Patent Application
20120039720
The present invention relates to a method of manufacturing a wind turbine blade or a part of a wind turbine blade, and in particular to a manufacturing method comprising use of layers of resin-preimpregnated fibres.
Wind turbine blades, and parts thereof, are often manufactured from layers of resin-preimpregnated fibres, called prepregs, which are arranged on a moulding surface and subjected to vacuum and heat to cause a melting or softening of the resin followed by a curing thereof.
A drawback related to the use of prepregs is that the material is often delivered rolled-up, and the shape retention of the material may cause problems during the lay-up process because of wrinkles of the fibres being formed. This is especially the case for large product thicknesses, where wrinkles in lower layers can worsen the distortions in upper layers even further than what is caused by shape retention of the individual layers alone.
Furthermore, the prepregs have only limited sidewise stability, and care must be taken to avoid misalignment of the fibres during lay-up. The handling of prepregs can be particularly difficult when prepregs of large size are cut to the desired shape at one working surface and subsequently has to be moved to and arranged on the moulding surface.
Another drawback is that the curing is an exothermic process and therefore may result in disadvantageous built-in thermal stresses and deformations in the finished product, especially for products having a large thickness. A further disadvantage related to the exothermic curing process is that the heat may result in degradation of material which cannot withstand the actual temperatures which arise during the curing process.
Hence, an improved manufacturing method would be advantageous, and in particular a manufacturing method overcoming the above mentioned disadvantages would be advantageous.
It is an object of the present invention to provide a method of manufacturing a wind turbine blade or a part of a wind turbine blade from prepregs by which method the average temperature increase across a given section during curing of the resin is lower than with corresponding known methods.
It is another object of the present invention to provide a method of manufacturing a wind turbine blade or a part of a wind turbine blade from prepregs by which method it is easier to prevent misalignment of the fibres during the lay-up process than with corresponding known methods. Such misalignment can be both in the thickness direction of the member being manufactured and sideways.
It is another object of the invention to provide a method of manufacturing a wind turbine blade or a part of a wind turbine blade from prepregs by which method it is easier to handle the layers during the lay-up process.
It is a further object of the present invention to provide an alternative to the prior art.
Thus, the above described object and several other objects are intended to be obtained in a first aspect of the invention by providing a method of manufacturing a wind turbine blade or a part of a wind turbine blade, the method comprising
By “cured” is preferably meant fully cured.
By such pre-assembling of the layers, the material may be easier to handle due to a larger stiffness caused by the cured layer(s), and because the fibres of the uncured layers are at least partly supported by the cured layer(s) so that it is easier to avoid misalignment of the fibres. This is particularly advantageous when layers of large size are cut to the desired shape at one working surface and subsequently has to be moved to and arranged on the moulding surface. Such pre-assembled layers are called pre-forms in the following; they may also be called slabs.
The incorporation of cured layers having a larger stiffness than the uncured layers also suppresses the tendency of uncured material delivered rolled-up to form wrinkles due to the shape retention of the material.
In an embodiment of the invention, layers of cured fibre reinforced resin are arranged on both sides of each layer of resin-preimpregnated fibres which makes it easier to handle the material during lay-up without the need to touch uncured resin. Furthermore, the cured layers are not sticky as the uncured ones, whereby it becomes easier to push the layers to the desired mutual position while arranging the pre-forms on the moulding surface. Alternatively, a plurality of layers of resin-preimpregnated fibres is arranged on top of each other, and a layer of cured fibre reinforced resin is arranged on the outer surface of each outer layer of resin-preimpregnated layers.
In another embodiment of the invention, layers of uncured resin-preimpregnated fibres are arranged on both sides of each layer of cured fibre reinforced resin. Hereby the adhesive effect of the uncured resin may make it easier to ensure that the layers stay in place during the lay-up process.
In another embodiment the layers are arranged so that one outer side surface of the assembled layers comprises cured resin, and the other outer surface comprises uncured resin. Hereby a compromise between the two last mentioned embodiments can be obtained. The uncured resin can act as an adhesive so that the mutual position of the layers is preserved.
The method may further comprise the steps of
In some embodiments of the invention, the assembling of the layers may comprise the step of applying a pressure on the layers. Hereby a stronger adhesive force is obtained.
