Method of making field emitters

Information

  • Patent Grant
  • 6620640
  • Patent Number
    6,620,640
  • Date Filed
    Tuesday, May 28, 2002
    22 years ago
  • Date Issued
    Tuesday, September 16, 2003
    21 years ago
Abstract
A process is provided for forming sharp asperities useful as field emitters. The process comprises patterning and doping a silicon substrate. The doped silicon substrate is anodized. The anodized area is then used for field emission tips. The process of the present invention is also useful for low temperature sharpening of tips fabricated by other methods. The tips are anodized, and then exposed to radiant energy and the resulting oxide is removed.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




This invention relates to field emission devices and, more particularly, to a method of fabricating field emitters useful in displays.




2. State of the Art




Cathode ray tube (CRT) displays, such as those commonly used in desk-top computer screens, function as a result of a scanning electron beam from an electron gun impinging on phosphors on a relatively distant screen. The electrons increase the energy level of the phosphors. When the phosphors return to their normal energy level, they release the energy from the electrons as a photon of light, which is transmitted through the glass screen of the display to the viewer. One disadvantage of a CRT is the depth of the display required to accommodate the raster scanner.




Flat panel displays have become increasingly important in appliances requiring lightweight portable screens. Currently, such screens use electroluminescent or liquid crystal technology. Another promising technology is the use of a matrix-addressable array of cold cathode emission devices to excite phosphor on a screen, often referred to as a field emitter display.




Spindt et al. discusses field emission cathode structures in U.S. Pat. Nos. 3,665,241, 3,755,704, and 3,812,559. To produce the desired field emission, a potential source is provided with its positive terminal connected to the gate or grid and its negative terminal connected to the emitter electrode (cathode conductor substrate). The potential source is variable for the purpose of controlling the electron emission current.




Upon application of a potential between the electrodes, an electric field is established between the emitter tips and the low potential anode grid, thus causing electrons to be emitted from the cathode tips through the holes in the grid electrode.




BRIEF SUMMARY OF THE INVENTION




The clarity or resolution of a field emission display is a function of a number of factors, including emitter tip sharpness. The process of the present invention is directed toward the fabrication of very sharp cathode emitter tips.




One aspect of the process of the present invention involves forming sharp asperities useful as field emitters. The process comprises patterning and doping a silicon substrate. The doped silicon substrate is anodized. Where the silicon substrate was doped, regions of very sharply defined spires of porous silicon are formed. These sharp spires or asperities are useful as emitter tips.




Another aspect is fabrication of emitter tips using porous silicon. The method comprises blanket doping and anodizing a silicon substrate. The unmasked, anodized substrate is then exposed to patterned ultraviolet light. The exposed areas are oxidized in air. The oxidized areas are either stripped with hydrofluoric acid or retained as an isolation mechanism.




A further aspect of the present invention is the sharpening of field emitters. The method comprises anodizing existing silicon emitters, thereby causing the emitters to become porous. The porous silicon tips are exposed to ultraviolet light and rinsed with a hydrogen halide. The ultraviolet light oxidizes the tips and they become sharper as the oxide is stripped.




Other features and advantages of the present invention will become apparent to those of skill in the art through a consideration of the ensuing description, the accompanying drawings, and the appended claims.











BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS




In the drawings, which illustrate what is currently considered to be the best mode for carrying out the invention:





FIG. 1

is a schematic cross-section of a field emission display having emitter tips;





FIG. 2

is a schematic cross-section of an anodization chamber;





FIGS. 3A-3B

are schematic cross-sections of one embodiment of the process of the present invention;





FIGS. 4A-4C

are schematic cross-sections of another embodiment of the process of the present invention; and





FIGS. 5A-5D

are schematic cross-sections of a further embodiment of the process of the present invention.











DETAILED DESCRIPTION OF THE INVENTION




Referring to

FIG. 1

, a representative field emission display employing a display segment


22


is depicted. Each display segment


22


is capable of displaying a pixel of information, or a portion of a pixel, as, for example, one green dot of a red/green/blue full-color triad pixel.




Preferably, a single crystal silicon layer serves as a substrate


11


. Alternatively, amorphous silicon deposited on an underlying substrate comprised largely of glass or other combination may be used as long as a material capable of conducting electrical current is present on the surface of a substrate so that it can be patterned and etched to form micro-cathodes


13


.




