11427740
The following is directed to abrasive articles, and particularly, abrasive articles including shaped abrasive particles.
Abrasive particles and abrasive articles made from abrasive particles are useful for various material removal operations including grinding, finishing, and polishing. Depending upon the type of abrasive material, such abrasive particles can be useful in shaping or grinding a wide variety of materials and surfaces in the manufacturing of goods. Certain types of abrasive particles have been formulated to date that have particular geometries, such as triangular shaped abrasive particles and abrasive articles incorporating such objects. See, for example, U.S. Pat. Nos. 5,201,916; 5,366,523; and 5,984,988.
Three basic technologies that have been employed to produce abrasive particles having a specified shape are (1) fusion, (2) sintering, and (3) chemical ceramic. In the fusion process, abrasive particles can be shaped by a chill roll, the face of which may or may not be engraved, a mold into which molten material is poured, or a heat sink material immersed in an aluminum oxide melt. See, for example, U.S. Pat. No. 3,377,660 (disclosing a process including flowing molten abrasive material from a furnace onto a cool rotating casting cylinder, rapidly solidifying the material to form a thin semisolid curved sheet, densifying the semisolid material with a pressure roll, and then partially fracturing the strip of semisolid material by reversing its curvature by pulling it away from the cylinder with a rapidly driven cooled conveyor).
In the sintering process, abrasive particles can be formed from refractory powders having a particle size of up to 10 micrometers in diameter. Binders can be added to the powders along with a lubricant and a suitable solvent, e.g., water. The resulting mixture, mixtures, or slurries can be shaped into platelets or rods of various lengths and diameters. See, for example, U.S. Pat. No. 3,079,242 (disclosing a method of making abrasive particles from calcined bauxite material including (1) reducing the material to a fine powder, (2) compacting under affirmative pressure and forming the fine particles of said powder into grain sized agglomerations, and (3) sintering the agglomerations of particles at a temperature below the fusion temperature of the bauxite to induce limited recrystallization of the particles, whereby abrasive grains are produced directly to size).
Chemical ceramic technology involves converting a colloidal dispersion or hydrosol (sometimes called a sol), optionally in a mixture, with solutions of other metal oxide precursors, into a gel or any other physical state that restrains the mobility of the components, drying, and firing to obtain a ceramic material. See, for example, U.S. Pat. Nos. 4,744,802 and 4,848,041. Other relevant disclosures on shaped abrasive particles and associated methods of forming and abrasive articles incorporating such particles are available at: abel-ip.com/publications/.
Still, there remains a need in the industry for improving performance, life, and efficacy of abrasive particles, and the abrasive articles that employ abrasive particles.
According to a first aspect, a shaped abrasive particle includes a body including a first surface, a second surface, a side surface extending between the first surface and second surface, and a flange portion extending from the side surface and the first major surface.
In another aspect, a shaped abrasive particle includes a body including a first surface, a second surface, and a side surface, wherein the body includes a gear-shaped two-dimensional shape including a plurality of teeth extending peripherally from the side surface of the body.
In another aspect, a shaped abrasive particle includes a body including a first surface, a second surface, and a side surface extending between a first surface and the second surface, wherein the first surface includes raised portions extending from exterior corners of the body along the first surface and joining in a center region of the first surface.
In another aspect, a shaped abrasive particle includes a body defining a partial-ellipsoid shape, the body including a first surface, a second surface, and a third surface extending between a portion of the first major surface and the second major surface, wherein at least a portion of the first surface and a portion of the second surface are connected to each other along a first edge and wherein a portion of the first surface and a portion of the third surface are connected to each other and define a second edge, and wherein a portion of the second surface and a portion of the third surface are connected to each other and define a third edge.
In another aspect, a shaped abrasive particle includes a body having a conical or frustoconical shape, wherein a surface of the body includes a plurality of protrusions extending in a spiral pathway.
In another aspect, a shaped abrasive particle includes a body defining a fin-shape, wherein the body includes a length, a width and a thickness and wherein the body includes a rectangular cross-sectional shape in the plane defined by the length and width and an elliptical cross-sectional shape in the plane defined by the width and thickness, and wherein the aspect ratio of width-to-thickness (w:t) is at least 2:1.
In another aspect, a shaped abrasive particle includes a rake-shaped body including a first group of projections extending from a central region of the body in a first direction and a second group of projections extending from the central region the body in a second direction, and wherein the first group of projections have a length (Lp1) that is different compared to a length (Lp2) of the second group of projections.
In another aspect, a shaped abrasive particle includes a body including a first surface, a second surface, and a side surface, wherein the body includes at least four distinct side surface portions separated by at least four exterior corners, and wherein at least one side surface portion includes a concave contour and wherein the particle includes a curved shape, wherein the first surface includes a substantially concave curvature and the second surface includes a substantially convex curvature.
In another aspect, a shaped abrasive particle includes a toothed body including a plurality of teeth extending from one side of the body, wherein the plurality of teeth define external corners of the body having an average spacing of less than 0.5(L), wherein L defines the length of the body.
In another aspect, a shaped abrasive agglomerate includes a body including a plurality of shaped abrasive particle portions bonded to each other to form the body of the shaped abrasive particle.
In another aspect, a shaped abrasive particle includes a body including at least a first surface, a second surface, a third surface, and a fourth surface, wherein each of the first, second, third, and fourth surfaces contact at least one of the other first, second, third, and fourth surfaces along at least one edge of the body, and wherein the first surface includes a concave contour.
In another aspect, a method of making a ceramic body includes creating a layer of material from a mixture including a precursor ceramic material; altering the surface of the layer with a gaseous or liquid material to create a pattern in an upper surface of the layer; and forming the layer into abrasive particles, wherein at least a portion of the abrasive particles includes a surface including at least a portion of the pattern created in the upper surface of the layer.
In another aspect, a method of forming a shaped abrasive particle includes placing a mixture including a ceramic precursor material into a production tool including a plurality of openings, wherein placing the mixture includes partially filling a majority of the openings of the plurality of openings.
In another aspect, a shaped abrasive particle includes a body including a plurality of discrete micro-voids distributed throughout the body, wherein the discrete micro-voids include a liquid or gas material.
In another aspect, a method of making shaped abrasive particles includes translating a production tool having openings over rollers and through a deposition zone configured to deposit a mixture into the openings, wherein in the deposition zone the production tool is translated over a primary roller having a greater diameter compared to any other rollers in contact with the production tool.
In another aspect, a shaped abrasive particle includes a multi-flanged body including a first shaped abrasive portion bonded to another shaped abrasive portion to form the body including at least two different flanges, and wherein the different flanges extend in different planes with respect to each other.
In another aspect, a shaped abrasive particle includes an annular body including a first surface, second surface, a third surface extending between the first surface and second surface, wherein the annular body includes a rounded contour, a central opening extend through the body, and wherein at least a portion of the first surface includes a non-planar contour.
The present disclosure may be better understood, and its numerous features and advantages made apparent to those skilled in the art by referencing the accompanying drawings.
The following is directed to abrasive articles including shaped abrasive particles. The methods herein may be utilized in forming shaped abrasive particles and using abrasive articles incorporating shaped abrasive particles. The shaped abrasive particles may be utilized in various applications, including for example fixed abrasive articles, such as coated abrasives, bonded abrasives, non-woven abrasive materials and the like. Alternatively, the shaped abrasive particles may be used in free abrasives. Various other uses may be derived for the shaped abrasive particles.
Methods for Making Shaped Abrasive Particles
Various methods may be utilized to obtain shaped abrasive particles. Some suitable processes used to fabricate the shaped abrasive particles can include, but is not limited to, depositing, printing (e.g., screen-printing), molding, pressing, casting, sectioning, cutting, dicing, punching, drying, curing, coating, extruding, rolling, and a combination thereof.
Shaped abrasive particles are formed such that each particle has substantially the same arrangement of surfaces and edges relative to each other for shaped abrasive particles having the same two-dimensional and three-dimensional shapes. As such, shaped abrasive particles can have a high shape fidelity and consistency in the arrangement of the surfaces and edges relative to other shaped abrasive particles of the same group having the same two-dimensional and three-dimensional shape. By contrast, non-shaped abrasive particles can be formed through different process and have different shape attributes. For example, non-shaped abrasive particles are typically formed by a comminution process, wherein a mass of material is formed and then crushed and sieved to obtain abrasive particles of a certain size. However, a non-shaped abrasive particle will have a generally random arrangement of the surfaces and edges, and generally will lack any recognizable two-dimensional or three dimensional shape in the arrangement of the surfaces and edges around the body. Moreover, non-shaped abrasive particles of the same group or batch generally lack a consistent shape with respect to each other, such that the surfaces and edges are randomly arranged when compared to each other. Therefore, non-shaped grains or crushed grains have a significantly lower shape fidelity compared to shaped abrasive particles.
The process of forming shaped abrasive particles can be initiated by forming a mixture 108 including a ceramic material and a liquid. In particular, the mixture 108 can be a gel formed of a ceramic powder material and a liquid. In accordance with an embodiment, the gel can be formed of the ceramic powder material as an integrated network of discrete particles.
The mixture 108 may contain a certain content of solid material, liquid material, and additives such that it has suitable rheological characteristics for use with the process detailed herein. That is, in certain instances, the mixture can have a certain viscosity, and more particularly, suitable rheological characteristics that form a dimensionally stable phase of material that can be formed through the process as noted herein. A dimensionally stable phase of material is a material that can be formed to have a particular shape and substantially maintain the shape for at least a portion of the processing subsequent to forming. In certain instances, the shape may be retained throughout subsequent processing, such that the shape initially provided in the forming process is present in the finally-formed object. It will be appreciated that in some instances, the mixture 108 may not be a shape-stable material, and the process may rely upon solidification and stabilization of the mixture 108 by further processing, such as drying.
The mixture 108 can be formed to have a particular content of solid material, such as the ceramic powder material. For example, in one embodiment, the mixture 108 can have a solids content of at least about 25 wt %, such as at least about 35 wt %, or even at least about 38 wt % for the total weight of the mixture 108. Still, in at least one non-limiting embodiment, the solids content of the mixture 108 can be not greater than about 75 wt %, such as not greater than about 70 wt %, not greater than about 65 wt %, not greater than about 55 wt %, not greater than about 45 wt %, or not greater than about 42 wt %. It will be appreciated that the content of the solids materials in the mixture 108 can be within a range between any of the minimum and maximum percentages noted above.
According to one embodiment, the ceramic powder material can include an oxide, a nitride, a carbide, a boride, an oxycarbide, an oxynitride, and a combination thereof. In particular instances, the ceramic material can include alumina. More specifically, the ceramic material may include a boehmite material, which may be a precursor of alpha alumina. The term “boehmite” is generally used herein to denote alumina hydrates including mineral boehmite, typically being Al2O3.H2O and having a water content on the order of 15%, as well as pseudoboehmite, having a water content higher than 15%, such as 20-38% by weight. It is noted that boehmite (including pseudoboehmite) has a particular and identifiable crystal structure, and therefore a unique X-ray diffraction pattern. As such, boehmite is distinguished from other aluminous materials including other hydrated aluminas such as ATH (aluminum trihydroxide), a common precursor material used herein for the fabrication of boehmite particulate materials.
Furthermore, the mixture 108 can be formed to have a particular content of liquid material. Some suitable liquids may include water. In accordance with one embodiment, the mixture 108 can be formed to have a liquid content less than the solids content of the mixture 108. In more particular instances, the mixture 108 can have a liquid content of at least about 25 wt % for the total weight of the mixture 108. In other instances, the amount of liquid within the mixture 108 can be greater, such as at least about 35 wt %, at least about 45 wt %, at least about 50 wt %, or even at least about 58 wt %. Still, in at least one non-limiting embodiment, the liquid content of the mixture can be not greater than about 75 wt %, such as not greater than about 70 wt %, not greater than about 65 wt %, not greater than about 62 wt %, or even not greater than about 60 wt %. It will be appreciated that the content of the liquid in the mixture 108 can be within a range between any of the minimum and maximum percentages noted above.
Furthermore, to facilitate processing and forming shaped abrasive particles according to embodiments herein, the mixture 108 can have a particular storage modulus. For example, the mixture 108 can have a storage modulus of at least about 1×104 Pa, such as at least about 4×104 Pa, or even at least about 5×104 Pa. However, in at least one non-limiting embodiment, the mixture 108 may have a storage modulus of not greater than about 1×107 Pa, such as not greater than about 2×106 Pa. It will be appreciated that the storage modulus of the mixture 108 can be within a range between any of the minimum and maximum values noted above.
The storage modulus can be measured via a parallel plate system using ARES or AR-G2 rotational rheometers, with Peltier plate temperature control systems. For testing, the mixture 108 can be extruded within a gap between two plates that are set to be approximately 8 mm apart from each other. After extruding the gel into the gap, the distance between the two plates defining the gap is reduced to 2 mm until the mixture 108 completely fills the gap between the plates. After wiping away excess mixture, the gap is decreased by 0.1 mm and the test is initiated. The test is an oscillation strain sweep test conducted with instrument settings of a strain range between 0.01% to 100%, at 6.28 rad/s (1 Hz), using 25-mm parallel plate and recording 10 points per decade. Within 1 hour after the test completes, the gap is lowered again by 0.1 mm and the test is repeated. The test can be repeated at least 6 times. The first test may differ from the second and third tests. Only the results from the second and third tests for each specimen should be reported.
Furthermore, to facilitate processing and forming shaped abrasive particles according to embodiments herein, the mixture 108 can have a particular viscosity. For example, the mixture 108 can have a viscosity of at least about 2×103 Pa s, such as at least about 3×103 Pa s, at least about 4×103 Pa s, at least about 5×103 Pa s, at least about 6×103 Pa s, at least about 8×103 Pa s, at least about 10×103 Pa s, at least about 20×103 Pa s, at least about 30×103 Pa s, at least about 40×103 Pa s, at least about 50×103 Pa s, at least about 60×103 Pa s, or at least about 65×103 Pa s. In at least one non-limiting embodiment, the mixture 108 may have a viscosity of not greater than about 100×103 Pa s, such as not greater than about 95×103 Pa s, not greater than about 90×103 Pa s, or even not greater than about 85×103 Pa s. It will be appreciated that the viscosity of the mixture 108 can be within a range between any of the minimum and maximum values noted above. The viscosity can be measured in the same manner as the storage modulus as described above.
Moreover, the mixture 108 can be formed to have a particular content of organic materials including, for example, organic additives that can be distinct from the liquid to facilitate processing and formation of shaped abrasive particles according to the embodiments herein. Some suitable organic additives can include stabilizers, binders such as fructose, sucrose, lactose, glucose, UV curable resins, and the like.
Notably, the embodiments herein may utilize a mixture 108 that can be distinct from slurries used in conventional forming operations. For example, the content of organic materials within the mixture 108 and, in particular, any of the organic additives noted above, may be a minor amount as compared to other components within the mixture 108. In at least one embodiment, the mixture 108 can be formed to have not greater than about 30 wt % organic material for the total weight of the mixture 108. In other instances, the amount of organic materials may be less, such as not greater than about 15 wt %, not greater than about 10 wt %, or even not greater than about 5 wt %. Still, in at least one non-limiting embodiment, the amount of organic materials within the mixture 108 can be at least about 0.01 wt %, such as at least about 0.5 wt % for the total weight of the mixture 108. It will be appreciated that the amount of organic materials in the mixture 108 can be within a range between any of the minimum and maximum values noted above.
Moreover, the mixture 108 can be formed to have a particular content of acid or base, distinct from the liquid content, to facilitate processing and formation of shaped abrasive particles according to the embodiments herein. Some suitable acids or bases can include nitric acid, sulfuric acid, citric acid, chloric acid, tartaric acid, phosphoric acid, ammonium nitrate, and ammonium citrate. According to one particular embodiment in which a nitric acid additive is used, the mixture 108 can have a pH of less than about 5, and more particularly, can have a pH within a range between about 2 and about 4.
As shown in
During extrusion within the application zone 112, the tool 110 can be in direct contact with a portion of the die 102 to facilitate extrusion of the mixture 108 into the one or more tool cavities 114. The tool 110 can be in the form of a screen, such as illustrated in
The tool 110 may be formed of a metal material, including for example, a metal alloy, such as stainless steel. In other instances, the tool 110 may be formed of an organic material, such as a polymer.
In accordance with an embodiment, a particular pressure may be utilized during extrusion. For example, the pressure can be at least about 10 kPa, such as at least about 500 kPa. Still, in at least one non-limiting embodiment, the pressure utilized during extrusion can be not greater than about 4 MPa. It will be appreciated that the pressure used to extrude the mixture 108 can be within a range between any of the minimum and maximum values noted above. In particular instances, the consistency of the pressure delivered by a piston 199 may facilitate improved processing and formation of shaped abrasive particles. Notably, controlled delivery of consistent pressure across the mixture 108 and across the width of the die 102 can facilitate improved processing control and improved dimensional characteristics of the shaped abrasive particles.
Prior to depositing the mixture 108 in the tool one or more tool cavities 114, a mold release agent can be applied to the surfaces of the tool one or more tool cavities 114, which may facilitate removal of precursor shaped abrasive particles 126 from the tool one or more tool cavities 114 after further processing. Such a process can be optional and may not necessarily be used to conduct the molding process. A suitable exemplary mold release agent can include an organic material, such as one or more polymers (e.g., PTFE). In other instances, an oil (synthetic or organic) may be applied as a mold release agent to the surfaces of the tool one or more tool cavities 114. One suitable oil may be peanut oil. The mold release agent may be applied using any suitable manner, including but not limited to, depositing, spraying, printing, brushing, coating, and the like.
