Patent Application
20110062287
The invention relates to a method of joining a thermoplastic material to a fibre composite material. In addition, the invention relates to a device comprising thermoplastic material and fibre composite material.
In aircraft construction in particular, thermoplastic materials are often attached to fibre composite materials by means of mechanical attachment, for example by means of screws, or by adhesive bonding. For example, plastics brackets which comprise thermoplastic material are often attached to components, such as for example a sidewall panel or a hat rack box, which comprise fibre composite material, within a pressurised area, for example within a cabin area of an aircraft.
Adhesive bonding of plastics brackets comprising thermoplastic material to components comprising fibre composite material requires very complex pretreatment of the adherend surfaces of the plastics brackets. The surfaces have first to be roughened and then pretreated with a primer. Only after this pretreatment can the plastics brackets be adhesively bonded to the components. Then it is necessary to wait for a certain period, as a rule 5 to 8 hours, until the adhesive has cured and exhibits the necessary initial adhesive strength. Adhesives which are heat-curing are also frequently used. When using such adhesives, the plastics brackets and components to be joined together have to be cured for up to 48 hours in an oven. The adhesive bonding process is thus very complex and time-consuming. Moreover, the adhesives include constituents which are hazardous to health.
Alternatively or in addition, plastics brackets comprising thermoplastic material are often attached to components comprising fibre composite material by means of screws. This has the disadvantage, however, that the size and position of the holes for the screws have to be known as early as during production of the plastics brackets and the components and that, in the event of a change to the attachment position in the components and/or in the plastics brackets, new holes have to be introduced. This is disadvantageous for the entire production process.
It is the object of the present invention to provide a method of joining a thermoplastic material to a fibre composite material which is less complex and time-consuming than known adhesive bonding methods, which, moreover, does not use any additional substances hazardous to health and which makes it simpler to change the position at which a thermoplastic material is joined to a fibre composite material compared with mechanical attachment, such as for example by means of screws.
This object is achieved by a method of joining a thermoplastic material to a fibre composite material in which the thermoplastic material is welded to the fibre composite material, wherein the fibre composite material is a fibre-reinforced matrix material or comprises a fibre-reinforced matrix material and wherein the matrix material is a thermoset or comprises a thermoset.
By welding the thermoplastic material to the fibre composite material, the time needed for joining the materials is very greatly reduced. It amounts in particular to just a few seconds. In addition, generally the materials do not have to be pretreated, and no additional substances hazardous to health are required. Moreover, no holes have to be formed in the components and plastics brackets, so making it easier to change the position at which the thermoplastic material is joined to the fibre composite material.
It is preferable for the thermoplastic material to be welded to the fibre composite material by “motion welding”. The term “motion welding” covers any relative motion between the thermoplastic material and the fibre composite material which generates heat of motion in the joint area which is sufficient to weld together the thermoplastic material and the fibre composite material. It is further preferred for the thermoplastic material and the fibre composite material to be moved relative to one another during motion welding in particular in such a way that the thermoplastic material is moved relative to the fibre composite material in such a way that the thermoplastic material starts to melt and the fibre composite material is heated. It is further preferred for the thermoplastic material and the fibre composite material to be moved relative to one another during motion welding in particular in such a way that the thermoplastic material is moved relative to the fibre composite material and the thermoplastics material and the fibre composite material are pressed against one another in such a way that the thermoplastic material starts to melt and the fibre composite material is heated.
In a simple manner, the motion welding allows a heat of motion, in particular a heat of friction, to be generated in the joint area between the thermoplastic material and the fibre composite material which is sufficient to weld the two materials together.
In the same way, the energy of the motion welding may also be used for targeted removal of the thermoplastic material.
The relative motion may be generated for example by rotary motion and/or vibratory motion of the thermoplastic material and of the fibre composite material relative to one another. When using a vibratory motion, the fibre composite material and the thermoplastic material are preferably joined together by vibration welding. In vibration welding, heat of friction is generated by the vibratory motion in the joint area between the thermoplastic material and the fibre composite material which is sufficient to weld together the two materials.
It is additionally preferable for the thermoplastic material to be welded to the fibre composite material by induction welding. For this purpose, an electrically conductive material is arranged in a joint area between the thermoplastic material and the fibre composite material and induction heat is generated in the electrically conductive material which is sufficient to cause the thermoplastic material to start to melt and to heat the fibre composite material. In induction welding, currents are preferably induced in the electrically conductive material which generate the induction heat by means of resistance effects and/or magnetic hysteresis. Preferably, to generate the induction heat, metallic particles and/or a metallic layer is/are introduced into the joint area between the thermoplastic material and the fibre composite material.
