Method of making nonwoven fabric comprising splittable fibers

Abstract
The present invention relates generally to a method of making nonwoven fabrics, wherein the fabrics are formed from splittable filaments or staple length fibers having a plurality of sub-components which are at least partially separable. The filaments or fibers are at least partially separated into their sub-components attendant to hydroentanglement, which can be effected on a three-dimensional image transfer device. Improved physical properties, including improved tensile strength, elongation, and Taber Abrasion resistance are achieved.
Description




TECHNICAL FIELD




The present invention relates generally to a method of making a nonwoven fabric exhibiting enhanced physical properties, including improved drape and hand, and more particularly to a method of making a nonwoven fabric comprising hydroentangling a precursor web at least partially comprising splittable filaments or staple length fibers, whereby the precursor web is imaged and patterned on a three-dimensional image transfer device.




BACKGROUND OF THE INVENTION




Nonwoven fabrics are used in a wide variety of applications where the engineered qualities of the fabric can be advantageously employed. These types of fabrics differ from traditional woven or knitted fabrics in that the fabrics are produced directly from a fibrous mat eliminating the traditional textile manufacturing processes of multi-step yarn preparation, and weaving or knitting. Entanglement of the fibers or filaments of the fabric acts to provide the fabric with a substantial level of integrity.




U.S. Pat. No. 3,485,706, to Evans, hereby incorporated by reference, discloses processes for effecting the hydroentanglement of nonwoven fabrics. More recently, hydroentanglement techniques have been developed which impart images or patterns to the entangled fabric by effecting hydroentanglement on three-dimensional image transfer devices. Such three-dimensional image transfer devices are disclosed in U.S. Pat. Nos. 5,098,764, and 5,244,711, hereby incorporated by reference, with the use of such image transfer devices being desirable for providing fabrics with the desired physical properties as well as an aesthetically pleasing appearance.




For specific applications, a nonwoven fabric must exhibit a combination of specific physical characteristics. For example, for some applications it is desirable that nonwoven fabrics exhibit both wet and dry strength characteristics comparable to those of traditional woven or knitted fabrics. While nonwoven fabrics exhibiting sufficient strength can typically be manufactured by selection of appropriate fiber or filament composition, fabric basis weight, and specific process parameters, the resultant fabrics may not exhibit the desired degree of drapeability and hand as traditional woven or knitted fabrics exhibiting comparable strength. While it is known in the prior art to treat nonwoven fabrics with binder compositions for enhancing their strength and durability, such treatment can undesirably detract from the drape and hand of the fabric.




While manufacture of nonwoven fabrics from homopolymer, single component filaments or fibers is well-known, use of multi-component “splittable” fibers or filaments can be advantageous for some applications. These types of splittable fibers or filaments comprise plural sub-components, typically comprising two or more different polymeric materials, with the sub-components arranged in side-by-side relationship along the length of the filaments or fibers. Various specific cross-sectional configurations are known, such as segmented-pie sub-components, islands-in-the-sea sub-components, flower-like sub-components, side-by-side sub-component arrays, as well as a variety of additional specific configurations.




The sub-components of splittable fibers or filaments can be separated by various chemical or mechanical processing techniques. For example, portions of the multi-component fiber or filament can be separated by heating, needlepunching, or water jet treatment. Suitable chemical treatment of some types of multi-component fibers or filaments acts to dissolve portions thereof, thus at least partially separating the sub-components of the fibers or filaments.




U.S. Pat. No. 4,476,186, to Kato et al., hereby incorporated by reference, discloses various forms of multi-component fibers and filaments, and contemplates formation of structures wherein splitting of the fibers or filaments on one or more surfaces of these structures provides desired physical properties. This patent particularly contemplates treatment of the fibrous structures with polyurethane compositions, to thereby form synthetic leather-like materials.




The present invention contemplates formation of nonwoven fabrics exhibiting desired physical properties, including wet and dry strength characteristics, as well as good drapeability and hand.