At a field emission site, a micro-cathode


13


has been constructed on top of the substrate


11


. The micro-cathode


13


is a protuberance which may have a variety of shapes, such as pyramidal, conical, or other geometry, which has a fine micropoint for the emission of electrons. Surrounding the micro-cathode


13


is a grid or gate structure


15


. When a voltage differential, through source


20


, is applied between the micro-cathode


13


and the gate structure


15


, a stream of electrons


17


is emitted toward a phosphor coated screen or faceplate


16


. This screen or faceplate


16


is an anode.




The electron emission tip of micro-cathode


13


is integral with substrate


11


and serves as a cathode. Gate structure


15


serves as a grid structure for applying an electrical field potential to its respective micro-cathode


13


.




A dielectric insulating layer


14


is deposited on the conductive micro-cathode


13


, which micro-cathode


13


can be formed from the substrate or from one or more deposited conductive films


12


, such as a chromium amorphous silicon bilayer. The dielectric insulating layer


14


also has an opening at the field emission site location.




Disposed between the faceplate


16


and baseplate


21


are located spacer support structures


18


which function to support the atmospheric pressure which exists on the faceplate


16


as a result of the vacuum which is created between the baseplate


21


and faceplate


16


for the proper functioning of the emitter tips of micro-cathode


13


.




The baseplate


21


of the invention comprises a matrix addressable array of micro-cathodes


13


, the substrate


11


on which the micro-cathodes


13


are created, the dielectric insulating layer


14


, and the grid structure


15


.




The process of the present invention provides a method for fabricating very sharp emitter tips of micro-cathode


13


useful in displays of the type illustrated in FIG.


1


.





FIG. 2

is a schematic cross-section of a representative anodization chamber


23


of the type used in the process of the present invention. A wafer


11


′ is suspended between two liquid baths and seals one bath from the other.




In the first bath is disposed a metallic electrode


24


, which, in this example, is platinum. The electrode


24


is a cathode and, therefore, has a positive charge when a voltage


26


(not shown) is placed between the baths. An electrode


25


is placed in the second bath. The electrode


25


is also platinum, in this example, and functions as an anode, as electrode


25


has a negative potential when a voltage


26


is placed between the baths.




In addition to water, the second bath also contains a hydrogen halide and a surfactant. The volume ratio of water to hydrogen halide to surfactant is 1:1:1. The preferred surfactant is an alcohol, such as isopropyl alcohol, which is relatively inexpensive and pure and commercially available. However, ethanol, 2-butanol, and Triton X100 are also suitable surfactants. The preferred hydrogen halide is hydrofluoric acid (HF).




When a voltage


26


is applied between the electrodes


24


,


25


, the chemicals in the second bath are attracted to the wafer


11


′ and react with it.




Electrochemical anodization of silicon in hydrofluoric acid etches a network of tiny pores into the silicon surface and forms a layer of porous material. Porous silicon forms at current densities from 10 to 250 mA/cm


2


in hydrofluoric acid concentrations from 1-49 weight percent, with resulting porosities from 27% to 70%.





FIGS. 3A-3B

illustrate the one embodiment of the process of the present invention.

FIG. 3A

illustrates a substrate


35


which has been patterned and subsequently doped. The substrate


35


comprises silicon and can be amorphous silicon, polycrystalline silicon, microgram silicon, and macrograin silicon, or any other suitable silicon-containing substrate.




The substrate


35


is patterned with a mask


32


. Mask


32


preferably comprises a photoresist or an oxide. The masked substrate


35


is then doped. The preferable dopant is boron, and therefore the doped regions


30


are P+.




The substrate


35


is then disposed in an anodization chamber


23


of the type described in FIG.


2


. The substrate


35


is anodized in the unmasked areas or doped regions


30


. The doped regions


30


become porous as a result of the chemicals reacting with the dopant in the substrate


35


. As the anodization process continues, the porous silicon develops a structure having randomly distributed, sharp spires or tips


33


, as illustrated in FIG.


3


B.




These tips


33


are useful as emitters in flat panel displays of the field emission type. The mask


32


is then stripped and the display fabricated. Alternatively, the mask


32


is left on the substrate


35


and functions as dielectric insulating layer


14


.





