Method Of Manufacturing A Solar Cell With Local Back Contacts

Abstract

The invention relates to the manufacturing process of a solar cell (1) with back contact and passivated emitter, comprising a dielectric stack (10) of at least two layers consisting of at least a first dielectric layer (11) made of AlOx in contact with a p-type silicon layer (3), and a second dielectric layer (13) deposited on the first dielectric layer (11). Besides, the method of manufacturing comprising a formation step of at least one partial opening (15) preferably by laser ablation into the dielectric stack (10), sparing at least partially the aforementioned first dielectric layer.

Description

The invention relates to a method of manufacturing a solar cell with local back contacts.

The method of this invention can be applied for several manufacturing designs, such as PERC (passivated emitter and rear cell), PERL (passivated emitter and rear locally-diffused) or IBC (Interdigitated Back Contact) type solar cells.

For all of them, good passivation properties on the back face of the wafer surface are mandatory in order to reduce recombination losses.

In PERC technology, for example, the back face of the solar cells comprises a reflective coating made of a dielectric layer and a metal layer. The dielectric layer provides the aforementioned passivation. This dielectric layer is opened locally in order to allow the contact between the bulk silicon and the metal layer deposited right after.

In silicon solar cells, the most commonly used dielectric layer is hydrogenated silicon nitride (SiNx:H). This layer shows intrinsically net positive charges, which create a parasitic emitter layer for the case of p-type substrates, also called inversion layer, which, after the creation of a metallic contact, is responsible for an increase in recombination.

Thus, in p-type silicon PERC solar cells, the standard passivation stack for the back side is made of silicon oxide (SiO2) and SiNx:H, in order to decrease this effect.

Recently, works have been reported on the use of aluminium oxide (AlOx) layers for passivating the back side of p-type silicon solar cells. These AlOx layers have been shown to have intrinsic negative charges, which prevent the creation of a parasitic emitter on p-type silicon and facilitate the field-effect passivation.

In addition, a common way to fabricate the local openings into the dielectric layers is by means of laser ablation, which goes completely through the passivation stack.

However, it was shown that laser ablation of the SiO2 and SiNx passivation layers melts the underlying silicon surface, inducing damages. Various types of laser-induced damages can be created such as delamination or cracks in the dielectric layers around the openings, melting of the silicon, overheating of the dielectric layers around the openings. These damages induce a decrease in the passivation performance.

Moreover, it was shown that the damages caused in AlOx/SiNx passivation layers could modify the charges in the AlOx layer, thus inducing a decrease in field-effect passivation and leading to the creation of a parasitic emitter layer detrimental to solar cell performance.

In line with the common knowledge in the field of the art, laser ablation of SiO2 or AlOx has to be done completely in order to enhance the performances. This is due to the fact that in case of partial ablation in a SiOx/SiNx stack, the performance of a solar panel decreases because a partial ablation induces an increase of the series resistance of the solar cell.

A document representing such a prior art is “Laser ablation of SIO2/SINX and ALOX/SINX backside passivation stacks for advanced cell architectures.” in: 26th European Photovoltaic Solar Energy Conference and Exhibition-EU-PVSEC. 2011. pp .2180-2183; (5-9 Sep. 2011; Hamburg, Germany).

This article teaches in particular in §4 that the optimal conditions are reached by a complete damage free laser ablation.

Complete laser ablation has been applied to SiO/SiNx and AlOx/SiNx layers. In case of AlOx/SiNx layers, the results showed lower performances as expected in view of the better passivation properties of AlOx as compared to SiO₂. Even a blistering effect has been observed.

The present invention aims at mitigating, at least partially, the drawbacks described above.

For this purpose, the invention proposes a method of manufacturing a solar cell with local back contacts comprising a dielectric stack of at least two layers presenting at least a first dielectric layer of AlOx in contact with a layer of p-type silicon and a second dielectric layer deposited on the first dielectric layer, characterized in that it comprises a step of formation of at least one partial opening in the dielectric stack, leaving at least partially the aforementioned first dielectric layer at the location of the partial opening.

Thanks to this process, the damages caused by the laser beam, such as the local heating and the delamination, occur only in the second dielectric layer, the first dielectric layer being at least partially preserved and the underlying bulk silicon is totally preserved.

In addition, although it was commonly admitted that laser ablation has to be complete in order not to increase series resistance of the solar cells, it was observed that the performances of the solar cells for partial laser ablation of AlOx even increased with respect to complete laser ablation.

In addition, the dielectric layers have passivation properties. A good passivation quality is thus maintained around the openings, which contributes to an improvement in short-circuit current and (Jsc), open circuit voltage (Voc), and in particular in the output compared to cells where the dielectric layer is completely ablated.

