The present invention relates to a method of forming a semiconductor layer and a method of manufacturing an organic thin film transistor.
In recent years, research and development of an organic thin film transistor element utilizing an organic semiconductor material has been actively carried out for a technique to make up for disadvantage of an thin film transistor (hereinafter also referred to as TFT) element utilizing a conventional silicon material (refer to Patent Document 1, Non-patent Document 1 and the like).
The organic TFT element can be manufactured by a low temperature manufacturing process, and enables use of a resin substrate which is difficult to break and light. Further, the organic TFT element is considered to enable to realize a flexible display employing a resin film as a support member (refer to Non-Patent Document 2 and the like).
Further, in recent years, many methods have been proposed in which a TFT, for use as a pixel driving element, for example, is manufactured under atmospheric pressure, employing a coating apparatus represented by an ink jet process for the purpose of high productivity and reduction of manufacturing cost. For example, there is disclosed a technique in which, in the process of forming a TFT for a liquid crystal panel or an organic EL (Electro Luminescence) panel used as display device, a droplet of a semiconductor liquid in which a semiconductor material is dissolved or dispersed in a solvent is jetted and sequentially applied onto a substrate employing a coating apparatus to form a semiconductor layer (refer to Patent Document 2).
It is necessary that the TFT for driving pixels in a display panel be formed on a substrate in the form of a matrix at the same interval as in the pixel alignment. During a process of forming a TFT, a head, in which nozzles for jetting the semiconductor liquid are aligned in a line, is moved on a substrate, so that the semiconductor liquid is sequentially jetted from the nozzles onto the substrate. The solvent of the semiconductor liquid jetted onto the substrate is gradually vaporized, in which, as the concentration of the semiconductor liquid increases, the semiconductor crystal of the semiconductor material grows. Thus, a semiconductor layer for a TFT is formed.
Non-Patent Document 1: Advanced Material, 2002, No. 2, page. 99 (Review)
Non-Patent Document 2: SID '01 Digest page 57
However, in a conventional crystal formation method, crystallization proceeds from the outer circumference of a droplet towards the center of the droplet, and there are plural sites which initiate crystallization. The plural crystallization initiation sites are difficult to control. Crystallization is initiated at the plural crystallization initiation sites, resulting in plural crystal grain boundaries. Accordingly, a semiconductor layer formed is not in the state approximate to a single crystal, but it is in the amorphous state or contains microcrystal aggregates in many portions thereof.
In the amorphous state, molecules are not regularly aligned, and the amorphous state lowers carrier mobility as compared with the crystalline state. Small crystals produce many particle interfaces between the crystals, and increase carrier trapping sites. A transistor made of such crystals has problem in that hysteresis is increased.
The present invention has been made in view of the aforementioned. An object of the invention is to provide a method of forming an organic semiconductor layer in which a large crystal semiconductor layer is formed on a substrate, and to provide a method of manufacturing an organic thin film transistor in which an organic thin film transistor with excellent properties is manufactured.
1. A method of forming an organic semiconductor layer comprising the steps of:
preparing a substrate having a groove formed on the surface;
applying, to the substrate, a droplet of an organic semiconductor liquid in which an organic semiconductor material is dissolved or dispersed in a solvent; and
drying the droplet to form the organic semiconductor layer,
wherein the droplet is applied to a position of the substrate where a part of the circumference of the droplet is introduced into the groove.
2. A method of forming an organic semiconductor layer of claim 1, wherein a configuration of the groove is 5 nm to 50 nm in depth in the thickness direction of the substrate and 450 nm to 1200 nm in width on the substrate surface to which the droplet is applied.
3. A method of manufacturing an organic thin film transistor comprising a gate electrode, a gate insulation layer, a source electrode, a drain electrode and an organic semiconductor layer, wherein the organic semiconductor layer is formed according to the method of claim 1 or 2.
According to the present invention, a large crystal organic semiconductor layer can be formed by applying a droplet of an organic semiconductor liquid to a position where a part of the outer circumference of the droplet is introduced into the groove. Further, the present invention can provide a method of manufacturing an organic thin film transistor having on a substrate a thin film transistor with excellent properties.
Next, the present invention will be explained in detail employing the embodiment of the invention, but the present invention is not limited thereto.