It is further preferred that the electrically conductive material is a slotted and stretched metal foil, for example, e.g. the metal foil with the tradename Astrostrike. The electrically conductive material is preferentially made of and/or comprises aluminium and/or copper. It is further preferred that the electrically conductive material is a metallic woven material and/or a metallic layer. It is further preferred that the electrically conductive material comprises or consists of metallic nano particles. The electrically conductive material, in particular the metallic layer, is preferentially generated by a thermal spraying method of one or several metal powders, which can comprise one or several metals, or by using a sintering technique with one or several metals or by melting of one or several metal foils and/or of one or several solder materials, in particular, on the thermoplastic material.
It is further preferred that induction heat is generated by using a medium frequency or a high frequency. In a preferred embodiment, a frequency within a frequency range of 10 to 50 kHz is used, in particular with a power within a range of 2 to 5 kW. In a further preferred embodiment, a frequency within a frequency range of 400 kHz to 1 MHz is used, in particular with a power smaller than 25 kW.
In a further preferred embodiment, the fibre composite material comprises CFRP material and an induction heat is generated in the CFRP material, in particular, without using an additional electrically conductive material. The induction heat is preferentially generated close to the surface of the CFRP material.
The fibre composite material is a fibre-reinforced matrix material or comprises a fibre-reinforced matrix material. The matrix material is a thermoset or comprises a thermoset. It is preferable for fibres of the fibre composite material to be unidirectionally oriented or to form a woven fabric. The fibre composite material is therefore preferably a fibre-reinforced plastic (FRP), i.e. in particular an in particular reinforced, thermoplastic and/or thermosetting matrix material provided with unidirectional fibres or fibres forming a woven fabric. It is additionally possible for the fibre composite material to be produced using a resin, in particular a polyaddition and/or a polycondensation resin. The fibre composite material is preferably arranged on a honeycomb structure, in particular a Nomex honeycomb. In this case, the honeycomb structure takes the form in particular of a layer, and the fibre composite material is applied in layers to two mutually facing sides of the honeycomb structure.
Provision may be made for the thermoplastic material to consist of one or more engineering thermoplastics or to comprise one or more engineering thermoplastics. Provision may further be made for the thermoplastic material to consist of polyamide or to comprise polyamide. Furthermore, the thermoplastic material can consist of or comprise polyetherimide (PEI) and/or polyetheretherketone (PEEK). In a preferred embodiment, the thermoplastic material comprises a fibre reinforcement, in particular a short fibre reinforcement, wherein the fibres can be, for example, carbon fibres and/or glass fibres. In a further preferred embodiment, the thermoplastic material does not comprise a fibre reinforcement.
By using this stated fibre composite material and thermoplastic materials, it is possible to produce a particularly good joint between these materials using the method according to the invention.
It is additionally preferable for the thermoplastic material to be a constituent of a bracket, in particular a support bracket, or for the bracket to consist of the thermoplastic material, and for the fibre composite material to be a constituent of a component or for the component to consist of the fibre composite material, such that the thermoplastic material of the bracket is welded together with the fibre composite material of the component in order to join the bracket to the component to form a bracket arrangement. A bracket may in this manner be joined simply and quickly to a component.
If the fibre composite material is joined to the thermoplastic material by motion welding, it is preferable for the bracket of thermoplastic material to be set in motion, while the fibre composite material of the component, to which it is to be joined, does not move.
Provision may be made for the component to be a sidewall panel in an aircraft, preferably in a space in the aircraft which is pressurisable when in operation, in particular in the cabin space of the aircraft, and/or a hat rack box of the aircraft or a part of the sidewall panel and/or a part of the hat rack box. Furthermore, it is preferable for the method to be performed within an aircraft, preferably within a space pressurisable when in operation, in particular within a cabin space, of an aircraft. The method according to the invention thus makes it possible simply, quickly and reliably to produce a welded joint between a thermoplastic material and a fibre composite material, in particular in an aircraft.
The bracket is preferably so constructed that it may support desired objects.
The invention additionally relates to a device comprising thermoplastic material and fibre composite material, the thermoplastic material and the fibre composite material comprising a joint which may be produced by the method according to the invention.
Preferred configurations of the device are listed in claims 20 to 24.
Preferred embodiments of the invention are explained in greater detail below with reference to drawings, in which
By means of the device 1, a bracket 5, for example in the height position illustrated in
The motion is then stopped, and the surfaces cool down. The heating phase and the cooling phase each last only a few seconds, in particular each phase lasts less than 5 seconds.
The joint between the fibre composite material and the thermoplastic material differs from a welded joint between other materials. In particular, the microscopic structure of the joint between a thermoplastic material and a fibre composite material, which may be produced by means of the method according to the invention, differs from the microscopic structure of a welded joint between other materials, for example between two metallic materials.
