The present invention relates to a method of manufacturing a wheel rim for a vehicle and, more particularly, a method of manufacturing a wheel rim for a vehicle having a non-constant thickness from a tubular material.
Patent Document 1 discloses one example of a vehicle wheel rim having a non-constant thickness from a plate material having a constant thickness. In the manufacturing method of the wheel rim having a non-constant thickness of Patent Document 1, a cylindrical hollow material having a constant thickness is manufactured from a flat plate material having a constant thickness, and then the cylindrical material is formed to a cylindrical hollow member having a non-constant thickness by flow-forming such as a flow-turning, spinning, etc. The cylindrical member is roll-formed to a wheel rim configuration so that the vehicle wheel rim having a non-constant thickness is manufactured.
However, there are the following problems with the manufacturing method of the vehicle wheel rim having a non-constant thickness using flow-forming:
(i) The equipment used in the flow-forming may be expensive.
In flow-forming, since a roll for pressing the tubular material to a mandrel may be moved in two directions, an axial direction of the material and a thickness direction of the material, the flow-forming equipment may be expensive multiple times as compared with an ironing apparatus where a punch may be moved in only one direction.
(ii) Productivity of the flow-forming may be low.
The productivity of flow-forming may be about one third of that of forming using an ironing apparatus. If a rim manufacturing line is diverged to three subsidiary lines and each of the three subsidiary lines is provided with flow-forming equipment, the problem of productivity will be solved. However, since three sets of flow-forming equipment must be provided, the equipment cost and the amount of space for equipment placement are three times of those of a single set of flow-forming equipment.
(iii) Pushing flaws made by the flow-forming roll may remain at a surface of the material, and the appearance quality decreases.
An object of the invention is to provide a method of manufacturing a wheel rim for a vehicle which can achieve at least one of (i) decreasing an equipment cost, (ii) improving a productivity and (iii) improving an appearance quality.
The present invention capable of achieving the above object is as follows:
(1) A method of manufacturing a wheel rim for a vehicle comprising:
ironing a tubular material to a tubular member having a non-constant thickness using an ironing apparatus which has a punch, a die having a convex and concave surface opposing the punch and a pressing member,
wherein the ironing comprises:
wherein when the tubular member is formed to a configuration of a wheel rim for a vehicle after the ironing at least a portion of the flange portion of the tubular material is formed to one of the flange portions of the rim of the wheel rim for a vehicle.
(2) A method of manufacturing a wheel rim for a vehicle according to item (1) above, wherein the flange portion of the tubular material has one or more axially intermediate bent portions.
(3) A method of manufacturing a wheel rim for a vehicle according to item (2) above, wherein a bending direction of at least one of the one or more axially intermediate bent portions and a bending direction of the bent portion are opposite to each other.
(4) A method of manufacturing a wheel rim for a vehicle according to item (2) or (3) above, wherein the axially intermediate bent portions are formed before the ironing and/or at the squeezing of the ironing.
(5) A method of manufacturing a wheel rim for a vehicle according to item (1) above, wherein at the ironing, the tubular material is received and pushed by an ejecting plate at an end of the tubular material opposite the flange portion of the tubular material.
(6) A method of manufacturing a wheel rim for a vehicle according to item (1) above, wherein the convex and concave surface is formed by providing at least one convex portion making a space between the die and the punch narrower than a thickness of the tubular material, at the die in an axial direction of the die along the side surface of the die opposing the punch.
(7) A method of manufacturing a tubular member according to item (1) above, wherein the convex and concave surface is formed by providing at least one convex portion making a space between the die and the punch narrower than a thickness of the tubular material, at the die in a circumferential direction of the die along the side surface of the die opposing the punch.
(8) A method of manufacturing a wheel rim for a vehicle according to item (1) above, further comprising roll-forming the tubular member having a non-constant thickness to a vehicle wheel rim configuration after the ironing.
According to the method of manufacturing a wheel rim for a vehicle according to item (1) above, since the tubular material is formed into the tubular member having a non-constant thickness by ironing, an equipment and a step of the conventional flow-forming may be unnecessary. As a result, the above-described problems (i), (ii) and (iii) existing in the flow-forming may be solved as the following ways (i), (ii) and (iii), respectively:
(i) Since the conventional flow-forming equipment may be replaced by the die and punch for ironing and the ironing apparatus in the present invention, and the combined cost of the die and punch for ironing and the ironing apparatus may be lower than that of the flow-forming equipment, the equipment cost may be decreased.
(ii) Since in the step of making the thickness of the material non-constant, the flow-forming may be replaced by ironing performed using the ironing apparatus in the present invention, a time period for making the thickness of the tubular material non-constant may be decreased to about one third of the time period required in the flow-forming, and the productivity may be improved. When a step of making a thickness of a cylindrical hollow material non-constant is provided to one rim manufacturing line, three sets of flow-forming equipment may be necessary to be provided in the conventional line. However, since the three sets of flow-forming equipment can be replaced by a single ironing apparatus according to the present invention, the problems relating to the costs and the space for placing equipment may be solved.