The mixture 108 may be deposited within the tool one or more tool cavities 114, which may be shaped in any suitable manner to form shaped abrasive particles having shapes corresponding to the shape of the tool one or more tool cavities 114.
Referring briefly to
As illustrated in
In such a case, a method for forming shaped abrasive particles may include placing a mixture 206, 306, 406 comprising a ceramic precursor material into a production tool having a plurality of openings, e.g., one of the tools 200, 300, 400 described herein having the respective tool cavities 202, 302, 402. Placing the mixture 206, 306, 406 comprises partially filling a majority of the cavities of the plurality of cavities. In certain instances, each of the plurality of tool cavities 202, 302, 402 formed in the production tools 200, 300, 400 can have the same two-dimensional shape or different two-dimensional shapes.
In another aspect, partially filling includes placing the mixture 206, 306, 406 into only a portion of the openings such that the openings comprise some mixture 206, 306, 406 and some void volume that is free of the mixture. Partially filling a majority of the openings can include controlling at least one variable from the group consisting of: orientation of the plurality of openings relative to a direction of translation of the production tool, speed of translation of the production tool, viscosity of the mixture, pressure applied to the mixture during placing of the mixture into the plurality of openings, material of the production tool, surface energy between the surface of the plurality of the openings and the mixture, and any combination thereof.
Each tool 200, 300, 400 as illustrated may include a plurality of tool cavities 202, 302, 402 oriented in a particular manner relative to each other. For example, each of the plurality of tool cavities 202, 302, 402 in each respective tool 200, 300, 400 can have substantially the same orientation relative to each other, and substantially the same orientation relative to the surface of the screen. However, it will be appreciated, that in other instances, the one or more tool cavities 202, 302, 402 within each tool 200, 300, 400 need not necessarily have the same orientation relative to each other.
Referring again to
In the molding process, the mixture 108 may undergo significant drying while contained in the tool cavity 114. Therefore, shaping may be primarily attributed to substantial drying and solidification of the mixture 108 in the tool one or more tool cavities 114 to shape the mixture 108.
After applying the mold release agent, the mixture 108 can be deposited within the mold cavities and dried. Drying may include removal of a particular content of certain materials from the mixture 108, including volatiles, such as water or organic materials. In accordance with an embodiment, the drying process can be conducted at a drying temperature of not greater than about 300° C., such as not greater than about 250° C., not greater than about 200° C., not greater than about 150° C., not greater than about 100° C., not greater than about 80° C., not greater than about 60° C., not greater than about 40° C., or even not greater than about 30° C. Still, in one non-limiting embodiment, the drying process may be conducted at a drying temperature of at least about −20° C., such as at least about −10° C. at least about 0° C. at least about 5° C. at least about 10° C., or even at least about 20° C. It will be appreciated that the drying temperature may be within a range between any of the minimum and maximum temperatures noted above.
In certain instances, drying may be conducted for a particular duration to facilitate the formation of shaped abrasive particles according to embodiments herein. For example, drying can be conducted for a duration of at least about 20 second, such as at least about 1 minute, at least about 2 minutes, at least about 4 minutes, at least about 6 minutes, at least about 8 minutes, at least about 10 minutes, at least about 30 minutes, at least about 1 hour, at least about 2 hours, at least about 4 hours, at least about 8 hours, at least about 12 hours, at least about 15 hours, at least about 18 hours, at least about 24 hours. In still other instances, the process of drying may be not greater than about 30 hours, such as not greater than about 24 hours, not greater than about 20 hours, not greater than about 15 hours, not greater than about 12 hours, not greater than about 10 hours, not greater than about 8 hours, not greater than about 6 hours, not greater than about 4 hours. It will be appreciated that the duration of drying can be within a range between any of the minimum and maximum values noted above.
Additionally, drying may be conducted at a particular relative humidity to facilitate formation of shaped abrasive particles according to the embodiments herein. For example, drying may be conducted at a relative humidity of at least about 20%, at least about 30%, at least about 40%, at least about 50%, at least about 60%, such as at least about 62%, at least about 64%, at least about 66%, at least about 68%, at least about 70%, at least about 72%, at least about 74%, at least about 76%, at least about 78%, or even at least about 80%. In still other non-limiting embodiments, drying may be conducted at a relative humidity of not greater than about 90%, such as not greater than about 88%, not greater than about 86%, not greater than about 84%, not greater than about 82%, not greater than about 80%, not greater than about 78%, not greater than about 76%, not greater than about 74%, not greater than about 72%, not greater than about 70%, not greater than about 65%, not greater than about 60%, not greater than about 55%, not greater than about 50%, not greater than about 45%, not greater than about 40%, not greater than about 35%, not greater than about 30%, or even not greater than about 25%. It will be appreciated that the relative humidity utilized during drying can be within a range between any of the minimum and maximum percentages noted above.
After completing the drying process, the mixture 108 can be released from the tool one or more tool cavities 114 to produce precursor shaped abrasive particles 126. Notably, before the mixture 108 is removed from the tool one or more tool cavities 114 or after the mixture 108 is removed and the precursor shaped abrasive particles 126 are formed, one or more post-forming processes may be completed. Such processes can include surface shaping, curing, reacting, radiating, planarizing, calcining, sintering, sieving, doping, and a combination thereof. For example, in one optional process, the mixture 108 or precursor shaped abrasive particles 126 may be translated through an optional shaping zone, wherein at least one exterior surface of the mixture or precursor shaped abrasive particles 126 may be shaped.
In still another embodiment, the mixture 108 as contained in the mold cavities or the precursor shaped abrasive particles 126 may be translated through an optional application zone, wherein a dopant material can be applied. In particular instances, the process of applying a dopant material can include selective placement of the dopant material on at least one exterior surface of the mixture 108 or precursor shaped abrasive particles. In an optional process, the mixture 108 may be treated with one or more acid or base materials. Treatment may occur post-calcination and may affect a distribution of dopant material within the shaped abrasive particle. In a particular instance, treatment with one or more acid or base materials may facilitate increased performance of the shaped abrasive particle. The process of applying a dopant can include doping (i.e., additives or a provision of additives to the gel prior to calcination). In alternative instances, an impregnation process may be used instead of doping, where impregnation utilizes an additive introduced to the precursor particles after calcination. Utilization of doping or impregnation may affect distribution of the dopant material within the final shaped abrasive particle which may also facilitate increased performance of the shaped abrasive particle.
The dopant material may be applied utilizing various methods including for example, spraying, dipping, depositing, impregnating, transferring, punching, cutting, pressing, crushing, and any combination thereof. In accordance with an embodiment, applying a dopant material can include the application of a particular material, such as a precursor. In certain instances, the precursor can be a salt, such as a metal salt, that includes a dopant material to be incorporated into the finally-formed shaped abrasive particles. For example, the metal salt can include an element or compound that is the precursor to the dopant material. It will be appreciated that the salt material may be in liquid form, such as in a dispersion comprising the salt and liquid carrier. The salt may include nitrogen, and more particularly, can include a nitrate. In other embodiments, the salt can be a chloride, sulfate, phosphate, and a combination thereof. In one embodiment, the salt can include a metal nitrate, and more particularly, consist essentially of a metal nitrate. In one embodiment, the dopant material can include an element or compound such as an alkali element, alkaline earth element, rare earth element, hafnium, zirconium, niobium, tantalum, molybdenum, vanadium, or a combination thereof. In one particular embodiment, the dopant material includes an element or compound including an element such as lithium, sodium, potassium, magnesium, calcium, strontium, barium, scandium, yttrium, lanthanum, cesium, praseodymium, niobium, hafnium, zirconium, tantalum, molybdenum, vanadium, chromium, cobalt, iron, germanium, manganese, nickel, titanium, zinc, and a combination thereof.
The forming process may further include a sintering process. For certain embodiments herein, sintering can be conducted after removing the mixture from the tool one or more tool cavities 114 and forming the precursor shaped abrasive particles 126. Sintering of the precursor shaped abrasive particles 126 may be utilized to densify the particles 126, which are generally in a green state. In a particular instance, the sintering process can facilitate the formation of a high-temperature phase of the ceramic material. For example, in one embodiment, the precursor shaped abrasive particles may be sintered such that a high-temperature phase of alumina, such as alpha alumina, is formed. In one instance, a shaped abrasive particle can comprise at least about 90 wt % alpha alumina for the total weight of the particle. In other instances, the content of alpha alumina may be greater such that the shaped abrasive particle may consist essentially of alpha alumina.
The body of the finally-formed shaped abrasive particles can have particular two-dimensional shapes. For example, the body can have a two-dimensional shape, as viewed in a plane defined by the length and width of the body, and can have a shape including a polygonal shape, ellipsoidal shape, a numeral, a Greek alphabet character, a Latin alphabet character, a Russian alphabet character, a complex shape utilizing a combination of polygonal shapes and a combination thereof. Particular polygonal shapes include rectangular, trapezoidal, pentagonal, hexagonal, heptagonal, octagonal, nonagonal, decagonal, and any combination thereof. In another instance, the finally-formed shaped abrasive particles can have a body having a two-dimensional shape such as an irregular quadrilateral, an irregular rectangle, an irregular trapezoid, an irregular pentagon, an irregular hexagon, an irregular heptagon, an irregular octagon, an irregular nonagon, an irregular decagon, and a combination thereof. An irregular polygonal shape is one where at least one of the sides defining the polygonal shape is different in dimension (e.g., length) with respect to another side. As illustrated in other embodiments herein, the two-dimensional shape of certain shaped abrasive particles can have a particular number of exterior points or external corners. For example, the body of the shaped abrasive particles can have a two-dimensional polygonal shape as viewed in a plane defined by a length and width, wherein the body comprises a two-dimensional shape having at least 4 exterior points (e.g., a quadrilateral), at least 5 exterior points (e.g., a pentagon), at least 6 exterior points (e.g., a hexagon), at least 7 exterior points (e.g., a heptagon), at least 8 exterior points (e.g., an octagon), at least 9 exterior points (e.g., a nonagon), and the like.
Referring now to
The resulting pressure of the force 506 may extrude the mixture 508 through the shaped die opening 510 and onto a conveyor belt 512. The conveyor belt 512 may be supported by, and rotate on, a first roller 514 and a second roller 516. In a particular embodiment, the mixture 508 can be same as the mixture 108, described above. Further, the mixture 508 can be extruded from the die 502 and a resulting extrudate 520 can undergo one or more post-forming processes, described above, to become a shaped abrasive particle having the shape of the shaped die opening 510.
In another aspect, the system 500 can further include a post-extrusion shaping device 522. The post-extrusion shaping device 522 may be a stamping device, a molding device, a pressing device, or some other device that may be used to alter, or otherwise modify, the shape of the extrudate 520 into another shape. For example, the post-extrusion shaping device 522 may include a piston driven stamp 524. The extrudate 520 may be moved into position under the post-extrusion shaping device 522 and the piston driven stamp 524 may be lowered onto the extrudate 520 in order to press the extrudate 520 into a stamped extrudate 526 having a different shape than that of the extrudate 520 after it is extruded onto the conveyor belt 512 from the die 502. Thereafter, the stamped extrudate 526 may undergo one or more of the post-forming processes described above to become a shaped abrasive particle having a shape corresponding to the interior shape of the piston driven stamp 524. It can be appreciated that the extrudate 520 or the stamped extrudate 526 can be shaped like one or more of the shaped abrasive particles described in detail herein. The stamp may be used to form all or a portion of the features of a shaped abrasive particle. For example, in certain instances, the stamp may be used to form a shaped abrasive particle having a particular shape from the extrudate. In still other instances, the stamp may be used to form only a portion of the extrudate, such as a surface of the extrudate, such that the stamp is configured to impart one or more surface features to the extrudate. In further instances, the extrudate 520 can be in the form of a ribbon, and the post-extrusion shaping device 522 and/or the piston driven stamp 524 can be used to stamp a shape (e.g., a shaped abrasive particle having a shape corresponding to the interior shape of the piston driven stamp 524) out of the ribbon.
The stamp can be used with other processes, such as a molding process or a screen printing process to alter a portion (e.g. a surface) of the precursor shaped abrasive particles made by printing or molding.
The resulting pressure of the force 606 may extrude the mixture 608 through the die opening 610 and onto a conveyor belt 612. The conveyor belt 612 may be supported by, and rotate on, a first roller 614, a second roller 616, and a third roller 618. The third roller 618 may be placed directly under the die 602 so that when the mixture 608 is extruded from the die 602, the extrusion force will not move the conveyor belt 612 away from the die 602. In a particular embodiment, the mixture 608 can be same as the mixture 108, described above.
As illustrated in the enlarged portion of
The system 600 illustrated in
Referring to
As shown in
During extrusion within the application zone 712, the tool 710 can be in direct contact with a portion of the die 702 to facilitate extrusion of the mixture 708 into the one or more tool cavities 714. However, a portion of the tool cavity 714 may be positioned outside of the application zone 712 to allow a portion of the mixture 708 to be extruded through and out of the tool cavity 714. The portion of the mixture 708 that is allowed to overflow the tool cavity 714 may form a lip or other structure on a shaped abrasive particle, as described in detail herein, when the tool 710, e.g., the screen, is peeled away from the backing plate 716 as illustrated in
After the mixture 708 is extruded through the die opening 718, the mixture 708 and tool 710 may be translated under a knife edge 724 attached to, or otherwise formed on, a surface of the die 702. The knife edge 724 may define a region at the front of the die 702 that facilitates displacement of the mixture 708 into the tool one or more tool cavities 714 of the tool 710. It can be appreciated that after the material 708 is extruded into and through the tool cavity 714, the material may undergo one or more of the post-forming processes, described above, to become a shaped abrasive particle having the shape of the tool cavity 714 and the overflow portion.
Referring now to
c illustrate various shaped abrasive particles formed with a plurality of voids. The voids can be discrete micro-voids that can be distributed throughout a body, such as uniformly distributed throughout the volume of the body. The discrete micro-voids can include a liquid or gas material. Further, the discrete micro-voids can be non-uniformly distributed through a particular body. As such, a particular body can include a greater content of discrete micro-voids in a central region of the body compare to a content of discrete micro-voids at a surface region of the body.
In another aspect, the discrete micro-voids can be uniformly distributed throughout the body, or sheet. Moreover, the discrete micro-voids can be non-homogenously distributed so that there are more voids in thicker parts of a body and less near edges of the body. The voids can be created by coating precursor abrasive particles with a second layer or double extruding two different types of mixtures. The micro-voids may also be formed by a subtractive process, including the use of one or more pore formers.
Shaped Abrasive Particles
Referring to
As illustrated, the shaped abrasive particle 1300 includes a body 1302 that includes a first surface 1304 and a second surface 1306 opposite the first surface 1304. As depicted, a side surface 1308 can extend between the first surface 1304 and the second surface 1306.
In a particular aspect, the teeth 1310 can extend along a length of the body 1302. Further, the teeth 1310 can extend along the entire length of the body 1302. As indicated in
As indicated in
As indicated, the shaped abrasive particle 1400 includes a body 1402 having a first surface 1404 and a second surface 1406 distanced from the first surface 1404. A side surface 1408 can extend between the first surface 1404 and the second surface 1406.
As depicted in
As illustrated, the shaped abrasive particle 1500 can include a body 1502 having a partial-ellipsoid shape. The body 1502 can include a first major surface 1504 and a second major surface 1506 jointed by a third surface 1508 that can extend between at least a portion of the first major surface 1504 and the second major surface 1506. The third surface 1508 can be generally arch shaped. The body 1502 can include a fourth surface 1510 that can extend between at least a portion of the first major surface 1504, the second major surface 1506, and the third surface 1508. The fourth surface 1510 can act as a base and as indicated in
As depicted in
In a particular aspect, the first major surface 1504 can include a convex shape. In another aspect, the first major surface 1504 can include a concave shape, as illustrated in
In a particular aspect, the first major surface 1504 and the second major surface 1506 may both include a convex shape. In another aspect, the first major surface 1504 and the second major surface 1506 may both include a concave shape. In another aspect, the first major surface 1504 may be include a convex shape while the second major surface 1506 includes a concave shape (or vice versa). In still another aspect, the first major surface 1504 can include a planar shape and the second major surface 1506 may both include a convex shape or a concave shape. Or, the second major surface 1506 may include a planar shape and the first major surface 1504 can include a convex shape or a concave shape. In a particular aspect, the shaped abrasive particle 1500 can be formed using one or more of the systems and methods, described herein.
As shown, the shaped abrasive particle 1600 can have a body 1602 that is generally frustoconical in shape. The body 1602 can include a first surface 1604 and a second surface 1606 that is substantially parallel to the first surface 1604. An angled side surface 1608 can extend between the first surface 1604 and the second surface 1606. The side surface 1608 can include a plurality of protrusions 1610 that can extend between the first surface 1604 and the second surface 1606 along a spiral pathway. As indicated in
As shown, the shaped abrasive particle 1700 can have a body 1702 that is generally conical in shape. The body 1702 can include a vertex 1704 and a surface 1706 that is spaced a distance from the vertex 1704. An angled side surface 1708 can extend between the vertex 1704 and the surface 1706. The side surface 1708 can include a plurality of protrusions 1710 that can extend between the vertex 1704 and the surface 1706 along a spiral pathway. As indicated in
As illustrated, the shaped abrasive particle 1800 includes a body 1802 attached to a base 1804. The body 1802 is generally fin-shaped and includes a length 1806, a width 1808, and a thickness 1808.