The coating apparatus 90 is an apparatus which applies an organic semiconductor liquid onto a predetermined position of a substrate 1 to form an organic semiconductor layer 10 in the form of a matrix. As shown in
X, Y and Z co-ordinate axes showing a three dimensional co-ordinate system are illustrated on the lower left in
The nozzle 81 as shown in
As is shown in
Next, a shape of the groove 19 and a position onto which a semiconductor liquid is jetted will be explained, employing
a) shows an example in which the section of the groove 19 is rectangular, and
The symbol d shows the depth of the groove 19 in the thickness direction (in the Z axis direction) of the substrate 1, the symbol w the width of the groove 19, and the symbol L the length of the groove 19.
a) is an illustration viewing from the positive direction of the Z axis one of the droplet 50b formed immediately alter the semiconductor liquid is applied onto the substrate 1 as explained in
When, as shown in
The tip of the semiconductor liquid 50c is thin, as compared to the depth d of the groove 19, as shown in
Thus, the groove 19 functions as an initiation site for crystallization in the semiconductor solution and can stably provide a large crystal.
Next, the relation between the groove 19 and a position onto which the semiconductor liquid is jetted will be explained.
The examples of
The groove 19, which does not intersect the region occupied by the droplet 50b of the semiconductor liquid, as shown in
With respect to the depth d and width w of the groove 19, the depth d is in the range of preferably from 5 nm to 50 nm, and the width w is in the range of preferably from 450 nm to 1200 nm, which will be explained later.
In the method of manufacturing an organic TFT of a bottom gate bottom contact type, the following steps S1 through S5 will be explained below.
S1: Step of forming a gate electrode and a gate insulation layer
S2: Step of forming a groove
S3: Step of forming a source electrode and a drain electrode
S4: Step of jetting a semiconductor liquid
S5: Step of drying the semiconductor liquid to form a semiconductor layer
The method of manufacturing a TFT of a bottom gate bottom contact type will be sequentially explained, employing
a) through 6(e) are sectional views of a channel portion of a TFT element.
As is shown in
In the embodiment of the invention, a material for the substrate 1 is not specifically limited. Examples of the substrate material include glass, polyimide, polyethylene terephthalate (PET), polyethylene naphthalate (PEN), and polyether sulfone (PES).
As a method for forming a gate electrode 2, there can be used a method in which a film composed of an electrode material is formed on the substrate 1 by a sputtering method or a vacuum deposition method and subjected to patterning according to photolithography, or a method in which an electrode material film is formed only at an intended portion of the substrate according to a droplet coating method or various printing methods.
When the film film is formed by a sputtering method or a vacuum deposition method, Au, Ag, Pb, Al, Cr, Pt, Cu, ITO, and the like can be used as the electrode material. In the droplet coating method, there can be used a metal nanoparticle ink in which metal nanoparticles such as Ag nanoparticles, Au nanoparticles, and AgPb nanoparticles are dispersed in a solvent; a metal oxide nanoparticle ink in which metal oxide nanoparticles such as ITO nanoparticles are dispersed in a solvent; an organic material dispersion ink in which an organic material such as PEDOT/PSS is dispersed in a solvent; and the like.
Next, a gate insulation layer 7 is formed. As a method of forming a gate insulation layer there are a spin coat method, a CVD method, a sputtering method and the like. As a material for the gate insulation layer 7 there can be used inorganic oxide such as silicon oxide, aluminum oxide, tantalum oxide, titanium oxide and the like; inorganic nitrides such as silicon nitride, aluminum nitride and the like; and organic compounds such as polyimide, polyamide, polyester, polyacrylate, a photo-radically polymerizable photocurable resin, a photo-cationically polymerizable photocurable resin, a copolymer containing a acrylonitrile component, polyvinyl phenol, polyvinyl alcohol, novolak resin, cyanoethylpullulan and the like.
As shown in
As a constitution of the groove 19, a groove may be physically formed on the surface of the gate insulation layer 7. As a method of physically forming a groove, there can be used an EB imaging method, an embossing method, a scraper method and the like. In two layers composed of a lower liquid affinity layer and an upper liquid repellency layer, a part of the lower liquid affinity layer may be exposed in the form of a groove so as to form a groove. Further, the groove may be formed by a liquid affinity pattern in the form of a groove, whose pattern is made after a liquid repellency/liquid affinity pattern is provided by surface processing of the liquid repellency monolayer on the liquid affinity layer such as patterning the monolayer through light irradiation.