(iii) Since flow-forming may be replaced by ironing conducted using the punch and the die, any pushing flaw due to the flow-forming roll may not remain at the surface of the tubular member, and an appearance quality may be improved.
Further, since at the ironing, after squeezing the flange portion of the tubular material by the pressing member and the die, at least a portion of the tubular material except the flange portion of the tubular material is ironed, the tubular material may be suppressed from being drawn into the die by the punch and moved relative to the die. As a result, forming with a high accuracy may be possible.
According to the method of manufacturing a wheel rim for a vehicle according to item (2) above, since the flange portion of the tubular material has one or more axially intermediate bent portions, even if the bending angles of the bent portion and the axially intermediate bent portions are small, the tubular material may be more resistant to being drawn into the die by the punch and moved relative to the die than in a case where the flange portion of the tubular material does not have axially intermediate bent portions. Further, when the bending angles are small, forming at succeeding steps may be easy.
According to the method of manufacturing a wheel rim for a vehicle according to item (3) above, since a bending direction of at least one of the one or more axially intermediate bent portions and a bending direction of the bent portion are opposite to each other, a portion of the flange portion of the tubular material located on a tip side of the axially intermediate bent portion whose bending direction is opposite to the bending direction of the bent portion may engage with the pressing member, whereby the tubular material may be more resistant to being drawn into the die by the punch and moved relative to the die during ironing, differently from a case where a bending direction of each of the one or more axially intermediate bent portions and a bending direction of the bent portion are the same.
According to the method of manufacturing a wheel rim for a vehicle according to item (4) above, since the one or more axially intermediate bent portions are formed before the ironing and/or at the squeezing of the ironing by bending one or more axially intermediate portions of the flange portion of the tubular material, the tubular material may be more resistant to being drawn into the die by the punch and moved relative to the die than a case where the axially intermediate bent portions are not formed at the flange portion of the tubular material.
According to the method of manufacturing a wheel rim for a vehicle according to item (5) above, since at the ironing, the tubular material is received and pushed by an ejecting plate at an end (an axially opposite end) of the tubular material opposite the flange portion of the tubular material, the tubular material may be more resistant to being drawn into the die by the punch and moved relative to the die.
According to the method of manufacturing a wheel rim for a vehicle according to item (6) above, since the convex and concave surface is formed by providing at least one convex portion making a space between the die and the punch narrower than a thickness of the tubular material, at the die in an axial direction of the die along the side surface of the die opposing the punch, a tubular member having a thickness that changes along the axial direction may be manufactured.
According to the method of manufacturing a wheel rim for a vehicle according to item (7) above, since the convex and concave surface is formed by providing at least one convex portion making a space between the die and the punch narrower than a thickness of the tubular material, at the die in a circumferential direction of the die along the side surface of the die opposing the punch, a tubular member having a thickness that changes along the circumferential direction may be manufactured.
According to the method of item (8) above, since the method has a step of roll-forming the tubular member having a non-constant thickness to form a vehicle wheel rim configuration after the ironing step, it is possible to manufacture a vehicle wheel rim which has a non-constant thickness and is light.
(a) illustrates a tubular material,
(b) illustrates a flange portion forming step,
a left half of (b) illustrating a case where forming only a flange portion of the tubular material is conducted, and
a right half of (b) illustrating a case where both forming a flange portion of the tubular material and forming an axially intermediate bent portion are conducted,
(b′) illustrates a tubular material after the flange portion forming step,
a left half of (b′) illustrating a case where forming only a flange portion of the tubular material is conducted, and
a right half of (b′) illustrating a case where both forming a flange portion of the tubular material and forming an axially intermediate bent portion are conducted at the flange forming step,
(c) illustrates an ironing step,
a left half of (c) illustrating a state before ironing where the flange portion of the tubular material is squeezed between a pressing member and a die, and
a right half of (c) illustrating a state after ironing, and
(c′) illustrates a tubular member having a non-constant thickness after ironing,
a left half of (c′) is a cross-sectional view of the tubular member, and
a right half of (c′) is a front view of the tubular member.
(a) illustrates a step of rounding a plate material having a constant thickness to form a rounded material and then welding opposite ends of the rounded material to manufacture the tubular material, and
(b) illustrates a step of cutting the pipe-like material to a predetermined length to manufacture the tubular material.
