Patent Application
20200079035
This disclosure relates generally to a method of forming a sporting implement. More particularly, aspects of this disclosure relate to forming a sporting implement using thermoplastic materials and fibers.
Many sporting implements are formed with glass or carbon fiber reinforced composite structures. These composite structures can be formed with thermoset resins (epoxies), which are not very resistant to impact, and may delaminate at the interface between fiber layers.
Fiber reinforced thermoplastic sporting elements have been made from thermoplastic pre-impregnated carbon/glass tapes that are laminated at various angles and then pressed at a high temperature above the melting point of that specific thermoplastic. Other fiber reinforced thermoplastic sporting elements use co-mingled fibers (carbon fiber interlaced with thermoplastic yarn) to create braids or woven fabric, which is placed in a mold and then heated again above the melting point of that specific thermoplastic. These materials typically require high processing temperatures and pressure.
It may be desirable to provide a method of forming fiber reinforced thermoplastic items that reduces or overcomes some or all of the difficulties inherent in prior known devices. Particular objects and advantages will be apparent to those skilled in the art, that is, those who are knowledgeable or experienced in this field of technology, in view of the following disclosure and detailed description of certain embodiments.
The following presents a general summary of aspects of the invention in order to provide a basic understanding of the invention and various features of it. This summary is not intended to limit the scope of the invention in any way, but it simply provides a general overview and context for the more detailed description that follows.
In accordance with a first aspect, a method of forming a sporting implement may include placing a plurality of fibers in a cavity formed in a first portion of a mold, where the mold has an inlet and an outlet. A second portion of the mold can be positioned in contact with the first portion such that the cavity cooperates with the second portion of the mold to define a chamber. A first material can be mixed with a second material to form a thermoplastic resin. The thermoplastic resin can be injected into the chamber through the inlet. The inlet and outlet are closed, and the thermoplastic resin completely polymerizes so as to form a fiber reinforced sporting element in the chamber the sporting element is removed from the chamber.
These and additional features and advantages disclosed here will be further understood from the following detailed disclosure of certain embodiments, the drawings thereof, and from the claims.
The foregoing and other features and advantages of the present embodiments will be more fully understood from the following detailed description of illustrative embodiments taken in conjunction with the accompanying drawings in which:
The figures referred to above are not drawn necessarily to scale, should be understood to provide a representation of particular embodiments, and are merely conceptual in nature and illustrative of the principles involved. Some features of the mold assembly and components depicted in the drawings have been enlarged or distorted relative to others to facilitate explanation and understanding. The same reference numbers are used in the drawings for similar or identical components and features shown in various alternative embodiments. Mold assemblies as disclosed herein would have configurations and components determined, in part, by the intended application and environment in which they are used.
In the following description of various example structures in accordance with the disclosure, reference is made to the accompanying drawings, which form a part hereof, and in which are shown by way of illustration of various structures in accordance with the disclosure. Additionally, it is to be understood that other specific arrangements of parts and structures may be utilized, and structural and functional modifications may be made without departing from the scope of the present disclosure. Also, while the terms “top” and “bottom” and the like may be used in this specification to describe various example features and elements of the disclosure, these terms are used herein as a matter of convenience, e.g., based on the example orientations shown in the figures and/or the orientations in typical use. Nothing in this specification should be construed as requiring a specific three dimensional or spatial orientation of structures in order to fall within the scope of this disclosure.
In general, as discussed herein, aspects of this disclosure relate to methods for fabricating sporting implements with in-situ polymerizable thermoplastic materials and fibers. The thermoplastic materials and fibers can be incorporated into any sporting implements, such as baseball bats, lacrosse sticks, hockey sticks, rackets, helmets, and other protective equipment.
Referring to
To form a sporting element in mold assembly 10, a plurality of fibers 22 are placed in cavity 14. In certain embodiments, fibers 22 are dry fibers. Fibers 22 may be braided fibers, woven fibers or fabric, or stitched tapes, for example. Exemplary fibers include carbon, glass, and aramid, for example. In certain embodiments, fibers 22 are elongate elements with a length significantly greater than their thickness or diameter. Fibers 22 may have a diameter of approximately 6.8 μm. The length of fibers 22 may vary depending on their location in cavity 14 and their ultimate location in the sporting element to be formed in mold assembly 10. For example, in an embodiment where the sporting element to be formed is a blade for a hockey stick, some fibers 22 may extend from one end of the blade to the other, and have a length of approximately 300 mm. In other embodiments, fibers 22 may be only a few mm long if, for example, they are positioned in the mold such that they are in the throat at an angle.