In a particular aspect, the body 1802 includes a rectangular cross-sectional shape in a plane defined by the length 1806 and the width 1808. Further, the body 1802 has a generally elliptical cross-sectional shape in a plane defined by the width 1808 and thickness 1810. In a particular aspect, an aspect ratio of the width 1808 to the thickness 1810 (w:t) is at least 2:1, such as at least 3:1, at least 4:1, at least 5:1, or at least 6:1. Further, in a particular aspect, w:t is no greater than 20:1, such as no greater than 15:1, no greater than 12:1, or no greater than 10:1.
In a particular aspect, the base 1804 of the shaped abrasive particle 1800 includes a diameter 1812 and a ratio of the diameter 1812 of the base 1804 to the width 1808 of the body 1802 (d:w) is at least 1:1, such as at least 2:1, at least 3:1, or at least 4:1. In another aspect, d:w is no greater than 10:1, no greater than 8:1, or no greater than 5:1.
As depicted, the body 1802 shaped abrasive particle 1800 includes a first surface 1814 and a second surface 1816 distanced therefrom. A side surface 1818 extends between the first surface 1814 and the second surface 1816. The side surface 1818 includes two side surface portions 1820 having a planar shape and two side surface portions 1822 having a convex shape. The two side portions 1822 having the convex shape are separated from each other by the two side portions 1820 having the planar shape. In a particular aspect, the shaped abrasive particle 1800 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 1900 is generally rake-shaped and includes a body 1902 having a central region 1904. A first group of castellated projections 1906 can extend from the central region 1904 of the body 1902 in a first direction. A second group of castellated projections 1908 can extend from the central region 1904 of the body 1902 in a second direction. In a particular aspect, the first group of castellated projections 1906 can have a length, LP1, and the second group of castellated projections 1908 can have a length, LP2. A ratio of LP1 to LP2 (LP1:LP2) can be at least 1:1, such as at least 1.5:1, or 2:1. In another aspect, LP1:LP2 may be no greater than 5:1, such as no greater than 4:1, or no greater than 3:1.
It can be appreciated that when used to form a coated abrasive article, the second group of castellated projections 1908 can extend into and adhere to a make coat that is disposed on a backing material. The first group of castellated projections 1906 can provide a plurality of grinding points for material removal during an abrasive operation. In a particular aspect, the shaped abrasive particle 1900 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 2000 includes a body 2002 having a first surface 2004 and a second surface 2006. Moreover, the body 2002 includes a side surface 2008 extending between the first surface 2004 and the second surface 2006. The side surface 2008 can include at least four distinct side surface portions, e.g., a first side surface portion 2010, a second side surface portion 2012, a third side surface portion 2014, and a fourth side surface portion 216. As shown, the side surface portions 2010, 2012, 2014, 2016 may be separated by at least four exterior corners 2020, 2022, 2024, 2026.
As indicated in
As indicated, the shaped abrasive particle 2100 can include a body 2102 that is generally toothed and includes a plurality of teeth 2104 extending from one side of the body 2102. As shown, the teeth 2014 may define external corners of the body 2102 and can include an average spacing 2106 between adjacent teeth 2104 of less than 0.5L, where L defines the length 2108 of the body. In another aspect, each of the teeth 2104 can include a tooth height and at least some of the teeth 2104 have a different height when compared to other teeth 2104 of the plurality of teeth 2104. In yet another aspect, each of the teeth 2104 can have the same height. Further, in another aspect, the body 2102 can include a peripheral surface and all of the teeth 2104 can be uniformly distributed around the peripheral surface. In another aspect, the teeth may be non-uniformly distributed around the peripheral surface of the body 2102. In another aspect, each of the teeth of the plurality of teeth 2104 defines a single point on the body 2102. In another aspect, each of the teeth of the plurality of teeth 2104 defines multiple points on the body 2102. In a particular aspect, the shaped abrasive particle 2100 can be formed using one or more of the systems and methods, described herein.
As indicated, the shaped abrasive particle 2200 can include a body 2202 having a first surface 2204 and a base 2206 spaced a distance from the first surface 2204. A plurality of structures 2208 can extend between the base 2206 and the first surface 2204 in an outward direction from a center 2210 of the body 2202. Each of the plurality of structures 2208 can include an isosceles triangle and each of the plurality of structures 2208 can be attached in the central region of the body 2202. Further, the body 2202 can include a bore 2212 that can extend along a length of the body 2202 and through the center 2210 of the body 2202. In a particular aspect, the shaped abrasive particle 2200 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 2300 can include a body 2302 having a first surface 2304 and a second surface 2306. A side surface 2308 can extend between the first surface 2304 and the second surface 2306. The side surface 2308 can include a first side surface portion 2310, a second side surface portion 2312, a third side surface portion 2314, and a fourth side surface portion 2316. In particular, the first surface 2304 of the body 2302 is concave and the first side surface portion 2310 can extend to the first surface 2304 to form a flashing 2318 on the body 2302 of the shaped abrasive particle 2300. The flashing 2318 can have a flashing length, LF, and the body 2302 can include a length, L. A ratio of the length of the body 2302 to the flashing length, L:LF, can be at least 10:1 such as at least 9:1, at least 8:1, at least 7:1, or at least 6:1. Further, the L:LF may be no greater than 2:1, no greater than 3:1, or no greater than 4:1. The increase length of the flashing 2318 can extend the useful life of the shaped abrasive grain 2300 and a coated abrasive article, such as an abrasive belt, on which the shaped abrasive grain 2300 is deposited. In a particular aspect, the shaped abrasive particle 2300 can be formed using one or more of the systems and methods, described herein.
The shaped abrasive particle 2400 includes a body 2402 having a first surface 2404, a second surface 2406, and a third surface 2408 that are connected to each other to form a pyramid shape with a hollow interior 2410. In a particular aspect, the shaped abrasive particle 2400 can be formed using one or more of the systems and methods, described herein.
As indicated, the shaped abrasive particle 2500 can include a body 2502 having a plurality of structures 2504 equally spaced around a center 2506 of the body 2502. Each of the plurality of structures 2504 can include an isosceles triangle shape and each of the plurality of structures 2504 can be attached, or otherwise bonded, to adjacent structures 2504 to form an opening 2506, or hole that extends along a length of the body 2502 through the center 2510 of the body 2502. In a particular aspect, the shaped abrasive particle 2500 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 2600 can include a body 2602. The body 2602 can be generally star shaped and flat. Moreover, the body 2602 can include a first point 2604, a second point 2606, a third point 2608, and a fourth point 2610. The points 2604, 2606, 2608, 2610 can be equally spaced around a center 2612 of the body 2602. In a particular aspect, the shaped abrasive particle 2600 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 2700 can include a body 2702. The body 2702 can be generally star shaped. Moreover, the body 2702 can include a first point 2704, a second point 2706, a third point 2708, and a fourth point 2710. The points 2704, 2706, 2708, 2710 can be equally spaced around a center 2712 of the body 2702. Moreover, the body 2702 of the shaped abrasive particle 2700 can have a thickness 2720 that increases from each point 2704, 2706, 2708, 2710 to the center 2712 of the body 2702. Further, the body 2702 can include a first central point 2722 and a second central point 2724 opposite the first central point 2722. In a particular aspect, the shaped abrasive particle 2700 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 2800 can include a body 2802 having a first triangular portion 2804 and a second triangular portion 2806. The triangular portions 2804, 2806 can be bonded, or otherwise fused, to each other along a central axis 2808. In particular, the triangular portions 2804, 2806 can be bonded to each other so that a side surface 2810 formed after bonding the triangular portions 2804, 2806 together includes an angle 2812.
The angle 2812 of the side surface 2810 can be less than or equal to 180°, such as less than or equal to 170°, less than or equal to 160°, less than or equal to 150°, less than or equal to 140°, or less than or equal to 130°. In another aspect, the angle 2812 of the side surface can be greater than or equal to 90°, such as greater than or equal to 100°, greater than or equal to 110°, or greater than or equal to 120°.
In another aspect, the triangular portions 2804, 2806 can be shaped so that a first surface 2814 formed when the triangular portions 2804, 2806 are bonded together also includes an angle 2816. The angle 2816 of the first surface 2814 can be less than or equal to 180°, such as less than or equal to 170°, less than or equal to 160°, less than or equal to 150°, less than or equal to 140°, or less than or equal to 130°. In another aspect, the angle 2816 of the first surface 2814 can be greater than or equal to 90°, such as greater than or equal to 100°, greater than or equal to 110°, or greater than or equal to 120°. In a particular aspect, the shaped abrasive particle 2800 can be formed using one or more of the systems and methods, described herein.
In another aspect, the triangular portions 2804, 2806 of the body 2802 of the shaped abrasive particle 2800 can be considered flanges and as shown, the flanges can extend in different planes with respect to each other at one or more of the angles described.
As illustrated, the shaped abrasive particle 2900 includes a body 2902. The body 2902 is toroid shaped, or annular, and includes the cross-sectional shape depicted in
As illustrated, the shaped abrasive particle 3000 includes a body 3002. The body 3002 is toroid shaped and includes the cross-sectional shape depicted in
The angle 3012 can be greater than or equal to 45°, such as greater than or equal 50°, greater than or equal 55°, or greater than or equal 60°. Further, the angle 3012 can be less than or equal to 85°, such as less than or equal to 80°, less than or equal to 75°, less than or equal to 70°, or less than or equal to 65°. In a particular aspect, the shaped abrasive particle 3000 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 3100 includes a body 3102. The body 3102 is toroid shaped and includes the cross-sectional shape depicted in
The angle 3116 can be greater than or equal to 90°, such as greater than or equal 100°, greater than or equal 110°, or greater than or equal 120°. Further, the angle 3116 can be less than or equal to 170°, such as less than or equal to 160°, less than or equal to 150°, less than or equal to 140°, or less than or equal to 130°. In a particular aspect, the shaped abrasive particle 3100 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 3200 includes a body 3202. The body 3202 is toroid shaped and includes the cross-sectional shape depicted in
As illustrated, the shaped abrasive particle 3300 includes a body 3302. The body 3302 is toroid shaped, or annular with a central opening extending through the body 3302 and a rounded contour, and includes the cross-sectional shape depicted in
As illustrated, a first side surface 3308 can extend between the first major surface 3304 and the second major surface 3306. As depicted in
In a particular aspect, the angle 3310 can be greater than or equal to 95°, such as greater than or equal 100°, greater than or equal 105°, or greater than or equal 110°. Further, the angle 3310 can be less than or equal to 150°, such as less than or equal to 140°, less than or equal to 130°, or less than or equal to 120°. The body 3302 can also include a second side surface 3312 that can extend between the first major surface 3304 and the second major surface 3306. As shown in
As illustrated, the shaped abrasive particle 3400 can include a body 3402 having a first triangular portion 3404 and a second triangular portion 3406. The triangular portions 3404, 3406 can be bonded, or otherwise fused, to each other along a side surface 3408, 3410 of each triangular portion 3404, 3406. In particular, the triangular portions 3404, 3406 can be bonded to each other so that in the side plan view of
The angle 3414 can be less than or equal to 120°, such as less than or equal to 110°, less than or equal to 100°, or less than or equal to 90°. In another aspect, the angle 3414 of can be greater than or equal to 50°, such as greater than or equal to 60°, greater than or equal to 70°, or greater than or equal to 80°. In another aspect, the first triangular portion 3404 can include a second surface 3418 and the second triangular portion 3406 can include a second surface 3420. When the triangular portions 3404, 3406 are bonded together, as depicted, the second surface 3418 of the first triangular portion 3404 can be coplanar with the second surface 3420 of the second triangular portion 3406, e.g., to form a base for the shaped abrasive particle 3400. In a particular aspect, the shaped abrasive particle 3400 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 3500 can include a body 3502 having a first triangular portion 3504 and a second triangular portion 3506. The triangular portions 3504, 3506 can be bonded, or otherwise fused, to each other along a side surface 3508, 3510 of each triangular portion 3504, 3506. In particular, the triangular portions 3504, 3506 can be equilateral triangles and the triangular portions 3504, 3506 can be bonded to each other so that in the side plan view of
The shaped abrasive particle 3900 can include a body 3902 that can be formed by creating a layer of material from a mixture comprising a precursor ceramic material. The body 3902 can include a pattern 3904 formed in an upper surface 3906 of the body 3902. The pattern 3904 can be formed by altering the upper surface 3906 of the body 3902 by exposing it to a gaseous or liquid material in order to create the pattern 3904 in the upper surface 3906 of the body 3902, e.g., the layer of material that forms the body 3902. In a particular aspect, the shaped abrasive particle 3900 can be formed into a plurality of abrasive particles, e.g., by crushing the shaped abrasive particle 3900. In such a case, at least a portion of the abrasive particles formed from the shaped abrasive particle 3900 can include a surface having at least a portion of the pattern created in the upper surface 3906 of the layer making up the body 3902. In a particular aspect, the shaped abrasive particle 3900 can be formed using one or more of the systems and methods, described herein. In particular, the shaped abrasive particle 3900 can be formed by first forming a sheet of gel and then, agitating surface of the sheet of gel, e.g., using air driven by a fan blade or impeller, before the gel is dried in order to create waves or ripple features in the upper surface of the sheet of gel to achieve the pattern shown in the abrasive particle 3900.
The shaped abrasive particle 4000 can include a body 4002 that can be formed by creating a layer of material from a mixture comprising a precursor ceramic material. The body 4002 can include a pattern 4004 formed in an upper surface 4006 of the body 4002. The pattern 4004 can be formed by altering the upper surface 4006 of the body 4002 by exposing it to a gaseous or liquid material in order to create the pattern 4004 in the upper surface 4006 of the body 4002, e.g., the layer of material that forms the body 4002. In a particular aspect, the shaped abrasive particle 4000 can be formed into a plurality of abrasive particles, e.g., by crushing the shaped abrasive particle 4000. In such a case, at least a portion of the abrasive particles formed from the shaped abrasive particle 4000 can include a surface having at least a portion of the pattern created in the upper surface 4006 of the layer making up the body 4002. In a particular aspect, the shaped abrasive particle 4000 can be formed using one or more of the systems and methods, described herein. In particular, the shaped abrasive particle 4000 can be formed by first forming a sheet of gel and then, agitating surface of the sheet of gel, e.g., using air driven by a fan blade or impeller, before the gel is dried in order to create waves or ripple features in the upper surface of the sheet of gel to achieve the pattern shown in the abrasive particle 4000.
As depicted, the shaped abrasive particle 4100 can include a body 4102 having a first surface 4104 and a second surface 4106. A side surface 4108 can extend between the first surface 4104 and the second surface 4106. The body 4102 can also include a flange 4110 that can extend from the side surface 4108 and the first surface 4104. In a particular aspect, the flange 4110 can include a rounded shape. Further, the flange 4110 can include a flange length 4112. The flange length 4112 can be less than a length 4114 of the body 4102. In another aspect, the flange 4110 can include a height 4116 and the height 4116 of the flange 4110 is not greater than a thickness 4118 of the body 4102. In another aspect, the body 4102 can only include a single flange 4110 and the flange 4110 extends along the periphery of the body 4102 for a distance that is not greater than 50% of the total peripheral length of the body 4102. In particular, the flange can extend around at least one exterior corner of the body 4102 and not greater than three exterior corners.
The body 4102 can include a narrow end 4120 and wide end 4122. The flange 4110 can extend from the narrow end 4120 of the body 4102. In a particular aspect, the shaped abrasive particle 4100 can be formed using one or more of the systems and methods, described herein.
As depicted, the shaped abrasive particle 4200 can include a body 4202 having a first surface 4204 and a second surface 4206. A side surface 4208 can extend between the first surface 4204 and the second surface 4206. The body 4202 can also include a flange 4210 that can extend from the side surface 4208 and the first surface 4204. In a particular aspect, the flange 4210 can include a rounded shape. Further, the flange 4210 can include a flange length 4212. The flange length 4212 can be less than a length 4214 of the body 4202. In another aspect, the flange 4210 can include a height 4216 and the height 4216 of the flange 4210 is not greater than a thickness 4218 of the body 4202. In another aspect, the body 4202 can only include a single flange 4210 and the flange 4210 extends along the periphery of the body 4202 for a distance that is not greater than 50% of the total peripheral length of the body 4202. In particular, the flange can extend around at least one exterior corner of the body 4202 and not greater than three exterior corners.
The body 4202 can include a narrow end 4220 and wide end 4222. The flange 4210 can extend from the wide end 4220 of the body 4202. In a particular aspect, the shaped abrasive particle 4200 can be formed using one or more of the systems and methods, described herein.
As indicated, the shaped abrasive particle 4300 can include a body 4302 having a peripheral surface 4304. A plurality of teeth 4306 can extend from the peripheral surface 4304 of the body 4302. As shown, the plurality of teeth 4306 do not extend to the corners 4308, 4310, 4312, 4314 of the body 4308. Further, each of the teeth 4304 can have the same height and all of the teeth 4304 can be uniformly distributed around the peripheral surface 4304 of the body. In a particular aspect, the shaped abrasive particle 4300 can be formed using one or more of the systems and methods, described herein.
As indicated, the shaped abrasive particle 4400 can include a body 4402 having a peripheral surface 4404. A plurality of teeth 4406 can extend from the peripheral surface 4404 of the body 4402. As shown, the plurality of teeth 4406 extend to, and form, the corners 4408, 4410, 4412, 4414 of the body 4408. Further, each of the teeth 4404 can have the same height and all of the teeth 4404 can be uniformly distributed around the peripheral surface 4404 of the body. In a particular aspect, the shaped abrasive particle 4400 can be formed using one or more of the systems and methods, described herein.