(a) illustrates a tubular member having a non-constant thickness before flaring, an upper half of (a) being a side view of the tubular member and a lower half of (a) being a cross-sectional view of the tubular member,
(b) illustrates a tubular member having a non-constant thickness after flaring, an upper half of (b) being a side view of the tubular member and a lower half of (b) being a cross-sectional view of the tubular member,
(c) is a side view of an upper roll and a lower roll between which a wall of the tubular member having a non-constant thickness is disposed, where the tubular member is shown in cross section (and an upper half of the upper roll is not shown),
(d) is a side view of the upper roll and the lower roll between which the wall of the tubular member having a non-constant thickness is roll-formed, where the tubular member is shown in cross section (and an upper half of the upper roll is not shown),
(e) is a front view of the upper roll and the lower roll between which the wall of the tubular member having a non-constant thickness is roll-foimed, (where an upper half of the upper roll is not shown) and
(f) is a cross-sectional view of the wheel rim for a wheel after roll-forming.
A method of manufacturing a wheel rim for a vehicle according to the present invention will be explained with reference to the drawings.
Portions common to all embodiments of the present invention are denoted with the same reference numerals throughout all embodiments of the present invention.
First, portions common to the all embodiments of the present invention will be explained.
As illustrated in
As illustrated in
(a) a flange portion forming step for bending an axial end portion of the tubular material 4 having a constant thickness in a direction crossing an axial direction of the tubular material 4, thereby forming in the tubular material 4 a bent portion 8 and a flange portion of the tubular material 9 on an end side of the bent portion 8; and
(b) an ironing step for manufacturing the tubular member 10A having a non-constant thickness using an ironing apparatus 20 including a punch 26, a die 22 having a convex and concave side surface 24 opposing the punch 26, and a pressing member 23.
Step (b) above may include steps of: causing the tubular material 4 to axially engage the die 22 at the flange portion of the tubular material 9; then moving the pressing member 23 relative to the die 22 thereby squeezing the flange portion of the tubular material 9 between the pressing member 23 and the die 22; and then moving the punch 26 relative to the die 22 thereby ironing at least a portion of the tubular material 4 except the flange portion of the tubular material 9 and manufacturing the tubular member 10A.
In (c) of
There is no particular limitation to the size (i.e., an axial length and an outer diameter) of the tubular material 4. However, to be used on a variety of vehicles (i.e., on a car or a truck) the tubular material 4 used to form on wheel rims may have an axial length of 76 mm-265 mm or 150 mm-230 mm. Further, an outer diameter of the tubular material 4 may be 177 mm-600 mm, or may be 280 mm-580 mm.
When the tubular material 4 includes the flange portion of the tubular material 9 and can engage the die 22 such as a case where the tubular material 4 is a cast member, the flange portion forming step may not be required.
Before the forming of the flange portion of the tubular material 9, as illustrated in
In the tubular material manufacturing step, as illustrated in (b) of
It may be conceived to burr (pierce-burr) a flat plate material to form a burred protrusion and to use the burred protrusion as a tubular material 4. However, if a hole caused in the flat plate material during the burring is enlarged in diameter to an extent that the burred protrusion can be used as the tubular material 4 for a wheel rim (for a car or a truck), a crack may be generated in the burred protrusion. Therefore, such a burred protrusion accompanied by a crack cannot be used as the tubular material 4.
In a case where a flange portion of the tubular material 9 is formed in the tubular material 4 during or after the flange portion forming step as illustrated in (b) of
The thickness of the tubular material 4 may be 2.0 mm-8.0 mm, or 2.3 mm-6.0 mm. The thickness of the tubular material 4 may not be limited to the range and can be selected freely.
In the flange portion forming step, the flange portion of the tubular material 9 may be a bent portion (e.g., a curved portion), bent (e.g., curved) at an angle smaller than 90 degrees from an axial direction of the tubular material 4. At least a portion of the flange portion of the tubular material 9 may extend in a direction crossing the axial direction of the tubular material 4. The flange portion of the tubular material 9 operates to engage the die 22 and to position the tubular material 4 relative to the die 22 in the axial direction of the tubular material at the ironing step and contributes to prevent the tubular material 4 from being dislocated relative to the die 22 in the axial direction.
One or more axially intermediate bent portions 9a may be formed at the flange portion of the tubular material 9. In the right portion of (b) in
Each of bending angles of the bent portion 8 and the axially intermediate bent portion 9a may be equal to or larger than 90 degrees. However, in a case where an end portion of the tubular member 10A is required to be re-formed as in the case where the tubular member 10A having a non-constant thickness is formed to a wheel rim configuration at a roll-forming step after the ironing step, the re-forming may be difficult, or it may be necessary to remove the flange portion of the tubular material 9 from the tubular member 10A. By forming the axially intermediate bent portion 9a, even if the bending angles of the axially intermediate bent portion 9a and the bent portion 8 are relatively small (e.g., smaller than 90 degrees), the tubular material 4 is prevented from being drawing by the punch 26 during the ironing step and the roll-forming is easy.