SUMMARY OF THE INVENTION




The present invention is directed to a method of making a nonwoven fabric which includes imaging and patterning of a precursor web by hydroentanglement on a three-dimensional image transfer device. Notably, the precursor web at least partially comprises splittable filaments or staple length fibers, each of which comprises plural sub-components which are at least partially separable from each other. Attendant to hydroentanglement, the high pressure liquid streams impinging upon the precursor web act to at least partially separate the sub-components of the splittable filaments or fibers from each other, thus creating filament or fiber components having relatively small deniers. Because of the relatively reduced bending modules exhibited by the fine-denier sub-components, imaging and entanglement of the web is enhanced for fabric formation. The resultant fabric exhibits relatively high wet and dry tensile strengths, without resort to application of binder compositions or the like, and thus exhibits desirable drapeability and hand. By virtue of the fabric's integrity, post-formation processes, such as jet dyeing, can be effected without the application of a binder composition, as is typically required.




In accordance with the disclosed embodiment, the present method comprises providing a precursor web at least partially comprising splittable, staple length fibers, wherein each of the splittable fibers comprises plural sub-components at least partially separable from each other. In presently preferred embodiments, splittable fibers having so-called segmented-pie and swirled configurations have been employed.




The present method further comprises providing a three-dimensional image transfer device having a foraminous forming surface. This type of image transfer device includes a distinct surface pattern or image which is imparted to the precursor web during fabric formation by hydroentanglement.




The precursor web is positioned on the image transfer device, with hydroentanglement effected by application of a plurality of high-pressure liquid streams. The high-pressure liquid streams act to entangle and integrate the fibers of the precursor web. By virtue of their high energy, the liquid streams at least partially separate the sub-components of the splittable fibers, thus enhancing the clarity of the image imparted to the precursor web from the image transfer device.




Depending upon the specific application for the resultant nonwoven fabric, various types of splittable, staple length fibers can be employed. In current embodiments, splittable staple length fibers have been used comprising nylon, and one of 1,4 cyclohexamethyl terephthalate and polyethylene terephthalate sub-components. It is also contemplated that the splittable fibers may be blended with staple length fibers selected from the group consisting of nylon, polyester and rayon.




Cross-lapping of a carded precursor web prior to positioning on the image transfer device desirably enhances the effect of the hydroentanglement treatment in patterning and imaging the precursor web. By virtue of the high degree of integrity imparted to the web attendant to hydroentanglement, the present method further contemplates that the nonwoven fabric can be jet dyed, subsequent to hydroentanglement, preferably without the application of a binder composition thereto.




A nonwoven fabric embodying the principles of the present invention can be formed to exhibit low air permeability, with the fabric thus being suitable for applications where the barrier properties of a fabric are important, such as for medical gowns and the like. The fabric is formed from a fibrous matrix at least partially comprising splittable, spunbond filaments, wherein each of the splittable filaments comprises plural sub-components at least partially separated from each other. Notably, the fabric has been found to exhibit desirably high strength and elongation, exhibiting permeability lower than a comparable melt blown fabric, while being three to four times stronger, with three to five times more elongation. Aside from medical applications, potential uses include filter media and personal hygiene articles.




Other features and advantages of the present invention will become readily apparent from the following detailed description, the accompanying drawings, and the appended claims.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a diagrammatic view of a hydroentangling apparatus for practicing the method of the present invention;





FIGS. 2-4

are views illustrating the configuration of a “left-hand twill” three-dimensional image transfer device;





FIGS. 5A and 5B

are isometric and plan views, respectively, of the configuration of a “pique” three-dimensional image transfer device;





FIGS. 6

is a diagrammatic plan view of the configuration of a “wave” pattern of a three-dimensional image transfer device;





FIG. 7

is a diagrammatic plan view of the configuration of the “enlarged basketweave” pattern of a three-dimensional image transfer device;





FIG. 7A

is a diagrammatic plan view of the configuration of the “placemat” pattern of a three-dimensional image transfer device;





FIGS. 8A

to


8


F are photomicrographs of nonwoven fabrics including fabrics formed in accordance with the present invention; and





FIG. 9

shows illustrations of a three-dimensional image transfer device having a “octagon and squares” pattern.











