Claims
- 1. A multitrack head including blocks of a magnetic ferrite and having a magnetic isolation glass filling slots separating said blocks for magnetic isolation between said blocks, said glass produced by the process comprising:
- mixing LT lead borosilicate glass at a weight percent ranging from 65 to 55 percent with the remainder being HT borosilicate glass, said mixing step producing a glass mixture;
- applying said glass mixture to the slots separating said blocks;
- glassing the slots with said glass mixture by heating said blocks and said glass mixture to a temperature sufficient to melt said glass mixture, said melted glass mixture filling the slots;
- hot isostatic pressing said glassed slots by subjecting said glassed slots and said blocks to sufficient temperature and pressure conditions to remove any bubbles present in said glass; and
- annealing said blocks with the glassed slots at a selected temperature which toughens the glass present in said slots.
- 2. A multitrack head as recited in claim 1 wherein said LT lead borosilicate glass used in said mixing step is present at approximately sixty percent by weight and said HT borosilicate glass used in said mixing step is present at approximately forty percent by weight.
- 3. A multitrack head as recited in claim 1 wherein said selected temperature in said annealing step is chosen according to a desired stress level for said glass present in said slabs.
- 4. A multitrack head as recited in claim 1 wherein said selected temperature in said annealing step is between 500.degree. C. and 520.degree. C.
- 5. A magnetic head including glass filling slots separating blocks of a magnetic ferrite for magnetic isolation between said blocks, wherein said glass comprises a mixture of LT lead borosilicate glass in the approximate range of 55 to 65 weight percent with the remainder being HT borosilicate glass.
- 6. A magnetic head as defined in claim 5 wherein a said glass comprises a mixture of LT lead borosilicate glass of approximately sixty percent by weight and of HT borosilicate glass of approximately forty percent by weight.
- 7. In a magnetic head having pole pieces and means for activating said pole pieces to write and/or read magnetic transitions to and/or from a magnetic media, at least one of said pole pieces including magnetic isolation glass between portions of said pole pieces, the improvement wherein said magnetic isolation glass comprises a mixture of an LT lead borosilicate glass and an HT borosilicate glass, said LT lead borosilicate being present in the range of from 55 to 65 weight percent with the remainder being HT borosilicate glass.
- 8. In a magnetic head as defined in claim 7 wherein said glass comprises a mixture of LT lead borosilicate glass of approximately sixty percent by weight and of HT borosilicate glass of approximately forty percent by weight.
- 9. A magnetic head for reading and/or writing magnetic transitions from and/or to a magnetic media comprising:
- pole pieces, at least one of said pole pieces requiring magnetic isolation;
- means including a coil for activating said pole pieces to provide a transducing action for reading and/or writing the magnetic transitions;
- at least one slot formed in said at least one of said pole pieces, said slot providing the magnetic isolation;
- a magnetic isolation glass filling said slot, said glass comprising a mixture of LT lead borosilicate glass in the approximate range of 55 to 65 weight percent with the remainder being HT borosilicate glass.
- 10. A magnetic head as defined in claim 9 wherein said glass comprises a mixture of LT lead borosilicate glass of approximately sixty percent by weight and of HT borosilicate glass of approximately forty percent by weight.
Parent Case Info
This application is a continuation of application Ser. No. 367,733 filed June 19, 1989, now abandoned.
US Referenced Citations (13)
Foreign Referenced Citations (1)
Number |
Date |
Country |
55-150118 |
Nov 1980 |
JPX |
Non-Patent Literature Citations (2)
Entry |
Nelson; IBM Technical Disclosure Bull, vol. 21; No. 5, 10-1978, p. 1776, "Glass Bonding Magnetic Heads Below Melting Point of Glass". |
IBM Technical Disclosure Bulletin, vol. 18, No. 6, Nov. 1975. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
367733 |
Jun 1989 |
|