In the ironing step, the tubular material 4 having a constant thickness (having the bent portion 8 and the flange portion of the tubular material 9) is set in the die 22 such that the tubular material 4 axially engages the die 22 by the flange portion of the tubular material 9. Then, the ironing apparatus 20 is operated whereby the pressing member 23 and the punch 26 are moved relative to the die 22 (to approach the die) only in the axial direction of the tubular material 4. When the pressing member 23 and the punch 26 are moved relative to the die 22, the pressing member 23 first contacts the flange portion of the tubular material 9 set in the die 22, thereby squeezing the flange portion of the tubular material 9 between the pressing member 23 and the die 22 (i.e., pressing the flange portion of the tubular material 9 to the die 22 by the pressing member 23), and the pressing member 23 stops. The punch 26 further moves relative to the die 22 (approaches the die) only in the axial direction of the tubular material 4, thereby ironing the portion of the tubular material 4 except the flange portion of the tubular material 9 by the convex and concave surface 24 of the die 22 and the punch 26, accompanied by a change in the diameter and the thickness of the tubular material 4.
Ironing increases the hardness of tubular material 4 due to work hardening and improvements in resistance and fatigue strength are obtained. Where the tubular material 4 is made from steel, the ironing rate (i.e., (a thickness before ironing−a thickness after ironing)/a thickness before ironing×100) may be equal to or smaller than 60%. If the ironing rate is larger than 60%, galling or cracking may be caused in the tubular member 10A. However, ironing at an ironing rate larger than 60% may be conducted.
While the tubular material 4 is ironed, the tubular material 4 is gradually lengthened (extended) in a moving direction of the punch 26.
Where a force required for the ironing is small, the pressing member 23 may be removed.
A lubrication treatment (e.g., phosphate coating, a lubricating oil coating, etc.) may be applied to the tubular material 4 before ironing or during ironing. This may suppress seizure and scratching. However, ironing may be conducted without the lubrication treatment.
The ironing apparatus 20 may be installed in a stamping machine 30 as shown in
The ram drive apparatus 34 of the stamping machine 30 can be a hydraulic press apparatus using a hydraulic cylinder, a mechanical press apparatus using a motor and a crank shaft, or a servo drive press apparatus using a servo motor and a ball screw. The plate drive apparatus 42 can be a hydraulic cylinder, an air cylinder, or an elevator mechanism using an electric motor.
The die 22 may be fixed and the punch 26 may be movable. As illustrated in (c) of
(a) by providing at least one convex portion 24a convex toward the protrusion 28 of the punch 26 relative to a portion (i.e., a concave portion 24b) located adjacent to the convex portion 24a along the side surface of the die 22 in an axial direction of the die as illustrated in
(b) by providing at least one convex portion 24a convex toward the protrusion 28 of the punch 26 relative to a portion (i.e., a concave portion 24b) located adjacent to the convex portion 24a along the side surface of the die 22 in a circumferential direction of the die as illustrated in
(c) by a combination of items (a) and (b) above.
A protruding amount of the convex portion 24a may be determined by an objective thickness of a corresponding portion of the wheel rim 10B for a vehicle (tubular member 10A) and may be constant or non-constant over each convex portion 24a. Further, in a case where a plurality of convex portions 24a are provided, protruding amounts of the respective convex portions 24a may be determined by objective thicknesses of corresponding portions of the wheel rim 10B for a vehicle (tubular member 10A), and the protruding amounts of the respective convex portions 24a may be equal or not equal to each other. The convex portion 24a may be provided at a portion or all portions of the side surface of the die 22 opposing the protrusion 28 of the punch 26.
As illustrated in
Further, in the axial direction of the die 22 along the side surface of the die, one convex portion 24a and a concave portion 24b, which is located ahead of the ejecting plate 40 in a moving direction of the ejecting plate 40 during ejecting the tubular member 10A from the die 22 and is adjacent to the one convex portion 24a, may be connected via a second inclined surface 24c2 which is not perpendicular to the axis of the die 22. The reason why the inclined surface 24c2 is provided is that, compared with a surface perpendicular to the axis of the die, a plastic flow of material due to ironing during the ironing may be easier.
Angles of the first inclined surface 24c1 and the second inclined surface 24c2 inclined from the axial direction of the die 22 along the side surface of the die 22 may be set at an angle equal to or smaller than 60 degrees, or equal to or smaller than 45 degrees, or equal to or smaller than 20 degrees, and or equal to or smaller than 10 degrees. The reason why the angle may be equal to or smaller than 10 degrees is that generation a scratches in the tubular member 10A due to ironing can be suppressed. An inclination angle relative to the axial direction of the side surface of the die 22, of a second inclined surface 24c2 located closest to the flange portion of the tubular material 9 may be larger than 60 degrees. An inclination angle of each first inclined surface 24c1 may be constant, or may change gradually. An inclination angle of each second inclined surface 24c2 may be constant, or may change gradually.