The term “approximately” as used herein is meant to mean close to, or about, a particular value, within the constraints of sensible commercial engineering objectives, costs, manufacturing tolerances, and capabilities in the field of manufacturing implements formed of thermoplastic materials and fibers. Similarly, the term “substantially” as used herein is meant to mean mostly the same as, or almost the same as, within the constraints of sensible commercial engineering objectives, costs, manufacturing tolerances, and capabilities in the field of manufacturing implements formed of thermoplastic materials and fibers.
In certain embodiments, fibers 22 may be randomly dispersed within cavity 14. In other embodiments, fibers 22 can be oriented in an orderly pattern within cavity 14. For example, fibers 22 can be woven. In certain embodiments, fibers 22 can be woven in a 3D structure having fibers oriented in three directions, namely the X direction (warp), the Y direction (weft), and the Z direction. An exemplary 3D woven fiber structure is described in U.S. application Ser. No. 15/448,769, the entire disclosure of which is incorporated herein by reference in its entirety.
In certain embodiments, fibers 22 may be coated in order to facilitate positioning of dry fibers 22 in cavity 14. Exemplary coatings for fibers 22 include epoxy, polyurethane, and aerosol adhesives. Other suitable coatings for fibers 22 will become readily apparent to those of skill in the art, given the benefit of this disclosure.
After fibers 22 are placed in cavity 14, a second portion 24 of mold assembly 10 is placed in contact with first portion 12, as illustrated in
With second portion 24 in contact with first portion 12, chamber 28 is in fluid communication with an exterior of mold assembly 10 by way of inlet 18 and by way of outlet 20.
In certain embodiments, it may be advantageous to reduce the humidity level in chamber 28. In order to do so, a vacuum pump 30 may be operably connected to chamber 28 by way of outlet 20 so as to create a vacuum within chamber 28. In other embodiments, a vacuum bag (not shown) could be placed over first portion 12 in the place of second portion 24.
Additionally, chamber 28 may be purged with a gas to help prevent moisture or any other contamination from affecting the formation of the sporting element within mold assembly 10. As seen in
The in-situ polymerization of a thermoplastic resin with fibers 22 in chamber 28 will now be discussed. As seen in
First resin material 36 and second resin material 40 are combined in a mixing chamber 42 to form a polymerizable thermoplastic resin 44. It is to be appreciated that thermoplastic resin 44 may be a thermoplastic matrix including nylon, polyurethane, or acrylic. In certain embodiments, first resin material 36 may be an acrylic monomer and second resin material 40 may be peroxide, which initiates polymerization of the acrylic monomer.
It is to be appreciated that mixing chamber 42 may be a static mixer or a dynamic mixer.
Thermoplastic resin 44 is then injected through inlet 18 into chamber 28 until chamber 28 is full. As illustrated in
Thermoplastic resin 44 is able to be injected into chamber 28 at low temperatures (i.e., room temperature) due to its low viscosity. In certain embodiments, thermoplastic resin 44 can be injected into chamber 28 at a temperature of between approximately 20° C. and approximately 60° C. Injection at such low temperatures reduces tooling needs and costs, thereby resulting in a less complex and less expensive manufacturing process.
Due to the low viscosity of the mixed thermoplastic resin 44, impregnation of fibers 22 with the resin is easier to accomplish. Thus, even with a fiber content above 50%, fibers 22 can be impregnated with thermoplastic resin 44.
The mixing of thermoplastic resin 44, rather than using pre-formed resin pellets helps reduce manufacturing costs and processing time.
With such a process, sporting elements with complex geometries can be formed in mold assembly 10. Further, such sporting elements have improved impact resistance, fatigue resistance, and delamination resistance.
The mixture of fibers 22 and thermoplastic resin 44 within chamber 28 will then polymerize and become a solid, thereby forming a fiber reinforced thermoplastic sporting element 50 having a shape matching that of chamber 28. Upon complete curing of sporting element 50, its melt temperature will be much higher, typically greater than approximately 200° C.
As seen in
As seen in
Advantageously, the sporting implements can be recycled since the thermoplastic resin can be reformed. Thus, if a hockey stick or baseball bat formed with this process is broken or compromised during use, it does not need to be thrown away. Rather, it can be recycled, or even repaired by applying heat and pressure to the sporting implement and thereby repairing/recycling the structure.
In another embodiment, as illustrated in
As seen in
Precursor 74 of fibers 64 and mat 70 may be fed through a guide 76 into a resin impregnator 78. Guide 76 may serve to form precursor 74 into a desired cross-sectional profile. In the illustrated embodiment, precursor 74 is formed in guide 76 to have a rectangular cross-section, which is suitable for forming a shaft for a hockey stick. In other embodiments, precursor 74 could be formed with a circular or elliptical cross-section. It is to be appreciated that guide 76 can be configured to provide any desired cross-sectional profile for precursor 74 depending on the desired characteristics of the shaft, which may include the flex profile and weight of the shaft.
