20100086800
Metals and metal alloys having a submicron or nanocrystalline structure are of great interest to the commercial and military segment. They have novel properties allowing for the development of completely new product opportunities. To date though, making bulk nanocrystalline materials of metals of interest has been problematic. Most of the success has occurred with thin films and sprayed coatings. Some success has been achieved with high energy milling, high deformation rate machining chips, equiangular extrusion, and easy glass formers. But these all have severe drawbacks. There is a need for a simple, cost effective means of making three dimensionally large, sub micron grain size, crystalline structures.
Metallic materials having a submicron, or nanocrystalline grain structure are of great interest due to their unique properties which include extended ductility and very high yield strengths. Much work has been done with thin films, coatings, and powders to make nanocrystalline structures, but the means of making three dimensionally large structures still remains elusive.
High energy milling is probably one of the most common ways of manufacturing metal powders having a submicron size grain structure. One problem with this approach is the powder frequently becomes heavily contaminated with microscopic particles that result from the wear of the mill, attriter or grinding media used in the process
Another technique pioneered by Purdue University and now being commercialized by Nanodynamics Inc. involves compacting machining chips created at high deformation rates. The cold work induced in the machining process results in nanocrystalline grain sizes in the chips. Like high energy milling this technique suffers contamination from the machining process and also requires the use of expensive secondary operations (Hot Isostatic Pressing, extrusion, explosive compaction, etc.) to consolidate the loose powder or chips into a bulk solid. Many times, if not carefully controlled, this secondary processing can damage the initial microstructure during consolidation.
Equi-channel angular extrusion (ECAE) is a high shear process where the metal or alloy is forced through a die changing the direction of flow. Very high strains are produced resulting in grain size refinement. However, the metal may have to be passed through the die multiple times (3-4) to produce a submicron grain size making the process work and cost intensive.
Others such as A. C. Hall, L. N. Brewer and T. J. Roemer, “Preparation of Aluminum coatings Containing Homogeneous Nanocrystalline Microstructures Using the cold Spray Process”, JTTEES 17:352-359 have shown that thin coatings made from submicron grain sized powders retain this submicron grain size when the coatings are made by cold spray. In certain instances with aluminum they have even reduced the submicron grain size.
We have discovered that certain metal powders of conventional grain size, substantially 5-10 microns and even larger, when projected at supersonic velocity, at relatively low temperature and deposited on a substrate form a dense solid having a submicron grain structure. This deposit can be made large in all three dimensions and the substrate easily removed to leave only the nanocrystalline deposit. This deposit differs from coatings in that refractory metal coatings are typically less than 0.5 mm thick, usually less than 0.1 mm and rely on remaining attached to the substrate to maintain their physical integrity. In this case the thickness dimension can be quite large up to 1-2 cm and beyond. The large thickness allows the deposit to be removed from the substrate and used in free standing applications.
We have demonstrated this behavior for Ta, Nb and Mo metals (all BCC structure and having a high melting point temperature), and believe it may be a universal phenomena that is velocity sensitive.
What we have discovered is a process for making three dimensionally large structures having a submicron grain structure. This submicron grain structure is also resistant to growth during processing at elevated temperatures which can be used to improve interparticle bond strength, eliminate work hardening and improve ductility. Additionally these deposits can be used as a starting material for ECAE processing reducing the number of passes required to 1 to develop a fully densified, fine, uniform structure.
In general, the process for producing three dimensionally large metallic structures comprised of submicron range sizes includes directing a supersonic powder jet against a substrate such that the powder adheres to the substrate and to itself to form a dense cohesive deposit. As a result products could be made from such deposits including, but not limited to, explosively formed projectiles, kinetic energy penetrators and hydrogen membranes. In the process the powdered jet may be comprised of refractory metal powders. The dense metal structure made from metal powders having a submicron grain size micro structure could thereby be useful as a refractory metal structure. The invention can be practiced where the powder is deposited by a supersonic jet and extruded by Equi channel angular extrusion. The deposit can remain attached to the substrate or could be removed from the substrate.
The invention could be practiced using a known cold spray system where, for example, a heated gas, such as nitrogen, is used to accelerate the powder and make a supersonic powder jet which is then directed against a substrate. When the supersonic powder jet is directed against the substrate and the powder adheres to the substrate and to itself, the resultant dense cohesive deposit results in a three dimensionally large metallic structure comprised of submicron grain sizes.
The results shown below were all attained using a Kinetics 4000 cold spray system. This is a standard commercially available system. In general, a cold spray process comprises directing on a target a gas flow wherein the gas flow forms a gas-powder mixture with a powder. A supersonic speed is imparted to the gas flow. The jet of supersonic speed is directed onto the surface of a substrate thereby cold spraying the substrate. PCT application U.S. 2008/062434 discloses cold spray techniques. All of the details of that application are incorporated herein by reference thereto. In a practice of this invention heated nitrogen gas at temperatures of 500-800 C and approximately 30 bars was used to accelerate the powder and make a supersonic powder jet. The jet was typically directed against a copper or steel substrate. The substrate was usually cylindrical, cylinder like or planar in nature. Tubular, bowl like and flat disks and rectangles were made. Metallographic samples were cut from the shapes and mechanically polished. The microstructure was examined using a FIB SEM in both secondary and back scatter mode. Special high purity tantalum, niobium and molybdenum powders made by HC Starck for cold spray applications were used in these experiments.