The punch 26 may have the protrusion 28 protruding toward the die 22 at a fore end portion of the punch moved toward the die 22 and irons the tubular material 4 by the protrusion 28. The flange portion of the tubular material 9 except in the vicinity of the bent portion 8 is not contacted by the punch 26 and is not ironed.
An end portion of the tubular material 4 opposite the flange portion of the tubular material 9 may be thinned or may not be thinned corresponding to whether or not the protrusion 24a of the die 22 is provided. More particularly, when the protrusion 24a is provided at a portion of the die 22 corresponding to the end portion of the tubular material 4 opposite the flange portion of the tubular material 9, as illustrated in
By stopping movement of the punch 26 relative to the die 22 when the protrusion 28 reaches an axially intermediate portion of the tubular material 4 and then drawing out the punch 26 from the die 22, as illustrated in
The ejecting plate 40 receives (supports) the tubular material 4 (in the axial direction of the tubular material 4) from a direction opposite to the direction in which the punch 26 moves during ironing (i.e., the direction in which the punch 26 pushes the tubular material 4), in order that the axial end portion of the tubular material 4 opposite the flange portion of the tubular material 9 extends axially more than an expected extending amount during ironing and is offset from an expected position relative to the die 22. Though the axial length of the tubular material 4 is gradually lengthened when the tubular material 4 is ironed, a position of the ejecting plate 40 is controlled by the plate drive apparatus 42 and the ejecting plate 40 recedes according to a change in the axial length of the tubular material 4, so that the ejecting plate 40 can push the tubular material 4 in the axial direction at a constant force, or at a substantially constant force, during ironing.
The load on the ejecting plate 40 may be controlled, or the amount of displacement of the ejecting plate 40 may be controlled.
By fixing the ejecting plate 40 at a predetermined position and receiving the tubular material 4 by the ejecting plate 40, it is possible to restrict a change in the axial length of the tubular material 4 and to keep the axial length of the tubular material.
As illustrated in (c) of
The ejecting plate 40 pushes the tubular member 10A in the direction opposite the direction in which the punch 26 moves (i.e., the direction in which the punch 26 pushes the tubular material 4) during ironing. The axial force which the ejecting plate 40 imposes on the tubular member 10A when removing the tubular member 10A may be equal to or larger than a force necessary to deform the tubular member 10A in the radial direction of the tubular member, thereby removing the tubular member 10A when the ejecting plate 40 axially pushes the tubular member 10A. The force is much smaller than the ironing force with which the punch 26 axially pushes the tubular material 4. Since the die 22 is not required to be divided in the circumferential direction of the die to remove the tubular member 10A, the die 22 may not be divided and may be constructed as an integral die.
The tubular member 10 having a non-constant thickness may include a thick portion (a portion where the thickness is not thinned) and a thin portion (a portion where the thickness is thinned). The thick portion (a portion not thinned in thickness) of the tubular member 10 may correspond to a portion where a large force is imposed (e.g., in the case of a wheel rim, a curved portion and a flange portion of the rim) during use of the final product. The thin portion (a portion thinned in thickness) may correspond to a portion where a small force is imposed (in the case of the wheel rim, a portion other than the curved portion and the flange portion of the rim) during use of the final product. Owing to the structures, lightening, material savings and cost reduction are obtained while maintaining a necessary strength and rigidity in the final product.
As illustrated in
As illustrated in (a) and (b) of
As illustrated in (c), (d) and (e) of
The wheel rim 10B for a vehicle after forming may include a flange portion of the rim 10a, a bead seat portion 10b, a side wall portion 10c, a drop portion 10d, a side wall portion 10e, a bead seat portion 10f and a flange portion of the rim 10g, in that order from one axial end to the other axial end of the rim. A wheel disk (not shown) may be fit into the rim 10B for a vehicle and then welded to the rim, whereby a wheel of a weld type is manufactured. Curved portions may exist between the above-listed portions of the rim. Larger stresses may be generated at the curved portions and the flange portions of the rim 10a and 10g than stresses generated at other portions. Preferably, the thicknesses of the curved portions and the flange portions of the rim 10a and 10g are larger than thicknesses of other portions. The roll-formed wheel rim 10B for a vehicle may be such a wheel rim as illustrated in
When a tubular material 4 having a constant thickness is formed into a wheel rim, conventionally, the constant thickness of the tubular material has not been formed to a non-constant thickness by ironing. Conventionally, the tubular material having a constant thickness is conveyed, as it is, to a rim configuration forming step that uses roll-forming. Even if the tubular material having a constant thickness is formed to a tubular material having a non-constant thickness, conventionally, any method other than spinning has not been considered for use as explained in the background, and in fact, has not been used. In the present invention, the ironing step is inserted between the step of manufacturing the tubular material 4 and the step for roll-forming the tubular member 10A, thereby making the tubular material 4 non-constant in thickness without using spinning.
Operations and technical advantages of portions common to all embodiments of the present invention will now be explained.
