The present invention relates to a method for joining materials.
Recently, in an automobile industry, technique for joining different kinds of materials such as aluminum and iron members which are hardly weldable together has become more and more important since lightweight material such as an aluminum member has been positively utilized from a viewpoint of making a vehicle light in weight for improvement of fuel efficiency. Conventionally, different kinds of materials hardly weldable together have been joined together by means of, for example, bolt-on fastening, joining through mechanical clinch or adhesion through adhesive agent.
Conventional technology pertinent to a method for joining materials of the invention has been disclosed, for example, in the following Patent Literature 1.
[Patent Literature 1] JP2004-136365A
However, for example, use of bolt-on fastening brings abut projecting of a bolt and a nut on front-back both sides of the materials to be joined, which leads to a design restriction of ensuring occupation space required for these projections; moreover, in bolt-on fastening, there are fears on loosening and dropout. Use of joining through mechanical clinch may disadvantageously bring about quality defects such as cracks and deformation since the joining is conducted mainly for and between thin sheets and only through pressing with no addition of heat to the materials.
Use of adhesion through adhesive agent is disadvantageous not only in aggravated workability and working environment but also aggravated recyclability due to difficulty in separation of the adhesive agent from the materials upon recycling.
The invention was made in view of the above and has its object to provide a method for joining materials which is free from projections accompanying a design restriction as well as loosening and dropout, which enables joining of materials widely ranging from thinner sheets to thicker plates while preventing quality defects such as cracks and deformation from occurring and which can conduct joining with excellent recyclability while maintaining excellent workability and working environment.
The invention is directed to a method for joining materials characterized in that it comprises overlapping the plural materials each with a joint hole to align the joint holes, fitting joint auxiliary material into said aligned joint holes, rotating and pressing a joint tool from one side in an overlapped direction of said respective materials onto the auxiliary material to soften said auxiliary material in solid phase through frictional heat generated so as to immerse the joint tool into the auxiliary material, whereby the auxiliary material is tightly fitted into the joint holes to provide a mechanical engaging part for the respective materials, extracting said joint tool, allowing said engaging part to harden, whereby the respective materials are joined together through the auxiliary material.
Thus, the mechanical engaging part provided by the auxiliary material tightly fitted into the joint holes with respect to the respective materials brings about anti-dropout and ant-rotation effects, whereby the respective materials are firmly joined together through the auxiliary material.
In this connection, no large projections such as bolt and nut are protruded unlike the bolt-on fastening, so that it is free from design restriction of ensuring occupation space required for such projections. The auxiliary material is tightly fitted into the joint holes, so that there is no fear of loosening and dropout unlike bolt-on fastening.
The respective materials are joined together through the auxiliary material fitted into the joint holes of the respective materials, which enables joining of the respective materials widely ranging from thinner sheets to thicker plates without unreasonable pressing force and with frictional heat applied to the auxiliary material by the joint tool to soften the auxiliary material, so that quality defects such as cracks and deformation can be prevented from occurring.
The respective materials are mechanically joined together through the engaging part without intermediate such as adhesive agent, so that the joining is free from aggravated workability and working environment unlike use of adhesive agent and has excellent recyclability since separation is readily performed upon recycling of the materials.
When the invention is worked concretely, a ridge on a joint auxiliary material fitted with a groove formed on an inner side surface of the joint hole may serve as engaging part; flanges formed on axially opposite ends of the auxiliary material to pinchingly hold the respective materials in an overlapped direction may serve as engaging part, at least one of said flanges being formed upon immersion of the joint tool to be completed as engaging part.
Further, in the invention, at least one of the respective materials is of the same kind as the auxiliary material, a boundary between the material and the auxiliary material which are of the same kind being stirred by rotation of the joint tool to provide a friction stir weld or joint.
The respective materials may be formed with spot-like joint holes, the joint tool being aligned with the joint holes so as to conduct spot joining; alternatively, the respective materials may be formed with slot-like joint holes, the joint tool being moved longitudinally of the joint holes so as to conduct continuous joining.
A method for joining materials of the invention as mentioned above can exhibit various excellent effects and advantages. Because of no large projections such as a bolt and a nut being protruded unlike bolt-on fastening, a design restriction can be substantially relieved and there is no fear of loosening and dropout unlike bolt-on fastening. Moreover, joining is enabled for materials widely ranging from thinner sheets to thicker plates while preventing quality defects such as cracks and deformation from occurring. Joining with excellent recyclability can be conducted while maintaining excellent workability and working environment.
Embodiments of the invention will be described in conjunction with the drawings.
An inner periphery of the joint hole 1a of the upper material 1 is threaded to provide a spiral groove 5. The backing member 4 has an upper surface formed with a concave 6 which confronts the joint holes 1a and 2a of the materials 1 and 2a and which has plane section greater than the joint holes 1a and 2a.
Arranged above the respective materials 1 and 2 and coaxially of the joint holes 1a and 2a is a cylindrical joint tool 8 with a pin 7 on its lower end adapted to be inserted into the joint holes 1a and 2a, the joint tool being supported rotatably and vertically movably by a joining device (not shown).