A source electrode 9 and a drain electrode 8 are formed on the substrate 1, as is shown in
After the substrate 1 on which the gate insulation layer 7 has been formed is washed, a source electrode 9 and a drain electrode 8 are formed on the substrate 1, employing photolithography, a droplet coating method or various printing methods in the same manner as used for forming the gate electrode 2. As electrode materials for the source electrode 9 and the drain electrode 8, there can be used the same electrode materials as those for the gate electrode 2.
As shown in
The semiconductor material is not limited, as long as it is dissolved or dispersed in a solvent. Therefore, the semiconductor material may be an organic low molecular material as well as an organic high molecular material to which a solubilizing side chain is attached for increasing solubility. Further, the semiconductor material may be a low molecular material, a high molecular material or an oligomer. Furthermore, the semiconductor material may be an organic-inorganic hybrid material or an inorganic material as long as it is simultaneously coated together with a solvent, followed by drying of the solvent to form a semiconductor layer. A semiconductor precursor liquid can be also used as the semiconductor material.
The solvent is not specifically limited and examples thereof include aromatic hydrocarbons, aliphatic hydrocarbons, alcohols, ketones, ethers, esters, halogenated hydrocarbons, and phenols. The solvent suitable for the semiconductor material can be selected from the above.
A semiconductor liquid, which has been introduced between the source electrode 9 and the drain electrode 8, is dried to form a semiconductor layer 10 as shown in
In the embodiment of the invention, explanation has been made above of the method of manufacturing a bottom gate bottom contact type organic TFT.
In the embodiment of the invention, an example of manufacturing a bottom gate bottom contact type organic TFT has been explained in the above. However, the method of forming an organic semiconductor layer in the embodiment of the invention also applies to a bottom gate top contact type organic TFT or a top gate type organic TFT.
Next, examples carried out in order to demonstrate the effect of the invention will be explained, however, the invention is not limited thereto.
One hundred and ninety-six glass substrates of a size of 50 mm×60 mm on the surface of which a chromium film with a thickness of 125 nm was formed were prepared. On each chromium film was formed a 500 nm thick acryl film (PC 403).
A groove 19 was formed on the acryl film of each of the one hundred and ninety-six substrates 1 so that the total 196 grooves were different in a depth d and/or a width w. The shape of the groove 19 was rectangular as shown in
As the semiconductor liquid, there was employed a solution in which a low molecular organic semiconductor material, 6,13-bistriisopropylsilylethynylpentacene was dissolved in an amount of 5% by weight in tetralin with a boiling point of 207.4° C.
The coating apparatus 90 as shown in
The head 80 was moved at a pitch of 352.5 μm in the direction as shown in an arrow B in
A chromium film with a thickness of 125 nm was formed on the surface of a glass substrate of a size of 50 mm×60 mm. On the chromium film was formed a 500 nm thick acryl film (PC 403).
A groove 19 was not formed on the surface of the acryl film of the substrate 1 as prepared above.
The semiconductor liquid was jetted onto the substrate 1 in the same manner as in Example 1 above. The semiconductor liquid jetted was dried at room temperature for 15 minutes to form a semiconductor layer, and then crystallization state of the semiconductor layer 10 formed above was observed employing a polarizing microscope.
In this experiment, each of 8000 semiconductor layers 10 formed on the substrate 1 was observed for crystallization state employing a polarizing microscope. The crystallization state of the semiconductor layer was evaluated according to the following four criteria, A, B, C and D:
A: Crystallinity is excellent over a broad portion of the semiconductor layer.
B: Crystallinity is excellent at a greater portion of the semiconductor layer, but uncrystallized portions are observed.
C: Variation of the crystal size is observed at different portions of the semiconductor layer but large crystals are observed in some portion of the semiconductor layer.
D: No large crystals are observed in the semiconductor layer.
The results are shown in Table 1.
As is apparent from Table 1, the grooves having a depth d of from 5 nm to 50 nm and a width w of from 450 nm to 1200 nm formed in Example 1 are evaluated as criterion A, and it has proved that such grooves provide high crystallinity and produce a large crystal.