In the present invention, since the tubular material 4 having a constant thickness is formed into the tubular member 10A having a non-constant thickness by ironing, the equipment and the step of conventional flow-forming may not be required to be provided. As a result, the afore-mentioned problems (i), (ii) and (iii) accompanied by the flow-forming may be solved as the following ways (i), (ii) and (iii), respectively:
(i) Since the conventional flow-forming equipment may be replaced by the die 22 and punch 26 for ironing and the ironing apparatus 20 (the stamping machine 30) in the present invention and the combined cost of the die 22 and punch 26 for ironing and the ironing apparatus 20 (the stamping machine 30) may be lower than that of the flow-forming equipment, the equipment cost may be decreased.
(ii) Since in the step of making the thickness of the tubular material 4 non-constant, the conventional flow-forming step may be replaced by the ironing step using the ironing apparatus 20 (the stamping machine 30) in the present invention, a time period for making the thickness of the tubular material 4 non-constant may be decreased to about one third of the time period required in the flow-forming, and the productivity may be improved. When a step of making a thickness of a cylindrical hollow material non-constant is provided to one rim manufacturing line, three sets of flow-forming equipment may be required to be provided in the conventional rim manufacturing line. However, since the three sets of the flow-forming equipment may be replaced by a single ironing apparatus 20 (the stamping machine 30) according to the present invention, the problems relating to a cost and a space required for placing the equipment existing in the flow-forming may be solved.)
(iii) Since the flow-forming is replaced by the ironing using the punch 26 and die 22, any pushing flaw due to the flow-forming roll may not remain at a surface of the material, and an appearance quality may be improved.
Since the punch 26 may be moved relative to the die 22 and the tubular material 4 may be ironed to form the tubular member 10A having a non-constant thickness, a movement of the punch 26 relative to the die 22 may be an axial movement only, accompanied by no radial movement, so that a stamping machine 30 may be used for the uni-directional movement of the punch 26 relative to the die 22. As a result, the time period of forming may be reduced and the equipment cost may be decreased.
Since after manufacturing the tubular member 10A having a non-constant thickness, the tubular member 10A may be taken out from the die 22 by adding an axial force to the tubular member 10A so that the tubular member 10A is deformed in the radial direction of the tubular member 10A, an integral die which is not divided in a circumferential direction may be used for the die 22. As a result, the equipment cost may be maintained low as compared with a case where a circumferentially divided die is used, because a mechanism for moving divided die elements in a radial direction is unnecessary to be provided. Further, no burr will be generated at a portion of the ironed tubular member corresponding to a butting portion of the circumferentially divided die elements, and no work for removing burrs will be necessary.
Since in the ironing step the flange portion of the tubular material 9 is caused to axially engage the die 22 and then the ironing is conducted, the tubular material 4 may be prevented from being moved as a whole in the direction in which the punch 26 pushes the tubular material 4 so that forming with a high accuracy may be possible.
Since the flange portion of the tubular material 9 is squeezed between the die 22 and the pressing member 23 during ironing and then at least a portion of the tubular material 4 other than the flange portion of the tubular material 9 is ironed, the tubular material 4 may be prevented from being moved as a whole in the axial direction in which the punch 26 pushes the tubular material 4, so that forming with a high accuracy may be possible.
The flange portion of the tubular material 9 is not thinned due to ironing, because the flange portion of the tubular material 9 except a vicinity of the bent portion 8 is not ironed. Since the flange portion of the tubular material 9 comes to the flange portion of the rim 10a (or 10g) after roll-forming, the flange portion of the tubular material may be maintained relatively thick when formed to a wheel rim 10B for a vehicle. As a result, durability of the wheel rim for a vehicle may be improved.
Since one or more axially intermediate bent portions 9a may be formed in the flange portion of the tubular material 9 at the flange portion forming step before the ironing step and/or at the squeezing step of the ironing step by bending one or more portions of an axially intermediate portion of the flange portion of the tubular material 9, the tubular material 4 may resist being drawn into the die by the punch 26 and moved relative to the die 22 than a case where the axially intermediate bent portions 9a are not formed at the flange portion of the tubular material 9.
Since a bending direction of at least one of the axially intermediate bent portions 9a and a bending direction of the bent portion 8 may be opposite to each other, a portion of the flange portion of the tubular material 9 between the axially intermediate bent portion 9a whose bending direction is opposite to the bending direction of the bent portion 8 and the axial end of the tubular member engages with the pressing member 23 whereby the tubular material 4 may resist being drawn into the die by the punch 26 and moved relative to the die 22 during ironing, differently from a case where a bending direction of each of the one or more axially intermediate bent portions 9a and a bending direction of the bent portion 8 are the same.
When the axially intermediate bent portion 9a may be formed at the flange portion forming step only, compared with a case where the axially intermediate bent portion 9a is formed at the squeezing step of the ironing step, the tubular material 4 may resist being dislocated relative to the die 22 when the flange portion of the tubular material 9 is squeezed between the pressing member 23 and the die 22.