According to other characteristics taken alone or in combination:

the step of formation of at least one partial opening in the dielectric stack comprises a laser ablation step,

the ablation step is carried out using a pulse laser which pulse duration is less than a few nanoseconds,

the first dielectric layer exhibits negative charges allowing field effect passivation,

the first dielectric layer has a thickness of at least a few monolayers after ablation,

the second dielectric layer is made of SiNx,

the ablation step is carried out using a laser which radiates in the UV region, more specifically around 355 nm.

Other advantages and characteristics will appear with the reading of the description of the following figures, among which:

FIG. 1 shows diagrams of manufacturing of a PERC type solar cell.

FIG. 2 shows a detail at the rear side after partial ablation of the dielectric stack.

FIG. 3 shows diagrams of manufacturing of a PERL type solar cell.

On all the figures the same references refer to the same elements.

On FIG. 1, diagrams represent three steps (a), (b) and (c) of the manufacturing method of a solar cell with passivated back surface and local back contacts according to the invention.

FIG. 1 example, consists of a PERC type solar cell (passivated emitter and rear cell).

Of course, these three steps do not represent the whole cell manufacturing method, but only the steps concerning the invention. The other manufacturing steps are known by the field specialists, and do not require a description within the framework of this invention.

As can be seen on FIG. 1(a), at this step of manufacture, the photovoltaic cell 1 comprises a layer 3 substrate or p-type silicon wafer, a layer 5 of n-doped silicon on the front face 7.

On the front face 7 is also deposited an anti-reflecting layer 9 (ARC for “antireflection coating”), for example, silicon nitride SiNx.

On the back face of cell 1 is deposited a stack 10 of at least two dielectric layers 11 and 13.

In the present example, the first dielectric layer 11 is aluminum oxide AlOx.

The second dielectric layer 13 is for example silicon nitride SiNx, in particular hydrogenated silicon nitride SINx:H.

The first dielectric layer 11 is in contact with substrate 3 and the second dielectric layer 13 is deposited on the first dielectric layer 11.

According to step (b), one can proceed with a formation step of at least one local opening 15 by laser ablation in passivation stack 10, leaving at least partially the aforementioned first dielectric layer 11. This step can thus be qualified as partial laser ablation of the passivation stack 10, meaning that the SiNx layer is completely ablated whereas the AlOx layer is not or only partially ablated. One thus can obtain the configuration shown according to a detail on FIG. 2.

For this ablation process, optimal laser conditions (i.e. pulse duration, wavelength, power, etc) allowing a partial ablation as described above can be determined experimentally and are specific to the dielectric stack to be ablated. For example, one can use a single pulse laser of less than a few nanoseconds, also picoseconds or femptoseconds pulses and in the UV range, in particular at 355 nm wavelength.

After ablation, the first dielectric layer 11 preferably has a layer thickness thick enough (at least 1 nm) to exhibit negative charges and thin enough to allow a low temperature diffusion of Al metal through AlOx to form the contact, for example a thickness of at least a few monolayers after ablation, meaning a thickness between 1 nm and 30 nm after ablation.

Thus, the silicon of substrate 3 is not damaged by laser ablation.

Typically, one carries out the aforementioned partial openings by laser ablation with any pattern suitable for good optical reflection properties and with optimal metalized contacted area. For example, one can use a pattern composed of partial openings of about 40 μm separated by 600 μm.

Thanks to this process, the damages caused by the laser beam such as for example the local heating and the delamination occur only on the level of the second dielectric layer 13, the first dielectric layer 11 being preserved.

Then, on step (c), one proceeds to a step of a metallization layer 17 application on the rear face 19 of the photovoltaic cell. Any Al-based metallization method can be applied. This can for example be carried out by Al-sputtering on the rear face 19 of the solar cell 1.

Finally, on step (d), one performs on the areas where at least one partial opening 15 is spared, a backsurface field (BSF) formation by firing in a furnace at a temperature T>740° C., for example at 815° C.

Thanks to the method according to the invention, a good passivation quality around the metal contacts is maintained, which contributes to an improvement of the values of short circuit current (Jsc) by 1.6% and of open circuit voltage (Voc) by 1.1% compared experimentally with solar cells manufactured according to state of the art processes where the passivation stack is completely ablated. Similarly, the fill factor FF is improved by 0.35% and the efficiency itself by approximately 3%.

FIG. 3 shows the manufacturing process of a solar cell similar to that on FIG. 1, but this time for a PERL type solar cell.

In this case and unlike PERC cells, in the regions of metal contacts to be fabricated, p+ doped zones 21 were created beforehand as local BSF, for example with B diffusion. Apart from this, steps (a) to (c) are similar.

