Claims
- 1. A method of manufacturing a mold with a dry ejector, comprising the steps of:
- providing a nominal length ejector made of metal;
- coating the nominal length ejector with a low friction coating of aluminum or an alloy thereof, and with less than a 0.0002 inch thick coating thereon;
- cutting the nominal length ejector through the metal and the coating to form an ejector of a selective size and forming a cut end with the coating at the corner at the cut end;
- deburring the cut end of the ejector while leaving the low friction metal coating substantially intact at the corner of the cut end without flaking or peeling the coating at the cut end corner; and
- placing the metal coated, cut-to-size in the mold.
- 2. A method in accordance with claim 1 in which the low friction metal coating comprises chromium and alloys thereof.
- 3. A method in accordance with claim 2 in which the coating has a thickness in the range of approximately 0.00004 inch to 0.0001 inch.
- 4. A method in accordance with claim 1 in which the step of deburring the cut end of the ejector comprises laying the ejector substantially flat against a fine abrasive emery paper, with the cut end in contact with the emery paper, and rotating it about its axis.
- 5. A method of producing a customized ejector, comprising the steps of:
- providing a nominal length ejector of steel;
- coating the nominal length ejector with a coating having a lower coefficient of friction that the steel and coating the ejector with a coating having a thickness in the range of 0.00004 to 0.0000001 inch that does not nominally increase the diameter of the ejector with respect to a bore in the mold for receiving the ejector;
- cutting the nominal length ejector through the steel and coating to form an ejector of a selective size to form a cut end with a corner thereon, and deburring the cut end of the ejector while leaving the low friction metal coating substantially intact at the corner without flaking or peeling the coating at the corner of the cut end.
- 6. A method in accordance with claim 5 in which the step of coating the nominal length ejector with a low friction metal coating comprises coating with chromium, nickel and alloys thereof.
Parent Case Info
This is a division of application Ser. No. 08/265,042, filed Jun. 23, 1994.
US Referenced Citations (21)
Divisions (1)
|
Number |
Date |
Country |
Parent |
265042 |
Jun 1994 |
|