1. Field of the Invention
The present invention generally relates to the formation of integrated circuits, and, more particularly, to the formation of field effect transistors having a channel region with a specified intrinsic stress to improve the charge carrier mobility.
2. Description of the Related Art
Integrated circuits comprise a large number of individual circuit elements, such as transistors, capacitors and resistors. These elements are connected internally to form complex circuits, such as memory devices, logic devices and microprocessors. The performance of integrated circuits can be improved by increasing the number of functional elements in the circuit in order to increase their functionality and/or by increasing the speed of operation of the circuit elements. A reduction of feature sizes allows the formation of a greater number of circuit elements on the same area, hence allowing an extension of the functionality of the circuit, and also reduces signal propagation delays, thus making an increase of the speed of operation of circuit elements possible.
Field effect transistors are used as switching elements in integrated circuits. They allow control of a current flowing through a channel region located between a source region and a drain region. The source region and the drain region are highly doped. In N-type transistors, the source and drain regions are doped with an N-type dopant. Conversely, in P-type transistors, the source and drain regions are doped with a P-type dopant. The doping of the channel region is inverse to the doping of the source region and the drain region. The conductivity of the channel region is controlled by a gate voltage applied to a gate electrode formed above the channel region and separated therefrom by a thin insulating layer. Depending on the gate voltage, the channel region may be switched between a conductive “on” state and a substantially non-conductive “off” state.
When reducing the size of field effect transistors, it is important to maintain a high conductivity of the channel region in the “on” state. The conductivity of the channel region in the “on” state depends on the dopant concentration in the channel region, the mobility of the charge carriers, the extension of the channel region in the width direction of the transistor and the distance between the source region and the drain region, which is commonly denoted as “channel length.” While a reduction of the width of the channel region leads to a decrease of the channel conductivity, a reduction of the channel length enhances the channel conductivity. An increase of the charge carrier mobility leads to an increase of the channel conductivity.
As feature sizes are reduced, the extension of the channel region in the width direction is also reduced. A reduction of the channel length entails a plurality of issues associated therewith. First, advanced techniques of photolithography and etching have to be provided in order to reliably and reproducibly create transistors having short channel lengths. Moreover, highly sophisticated dopant profiles, in the vertical direction as well as in the lateral direction, are required in the source region and in the drain region in order to provide a low sheet resistivity and a low contact resistivity in combination with a desired channel controllability.
In view of the problems associated with a further reduction of the channel length, it has been proposed to also enhance the performance of field effect transistors by increasing the charge carrier mobility in the channel region. In principle, at least two approaches may be used to increase the charge carrier mobility.
First, the dopant concentration in the channel region may be reduced. Thus, the probability of scattering events of charge carriers in the channel region is reduced, which leads to an increase of the conductivity of the channel region. Reducing the dopant concentration in the channel region, however, significantly affects the threshold voltage of the transistor device. This makes the reduction of dopant concentration a less attractive approach.
Second, the lattice structure in the channel region may be modified by creating tensile or compressive strain. This leads to a modified mobility of electrons and holes, respectively. Depending on the magnitude of the strain, a biaxial tensile strain may increase the mobility of electrons in a silicon layer on an insulating substrate or a substrate comprising an insulating layer provided under the silicon layer by up to 300%, and may also increase the hole mobility when above a 30% SiGe equivalent level. The mobility of holes may also be increased by providing a silicon layer having a compressive strain.
A method of forming a filed effect transistor wherein the channel region is formed in a strained silicon layer provided on an insulating layer will be described in the following with reference to
a shows a schematic cross-sectional view of a semiconductor structure 100 in a first stage of the prior art manufacturing process. A substrate 101, which may, for example, comprise a silicon wafer, is provided. On the substrate, a layer 102 of an insulating material is formed, for example by means of known methods of deposition and/or oxidation. In some examples of prior art processes, the layer 102 of insulating material may comprise silicon dioxide.
