Method of forming a stabilized vulcanizate of chloro rubbers and said vulcanizate

Abstract

Calcium aluminum hexahydrate is a useful curative-stabilizer for halogenated rubbers such as chloronated polyethylene, chlorosulfonated polyethylene and polychloroprene as it can yield vulcanizates free of leachable lead. Also, these vulcanizates with about 1 to about 30 or more parts with about 3 to about 15 parts calcium aluminum hexahydrate being highly desirable give satisfactory to improved heat ageing properties as well as oil ageing properties.

Description

FIELD

This invention relates to an improved method to vulcanize or cure halogenated rubbers and to the resulting vulcanizates. By this method, the halogenated rubbers are vulcanized with an activator or activators to give a vulcanizate free of poisonous lead and having physical properties essentially equal to lead vulcanizates. More specifically, this invention relates to a vulcanizate of a halogenated rubber containing from 1 to about 30 and higher parts of calcium aluminum hexahydrate.

BACKGROUND OF THE INVENTION

Halogenated rubbers such as chlorosulfonated polyethylene and chlorinated polyethylene require activators to aid in curing the rubber and to stabilize the cured rubber. In the case of chlorosulfonated polyethylene and chlorinated polyethylene rubbers, metal oxides, and hydroxides of lead, cadmium, magnesium, calcium and barium have been used as activators and stabilizers. Toxicity concerns have decreased the use of barium, cadmium and lead which leaves calcium and magnesium as the most common stabilizer. These are known to be moisture sensitive and cause water absorption and are very unsatisfactory for producing vulcanizates for tank linings.

In the case of polychloroprene rubber, oxides of zinc and magnesium and lead are commonly used to activate the cure and stabilize the vulcanizate. Zinc is known to produce moisture sensitivity, resulting in water absorption. In cases where water immersion is needed, lead oxides are preferred in place of zinc oxide and magnesium oxide. Landfill requirements require a limited lead content in acidic leachate tests and lead stabilized polymers are recognized as a disposal problem. Consequently, a need exists for an improved curative-stabilizer for the halogenated rubber vulcanizates other than lead salts.

FIG. 1 is a cross-sectional view through the tank 2 of a tank truck showing the Neoprene lining 3 cured with calcium aluminum hexahydrate.

The halogen-containing rubbers used in this invention are known and can be properly selected. Examples include halogen-containing olefin rubbers such as chlorinated polyethylene rubber, chlorinated polypropylene rubber, chlorosulfonated polyethylene rubber, chlorinated ethylene/propylene rubber, chlorinated ethylene/propylene/diene rubber, chlorinated ethylene/1-butene rubber, chlorinated ethylene/4-methylpentene rubber, chlorinated butyl rubber, and epihalohydrin rubbers such as polyepichlorohydrin rubber, epichlorohydrin/ethylene oxide copolymer rubber and epichlorohydrin/allyl glycidyl ether copolymer rubber, fluorine rubbers; chlorine-containing and polychloroprene rubbers.

We have discovered that the use of calcium aluminum hexahydrate in the curing recipes for halo rubbers yields vulcanizates with improved stabilizing effects in heat ageing, oil ageing and hydraulic fluid ageing relative to the vulcanizates of halo rubbers cured with a recipe containing the industry's best curative, lead oxide. This, indeed, is an important discovery in view of the fact lead oxide vulcanizates present a disposal problem due to the problem of ground water contaminated by extracted lead. Further, these improved properties of the invention vulcanizates make these invention vulcanizates desirable for use in making Freon hose, hydraulic hose as well as gaskets, seals and other industrial products like underground cable coating and tank linings.

Synthetic crystalline calcium aluminum hexahydrate produces a high state of cure in polychloroprene rubbers while eliminating the stabilizer lead oxide or magnesium oxide/zinc oxide combination. Hence, if the harmful effects of environmental contamination by lead forces lead's replacement, the instant invention would be preferred for a replacement for lead with advantages in heat ageing, oil ageing and hydraulic fluid ageing.

