This invention relates with manufacturing of magnetic recording media for hard disk drives with low switching field and high density storage capabilities.
A magnetic recording device such as hard disk drive would have the following key components: a recording medium to store information, a writing head to produce localized magnetic fields for writing information and a read sensor to convert the magnetic field from the media to electrical signals.
Each magnetic bit in the current perpendicular magnetic recording (PMR) medium comprises several thermally stable magnetic grains. Further increase in the areal density requires a reduction in the grain size to retain the signal-to-noise ratio.
However, the thermal stability factor (KuV/kBT, where Ku is the magnetocrystalline anisotropy, V the magnetic grain volume, kB the Boltzmann constant and T the absolute temperature) of each magnetic grain should be >60.1,2 Therefore, the reduction in the magnetic grain size reduces the thermal stability as a result of super-paramagnetism.3
Super-paramagnetism is a phenomenon by virtue of which magnetization direction of smaller magnetic particle switches without any applied magnetic field due to ambient thermal energy. In this case thermal energy (kBT), becomes comparable to the anisotropy energy (KuV) and magnetizations thermally flip the direction, which undesirably causes random data corruption. Putting another way, the magnetic grains lose the data undesirably without any applied field. Thus decreasing grain size is not by itself a solution to increasing areal density.
An alternative to delay the superparamagnetism is by using a material with large Ku in order to keep the magnetic grains thermally stable, and hence the thermally stable bits. Prior art writing heads currently have a limitation of the maximum writing field of 24 kOe, and are unable to switch high Ku mediums such as CoPt and FePt, since switching field is proportional to magnetocrystalline anisotropy. One of the key challenges for the realization of high Ku materials based media for industrial application is to reduce the switching field.4
Exchange coupled composite (ECC) bilayer media5 or exchange spring media6 (independently proposed by Victora et al. and Suess et al., respectively) may be effective at reducing the switching field. Such medium consist of magnetically hard and soft regions within each magnetic grain, where soft region assists hard region to reduce the switching field by formation of domain wall at the opposite end of the hard\soft interface followed by domain wall propagation towards the interface (
Furthermore it has been theoretically predicted and experimentally observed that multilayer media or “graded media” in which anisotropy varies substantially continuously along the film growth direction, may be more effective for switching field reduction than the bilayer ECC media.7,8 However, preparing graded media is extremely challenging task using conventional sputtering technique. An approach to fabricate Fe/FePt graded media has been reported where Fe was deposited at high temperature on FePt, and composite film was annealed at high temperature.9 In this case diffusion of Fe into FePt may produce graded media. However, major drawback of this technique is that the control of Fe diffusion is very difficult. Moreover, annealing may also induce grain growth in the lateral direction, which undesirably deteriorates the signal-to-noise ratio.
Another approach being used is introducing an impurity during sputtering into the layer to increase the magnetic softness of hard magnetic material. But this way there are different layers formed with reduced impurity content hence it is more of a multilayer medium rather than a continuously graded media.10
In general terms the invention uses ion-implantation to achieve the graded media. The ions may be implanted into the recording layer in such a manner that the doping profile has its peak at the top surface of recording layer and a gradual tail goes deep into the recording layer hence creating a gradient in anisotropy across the recording layer.
In a first specific expression of the invention there is provided a magnetic data storage medium comprising: an ion doped magnetic recording layer having a continuous grading of coercivity or anisotropy, wherein the coercivity or anisotropy is at a minimum substantially at one side of the magnetic recording layer, and having substantial portion of maximum coercivity or anisotropy at the other side of the magnetic recording layer.
The magnetic recording layer may be a high magnetocrystalline anisotropy material.
The high magnetocrystalline anisotropy material may be selected from the group consisting or CoPt, FePt, SmCo5 and any other magnetic materials comprising uniaxial magnetic anisotropy >1×107 ergs/cc.
The continuous grading of coercivity or anisotropy may have a relatively sharp gradient profile at the interface of the overcoat and the recording layer, wherein an ion density is at a maximum substantially at the interface and the coercivity is a minimum substantially at the interface.
The ions may be selected from the group consisting of helium (He+), (C+), nitrogen (N2+), argon (Ar+), cobalt (Co+), antimony (Sb+) and any combination thereof.
The ions may be cobalt (Co+).
The fluence of the ions may range from 1014 to 5×1016 ions/cm2.
In a second specific expression of the invention there is provided a method of fabricating a magnetic data storage medium comprising: providing a magnetic recording layer, and implanting ions into the magnetic recording layer to provide a continuous graded level of ion doping within the magnetic recording layer.
The step of implanting ions may comprise selecting a species of ions, an angle of implantation and an energy of implantation to achieve a maximum doping level substantially at one side of magnetic recording layer and having substantially undoped portion at the other side
The species of ions may be selected from the group consisting of helium (He+), carbon (C+), nitrogen (N2+), argon (Ar+), cobalt (Co+), antimony (Sb+) and any combination thereof.
The method may further comprise selecting a fluence of the ions from between 1014 to 5×1016 ions/cm2.
In order that the invention may be fully understood and readily put into practical effect there shall now be described by way of non-limitative example only, example embodiments described below with reference to the accompanying illustrative drawings in which:
According to the example embodiment it is proposed to fabricate a graded media using an ion-implantation method, which is described as follows.