DETAILED DESCRIPTION




While the present invention is susceptible of embodiment in various forms, there is shown in the drawings, and will hereinafter be described, preferred embodiments of the invention, with the understanding that the present disclosure is to be considered as an exemplification of the invention, and is not intended to limit the invention to the specific embodiment illustrated.




The present invention is directed to a method of forming nonwoven fabrics by hydroentanglement, wherein imaging and patterning of the fabrics is enhanced by hydroentanglement on a three-dimensional image transfer device. Enhanced physical properties of the resultant fabric, including enhanced patterning and imaging, is achieved by providing a precursor web at least partially comprising splittable filaments or fibers, that is, filaments or fibers which can each be divided into plural sub-components. Through the use of high-pressure water jets for effecting hydroentangling and imaging, these splittable fibers or filaments are at least partially separated into their sub-components, with the high pressure water jets acting on these sub-components. By virtue of the reduced bending modules of these relatively fine-denier sub-components, enhanced imaging and patterning of the fabric is achieved. Notably, the drapeability and hand of the resultant fabric is enhanced, thus enhancing versatile use of the fabric.




With reference to

FIG. 1

, therein is illustrated an apparatus for practicing the present method for forming a nonwoven fabric. The fabric is formed from a precursor web comprising a fibrous matrix which typically comprises staple length fibers, but which may comprise substantially continuous filaments. The fibrous matrix is preferably carded and cross-lapped to form the precursor web, designated P. In accordance with the present invention, the precursor web at least partially comprises splittable staple length fibers or filaments.





FIG. 1

illustrates a hydroentangling apparatus for forming nonwoven fabrics in accordance with the present invention. The apparatus includes a foraminous forming surface in the form of a belt


10


upon which the precursor web P is positioned for pre-entangling by entangling manifold


12


. Pre-entangling of the precursor web, prior to imaging and patterning, is subsequently effected by movement of web P sequentially over a drum


14


having a foraminous forming surface, with entangling manifold


16


effecting entanglement of the web. Further entanglement of the web can be effected on the foraminous forming surface of a drum


18


by entanglement manifold


20


, with subsequent movement of the web over successive foraminous drums


22


for successive entangling treatment by entangling manifolds


24


′,


24


′.




The entangling apparatus of

FIG. 1

further includes an imaging and patterning drum


24


comprising a three-dimensional image transfer device for effecting imaging and patterning of the now-entangled precursor web. The image transfer device includes a movable imaging surface which moves relative to a plurality of entangling manifolds


26


which act in cooperation with three-dimensional elements defined by the imaging surface of the image transfer device to effect imaging and patterning of the fabric being formed.





FIG. 1

also illustrates a J-box or scray


23


which can be employed for supporting the precursor web P as it is advanced onto the image transfer device, to thereby minimize tension within the precursor web. By controlling the rate of the advancement of the precursor web onto the imaging surface to minimize, or substantially eliminate, tension within the web, enhanced hydroentanglement of the precursor web can be effected. Hydroentanglement results in portions of the precursor web being displaced from on top of the three-dimensional surface elements of the imaging surface to form an imaged and patterned nonwoven fabric. By use of relatively high-pressure hydroentangling jets, the splittable fibers or filaments of the precursor web are at least partially separated into sub-components, with enhanced imaging and patterning thus resulting.