FIGS. 4A-4C

illustrate another embodiment of the process of the present invention.

FIG. 4A

illustrates substrate


45


which has a “blanket” dopant layer


40


. “Blanket” doping referring to the doping of substantially the entire surface of the substrate


45


. As in the previous embodiment, the substrate


45


comprises silicon and can be amorphous silicon, polycrystalline silicon, micrograin silicon, and macrograin silicon, or any other suitable silicon-containing substrate. The preferred dopant in this embodiment is also boron, and therefore the doped layer is P+.





FIG. 4B

illustrates the substrate


45


after it has undergone an anodization step, in which the dopant layer


40


becomes porous. The anodization take places in an anodization chamber


23


of the type illustrated in FIG.


2


. Since substantially the whole surface of the substrate


45


is doped and unmasked, substantially the whole dopant layer


40


is anodized.




As shown in

FIG. 4C

, subsequent to the anodization step, substrate


45


is patterned with a mask


46


. The mask


46


preferably comprises a photoresist or an oxide. The substrate


45


is then exposed to electromagnetic radiation (e.g., ultraviolet light) at or about room temperature for approximately 5 to 10 minutes. These parameters will vary with the intensity of the light selected.




Alternatively, the substrate


45


is simply exposed to patterned electromagnetic radiation, e.g., light that is shined through a photolithographic mask. This process is analogous to the process for exposing photoresist with a stepper. The preferred wavelength of light is in the ultraviolet spectrum.




The areas exposed to light are oxidized in air (actually, by the oxygen in the atmosphere). The oxidized areas can be used for isolation, or the oxide can be removed by rinsing in a hydrogen halide, such as hydrofluoric acid. The tips


43


are useful as field emitters of the type discussed in FIG.


1


.





FIGS. 5A-5D

illustrate low temperature oxidation sharpening of emitter tips using the process of the present invention.

FIG. 5A

illustrates a tip


53


on a substrate


51


made by any of the methods know in the art, and most commonly comprises silicon. The radius of curvature of the apex of the tip


53


is somewhat rounded.





FIG. 5B

shows the tip


53


on the substrate


51


after the tip


53


has been anodized, according to the process of the present invention. The tip


53


is placed in an anodization chamber of the type shown in

FIG. 2. A

porous layer


54


forms on the tip


53


as a result of the anodization, as shown in FIG.


5


B.




The tip


53


is then exposed to radiant energy, preferably light, in the ultraviolet spectrum. The tip


53


is exposed to the ultraviolet light at room temperature (e.g., approximately 22° C.-100° C.) in air. The oxygen in the atmosphere oxidizes the porous layer


54


on the tip


53


, when the tip


53


is irradiated, thereby forming oxide layer


55


, as illustrated in FIG.


5


C.




The oxide layer


55


is then stripped, preferably in a hydrogen halide. Hydrofluoric acid (HF) is the preferred hydrogen halide. When the oxide layer


55


is removed, the tip


53


on the substrate


51


is noticeably sharper, as shown in FIG.


5


D.




There are several advantages to the process of the present invention. One of the most important is that the process takes place at or about room temperature. The anodization process of the present invention results in a very high surface area that is easily oxidized. Most oxidation processes of semiconductor substrates are done in a steam ambient requiring high temperatures. The porous silicon is oxidized by ultraviolet light at low temperatures, i.e., 20° C.100° C.




All of the U.S. Patents cited herein are hereby incorporated by reference herein as if set forth in their entirety.




While the particular process, as herein shown and disclosed in detail, is fully capable of obtaining the objects and advantages herein before stated, it is to be understood that it is merely illustrative of the presently preferred embodiments of the invention, and that no limitations are intended to the details of construction or design herein shown other than as described in the appended claims. For example, one having ordinary skill in the art will realize that the parameters can vary.