When the axially intermediate bent portion 9a is formed at the squeezing step of the ironing step only, it may not be necessary to form the axially intermediate bent portion 9a at the tubular material manufacturing step and therefore, it may be easy to form the bent portion 8 and the flange portion of the tubular material 9 (it may be possible to simplify the flange portion forming step).
Since the tubular material 4 may be supported at the end portion by the ejecting plate 40 and is ironed, the tubular material 4 may further resist being moved as a whole in the axial direction in which the punch 26 pushes the tubular material 4. Further, control of the extension amount of the tubular material 4 during ironing may be easy.
Since the convex and concave surface 24 is formed by providing at least one convex portion 24a making a space between the die 22 and the punch 26 narrower than a thickness of the tubular material 4 having a constant thickness at the die 22, in an axial direction of the die 22 along the side surface of the die 22, a tubular member 10A having a thickness that changes in the axial direction may be manufactured.
Since the convex and concave surface 24 is formed by providing at least one convex portion 24a making a space between the die 22 and the punch 26 narrower than a thickness of the tubular material 4 having a constant thickness at the die 22, in a circumferential direction of the die 22 along the side surface of the die 22, a tubular member 10a having a thickness that changes in the circumferential direction may be manufactured.
Since the method of manufacturing the tubular member has the step of roll-forming the tubular member 10A having a non-constant thickness to a wheel rim having a rim configuration, it is possible to manufacture a wheel rim 10B having a non-constant thickness, and that may be light and improved in durability, by forming at least one portion of the flange portion of the rim 10a (or 10g) which needs greater thickness, from the flange portion of the tubular material 9.
Next, structures unique to each embodiment of the present invention will be explained.
In the method of manufacturing the wheel rim 10B for a vehicle according to the first embodiment of the present invention, as illustrated in (c) of
As illustrated in
An inner diameter of a portion of the outer die 22 where the convex portion 24a is provided may be larger than an outer diameter of a portion of the tubular material 4 other than the flange portion of the tubular material 9 before ironing. Therefore, the tubular material 4 before ironing can be easily set to the outer die 22.
An outer diameter of the protrusion 28 of the inner punch 26 may be larger than an inner diameter of the tubular material 4 other than the flange portion of the tubular material 9 before ironing. Therefore, a convex and concave configuration of the convex and concave surface 24 of the die 22 can be transferred to the tubular material 4 by pushing the tubular material 4 to the die 22 by ironing.
A difference between an outer radius of the protrusion 28 of the inner punch 26 and an inner radius of the portion of the outer die 22 where the convex portion 24a is provided may be smaller than the thickness of the tubular material 4 before ironing. Therefore, the thickness of the tubular material 4 can be thinned by ironing at the convex portion 24a.
When the punch 26 is moved by the ironing apparatus 20 (e.g., the stamping machine 30) into the cylindrical bore 22a of the outer die 22 set with the tubular material 4, the protrusion 28 of the punch 26 irons the tubular material 4 thereby enlarging the diameter of the tubular material 4, and the portion of the outer die 22 where the convex portion 24a is provided reduces the thickness of the tubular material 4.
When a difference between the inner radius of a portion of the outer die 22 where the convex portion 24a is not provided and the outer radius of the protrusion 28 of the inner punch 26 is equal to or larger than the thickness of the tubular material 4 before ironing, the thickness of the tubular material 4 is not thinned due to ironing more than a reduction in thickness of the tubular material generated when the inner radius of the tubular material 4 is enlarged by the protrusion 28 of the punch 26. The thickness of the tubular material 4 can be thickened relative to an initial thickness of the tubular material 4, and by controlling the ejecting plate 40 for receiving the tubular material 4, the thickness of the tubular material 4 can be further thickened.
When the tubular material 4 is ironed, the tubular material 4 is liable to move as a whole in the axial direction in which the inner punch 26 pushes the tubular material 4. The axial movement of the tubular material 4 may be suppressed because the flange portion of the tubular material 9 engages the flange receiving portion 22c of the outer die 22, because the flange portion of the tubular material 9 is squeezed between the pressing member 23 and the die 22, and because the ejecting plate 40 receives the tubular material 4 in a direction opposite the direction in which the inner punch 26 pushes the tubular material 4. As a result, the axial positions of a thick portion and a thin portion formed in the tubular member 10 may be prevented from being dislocated from the axial positions of the convex and concave surface 24 of the outer die 22. In a wheel rim 10B manufactured by roll-forming the tubular member 10A, a portion where a relatively large thickness is required may be thick, and a portion where a relatively large thickness is not required may be thin, so that the wheel rim 10B may be light.
