The invention relates to a method for manufacturing a front face for protecting the discharge end of a burner with two or more coaxial channels, the front face comprising a central aperture corresponding to the discharge end of the burner, a front side wall and a backside wall spaced by one or more baffles defining a coolant flow path with a first end provided with a coolant inlet and a second end having a coolant discharge outlet.
Such a front face is particularly useful for protecting burners used for the partial combustion of carbonaceous fuels, such as finely divided solid fuel carried by a gas, e.g., pulverized coal carried by a carrier gas such as nitrogen gas or carbon dioxide, using an oxygen-containing gas, e.g., for producing pressurized synthesis gas, fuel gas or reducing gas.
Partial combustion, also known as gasification, of a solid carbonaceous fuel is obtained by the reaction of the fuel with oxygen. The fuel contains as combustible components, mainly carbon and hydrogen. The gas-carried finely divided carbonaceous fuel and the oxygen-containing gas are passed via the separate channels in the burner into a reactor at relatively high velocity. In the reactor a flame is maintained in which the fuel reacts with the oxygen in the oxygen-containing gas at temperatures above 1300° C. to form mainly carbon monoxide and hydrogen.
The term “oxygen-containing gas” as used herein is intended to refer to gas containing free oxygen, O2, and to include air, oxygen-enriched air, i.e., more than 21 mole % oxygen, and also substantially pure oxygen, i.e., more than about 95 mole % oxygen, with the remainder comprising gases normally found in air such as nitrogen, and/or rare gases.
The term “solid carbonaceous fuel” as used herein is intended to include various gas carried combustible materials and mixtures thereof from the group of coal, coke from coal, coal liquefaction residues, petroleum coke, soot, biomass, and particulate solids derived from oil shale, tar sands and pitch. The coal may be of any type, including lignite, sub-bituminous, bituminous and anthracite. The solid carbonaceous fuels are preferably ground to a particle size so that at least about 90% by weight of the material is less than 90 microns and moisture content is less than about five percent weight.
U.S. Pat. No. 4,887,962 and U.S. Pat. No. 4,865,542 disclose a burner for such a partial combustion process. The burner comprises a central channel with an outlet for supplying the fuel to the combustions zone, and a coaxial annular channel with an outlet surrounding the central channel's outlet to supply an oxygen containing gas intersecting and mixing with the flow of solid fuel from the outlet of the central channel. The burner further comprises a front face disposed at the discharge end of the burner. The front face has a central aperture through which the fuel and the oxygen containing gas flow to the combustion zone. The front face is a double walled member comprising a central aperture corresponding to the discharge end of the burner, a front side wall and a backside wall spaced by a spiral baffle defining a spiral flow path with a first end operatively connected to a coolant supply conduit and a second end having an outlet operatively connected to a coolant discharge conduit.
At the discharge end, the combustion temperatures can be as high as 1300° C. or higher. This causes thermal stresses and deterioration of the burner during prolonged operation, particularly by fatigue stresses, which may ultimately result in leaks of coolant. Moreover, during operation burner heads also undergo high mechanical pressure loads.
It is an object of the present invention to provide a method of manufacturing a front face allowing a front face construction which balances optimized heat dissipation with a high mechanical strength.
The object of the invention is achieved by a method for manufacturing a front face for protecting the discharge end of a burner wherein the front side wall and the one or more baffles are machined out of a single piece of metal and wherein the backside wall is welded on the free top end of the one or more baffles by welding the backside wall from its surface opposite the contact surface with the baffle top ends. By making the baffle and the front wall from one single piece, the mechanical strength of the structure can be optimized, allowing the use of thinner walls which improves heat transfer. The front wall of the front face can be made free of welding spots. Suitable machining methods are for instance milling, spark erosion, electrical discharge machining and the like.
The baffle can for example be a single spiral baffle, defining a spiral flow path, as in U.S. Pat. No. 4,887,962. A spiral flow path can also be realized by using a set of three or more concentric baffles defining concentric channel sections at least one of these channel sections being blocked by a partition bridging an inner and an outer baffle just after an interruption in the inner baffle, thus leading the flow path to a next concentric channel section closer to the front face center. The foregoing method creates an approximate spiral flow path. It has been found that a number of two or three concentric flow path sections result in effective heat dissipation with only limited pressure drop. However, the number of concentric sections can also be higher if so desired.
The front face can have a circumferential wall closing off the space between the front and backside walls. The circumferential wall can for example be an extension of the spiral baffle defining the flow path.
A suitable steel type for manufacturing the front wall with the baffles, and optionally also the backside wall, is a steel alloy comprising 45-60 wt. % of nickel, and, optionally, 17-25 wt. % of chromium. Particularly suitable are steel types according to US standard UNS N07718 (German standard W. Nr. 2.4668), such as Inconel® 718 commercially available from Special Metals Corporation, Nicrofer® 5219 of ThyssenKrupp, Allvac® 718 of Allvac, Haynes® 718 of Haynes International, and Altemp® 718 of Allegheny Ludlum. It has been found that such nickel chromium steels not only combine high tensile strength with good corrosion resistance, but also show excellent thermal conductivity. Particularly the chromium content improves the resistance against corrosion and sulfidation.
The steel alloy may for instance comprise 4-6 wt. % of niobium, and/or 2-4 wt. % molybdenum, and/or at least one element of the group of titanium, aluminium, cobalt, carbon, manganese, silicon, phosphorus, sulphur, boron, and copper, in an amount of 0.004-1.3 wt. % per element. Particularly the use of niobium, aluminium, and titanium can result in improved mechanical properties. The composition is balanced to 100% predominantly with iron.