Claims
  • 1. A method for fabricating field emitters, the method comprising:forming a pattern on a substrate comprising silicon to define isolated exposed regions; doping said isolated exposed regions of said substrate; and anodizing said isolated exposed regions of said substrate to form regions of field emitter tips, wherein said regions of field emitter tips are isolated by adjacent regions with relatively undoped silicon.
  • 2. The method of claim 1, wherein forming comprises forming said pattern on at least one of a polycrystalline silicon substrate, an amorphous silicon substrate, a microgram silicon substrate and a macrograin silicon substrate.
  • 3. The method of claim 1, wherein anodizing comprises anodizing with at least one of hydrogen halide, water, and a surfactant.
  • 4. The method of claim 3, wherein anodizing comprises anodizing with said surfactant comprising at least one of ethanol, isopropyl alcohol, 2-butanol, and Triton X100.
  • 5. The method of claim 3, wherein anodizing comprises anodizing with said hydrogen halide comprising hydrofluoric acid (HF), said hydrofluoric acid being 49 weight percent prior to anodization.
  • 6. The method of claim 5, wherein anodizing comprises anodizing in an electrochemical bath with a current of less than 250 mA/cm2 being applied to said electrochemical bath.
  • 7. A process for forming sharp asperities useful as field emitters, the process comprising:patterning a silicon substrate to form patterned and exposed areas on said silicon substrate; and selectively anodizing said exposed areas of said silicon substrate to form a plurality of said sharp asperities in each of said exposed areas.
  • 8. The process of claim 7, further comprising doping said exposed areas on said substrate with boron.
  • 9. The process of claim 7, wherein selectively anodizing comprises anodizing with an aqueous solution of at least one of a hydrogen halide and a surfactant.
  • 10. The process of claim 9, wherein anodizing comprises anodizing with at least one of ethanol, isopropyl alcohol, 2-butanol, and Triton X100.
  • 11. The process of claim 9, wherein anodizing comprises anodizing with said hydrogen halide comprised of hydrofluoric acid.
  • 12. The process of claim 7, wherein patterning comprises patterning with at least one of a photoresist and an oxide mask.
  • 13. The process of claim 7, wherein selectively anodizing comprises anodizing said silicon substrate in a solution comprising water, hydrofluoric acid, and isopropyl alcohol in a volume ratio of 1:1:1.
  • 14. The process of claim 7, wherein patterning comprises patterning a silicon substrate comprising at least one of a polycrystalline silicon substrate, an amorphous silicon substrate, a microgram silicon substrate and a macrograin silicon substrate.
  • 15. A method of fabricating isolated arrays of emitter tips, the method comprising:forming patterned regions and unpatterned regions on a silicon substrate; doping said unpatterned regions of said silicon substrate; and anodizing said unpatterned regions on said silicon substrate to form the arrays of emitter tips in said unpatterned regions on said silicon substrate, the arrays of emitter tips separated by said patterned regions of said silicon substrate.
  • 16. The method of claim 15, wherein forming comprises patterning said silicon substrate with an oxide.
  • 17. The method of claim 16, further comprising disposing said array of emitter tips in a field emission display having an anode grid, wherein said oxide functions as an insulator to electrically isolate said array of emitter tips from said anode grid.
  • 18. The method of claim 15, wherein doping comprises doping said silicon substrate with boron.
  • 19. The method of claim 17, wherein anodizing comprises anodizing with an aqueous solution of at least one of a hydrogen halide and a surfactant.
  • 20. The method of claim 15, wherein forming comprises patterning said silicon substrate with a photoresist.
  • 21. The method of claim 20, further comprising removing said photoresist from said silicon substrate.
  • 22. The method of claim 15, wherein forming comprises patterning a silicon substrate comprising at least one of a polycrystalline silicon substrate, an amorphous silicon substrate, a microgram silicon substrate and a macrograin silicon substrate.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of application Ser. No. 09/782,396, filed Feb. 13, 2001, now U.S. Pat. No. 6,426,234, which is a continuation of application Ser. No. 08/864,496, filed May 28, 1997, now U.S. Pat. No. 6,187,604 B1, issued Feb. 13, 2001.