In the method of manufacturing the wheel rim 10B for a vehicle according to the first embodiment of the present invention, the die 22 may be constructed of the outer die having the cylindrical bore 22a and the inner side surface 22b which is the convex and concave surface 24, and the punch 26 may be constructed of the inner punch which moves into and out from the cylindrical bore 22a of the outer die 22. The outer die 22 may be fixed to the bolster 38 located at a lower portion of the ironing apparatus 20 (the stamping machine 30), and the inner punch 26 may be fixed to the ram 36 located at an upper portion of the ironing apparatus 20 (the stamping machine 30). The inner punch 26 is moved up and down in the vertical direction relative to the outer die 22. By this structure, the ironing apparatus 20 (the stamping machine 30) can be used for manufacturing of the tubular member 10A.
Further, since the flange portion of the tubular material 9 may be bent outwardly in the radial direction of the tubular material 4, it may be easy to form the ironed tubular member 10A to the wheel rim 10B for a vehicle by flaring and roll-forming.
In the method of manufacturing the tubular member 10 according to the second embodiment of the present invention, as illustrated in
A flange receiving portion 22d, with which the flange portion of the tubular material 9 engages, may be formed at an upper end portion of the outer side surface 22e of the inner die 22. The tubular material 4 may be set to the inner die 22 by causing the flange portion of the tubular material 9 to contact and engage the flange receiving portion 22d.
An outer diameter of a portion of the inner die 22 where the convex portion 24a is provided may be smaller than an inner diameter of a portion of the tubular material other than the flange portion of the tubular material 9 before ironing. Therefore, the tubular material 4 before ironing can be easily set to the inner die 22.
An inner diameter of the protrusion 28 of the outer punch 26 may be smaller than an outer diameter of the tubular material other than the flange portion of the tubular material 9 before ironing. Therefore, an convex and concave configuration can be formed to the tubular material 4 by pushing the tubular material 4 to the die 22 during ironing.
A difference between an inner radius of the protrusion 28 of the outer punch 26 and an outer radius of the portion of the inner die 22 where the convex portion 24a is provided may be smaller than the thickness of the tubular material 4 before ironing. Therefore, the thickness of the tubular material 4 can be thinned at the convex portion 24a by ironing.
When the outer punch 26 is moved by the ironing apparatus 20 (e.g., the press machine 30) toward the inner die 22 at which the tubular material 4 is set and the inner die 22 enters the cylindrical bore 26a of the outer punch 26, the protrusion 28 of the outer punch 26 irons the tubular material 4 thereby shrinking the diameter of the tubular material 4, and the portion of the inner die 22 where the convex portion 24a is provided thins the thickness of the tubular material 4.
When a difference between the outer radius of the portion of the inner die 22 where the convex portion 24a is not provided and the inner radius of the protrusion 28 of the outer punch 26 is equal to or larger than the thickness of the tubular material 4 before ironing, the thickness of the tubular material 4 is not thinned during ironing. The thickness of the tubular material 4 may even be increased relative to an initial thickness of the tubular material 4.
When the tubular material 4 is ironed, the tubular material 4 is liable to move as a whole in the axial direction in which the outer punch 26 pushes the tubular material 4. However, the axial movement of the tubular material 4 may be suppressed because the flange portion of the tubular material 9 engages the flange receiving portion 22d of the inner die 22, because the flange portion of the tubular material 9 is squeezed between the pressing member 23 and the die 22, and because the ejecting plate 40 receives the tubular material 4 in a direction opposite the direction where the outer punch 26 pushes the tubular material 4. As a result, the axial positions of a thick portion and a thin portion formed in the tubular member 10 may be prevented from being dislocated relative to the axial positions of the convex and concave surface 24 of the inner die 22. In a wheel rim 10B for a vehicle manufactured by roll-forming the tubular member 10A, a portion where a relatively large thickness is required may be thick, and a portion where a relatively large thickness is not required may be thin, so that the wheel rim 10B may be light.
In the method of manufacturing the wheel rim 10B for a vehicle according to the second embodiment of the present invention, the die 22 may be constructed of the inner die having the outer side surface which is the convex and concave surface 24, and the punch 26 may be constructed of the outer punch having the cylindrical bore 26a and the inner side surface. The inner die 22 may be fixed to the lower bolster 38 of the ironing apparatus 20 (the stamping machine 30), and the outer punch 26 may be fixed to the upper ram 36 of the ironing apparatus 20 (the stamping machine 30). The outer punch 26 may be stroked in the vertical direction relative to the inner die 22. By this structure, the ironing apparatus 20 (the stamping machine 30) can be used for manufacturing of the tubular member 10A.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2010-031955 | Feb 2010 | JP | national |
This is a continuation of International Application Serial No. PCT/JP2011/053201, filed on Feb. 16, 2011, which claims priority from Japanese Patent Application No. JP2010-031955, filed on Feb. 17, 2010, the disclosures of both of which are hereby incorporated by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2011/053201 | Feb 2011 | US |
| Child | 13587478 | US |