depending on the reagents, ratio and reaction temperature.
In further examples, the one step or the two-step gelation includes combining X moles of the F—SO2-Rf—SO2—F, Y moles of the NH2—SO2-Rf—SO2—NH2 and Z moles of the perfluorinated polymer (calculated by sulfonamide groups), according to an equation X/(Y+0.5Z)≧1, where X, Y and Z are variable, X>0, Y≧0 and Z>0.
Optionally, after the above gelation step, the unreacted sulfonamide groups in the perfluorinated polymer can be further treated with a second chemical agent to convert to SI groups and terminate the side chains with either a —CF3 or a —SO2—F, where the —SO2—F can be converted into a sulfonic acid group by a base solution treatment. For example, the second chemical agent, optionally with additional polar solvent and amine catalyst, is directly added into the reaction mixture from the above gelation step. Or the second chemical agent reacts with the isolated polymer product from the above gelation step in a reaction vessel with at least one polar solvent and at least one amine catalyst (as described above).
In a further example, the second chemical agent is selected from F—SO2-Rf—SO2—F, F—SO2-(Rf-SI)m-Rf—SO2—F and F—SO2-(Rf-SI)m′—(CF2)m″CF3, where Rf is independently selected from —(CF2)— where n is 1-6 and —(CF2)n′—O—(CF2)n′— where n′ is 1-4, SI is sulfonimide, and m, m′ and m″ are 0-6, respectively.
To a 20-ml glass vial in a nitrogen-protected glove box, 223 mg (0.25 mmol) of a perfluorinated polymer in sulfonamide form from the amidification step, 188 mg (2.5 mmol) of F—SO2—(CF2)4—SO2—F, 0.35 ml (Aldrich>99.5%, 2.5 mmol) of TEA, and 0.64 ml (Aldrich, anhydrous) of ACN were added. The reaction mixture was heated at 50° C. and stirred for 5 hours to form yellow gel. The reaction mixture was then heated at 80° C. and stirred for 1 day. The product gel was slowly acidified in 1M HCl solution for 12 hours at room temperature. The acidified gel was purified by immersing into 30% H2O2 for 3 weeks at room temperature and dried in hood to give colorless product.
The EW of the isolated polymer product is measured to be approximately 500 g/mol by titration. No sulfonamide group was detected by infrared spectroscopy. The water uptake ratio is up to 540%, but the product polymer is insoluble in boiling water. Under 80° C. and a wide RH range (20-95% RH), the polymer product exhibited ˜2.8 times proton conductivity of Nafion® 112 membrane.
The sulfonamide polymer from the amidification step (1.5 g, 2.14 mmol) was placed into vial and 9 mL of ACN was added. The reaction mixture was stirred until suspension formed, then F—SO2—(CF2)2—SO2—F (1.8 g, 6.77 mmol) and 2.5 mL of TEA were added. The reaction mixture was sonicated for 6 hours followed by stifling at 55-60° C. for 1 day. Then the reaction temperature was increased to 80-85° C. and reaction mixture was stirred for additional 1 day (One-step Gelation).
F—SO2—(CF2)2—SO2—F (1.8 g, 6.77 mmol), 3 mL of ACN and 2.5 mL of TEA was added to the reaction mixture, followed by 6-hour sonication, 1 day stifling at 55-60° C. and 1 day stirring at 80-85° C. (Post-treatment).
The reaction mixture was treated with KOH/H2O/DMSO (15/35/50 wt %) solution at 80-90° C. for about 1 hour, washing with D.I. water, then acidified and purified as described in Example C-1 to give colorless isolated polymer product with 64% yield.
A solution of NH2—SO2—(CF2)4—SO2—NH2 (0.0654 g, 0.182 mmol) and F—SO2—(CF2)4—SO2—F (0.143 g, 0.374 mmol) in 0.4 mL of ACN and 0.1 mL TEA was stirred at 75-80° C. for 2.5 hours, giving F—SO2—((CF2)4—SI)m—(CF2)4—SO2—F solution, where m is equal to 2 on average.
Half of the amount of the above F—SO2—((CF2)4—SI)m—(CF2)4—SO2—F solution was added in a glove box to a solution of sulfonamide polymer from the amidification step (0.081 g, 0.182 mmol) in 0.3 mL of ACN and 0.1 mL of TEA. The reaction mixture was stirred for 64 hours at 55-60° C. (gelation occurred in ˜10 hours). Then F—SO2—(CF2)4—SO2—F (0.07 g, 0.183 mmol), ACN (0.3 mL), TEA (0.1 mL) were added to the reaction mixture and the mixture was stirred additional 16 hours at 55-60° C. and 20 hours at 80-85° C. (post-treatment step). After work-up as described in above examples, the polymer product is isolated with a yield of 45%.
By changing the types of starting polymers, reaction agents, agents' ratio and/or reaction conditions, product polymers with various structures, different EW and different physical properties (including mechanical and proton conductivity properties) can be obtained. Both stifling and two-step gelation were useful to improve the product polymer yield.
Using the same method as described above, and starting from PSEPVE homopolymer, water-insoluble product polymer with high proton conductivity were obtained (shown in the
Type-1: by two-step gelation with F—SO2—(CF2)2—O—(CF2)2—SO2—F and NH2—SO2—(CF2)4—SO2—NH2;
Type-2: by two-step gelation with F—SO2—(CF2)4—SO2—F and NH2—SO2—(CF2)4—SO2—NH2;
Type-3: by one-step gelation with F—SO2—(CF2)4—SO2—F.
Although a combination of features is shown in the illustrated examples, not all of them need to be combined to realize the benefits of various embodiments of this disclosure. In other words, a system designed according to an embodiment of this disclosure will not necessarily include all of the features shown in the Structure 1 or all of the portions schematically shown in the Structure 1. Moreover, selected features of one example embodiment may be combined with selected features of other example embodiments.
The preceding description is exemplary rather than limiting in nature. Variations and modifications to the disclosed examples may become apparent to those skilled in the art that do not necessarily depart from the essence of this disclosure. The scope of legal protection given to this disclosure can only be determined by studying the following claims.