The present invention relates to a method of forming a crankshaft bushing and, more particularly, a method of forming a crankshaft bushing using a powder metal process with a compaction die combined with punches and core rods.
Ordinary powder metal procedures and methods for forming crankshaft bushings and similar components having a generally cylindrical axial internal opening are useful. However, if a modification is necessary to the internal axial opening within the bushing, such as the forming of a slightly convex surface, such traditional powder metal methods require further finishing. Such further finishing is usually in the form of machining wherein the external cylindrical geometry of the outer diameter is ground such that the slightly convex surface is accurately oriented to the outer geometry. Such additional machining steps are not desirable from a cost point of view and from a productivity point of view.
Accordingly, is an object of the present invention to provide an improved method for forming a crankshaft bushing or similar component utilizing powder metal methods.
It is another object of the present invention to provide a method of forming a crankshaft bushing or similar component using powder metal procedures wherein an internal surface of the bushing includes a generally flat or slightly convex surface.
A method of forming a crankshaft bushing or similar product using powder metallurgy techniques is provided.
Typically, a compaction die having a generally cylindrical axial internal opening is provided. A lower punch is provided having an exterior surface that corresponds to the internal opening of the compaction die. An upper punch is provided having an exterior surface that also corresponds to the internal opening of the compaction die.
The lower punch itself further has an internal opening that is generally cylindrical and axial. A lower core rod has an exterior surface that corresponds to the internal opening of the lower punch.
The upper punch also has a generally cylindrical axial internal opening. An upper core rod is provided that has an exterior surface that corresponds to the internal opening in the upper punch.
A metal powder is introduced into an internal opening of the compaction die. The metal powder is compacted to form a powder metal blank by having the lower punch and upper punch enter the internal opening of the compaction die. Further the lower core rod passes through the axial opening in the lower punch and the upper core rod passes through the opening in the upper punch to also enter the compaction die in a manner such that a top surface of the lower core rod and a bottom of the upper core rod approach each other. Accordingly, a powder metal blank in the general form of the bushing or similar product is formed.
Further, the lower core rod includes a generally flat or slightly convex section on its exterior surface which section is tapered from the top surface of the lower core rod downwardly to an intersection with an exterior wall section of the lower core rod. Similarly, the upper core rod includes a generally flat or slightly convex section on its exterior surface which section is tapered from the bottom surface of the upper core rod upwardly to an intersection with an exterior wall section of the upper core rod to form the generally flat or slightly convex section on the powder metal blank.
Further, the lower core rod itself includes a generally cylindrical axial internal opening. Upon compaction of the metal powder in the internal opening of the compaction die, excess metal powder can exit the internal opening of the compaction die through the internal opening in the lower core rod.
In the drawings,
Referring to
Lower punch 14 is again seen to be a generally cylindrical structure with an outer diameter corresponding to internal opening 13 of compaction die 12. Lower punch 14 has a usually cylindrical outer surface 16, with again a usually cylindrical axial internal opening 18. Lower punch 14 again is usually comprised of a tool steel, and is usually about 4 to 6 inches in length (10.16 to 15.24 centimeters).
Lower core rod 20 is seen to comprise a generally cylindrical structure having an outer surface 22 that corresponds to internal opening 18 of lower punch 14. Lower core rod 20 also includes an axial, usually cylindrical internal opening 24 that extends from the top surface 26 of lower core rod 22 to the bottom 25 of lower core rod 20. Again lower core rod 20 is usually comprised of tool steel and is generally 6 to 8 inches in length (15.24 to 20.32 centimeters).
Upper punch 30 is seen to be generally cylindrical structure having an outer generally cylindrical surface 32 and an internal generally cylindrical axial opening 34. Again the dimensions of upper punch 30 would be similar to the dimension of lower punch 14 in that outer surface 32 of outer punch 30 would enter internal opening 13 in compaction die 12 from the top; whereas lower punch 14 enters opening 13 of compaction die 12 from the bottom. Upper punch 30 is also seen to have an internal generally cylindrical axial opening 34 of a similar dimension to the internal opening 18 of lower punch 14. Upper punch 30 is usually comprised of tool steel and usually has a length of 2 to 3 inches (5.08 to 7.62 centimeters).