The enhanced imaging and patterning achieved through practice of the present invention is evidenced by the appended microphotographs of

FIGS. 8A

to


8


F. The fabric samples designated “CLC-205” were formed from conventional, non-splittable fibers, comprising a 50%/50% blend of polyethylene terephthalate (PET)/nylon fibers. The samples designated “CLC-069B” comprise 100% splittable staple length fibers, having 16 sub-components in a segmented-pie configuration. This type of fiber, available from Fiber Innovation Technology, Inc., under the designation Type 502, comprises a PET/nylon blend, with 8 sub-component segments each of PET and nylon. This type of fiber has a nominal denier of 3.0, with each sub-component having a denier of 0.19. Samples designated “CLC-096” were formed from Unitika splittable staple length fibers, production designation N91, having a denier of 2.5, with 20 sub-components in a segmented-pie configuration, with each sub-component having a 0.12 denier. These splittable fibers also comprise a blend of PET/nylon.




With reference to the microphotographs, it will be observed from the “top light” and “dark field” views that by comparison of the control sample (CLC-205) with sample CLC-069B (F.I.T. splittable fibers), that the splittable fiber sample shows more uniform coverage, with a clearer image, or better image clarity. The dark field comparison shows a much deeper image than that achieved with the control non-splittable fiber sample, with bundling or roping of the entwined sub-denier fiber components being evident. It is believed that the improved image clarity (i.e., less fuzzy pattern) is achieved by virtue of the enhanced fiber entanglement, which is achieved by the relatively reduced bending modules of the sub-components of the splittable fibers.




Comparison of the Unitika splittable fiber sample (CLC-096A) with the control, non-splittable fiber sample also shows improved image clarity, with better definition of the imaged pattern. Interconnecting regions of the pattern, at which less fiber is present, are not as well defined in the control, non-splittable fiber sample, as in the sample formed from splittable fibers in accordance with the present invention. Comparison of the two splittable fiber samples, CLC-069B and CLC-096A, shows the former to provide better defined fiber transition regions, which is believed to be achieved by virtue of this type of fiber being more easily splittable attendant to hydroentangling processing. Very fine sub-denier composite fibers can be hard to make, and can complicate splitting of the fibers, such as by hydroentangling processes. This phenomenon suggests optimum results may be achieved through use of splittable fibers having a certain maximum number of splittable sub-components.




EXAMPLES




Appended Table 1 (2 pages) sets forth test data regarding various sample nonwoven fabrics formed in accordance with the principles of the present invention, including comparison to control samples. Reference to various image transfer devices (ITD) refers to configurations illustrated in the appended drawings. Reference to “100×98” and “22×23” refers to foraminous forming screens. Reference to “20×20”, “12×12”, “14×14”, and “6×8” refers to a three-dimensional image transfer device having an array of “pyramidal” three-dimensional surface elements, configured generally in accordance with FIG. 9 of U.S. Pat. No. 5,098,764, hereby incorporated by reference. The referenced “placemat” image transfer device is a composite image comprised of a background “tricot” pattern (in accordance with U.S. Pat. No. 5,670,234, hereby incorporated by reference), a central “vine and leaf” pattern, and a circumferential “lace” pattern. The overall dimension of the rectangular image is approximately 10 inches by 13 inches. The approximate depth of the image in the background region is 0.025 inches, and in the “vine and leaf” and “lace” regions is 0.063 inches. Reference to “prebond” refers to a fabric tested after pre-entangling, but formed without imaging on a image transfer device.




For manufacture of the fabric samples, an apparatus as illustrated in

FIG. 1

was employed. Pre-entangling manifolds at drums


14


,


18


, and


22


were operated at 40 bar, 50 bar, 80 bar, and 81 bar, respectively, unless otherwise noted. The three manifolds


26


at the image transfer device


25


were operated at or in excess of 2500 psi, unless otherwise noted.