Such a pressure may be applied by use of at least one roller. One roller may be used in combination with a plane surface or with one or more other rollers. The at least one roller may also be used to move the material, or the movement may be accomplished by other pulling or pushing means.
The thickness of each layer may be between 0.3 and 2 mm, such as between 0.3 and 0.5 mm, or between 0.5 and 1 mm, or between 1 and 2 mm. In some embodiments, the at least one layer of resin-preimpregnated fibres and the at least one layer of cured fibre reinforced resin have substantially the same thickness before assembly.
The fibres may be uni-directionally arranged, but any fibre orientation is considered to be covered by the scope of the invention. The fibres may also be arranged in more direction and/or interwoven within each or some of the layers. The fibre orientation may also differ between the layers, e.g. to obtain fibre reinforcement in several directions from layers or uni-directionally arranged fibres.
In some embodiments of the invention, the resin and/or the fibres may be the same types in the at least one layer of resin-preimpregnated fibres and the at least one layer of cured fibre reinforced resin. Hereby it may be possible to avoid abrupt changes in mechanical properties which could cause stress concentrations during loading. Similar properties may e.g. be obtained if the at least one layer of cured fibre reinforced resin is provided by curing at least one layer of resin-preimpregnated fibres of the same type as used for the remainder of the composite.
The at least one resin may be selected from: epoxy, polyester, vinyl ester, and phenol. The fibres may e.g. be carbon, glass or aramide fibres.
A method as described above may e.g. be used to manufacture a wind turbine blade shell member or a wind turbine blade spar member. It may e.g. be used to manufacture the trailing edge stringer or the connecting stringer of a wind turbine blade shell member.
A second aspect of the invention is related to a wind turbine blade shell member manufactured by a method as described above.
A third aspect of the invention is related to a wind turbine blade spar member manufactured by a method as described above.
A fourth aspect of the invention is related to a pre-form for use in a wind turbine blade, the pre-form comprising at least one of layer of uncured resin pre-impregnated fibres and at least one layer of cured fibre reinforced resin in an at least partly overlaying relationship, wherein the layers are arranged in a sequence which is starting and ending with a cured layer. Hereby it may be easier to handle the pre-form without the need to touch uncured resin.
Alternatively, the layers may be arranged in a sequence which is starting and ending with an uncured layer. Hereby the adhesive effect of the uncured resin may make it easier to ensure that the layers stay in place during the lay-up process.
The layers may alternatively be arranged in a sequence starting with a cured layer and ending with an uncured layer, or vice versa. Hereby a compromise between the two last mentioned embodiments can be obtained. The uncured resin can act as an adhesive so that the mutual position of the layer is preserved.
By pre-form is preferably meant a pre-shaped fibrous reinforcement which may be formed to desired shape and size prior to being placed on a moulding surface. Such a pre-form of cured and uncured layers may facilitate handling of the material during arrangement on the moulding surface. The pre-forms may also be made on a plane surface to that the final geometry is obtained during the subsequent step.
The pre-form may comprise a plurality of layers of uncured resin pre-impregnated fibres and a plurality of layers of cured fibre reinforced resin. However, it may also comprise only one layer of one or both types. The layers may be arranged alternately as cured and uncured, respectively, or vice versa.
The first, second, third and fourth aspects of the present invention may each be combined with any of the other aspects. These and other aspects of the invention will be apparent from and elucidated with reference to the embodiments described hereinafter.
The method of manufacturing a composite member according to the invention will now be described in more detail with regard to the accompanying figures. The figures show one way of implementing the present invention and is not to be construed as being limiting to other possible embodiments falling within the scope of the attached claim set.
A manufacturing method which is often used for the manufacturing of wind turbine blades or parts thereof, such as the blade shell, is by use of prepregs. A number of prepregs are arranged on top of each other and consolidated by application of vacuum and heat.
In a manufacturing method according to the present invention, the above described problems are counteracted by embedding of already cured material in the composite member. This cured material will typically be made from one or more layers of prepregs of the same or similar type as what is used for the remainder of the composite member. Hereby stress concentrations due to abrupt changes in mechanical properties through the thickness can be avoided.