In addition to the substrate 101, an auxiliary substrate 103, which is shown in
The strain-creating layer 104 comprises a material having a lattice constant other than the lattice constant of the semiconductor material 105. When the semiconductor material of the layer 105 is deposited on the strain-creating layer 104, the crystalline structure of the semiconductor material 105 is influenced by the crystal lattice of the strain-creating layer 104. Thus, a global biaxial strain can be created in the layer 105 of semiconductor material.
If the lattice constant of the material of the strain-creating layer 104 is greater than the lattice constant which the semiconductor material of the layer 105 adopts in a bulk crystal, the atoms in the layer 105 arrange at a greater distance than in a bulk crystal of the semiconductor material. Thus, the layer 105 of semiconductor material comprises a tensile strain. Conversely, if the lattice constant of the material of the strain-creating layer 104 is smaller than that of the semiconductor material of layer 105 in a bulk crystal, the layer 105 of semiconductor material is formed with an intrinsic compressive strain. In examples of prior art processes wherein the layer 105 of semiconductor material comprises silicon, a strain-creating layer 104 comprising an alloy of silicon and germanium may be used to create a tensile strain. In order to create a compressive strain in the layer 105 when comprising silicon, the strain-creating layer 104 may be made of an alloy of silicon and carbon.
The auxiliary substrate 103 is bonded to the substrate 101. To this end, the auxiliary substrate 103 and the substrate 101 are arranged such that the layer 105 of semiconductor material and the layer 102 of insulating material contact each other, as shown in
A schematic cross-sectional view of the semiconductor structure 100 in a later stage of the manufacturing process according to the state of the art is shown in
A schematic cross-sectional view of the semiconductor structure 100 in a further stage of the manufacturing process according to the state of the art is shown in
Subsequently, a gate electrode 109, which is separated from the active region 181 by a gate insulation layer 108, is formed over the active region. In the formation of the gate electrode 109 and the gate insulation layer 108, as well as in the formation of the shallow trench isolations 106, 107, techniques known to persons skilled in the art, such as advanced methods of deposition, photolithography, etching and oxidation, may be employed.
After the formation of the gate electrode 109, the semiconductor structure 100 is irradiated with ions 110 of a dopant material, which are indicated by arrows in
A further stage of the manufacturing process according to the state of the art is shown in
A problem of the method of forming a field effect transistor according to the state of the art is that the strain-induced enhancement of the mobility of electrons and/or holes in the channel region is significantly reduced at short channel lengths. While in transistors having a relatively large channel length considerably greater than about 50 nm or more, an increase of the drive current by up to 100% may be obtained, in transistors having a relatively short channel length of about 50 nm or less, only an increase of the transistor drive current of about 5-10% is observed.
The present invention is directed to various methods and systems that may solve, or at least reduce, some or all of the aforementioned problems.
The following presents a simplified summary of the invention in order to provide a basic understanding of some aspects of the invention. This summary is not an exhaustive overview of the invention. It is not intended to identify key or critical elements of the invention or to delineate the scope of the invention. Its sole purpose is to present some concepts in a simplified form as a prelude to the more detailed description that is discussed later.
According to an illustrative embodiment of the present invention, a method of forming a field effect transistor comprises providing a substrate comprising a biaxially strained layer of a semiconductor material. A gate electrode is formed on the biaxially strained layer of semiconductor material. A raised source region and a raised drain region are formed adjacent the gate electrode. Ions of a dopant material are implanted into the raised source region and the raised drain region to form an extended source region and an extended drain region.
According to another illustrative embodiment of the present invention, a method of forming a field effect transistor comprises providing a substrate comprising a layer of a semiconductor material. A mask having an opening is formed on the layer of semiconductor material. A recess is formed in a portion of the layer of semiconductor material exposed at a bottom of the opening. On the exposed portion of the layer of semiconductor material, a layer of an insulating material is formed. The opening is filled with a gate electrode material. The mask is selectively removed, wherein at least a portion of the gate electrode material in the opening remains on the substrate to form a gate electrode.