A further aspect of the present invention contemplates a nonwoven fabric formed from spunbond filaments, wherein each of the filaments comprises plural sub-components which are at least partially separated from each other. Table 2 sets forth certain physical properties of spunbond, as well as staple length, fabrics formed in accordance with the present invention on a foraminous forming surface in the form of a 100 mesh forming screen. As will be observed, fabrics formed in accordance with the present invention from splittable, spunbond filaments, all exhibited very good Taber Abrasion resistance to roping, greater than 35 cycles. In the sample in which the filaments were formed from polyester and polyethylene (8-segment crescent configuration), the fabric exhibited a ratio of machine direction tensile strength to basis weight of 19. For other samples formed from spunbond filaments, comprising polyester and nylon, the ratio of machine direction tensile strength to basis weight was at least about 23. As will be noted, all fabrics formed from spunbond filaments exhibit air permeability no greater than about 26 cfm (ft.


3


/min.), which can be desirable for certain applications.




Table 2 also shows fabrics formed in accordance with the present invention from splittable fibers. These samples were formed from bicomponent staple fibers comprising polyester and nylon, and exhibited a ratio of machine direction tensile strength to basis weight of at least about 22; these samples all exhibit a Taber Abrasion resistance to roping greater than 35 cycles (i.e., no roping).




Table 2 sets forth comparative data for a representative polyester and pulp fabric (designated PET/pulp). The greater tensile strength, elongation, and Taber Abrasion of fabrics formed in accordance with the present invention will be noted.




From the foregoing, numerous modifications and variations can be effected without departing from the true spirit and scope of the novel concept of the present invention. It is to be understood that no limitation with respect to the specific embodiment disclosed herein is intended or should be inferred. The disclosure is intended to cover, by the appended claims, all such modifications as fall within the scope of the claims.



















TABLE 1











Physical Property




CLC-220-NF




CLC-098A-NF




Delta




CLC-098B-NF




Delta




CLC-098C-NF




Delta









Image




100 × 98 Screen




Wave




220 v. 098A




Oct/Sq.




220 v. 098B




22 × 23




220 v. 098C






Weight




2.06




2.15




4%




2.08




1%




2.07




0%






Bulk




0.014




0.021




33%




0.019




26%




0.019




26%






Tensile - Dry [MD]




37.5




42.7




12%




41.8




10%




42.4




12%






Tensile - Wet [MD]




35.2




39.8




12%




34.1




−3%




45.9




23%







 −6%




 −7%





−18%





   8%






Elongation - Dry [MD]




35.4




53.9




34%




40.0




11%




34.3




−3%






Elongation - Wet [MD]




44.4




44.7




1%




41.0




−8%




42.3




−5%







  20%




−17%





   2%





  19%






Tensile - Dry [CD]




23.1




20.6




−11%




16.9




−27%




23.7




3%






Tensile-Wet [CD]




16.0




18.2




12%




18.4




13%




18.4




13%







−31%




−12%





   8%





−23%






Elongation - Dry [CD]




128.6




98.8




−23%




96.8




−25%




93.0




−28%






Elongation - Wet [CD]




122.8




109.3




−11%




103.0




−16%




87.6




−29%







 −5%




  10%





   6%





 −6%






Handle [MD]




37




21




−43%






Handle [CD]




4




3




−25%






Cantilever Bend [MD]




7.7




7.2




−6%






Cantilever Bend [CD]




3.1




2.7




−13%






Absorbency Capacity




676




805




16%




698




3%




716




6%






Air Perm




85




111




23%




386




78%




407




79%






Modulus 3% [MD]




1.03




0.68




−34%





#DIV/0!





#DIV/0!






Modulus 5% [MD]




1.17




0.78




−33%





#DIV/0!





#DIV/0!






Modulus 10% [MD]




1.14




0.83




−27%





#DIV/0!





#DIV/0!






Modulus 20% [MD]




1.03




0.9




−13%





#DIV/0!





#DIV/0!






Modulus 3% [CD]




0.05




0.015




−70%





#DIV/0!