The useful calcium aluminum hexahydrate is also called tri-calcium aluminate hexahydrate with the formula Ca.sub.3 Al.sub.2 (OH).sub.12 and is available from the Huber Corporation.

The calcium oxide and calcium and magnesium salts of the organic acids, for instance, phthalic acids, and specifically terephthalic acid are useable to advantage in curing and producing these vulcanizates with calcium aluminum hexahydrate.

The BET specific surface area of the compound of the above formula may be properly chosen, and is preferably about 20 to about 100 m.sup.2 /g. The particle diameter of the compound of the formula is preferably small to obtain good dispersibility in a rubber material. For example, it has a secondary particle diameter of about 0.1 to about 10 microns.

The curative product of the stabilized formula used in this invention can have specific surface area, for example, about 20 to about 300 m.sup.2 /g, preferably about 20 to about 200 m.sup.2 /g, and a particle diameter of about 0.1 to about 10 microns.

The curable rubber composition may contain various compounding agents known in the art such as fillers, reinforcing agents, plasticizers, processing aids, cross-linking agents, antioxidants, pigments and fire retardants. These compounding agents may be used in amounts generally known in the art. For examples, the amounts may be about 5 to about 200 phr for the fillers, about 5 to about 150 phr for the reinforcing agents, about 1 to about 20 phr for the plasticizers, about 1 to about 10 phr for the processing aids, about 0.1 to about 10 phr for the cross-linking agents, about 0.1 to about 10 phr for the antioxidants, about 0.1 to about 10 phr for the pigments and about 1 to about 200 phr for the fire retardants, each based on the weight of the one hundred parts of halogen-containing rubber.

Examples of the fillers include carbon black, silicic anhydride, hydrous silicic acid, calcium silicate, aluminum silicate, clay, talc, calcium carbonate, basic magnesium carbonate, alumina hydrate, diatomaceous earth, barium sulfate, mica, alumina sulfate, lithopone, asbestos and graphite.

Examples of the reinforcing agents include high-styrene resins, coumarone-indene resin, phenolic resins, modified melamine resins, petroleum resins, lignin, cotton, rayon, nylon, Vinylon, polyesters, glass fibers, carbon fibers and steel cords.

Examples of the plasticizers include pine tar, tall oil, rapeseed oil, cottonseed oil, peanut oil, castor oil, palm oil, mineral oil-type softeners, phthalic acid derivatives (e.g., DBP, DHP, DOP, and DIDP), sebacic acid derivatives such as DES and DOS and adipic acid derivatives (such as DOA and DIOA).

Examples of the processing aids include Struktol WB212 (a mixture of high-molecular-weight fatty acid esters) and RP-10 (dixylyl disulfide mixture); and rubber hardening agents such as benzidine, p-aminophenol and p-phenylenediamine.

Examples of the pigments include titanium white, lithopone, zinc sulfide, cadmium red, cadmium yellow, barium yellow, strontium yellow, chrome yellow, ultramarine, Prussian blue, cobalt blue, chromium oxide, cobalt green, carbon black, Hansa Yellow G, Lake Red C, benzidine orange, phthalocyanine blue, and phthalocyanine green.

Examples of the fire retardants include aluminum hydroxide, magnesium hydroxide, antimony trioxide, tetrabromobisphenol A, chlorinated paraffin, tricresyl phosphate, triethyl phosphate, perchloropentacyclodecane and chlorinated polyphenyl.

To further illustrate and exemplify the invention, a number of chloronated rubbers were compounded and tested. In a clean cold banbury, the compounding ingredients listed in Tables 1 and 3 below were mixed in the amounts by weight until the mixture in the banbury reach 180.degree. F. and then mixed an additional minute after the accelerator and the acid scavenger was added and the mixture was dropped from the banbury when the temperature reached 260.degree. F.

The nature of these mixes is shown in Tables 1 and 3 and the properties of their vulcanizates is shown in Tables 2 and 4.

The chlorosulfonated polyethylene compositions were cured at 310.degree. F. for a time equal to the Rheometer T90 plus 10%. The polychloroprene compositions were cured at 300.degree. F. for a time equal to the Rheometer T90 plus 10%.