Then, after the metallization step (c), one carries out an annealing step for the formation of the metal contacts on the back side region 19, for example at 400° C. In this case also, an increase in the performances of the cell was also observed.

Claims

1. A method of manufacturing a solar cell having a front face and a back face, the method comprising: providing a dielectric stack disposed between the front face and the back face of the solar cell, wherein the dielectric stack comprises at least a first dielectric layer comprising Aluminum Oxide (AlOx) and a second dielectric layer, each of the first dielectric layer and the second dielectric layer comprising an associated top surface and bottom surface, wherein the top surface of the first dielectric layer is in contact with a layer of p-type silicon and the second dielectric layer is deposited on the bottom surface of the first dielectric layer;forming at least one partial opening in the dielectric stack, wherein the at least one partial opening is formed in at least a portion of the first dielectric layer; andproviding one or more metal contacts on the back face of the solar cell.

2. The method of claim 1 wherein forming the at least one partial opening the dielectric stack comprises forming the at least one partial opening in the dielectric stack through laser ablation.

3. The method of claim 2 wherein forming the at least one partial opening through laser ablation comprises applying a pulse laser with a pulse duration less than a few nanoseconds (ns) to at least a portion of the first dielectric layer.

4. The method of claim 1 wherein providing the dielectric stack comprises providing the first dielectric layer, wherein the first dielectric layer further is provided having a negative charge characteristic, which allows for field effect passivation of the first dielectric layer.

5. A method of claim 2 wherein within the at least one partial opening, the first dielectric layer is provided having a thickness of at least a few monolayers.

6. The method of claim 2 wherein within the at least one partial opening, the first dielectric layer has a thickness between 1 nanometer (nm) and 30 nm.

7. The method of claim 1 wherein the second dielectric layer comprises Silicon Nitride (SiNx).

8. The method of claim 2 wherein forming the at least one partial opening through laser ablation comprises radiating a laser on the at least a portion of the first dielectric layer, wherein the laser radiates in an ultra-violet (UV) region, wherein the UV region comprises a wavelength at or around 355 nanometers (nm).

9. The method of claim 2 further comprising: applying a metallization layer to the cell.

10. The method of claim 9 wherein applying the metallization layer comprises applying an Aluminum (Al) based metallization layer to the back face of the solar cell.

11. The method of claim 9 further comprising: applying a backsurface field (BSF) formation on areas of the solar cell not including the at least one partial opening, wherein the BSF formation is formed at a temperature greater than 740 degrees Celsius.

12. The method of claim 9 wherein providing one or more metal contacts on the back face of the solar cell comprises forming the metal contacts by annealing the back face of the solar cell at a predetermined temperature, wherein the predetermined temperature may be a least 400 degrees Celsius.

13. A solar cell with a front face and a back face, the solar cell comprising: a dielectric stack disposed between the front face and the back face of the solar cell, the dielectric stack comprising: at least a first dielectric layer comprising Aluminum Oxide (AlOx) and a second dielectric layer, each of the first dielectric layer and the second dielectric layer comprising an associated top surface and bottom surface, wherein the top surface of the first dielectric layer is in contact with a layer of p-type silicon and the second dielectric layer is deposited on the bottom surface of the first dielectric layer; andat least one partial opening formed in the dielectric stack, wherein the at least one partial opening is formed in at least a portion of the first dielectric layer;the solar cell further comprising: one or more metal contacts disposed on the back face of the solar cell.

14. The solar cell of claim 13 wherein within the at least one partial opening, the first dielectric layer has a thickness of at least a few monolayers,

15. The solar cell of claim 13 wherein within the at least one partial opening, the first dielectric layer has a thickness between 1 nanometer (nm) and 30 nm.

16. The solar cell of claim 13 wherein the second dielectric layer comprises Silicon Nitride (SiNx).

17. The solar cell of claim 13 wherein the back face of the solar cell comprises a metallization layer.

18. The solar cell of claim 17 wherein the metallization layer comprises aluminum (Al).

19. The solar cell of claim 17 wherein the solar cell further comprises a backsurface field (BFT) formation, wherein the BFT formation is formed on areas of the solar cell not including the at least one partial opening.

20. A solar cell having a front face and a back face, the solar cell comprising: a dielectric stack disposed between the front face and the back face of the solar cell, the dielectric stack comprising: a first dielectric layer having a top surface and a bottom surface, the first dielectric layer comprising Aluminum Oxide (AlOx);a layer of p-type silicon disposed over at least a portion of the top surface of said first dielectric layer; anda second dielectric layer disposed over a bottom surface of said first dielectric layer; andwherein said dielectric stack is provided having at least one partial opening and the at least one partial opening is formed in at least a portion of said first dielectric layer; andone or more metal contacts disposed on the back face of the solar cell.