As indicated, the shaped abrasive particle 4500 can include a body 4502 having a peripheral surface 4504. A plurality of teeth 4506 can extend from the peripheral surface 4504 of the body 4502. As shown, the plurality of teeth 4506 extend to, and form, the corners 4508, 4510, 4512, 4514 of the body 4508. Further, each of the teeth 4504 can have different heights when compared to other teeth and the teeth 4504 of varying sizes can be uniformly distributed around the peripheral surface 4504 of the body. In a particular aspect, the shaped abrasive particle 4500 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 4600 can include a body 4602. The body 4602 can be generally star shaped. Moreover, the body 4602 can include a first point 4604, a second point 4606, a third point 4608, and a fourth point 4610. The points 4604, 4606, 4608, 4610 can be equally spaced around a central portion 4612 of the body 4602. Moreover, the body 4602 of the shaped abrasive particle 4600 can have a thickness 4620 that can increase from the central portion 4612 of the body 4602 outwardly toward each point 4604, 4606, 4608, 4610. In a particular aspect, the shaped abrasive particle 4600 can be formed using one or more of the systems and methods, described herein.
As illustrated, the shaped abrasive particle 4700 can include a body 4702 that can be generally shaped like an arrowhead, or a shark's tooth. The body 4702 can include a first major surface 4704 and a second major surface 4706. A side surface 4708 can extend between the first major surface 4704 and the second major surface 4706. The side surface 4708 can include a first portion 4710, a second portion 4712, and a third portion 4714. The first portion 4710 can form an angle 4714 with respect to the second portion 4712. The angle 4714 can be less than or equal to 75°, such as less than or equal to 60°, less than or equal to 50°, less than or equal to 40°, or less than or equal to 35°. In another aspect, the angle 4714 can be greater than or equal to 15°, such as greater than or equal to 20°, greater than or equal to 25°, or greater than or equal to 30°.
As illustrated, the shaped abrasive particle 4800 can include a body 4802 that can be generally shaped like an arrowhead, or a shark's tooth. The body 4802 can include a first major surface 4804 and a second major surface 4806. A side surface 4808 can extend between the first major surface 4804 and the second major surface 4806. The side surface 4808 can include a first portion 4810, a second portion 4812, and a third portion 4814. The first portion 4810 can form an angle 4814 with respect to the second portion 4812. The angle 4814 can be less than or equal to 75°, such as less than or equal to 60°, less than or equal to 50°, less than or equal to 40°, or less than or equal to 35°. In another aspect, the angle 4814 can be greater than or equal to 15°, such as greater than or equal to 20°, greater than or equal to 25°, or greater than or equal to 30°.
The shaped abrasive particles described herein can be formed such that each respective body can include a crystalline material, and more particularly, a polycrystalline material. Notably, the polycrystalline material can include abrasive grains. In one embodiment, the body can be essentially free of an organic material, including for example, a binder. More particularly, the body can consist essentially of a polycrystalline material.
In one aspect, the body of each shaped abrasive particle can be an agglomerate including a plurality of abrasive particles, grit, and/or grains bonded to each other to form the body of the abrasive particle. Suitable abrasive grains can include nitrides, oxides, carbides, borides, oxynitrides, oxyborides, diamond, and a combination thereof. In particular instances, the abrasive grains can include an oxide compound or complex, such as aluminum oxide, zirconium oxide, titanium oxide, yttrium oxide, chromium oxide, strontium oxide, silicon oxide, and a combination thereof. In one particular instance, each shaped abrasive particle can be formed such that the abrasive grains forming the body thereof can include alumina, and more particularly, may consist essentially of alumina. Moreover, in particular instances, the shaped abrasive particle can be formed from a seeded sol-gel.
The abrasive grains (i.e., crystallites) contained within the body may have an average grain size that is generally not greater than about 100 microns. In other embodiments, the average grain size can be less, such as not greater than about 80 microns, not greater than about 50 microns, not greater than about 30 microns, not greater than about 20 microns, not greater than about 10 microns, or even not greater than about 1 micron, not greater than about 0.9 microns, not greater than about 0.8 microns, not greater than about 0.7 microns, or even not greater than about 0.6 microns. Still, the average grain size of the abrasive grains contained within each body can be at least about 0.01 microns, such as at least about 0.05 microns, at least about 0.06 microns, at least about 0.07 microns, at least about 0.08 microns, at least about 0.09 microns, at least about 0.1 microns, at least about 0.12 microns, at least about 0.15 microns, at least about 0.17 microns, at least about 0.2 microns, or even at least about 0.5 microns. It will be appreciated that the abrasive grains can have an average grain size within a range between any of the minimum and maximum values noted above.
In accordance with certain embodiments, one or more of the abrasive particles described herein can be a composite article including at least two different types of grains within the respective body. It will be appreciated that different types of grains are grains having different compositions with regard to each other. For example, the body can be formed such that is includes at least two different types of grains, wherein the two different types of grains can be nitrides, oxides, carbides, borides, oxynitrides, oxyborides, diamond, and a combination thereof.
In accordance with an embodiment, the shaped abrasive particles described herein can have an average particle size, as measured by the largest dimension measurable on the body thereof, of at least about 100 microns. In fact, the shaped abrasive particles can have an average particle size of at least about 150 microns, such as at least about 200 microns, at least about 300 microns, at least about 400 microns, at least about 500 microns, at least about 600 microns, at least about 700 microns, at least about 800 microns, or even at least about 900 microns. Still, the shaped abrasive particles can have an average particle size that is not greater than about 5 mm, such as not greater than about 3 mm, not greater than about 2 mm, or even not greater than about 1.5 mm. It will be appreciated that the abrasive particle 300 can have an average particle size within a range between any of the minimum and maximum values noted above.
The shaped abrasive particles of the embodiments herein, e.g., the bodies thereof, can have particular compositions. For example, the bodies may include a ceramic material, such as a polycrystalline ceramic material, and more particularly an oxide. The oxide may include, for example alumina. In certain instances, the bodies may include a majority content of alumina, such as at least about 95 wt % alumina for the total weight of the body, or such as at least about 95.1 wt %, at least about 95.2 wt %, at least about 95.3 wt %, at least about 95.4 wt %, at least about 95.5 wt %, at least about 95.6 wt %, at least about 95.7 wt %, at least about 95.8 wt %, at least about 95.9 wt %, at least about 96 wt %, at least about 96.1 wt %, at least about 96.2 wt %, at least about 96.3 wt %, at least about 96.4 wt %, at least about 96.5 wt %, at least about 96.6 wt %, at least about 96.7 wt %, at least about 96.8 wt %, at least about 96.9 wt %, at least about 97 wt %, at least about 97.1 wt %, at least about 97.2 wt %, at least about 975.3 wt %, at least about 97.4 wt %, or even at least about 97.5 wt % alumina for the total weight of the body. Still, in another non-limiting embodiment, the bodies may include a content of alumina not greater than about 99.5 wt %, such as not greater than about 99.4 wt %, not greater than about 99.3 wt %, not greater than about 99.2 wt %, not greater than about 99.1 wt %, not greater than about 99 wt %, not greater than about 98.9 wt %, not greater than about 98.8 wt %, not greater than about 98.7 wt %, not greater than about 98.6 wt %, not greater than about 98.5 wt %, not greater than about 98.4 wt %, not greater than about 98.3 wt %, not greater than about 98.2 wt %, not greater than about 98.1 wt %, not greater than about 98 wt %, not greater than about 97.9 wt %, not greater than about 97.8 wt %, not greater than about 97.7 wt %, not greater than about 97.6 wt %, or even not greater than about 97.5 wt % alumina for the total weight of the body 1201. It will be appreciated that the bodies may include a content of alumina within a range between any of the minimum and maximum values noted above.
The bodies of the shaped abrasive particles may be formed to include certain additives. The additives can be non-organic species, including but not limited to an oxide. In one particular instance, the additive may be a dopant material, which may be present in a particular minor amount sufficient to affect the microstructure of the material, but present in a greater content than a trace amount or less. The dopant material may include an element selected from the group of hafnium, zirconium, niobium, tantalum, molybdenum, vanadium, lithium, sodium, potassium, magnesium, calcium, strontium, barium, scandium, yttrium, lanthanum, cesium, praseodymium, chromium, cobalt, iron, germanium, manganese, nickel, titanium, zinc, and a combination thereof. In still a more particular embodiment, the dopant material may include magnesium, and may be a magnesium-containing species, including but not limited to, magnesium oxide (MgO).
According to one embodiment, the magnesium-containing species can be a compound including magnesium and at least one other element. In at least one embodiment, the magnesium-containing compound can include an oxide compound, such that the magnesium-containing species includes magnesium and oxygen. In yet another embodiment, the magnesium-containing species can include aluminum, and more particularly may be a magnesium aluminate species. For example, in certain instances, the magnesium-containing species can be a spinel material. The spinel material may be stoichiometric or non-stoichiometric spinel.
The magnesium-containing species may be a distinct phase of material formed in the body as compared to another primary phase, including for example, an alumina phase. The magnesium-containing species may be preferentially disposed at the grain boundaries of the primary phase (e.g., alumina grains). In still other instances, the magnesium-containing species may be primarily and uniformly dispersed throughout the volume of the grains of the primary phase.
The magnesium-containing species may be a strength-altering material. For example, in at least one embodiment, the addition of the magnesium-containing species can be configured to reduce the strength of the body compared to a body that does not include the magnesium-containing species.
Certain compositions of the shaped abrasive particles of the embodiments can include a particular content of magnesium oxide. For example, the bodies of any of the shaped abrasive particles may include a content of a magnesium-containing species of at least about 0.5 wt %, such as at least about 0.6 wt %, at least about 0.7 wt %, at least about 0.8 wt %, at least about 0.9 wt %, at least about 1 wt %, at least about 1.1 wt %, at least about 1.2 wt %, at least about 1.3 wt %, at least about 1.4 wt %, at least about 1.5 wt %, at least about 1.6 wt %, at least about 1.7 wt %, at least about 1.8 wt %, at least about 1.9 wt %, at least about 2 wt %, at least about 2.1 wt %, at least about 2.2 wt %, at least about 2.3 wt %, at least about 2.4 wt %, or even at least about 2.5 wt % for the total weight of the body 1201. In still another non-limiting embodiment, the body 1201 may include a content of a magnesium-containing species of not greater than about 5 wt %, such as not greater than about 4.9 wt %, not greater than about 4.8 wt %, not greater than about 4.7 wt %, not greater than about 4.6 wt %, not greater than about 4.5 wt %, not greater than about 4.4 wt %, not greater than about 4.3 wt %, not greater than about 4.2 wt %, not greater than about 4.1 wt %, not greater than about 4 wt %, not greater than about 3.9 wt %, not greater than about 3.8 wt %, not greater than about 3.7 wt %, not greater than about 3.6 wt %, not greater than about 3.5 wt %, not greater than about 3.4 wt %, not greater than about 3.3 wt %, not greater than about 3.2 wt %, not greater than about 3.1 wt %, not greater than about 3 wt %, not greater than about 2.9 wt %, not greater than about 2.8 wt %, not greater than about 2.7 wt %, not greater than about 2.6 wt %, or even not greater than about 2.5 wt %. It will be appreciated that the content of a magnesium-containing species within the bodies may be within a range between any of the minimum and maximum values noted above. Furthermore, in at least one embodiment, the bodies of the shaped abrasive particles may consist essentially of alumina (Al2O3) and the magnesium-containing species.
Moreover, the bodies of the shaped abrasive particle of any of the embodiments herein may be formed of a polycrystalline material including grains, which may be made of materials such as nitrides, oxides, carbides, borides, oxynitrides, diamond, and a combination thereof. Further, the bodies can be essentially free of an organic material, essentially free of rare earth elements, and essentially free of iron. The bodies may be essentially free of nitrides, essentially free of chlorides, essentially free of nitrides, or essentially free of oxynitrides. Being essentially free is understood to mean that the body is formed in a manner to exclude such materials, but the body may not necessarily be completely free of such materials as they may be present in trace amounts or less.
Certain features, for clarity, described herein in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination. Further, reference to values stated in ranges includes each and every value within that range.
Benefits, other advantages, and solutions to problems have been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any feature(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential feature of any or all the claims.
The specification and illustrations of the embodiments described herein are intended to provide a general understanding of the structure of the various embodiments. The specification and illustrations are not intended to serve as an exhaustive and comprehensive description of all of the elements and features of apparatus and systems that use the structures or methods described herein. Separate embodiments may also be provided in combination in a single embodiment, and conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination. Further, reference to values stated in ranges includes each and every value within that range. Many other embodiments may be apparent to skilled artisans only after reading this specification. Other embodiments may be used and derived from the disclosure, such that a structural substitution, logical substitution, or another change may be made without departing from the scope of the disclosure. Accordingly, the disclosure is to be regarded as illustrative rather than restrictive.
The description in combination with the figures is provided to assist in understanding the teachings disclosed herein. The following discussion will focus on specific implementations and embodiments of the teachings. This focus is provided to assist in describing the teachings and should not be interpreted as a limitation on the scope or applicability of the teachings. However, other teachings can certainly be used in this application.
As used herein, the terms “comprises,” “comprising,” “includes,” “including,” “has,” “having” or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a method, article, or apparatus that comprises a list of features is not necessarily limited only to those features but may include other features not expressly listed or inherent to such method, article, or apparatus. Further, unless expressly stated to the contrary, “or” refers to an inclusive-or and not to an exclusive-or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).
Also, the use of “a” or “an” is employed to describe elements and components described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural, or vice versa, unless it is clear that it is meant otherwise. For example, when a single item is described herein, more than one item may be used in place of a single item. Similarly, where more than one item is described herein, a single item may be substituted for that more than one item.
Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. The materials, methods, and examples are illustrative only and not intended to be limiting. To the extent not described herein, many details regarding specific materials and processing acts are conventional and may be found in reference books and other sources within the structural arts and corresponding manufacturing arts.
Many different aspects and embodiments are possible. Some of those aspects and embodiments are described herein. After reading this specification, skilled artisans will appreciate that those aspects and embodiments are only illustrative and do not limit the scope of the present invention. Embodiments may be in accordance with any one or more of the embodiments as listed below.
Embodiment 1. A shaped abrasive particle comprising a body including a first surface, a second surface, a side surface extending between the first surface and second surface, and a flange portion extending from the side surface and the first major surface.
Embodiment 2. The shaped abrasive particle of embodiment 1, wherein the flange comprises a rounded shape.
Embodiment 3. The shaped abrasive particle of embodiment 1, wherein the flange comprises a length that is less than a length of the body.
Embodiment 4. The shaped abrasive particle of embodiment 1, wherein the flange has a height that is not greater than a thickness of the body.
Embodiment 5. The shaped abrasive particle of embodiment 1, wherein the body comprises a single flange and wherein the single flange extends from the body and extends for a distance of not greater than 50% of a total peripheral length of the body.
Embodiment 6. The shaped abrasive particle of embodiment 5, wherein the single flange extends around at least 1 exterior corner and not greater than 3 exterior corners.
Embodiment 7. A shaped abrasive particle having a body including a first surface, a second surface, and a side surface, wherein the body comprises a gear-shaped two-dimensional shape including a plurality of teeth extending peripherally from the side surface of the body.
Embodiment 8. The shaped abrasive particle of embodiment 7, wherein the plurality of teeth extend along a length of the body.
Embodiment 9. The shaped abrasive particle of embodiment 7, wherein the plurality of teeth extend along an entire length of the body.
Embodiment 10. The shaped abrasive particle of embodiment 7, wherein each of the teeth of the plurality of teeth comprises a two-dimensional shape.
Embodiment 11. The shaped abrasive particle of embodiment 10, wherein the two-dimensional shape is symmetric about at least a bisecting axis.
Embodiment 12. The shaped abrasive particle of embodiment 10, wherein the two-dimensional shape is asymmetric about a bisecting axis.
Embodiment 13. A shaped abrasive particle having a body including a first surface, a second surface, and a side surface extending between a first surface and the second surface, wherein the first surface comprises raised portions extending from exterior corners of the body along the first surface and joining in a center region of the first surface.
Embodiment 14. The shaped abrasive particle of embodiment 13, wherein the raised portions extend linearly from the exterior corners to the center region, and wherein the raised portions define and separate a plurality of depressed regions that abut the raised portions and at least a portion of the side surface of the body.
Embodiment 15. The shaped abrasive particle of embodiment 13, wherein the second surface comprises raised portions extending from exterior corners of the body along the first surface and joining in a center region of the first surface.
Embodiment 16. The shaped abrasive particle of embodiment 15, wherein the raised portions of the first surface and the second surface have substantially the same arrangement relative to each other.
Embodiment 17. The shaped abrasive particle of embodiment 15, wherein the raised portions extend linearly from the exterior corners to the center region, and wherein the raised portions define and separate a plurality of depressed regions that abut the raised portions and at least a portion of the side surface of the body.
Embodiment 18. A shaped abrasive particle having a body defining a partial-ellipsoid shape, the body including a first surface, a second surface, and a third surface extending between a portion of the first major surface and the second major surface, wherein at least a portion of the first surface and a portion of the second surface are connected to each other along a first edge and wherein a portion of the first surface and a portion of the third surface are connected to each other and define a second edge, and wherein a portion of the second surface and a portion of the third surface are connected to each other and define a third edge.
Embodiment 19. The shaped abrasive particle of embodiment 18, wherein the first surface comprises a concave shape.
Embodiment 20. The shaped abrasive particle of embodiment 18, wherein the first surface comprises a planar shape.
Embodiment 21. The shaped abrasive particle of embodiment 18, wherein second surface comprises a convex shape.