______________________________________Table 1 of RecipesIngredients A B C D______________________________________Chlorosulfonated 100 100 100 100polyethyleneCarbon black 75 75 75 75PEG* 3 3 3 3PE wax 3 3 3 3TOTM 15 15 15 15Litharge 10Lime (CaO) 10Mg (OH).sub.2 10Calcium aluminum 10hexahydrateCurative 3.5 3.5 3.5 3.5Totals 209.50 209.50 209.50 209.50Sp. Gr. 1.382 1.358 1.362 1.363______________________________________ *PEG designates a polyethylene glycol of varying molecular weight or a wa of the PEG type. TABLE 2______________________________________Tests and Properties of the Vulcanizates of the Recipesof Table 1Tests Recipe DesignationRheometer 310F A B C D______________________________________T90 32.5 40.2 41.3 31.0Amount 41.9 46.8 34.3 41.9Rate 1.19 1.00 .81 1.71Original Vulcanizate PropertiesTensile 2450 2598 1798 2052Elongation 138 132 168 113Shore A Hardness 77 80 80 84Tear 167 183 170 154Compression Set at 7 Hours @ 250.degree. F.% Set 35 48 43 33Compression Set at 72 Hours @ 300.degree. F.% Set 56 73 63 56Oven-Aged for 7 Days @ 250.degree. F.Tensile 2253 2521 1999 1950% Retained Tensile 92 97 111 95Elongation 116 113 137 102% Retained 84 86 82 90ElongationShore A 85 87 84 83Point Change 8 7 4 1Oven Aged for 7 Days @ 300.degree. F.Tensile 1295 1529 1487 1433% Retained Tensile 53 59 83 70Elongation 29 30 23 43% Retained 21 23 14 38ElongationShore A Hardness 94 94 96 93Point Change 17 14 16 9Oil Ageing ASTM No. 3 Test for 70 Hours @ 250.degree. F.Tensile 1670 1842 1136 1475% Retained Tensile 68 71 63 72Elongation 94 103 108 85% Retained 68 78 64 75ElongationShore A 64 63 60 65Point Change -13 -17 -20 -19Volume Change +47 +45 +54 +45Oil Ageing ASTM No. 3 Test for 70 Hours @ 300 FTensile 1455 1637 1061 1351% Retained Tensile 59 63 59 66Elongation 83 100 104 81% Retained 60 76 62 72ElongationShore A 61 62 54 65Point Change -16 -18 -26 -19Volume Change +49 +44 +57 +47Exxon FN 1973 Test Immersion for 70 Hours @ 300 FTensile 1675 1650 1319 1621% Retained Tensile 68 64 73 79Elongation 86 75 94 81% Retained 62 57 56 72ElongationShore A 71 72 68 72Percent Change -6 -8 -12 -12Volume Change +21 +18 +23 +20______________________________________Recipes of Table 3Recipe CompoundsIngredients E F G H______________________________________Polychloroprene 100 100 100 100Polybutadiene 5.0 5.0 5.0 5.0RubberCarbon Black 44.0 44.0 44.0 44.0Dibutylphthalate 15.0 15.0 15.0 15.0Octamine 2.0 2.0 2.0 2.0Stearic Acid .5 .5 .5 .5MBTS 1.0 1.0 1.0 1.0Red Lead 15.0Calcium Aluminum 15.0 7.5 7.5HexahydrateCa(OH).sub.2 7.5Magnesium 7.5TerephthalateTotal 182.10 182.10 182.10 182.10Sp. Gr. 1.397 1.355 1.352 1.331______________________________________ TABLE 4______________________________________Tests and Properties of the Vulcanizates of the Recipesof Table 1Rheometer 300.degree. F. E F G H______________________________________T90 34.7 29.6 26.5 16.2Amount 31.9 34.8 42.1 32.9Rate .73 1.17 1.66 2.56Original PropertiesTensile 2206 2415 2318 1882Elongation 602 423 404 639Modulus 300% 985 1597 1647 776Shore A 52 64 65 53Heat Ageing for 70 Hours @ 212.degree. F.Tensile 2922 2437 2092 2136% Retained 132 101 90 113TensileElongation 433 337 286 339% Retained 72 80 71 53ElongationShore A 65 67 73 70Point Change 13 3 8 17ASTM No. 3 Oil Ageing for 70 Hours @ 212.degree. F.Tensile 1324 1047 1114 559% Retained 60 43 48 30TensileElongation 303 282 275 297% Retained 50 67 65 46ElongationShore A 73 97 98 85HardnessPoint Change 21 33 33 32Volume Change +89.9 +97.0 +101.0 +151.3Compression Set 72 Hours @ 212.degree. F.% Set 88 82 84 94______________________________________

