Method of making a porous tire tread mold

Abstract

A method of making a tire mold segment with a porous metal tread surface for a tire mold wherein an annular segmental tire model of refractory material is formed with tire model segments which are used to shape and form each tire mold segment from powdered metal by applying heat and pressure to sinter the powdered metal as it is shaped by the tire model segment. Blades may be mounted in the tire model segments for transfer to the tire mold segments for molding slits a tire tread.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of Invention

[0002] This invention relates to tire molds and especially to the method of making mold segments of sintered powdered metal from tire model segments of a refractory material utilizing pressure vessels and heaters.

[0003] 2. Description of the Related Art

[0004] In the manufacture of tires the composite rubber reinforced article is vulcanized under heat and pressure. During this operation, it is important that the gases and moisture be vented and not trapped in the tire where this may cause the tire to fail. It has been found that metal parts made from powdered metal have pores which have the capability of absorbing gases during a molding process. This property has been utilized in molding and casting by forming and compressing parts under pressure in various applications shown and described in U.S. Pat. No. 5,850,590. Also in U.S. Pat. No. 5,623,727 parts have been made by using a model or forging die on a moveable ram for shaping and forming a part from powdered metal. In U.S. Pat. No. 5,625,861 a process is disclosed for producing a porous metal body by shaping powdered metal in a capsule under pressure.

[0005] The object of this invention is to provide a segmental tire mold with porous molding surfaces to absorb gases and moisture during curing of a tire without the necessity of providing vents which may be filled with rubber and result in projecting fingers on the tire which need to be trimmed. The absorption of gases and moisture in the pores of the mold can also be provided in locations where it is difficult to provide vents.

SUMMARY OF THE INVENTION

[0006] In accordance with one aspect of the invention, there is provided a method of making a porous metal tread segment for a tire mold from metal powder comprising:

[0007] (a) forming a segmented tire mold model of refractory material;

[0008] (b) mounting the model in a milling machine;

[0009] (c) cutting a tread surface in the model;

[0010] (d) compacting the metal powder against a segment of the model to form the tread segment;

[0011] (e) heating the tread segment to sinter the metal powder; and

[0012] (f) machining the tread segment for mounting in a segmental tire mold mechanism.

[0013] Still other benefits and advantages of the invention will become apparent to those skilled in the art to which it pertains upon a reading and understanding of the following detailed specification.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] The invention may take physical form in certain parts and arrangement of parts, preferred embodiments of which will be described in detail in this specification and illustrated in the accompanying drawings which form a part hereof and herein:

[0015] FIG. 1 is a schematic view in perspective showing a tire mold model with one segment broken away.

[0016] FIG. 2 is a schematic view showing the forming of the tire mold segment by the tire model segment utilizing cold isostatic pressing of the powdered metal.

[0017] FIG. 3 is a schematic view showing the forming of the tire mold segment by the tire model segment utilizing hot isostatic pressing of the powdered metal.

[0018] FIG. 4 is a schematic view showing the forming of the tire mold segment by the tire model segment utilizing a hydraulic uniaxial press.

[0019] FIG. 5 is a cross-section of a self-venting tire mold having machined porous tire mold segments made in accordance with the method of the invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0020] Referring now to the drawings wherein the showings are for the purpose of illustrating preferred embodiments of the invention only and not for purpose of limiting the same FIG. 1 shows a segmental tire mold model 10 which is machined from a refractory material such as graphite with a tread pattern 12 cut into the outer surface. Slots 14 may also be milled in the surface for insertion of blades 16. The tire mold model 10 is divided into tire model segments 18 each of which may then be used as a model or forging die to provide the mold cavity in a tire mold segment 20.

[0021] As shown in FIG. 2 the mold segment 20 is made by a cold isostatic compaction and sintering process. A tire model segment 18 is placed in a flexible mold such as a rubber bag 22, a metal or alloy powder 24 is placed in the bag around the tire model segment and a plug 26 provided to close an opening 27 in the rubber bag. The model segment 18 and metal powder 24 in the bag 22 are then placed in a high-pressure chamber 28, which is filled with a fluid such as oil 30. High pressure is applied to the powdered metal forming a tire mold segment 20 by communicating the oil 30 under pressure through a conduit 32, to the chamber 28 for a predetermined period of time. This compacts the powder 24 against the model segment 18 to form the tread segment 20. The fragile green tire mold segment 20 is then removed from the high pressure chamber 28 and from the rubber bag 22 and placed in a continuous batch furnace where it is sintered at high temperatures which creates interparticle welds and forms a high strength metallurgical part. The sintered tire mold segment 20 may contain the blades 16 which remain fastened to the tire mold segment surface after the graphite model segment 18 has been removed. The tire mold segment 20 may then be machined to a shape such as that shown in FIG. 5.