According to yet another illustrative embodiment of the present invention, a semiconductor structure comprises a substrate comprising a layer of a semiconductor material having a biaxial strain and being formed on a layer of an insulating material. A gate electrode is formed over the layer of semiconductor material and a raised source region and a raised drain region are formed adjacent the gate electrode. A source side channel contact region and a drain side channel contact region located adjacent a channel region are subject to the biaxial strain, the channel region being located below the gate electrode.
The invention may be understood by reference to the following description taken in conjunction with the accompanying drawings, in which like reference numerals identify like elements, and in which:
a-1f show schematic cross-sectional views of a semiconductor structure in stages of a manufacturing process according to the state of the art;
a-2c show schematic cross-sectional views of a semiconductor structure in stages of a manufacturing process according to an embodiment of the present invention; and
a-3d show schematic cross-sectional views of a semiconductor structure in stages of a manufacturing process according to another embodiment of the present invention.
While the invention is susceptible to various modifications and alternative forms, specific embodiments thereof have been shown by way of example in the drawings and are herein described in detail. It should be understood, however, that the description herein of specific embodiments is not intended to limit the invention to the particular forms disclosed, but on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the appended claims.
Illustrative embodiments of the invention are described below. In the interest of clarity, not all features of an actual implementation are described in this specification. It will of course be appreciated that in the development of any such actual embodiment, numerous implementation-specific decisions must be made to achieve the developers' specific goals, such as compliance with system-related and business-related constraints, which will vary from one implementation to another. Moreover, it will be appreciated that such a development effort might be complex and time-consuming, but would nevertheless be a routine undertaking for those of ordinary skill in the art having the benefit of this disclosure.
The present invention will now be described with reference to the attached figures. Various structures, systems and devices are schematically depicted in the drawings for purposes of explanation only and so as to not obscure the present invention with details that are well known to those skilled in the art. Nevertheless, the attached drawings are included to describe and explain illustrative examples of the present invention. The words and phrases used herein should be understood and interpreted to have a meaning consistent with the understanding of those words and phrases by those skilled in the relevant art. No special definition of a term or phrase, i.e., a definition that is different from the ordinary and customary meaning as understood by those skilled in the art, is intended to be implied by consistent usage of the term or phrase herein. To the extent that a term or phrase is intended to have a special meaning, i.e., a meaning other than that understood by skilled artisans, such a special definition will be expressly set forth in the specification in a definitional manner that directly and unequivocally provides the special definition for the term or phrase.
The present invention is generally based on the realization that the loss of charge carrier mobility in the channel region of a field effect transistor formed by means of the method according to the state of the art described above with reference to
During the formation of the source extension 111 and the drain extension 112, a portion of the ions 110 impinges in the vicinity of the channel region 123 below the gate electrode and pushes atoms away from their sites. Thus, the order of the strained crystal lattice of the layer 105 of semiconductor material is destroyed and the atoms arrange in an amorphous configuration. Thereby, an at least partial relaxation of the biaxial strain occurs. Such relaxation may occur not only in the source extension 111 and the drain extension 112 which are amorphized but also in the vicinity thereof. Similarly, in the formation of the shallow trench isolations 106, 107, the strain in portions of the layer 105 in the vicinity thereof may relax at least partially.
In field effect transistors having a large channel length of considerably more than about 50 nm, the at least partial relaxation of strain occurs only in a small portion of the channel region 123. In advanced field effect transistors having a channel length of about 50 nm or less, however, those portions of the layer 105 of semiconductor material wherein the biaxial strain is relaxed at least partially may comprise a significant portion of the channel region 181, which can lead to the experimentally observed lower charge carrier mobility in such transistors.
In embodiments of the present invention, a source side channel contact region and a drain side channel contact region located adjacent a channel region of a field effect transistor are subject to a biaxial strain of a layer of semiconductor material wherein the channel region and the channel contact regions are formed. Hence, the biaxial strain is provided all around the channel region, such that substantially no relaxation of strain may occur in the channel region. Thus, a reduction of the charge carrier mobility in the channel region may be substantially avoided.