In
The turning and lifting unit 2 and the control unit 3 may take the form, for example, of the stationary device described in U.S. Pat. No. 5,160,393. Alternatively, the turning and lifting unit 2, the control unit 3 and the bracket holder 4 may also be of hand-held construction.
The bracket 5 comprises thermoplastic material at least in the area of the joint with the fibre composite material, which material is joined to the fibre composite material in a manner according to the invention. A resultant sequence of layers in the joint area is shown schematically in
The thermoplastic material 10 is preferably an engineering thermoplastic and more preferably polyamide. According to the invention, however, the thermoplastic material may also be a standard thermoplastic or a high performance thermoplastic. The engineering thermoplastic used may preferably be PA66 (with or without glass fibres), in particular PA66-GF30 and PA60-GF30, PA12, PC (polycarbonates) or PMMA. The materials PA66, PA12 and PC are preferably provided with flame retardant and therefore preferably comprise particularly good fire characteristics.
The high performance thermoplastic used may preferably be PEI (polyetherimides), with or without glass fibres, and glass fibre-reinforced modifications thereof. Further high performance thermoplastic materials may be, for example: aromatic polyetherketones (PAEK), PPSU (polyphenylsulfone) and PAI (polyamideimides).
The fibre composite material 11, which is preferably an FRP material, may for example comprise carbon fibres and/or glass fibres, in particular a CFRP material and/or a GRP material. The fibre composite material is preferably produced using a resin, in particular using a polyaddition and/or polycondensation resin. The sequence of layers comprising fibre composite material layers 11, 13 and an interposed honeycomb structure 12 is also known as a sandwich. A foam may be used instead of or in addition to the honeycomb structure 12.
The layers 11, 13 of the fibre composite material preferably have a thickness in the range from 0.1 to 0.2 mm and more preferably a thickness of 0.15 mm.
The microscopic sequence of the joining process may possibly be described as follows.
During welding, the surface of the thermoplastic material passes into a high-viscosity phase, which lies above the glass transition range and below the melting point. This means that the thermoplastic material merely starts to melt. At the same time, the surface of the fibre composite material is heated and enters into a quasi-chemical union with the high-viscosity phase of the thermoplastic material. If the fibre composite material comprises resins, in zo particular polyaddition and/or polycondensation resins, resins which may as yet be uncured enter into a quasi-chemical union with the high-viscosity phase of the thermoplastic material, i.e. the resins may not be cured completely, for example, more than 50 percent of the resins may be cured, in particular more than 80 percent may be cured, wherein uncured resins may enter into a quasi-chemical union with the high-viscosity phase of the thermoplastic material.
Moreover, the joint could come about in that the high-viscosity thermoplastic material of the bracket is drawn through micropores in the fibre composite material, such that the thermoplastic material penetrates the fibre composite material, so producing the joint. The high-viscosity thermoplastic material could, moreover, be drawn into the fibre composite material and through the fibre composite material in such a way that it effects anchoring on the side of the fibre composite material remote from the thermoplastic material and so produces the joint. The high-viscosity phase of the thermoplastic material could in particular be drawn through the fibre composite material when the fibre composite material is applied to a honeycomb structure, as shown for example in
In another embodiment, the thermoplastic material is welded to the fibre composite material by induction welding, wherein an electrically conductive material is arranged in a joint area between the thermoplastic material and the fibre composite material. It is preferred that the electrically conductive material is a slotted and stretched metal foil, for example, a metal foil with the tradename Astrostrike. The electrically conductive material is preferentially made of and/or comprises aluminium and/or copper. In another preferred embodiment, the electrically conductive material is a metallic woven material and/or a metallic layer. In a further preferred embodiment, the electrically conductive material comprises or consists of metallic nano particles. The electrically conductive material, in particular the metallic layer, is preferentially generated by a thermal spraying method of one or several metal powders, which can comprise one or several metals, or by using a sintering technique with one or several metals or by melting of one or several metal foils and/or of one or several solder materials, in particular, on the thermoplastic material.
In a preferred embodiment, induction heat is generated by using a medium frequency or a high frequency. It is preferred that a frequency within a frequency range of 10 to 50 kHz is used, in particular with a power within a range of 2 to 5 kW. In a further preferred embodiment, a frequency within a frequency range of 400 kHz to 1 MHz is used, in particular with a power smaller than 25 kW.
In a further preferred embodiment, the fibre composite material comprises CFRP material and an induction heat is generated in the CFRP material, in particular, without using an additional electrically conductive material. The induction heat is preferentially generated close to the surface of the CFRP material.
Examples of the method according to the invention for joining a thermoplastic material to a fibre composite material are described below.