Embodiment 22. The shaped abrasive particle of embodiment 18, wherein the third surface comprises a concave shape.
Embodiment 23. The shaped abrasive particle of embodiment 18, wherein the third surface comprises a planar shape.
Embodiment 24. The shaped abrasive particle of embodiment 18, wherein the first edge comprises a curved or elliptical contour.
Embodiment 25. The shaped abrasive particle of embodiment 18, wherein the third edge comprises a curved or elliptical contour.
Embodiment 26. A shaped abrasive particle comprising a body having a conical or frustoconical shape, wherein a surface of the body comprises a plurality of protrusions extending in a spiral pathway.
Embodiment 27. The shaped abrasive particle of embodiment 26, wherein the body comprises a first surface, a second surface substantially parallel to the first surface and a side surface extending between the first surface and the second surface, and wherein the side surface comprises the plurality of protrusions.
Embodiment 28. A shaped abrasive particle having a body defining a fin-shape, wherein the body comprises a length, a width and a thickness and wherein the body comprises a rectangular cross-sectional shape in the plane defined by the length and width and an elliptical cross-sectional shape in the plane defined by the width and thickness, and wherein the aspect ratio of width-to-thickness (w:t) is at least 2:1.
Embodiment 29. The shaped abrasive particle of embodiment 28, wherein the body comprises a first surface, a second surface, and a side surface, wherein the side surface comprises two side surface portions comprising a convex shape and two side surface portions comprising a planar shape, and wherein the two side surface portions comprising the convex shape are separated by the side surface portions having the planar shape.
Embodiment 30. A shaped abrasive particle having a rake-shaped body including a first group of projections extending from a central region of the body in a first direction and a second group of projections extending from the central region the body in a second direction, and wherein the first group of projections have a length (Lp1) that is different compared to a length (Lp2) of the second group of projections.
Embodiment 31. A shaped abrasive particle having a body including a first surface, a second surface, and a side surface, wherein the body comprises at least four distinct side surface portions separated by at least four exterior corners, and wherein at least one side surface portion comprises a concave contour and wherein the particle comprises a curved shape, wherein the first surface comprises a substantially concave curvature and the second surface comprises a substantially convex curvature.
Embodiment 32. A shaped abrasive particle having a toothed body including a plurality of teeth extending from one side of the body, wherein the plurality of teeth define external corners of the body having an average spacing of less than 0.5(L), wherein L defines the length of the body.
Embodiment 33. The shaped abrasive particle of embodiment 32, wherein each of the teeth of the plurality of teeth comprises a height and wherein at least some of the teeth have a different height compared to other teeth of the plurality of teeth.
Embodiment 34. The shaped abrasive particle of embodiment 32, wherein each of the teeth of the plurality of teeth comprises a height and wherein all of the teeth have a same height compared to each other.
Embodiment 35. The shaped abrasive particle of embodiment 32, wherein the plurality of teeth are uniformly distributed around a peripheral surface of the body.
Embodiment 36. The shaped abrasive particle of embodiment 32, wherein the plurality of teeth are non-uniformly distributed around a peripheral surface of the body.
Embodiment 37. The shaped abrasive particle of embodiment 32, wherein each of the teeth of the plurality of teeth define a single point on the body.
Embodiment 38. The shaped abrasive particle of embodiment 32, wherein each of the teeth of the plurality of teeth define multiple points on the body.
Embodiment 39. A shaped abrasive agglomerate having a body including a plurality of shaped abrasive particle portions bonded to each other to form the body of the shaped abrasive particle.
Embodiment 40. The shaped abrasive particle of embodiment 39, wherein the body comprise a central hole extending through a thickness of the particle.
Embodiment 41. The shaped abrasive particle of embodiment 39, wherein each of the shaped abrasive particle portions of the plurality of shaped abrasive particle portions have a triangular two-dimensional shape and wherein each of the triangles are joined to each other along an edge.
Embodiment 42. A shaped abrasive particle having a body including at least a first surface, a second surface, a third surface, and a fourth surface, wherein each of the first, second, third, and fourth surfaces contact at least one of the other first, second, third, and fourth surfaces along at least one edge of the body, and wherein the first surface comprises a concave contour.
Embodiment 43. The shaped abrasive particle of embodiment 42, wherein the body is in the shape of a pyramid with a tip and a base, and wherein the first surface defines the base.
Embodiment 44. A method of making a ceramic body comprising: creating a layer of material from a mixture comprising a precursor ceramic material; altering the surface of the layer with a gaseous or liquid material to create a pattern in an upper surface of the layer; and forming the layer into abrasive particles, wherein at least a portion of the abrasive particles comprises a surface including at least a portion of the pattern created in the upper surface of the layer.
Embodiment 45. A method of forming a shaped abrasive particle comprising: placing a mixture comprising a ceramic precursor material into a production tool comprising a plurality of openings, wherein placing the mixture comprises partially filling a majority of the openings of the plurality of openings.
Embodiment 46. The method of embodiment 45, wherein partially filling comprises placing the mixture into only a portion of the openings such that the openings comprise some mixture and some void volume that is free of the mixture.
Embodiment 47. The method of embodiment 45, wherein partially filling a majority of the openings includes controlling at least one variable from the group consisting of: orientation of the plurality openings relative to a direction of translation of the production tool; speed of translation of the production tool; viscosity of the mixture; pressure applied to the mixture during placing of the mixture into the plurality openings; material of the production tool; surface energy between the surface of the plurality of the openings and the mixture; and any combination thereof.
Embodiment 48. A shaped abrasive particle having a body including plurality of a discrete micro-voids distributed throughout the body, wherein the discrete micro-voids include a liquid or gas material.
Embodiment 49. The shaped abrasive particle of embodiment 48, wherein the discrete micro-voids are non-uniformly distributed throughout the body.
Embodiment 50. The shaped abrasive particle of embodiment 48, wherein the discrete micro-voids are non-uniformly distributed throughout the body including a greater content of the discrete micro-voids in a central region of the body compared to a content of discrete micro-voids at a surface region of the body.
Embodiment 51. The shaped abrasive particle of embodiment 48, wherein the discrete micro-voids are uniformly distributed throughout the body.
Embodiment 52. A method of making shaped abrasive particles comprising translating a production tool having openings over rollers and through a deposition zone configured to deposit a mixture into the openings, wherein in the deposition zone the production tool is translated over a primary roller having a greater diameter compared to any other rollers in contact with the production tool.
Embodiment 53. A shaped abrasive particle having a multi-flanged body including a first shaped abrasive portion bonded to another shaped abrasive portion to form the body including at least two different flanges, and wherein the different flanges extend in different planes with respect to each other.
Embodiment 54. A shaped abrasive particle having an annular body comprising a first surface, second surface, a third surface extending between the first surface and second surface, wherein the annular body comprises a rounded contour, a central opening extend through the body, and wherein at least a portion of the first surface comprises a non-planar contour.
The above-disclosed subject matter is to be considered illustrative, and not restrictive, and the appended claims are intended to cover all such modifications, enhancements, and other embodiments, which fall within the true scope of the present invention. Thus, to the maximum extent allowed by law, the scope of the present invention is to be determined by the broadest permissible interpretation of the following claims and their equivalents, and shall not be restricted or limited by the foregoing detailed description.
The Abstract of the Disclosure is provided to comply with Patent Law and is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims. In addition, in the foregoing Detailed Description of the Drawings, various features may be grouped together or described in a single embodiment for the purpose of streamlining the disclosure. This disclosure is not to be interpreted as reflecting an intention that the claimed embodiments require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter may be directed to less than all features of any of the disclosed embodiments. Thus, the following claims are incorporated into the Detailed Description of the Drawings, with each claim standing on its own as defining separately claimed subject matter.
This application is a continuation of U.S. patent application Ser. No. 15/420,701, entitled “ABRASIVE ARTICLE INCLUDING SHAPED ABRASIVE PARTICLES,” by Todd M. COTTER et al., filed Jan. 31, 2017, which is assigned to the current assignee hereof and incorporated herein by reference in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 345604 | Semper | Jul 1886 | A |
| 1910444 | Nicholson | May 1933 | A |
| 2033991 | Melton et al. | Mar 1936 | A |
| 2036903 | Webster | Apr 1936 | A |
| 2049874 | Sherk | Aug 1936 | A |
| 2148400 | Crompton, Jr. | Feb 1939 | A |
| 2248064 | Carlton et al. | Jul 1941 | A |
| 2248990 | Heany | Jul 1941 | A |
| 2290877 | Heany | Jul 1942 | A |
| 2318360 | Benner et al. | May 1943 | A |
| 2376343 | Carlton | May 1945 | A |
| 2563650 | Heinemann et al. | Aug 1951 | A |
| 2880080 | Rankin et al. | Mar 1959 | A |
| 3041156 | Rowse et al. | Jun 1962 | A |
| 3067551 | Maginnis | Dec 1962 | A |
| 3079242 | Glasgow | Feb 1963 | A |
| 3079243 | Ueltz | Feb 1963 | A |
| 3123948 | Kistler et al. | Mar 1964 | A |
| 3141271 | Fischer et al. | Jul 1964 | A |
| 3276852 | Lemelson | Oct 1966 | A |
| 3377660 | Marshall et al. | Apr 1968 | A |
| 3379543 | Norwalk | Apr 1968 | A |
| 3387957 | Howard | Jun 1968 | A |
| 3454385 | Amero | Jul 1969 | A |
| 3477180 | Robertson, Jr. | Nov 1969 | A |
| 3480395 | McMullen et al. | Nov 1969 | A |
| 3481723 | Kistler et al. | Dec 1969 | A |
| 3491492 | Ueltz | Jan 1970 | A |
| 3495359 | Smith et al. | Feb 1970 | A |
| 3536005 | Derrickson | Oct 1970 | A |
| 3590799 | Guuchowicz | Jul 1971 | A |
| 3608050 | Carman et al. | Sep 1971 | A |
| 3608134 | Cook | Sep 1971 | A |
| 3615308 | Amero | Oct 1971 | A |
| 3619151 | Sheets, Jr. et al. | Nov 1971 | A |
| 3637360 | Ueltz | Jan 1972 | A |
| 3670467 | Walker | Jun 1972 | A |
| 3672934 | Larry | Jun 1972 | A |
| 3808747 | Kenagy | May 1974 | A |
| 3819785 | Argyle et al. | Jun 1974 | A |
| 3859407 | Blanding et al. | Jan 1975 | A |
| 3874856 | Leeds | Apr 1975 | A |
| 3909991 | Coes, Jr. | Oct 1975 | A |
| 3940276 | Wilson | Feb 1976 | A |
| 3950148 | Fukuda | Apr 1976 | A |
| 3960577 | Prochazka | Jun 1976 | A |
| 3977132 | Sekigawa | Aug 1976 | A |
| 3986885 | Lankard | Oct 1976 | A |
| 3991527 | Maran | Nov 1976 | A |
| 4004934 | Prochazka | Jan 1977 | A |
| 4037367 | Kruse | Jul 1977 | A |
| 4045919 | Moritomo | Sep 1977 | A |
| 4055451 | Cockbain et al. | Oct 1977 | A |
| 4073096 | Ueltz et al. | Feb 1978 | A |
| 4114322 | Greenspan | Sep 1978 | A |
| 4150078 | Miller et al. | Apr 1979 | A |
| 4194887 | Ueltz et al. | Mar 1980 | A |
| 4252544 | Takahashi | Feb 1981 | A |
| 4261706 | Blanding et al. | Apr 1981 | A |
| 4286905 | Samanta | Sep 1981 | A |
| 4304576 | Hattori et al. | Dec 1981 | A |
| 4314827 | Leitheiser et al. | Feb 1982 | A |
| 4341663 | Derleth et al. | Jul 1982 | A |
| 4393021 | Eisenberg et al. | Jul 1983 | A |
| 4452911 | Eccles et al. | Jun 1984 | A |
| 4457767 | Poon et al. | Jul 1984 | A |
| 4469758 | Scott | Sep 1984 | A |
| 4505720 | Gabor et al. | Mar 1985 | A |
