Patent Application
20200055151
This application claims priority from European Patent Application No. 18189313.2 filed Aug. 16, 2018, the disclosures of which are incorporated herein by reference in their entirety.
The present invention relates to a method of manufacturing a welding stud. More specifically, the present invention is directed to a method of manufacturing welding studs made of two different materials.
Welding studs are used, notably in the automotive industry, to fix studs onto the surface of workpieces. For example, the welding studs are fastened in a welding process onto a part of a chassis, wherein the welded stud is welded by its welding part to the chassis part, and components are then fastened onto a function part of the welding stud by use of nuts or clamps.
In many areas of technology, the focus is on lightweight assemblies and constructions. In particular light weight material are used. Lightweight materials might be for example high-strength steel, aluminum, or glass fiber-reinforced polymer composites and may be used replacing heavy steel materials. Such materials can decrease component weight by 10 to 60 percent. In light-weight car bodies, lightweight materials are used as construction materials, notably to reduce the fuel consumption. However, the strength of some of these materials, for example the aluminum alloy is considerably lower than the strength of heavy steel. The lack of strength is problematic when releasable connections of components are to be made. Therefore, such interface are still often made with steel. On the other side, aluminium material can be easily welded to a workpiece, but the welding of heavy steel may be more difficult.
In order to provide a light welding stud easily weldable, document EP1207000 discloses a welding stud comprising a welding portion and a function portion. The welding portion is made of lightweight material and the function portion is made of steel. The function portion has a tip which engages complementary recess of the welding portion and the tip and the recess are connected by a friction welding connection.
The connection by friction welding of materials such like aluminum alloy and steel might be brittly, notably due to the formation of intermetallic phase seams. The contact between the two portions is not always secured, in particularly under vibrating load. Besides, a risk of corrosion may occur. Finally, the friction welding connection enable only few shape or cross-section shape of the portions.
It is hence an object of the present invention to at least alleviate the aforementioned shortcomings. More particularly one objective of the present invention is to provide a method of easily manufacturing a light welding stud, resistant to corrosion, with a good sealing and a secured connection between the two parts or portions.
To this aim, according to the invention, it is provided a method of manufacturing a welding stud adapted to be welded to a workpiece and comprising a welding portion of light metal and a function portion of steel, characterized by the following steps:
a. Providing a welding part of light material, wherein the welding part comprises one of a recess or a protrusion;
b. Providing a function part of steel comprising the other of the recess or protrusion;
c. Providing a press with a die and a punch;
d. Arranging the welding part and the function part together such that the protrusion cooperates with the recess;
e. Manufacturing the welding stud by pressing the welding part and the function part into the die by the punch such that the protrusion cooperates with the recess to form the welding stud with the welding part forming the welding portion and the function part forming the function portion.
The welding stud is made of two different materials allowing an assembly of the welding stud to different components, without reducing the strength or the torques which might apply to the function part. The manufacture of the hybrid welding stud is done by cold forming and more particularly through impact extrusion. The welding part and the function part are securely connected to each other. The manufacture is easy to implement.
In an embodiment, the function part comprises a shank extending along a longitudinal axis, a press-fit area and a flange arranged between the shank and the press-fit area, wherein the flange extends radially outwardly from the shank. Thus, the flange forms a first supporting surface facing the shank and an abutment surface for the welding part or welding portion opposite the supporting surface.
In an embodiment, the shank comprises a threaded portion. The threaded portion allows the fixation of different components. The impact extrusion is still possible.
In an embodiment, the punch is connected to the shank and wherein the welding part is arranged on the die. The welding part can easily be arranged on the die.
In an additional embodiment, the press-fit area is the protrusion and the protrusion comprises a frusto conical shape with the smaller-diameter end extending from the flange and the larger-diameter end arranged in the recess. The frusto conical shape allows a better junction of the parts.
In an additional embodiment, the outer surface of the protrusion extends with an angle between 2 and 7 deg. with regard to the longitudinal axis. For example, the angle is of 5 degrees. This angle allows an improved assembly.
In an embodiment, the die comprises a die recess with a chamfered edge. The chamfered edge allows a better disassembly of the welding stud from the die and also to create a chamfered area on the welding stud.
In an embodiment, the press-fit area is a recess. The recess is adapted to cooperate with a protrusion from the function part. The welding part thus forms a sleeve.
In an embodiment, the recess is defined by lateral walls, wherein the lateral walls comprise an inner surface, an outer surface, wherein the inner surface extends sensibly parallel to the longitudinal axis, wherein the outer surface extends radially outwardly tapered from the flange. Thus, the lateral walls, in cross section have a triangle shape.
In an embodiment, the welding stud is formed by pressing the lateral walls toward the longitudinal axis when the function part extends in the recess such that the free ends of the lateral walls anchor in the function part.
In an embodiment, the die comprises a die recess closed by an ejector pin. The ejector pin allows to better disassemble the welding stud from the die and to improve the process speed.
In an embodiment, the ejector pin is tapered to form a tip on the function portion during the press of the function part.
In an embodiment the welding part is in aluminium material. The aluminium material (or aluminium alloy) comprises good welding properties.
The present invention is further directed to a welding stud realized according to the above-mentioned method.
Other characteristics and advantages of the invention will readily appear from the following description of embodiments, provided as non-limitative examples, in reference to the accompanying drawings.
On the different figures, the same reference signs designate identical or similar elements.
For instance, the welding portion 12, 12′ is made of a good weldable material such as aluminium alloy, whereas the function portion is made of steel material.
The welding portion 12, 12′ is made from a welding part 120, 120′, whereas the function portion 14 comes from a function part 140, 140′. The welding part is made in a first material, and notably in light-weight material such as aluminium. The function art is made of steel.