According to some embodiments of the present invention, a raised source region and a raised drain region are formed in the vicinity of the gate electrode of the field effect transistor. In the formation of a source extension and a drain extension of the transistor, ions of a dopant material are implanted into the raised source region and the raised drain region. Thus, an amorphization of the source side channel contact region and the drain side channel contact region and a relaxation of the biaxial strain induced thereby may be substantially avoided. Thus, the biaxial strain in the channel contact regions may be maintained. Thereafter, an annealing process may be performed. In the annealing process, the dopant material may diffuse into the channel contact regions. Since the diffusion of the dopant material can occur without there being a relaxation of strain, the channel contact regions can remain subject to the biaxial strain.
In other embodiments of the present invention, the gate electrode of the field effect transistor can be formed in a recess of a layer of semiconductor material. Thus, the channel region of the field effect transistor which is located below the gate electrode is lowered relative to the surface of the layer of semiconductor material in and on which the field effect transistor is formed. Thus, an amorphization and a corresponding relaxation of strain in the vicinity of the channel region may also be substantially avoided when an ion implantation is performed to form the extended source region and the extended drain region.
In the following, further embodiments of the present invention will be described with reference to
Similar to the formation of the semiconductor structure 100 by means of the prior art method described above with reference to
In some embodiments of the present invention, the layer 205 of semiconductor material can comprise silicon. In such embodiments, a strain-creating layer comprising an alloy of silicon and germanium may be used to create a biaxial tensile strain in the layer 205, whereas a strain-creating layer comprising an alloy of silicon and carbon can be used to create a biaxial compressive strain in the layer 205.
The layer 202 of insulating material is formed on the substrate 201. Thereafter, the auxiliary substrate is bonded to the substrate 201, wherein the layer 205 of semiconductor material contacts the layer 202 of insulating material. This may be done by means of a bonding process known to persons skilled in the art. Then, the auxiliary substrate and the strain-creating layer are removed by means of known methods such that the layer 205 of semiconductor material is exposed on the surface of the substrate 201. Similar to the method according to the state of the art described above, the biaxial strain in the layer 205 is maintained after the removal of the auxiliary substrate and the strain-creating layer.
The shallow trench isolations 206, 207 can be formed by means of known advanced methods of photolithography, etching, deposition and/or oxidation. In the formation of the active region 281, which may be performed after the formation of the shallow trench isolations 206, 207, an ion implantation may be performed to introduce a dopant material into the layer 205 of semiconductor material. Thereafter, the gate insulation layer 208, the gate electrode 209, the offset spacers 210, 211 and the cap layer 212 can be formed using known methods of photolithography, etching, deposition and/or oxidation.
In some embodiments of the present invention, the shallow trench isolations 206, 207, the offset spacers 210, 211 and the cap layer 212 can comprise silicon dioxide, silicon nitride and/or silicon oxynitride. The gate electrode 209 can comprise polysilicon.
A raised source region 213 and a raised drain region 214 are formed adjacent the gate electrode 209. This can be done by means of selective epitaxial growth. Selective epitaxial growth is a variant of plasma enhanced chemical vapor deposition wherein a layer of material is deposited only over exposed portions of the layer 205 of semiconductor material, whereas there is no deposition in portions of the semiconductor structure 200 comprising other materials than the semiconductor material of the layer 205.
In plasma enhanced chemical vapor deposition, which is a process well known to persons skilled in the art, the semiconductor structure 200 is inserted into a reactor. Reactant gases are supplied to the reactor. A radio frequency electric voltage and/or a DC bias voltage are applied to the reactant gases and/or the semiconductor structure 200 to induce a glow discharge wherein reactive precursors are formed from the reactant gases. At the surface of the semiconductor structure 200 and/or in the vicinity thereof, the reactive precursors and/or the reactant gases react chemically with each other. In this chemical reaction, a material is formed which is then deposited on the semiconductor structure 200. Products of the chemical reaction other than the deposited material are removed from the reactor.
