Claims
- 1. A method of manufacturing a ceramic superconductor product, comprising the steps of:
- preparing a starting powder consisting essentially of a ceramic superconductor of the required stoichiometry range of said ceramic superconductor product;
- sintering said starting powder to densify said powder using a partial pressure of p(O.sub.2) of about 0.1 Pa to 100 Pa and generating from said starting powder of ceramic superconductor a mixture consisting essentially of said ceramic superconductor and nonsuperconductor second phases during said sintering step; and
- annealing said sintered powder until said mixture of ceramic superconductor and nonsuperconducting second phases converts to said ceramic superconductor product having the required stoichiometry range.
- 2. The method as defined in claim 1 wherein said step of sintering and generating comprises annealing below the melting point of said ceramic superconductor to generate a fine grained dispersion of said mixture of second phases in the matrix of said first phase.
- 3. The method as defined in claim 2 wherein said mixture of second phases pins grain boundaries of said ceramic superconductor thereby preventing substantial grain growth of said ceramic superconductor during said sintering step.
- 4. The method as defined in claim 1 wherein said ceramic superconductor compound consists essentially of 123YBaCu-oxide.
- 5. The method as defined in claim 1 wherein said ceramic superconductor is selected from the group consisting of 1223 TlBaCaCu-oxide 1212 TlBaCaCu-oxide, 2212 TlBaCaCu-oxide, 2223 TlBaCaCu-oxide, 2234 TlBaCaCu-oxide, 2212 BiSrCaCu-oxide and 2223 BiSrCaCu-oxide.
- 6. The method as defined in claim 1 wherein the step of maintaining a p(O.sub.2) atmosphere during sintering includes maintaining a pressure in the range of about 0.1Pa to about 42 Pa and said starting powder is a 123 YBaCu-oxide.
- 7. The method as defined in claim 6 wherein said sintered compound has a grain size distribution less than about 0.5 to 15 mm.
- 8. The method as defined in claim 7 wherein said sintering step includes a sintering temperature less than about 950.degree. C. and more than about 850.degree. C.
- 9. The method as defined in claim 1 wherein said sintering step includes a sintering temperature below the temperature at which microcracking occurs in said ceramic superconductor.
- 10. A method of manufacturing a ceramic superconductor product, comprising the steps of:
- preparing a starting powder of a ceramic superconductor having a composition selected from the ceramic superconductor systems TlBaCaCuO, YBaCuO and BiSrCaCuO and having the required stoichiometry range of said ceramic superconductor product;
- sintering said starting powder/under a controlled p(O.sub.2) atmosphere of less than about 100Pa and more than 0.1 Pa to densify said powder to at least about 90% theoretical density and generating a second phase consisting essentially of said ceramic superconductor and nonsuperconducting phases decomposed from said ceramic superconductor enabling the controlling of grain growth of said ceramic superconductor; and
- annealing said sintered powder until said second nonsuperconducting phases convert to said ceramic superconductor product having the required stoichiometry range.
- 11. The method as defined in claim 10 wherein said p(O.sub.2) atmosphere is controlled to achieve the desired amount and form of said nonsuperconducting phases.
- 12. The method as defined in claim 10 wherein said sintering temperature is maintained below the temperature at which microcracking occurs in said ceramic superconductor.
- 13. The method as defined in claim 10 wherein said starting powder after sintering has a fracture strength of at least about 230 Mpa.
- 14. The method as defined in claim 10 wherein said ceramic superconductor consists essentially of 123 YBaCu-oxide and said second nonsuperconducting phases comprise Cu.sub.2 O, BaCuO.sub.2 and Y.sub.2 BaCuO.sub.5.
- 15. The method as defined in claim 14 wherein said annealing step is performed at about 840.degree. C.
- 16. The method as defined in claim 15 wherein said annealing step is performed in O.sub.2.
- 17. The method as defined in claim 10 wherein said second phase inhibits grain growth during said sintering step.
Government Interests
The U.S. Government has certain rights in this invention pursuant to Contract No. W-31-109-Eng-38 of the Department of Energy.
US Referenced Citations (6)