More particularly, in order to manufacture the welding stud of
For instance, for the welding stud 10 of
Before the cold forming process, the welding part 120 and the function part 140 are independent from each other. After the cold forming process, both parts are fixedly joined to each other.
As illustrated in
The welding portion 12, 12′ comprises a rear section 20, 20′ opposite the top section 16, 16′. The rear section 20, 20′ is adapted to face the function portion 14, 14′.
The top section 16, 16′ is formed by a top section 160, 160′ of the welding part 120, 120′. The rear section 20, 20′ is formed by a rear section 200, 200′ of the welding part 120, 120′.
In the first embodiment, illustrated in
In the embodiment of
The shank 141 comprises a screwthread portion.
The press-fit area 142 is a protrusion. More particularly the press-fit area 142 is formed by the continuity of the shank beyond the flange. For instance, the protrusion comprises a frusto conical shape with the smaller-diameter end extending from the flange and the larger-diameter end being a free end. The protrusion comprises a protrusion length Lp along the longitudinal axis X. The outer surface of the protrusion extends with an angle between 2 and 7 deg. with regard to the longitudinal axis. For example, the angle is of sensibly 5 degrees.
The protrusion is adapted to be arranged in the recess 22 just before the cold forming process, as illustrated in
For the impact extrusion process, the welding part 120 is arranged in the die D (or a mold). The die is for example located on a mechanical or hydraulic press. More particularly, the die D has an inner wall defining an extrusion cavity C. The cavity C comprises a bottom end. The shape of the extraction cavity corresponds to the size required for the generation of the welding portion.
The bottom end can include a protruding point for generating a dimple in the welding portion. The bottom end can be partially or completely formed by an ejector pin 150, allowing a better ejection of the welding stud once formed.
The free end of the inner wall can be chamfered, allowing a better cold forming and a better ejection. The welding part is disposed for instance on the chamfered edge.
The press comprises also the punch P. The punch P is securely connected to the function part 140, such that the punch and the function part form together a punching unit. A portion of the punching unit is receivable in the die D. More particularly, the protrusion is receivable in the die D. The manufacture of the welding stud can be performed by advancing the punching unit into the recess 220 with sufficient force to extrude metal from the welding part between the punching unit and the die to form the desired welding portion, as depicted in
More particularly, after the cold forming, the welding portion 12 entirely surrounds the protrusion and abuts against the flange 142. The shape and the size of the recess gives the shape and the size of the welding portion formed. The chamfered edge allows the welding portion 12 to form a slope in the direction of the flange, such that the surface of the flange facing the protrusion is entirely covered by the welding portion. The thickness of the welding portion around the protrusion is sensibly constant. The bottom of the welding portion (which forms the top section 16) is thick enough to be welded to a workpiece without undamaging or interfering with the function portion.
In the first embodiment, the cold forming modifies the shape of the welding part 120 to form the welding portion 12, whereas the shape of the function part 140 remains sensibly unchanged and corresponds to the shape of the function portion 14.
In the second embodiment, in reference to
As illustrated in
The welding part 120′, in the second embodiment is a token having a first section 121′ with a first diameter adapted to be inserted in the recess of the function part, and a second section 122′ with a second diameter, larger than the first diameter and adapted to remain outside the recess. The first diameter and the recess diameter are substantially similar. The interface between the first section and the second section forms an elbow 123′ and the edge of the lateral walls of the function part is adapted to rest against said elbow.
During the cold forming, the lateral walls W of the recess are pressed radially in the direction of the token, and more particularly in the direction of the first section. By pressing the lateral walls in the direction of the first section, the token is deformed. The free end of the lateral wall W anchors in the first section. The deformation of the function part 140′ can be such that, the outer surface of the lateral wall extends sensibly parallel to the longitudinal axis X after the cold forming. For instance, after the cold forming, the inner surface of the lateral wall defines in cross section an angle h.
During the impact extrusion, it is to be noted that the flange 142′ and more particularly the support surface of the flange facing the shank 141′ is not deformed. Thus, the diameter of the flange Df remains unchanged before and after cold forming. For this purpose, the diameter of the second section of the token Db, the diameter of the flange Df, the end diameter of the lateral wall after deformation Dd, and the thickness of the flange along the lateral axis X are specially matched to one another. For instance, as depicted in the drawings, the end diameter of the lateral wall after deformation Dd is greater than the diameter of the flange Df. Besides, the end diameter of the lateral wall after deformation Dd is greater than the diameter of the second section of the token Db. The recess diameter is smaller than the end diameter of the lateral wall after deformation Dd. More particularly, the ratio between the recess diameter (or the first diameter) and the end diameter of the lateral wall after deformation Dd is between 0.2 and 0.9. For instance the ratio is of 0.8.
The angle g is chosen so that it generates sufficient pressure in the formed state (angle h) to hold the token in the function part. The angle g is for example between 15 and 35 degrees, or between 20 and 30 degrees and more particularly the angle g may be of 26 degrees.
The longitudinal length f between the supporting surface of the flange 141′ and the outside edge of the second section of the welding part is to be matched with the final length e between the supporting surface of the flange 141′ and the outside edge of the second section 122′ of the welding portion.
By increased torsional loading, the functional part 140′ (more particularly in the recess) and the welding part 120′ (only the first section 121′, not the second section designed to form the welding nugget) can be arranged with a particular contour, which avoids twisting of the aluminium to steel component under torque loading, e.g. hexagonal shaper, internal serration, hexagon or octagon. Alternatively, the cold forming operation may be performed on the outer surface of the lateral wall to create for instance a polygon contour. The shape is then transferred from the function portion 14′ to the welding portion 12′ and thus a positive connection of the function parts and welding parts is generated and prevents rotation of the components to each other.
Although exemplary embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes may be made to these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.