| 4541842 | Rostoker | Sep 1985 | A |
| 4548617 | Miyatani et al. | Oct 1985 | A |
| 4570048 | Poole | Feb 1986 | A |
| 4618349 | Hashimoto et al. | Oct 1986 | A |
| 4623364 | Cottringer et al. | Nov 1986 | A |
| 4656330 | Poole | Apr 1987 | A |
| 4657754 | Bauer et al. | Apr 1987 | A |
| 4659341 | Ludwig et al. | Apr 1987 | A |
| 4678560 | Stole et al. | Jul 1987 | A |
| 4711750 | Scott | Dec 1987 | A |
| 4728043 | Ersdal et al. | Mar 1988 | A |
| 4744802 | Schwabel | May 1988 | A |
| 4770671 | Monroe | Sep 1988 | A |
| 4786292 | Janz et al. | Nov 1988 | A |
| 4797139 | Bauer | Jan 1989 | A |
| 4797269 | Bauer et al. | Jan 1989 | A |
| 4799939 | Bloecher et al. | Jan 1989 | A |
| 4829027 | Cutler et al. | May 1989 | A |
| 4832706 | Yates | May 1989 | A |
| 4848041 | Kruschke | Jul 1989 | A |
| 4858527 | Masanao | Aug 1989 | A |
| 4863573 | Moore et al. | Sep 1989 | A |
| 4876226 | Fuentes | Oct 1989 | A |
| 4881951 | Wood et al. | Nov 1989 | A |
| 4917852 | Poole et al. | Apr 1990 | A |
| 4918116 | Gardziella et al. | Apr 1990 | A |
| 4925457 | Dekok et al. | May 1990 | A |
| 4925815 | Tani et al. | May 1990 | A |
| 4930266 | Calhoun et al. | Jun 1990 | A |
| 4942011 | Bolt et al. | Jul 1990 | A |
| 4954462 | Wood | Sep 1990 | A |
| 4960441 | Pellow et al. | Oct 1990 | A |
| 4961757 | Rhodes et al. | Oct 1990 | A |
| 4963012 | Tracy | Oct 1990 | A |
| 4964883 | Morris et al. | Oct 1990 | A |
| 4970057 | Wilkens et al. | Nov 1990 | A |
| 4997461 | Markhoff-Matheny et al. | Mar 1991 | A |
| 5000760 | Ohtsubo et al. | Mar 1991 | A |
| 5009675 | Kunz et al. | Apr 1991 | A |
| 5009676 | Rue et al. | Apr 1991 | A |
| 5011508 | Wald et al. | Apr 1991 | A |
| 5011510 | Hayakawa et al. | Apr 1991 | A |
| 5014468 | Ravipati et al. | May 1991 | A |
| 5024795 | Kennedy et al. | Jun 1991 | A |
| 5032304 | Toyota | Jul 1991 | A |
| 5035723 | Kalinowski et al. | Jul 1991 | A |
| 5035724 | Pukari et al. | Jul 1991 | A |
| 5042991 | Kunz et al. | Aug 1991 | A |
| 5049166 | Kirkendall | Sep 1991 | A |
| 5049645 | Nagaoka et al. | Sep 1991 | A |
| 5053367 | Newkirk et al. | Oct 1991 | A |
| 5053369 | Winkler et al. | Oct 1991 | A |
| 5076991 | Poole et al. | Dec 1991 | A |
| 5078753 | Broberg et al. | Jan 1992 | A |
| 5081082 | Hai-Doo et al. | Jan 1992 | A |
| 5085671 | Martin et al. | Feb 1992 | A |
| 5090968 | Pellow | Feb 1992 | A |
| 5094986 | Matsumoto et al. | Mar 1992 | A |
| 5098740 | Tewari | Mar 1992 | A |
| 5103598 | Kelly | Apr 1992 | A |
| 5108963 | Fu et al. | Apr 1992 | A |
| 5114438 | Leatherman et al. | May 1992 | A |
| 5120327 | Dennis | Jun 1992 | A |
| 5123935 | Kanamaru et al. | Jun 1992 | A |
| 5129919 | Kalinowski et al. | Jul 1992 | A |
| 5131926 | Rostoker et al. | Jul 1992 | A |
| 5132984 | Simpson | Jul 1992 | A |
| 5139978 | Wood | Aug 1992 | A |
| 5152917 | Pieper et al. | Oct 1992 | A |
| 5160509 | Carman et al. | Nov 1992 | A |
| 5164744 | Yoshida et al. | Nov 1992 | A |
| 5173457 | Shorthouse | Dec 1992 | A |
| 5178849 | Bauer | Jan 1993 | A |
| 5180630 | Giglia | Jan 1993 | A |
| 5185012 | Kelly | Feb 1993 | A |
| 5185299 | Wood et al. | Feb 1993 | A |
| 5190568 | Tselesin | Mar 1993 | A |
| 5194072 | Rue et al. | Mar 1993 | A |
| 5201916 | Berg et al. | Apr 1993 | A |
| 5203886 | Sheldon et al. | Apr 1993 | A |
| 5213591 | Celikkaya et al. | May 1993 | A |
| 5215552 | Sung | Jun 1993 | A |
| 5219462 | Bruxvoort et al. | Jun 1993 | A |
| 5219806 | Wood | Jun 1993 | A |
| 5221294 | Carman et al. | Jun 1993 | A |
| 5224970 | Harakawa et al. | Jul 1993 | A |
| 5227104 | Bauer | Jul 1993 | A |
| 5244477 | Rue et al. | Sep 1993 | A |
| 5244849 | Roy et al. | Sep 1993 | A |
| 5273558 | Nelson et al. | Dec 1993 | A |
| 5277702 | Thibault et al. | Jan 1994 | A |
| 5282875 | Wood | Feb 1994 | A |
| 5288297 | Ringwood | Feb 1994 | A |
| 5300130 | Rostoker | Apr 1994 | A |
| 5304331 | Leonard et al. | Apr 1994 | A |
| 5312789 | Wood | May 1994 | A |
| 5312791 | Coblenz et al. | May 1994 | A |
| 5314513 | Miller et al. | May 1994 | A |
| 5366523 | Rowenhorst et al. | Nov 1994 | A |
| 5366525 | Fujiyama | Nov 1994 | A |
| 5372620 | Rowse et al. | Dec 1994 | A |
| 5373786 | Umaba | Dec 1994 | A |
| 5376598 | Preedy et al. | Dec 1994 | A |
| 5376602 | Nilsen | Dec 1994 | A |
| 5383945 | Cottringer et al. | Jan 1995 | A |
| 5395407 | Cottringer et al. | Mar 1995 | A |
| 5409645 | Torre, Jr. et al. | Apr 1995 | A |
| 5429648 | Wu | Jul 1995 | A |
| 5431967 | Manthiram | Jul 1995 | A |
| 5435816 | Spurgeon et al. | Jul 1995 | A |
| 5437754 | Calhoun | Aug 1995 | A |
| 5441549 | Helmin | Aug 1995 | A |
| 5443603 | Kirkendall | Aug 1995 | A |
| 5447894 | Yasuoka et al. | Sep 1995 | A |
| 5453106 | Roberts | Sep 1995 | A |
| 5454844 | Hibbard et al. | Oct 1995 | A |
| 5470806 | Krstic et al. | Nov 1995 | A |
| 5479873 | Shintani et al. | Jan 1996 | A |
| 5482756 | Berger et al. | Jan 1996 | A |
| 5486496 | Talbert et al. | Jan 1996 | A |
| 5496386 | Broberg et al. | Mar 1996 | A |
| 5498268 | Gagliardi et al. | Mar 1996 | A |
| 5500273 | Holmes et al. | Mar 1996 | A |
| 5514631 | Cottringer et al. | May 1996 | A |
| 5516347 | Garg | May 1996 | A |
| 5516348 | Conwell et al. | May 1996 | A |
| 5523074 | Takahashi et al. | Jun 1996 | A |
| 5525100 | Kelly et al. | Jun 1996 | A |
| 5527369 | Garg | Jun 1996 | A |
| 5543368 | Talbert et al. | Aug 1996 | A |
| 5549962 | Holmes et al. | Aug 1996 | A |
| 5551963 | Larmie | Sep 1996 | A |
| 5560745 | Roberts | Oct 1996 | A |
| 5567150 | Conwell et al. | Oct 1996 | A |
| 5567214 | Ashley | Oct 1996 | A |
| 5567251 | Peker et al. | Oct 1996 | A |
| 5571297 | Swei et al. | Nov 1996 | A |
| 5576409 | Mackey | Nov 1996 | A |
| 5578095 | Bland et al. | Nov 1996 | A |
| 5578222 | Trischuk et al. | Nov 1996 | A |
| 5582625 | Wright et al. | Dec 1996 | A |
| 5584896 | Broberg et al. | Dec 1996 | A |
| 5584897 | Christianson et al. | Dec 1996 | A |
| 5591685 | Mitomo et al. | Jan 1997 | A |
| 5593468 | Khaund et al. | Jan 1997 | A |
| 5599493 | Ito et al. | Feb 1997 | A |
| 5603738 | Zeiringer et al. | Feb 1997 | A |
| 5609706 | Benedict et al. | Mar 1997 | A |
| 5611829 | Monroe et al. | Mar 1997 | A |
| 5618221 | Furukawa et al. | Apr 1997 | A |
| 5628952 | Holmes et al. | May 1997 | A |
| 5641469 | Garg et al. | Jun 1997 | A |
| RE35570 | Rowenhorst et al. | Jul 1997 | E |
| 5645619 | Erickson et al. | Jul 1997 | A |
| 5651925 | Ashley et al. | Jul 1997 | A |
| 5656217 | Rogers et al. | Aug 1997 | A |
| 5667542 | Law et al. | Sep 1997 | A |
| 5669941 | Peterson | Sep 1997 | A |
| 5669943 | Horton et al. | Sep 1997 | A |
| 5672097 | Hoopman | Sep 1997 | A |
| 5672554 | Mohri et al. | Sep 1997 | A |
| 5683844 | Mammino | Nov 1997 | A |
| 5702811 | Ho et al. | Dec 1997 | A |
| 5725162 | Garg et al. | Mar 1998 | A |
| 5736619 | Kane et al. | Apr 1998 | A |
| 5738696 | Wu | Apr 1998 | A |
| 5738697 | Wu et al. | Apr 1998 | A |
| 5751313 | Miyashita et al. | May 1998 | A |
| 5759481 | Pujari et al. | Jun 1998 | A |
| 5776214 | Wood | Jul 1998 | A |
| 5779743 | Wood | Jul 1998 | A |
| 5785722 | Garg et al. | Jul 1998 | A |
| 5810587 | Bruns et al. | Sep 1998 | A |
| 5820450 | Calhoun | Oct 1998 | A |
| 5830248 | Christianson et al. | Nov 1998 | A |
| 5840089 | Chesley et al. | Nov 1998 | A |
| 5849646 | Stout et al. | Dec 1998 | A |
| 5855997 | Amateau | Jan 1999 | A |
| 5863306 | Wei et al. | Jan 1999 | A |
| 5866254 | Peker et al. | Feb 1999 | A |
| 5876793 | Sherman et al. | Mar 1999 | A |
| 5885311 | McCutcheon et al. | Mar 1999 | A |
| 5893935 | Wood | Apr 1999 | A |
| 5902647 | Venkataramani | May 1999 | A |
| 5908477 | Harmer et al. | Jun 1999 | A |
| 5908478 | Wood | Jun 1999 | A |
| 5919549 | Van et al. | Jul 1999 | A |
| 5924917 | Benedict et al. | Jul 1999 | A |
| 5946991 | Hoopman | Sep 1999 | A |
| 5975987 | Hoopman et al. | Nov 1999 | A |
| 5980678 | Tselesin | Nov 1999 | A |
| 5984988 | Berg et al. | Nov 1999 | A |
| 5989301 | Laconto, Sr. et al. | Nov 1999 | A |
| 5997597 | Hagan | Dec 1999 | A |
| 6016660 | Abramshe | Jan 2000 | A |
| 6019805 | Herron | Feb 2000 | A |
| 6024824 | Krech | Feb 2000 | A |
| 6027326 | Cesarano, III et al. | Feb 2000 | A |
| 6039775 | Ho et al. | Mar 2000 | A |
| 6048577 | Garg | Apr 2000 | A |
| 6053956 | Wood | Apr 2000 | A |
| 6054093 | Torre, Jr. et al. | Apr 2000 | A |
| 6080215 | Stubbs et al. | Jun 2000 | A |
| 6080216 | Erickson | Jun 2000 | A |
| 6083622 | Garg et al. | Jul 2000 | A |
| 6096107 | Caracostas et al. | Aug 2000 | A |
| 6110241 | Sung | Aug 2000 | A |
| 6129540 | Hoopman et al. | Oct 2000 | A |
| 6136288 | Bauer et al. | Oct 2000 | A |
| 6146247 | Nokubi et al. | Nov 2000 | A |
| 6179887 | Barber, Jr. et al. | Jan 2001 | B1 |
| 6206942 | Wood | Mar 2001 | B1 |
| 6228134 | Erickson | May 2001 | B1 |
| 6238450 | Garg et al. | May 2001 | B1 |
| 6258137 | Garg et al. | Jul 2001 | B1 |
| 6258141 | Sung et al. | Jul 2001 | B1 |
| 6261682 | Law | Jul 2001 | B1 |
| 6264710 | Erickson | Jul 2001 | B1 |
| 6277160 | Stubbs et al. | Aug 2001 | B1 |
| 6277161 | Castro et al. | Aug 2001 | B1 |
| 6283997 | Garg et al. | Sep 2001 | B1 |
| 6284690 | Nakahata et al. | Sep 2001 | B1 |
| 6287353 | Celikkaya | Sep 2001 | B1 |
| 6306007 | Mori et al. | Oct 2001 | B1 |
| 6312324 | Mitsui et al. | Nov 2001 | B1 |
| 6319108 | Adefris et al. | Nov 2001 | B1 |
| 6331343 | Perez et al. | Dec 2001 | B1 |
| 6371842 | Romero | Apr 2002 | B1 |
| 6391812 | Araki et al. | May 2002 | B1 |
| 6398989 | Bergstrom | Jun 2002 | B1 |
| 6401795 | Cesarano, III et al. | Jun 2002 | B1 |
| 6403001 | Hayashi | Jun 2002 | B1 |
| 6413286 | Swei et al. | Jul 2002 | B1 |
| 6428392 | Sunahara et al. | Aug 2002 | B1 |
| 6451076 | Nevoret et al. | Sep 2002 | B1 |
| 6475253 | Culler et al. | Nov 2002 | B2 |
| 6511938 | Liu | Jan 2003 | B1 |
| 6524681 | Seitz et al. | Feb 2003 | B1 |
| 6531423 | Schwetz et al. | Mar 2003 | B1 |
| 6537140 | Miller et al. | Mar 2003 | B1 |
| 6579819 | Hirosaki et al. | Jun 2003 | B2 |
| 6582623 | Grumbine et al. | Jun 2003 | B1 |
| 6583080 | Rosenflanz | Jun 2003 | B1 |
| 6599177 | Nevoret et al. | Jul 2003 | B2 |
| 6646019 | Perez et al. | Nov 2003 | B2 |
| 6652361 | Gash et al. | Nov 2003 | B1 |
| 6669745 | Prichard et al. | Dec 2003 | B2 |
| 6685755 | Ramanath et al. | Feb 2004 | B2 |
| 6696258 | Wei | Feb 2004 | B1 |
| 6702650 | Adefris | Mar 2004 | B2 |
| 6737378 | Hirosaki et al. | May 2004 | B2 |
| 6749496 | Mota et al. | Jun 2004 | B2 |
| 6750173 | Rizkalla | Jun 2004 | B2 |
| 6752700 | Duescher | Jun 2004 | B2 |
| 6755729 | Ramanath et al. | Jun 2004 | B2 |
| 6802878 | Monroe | Oct 2004 | B1 |
| 6821196 | Oliver | Nov 2004 | B2 |
| 6833014 | Welygan et al. | Dec 2004 | B2 |
| 6843815 | Thurber et al. | Jan 2005 | B1 |
| 6846795 | Lant et al. | Jan 2005 | B2 |
| 6878456 | Castro et al. | Apr 2005 | B2 |
| 6881483 | McArdle et al. | Apr 2005 | B2 |
| 6888360 | Connell et al. | May 2005 | B1 |
| 6913824 | Culler et al. | Jul 2005 | B2 |
| 6942561 | Mota et al. | Sep 2005 | B2 |
| 6949128 | Annen | Sep 2005 | B2 |
| 6974930 | Jense | Dec 2005 | B2 |
| 7022179 | Dry | Apr 2006 | B1 |
| 7044989 | Welygan et al. | May 2006 | B2 |
| 7112621 | Rohrbaugh et al. | Sep 2006 | B2 |
| 7141522 | Rosenflanz et al. | Nov 2006 | B2 |
| 7168267 | Rosenflanz et al. | Jan 2007 | B2 |
| 7169198 | Moeltgen et al. | Jan 2007 | B2 |
| 7267604 | Yoshizawa et al. | Sep 2007 | B2 |
| 7267700 | Collins et al. | Sep 2007 | B2 |
| 7294158 | Welygan et al. | Nov 2007 | B2 |
| 7297170 | Welygan et al. | Nov 2007 | B2 |
| 7297402 | Evans et al. | Nov 2007 | B2 |
| 7364788 | Kishbaugh et al. | Apr 2008 | B2 |
| 7373887 | Jackson | May 2008 | B2 |
| 7384437 | Welygan et al. | Jun 2008 | B2 |
| 7404832 | Ohtsubo et al. | Jul 2008 | B2 |
| 7488544 | Schofalvi et al. | Feb 2009 | B2 |
| 7507268 | Rosenflanz | Mar 2009 | B2 |
| 7553346 | Welygan et al. | Jun 2009 | B2 |
| 7556558 | Palmgren | Jul 2009 | B2 |
| 7560062 | Gould et al. | Jul 2009 | B2 |
| 7560139 | Thebault et al. | Jul 2009 | B2 |
| 7563293 | Rosenflanz | Jul 2009 | B2 |
| 7611795 | Aoyama et al. | Nov 2009 | B2 |
| 7618684 | Nesbitt | Nov 2009 | B2 |
| 7632434 | Duescher | Dec 2009 | B2 |
| 7662735 | Rosenflanz et al. | Feb 2010 | B2 |
| 7666344 | Schofalvi et al. | Feb 2010 | B2 |
| 7666475 | Morrison | Feb 2010 | B2 |
| 7669658 | Barron et al. | Mar 2010 | B2 |
| 7670679 | Krishna et al. | Mar 2010 | B2 |
| 7695542 | Drivdahl et al. | Apr 2010 | B2 |
| 7858189 | Wagener et al. | Dec 2010 | B2 |
| 7867302 | Nevoret et al. | Jan 2011 | B2 |
| 7906057 | Zhang et al. | Mar 2011 | B2 |
| 7968147 | Fang et al. | Jun 2011 | B2 |
| 7972430 | Millard et al. | Jul 2011 | B2 |
| 8021449 | Seth et al. | Sep 2011 | B2 |
| 8034137 | Erickson et al. | Oct 2011 | B2 |
| 8049136 | Mase et al. | Nov 2011 | B2 |
| 8070556 | Kumar et al. | Dec 2011 | B2 |
| 8123828 | Culler et al. | Feb 2012 | B2 |
| 8141484 | Ojima et al. | Mar 2012 | B2 |
| 8142531 | Adefris et al. | Mar 2012 | B2 |
| 8142532 | Erickson et al. | Mar 2012 | B2 |
| 8142891 | Culler et al. | Mar 2012 | B2 |
| 8251774 | Joseph et al. | Aug 2012 | B2 |
| 8256091 | Duescher | Sep 2012 | B2 |