Upper core rod 36 is seen to be generally cylindrical structure having an outer surface 38 that is generally cylindrical and sized to fit into internal opening 34 of upper punch 30. Upper core rod 36 is also seen to have a bottom surface 40 which is seen to approach and align with top surface 26 of lower core rod 20. Bottom surface 40 of upper core rod 36 is also seen to include a protrusion 42 which is usually of a tapered cylindrical or pyramidal type structure. Such protrusion 42 is seen to align with and enter a corresponding depression 44 in the top surface 26 of lower core rod 20.
Further, lower core rod 20 is seen to have a flattened or slightly concave surface 48 that extends from outer surface 22 of lower core rod 22 to the top surface 26 of lower core rod 20. Similarly, upper core rod 36 is seen to have a flattened surface 46 that extends from the outer surface 38 of upper core rod 36 to the bottom surface 40 of upper core rod 36.
Referring now to
Referring now to
Referring now to
The material for bushing 50 can be, as mentioned above, any low alloy material that would produce a strong wear resistant metallic structure.
In general, a method of manufacturing a bushing in accordance with one aspect of the present invention comprises the steps of providing an initial metal alloy powder comprising the desired elemental components, with the balance essentially iron. A suitable lubricant is added in accordance with powder metal practice to form lubricated metal powder. The lubricated metal powder is then injected into the internal opening of compaction die 12. The metal powder is then compacted, typically at a pressure of between 40 and 65 tons per square inch, to form a die compacted metal blank. The compaction is accomplished by having the upper punch 30 and lower punch 14 enter the opening in compaction die 12 under suitable pressures, while the lower core rod 20 and upper core rod 36 both enter the internal opening of compaction die 12 through the respective openings in lower punch 14 and upper punch 30. The partial flatten surfaces on bushing 50 are created by the alignment of lower core rod 20 and upper core rod 36, with top surface 26 of lower core rod 20 and bottom surface 40 of upper core rod 36 approaching and eventually contacting each other with upper core rod protrusion 42 entering depression 44 in lower core rod top surface 26.
Examples of the method of carrying out the present invention follow:
In a method of manufacturing a crankshaft bushing, a metal powder of particle sizes between 45 and 250 micron was provided comprising, by weight, 0.5% C composition and 0.85% Mo composition, with the balance essentially iron. A 0.75 percent of EBS was added as a lubricant to form a lubricated metal powder. The lubricated metal powder was compacted at a pressure of 45 tons per square inch in a compaction die utilizing a lower punch having a lower core rod and an upper punch having an upper core rod. The resulting die compacted metal blank was then sintered at a temperature of 2080° F. for 15 minutes, the sintered metal blank was then quenched from an initial temperature of 1650° F. to a temperature of 150° F. The quenched metal blank was then tempered at a temperature of 380° F. for 120 minutes. The final tempered metal blank was then finish ground to the final bushing dimensions and configurations.
In a method of manufacturing a crankshaft bushing, a metal powder of particle sizes between 45 and 250 micron was provided comprising, by weight, 0.5% C composition and 1.5% Mo composition, with the balance essentially iron. A 0.75 percent of EBS was added as a lubricant to form a lubricated metal powder. The lubricated metal powder was compacted at a pressure of 45 tons per square inch in a compaction die utilizing a lower punch having a lower core rod and an upper punch having an upper core rod. The resulting die compacted metal blank was then sintered at a temperature of 2080° F. for 15 minutes, the sintered metal blank was then quenched from an initial temperature of 1650° F. to a temperature of 150° F. The quenched metal blank was then tempered at a temperature of 380° F. for 120 minutes. The final tempered metal blank was then finish ground to the final bushing dimensions and configurations.