[0022] Referring to FIG. 3 equipment for making a tire mold segment 42 by a hot isostatic process is illustrated in which the tire model segment 18 is placed in a pressure vessel such as an uniaxial press 34 with heaters 36 for heating the model segment and powdered metal 38 in a flexible container 40 while under pressure from a source outside the pressure vessel through a conduit 41 to compact the powdered metal 38 against the model segment 18 to shape a tire mold segment 42. The powdered metal 38 is then be sintered to provide the optimum physical properties for the tire mold segment 42. Here again the blades 16 remain in the tire mold segment 42 after it is sintered. The resulting tire mold segment 42 may then be removed from the pressure vessel 34 and the container 40 so that the tire model segment 18 can be removed and the tire mold segment 42 machined in the same manner as described for the segment 20 shown in FIG. 5.

[0023] Referring to FIG. 4 a pseudo-isostatic compaction process is illustrated in which the tire model segment 18 is placed in a press 44 with a hydraulic ram 46, having a top punch 48 extending into a die cavity 50 for compressing powdered metal 52 against the tire model segment 18. This may be done in a container 54 having heaters 36 to heat the compressed powdered metal 52 forming a tire mold segment 56. Doing the sintering process the blades 16 in the tire model segment 18 may be transferred to the tire mold segment 56 and become a part of the tire mold segment after the pressure and sintering process is completed.

[0024] Prior to compaction and sintering an appropriate release coating is applied to the tire model segments 18 and since they are designed with no undercuts and a minimum amount of draft at all points the tire mold segments 42 and 56 should separate from the tire model segments 18 without fracture of the model segments. A hydraulic press (not shown) may be used to remove the model segments 18 from the mold segments 42 and 56, if needed.

[0025] After forming the sides, back surfaces and the S-diameter surface the tire mold segments 42 and 56 can be finish machined and the mold segments assembled with other segments into a common segmental mold mechanism 57 such as that shown in FIG. 5. The tire mold segments 20 are mounted on radially moveable press segments 58 having tapered actuating surfaces 60 for moving the segments radially upon opening and closing of the tire mold.

[0026] During vulcanization of a tire in the tire mold 62 the gases and moisture generated will be absorbed in pores 64 in the tire mold segments 20. After vulcanization and removal of the tire the gases and moisture may escape from the pores 64.

[0027] If desired a backing plate (not shown) may be positioned in back of each of the tire mold segments 42, 56 and the powdered metal 38 compacted against and welded to the backing plate during the sintering operation. This reduces the quantity of powdered material which must be sintered.

[0028] While certain representative embodiments and details have been shown for the purpose of illustrating the invention, it will be apparent to those skilled in the art that various changes and modifications may be made therein without departing from the scope of the invention.

[0029] Having thus described the invention, it is now claimed:

Claims

1. A method of making a porous metal tread segment for a tire mold from metal powder comprising: (a) forming a segmented tire mold model of refractory material; (b) mounting said model in a milling machine; (c) cutting a tread surface in said model; (d) compacting said metal powder against a segment of said model to form said tread segment; (e) heating said tread segment to sinter said metal powder; and (f) machining said tread segment for mounting in a segmental tire mold mechanism.

2. The method of claim 1 further characterized by said refractory material being graphite.

3. The method of claim 1 further characterized by said tread mold segment being formed by compacting said metal powder against said segment of said model in a uniaxial press and heating said tread segment to create interparticle welds with high strength.

4. The method of claim 1 further characterized by simultaneous heating and compacting said metal powder to make said tread segment.

5. The method of claim 1 further characterized by said segment of said model and said metal powder being placed in a flexible bag and located in a high pressure chamber in a uniaxial press and applying heat and pressure to said chamber to compact said metal powder against said segment of said model to shape said mold segment and create interparticle welds in a porous material.

6. The method of claim 1 further characterized by slots being cut in said segmented tire mold and blades inserted in said slots after cutting a tread surface in said model whereby after sintering of said metal powder and forming said tire mold segments said blades will be embedded in a tread surface of said tread mold segment for forming slits in tires molded with said tread segments.

7. A method of shaping and vulcanizing a tire comprising: (a) placing said tire in a tire mold having a porous tread shaping surface; (b) closing said mold to move said tread shaping surface into tread shaping engagement with said tire; (c) applying heat and pressure to said tire whereby gases and moisture are absorbed by said porous tread shaping surface as said tire is vulcanized; (d) lowering said temperature and reducing said pressure in said mold; (e) opening said mold and, (f) removing said tire permitting gases and moisture absorbed by said porous surface to escape from said porous tread shaping surface.

8. The method of claim 8 further characterized by said tire mold having a plurality of segments and each of said segments having a part of said porous tread shaping surface.