While certain representative embodiments and details have been shown for the purpose of illustrating the invention, it will be apparent to those skilled in this art that various changes and modifications may be made therein without departing from the spirit or scope of the invention.

Claims

1. In a method for curing a curable rubber composition composed of a halogen containing rubber and a member selected from the group consisting of a vulcanizing agent and a vulcanization accelerator under heat in the presence of an acid acceptor, the improvement wherein said acid acceptor composition is calcium aluminum hexahydrate of the formula

Ca.sub.3 Al.sub.2 (OH).sub.12.

2. The method of claim 1 wherein the vulcanized halogenated rubber is selected from the class consisting of polychloroprene, chlorosulfonated polyethylene rubber and chlorinated polyethylene rubber.

3. The method of claim 1 wherein the amount of the acid acceptor is present in about 1 to about 30 parts per hundred of rubber.

4. The method of claim 1 wherein the vulcanizate contains in addition to the acid acceptor, calcium aluminum hexahydrate about 1 to 25 parts per hundred of rubber (phr) of a stabilizer selected from the class consisting of MgO, CaO, Ca(OH).sub.2, Mg(OH).sub.2 and calcium or magnesium salt of an organic acid.

5. The method of claim 1 wherein the halogen-contain rubber is cured at about 175.degree. F. to about 350.degree. F.

6. A vulcanized halogenated rubber selected from the group consisting of polychloroprene, chlorosulfonated polyethylene rubber and chlorinated polyethylene containing a curative-stabilizer, calcium aluminum hexahydrate.

7. The vulcanized halogenated rubber of claim 6 wherein the curative-stabilizer is present in about 1 to about 30 parts per hundred of rubber.

8. The vulcanizate of claim 6 wherein the vulcanizate contains in addition to the curative stabilizer, calcium aluminum hexahydrate, about 1 to about 25 parts per hundred of rubber (phr) of at least one stabilizer selected from the group consisting of MgO, CaO, Ca(OH).sub.2, Mg(OH).sub.2 and a calcium or magnesium salt of an organic acid.

9. A method of producing cured synthetic resins containing halogens and/or acidic substances having improved heat resistance, color, and heat aging properties, comprising mixing said synthetic resin containing halogen and/or acidic substance with calcium aluminum hexahydrate of the formula Ca.sub.3 Al.sub.2 (OH).sub.12 to form a mixture and heating said mixture at a temperature to effect cure of said resin.

10. The method of claim 9 wherein the mixture is heated at about 175.degree. F. to about 350.degree. F.

11. An improved heat resistance, color retention and water resistant vulcanized halogened rubber selected from the group consisting of polychloroprene, chlorosulfonated polyethylene rubber and chlorinated polyethylene containing a curative-stabilizer of calcium aluminum hexahydrate having the formula Ca.sub.3 Al.sub.2 (OH).sub.12.

12. The vulcanizate of claim 11 wherein the vulcanizate contains in addition to the curative stabilizer, calcium aluminum hexahydrate, about 1 to about 25 parts per hundred of rubber (phr) of at least one stabilizer selected from the group consisting of MgO, CaO, Ca(OH).sub.2, Mg(OH).sub.2 and a calcium or magnesium salt of an organic acid.