1) Granular media of CoCrPt and FePt are deposited on Ru and CrRu underlayer respectively. The magnetic recording layer is a high magnetocrystalline anisotropy material and may comprise CoPt, SmCo5, or any other magnetic materials having uniaxial magnetic anisotropy >1×107 ergs/cc.
2) Ru and CrRu underlayer were chosen for high anisotropy CoCrPt and FePt magnetic recording layer, since it will control the easy axis of magnetization along the film normal direction required for perpendicular magnetic recording.
3) Magnetic recording layer is implanted with suitable ion species, dose and energy.
4) Ion implantation results shows uniform Gaussian doping profile 200 inside the film (
5) Ideally, the profile 300 in media should be as shown in
6) Ion-implantation of Helium 400 and Carbon 402 (
The ion species chosen for the graded media application should preferably be able to reduce the anisotropy constant without changing the thermal stability of grains and remanent magnetization or saturation magnetization. Ion species which have been tried are helium (He+), carbon (C+), nitrogen (N2+), argon (Ar+), cobalt (Co+) and antimony (Sb+) starting with fluence ranging from 1014 up to 5×1016 ions/cm2. No change in Saturation magnetization (MS) was observed for helium and cobalt, whereas, all other species showed reduction in MS. The coercivity or anisotropy constant reduced with increasing fluence for a given species and the mass of ion species. Thermal stability factor was seen to be constant around 60 for nitrogen, oxygen and cobalt till a fluence of 5×1015 ions/cm2.
Ion species like cobalt may be preferred for some applications where a reduced anisotropy constant without adversely affecting the saturation magnetization and thermal stability of the grains, with increasing fluence, is desirable.
Ion implantation by adjusting the energy of the implanted ions in such a way that ion implantation peak is at the top surface of recording layer and a gradual tail goes deep into the recording layer a continuous gradient of anisotropy across the recording layer can be created. Due to precise control of the doping profile, ion implantation may be very uniform compared to other methods which have been used in the prior art for graded media fabrication.
Whilst there has been described in the foregoing description embodiments of the present invention, it will be understood by those skilled in the technology concerned that many variations in details of design, construction and/or operation may be made without departing from scope as claimed.
This application is a Continuation of application Ser. No. 13/982,987, filed on Jul. 31, 2013, which is a national stage application of International Application No. PCT/SG12/00028, filed on Jan. 31, 2012.
Number | Name | Date | Kind |
---|---|---|---|
20080299416 | Yoon | Dec 2008 | A1 |
20090068500 | Kong et al. | Mar 2009 | A1 |
20090244783 | Shimizu et al. | Oct 2009 | A1 |
20110299194 | Aniya et al. | Dec 2011 | A1 |
Entry |
---|
Abraham, C., et al. “Linear Decrease in the Magnetocrystalline Anisotropy” Physical Review, vol. 120, No. 5. Dec. 1960. pp. 1576-1579. |
Bean, C., et al. “Superparamagnetism” Journal of Applied Physics, Volo. 30, No. 4. Apr. 1959. pp. 120S-129S. |
Charap, S., et al. “Thermal Stability of Recorded Information at High Densities” IEEE Transactions on Magnetics, vol. 33, No. 1. Jan. 1997. pp. 978-983. |
Chen, J., et al. “FEPT-C Graded Media for Ultra-High Denisty Magnetic Recording” Journal of Applied Physics, vol. 43, No. 18. May 2010. pp. 1-5. |
Goll, D., et al. “Magnetic Properties of Exchange-Coupled L10-FEPT/FE Composite Elements” IEEE Transactions on Magnetics, vol. 44, No. 11. Nov. 2008. pp. 3472-3475. |
Moser, A., et al. “Magnetic Recording: Advancing Into the Future” Journal of Applied Physics, vol. 35. Oct. 2002. pp. 157R-167R. |
Piramanayagam, S. “Perpendicular Recording Media for Hard Disk Drives” Journal of Applied Physics, vol. 102, Issue 1. Jul. 2007. pp. 1-22. |
Rottmayer, R., et al. “Heat-Assisted Magnetic Recording” IEEE Transactions on Magnetics, vol. 42, No. 10. Oct. 2006. pp. 2417-2421. |
Suess, D., et al. “Exchange Spring Media for Perpendicular Recording” Applied Physics Letters, vol. 87, Issue 1. Jul. 2005. pp. 1-3. |
Suess, D., et al. “Multilayer Exchange Spring Media for Magnetic Recording” Applied Physics Letters, vol. 89. Sep. 2006. pp. 1-3. |
Victora, R., et al. “Composite Media for Perpendicular Magnetic Recording” IEEE Transactions on Magnetics, vol. 41, No. 2. Feb. 2005. pp. 537-542. |
Zha, C., et al. “Continuously Graded Anisotropy in Singe (FE53PT47)100-XCUX Films” Applied Physics Letters, vol. 97, Issue 18. Nov. 2010. (4 Pages). |
Zha, C., et al. “Gradient Ordered L10FEPTCU Films With Graded Anisotropy” 11th Joint MMM-Intermag Conference. Jun. 2010. p. 771. |
“List of IBM Patents or Patent Applications Treated as Related”. |
Number | Date | Country | |
---|---|---|---|
20150118521 A1 | Apr 2015 | US |
Number | Date | Country | |
---|---|---|---|
61438133 | Jan 2011 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 13982987 | US | |
Child | 14510580 | US |