US Referenced Citations (16)
Number Name Date Kind
3665241 Spindt et al. May 1972 A
3755704 Spindt et al. Aug 1973 A
3812559 Spindt et al. May 1974 A
4923421 Brodie et al. May 1990 A
5232549 Cathey et al. Aug 1993 A
5269877 Bol Dec 1993 A
5329207 Cathey et al. Jul 1994 A
5393647 Neukermans et al. Feb 1995 A
5430300 Yue et al. Jul 1995 A
5529524 Jones Jun 1996 A
5652474 Wilshaw et al. Jul 1997 A
5844251 MacDonald et al. Dec 1998 A
5923948 Cathey, Jr. Jul 1999 A
5981303 Gilton Nov 1999 A
6080032 Alwan Jun 2000 A
6187604 Gilton Feb 2001 B1
Non-Patent Literature Citations (20)
Entry
Sze, S.M., VLSI Technology, 2nd Ed., pp. 115-116.
Xie, Y.H., et al., “Luminescence and Structural Study of Porous Silicon Films,” American Institute of Physics, Mar. 1992, pp. 2403-2407.
Bsiesy, A., et al., “Anodic Oxidation of Porous Silicon Layers Formed on Lightly p-Doped Substrates,” J. Electrochem. Soc., vol. 138, No. 11, Nov. 1991, pp. 3450-3456.
George, T., et al., “Microstructural Investigations of Ligh-Emitting Porous Si Layers,” American Institute of Physics, May 1992, pp. 2359-2361.
Solomons, T.W. Graham, “Organic Chemistry,” 2nd Ed., John Wiley & Sons, New York, 1976, pp. 63-64.
Wolf, Stanley, et al., “Silicon Processing for the VLSI Era,” vol. 1, pp. 407-409, 1986.
Neamen, Donald A., “Semiconductor Physics and Devices,” Solar Cells, pp. 615-625.
Seidel, H., et al., “Anistropic Etching of Crystalline Silicon in Alkaline Solutions,” J. Electrochem. Soc., vol. 137, No. 11, Nov. 1990, pp. 3612-3626.
Beale, M.I.J., et al., “Microstructure and Formation Mechanism of Porous Silicon,” American Institute of Physics, Jan. 1985, pp. 86-88.
Izidinov, S.O., et al., “Anomalously High Photovoltaic Activity of Polished n-Type Silicon During Anodic Porous-Layer Formation in Hydrofluoric-Acid Solutions,” Elektrokhimiya, vol. 23, No. 11, pp. 1554-1559, Nov. 1987 (translated).
Motohiro, Tomoyoshi, et al., “Excitation Spectra of the Visible Photoluminescence of Anodized Porous Silicon,” J. Appl. Phys., 1992.
Smith, R.L., et al., “Porous Si Formation Mechanisms,” American Institute of Physics, Apr. 1992, pp. R1-R22.
Koyama, Hideki, et al., “Photoelectrochemical Effects of Surface Modification of n-Type Si with Porous Layer,” J. Electrochem. Soc., vol. 138, No. 1, Jan. 1991, pp. 254-260.
Imai, Kazuo, et al., FIPOS (Full Isolation by Porous Oxidized Silicon) Technology and Its Application to LSI's IEEE Transactions on Electron Devices, vol. ED-31, No. 3, Mar. 1984, pp. 297-302.
Seidel, H., et al., “Anisotropic Etching of Crystalline Silicon in Alkaline Solutions,” J. Electrochem. Soc., vol. 137, No. 11, Nov. 1990, pp. 3626-3632.
Branston et al., “Field Emission from Metal-Coated Silicon Tips,” Oct. 1991, IEEE Transactions on Electron Devices, vol. 38, No. 10, pp. 2329-2313.
Arita, Yoshinobu, et al., “Formation and Properties of Porous Silicon Film,” J. Electrochem. Soc., vol. 124, No. 2, pp. 285-295.
Anderson, Rolfe C., et al., “Investigations of the Electrical Properties of Porous Silicon,” J. Electrochem. Soc., Nov. 1991, pp. 3406-3411.
Koshida, Nobuyoshi, et al., “Characterization Studies of p-Type Porous Si and Its Photoelectrochemical Activation,” J. Electrochem. Soc., Mar. 1991, pp. 837-841.
Turner, Dennis R., “Electropolishing Silicon in Hydrofluoric Acid Solutions,” J. Electrochem. Soc., Jul. 1958, pp. 402-408.
Continuations (2)
Number Date Country
Parent 09/782396 Feb 2001 US
Child 10/156284 US
Parent 08/864496 May 1997 US
Child 09/782396 US