The properties of the material layer deposited in plasma enhanced chemical vapor deposition is influenced by parameters such as temperature, pressure, composition of the reactant gas, as well as the electric power supplied via the radio frequency electric voltage and/or the DC bias voltage. In selective epitaxial growth performed in the formation of the raised source region 213 and the raised drain region 214, these parameters are adapted such that material deposition occurs substantially only on portions of the semiconductor structure 200 wherein the semiconductor material of the layer 205 is exposed. The deposited material adapts to the crystal structure of the layer 205 of semiconductor material. Thus, epitaxial growth is obtained.
In embodiments of the present invention wherein the layer 205 of semiconductor material comprises silicon and the shallow trench isolations 206, 207, as well as the cap layer 212 and the offset spacers 210, 211, comprise silicon dioxide and/or silicon nitride, the selective epitaxial growth process may be adapted to selectively deposit silicon on portions of the layer 205 of semiconductor material exposed adjacent the gate electrode 209.
In such embodiments, SiCl4 and H2 can be used as reactants. At growth temperature, these reactants react to silicon and hydrochloric acid. The reaction can proceed in both directions. The etching created in the back-reaction is important in the inhibition of silicon growth on the shallow trench isolations 206, 207 and the cap layer 212 as well as the offset spacers 210, 211.
After the formation of the raised source region 213 and the raised drain region 214, an ion implantation can be performed wherein a beam comprising ions 220 of a dopant material is directed to the semiconductor structure 200. The ions 220 impinge on the surface of the semiconductor structure 200, in particular on the surface of the raised source region 213 and the raised drain region 214. The ions have a speed relative to the raised source region 213 and the raised drain region 214 which depends on the energy of the ions 220. The energy of the ions 220 may be controlled by controlling a voltage which is used to accelerate the ions 220. At least a portion of the ions 220 penetrates the raised source region 213 and the raised drain region 214 and interacts with atoms in the raised source region 213 and the raised drain region 214. Due to this interaction, the ions loose energy. Thus, the ions 220 are decelerated and, finally, stopped. A penetration depth P to which the ions 220 penetrate the raised source region 213 and the raised drain region 214 depends on the energy of the ions 220 as well as the type of ions and the material properties of the raised source region 213 and the raised drain region 214. Thus, the penetration depth P may be controlled by varying one or more of these parameters. In particular, the penetration depth can be controlled by varying the energy of the ions 220. An ion dose applied in the ion implantation can be such that the raised source region 213 and the raised drain region 214 or portions thereof are amorphized.
The penetration depth P of the ions 220 can be equal to or smaller than a depth d of the raised source region 213 and the raised drain region 214. Thus, substantially no ions 220 penetrate the layer 205 of semiconductor material. Therefore, substantially no amorphization of the layer 205 of semiconductor material occurs and substantially no relaxation of the biaxial strain in the layer 205 occurs. Thus, the layer 205 of semiconductor material remains biaxially strained. In particular, a source side channel contact region 221 and a drain side channel contact region 222, which are located below the raised source region 213 and the raised drain region 214, respectively, and adjacent a channel region 223 located below the gate electrode 209, remain biaxially strained.
A schematic cross-sectional view of the semiconductor structure 200 in a further stage of the manufacturing process is shown in
Then, a further ion implantation can be performed to form a source region 217 and a drain region 218, as indicated by arrows 290 in
The sidewall spacers 219, 220 absorb ions impinging thereon. Thus, the source region 217 and the drain region 218 are spaced apart from the gate electrode 209 and the channel region 208 such that the source region 217 and the drain region 218 do not overlap the source side channel contact region 221 and the drain side channel contact region 222.