According to Example 1, a bracket, which comprises thermoplastic material and is illustrated schematically and by way of example in
In this exemplary embodiment, the bracket 33 comprises a disc-shaped attachment portion 34, which is joined to the FRP material, and a holding element 35. The attachment portion 34 and the holding element 35 have a polyamide PA66 content of 70% and a glass fibre content of 30%. The holding element 35 serves to hold an object, such as for example an electrical lead or heavier objects. The thickness of the attachment portion amounts in this example to 2.2 mm, and the diameter of the attachment portion amounts in this example to 24 mm.
In this example, the FRP material is a GRP laminate, the top outer ply of the laminate, with which the surface 36 of the bracket 33 is to be connected, being 40% resin and 60% glass fibre fabric. The thickness of the laminate amounts to 2 mm.
The bracket is secured in the bracket holder 4 of the device 1 illustrated schematically in
The pressure which acts during the welding process between the thermoplastic material and the FRP material amounts in this example to 0.5, 1.0 and 1.5 bar. For each of these pressures a joint was produced in this example according to the invention between the bracket, which comprises the thermoplastic material, and the FRP material. During the welding process, the bracket, which comprises thermoplastic material, is rotated relative to the FRP material in this exemplary embodiment at an angular frequency of 120 Hz. The welding depth amounts in this exemplary embodiment to 0.35 mm. In this exemplary embodiment the welding process was controlled by means of the welding depth, i.e. the welding process was terminated as soon as the predetermined welding depth had been reached.
To check the joints between the thermoplastic material and the FRP material, tensile shear strength was determined. Each of the joints produced according to the invention has excellent tensile shear strengths. These tensile shear strengths are sufficient, for example, to attach brackets for holding heavy objects to FRP components.
In this example too, the bracket described in Example 1 is used. In this example, the FRP material is CFRP laminate, the top outer ply of the laminate, to which the bracket is joined, being 45% resin and 55% carbon fibre fabric. The thickness of the laminate amounts to 2 mm.
The method according to the invention for connecting a thermoplastic material (bracket) to an FRP material (surface of the CFRP laminate) was performed zo using the device 1 illustrated schematically in
In this example the angular frequency amounts to 160 Hz and the welding time to 3 s. The welding time is the time for which the bracket is moved relative to the FRP material and a predetermined pressure, which amounts in this example to 1.0 bar, is present between the thermoplastic material and the FRP material. The welding process is regulated in this example by means of the welding time, i.e. the welding process was performed in each case for 3 s. In these examples too, the tensile shear strength was determined.
Joints between a thermoplastic material and an FRP material produced with the test parameters according to Example 2 exhibit excellent tensile shear strengths, which are sufficient for example to attach a bracket of thermoplastic material for holding heavy objects to an FRP component.
Although motion welding has been described in the examples, the invention is not limited to motion welding. According to the invention, any type of welding may be used which leads to the development of heat which is sufficient to produce the joint according to the invention. For example, the heat may also be introduced by means of radiation, in particular by infrared welding or laser welding. Alternatively or in addition, the heat may also be introduced by convection, in particular by hot gas welding or extrusion welding or by non-contact welding using hot air.
In addition, the thermoplastic material may be welded together with the fibre composite material by induction welding. For this purpose, an electrically conductive material is arranged in a joint area between the thermoplastic material and the fibre composite material and induction heat is generated in the electrically conductive material which is sufficient to cause the thermoplastic material to start to melt and to heat the fibre composite material. In induction welding, currents are preferably induced in the electrically conductive material which generate the induction heat by means of resistance effects and/or magnetic hysteresis. Preferably, to generate the induction heat, metallic particles and/or a metallic layer is/are introduced into the joint area between the thermoplastic material and the fibre composite material.
Although the invention has been described by way of example with reference to a bracket, which is joined to an FRP material, the invention is not restricted to joining a bracket to an FRP material. According to the invention, other objects which comprise thermoplastic material and/or consist thereof may be joined to fibre composite material, in particular to FRP material. The invention is also not restricted to specific bracket shapes.
Furthermore, the invention is not restricted to circular motion between the thermoplastic material and the fibre composite material. According to the invention, any relative motion between these two materials, during which the fibre composite material and the thermoplastic material are in contact with one another, may be used in order to generate the heat of motion needed for the welding process. This relative motion may be composed of rotary motion and linear motion. In addition, the relative motion may also be just linear motion.
The invention is not restricted to the pressures, welding times, welding depths or frequencies stated in the exemplary embodiment. As already explained above, according to the invention any desired relative motion between the thermoplastic material and the fibre composite material may be performed and any desired pressures may be used between the fibre composite material and the thermoplastic material, as long as a heat of motion is generated which is sufficient to weld these two materials together.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2007 003 357.7 | Jan 2007 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP08/50528 | 1/17/2008 | WO | 00 | 11/18/2009 |