Patent Application
20170348956
This invention relates to an improved method of manufacturing a composite panel using lauan and the panel made using the method (while the method is applicable to panels using lauan or other moisture-carrying or moisture-absorbing materials, reference will for the most part be limited to lauan, in the interest of conciseness). In the conventional production of composite panels with lauan, a gel coat layer is first laid down on a mold, followed by a layer of resin and glass fibers, thus forming a wet laminate. A layer of lauan is then applied directly to the wet laminate. The resin contains one or more promoters, and depending on the resin used, peroxide may also be added to the resin just before it is introduced into the mold. The peroxide acts as a cure initiator by reacting with the promoter and causing the resin to polymerize and harden. It additionally results in the resin bonding to the lauan, forming a flat, hard composite sheet.
Sometimes the lauan, although apparently exhibiting acceptable adhesion, does not form a strong bond to the cured laminate, resulting in a panel that can undergo delamination. The present inventor has determined that this problem is more likely to occur with increased water content of the lauan. The inventor thus believes that the problem is due to excess moisture in the lauan, and that this water inhibits the cure of the resin at the interface by interfering with the reaction between peroxide and promoter, resulting in poor adhesion to the lauan. Unfortunately, attempting to solve this problem by simply adding extra promoter to the resin is not practical. The extra promoter changes the speed at which polymerization occurs, thus causing timing problems in the production process, as well as increasing consumption of the promoter.
One might attempt to manage this problem by inspecting all lauan for moisture content before using it. This reduces the likelihood of producing panels that are subject to delamination, but requires extra labor for the inspection, as well as storing the high-moisture lauan and returning it to the vendor. Similarly, attempting to dry the too-moist pieces of lauan before use would require still more labor, as well as requiring the availability of drying equipment and use of energy for the drying process.
The present method involves applying promoter at the resin-substrate (e.g., lauan) interface. This is preferably done by spraying the promoter onto the top surface of the resin before the lauan is placed on top, but it may instead be done by spraying or rolling the promoter onto the lauan itself. Most generally, it may be done by providing promoter at the resin-lauan interface in any manner that may be convenient (provided that little to no extra promoter is added to the rest of the resin layer). The present inventor has found that doing this may reduce the likelihood of delamination even with lauan that happens to have a high moisture content that would otherwise be problematic, and in fact, may enable one to reduce or even practically eliminate the problem rather than just managing it.
According to certain embodiments, a method of manufacturing a lauan composite panel, and the panel so made, are provided. A layer of gel coat is formed on a mold surface, a wet laminate containing a resin is applied to the layer of gel coat on the mold surface, a lauan or other substrate is placed on the wet laminate, and the combination is cured. Prior to curing, there is provided a layer of a bonding promoter at the interface of the lauan substrate with the wet laminate, additional to any amount of promoter(s) present in the resin of the wet laminate.
The features and advantages herein will become more apparent from the detailed description set forth below when taken in conjunction with the drawings, in which like reference numbers indicate identical or functionally similar elements.
As stated above, the conventional method of manufacturing a lauan composite panel involves forming a layer of gel coat on the surface of a mold of at least the size of the panel to be made. On the gel coat is formed a wet laminate, of a resin containing a promoter and possibly peroxide, and fiber glass fibers as a reinforcement. The wet laminate may be sprayed onto the gel coat, such as by spraying the resin onto the gel coat, followed by (or mixed with) the glass fibers, and then rolling the surface of the layer to achieve evenness. A sheet of lauan is then positioned on the wet laminate; for a typical panel, a number of pieces of lauan are actually used, and are placed abutting each other to cover the wet laminate.
The wet laminate is then cured. This may be done by encasing the entire mold in a vacuum bag, exposing the mold with the gel coat and other layers on it to a vacuum, and applying heat. Alternatively, heat alone may be used.