The grooves formed in Example 1 other than those described above are evaluated as criterion B or C, which cause variation in the crystal size but produce a large crystal. The above results show that the groove is preferably one having a depth d of from 5 nm to 50 nm and a width w of from 450 nm to 1200 nm in order to obtain stably a large crystal with high crystallinity.
The substrate 1 on which a groove is not formed in Comparative example 1 is evaluated as criterion D, and does not produce a large crystal.
In Example 2 and Comparative example 2 which will be explained in the following, a 90 mm×120 mm glass substrate on the surface of which a chromium film having a thickness of 125 nm was employed as a substrate 1. In Example 2, 428×570, total 243960 bottom gate bottom contact type TFTs were formed on the substrate 1.
In this example, a bottom gate bottom contact type TFT was prepared according to the steps of S1 to S5 as explained in
The following steps will be sequentially explained employing the same step numbers as shown in
A light sensitive resist was applied onto the substrate 1 on which a conductive layer had been formed, exposed to light through a photomask with a pattern of a gate electrode 2, and developed to form a resist layer in the form of the gate electrode 2. Subsequently, the resist layer was subjected to etching treatment and removed to form the gate electrode 2.
Subsequently, a SiO2 film was formed employing a sputtering method or a CVD method to form an insulation layer. After that, a light sensitive acrylate material was coated on the insulation layer employing a spin coat method to have a light sensitive acrylate material film with a thickness of 100 nm and subjected to patterning according to photolithography to form a gate insulation layer 7 which was composed of the two films, the SiO2 film and the light sensitive acrylate material film.
Employing an EB imaging method, the groove 19 having a depth d of 30 nm, a width w of 800 nm and a length L of 100 μm was provided in a channel region to be in parallel with the longitudinal direction of the channel, as shown in
A source electrode 9 with a thickness of 50 μm and a drain electrode 8 with a thickness of 50 μm, each composed of Au, were formed according to photolithography.
The droplet 50a of a semiconductor liquid was jetted from the nozzle 81, as the head 80 was moved at a pitch of 140 μm in the direction as shown in the arrow 13. As the semiconductor liquid, a solution in which 6,13-bis(triethylsilylethynyl)pentacene was dissolved in an amount of 5% by weight in tetrahydronaphthalene was used.
The semiconductor liquid, which had been introduced between the source electrode 9 and the drain electrode 8, was dried to form a semiconductor layer 10, as shown in
This comparative example was carried out to confirm the effects of the groove 19 formed in the step S2 in Example 2. In this Comparative Example 2, a bottom gate bottom contact type TFT was prepared in the same manner as in Example 2, except that the step S2 of forming a groove was not carried out
In this experiment, one thousand TFT elements were selected randomly from 243960 TFT elements formed on the substrate 1, and evaluated.
Electric current was applied to each of the TFT elements, and mobility was measured. The average mobility and the On/Off electric current ratio of the TFT elements prepared in Example 2 gave 0.3 cm2/Vs and a seven-digit value, respectively. While the average mobility and the On/Off electric current ratio of the TFT elements prepared in Comparative Example 2 gave 0.08 cm2/Vs and a six-digit value, respectively. It has proved that the TFT element, which was prepared employing the groove 19 in Example 2, is a TFT element with excellent properties, providing a high mobility and a high On/Off electric current ratio, as compared with the TFT element which was prepared without employing a groove in Comparative Example 2.
In this embodiment, a manufacturing method of a bottom gate bottom contact type organic TFT is disclosed as an example. However, the manufacturing method of the present invention is not specifically limited to the manufacturing method of a bottom gate bottom contact type organic TFT, and also applies to a bottom gate top contact type organic TFT or a top gate type organic TFT.
The present invention can provide a method of forming an organic semiconductor layer in which a large crystal organic semiconductor layer is formed on a substrate and a method of manufacturing an organic thin film transistor in which an organic thin film transistor with excellent properties is manufactured.
Number | Date | Country | Kind |
---|---|---|---|
2008-030214 | Feb 2008 | JP | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/JP2009/051562 | 1/30/2009 | WO | 00 | 8/9/2010 |