Resin may then be injected into the fibers 64 and mat 70 of precursor 74 in resin impregnator 78. The resin injected into and impregnated in fibers 64 and mat 70 in precursor 74 may be a liquid thermoplastic such as nylon, polyurethane, or acrylic, for example. Other suitable resins will become readily apparent to those skilled in the art, given the benefit of this disclosure. In certain embodiments, resin may be at a temperature of approximately 70° C. as it is injected into fibers 64 and mat 70 of precursor 74 in resin impregnator 78.
Precursor 74 may then be fed into a die 86, where heat may be applied to precursor 74, thereby curing precursor 74 and forming a continuous linear member 88, which can ultimately be cut into individual sporting elements 62. The temperature of die 86 may vary along its length, and may be dependent on the speed at which precursor 74 is pulled through pultrusion device 60. In certain embodiments, in a front, or first portion 90 of die 86, a temperature of die 86 may be approximately 85° C., with precursor 74 traveling through pultrusion device 60 at a speed of approximately 8-12 cm/min. In a central, or second portion 92 of die 86 downstream of first portion 90, a temperature of die 86 may be approximately 95° C. In a rear, or third portion 94 of die 86 downstream of second portion 92, a temperature of die 86 may be approximately 105° C. It is to be appreciated that the temperature of die 86 may be dependent on the speed at which precursor 74 is travelling through die 86, with slower speeds requiring lower temperatures and faster speeds requiring higher temperatures in order to properly cure precursor 74. In certain embodiments, precursor 74 may travel through pultrusion device 60 at a speed of approximately 1 m/min., which would result in different temperatures of die 86 at first portion 90, second portion 92, and third portion 94.
In the illustrated embodiment, resin impregnator 78 is upstream of die 86, with performer 84 positioned between resin impregnator 78 and die 86. It is to be appreciated that in certain embodiments, resin impregnator 78 could be immediately adjacent and upstream of die 86.
A controller 96 may be used to control pultrusion device 60, controlling parameters such as the speed at which precursor 74 travels through pultrusion device 60, and the temperature at resin impregnator 78 and die 86. Controller 96 may include a touch screen 98 in certain embodiments, providing an operator an easy to use interface to control pultrusion device 60.
One or more pulling devices 100 may be positioned downstream of die 86, which may serve to pull precursor 74 and linear member 88 through pultrusion device 60. In certain embodiments, a pair of reciprocating pulling devices 100 may operate in alternating fashion to grasp linear member 88 and pull precursor 74 through pultrusion device 60.
A cutting device 102 may be positioned downstream of pulling devices 100, and may serve to cut linear member 88 into individual sporting elements 62 having a predetermined length. As noted above, the illustrated embodiment shows a parallel pair of precursors 74 and corresponding linear members 88 being cut into corresponding pairs of sporting elements 62. In certain embodiments, cutting device 102 may be a saw. It is to be appreciated that in other embodiments cutting device 102 can be a heated blade. Other suitable cutting devices will become readily apparent to those skilled in the art, given the benefit of this disclosure.
In the illustrated embodiment, a second sporting element 62 is formed simultaneously side-by-side with sporting element 62 in pultrusion device 60. It is to be appreciated that in other embodiments a single sporting element 62, or more than two such sporting elements 62, could be formed in pultrusion device 60.
An alternative embodiment is illustrated in
In certain embodiments, as illustrated in
Those having skill in the art, with the knowledge gained from the present disclosure, will recognize that various changes can be made to the disclosed apparatuses and methods in attaining these and other advantages, without departing from the scope of the present disclosure. As such, it should be understood that the features described herein are susceptible to modification, alteration, changes, or substitution. For example, it is expressly intended that all combinations of those elements and/or steps which perform substantially the same function, in substantially the same way, to achieve the same results are within the scope of the embodiments described herein. Substitutions of elements from one described embodiment to another are also fully intended and contemplated. The specific embodiments illustrated and described herein are for illustrative purposes only, and not limiting of that which is set forth in the appended claims. Other embodiments will be evident to those of skill in the art. It should be understood that the foregoing description is provided for clarity only and is merely exemplary. The spirit and scope of the present disclosure is not limited to the above examples, but is encompassed by the following claims. All publications and patent applications cited above are incorporated by reference in their entirety for all purposes to the same extent as if each individual publication or patent application were specifically and individually indicated to be so incorporated by reference.
This application claims priority to U.S. Provisional Application No. 62/730,232, filed Sep. 12, 2018, which is hereby incorporated by reference in its entirety.