| 8333360 | Rule et al. | Dec 2012 | B2 |
| 8440602 | Gonzales et al. | May 2013 | B2 |
| 8440603 | Gonzales et al. | May 2013 | B2 |
| 8445422 | Gonzales et al. | May 2013 | B2 |
| 8470759 | Gonzales et al. | Jun 2013 | B2 |
| 8480772 | Welygan et al. | Jul 2013 | B2 |
| 8530682 | Sachs | Sep 2013 | B2 |
| 8568497 | Sheridan | Oct 2013 | B2 |
| 8628597 | Palmgren et al. | Jan 2014 | B2 |
| 8783589 | Hart et al. | Jul 2014 | B2 |
| 8852643 | Gonzales et al. | Oct 2014 | B2 |
| 8920527 | Seider et al. | Dec 2014 | B2 |
| 8921687 | Welser | Dec 2014 | B1 |
| 9017439 | Yener et al. | Apr 2015 | B2 |
| 9079154 | Rosendahl | Jul 2015 | B2 |
| 9181477 | Collins et al. | Nov 2015 | B2 |
| 9211634 | Rehrig et al. | Dec 2015 | B2 |
| 9259726 | Gopal | Feb 2016 | B2 |
| 9375826 | Tian et al. | Jun 2016 | B2 |
| 9717674 | Guskey et al. | Aug 2017 | B1 |
| 9758724 | Collins et al. | Sep 2017 | B2 |
| 9982175 | Sarangi et al. | May 2018 | B2 |
| D849066 | Hanschen et al. | May 2019 | S |
| D849067 | Hanschen et al. | May 2019 | S |
| 10364383 | Yener et al. | Jul 2019 | B2 |
| D862538 | Hanschen et al. | Oct 2019 | S |
| D870782 | Hanschen et al. | Dec 2019 | S |
| 10556323 | Alkhas et al. | Feb 2020 | B2 |
| 10557068 | Oldenkotte et al. | Feb 2020 | B2 |
| 10563105 | Cotter | Feb 2020 | B2 |
| 10655038 | Martinez et al. | May 2020 | B2 |
| 10710211 | Lehuu et al. | Jul 2020 | B2 |
| 10717908 | Hejtmann et al. | Jul 2020 | B2 |
| 20010027623 | Rosenflanz | Oct 2001 | A1 |
| 20020026752 | Culler et al. | Mar 2002 | A1 |
| 20020068518 | Cesena et al. | Jun 2002 | A1 |
| 20020084290 | Materna | Jul 2002 | A1 |
| 20020090891 | Adefris et al. | Jul 2002 | A1 |
| 20020151265 | Adefris | Oct 2002 | A1 |
| 20020170236 | Larson et al. | Nov 2002 | A1 |
| 20020174935 | Burdon et al. | Nov 2002 | A1 |
| 20020177391 | Fritz et al. | Nov 2002 | A1 |
| 20030008933 | Perez et al. | Jan 2003 | A1 |
| 20030022961 | Kusaka et al. | Jan 2003 | A1 |
| 20030029094 | Moeltgen et al. | Feb 2003 | A1 |
| 20030085204 | Lagos | May 2003 | A1 |
| 20030109371 | Pujari et al. | Jun 2003 | A1 |
| 20030110707 | Rosenflanz et al. | Jun 2003 | A1 |
| 20030126800 | Seth et al. | Jul 2003 | A1 |
| 20030228738 | Beaudoin | Dec 2003 | A1 |
| 20040003895 | Amano et al. | Jan 2004 | A1 |
| 20040148868 | Anderson et al. | Aug 2004 | A1 |
| 20040148967 | Celikkaya et al. | Aug 2004 | A1 |
| 20040202844 | Wong | Oct 2004 | A1 |
| 20040224125 | Yamada et al. | Nov 2004 | A1 |
| 20040235406 | Duescher | Nov 2004 | A1 |
| 20040244675 | Kishimoto et al. | Dec 2004 | A1 |
| 20050020190 | Schutz et al. | Jan 2005 | A1 |
| 20050060941 | Provow et al. | Mar 2005 | A1 |
| 20050060947 | McArdle et al. | Mar 2005 | A1 |
| 20050064805 | Culler et al. | Mar 2005 | A1 |
| 20050081455 | Welygan et al. | Apr 2005 | A1 |
| 20050118939 | Duescher | Jun 2005 | A1 |
| 20050132655 | Anderson et al. | Jun 2005 | A1 |
| 20050218565 | DiChiara, Jr. | Oct 2005 | A1 |
| 20050223649 | O'Gary et al. | Oct 2005 | A1 |
| 20050232853 | Evans et al. | Oct 2005 | A1 |
| 20050245179 | Luedeke | Nov 2005 | A1 |
| 20050255801 | Pollasky | Nov 2005 | A1 |
| 20050266221 | Karam et al. | Dec 2005 | A1 |
| 20050271795 | Moini et al. | Dec 2005 | A1 |
| 20050284029 | Bourlier et al. | Dec 2005 | A1 |
| 20060049540 | Hui et al. | Mar 2006 | A1 |
| 20060126265 | Crespi et al. | Jun 2006 | A1 |
| 20060135050 | Petersen et al. | Jun 2006 | A1 |
| 20060177488 | Caruso et al. | Aug 2006 | A1 |
| 20060185256 | Nevoret et al. | Aug 2006 | A1 |
| 20070011951 | Gaeta et al. | Jan 2007 | A1 |
| 20070020457 | Adefris | Jan 2007 | A1 |
| 20070051355 | Sung | Mar 2007 | A1 |
| 20070072527 | Palmgren | Mar 2007 | A1 |
| 20070074456 | Orlhac et al. | Apr 2007 | A1 |
| 20070087928 | Rosenflanz et al. | Apr 2007 | A1 |
| 20070234646 | Can et al. | Oct 2007 | A1 |
| 20080017053 | Araumi et al. | Jan 2008 | A1 |
| 20080072500 | Klett et al. | Mar 2008 | A1 |
| 20080098659 | Sung | May 2008 | A1 |
| 20080121124 | Sato | May 2008 | A1 |
| 20080172951 | Starling | Jul 2008 | A1 |
| 20080176075 | Bauer et al. | Jul 2008 | A1 |
| 20080179783 | Liu et al. | Jul 2008 | A1 |
| 20080230951 | Dannoux et al. | Sep 2008 | A1 |
| 20080262577 | Altshuler et al. | Oct 2008 | A1 |
| 20080271384 | Puthanangady et al. | Nov 2008 | A1 |
| 20080286590 | Besida et al. | Nov 2008 | A1 |
| 20080299875 | Duescher | Dec 2008 | A1 |
| 20090016916 | Rosenzweig et al. | Jan 2009 | A1 |
| 20090017276 | Hoglund et al. | Jan 2009 | A1 |
| 20090017736 | Block et al. | Jan 2009 | A1 |
| 20090098365 | Moeltgen | Apr 2009 | A1 |
| 20090165394 | Culler et al. | Jul 2009 | A1 |
| 20090165661 | Koenig et al. | Jul 2009 | A1 |
| 20090169816 | Erickson et al. | Jul 2009 | A1 |
| 20090208734 | Macfie et al. | Aug 2009 | A1 |
| 20090246464 | Watanabe et al. | Oct 2009 | A1 |
| 20100000159 | Walia et al. | Jan 2010 | A1 |
| 20100003900 | Sakaguchi et al. | Jan 2010 | A1 |
| 20100003904 | Duescher | Jan 2010 | A1 |
| 20100040767 | Uibel et al. | Feb 2010 | A1 |
| 20100056816 | Wallin et al. | Mar 2010 | A1 |
| 20100064594 | Pakalapati et al. | Mar 2010 | A1 |
| 20100068974 | Dumm | Mar 2010 | A1 |
| 20100146867 | Boden et al. | Jun 2010 | A1 |
| 20100151195 | Culler et al. | Jun 2010 | A1 |
| 20100151196 | Adefris et al. | Jun 2010 | A1 |
| 20100151201 | Erickson et al. | Jun 2010 | A1 |
| 20100190424 | Francois et al. | Jul 2010 | A1 |
| 20100201018 | Yoshioka et al. | Aug 2010 | A1 |
| 20100251625 | Gaeta | Oct 2010 | A1 |
| 20100292428 | Meador et al. | Nov 2010 | A1 |
| 20100307067 | Sigalas et al. | Dec 2010 | A1 |
| 20100319269 | Erickson | Dec 2010 | A1 |
| 20100330886 | Wu et al. | Dec 2010 | A1 |
| 20110008604 | Boylan | Jan 2011 | A1 |
| 20110111563 | Yanagi et al. | May 2011 | A1 |
| 20110124483 | Shah et al. | May 2011 | A1 |
| 20110136659 | Allen et al. | Jun 2011 | A1 |
| 20110146509 | Welygan et al. | Jun 2011 | A1 |
| 20110152548 | Sachs | Jun 2011 | A1 |
| 20110160104 | Wu et al. | Jun 2011 | A1 |
| 20110244769 | David et al. | Oct 2011 | A1 |
| 20110289854 | Moren et al. | Dec 2011 | A1 |
| 20110314746 | Erickson et al. | Dec 2011 | A1 |
| 20120000135 | Eilers et al. | Jan 2012 | A1 |
| 20120034847 | Besse et al. | Feb 2012 | A1 |
| 20120055098 | Ramanath et al. | Mar 2012 | A1 |
| 20120100366 | Dumm et al. | Apr 2012 | A1 |
| 20120137597 | Adefris et al. | Jun 2012 | A1 |
| 20120144754 | Culler et al. | Jun 2012 | A1 |
| 20120144755 | Erickson et al. | Jun 2012 | A1 |
| 20120153547 | Bauer et al. | Jun 2012 | A1 |
| 20120167481 | Yener et al. | Jul 2012 | A1 |
| 20120168979 | Bauer et al. | Jul 2012 | A1 |
| 20120227333 | Adefris et al. | Sep 2012 | A1 |
| 20120231711 | Keipert et al. | Sep 2012 | A1 |
| 20120308837 | Schlechtriemen et al. | Dec 2012 | A1 |
| 20130000212 | Wang et al. | Jan 2013 | A1 |
| 20130000216 | Wang et al. | Jan 2013 | A1 |
| 20130009484 | Yu | Jan 2013 | A1 |
| 20130036402 | Mutisya et al. | Feb 2013 | A1 |
| 20130045251 | Cen et al. | Feb 2013 | A1 |
| 20130067669 | Gonzales et al. | Mar 2013 | A1 |
| 20130072417 | Perez-Prat et al. | Mar 2013 | A1 |
| 20130074418 | Panzarella et al. | Mar 2013 | A1 |
| 20130125477 | Adefris | May 2013 | A1 |
| 20130180180 | Yener et al. | Jul 2013 | A1 |
| 20130186005 | Kavanaugh | Jul 2013 | A1 |
| 20130186006 | Kavanaugh et al. | Jul 2013 | A1 |
| 20130199105 | Braun et al. | Aug 2013 | A1 |
| 20130203328 | Givot et al. | Aug 2013 | A1 |
| 20130212952 | Welygan et al. | Aug 2013 | A1 |
| 20130236725 | Yener et al. | Sep 2013 | A1 |
| 20130255162 | Welygan et al. | Oct 2013 | A1 |
| 20130260656 | Seth et al. | Oct 2013 | A1 |
| 20130267150 | Seider et al. | Oct 2013 | A1 |
| 20130283705 | Fischer et al. | Oct 2013 | A1 |
| 20130296587 | Rosendahl | Nov 2013 | A1 |
| 20130305614 | Gaeta et al. | Nov 2013 | A1 |
| 20130337262 | Bauer et al. | Dec 2013 | A1 |
| 20130337725 | Monroe | Dec 2013 | A1 |
| 20130344786 | Keipert | Dec 2013 | A1 |
| 20140000176 | Moren et al. | Jan 2014 | A1 |
| 20140007518 | Yener et al. | Jan 2014 | A1 |
| 20140080393 | Ludwig | Mar 2014 | A1 |
| 20140106126 | Gaeta et al. | Apr 2014 | A1 |
| 20140107356 | Gopal | Apr 2014 | A1 |
| 20140182216 | Panzarella et al. | Jul 2014 | A1 |
| 20140182217 | Yener et al. | Jul 2014 | A1 |
| 20140186585 | Field, III et al. | Jul 2014 | A1 |
| 20140250797 | Yener et al. | Sep 2014 | A1 |
| 20140256238 | Van et al. | Sep 2014 | A1 |
| 20140287658 | Flaschberger et al. | Sep 2014 | A1 |
| 20140290147 | Seth et al. | Oct 2014 | A1 |
| 20140352721 | Gonzales et al. | Dec 2014 | A1 |
| 20140352722 | Gonzales et al. | Dec 2014 | A1 |
| 20140357544 | Gonzales et al. | Dec 2014 | A1 |
| 20140378036 | Cichowlas et al. | Dec 2014 | A1 |
| 20150000209 | Louapre et al. | Jan 2015 | A1 |
| 20150000210 | Breder et al. | Jan 2015 | A1 |
| 20150007399 | Gonzales et al. | Jan 2015 | A1 |
| 20150007400 | Gonzales et al. | Jan 2015 | A1 |
| 20150089881 | Stevenson et al. | Apr 2015 | A1 |
| 20150126098 | Eilers et al. | May 2015 | A1 |
| 20150128505 | Wang et al. | May 2015 | A1 |
| 20150183089 | Iyengar et al. | Jul 2015 | A1 |
| 20150209932 | Lehuu et al. | Jul 2015 | A1 |
| 20150218430 | Yener et al. | Aug 2015 | A1 |
| 20150232727 | Erickson | Aug 2015 | A1 |
| 20150291865 | Breder et al. | Oct 2015 | A1 |
| 20150291866 | Arcona et al. | Oct 2015 | A1 |
| 20150291867 | Breder et al. | Oct 2015 | A1 |
| 20150343603 | Breder et al. | Dec 2015 | A1 |
| 20160090516 | Yener et al. | Mar 2016 | A1 |
| 20160177152 | Braun | Jun 2016 | A1 |
| 20160177153 | Josseaux | Jun 2016 | A1 |
| 20160177154 | Josseaux et al. | Jun 2016 | A1 |
| 20160186028 | Louapare et al. | Jun 2016 | A1 |
| 20160214903 | Humpal et al. | Jul 2016 | A1 |
| 20160298013 | Bock et al. | Oct 2016 | A1 |
| 20160303704 | Chou et al. | Oct 2016 | A1 |
| 20160303705 | Chou et al. | Oct 2016 | A1 |
| 20160304760 | Bock et al. | Oct 2016 | A1 |
| 20160311081 | Culler et al. | Oct 2016 | A1 |
| 20160311084 | Culler et al. | Oct 2016 | A1 |
| 20160326416 | Bauer et al. | Nov 2016 | A1 |
| 20160340564 | Louapre et al. | Nov 2016 | A1 |
| 20160354898 | Nienaber et al. | Dec 2016 | A1 |
| 20160362589 | Bauer | Dec 2016 | A1 |
| 20170066099 | Nakamura | Mar 2017 | A1 |
| 20170114260 | Bock et al. | Apr 2017 | A1 |
| 20170129075 | Thurber et al. | May 2017 | A1 |
| 20170225299 | Keipert et al. | Aug 2017 | A1 |
| 20170335156 | Bauer et al. | Nov 2017 | A1 |
| 20170349797 | Yener et al. | Dec 2017 | A1 |
| 20180086957 | Sahlin et al. | Mar 2018 | A1 |
| 20180161960 | Wilson et al. | Jun 2018 | A1 |
| 20180169837 | Liu | Jun 2018 | A1 |
| 20180215975 | Marazano et al. | Aug 2018 | A1 |
| 20180215976 | Cotter et al. | Aug 2018 | A1 |
| 20180318983 | Wilson et al. | Nov 2018 | A1 |
| 20190022826 | Franke et al. | Jan 2019 | A1 |
| 20190030684 | Van et al. | Jan 2019 | A1 |
| 20190091835 | Culler et al. | Mar 2019 | A1 |
| 20190126436 | Westberg et al. | May 2019 | A1 |
| 20190217442 | Gaeta et al. | Jul 2019 | A1 |
| 20190249052 | Eckel et al. | Aug 2019 | A1 |
| 20190270182 | Eckel et al. | Sep 2019 | A1 |
| 20190309201 | Dumont et al. | Oct 2019 | A1 |
| 20190322915 | Jiwpanich et al. | Oct 2019 | A1 |
| 20190330505 | Bujnowski et al. | Oct 2019 | A1 |
| 20190337124 | Liu et al. | Nov 2019 | A1 |
| 20190338172 | Erickson et al. | Nov 2019 | A1 |
| 20190338173 | Yener et al. | Nov 2019 | A1 |
| 20190351531 | Nelson et al. | Nov 2019 | A1 |
| 20190366511 | Huber | Dec 2019 | A1 |
| 20190382637 | Braun et al. | Dec 2019 | A1 |
| 20200139512 | Culler et al. | May 2020 | A1 |
| 20200148927 | Arcona et al. | May 2020 | A1 |
| 20200156215 | Jusuf et al. | May 2020 | A1 |
| 20200157396 | Cotter et al. | May 2020 | A1 |
| 20200157397 | Stevenson et al. | May 2020 | A1 |
| 20200199426 | Yener et al. | Jun 2020 | A1 |
| 20210087445 | Cotter | Mar 2021 | A1 |
| Number | Date | Country |
|---|---|---|
| 743715 | Oct 1966 | CA |
| 2423788 | Jul 2002 | CA |
| 685051 | Mar 1995 | CH |
| 1229007 | Jul 2005 | CN |
| 1774488 | May 2006 | CN |
| 101389466 | Mar 2009 | CN |
| 101970347 | Feb 2011 | CN |
| 101980836 | Feb 2011 | CN |
| 102281992 | Dec 2011 | CN |
| 103189164 | Jul 2013 | CN |
| 103842132 | Jun 2014 | CN |
| 102123837 | Jul 2014 | CN |
| 104125875 | Oct 2014 | CN |
| 104994995 | Oct 2015 | CN |
| 105622071 | Jun 2016 | CN |
| 105713568 | Jun 2016 | CN |
| 3923671 | Feb 1998 | DE |
| 102012023688 | Apr 2014 | DE |
| 202014101739 | Jun 2014 | DE |
| 202014101741 | Jun 2014 | DE |
| 102013202204 | Aug 2014 | DE |
| 102013210158 | Dec 2014 | DE |
| 102013210716 | Dec 2014 | DE |
| 102013212598 | Dec 2014 | DE |
| 102013212622 | Dec 2014 | DE |
| 102013212634 | Dec 2014 | DE |
| 102013212639 | Dec 2014 | DE |
| 102013212644 | Dec 2014 | DE |
| 102013212653 | Dec 2014 | DE |
| 102013212654 | Dec 2014 | DE |
| 102013212661 | Dec 2014 | DE |
| 102013212666 | Dec 2014 | DE |
| 102013212677 | Dec 2014 | DE |
| 102013212680 | Dec 2014 | DE |
| 102013212687 | Dec 2014 | DE |
| 102013212690 | Dec 2014 | DE |
| 102013212700 | Dec 2014 | DE |
| 102014210836 | Dec 2014 | DE |
| 0078896 | May 1983 | EP |
| 0152768 | Aug 1985 | EP |