An ion dose applied in the formation of the source region 217 and the drain region 218 may be adapted such that the material of portions of the raised source region 213, the raised drain region 214 and the layer 205 of semiconductor material which are exposed to the bombardment of ions is at least partially amorphized. Since, however, the source region 217 and the drain region 218 do not overlap the source side channel contact region 221 and the drain side channel contact region 222, the latter regions are not amorphized. Hence, there is no amorphization of the channel contact regions 221, 222 such that there is no relaxation of strain in the channel contact regions 221, 222. Thus, the channel contact regions 221, 222 remain biaxially strained.
The source region 217 and the drain region 218 need not overlap the layer 205 of semiconductor material. In other embodiments of the present invention, a depth of the source region 217 and the drain region 218 can be smaller than the thickness d of the raised source region 213 and the raised drain region 214. Thus, the source region 217 and the drain region 218 are provided in the raised source region 213 and the raised drain region 214, respectively.
A schematic cross-sectional view of the semiconductor structure 200 in a further stage of the manufacturing process is shown in
In the annealing process, a re-crystallization of the amorphized material in the extended source region 215, the extended drain region 216, the source region 217 and the drain region 218 may occur. In the re-crystallization, the atoms in the amorphized regions re-arrange and assume a crystalline order. Additionally, in the annealing process, the dopant material introduced in the ion implantation is incorporated into the crystal lattice of the semiconductor layer 205 and/or the raised source region 213 and the raised drain region 214 such that dopant atoms may act as electron donors or acceptors.
Furthermore, a diffusion of dopant atoms may occur in the annealing process. Due to diffusion, the dopant distribution in the semiconductor structure 200 is altered. In particular, dopant atoms may leave those portions of the semiconductor structure 200 which were exposed to the ion bombardment in the ion implantation processes and enter neighboring portions of the semiconductor structure 200. In particular, dopant atoms may diffuse into the source side channel contact region 221 and the drain side channel contact region 216 adjacent the channel region 223. Thus, the extended source region 215 and the extended drain region 216, the doping of which is inverse to that of the channel region 223, may grow until they include the source side channel contact region 221 and the drain side channel contact region 222. Dopant diffusion, however, does not substantially alter the biaxial strain of the layer 205 of semiconductor material. Thus, the channel contact regions 221, 222 are doped, but remain biaxially strained.
An annealing process adapted to induce dopant diffusion into the source side channel contact region 221 and the drain side channel contact region 222 need not be performed after the formation of the source region 217 and the drain region 218. In other embodiments of the present invention, such annealing can be performed after the formation of the extended source region 215 and the extended drain region 216. Thus, a diffusion of the dopant material introduced into the extended source region 215 and the extended drain region 216 can be controlled independently of the diffusion of the dopant material introduced into the source region 217 and the drain region 218. Advantageously, this allows a more precise control of the distribution of the dopant material.
As detailed above, the present invention allows the formation of the field effect transistor 280 wherein a relaxation of the biaxial strain of the layer 205 of semiconductor material in the channel region 223 and the adjacent channel contact regions 221, 226 may be substantially avoided or reduced. Thus, a reduction of the charge carrier mobility in these regions and, in particular, in the channel region 223, which is caused by the relaxation of strain, may be reduced compared to a field effect transistor formed by means of the prior art method described above with reference to
Further embodiments of the present invention will be described with reference to
Similar to the formation of the semiconductor structure 200 described above with reference to
A mask 350 is formed on the layer 305 of semiconductor material. The mask 350 can comprise a dielectric material, for example silicon dioxide, silicon nitride and/or silicon oxynitride. The formation of the mask 350 can be performed by means of known deposition techniques comprising chemical vapor deposition and/or plasma enhanced chemical vapor deposition.
An opening 360 is formed in the mask 350. This can be done by means of advanced photolithographic techniques well known to persons skilled in the art. The opening 360 is provided between the shallow trench isolations 306, 307 at a location where it is planned to provide a gate electrode of a field effect transistor to be formed in the semiconductor structure 300.