#DIV/0!






Modulus 5% [CD]




0.05




0.015




−70%





#DIV/0!





#DIV/0!






Modulus 10% [CD]




0.05




0.02




−60%





#DIV/0!





#DIV/0!






Modulus 20% [CD]




0.05




0.025




−50%





#DIV/0!





#DIV/0!






Load @ 10% Elong. [MD]




12.29




8.2




−33%





#DIV/0!





#DIV/0!






Load @ 10% Elong. [CD]




0.41




0.13




−68%





#DIV/0!





#DIV/0!






Load @ 20% Elong. [MD]




23.01




18.3




−20%





#DIV/0!





#DIV/0!






Load @ 20% Elong. [CD]




0.94




0.34




−64%





#DIV/0!





#DIV/0!






















Physical Property




CLC-220-NF




CLC-098A-NF




Delta




CLC-205-NF




CLC-069B-NF




Delta











Image




100 × 98 Mesh




Wave




220 v. 098A




Wave




Wave




205 v. 069B







Weight




2.06




2.15




4%




3.1




3




−3%







Bulk




0.014




0.021




33%




0.039




0.026




−33%







Tensile - Dry [MD]




37.5




42.7




12%




68.3




59.1




−13%







Tensile - Wet [MD]




35.2




39.8




12%




66.9




59.4




−11%







Delta [Dry v. Wet]




 −6%




 −7%





 −2%




 1%







Elongation - Dry [MD]




35.4




53.9




34%




64.6




44.3




−31%







Elongation - Wet [MD]




44.4




44.7




1%




65.5




49.1




−25%







Delta [Dry v. Wet]




  20%




−17%





   1%




10%







Tensile - Dry [CD]




23.1




20.6




−11%




36.5




28.2




−23%







Tensile - Wet [CD]




16.0




18.2




12%




36.2




27.5




−24%







Delta [Dry v. Wet]




−31%




−12%





 −1%




−2%







Elongation - Dry [CD]




128.6




98.8




−23%




172.2




117.8




−32%







Elongation - Wet [CD]




122.8




109.3




−11%




149.0




118.4




−21%







Delta [Dry v. Wet]




 −5%




  10%





−13%




 1%







Handle [MD]




37




21




−43%




35




46




23%







Handle [CD]




4




3




−25%




8




7




−13%







Cantilever Bend [MD]




7.7




7.2




−6%






#DIV/0!







Cantilever Bend [CD]




3.1




2.7




−13%






#DIV/0!







Absorbency




676




805




16%






#DIV/0!







Air Perm




85




111




23%






#DIV/0!







Modulus 3% [MD]




1.03




0.68




−34%




0.27




0.45




40%







Modulus 5% [MD]




1.17




0.78




−33




0.39




0.68




43%







Modulus 10% [MD]




1.14




0.83




−27%




0.54




0.9




40%







Modulus 20% [MD]




1.03




0.9




−13%




0.72




1.07




33%







Modulus 3% [CD]




0.05




0.015




−70%




0.02




0.01




−50%







Modulus 5% [CD]




0.05




0.015




−70%




0.02




0.01




−50%







Modulus 10% [CD]




0.05




0.02




−60%




0.02




0.01




−50%







Modulus 20% [CD]




0.05




0.025




−50%




0.03




0.02




−33%







Load @ 10% Elong. [MD]




12.29




8.2




−33%




5.86




10.11




42%







Load @ 10% Elong. [CD]




0.41




0.13




−68%




0.12




0.4




70%







Load @ 20% Elong. [MD]




23.01




18.3




−20%




15.22




22.85




33%







Load @ 20% Elong. [CD]