To improve mechanical properties, the front face is preferably subjected to a precipitation hardening treatment or age hardening. This can be carried out, e.g., after welding the backside wall to the free baffle top ends. Additionally, particularly if a nickel steel alloy is used comprising carbide forming constituents such as niobium, the front face can be subjected to a solution anneal treatment, e.g. before the precipitation hardening takes place and after welding. The front face can for example be subjected to a solution anneal treatment at 900-1000° C. followed by rapid cooling, e.g., in water, followed by a precipitation hardening treatment at 720° C. for 8 hours, furnace cooling to 620° C. for a total aging time of 18 hours, followed by air cooling. Alternatively, the front face can for example be subjected to a solution anneal treatment at 1000-1150° C. followed by rapid cooling, e.g., in water, followed by a precipitation hardening treatment at 760° C. for 10 hours, furnace cooling to 650° C. for a total aging time of 20 hours, followed by air cooling.
The present invention allows the use of thin-walled structures that can withstand high heat fluxes. The front side wall of the front face can be as thin as 0.5-3 mm. Due to the internal pressure by the coolant during operation, the baffles defining the coolant flow path should have a sufficient tensile strength. Depending on the total length of baffles, the baffle can have a thickness of, e.g., 0.5-3 mm.
The invention further relates to a burner for the partial combustion of a gas carried carbonaceous fuel comprising a front face manufactured according to any one of the methods described above.
The invention will now be described in more detail, by way of example only, with reference to the accompanying drawings, wherein:
The inner wall 3 has a constant inner diameter. The downstream wall part 3B has a conically expanded part 8 with enlarged outer diameter declining towards the discharge outlet 4 so as to form an annular bulge with—in this particular embodiment—a triangular cross section. The downstream part of outer wall 5B forms a cylinder with a conical end 9 convergent in flow direction. The bulging part 8 of the downstream inner wall part 3B and the conical end 9 of the downstream outer wall part 5B define an annular slit 10 of even width and wherein part 8 has a diameter decreasing in the direction of the discharge outlet 4. This annular slit 10 forms the discharge outlet 7 of the coaxial channel 6.
The inner and outer channel wall parts 3A, 3B, 5A and 5B are welded to a circular connection block 11. The circular connection block 11 is provided with a concentric circular array of openings 12 allowing flow-through from the upstream part of the coaxial channel 6 to the downstream part of it and a central aperture 13 in line with the central channel 2. In between the openings 12, the connection block 11 bridges the inner and outer walls 3, 5.
The coaxial channel 6 is encased by a cooling jacket 14 with an upstream part 14A at the upstream side of the connection block 11 and a downstream part 14B at the downstream part of the connection block 11. Two coaxial casings 15A, 16A are welded to the upstream side of connection block 11 to form two coaxial compartments, inner compartment 17A, and outer compartment 18A.
The downstream part of the cooling jacket 14B comprises an inner jacket wall 15B, forming the downstream extension of upstream inner casing 15A, and an outer jacket wall 16B, forming the downstream extension of upstream casing 16A. The space 18B between the jacket walls 15B, 16B forms the downstream extension of the upstream cooling jacket compartment 18A and is divided by baffles 19 into spiral channels. The space 17B between inner jacket wall 15B and the outer wall part 5B forms the downstream extension of the upstream inner compartment 17A. The connection block 11 is provided with two concentric circular arrays of openings 20 connecting the upstream cooling jacket compartments 17A, 18A with the downstream cooling jacket compartments 17B, 18B respectively.
Downstream the cooling jacket section 14B, a double walled front face 21 is disposed under right angles with the cooling jacket walls 15B, 16B. The front face 21 has an inner edge 22 defining a central opening 23 and adjoining the outer edge of the coaxial channels outer wall 5B. The front face 21 has an outer diameter which is smaller than the outer diameter of the upstream cooling jacket part 14A. In flow direction the downstream cooling jacket part 14B tapers down from the same outer diameter as upstream cooling jacket casing 14A to the outer diameter of the front face 21.
The burner 1 of
The upstream inner cooling jacket compartment 17A is connected to a supply of a liquid coolant. The coolant flows from the inner cooling jacket compartment 17A, via openings 20 in block 11, downstream compartment 17B, coolant inlet 30, flow path sections 27 in front face 21, coolant discharge outlet 31, outer cooling jacket compartment 18B, openings 20 in block 11, and outer compartment 18A to a coolant discharge. A circumferential end wall 32 closes off the space between the front wall 24 and the back side wall 25 of the front face 21.
The front side wall 24, the concentric baffles 26 and the circumferential wall 32 are machined out of a single piece of a nickel chromium steel alloy. The backside wall 25 is composed of concentric segments 33 corresponding to the concentric flow path sections defined by the baffles 26. The segments 33 are positioned on top of the free baffle ends, bridging the baffles 26. After that, the back side wall segments 33 are welded to the baffles 26. After welding, the front face 21 is subjected to anneal solution treatment, followed by precipitation hardening.
| Number | Date | Country | Kind |
|---|---|---|---|
| 07113847.3 | Aug 2007 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2008/060277 | 8/5/2008 | WO | 00 | 1/11/2012 |
| Number | Date | Country | |
|---|---|---|---|
| 60954342 | Aug 2007 | US |