A second spray head sprays promoter onto the wet laminate, as shown to the left of the first spray head. This promoter may be the same as is included in the wet laminate itself, but that need not be the case, as discussed below. The wet laminate, coated with the promoter by the second spraying head, is then covered with the required number of pieces of lauan. (To be more precise, the wet laminate may not be exactly and completely covered by the lauan, as a peripheral portion of the laminate may remain uncovered.)
When the entire mold has been provided with each of the mentioned layers, it is enclosed in a vacuum bag (not illustrated), and the resin of the wet laminate is cured under vacuum and heat. Alternatively, other techniques of curing may be used. The finished panel is then released from the mold and cut to size if necessary.
An example of a panel manufactured in this fashion is shown in
While reference has been made above simply to a promoter being applied to the lauan-laminate interface, in practice of course what is applied is a solution of the promoter(s), so that what is applied includes one or more promoters, a solvent, and if needed a material to dilute the concentration of the promoter(s) to the desired value. It is believed that the following may be used as suitable promoters, although it should be understood that neither this list nor the following list of solvents is intended to be exhaustive:
The mixture ratio of solvent to promotor can range, for example, from 10:1 to 1000:1, or more particularly from 20:1 to 800:1, or from 50:1 to 500:1, or from 100:1 to 300:1.
One preferred embodiment applies 1% cobalt-acetone drying solution as the solvent-promoter mixture, applied to the lauan with target coverage of 3 grams/square foot (about 32 grams/square meter). Another example uses cobalt with mineral spirits. Other mixtures, as stated, may be used.
Also, the promoter used in the solvent-promoter mixture may be one (or more) also used in the resin, or instead may include one or more not used in the resin.
While the embodiment described above with reference to
Another example is illustrated in
Additional variations in the method are within the broad scope of the present invention. For example, while only application by spraying or by use of a roller have been mentioned, any other mechanized or manual method of application of the promoter that may be found convenient may be used. Also, an individual mold may be used for each panel, or a continuous mold may be used. Again, the mold may be moved past each work station in turn for application of the gel coat, of the wet laminate, of the promoter and of the lauan, and then for the curing, or alternatively the mold may be stationary.
Results obtained have been good, based on testing including for regularity of product surface or surface profile, and mechanical, such as flex, tensile and, block pull tests, with moisture contents from 0 to 19% (and, particularly, with high moisture content, of e.g., 13-18% and especially 14-17%; all % are weight-%). Moreover, the inventor has found that advantageous results may be obtained regardless of whether the lauan used is sanded or not, and for different thicknesses of lauan. Additionally, the method may yield advantageous results whether the resin used contains a filler, such as mica, or not. Further, it is believed that this method may produce satisfactory results with any moisture content up to the level at which the lauan would be unacceptable based on other criteria.
Furthermore, while this method has been described with particular relation to the manufacture of a panel having a lauan substrate bonded to a resin-fiberglass layer that is bonded to a gel coat, the method is applicable as well to the manufacture of other types of article in which it is desired to bond lauan or a similar material to a resin layer, whether containing glass fibers or not. The method is also applicable to other woods than lauan, such as plywood, and to other substrates that may carry or absorb moisture.
While various example embodiments of the present invention have been described above, it should be understood that they have been presented by way of example, and not limitation. It will be apparent to persons skilled in the relevant art(s) that various changes in form and detail can be made therein. Thus, the present invention should not be limited by any of the above described example embodiments, but should be defined only in accordance with the following claims and their equivalents.
Further, the purpose of the following Abstract is to enable the U.S. Patent and Trademark Office and the public generally, and especially the scientists, engineers and practitioners in the art who are not familiar with patent or legal terms or phraseology, to determine quickly from a cursory inspection the nature and essence of the technical disclosure of the application. The Abstract is not intended to be limiting as to the scope of the example embodiments presented herein in any way. It is also to be understood that the procedures recited in the claims need not be performed in the order presented.
This application claims benefit under 35 U.S.C. §119(e) of Patent Application No. 62/345,946, filed Jun. 6, 2016. The contents of that prior application are incorporated by reference herein in their entirety, as if set forth fully herein.