A possible manufacturing method is shown schematically in
In an alternative manufacturing method, pre-forms are first made on a consolidation table, also called work plate, where they are laid up and consolidated but not cured, typically by use of vacuum as described above. This consolidation step does not necessarily comprise heating. The pre-forms are subsequently arranged on a moulding surface and cured as described above to obtain the final geometry. The pre-forms will be described in further details below.
The pre-cured layers 2 will not develop heat but will on the contrary absorb some of the heat caused by the exothermic curing process of the resin in the prepregs 1. This results in a lower average temperature during curing than for a composite member of the same thickness but made fully from uncured prepregs 1. The actual relative amounts of pre-cured material 2 and uncured material 1 should be chosen to ensure that the temperature development does not become damaging for the material itself or for neighbouring material. An appropriate sequence and number of layers 1, 2 for a given application may e.g. be determined by experimentation and/or by computer simulations.
In
The resins will typically be one of epoxy, polyester, vinyl ester and phenol, but any resin material used for prepregs is covered by the present invention. The fibres may e.g. be glass, carbon or aramide.
Another problem related to the use of prepregs 1 is illustrated schematically in
The prepregs are typically cut to the desired size and shape at one working surface and subsequently, typically manually, moved to and arranged on the moulding surface. The uncured prepregs have a relatively low stiffness which makes them difficult to handle, especially for large sizes. In a method according to the present invention at least one layer of cured fibre reinforced resin is assembled with at least on layer of uncured resin-preimpregnated fibres prior to placing the layers on a moulding surface. Hereby the handling of the layers can be eased since it is not necessary to move the uncured, and thereby more flexible, layers individually from the working surface to the moulding surface. Hereby a better stability both in-plane and out-of-plane is obtained resulting in a reduced risk of fibre misalignment during the lay-up process.
In some embodiments of the invention, a step in the manufacturing method comprises assembly of one layer of uncured prepreg 1 with a layer of cured prepreg 2 on each side as shown schematically in
The sticky effect of the uncured resin may be utilized to join the layers 1,2 shown in
As described above, a potential problem with known art is that the curing of the resin is an exothermic process, and especially for large thicknesses the heat developed by the curing material elevates the temperature to above the oven temperature. This temperature increase may result in degradation of the material and/or thermal stresses being built into the composite member which can be critical during use due to the lowered load carrying capacity. By having pre-cured material substituting some of the uncured prepregs, the ratio between the energy releasing material, i.e. initially uncured, and energy absorbing material, i.e. cured, is offset towards more absorbing material. The material will therefore be less exothermic during curing resulting in a faster process without compromising the risk of material degradation and thereby lowered mechanical properties of the composite member.
A method as described for the trailing edge stringer may also be used to manufacture a connecting stringer 15 as shown schematically in
When the above method is used to manufacture a composite member with a surface having a large curvature, and in particular a double-curvature, the layers are typically in the form of tapes (not shown). With known manufacturing methods, the fibre orientation is then easily distorted which may be substantially overcome by the use of pre-cured layers 2 as described above. The tapes may furthermore be held in place by successive layers being arranged with some overlap.
Although the present invention has been described in connection with the specified embodiments, it should not be construed as being in any way limited to the presented examples. E.g. the embedding of pre-cured material 2 as described above can be used at any position in the geometry of a wind turbine blade. The scope of the present invention is set out by the accompanying claim set. In the context of the claims, the terms “comprising” or “comprises” do not exclude other possible elements or steps. Also, the mentioning of references such as “a” or “an” etc. should not be construed as excluding a plurality. The use of reference signs in the claims with respect to elements indicated in the figures shall also not be construed as limiting the scope of the invention. Furthermore, individual features mentioned in different claims, may possibly be advantageously combined, and the mentioning of these features in different claims does not exclude that a combination of features is not possible and advantageous.
| Number | Date | Country | Kind |
|---|---|---|---|
| PA 2009 00089 | Jan 2009 | DK | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/DK2010/050012 | 1/21/2010 | WO | 00 | 10/14/2011 |
| Number | Date | Country | |
|---|---|---|---|
| 61205721 | Jan 2009 | US |