| 0293163 | Nov 1988 | EP |
| 0480133 | Apr 1992 | EP |
| 0652919 | May 1995 | EP |
| 0662110 | Jul 1995 | EP |
| 0500369 | Jan 1996 | EP |
| 0609864 | Nov 1996 | EP |
| 0771769 | May 1997 | EP |
| 0812456 | Dec 1997 | EP |
| 0651778 | May 1998 | EP |
| 0614861 | May 2001 | EP |
| 0931032 | Jul 2001 | EP |
| 0833803 | Aug 2001 | EP |
| 1207015 | May 2002 | EP |
| 1356152 | Oct 2003 | EP |
| 1371451 | Dec 2003 | EP |
| 1383631 | Jan 2004 | EP |
| 1015181 | Mar 2004 | EP |
| 1492845 | Jan 2005 | EP |
| 1851007 | Nov 2007 | EP |
| 1960157 | Aug 2008 | EP |
| 2176031 | Apr 2010 | EP |
| 2184134 | May 2010 | EP |
| 2242618 | Oct 2010 | EP |
| 2390056 | Nov 2011 | EP |
| 1800801 | Mar 2012 | EP |
| 2445982 | May 2012 | EP |
| 2507016 | Oct 2012 | EP |
| 2537917 | Dec 2012 | EP |
| 2567784 | Mar 2013 | EP |
| 2631286 | Aug 2013 | EP |
| 2692813 | Feb 2014 | EP |
| 2692814 | Feb 2014 | EP |
| 2692815 | Feb 2014 | EP |
| 2692816 | Feb 2014 | EP |
| 2692817 | Feb 2014 | EP |
| 2692818 | Feb 2014 | EP |
| 2692819 | Feb 2014 | EP |
| 2692820 | Feb 2014 | EP |
| 2692821 | Feb 2014 | EP |
| 2719752 | Apr 2014 | EP |
| 2720676 | Apr 2014 | EP |
| 2012972 | Jun 2014 | EP |
| 3319758 | May 2018 | EP |
| 3342839 | Jul 2018 | EP |
| 3444313 | Jul 2020 | EP |
| 2354373 | Jan 1978 | FR |
| 986847 | Mar 1965 | GB |
| 1456765 | Nov 1976 | GB |
| 1466054 | Mar 1977 | GB |
| 53064890 | Jun 1978 | JP |
| 60-006356 | Jan 1985 | JP |
| 62002946 | Jan 1987 | JP |
| 63036905 | Jul 1988 | JP |
| 3079277 | Apr 1991 | JP |
| 03-287687 | Dec 1991 | JP |
| 5285833 | Nov 1993 | JP |
| 6114739 | Apr 1994 | JP |
| 7008474 | Feb 1995 | JP |
| 3030861 | Aug 1996 | JP |
| 10113875 | May 1998 | JP |
| 2779252 | Jul 1998 | JP |
| 10330734 | Dec 1998 | JP |
| H10315142 | Dec 1998 | JP |
| 2957492 | Oct 1999 | JP |
| 2000091280 | Mar 2000 | JP |
| 2000-336344 | Dec 2000 | JP |
| 2000354967 | Dec 2000 | JP |
| 3160084 | Apr 2001 | JP |
| 2001162541 | Jun 2001 | JP |
| 03194269 | Jul 2001 | JP |
| 2001180930 | Jul 2001 | JP |
| 2001207160 | Jul 2001 | JP |
| 2002-038131 | Feb 2002 | JP |
| 2002210659 | Jul 2002 | JP |
| 2003-049158 | Feb 2003 | JP |
| 2004-510873 | Apr 2004 | JP |
| 2004209624 | Jul 2004 | JP |
| 2006130586 | May 2006 | JP |
| 2006130636 | May 2006 | JP |
| 2006159402 | Jun 2006 | JP |
| 2006-192540 | Jul 2006 | JP |
| 2007-537891 | Dec 2007 | JP |
| 2008132560 | Jun 2008 | JP |
| 2008194761 | Aug 2008 | JP |
| 2008531305 | Aug 2008 | JP |
| 2012512046 | May 2012 | JP |
| 2012512047 | May 2012 | JP |
| 2012512048 | May 2012 | JP |
| 2012530615 | Dec 2012 | JP |
| 5238725 | Jul 2013 | JP |
| 5238726 | Jul 2013 | JP |
| 2014503367 | Feb 2014 | JP |
| 2017518889 | Jul 2017 | JP |
| 2017538588 | Dec 2017 | JP |
| 2018510073 | Apr 2018 | JP |
| 20140106713 | Sep 2014 | KR |
| 171464 | Nov 1982 | NL |
| 9402559 | Feb 1994 | WO |
| 9503370 | Feb 1995 | WO |
| 9518192 | Jul 1995 | WO |
| 9520469 | Aug 1995 | WO |
| 9627189 | Sep 1996 | WO |
| 9711484 | Mar 1997 | WO |
| 9714536 | Apr 1997 | WO |
| 9906500 | Feb 1999 | WO |
| 1999038817 | Aug 1999 | WO |
| 9954424 | Oct 1999 | WO |
| 0064630 | Nov 2000 | WO |
| 0114494 | Mar 2001 | WO |
| 0123323 | Apr 2001 | WO |
| 02097150 | Dec 2002 | WO |
| 03087236 | Oct 2003 | WO |
| 2005080624 | Sep 2005 | WO |
| 2005112601 | Dec 2005 | WO |
| 2006027593 | Mar 2006 | WO |
| 2006062597 | Jun 2006 | WO |
| 2007041538 | Apr 2007 | WO |
| 2009085578 | Jul 2009 | WO |
| 2009085841 | Jul 2009 | WO |
| 2009098017 | Aug 2009 | WO |
| 2010077509 | Jul 2010 | WO |
| 2010085587 | Jul 2010 | WO |
| 2010151201 | Dec 2010 | WO |
| 2011005425 | Jan 2011 | WO |
| 2011068714 | Jun 2011 | WO |
| 2011068724 | Jun 2011 | WO |
| 2011087649 | Jul 2011 | WO |
| 2011109188 | Sep 2011 | WO |
| 2011133438 | Oct 2011 | WO |
| 2011139562 | Nov 2011 | WO |
| 2011149625 | Dec 2011 | WO |
| 2012018903 | Feb 2012 | WO |
| 2012061016 | May 2012 | WO |
| 2012061033 | May 2012 | WO |
| 2012092590 | Jul 2012 | WO |
| 2012092605 | Jul 2012 | WO |
| 2012112305 | Aug 2012 | WO |
| 2012112322 | Aug 2012 | WO |
| 2010070294 | Aug 2012 | WO |
| 2012141905 | Oct 2012 | WO |
| 2012092590 | Oct 2012 | WO |
| 2012140617 | Oct 2012 | WO |
| 2013003830 | Jan 2013 | WO |
| 2013003831 | Jan 2013 | WO |
| 2013009484 | Jan 2013 | WO |
| 2013036402 | Mar 2013 | WO |
| 2013040423 | Mar 2013 | WO |
| 2013045251 | Apr 2013 | WO |
| 2013049239 | Apr 2013 | WO |
| 2013070576 | May 2013 | WO |
| 2013101575 | Jul 2013 | WO |
| 2013102170 | Jul 2013 | WO |
| 2013102176 | Jul 2013 | WO |
| 2013102177 | Jul 2013 | WO |
| 2013106597 | Jul 2013 | WO |
| 2013106602 | Jul 2013 | WO |
| 2013151745 | Oct 2013 | WO |
| 2013149209 | Oct 2013 | WO |
| 2013177446 | Nov 2013 | WO |
| 2013186146 | Dec 2013 | WO |
| 2013188038 | Dec 2013 | WO |
| 2014005120 | Jan 2014 | WO |
| 2014020068 | Feb 2014 | WO |
| 2014020075 | Feb 2014 | WO |
| 2014022453 | Feb 2014 | WO |
| 2014022462 | Feb 2014 | WO |
| 2014022465 | Feb 2014 | WO |
| 2014161001 | Feb 2014 | WO |
| 2014057273 | Apr 2014 | WO |
| 2014062701 | Apr 2014 | WO |
| 2014070468 | May 2014 | WO |
| 2014106173 | Jul 2014 | WO |
| 2014106211 | Jul 2014 | WO |
| 2014124554 | Aug 2014 | WO |
| 2014137972 | Sep 2014 | WO |
| 2014140689 | Sep 2014 | WO |
| 2014165390 | Oct 2014 | WO |
| 2014176108 | Oct 2014 | WO |
| 2014206739 | Dec 2014 | WO |
| 2014206890 | Dec 2014 | WO |
| 2014206967 | Dec 2014 | WO |
| 2014209567 | Dec 2014 | WO |
| 2014210160 | Dec 2014 | WO |
| 2014210442 | Dec 2014 | WO |
| 2014210532 | Dec 2014 | WO |
| 2014210568 | Dec 2014 | WO |
| 2015050781 | Apr 2015 | WO |
| 2015073346 | May 2015 | WO |
| 2015048768 | Jun 2015 | WO |
| 2015088953 | Jun 2015 | WO |
| 2015089527 | Jun 2015 | WO |
| 2015089528 | Jun 2015 | WO |
| 2015089529 | Jun 2015 | WO |
| 2015100018 | Jul 2015 | WO |
| 2015100020 | Jul 2015 | WO |
| 2015100220 | Jul 2015 | WO |
| 2015102992 | Jul 2015 | WO |
| 2015112379 | Jul 2015 | WO |
| 2015130487 | Sep 2015 | WO |
| 2015158009 | Oct 2015 | WO |
| 2015160854 | Oct 2015 | WO |
| 2015160855 | Oct 2015 | WO |
| 2015160857 | Oct 2015 | WO |
| 2015164211 | Oct 2015 | WO |
| 2015165122 | Nov 2015 | WO |
| 2015167910 | Nov 2015 | WO |
| 2015179335 | Nov 2015 | WO |
| 2015180005 | Dec 2015 | WO |
| 2015184355 | Dec 2015 | WO |
| 2016028683 | Feb 2016 | WO |
| 2016044158 | Mar 2016 | WO |
| 2016064726 | Apr 2016 | WO |
| 2016089675 | Jun 2016 | WO |
| 2016105469 | Jun 2016 | WO |
| 2016105474 | Jun 2016 | WO |
| 2016160357 | Oct 2016 | WO |
| 2016161157 | Oct 2016 | WO |
| 2016161170 | Oct 2016 | WO |
| 2016167967 | Oct 2016 | WO |
| 2016187570 | Nov 2016 | WO |
| 2016196795 | Dec 2016 | WO |
| 2016201104 | Dec 2016 | WO |
| 2016205133 | Dec 2016 | WO |
| 2016205267 | Dec 2016 | WO |
| 2016210057 | Dec 2016 | WO |
| 2017007703 | Jan 2017 | WO |
| 2017007714 | Jan 2017 | WO |
| 2017062482 | Apr 2017 | WO |
| 2017083249 | May 2017 | WO |
| 2017083255 | May 2017 | WO |
| 2016105543 | Sep 2017 | WO |
| 2017151498 | Sep 2017 | WO |
| 2018010730 | Jan 2018 | WO |
| 2018026669 | Feb 2018 | WO |
| 2018057465 | Mar 2018 | WO |
| 2018057558 | Mar 2018 | WO |
| 2018063902 | Apr 2018 | WO |
| 2018063958 | Apr 2018 | WO |
| 2018063960 | Apr 2018 | WO |
| 2018063962 | Apr 2018 | WO |
| 2018064642 | Apr 2018 | WO |
| 2018080703 | May 2018 | WO |
| 2018080704 | May 2018 | WO |
| 2018080705 | May 2018 | WO |
| 2018080755 | May 2018 | WO |
| 2018080756 | May 2018 | WO |
| 2018080765 | May 2018 | WO |
| 2018080778 | May 2018 | WO |
| 2018080784 | May 2018 | WO |
| 2018081246 | May 2018 | WO |
| 2018118688 | Jun 2018 | WO |
| 2018118690 | Jun 2018 | WO |
| 2018118695 | Jun 2018 | WO |
| 2018118699 | Jun 2018 | WO |
| 2018134732 | Jul 2018 | WO |
| 2018136268 | Jul 2018 | WO |
| 2018136269 | Jul 2018 | WO |
| 2018136271 | Jul 2018 | WO |
| 2018172193 | Sep 2018 | WO |
| 2018207145 | Nov 2018 | WO |
| 2018236989 | Dec 2018 | WO |
| 2019001908 | Jan 2019 | WO |
| 2019069157 | Apr 2019 | WO |
| 2019102312 | May 2019 | WO |
| 2019102328 | May 2019 | WO |
| 2019102329 | May 2019 | WO |
| 2019102330 | May 2019 | WO |
| 2019102331 | May 2019 | WO |
| 2021161129 | Aug 2019 | WO |
| 2019167022 | Sep 2019 | WO |
| 2019197948 | Oct 2019 | WO |
| 2019207415 | Oct 2019 | WO |
| 2019207416 | Oct 2019 | WO |
| 2019207417 | Oct 2019 | WO |
| 2019207423 | Oct 2019 | WO |
| 2019215571 | Nov 2019 | WO |
| 2020025270 | Feb 2020 | WO |
| 2020035764 | Feb 2020 | WO |
| 2020075005 | Apr 2020 | WO |
| 2020079522 | Apr 2020 | WO |
| 2020084382 | Apr 2020 | WO |
| 2020084483 | Apr 2020 | WO |
| 2020089741 | May 2020 | WO |
| 2020128708 | Jun 2020 | WO |
| 2020128716 | Jun 2020 | WO |
| 2020128717 | Jun 2020 | WO |
| 2020128719 | Jun 2020 | WO |
| 2020128720 | Jun 2020 | WO |
| 2020128752 | Jun 2020 | WO |
| 2020128779 | Jun 2020 | WO |
| 2020128780 | Jun 2020 | WO |
| 2020128781 | Jun 2020 | WO |
| 2020128783 | Jun 2020 | WO |
| 2020128787 | Jun 2020 | WO |
| 2020128794 | Jun 2020 | WO |
| 2020128833 | Jun 2020 | WO |
| 2020128838 | Jun 2020 | WO |
| 2020128842 | Jun 2020 | WO |
| 2020128844 | Jun 2020 | WO |
| 2020128845 | Jun 2020 | WO |
| 2020128852 | Jun 2020 | WO |
| 2020128853 | Jun 2020 | WO |
| 2020128856 | Jun 2020 | WO |
| 2021009600 | Jan 2021 | WO |
| 2021014271 | Jan 2021 | WO |
| 2021074756 | Apr 2021 | WO |
| 2021074768 | Apr 2021 | WO |
| 2021079331 | Apr 2021 | WO |
| 2021081571 | May 2021 | WO |
| 2021105030 | Jun 2021 | WO |
| 2021116883 | Jun 2021 | WO |
| 2021137092 | Jul 2021 | WO |
| 2021179025 | Sep 2021 | WO |
| 2021186326 | Sep 2021 | WO |
| 2021214065 | Oct 2021 | WO |
| 2021214576 | Oct 2021 | WO |
| 2021234540 | Nov 2021 | WO |
| Entry |
|---|
| VSM Actirox Fibre Discs, The Latest Generation of Abrasives for Maximum Stock Removal [PDF] VSM Abrasives Ltd., Apr. 2019 [retrieved on May 15, 2019]. Retrieved from https://uk.vsmabrasives.com/fileadmin/user_upload/ACTIROX/VSM-ACTIROX-EN.pdf. |
| Torre, “Investigation of Shaped Abrasive Particles vol. 1: Review of U.S. Pat. No. 6,054,093 Apr. 25, 2000” © Apr. 2011, 5 pages. |
| Austin, Benson M., “Thick-Film Screen Printing,” Solid State Technology, Jun. 1969, pp. 53-58. |
| Avril, Nicholas Joseph, “Manufacturing Glass-fiber Reinforcement for Grinding Wheels,” Massachusetts Institute of Technology, 1996, 105 pgs. |
| Bacher, Rudolph J., “High Resolution Thick Film Printing,” E.I. du Pont de Nemours & Company, Inc., pp. 576-581, date unknown. |
| Besse, John R., “Understanding and controlling wheel truing and dressing forces when rotary plunge dressing,” Cutting Tool Engineering, Jun. 2012, vol. 64, Issue 6, 5 pages. |
| Brewer, L. et al., Journal of Materials Research, 1999, vol. 14, No. 10, pp. 3907-3912. |
| Ciccotti, M. et al., “Complex dynamics in the peeling of an adhesive tape,” International Journal of Adhesion & Adhesives 24 (2004) pp. 143-151. |
| DuPont, “Kevlar Aramid Pulp”, Copyright 2011, DuPont, 1 page. |
| Wu, J. et al., Friction and Wear Properties of Kevlar Pulp Reinforced Epoxy. |
| J. European Ceramic Society 31, Abstract only (2011) 2073-2081. |
| Riemer, Dietrich E., “Analytical Engineering Model of the Screen Printing Process: Part II,” Solid State Technology, Sep. 1988, pp. 85-90. |
| Miller, L.F., “Paste Transfer in the Screening Process,” Solid State Technology, Jun. 1969, pp. 46-52. |
| Morgan, P. et al., “Ceramic Composites of Monazite and Alumina,” J. Am. Ceram. Soc., 78, 1995, 1553-63. |
| Riemer, Dietrich E., “Analytical Engineering Model of the Screen Printing Process: Part I,” Solid State Technology, Aug. 1988, pp. 107-111. |
| Winter Catalogue No. 5, Dressing tools, Winter diamond tools for dressing grinding wheels, 140 pages. |
| Badger, Jeffrey, “Evaluation of Triangular, Engineered-Shape Ceramic Abrasive in Cutting Discs,” Supplement to the Welding Journal, Apr. 2014, vol. 93, pp. 107-s to 115-s. |
| 3M Cubitron II Abrasive Belts Brochure, Shaping the Future, Jan. 2011, 6 pages. |
| Vanstrum et al., Precisely Shaped Grain (PSG): 3M's Innovation in Abrasive Grain Technology, date unknown, 1 page. |
| Graf, “Cubitron II: Precision-Shaped Grain (PSG) Turns the Concept of Gear Grinding Upside Down,” gearsolutions.com, May 2014, pp. 36-44. |
| DOW Machine Tool Accessories, Grinding & Surface Finishing, www.1mta.com, Nov. 2014, 72 pages. |
| Kumar et al., “Composites by rapid prototyping technology”, Material & Design, Feb. 2010, vol. 31, Issue 2, pp. 850-856. |
| Lewis et al., “Direct Ink Writing of Three-Dimensional Ceramic Structures”, Journal of the American Ceramic Society, US, Nov. 30, 2006, vol. 89, Issue 12, pp. 3599-3609. |
| International Search Report with regard to International application No. PCT/US2017/031998, dated Aug. 21, 2017. |
| International Search Report with regard to International application No. PCT/US2017/031992, dated Aug. 21, 2017. |
| International Search Report and Written Opinion for Application No. PCT/US2016/036701, dated Sep. 1, 2016, 12 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20200157396 A1 | May 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15420701 | Jan 2017 | US |
| Child | 16749490 | US |