0.94




0.34




−64%




0.3




0.97




69%



























TABLE 2











Sample ID




Shape




Polymer Combination




Fiber Process




Foraminous Surface









2.3 EFP





PET/Pulp




staple







91-51-04




8-seg crescent




PET/PE




bicomponent spunbond




100 Mesh






91-51-08




8-seg crescent




PET/Nylon




bicomponent spunbond




100 Mesh






23-12-02




16-seg pie




PET/Nylon




bicomponent spunbond




100 Mesh






23-12-03




16-seg pie




PET/Nylon




bicomponent spunbond




100 Mesh






23-12-04




16-seg pie




PET/Nylon




bicomponent spunbond




100 Mesh






CLC-2100




seg pie




PET/Nylon




bicomponent staple




100 Mesh






CLC-3000




seg pie




PET/Nylon




bicomponent staple




100 Mesh






CLC-4000




seg pie




PET/Nylon




bicomponent staple




100 Mesh





















Basis Weight




Air




MD Grab Tensile





MDT/BW




MD Grab



















Sample ID




gsm




oz/yd


2






cfm




g/cm




lb/In




MDT/BW




% of EFP




Elongation %






















2.3 EFP




77.487




2.3




36





38




17








91-51-04




96




2.85




11




 9659




54




19




112%




44






91-51-08




113




3.35




14




14469




81




24




142%




50






23-12-02




76.83




2.28




22




11750




66




29




170%




44






23-12-03




76.20




2.26




18




10757




60




27




157%




41






23-12-04




78.32




2.32




26




 9624




54




23




136%




37






CLC-2100




76.10




2.26




34




 9664




54




24




141%




45






CLC-3000




78.34




2.33




29




10429




58




25




148%




43






CLC-4000




81.52




2.42




27




 9576




54




22




130%




38

























CD Grab










CD Grab





CDT/BW




Elongation




Energy




Taber Abrasion




HH




















Sample ID




g/cm




lb/in




CDT/BW




% of EFP




%




hp-hr/lb




til roping




til fail




cm























2.3 EFP





21




 9







35




182




24






91-51-04




3247




18




 6




 71%




115




2.12




no




181






91-51-08




6184




35




10




115%




100




1.8




no roping




>250




32.9






23-12-02




5532




31




14




151%




 99




1.14




no roping




>250




33.5






23-12-03




3729




21




 9




103%




 82




1.86




no roping




>250






23-12-04




4470




25




11




120%




 88




2.72




no roping




>250






CLC-2100




4553




25




11




125%




109




1.27




no roping




189






CLC-3000




4388




25




11




117%




102




1.81




no roping




>250






CLC-4000




4147




23




10




107%




110




2.45




no roping




>250




23.3













Claims
  • 1. A method of making a nonwoven fabric, comprising the steps of:providing a precursor web at least partially comprising splittable, staple length fibers, wherein each of said splittable fibers comprises plural sub-components at least partially separable from each other; providing a three-dimensional image transfer device having a foraminous forming surface; positioning said precursor web on said image transfer device, and hydroentangling said precursor web with a plurality of liquid streams to thereby at least partially separate the sub-components of said splittable fibers and impart an image from said image transfer device to said precursor web to form a nonwoven fabric exhibiting a ratio of machine direction tensile strength to basis weight of at least about 22, and a Taber Abrasion resistance to roping greater than 35 cycles.
  • 2. A method of making a nonwoven fabric in accordance with claim 1, further comprising the step of:jet dyeing said nonwoven fabric.
  • 3. A method of making a nonwoven fabric, comprising the steps of:providing a precursor web at least partially comprising splittable, staple length fibers, wherein each of said splittable fibers comprises plural sub-components at least partially separable from each other; providing a three-dimensional image transfer device having a foraminous forming surface; positioning said precursor web on said image transfer device, and hydroentangling said precursor web with a plurality of liquid streams to thereby at least partially separate the sub-components of said splittable fibers and impart an image from said image transfer device to said precursor web to form a nonwoven fabric, wherein said step of providing set precursor web includes pro ding splittable, staple length fibers wherein the sub-components consist of nylon and one of 1,4 cyclohexamethyl terephthalate and polyethylene terephthalate.