The overlapped materials 1 and 2 are joined together by the joint tool 8 which is lowered, while being rotated, to be pressed onto the auxiliary material 3 in the joint holes 1a and 2a as shown in
Then, the joint tool 8 is lowered into the state shown in
Moreover, especially in this embodiment, the lower material 2 is of the same kind as the auxiliary material 3, so that when the pin 7 of the joint tool 8 is rotated and immersed into the auxiliary material 3, a boundary between the material 2 and the auxiliary material 3 which are of the same kind is stirred by rotation of the joint tool 8 to provide a friction stir weld or joint 10.
Then, as shown in
Moreover, afforded Between the iron material 1 and the aluminum auxiliary material 3 is an effect of diffusion bonding or joint due to diffusion of atoms generated between them since the joint auxiliary material 3 softened in solid phase due to the frictional heat generated is fitted with and pressed on the material 1 in a temperature condition of lower than a melting point.
In fact, verification experiments on tensile shear strength conducted by the inventor revealed that good tensile shear strength as many as 8.75 kN is obtained in a case where the upper material 1 is made of SS400 iron with thickness of 5 mm, the lower material 2 being made of 6000-series aluminum with thickness of 7 mm, the joint auxiliary material 3 being made of 6000-series aluminum which is the same kind with the material 2.
In the embodiment, the respective materials 1 and 2 are firmly joined together with no large projections such as a bolt and a nut unlike bolt-on fastening, so that there is no design restriction of ensuring occupation space required for such projections. Moreover, the auxiliary material 3 is tightly fitted into the joint holes 1a and 2a, so that there are no fears on loosening and dropout unlike bolt-on fastening.
In the embodiment illustrated, the flanges 6′ and 6″ are slightly protruded out of the upper and lower surfaces of the respective materials 1 and 2. Upon formation of the flanges 6′ and 6″, the upper and lower surfaces of the materials 1 and 2, respectively, may be countersunk to provide concaves contiguous with the joint holes 1a and 2a and having plane sections greater than the joint holes 1a and 2a such that the flanges 6′ and 6″ are fitted into the upper and lower countersunk concaves, respectively. This makes flat the final contour of the upper and lower surfaces of the materials 1 and 2, respectively.
Moreover, in the embodiment, the respective materials 1 and 2 are joined together through the auxiliary material 3 fitted into the joint holes 1a and 2a of the respective materials 1 and 2, which enables joining of the respective materials 1 and 2 widely ranging from thinner sheets to thicker plates without unreasonable pressing force and with frictional heat applied to the auxiliary material 3 by the joint tool 8 to soften the auxiliary material, so that quality defects such as cracks and deformation can be prevented from occurring.
The respective materials 1 and 2 are mechanically joined together through the engaging part without intermediate such as adhesive agent, so that the joining is free from aggravated workability and working environment unlike use of adhesive agent and has excellent recyclability since separation is readily performed upon recycling of the materials.
Thus, according to the above-mentioned embodiment, design restrictions can be substantially relieved since there are no large projections such as a bolt and a nut unlike bolt-on fastening and fears on loosening and dropout are released unlike bolt-on fastening. Moreover, joining is enabled over wide variety of materials widely ranging from thin sheets to thicker plates while preventing quality defects such as cracks and deformation from occurring. Further, joining can be made with excellent recyclability while maintaining workability and working environment good.
Exemplified in the embodiment illustrated in the above is the spiral groove 5 threaded on the inner periphery of the joint hole 1a; however, the groove 5 is not always limited to that formed spirally. For example, a combination of ring- and spline-shaped grooves 5 (or a combination of spiral and spline-shaped grooves 5) may attain the anti-dropout and anti-rotation effects without using the flanges 6′ and 6″. The respective materials 1 and 2 and the auxiliary material 3 may be of different kinds so as not to form a friction stir weld or joint 10 between them.
In the above embodiment, the flanges 6′ and 6″ formed on axially opposite ends of the auxiliary material 3 to pinchingly hold the respective materials 1 and 2 in an overlapped direction serves as engaging parts, these flanges 6′ and 6″ being concurrently formed upon immersion of the joint tool 8; alternatively, as shown in
When the auxiliary material 3 with the flange 6″ at its upper end in advance is employed, the auxiliary material 3 may be manually set in the joint holes 1a and 2a before the joining device is installed, so that a device such as a feeder for locating the auxiliary material 3 in the joint holes 1a and 2a becomes unnecessary.
The above-mentioned embodiment is exemplified with the spot-like joint holes 1a and 2a formed on the materials 1 and 2, the joint tool 8 being aligned with the joining holes 1a and 2a so as to conduct spot joining; alternatively, the joining holes 1a and 2a may be formed in a slot form so as to conduct continuous joining by the joining tool 8 moved longitudinally of the joining holes 1a and 2a.
It is to be understood that a method for joining materials according to the invention is not limited to the above-mentioned embodiment and that various changes and modifications may be made without departing from the scope of the invention. For example, the respective materials are not always different materials; the claimed joining method may be similarly applicable to the respective materials being of the same kind. As the respective materials and the auxiliary material, not only metal materials may be applicable but also high-molecular-weight materials and the like may be properly applicable. The auxiliary material may be preliminarily formed with a guide bore for guiding immersion of a joint tool. The sectional configuration of the joint holes are not limited to rectangular as shown; the joint holes with various different sections may be appropriately employed so as to attain greater joint area for the purpose of improving strength.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2006-072697 | Mar 2006 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2007/000229 | 3/15/2007 | WO | 00 | 9/10/2008 |