In some embodiments of the present invention, a length of the opening 360 can be reduced. To this end, a material layer 351 is deposited over the semiconductor structure 300 by means of a known deposition process. The deposition process can be isotropic such that a thickness of the material layer 351 over substantially horizontal portions of the mask 350 and the layer 305 of semiconductor material is substantially equal to a thickness of the material layer 351 over inclined portions of the mask 350 such as the sidewalls of the opening 360, wherein the thickness is measured in a direction substantially perpendicular to the surface of the layer 351 at the respective location. The material of the layer 351 can be identical to the material of the mask 350. In other embodiments of the present invention, different materials may be used for the mask 350 and the material layer 351.
A schematic cross-sectional view of the semiconductor structure 300 in a later stage of the manufacturing process is shown in
A recess 370 is formed in a portion of the layer 305 which is exposed at the bottom of the opening. To this end, an etching process can be performed wherein the semiconductor structure 300 is exposed to an etchant adapted to selectively remove the material of the layer 305 of semiconductor material, leaving the mask 350 and the spacing elements 352, 353 substantially intact. In some embodiments of the present invention, the etching process can be anisotropic such that a length of the recess 370 is substantially equal to the length of the opening 360. In other embodiments of the present invention, an isotropic etching process can be performed to form the recess 370. The recess 370 can have a depth d′.
On the bottom of the recess 370, a gate insulation layer 308 is formed on the exposed portion of the layer 305 of semiconductor material which may be done by means of oxidation and/or deposition processes well known to persons skilled in the art.
The opening 360 and the recess 370 are filled with a gate electrode material, for example, polysilicon. To this end, a layer 354 of the gate electrode material is deposited over the semiconductor structure 300, which may be done by means of deposition processes known to persons skilled in the art. Then, the semiconductor structure 300 is planarized, which, in some embodiments of the present invention, can be done by means of a chemical mechanical polishing process.
In chemical mechanical polishing, the semiconductor structure 300 is moved relative to a polishing pad. A slurry is supplied to an interface between the semiconductor structure 300 and the polishing pad. The slurry comprises a chemical compound which reacts with the material on the surface of the semiconductor structure 300, in particular with the gate electrode material and/or the material of the mask 350 and the spacing elements 352, 353. Products of the chemical reaction are removed by means of an abrasive component in the slurry.
In the chemical mechanical polishing process, portions of the layer 354 of gate electrode material located over the mask 350 are removed. Additionally, in some embodiments of the present invention, the chemical mechanical polishing process may remove portions of the mask 350 and a portion of the gate electrode material in the opening 370. Thus, rounded edges of the spacing elements 352 and/or the opening 360 at the top of the opening, as well as a portion of the gate electrode material in the vicinity of the top of the opening 360, having a length greater than the length of the opening 360 at its bottom may be removed.
After the chemical mechanical polishing process, the mask 350 is exposed at the surface of the semiconductor structure 300 and the opening 360 is filled with a plug comprising the gate electrode material.
A schematic cross-sectional view of the semiconductor structure 300 in a further stage of the manufacturing process is shown in
Similar to the embodiments of the present invention described above with reference to
A schematic cross-sectional view of the semiconductor structure 300 in a further stage of the manufacturing process is shown in
The diffusion of dopant material substantially does not alter the biaxial strain in the channel contact regions 321, 322. Thus, the source side channel contact region 321 and the drain side channel contact region 322 are formed with a biaxial strain. Hence, there is substantially no relaxation of the biaxial strain in the channel region 323 and, consequently, a reduction of the charge carrier mobility in the channel region 323 can be substantially avoided.
The present invention may be applied in order to form field effect transistors having a channel length (indicated as “1” in
As detailed above, the manufacturing method described above with reference to
The particular embodiments disclosed above are illustrative only, as the invention may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. For example, the process steps set forth above may be performed in a different order. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. It is therefore evident that the particular embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of the invention. Accordingly, the protection sought herein is as set forth in the claims below.
Number | Date | Country | Kind |
---|---|---|---|
10 2006 019 934.0 | Apr 2006 | DE | national |
Number | Date | Country | |
---|---|---|---|
Parent | 11566287 | Dec 2006 | US |
Child | 12752487 | US |