  • 4. A method of making a nonwoven fabric, comprising the steps of:providing a precursor web at least partially comprising splittable, staple length fibers, wherein each of said splittable fibers comprises plural sub-components at least partially separable from each other; providing a three-dimensional image transfer device having a foraminous forming surface; positioning said precursor web on said image transfer device, and hydroentangling said precursor web with a plurality of liquid streams to thereby at least partially separate the sub-components of said splittable fibers and impart an image from said image transfer device to said precursor web to form a nonwoven fabric, wherein said step of providing said precursor web includes providing said web with a blend of said splittable staple length fibers, and fibers selected from the group consisting of nylon, polyester and rayon.
  • 5. A method of making a nonwoven fabric, comprising the steps of:providing a precursor web at least partially comprising splittable, staple length fibers, wherein each of said splittable fibers comprises plural sub-components at least partially separable from each other; providing a three-dimensional image transfer device having a foraminous forming surface; and positioning said precursor web on said image transfer device, and hydroentangling said precursor web with a plurality of liquid streams to thereby at least partially separate the sub-components of said splittable fibers and impart an image from said image transfer device to said precursor web to form a nonwoven fabric, further comprising the steps of cross-lapping said precursor w b prior to positioning on said image transfer device.
  • 6. A method of making a nonwoven fabric, comprising the steps of:providing a precursor web at least partially comprising splittable, staple length fibers, wherein each of said splittable fibers comprises plural sub-components at least partially separable from each other; providing a three-dimensional image transfer device having a foraminous forming surface; positioning said precursor web on said image transfer device, d hydroentangling said precursor web with a plurality of liquid streams to thereby at leas partially separate the sub-components of said splittable fibers and impart an image from said image transfer device to said precursor web to form a nonwoven fabric, wherein said step of providing said precursor web includes providing said splittable fibers with a denier of about 2.5 to 3.5, with sub-component of said splittable fibers each having a denier of about 0.1 to 0.3.
US Referenced Citations (31)
Number Name Date Kind
2862251 Kalwaites Dec 1958 A
3485707 Evans Dec 1969 A
3692618 Dorschner et al. Sep 1972 A
4107374 Kusunose et al. Aug 1978 A
4476186 Kato et al. Oct 1984 A
4560385 Baravian Dec 1985 A
4668566 Braun May 1987 A
4774110 Murakami et al. Sep 1988 A
4997611 Hartmann Mar 1991 A
5098764 Drelich et al. Mar 1992 A
5142750 Dyer et al. Sep 1992 A
5142753 Bolliand et al. Sep 1992 A
5244711 Drelich et al. Sep 1993 A
5290626 Nishioi et al. Mar 1994 A
5355565 Baravian Oct 1994 A
5482772 Strack et al. Jan 1996 A
5635290 Stopper et al. Jun 1997 A
5670234 Suehr et al. Sep 1997 A
5827597 James et al. Oct 1998 A
5840633 Kurihara et al. Nov 1998 A
5888916 Tadokoro et al. Mar 1999 A
5894747 Abernathy et al. Apr 1999 A
5899785 Groten et al. May 1999 A
5965084 Nishijima Oct 1999 A
5970583 Groten et al. Oct 1999 A
6103061 Anderson et al. Aug 2000 A
6200669 Marmon et al. Mar 2001 B1
6228490 Nagano et al. May 2001 B1
6444312 Dugan Sep 2002 B1
6461729 Dugan Oct 2002 B1
20020187329 Ista et al. Dec 2002 A1
Non-Patent Literature Citations (1)
Entry
“Advanced Fiber Spinning Technology”, edited by Professor T. Nakajima, Japanese Edition first published 1992, pp. 104-128, pp. 186-206, pp. 224-252.
Provisional Applications (1)
Number Date Country
60/204721 May 2000 US