Patent Application
20060228467
1. Field of the Invention
The present invention relates to a method of manufacturing an electrode used for lithium secondary batteries.
2. Description of Related Art
Silicon is a material that can be alloyed with lithium. Because of its large theoretical capacity, silicon has received attention as an electrode material that achieves high energy density for lithium secondary batteries. Published PCT Application WO01/029912, which is assigned to the assignee of the present invention, proposes a lithium secondary battery electrode in which a thin film composed of silicon is formed on a current collector, as an electrode for a lithium secondary battery that exhibits high charge-discharge capacity and good charge-discharge cycle performance.
However, in the process of forming the thin film used for the electrode, it is difficult to form a flat and smooth surface, and protrusions form on the surface. When such an electrode is used to fabricate a battery, the protrusions formed on the electrode surfaces penetrate the separator and come into contact with the counter electrode, causing a short-circuit failure of the battery.
Examples of the method of forming the thin film include CVD, sputtering, evaporation, and thermal spraying. In the following, vacuum evaporation is discussed, in which the above-described problem tends to occur noticeably.
Electron beam evaporation, which is one type of the vacuum evaporation, uses an evaporation system as illustrated in
When the electron beam is applied to the evaporation source material 3 and the evaporation source material 3 is heated to evaporate, so-called bumping of the evaporation source material 3 can take place because of the influence of gases and impurities that contaminate the interior of the evaporation source material 3, and the phenomenon of scattering particles, known as splash, may occur. These particles adhere onto the electrode surface, and result in formation of protrusions on the electrode surface.
Techniques for preventing the bumping of the evaporation source material have been proposed. Japanese Published Unexamined Patent Application Nos. 5-171412 and 7-34224 describe a technique to control a fabrication method of the evaporation source material and a technique to control the shape and composition of the evaporation source material, both of which are intended for use in forming a silicon monoxide thin film. Japanese Published Unexamined Patent Application No. 2004-204314 describes a technique to control the procedure of heating the evaporation source material for use in forming a metal thin film. Nevertheless, it has been difficult to completely prevent the bumping of evaporation source material. In particular, in the case of depositing a silicon thin film, techniques to prepare the evaporation source material and to control the procedure of heating the evaporation source material for preventing the bumping have not yet been established and it has been difficult to prevent the bumping phenomenon over a long time period.
Accordingly, it is an object of the present invention to provide a method of manufacturing an electrode for lithium secondary batteries having flat and smooth surfaces and a thin film deposited on a current collector.
The present invention provides a method of manufacturing an electrode for lithium secondary batteries, comprising: depositing a thin film of active material on a current collector; and performing a compression process after depositing the thin film.
The above-described manufacturing method reduces the heights of the protrusions adhered on the electrode surfaces by compressing the electrode surfaces after depositing the thin film, and therefore reduces short-circuit failures in the batteries that employ the electrodes produced according to the method.
As described in the following examples, the short-circuiting of the battery resulting from the protrusions formed on the electrode surfaces due to splash is dependent on the height of the protruding portions. The probability of the short-circuiting increases when the height of the protrusions exceeds a certain value. Therefore, by controlling the height of the protrusions formed on the electrode surfaces to be a predetermined value of 80 μm or less, the short-circuit failures can be lessened. In the present invention, it is preferable to use pressure rollers, which can be incorporated in the thin-film deposition system so that the manufacturing process can be simplified, as the method for compressing the electrode surface.
When carrying out the pressing process for the electrode surfaces with the use of pressure rollers, the heights of the protrusions can be reduced without causing adverse effects on battery performance if the gap between the pressure rollers is set at about 20% to about 100% of the current collector thickness in the compression process. If the degree of the compression is too low, the effect of reducing the heights of the protrusions will be small, while if the degree of the compression is too high, the silicon thin film may peel off or the current collector may rupture.
It is preferable that the current collector to be used in the present invention be formed of a metal that does not alloy with lithium. Examples of such a material include copper, alloys containing copper, nickel, and stainless steels. Examples of the alloys containing copper include phosphor bronze and red brass. When the surfaces or the entirety of the current collector is composed of copper, which has relatively low hardness, among these examples, an effect of burying the protrusions, formed on the electrode surface due to the splash, into the current collector in the compression process is attained, which synergistically enhances the effect of reducing the heights of the protrusions.
The present invention pertains to a method of manufacturing an electrode for lithium secondary batteries and may be applied to the manufacturing of either the negative electrode or the positive electrode. When a material containing silicon is used as the active material, it is generally used for the negative electrode.
The present invention makes it possible to provide an electrode for lithium secondary batteries that has a thin film deposited on the current collector and that has a flat and smooth surface, and thus to reduce the failure of products dramatically. Therefore, the productivity of manufacturing the battery employing the electrode increases.
Hereinbelow, the present invention is described in further detail based on preferred embodiments thereof. It should be construed, however, that the present invention is not limited to the following preferred embodiments and various changes and modifications are possible without departing from the scope of the invention.
Preparation of Electrode
Copper was deposited on surfaces of a rolled copper foil (thickness 26 mm) by an electrolytic process to roughen the surfaces, and the surface-roughed copper foil was used as the current collector. The surfaces of the current collector had an arithmetical mean roughness Ra of 0.5 μm. Arithmetical mean roughness Ra is defined in Japanese Industrial Standard (JIS) B 0601, and it can be measured by a contact probe profilometer. The use of the surface-roughed copper foil can prevent a silicon thin film from peeling off from the current collector. Such peeling occurs due to the film stress of the silicon thin film or the stress originating from the expansion/shrinkage in volume of the silicon thin film during charge/discharge. On the current collector thus prepared, a silicon thin film was deposited in the following manner, using the thin-film deposition system as shown in
The current collector 1 thus prepared was wound around the roller 6, and the current collector 1 was transferred in the direction indicated by the arrow A so as to be wound up by the roller 7. The current collector 1 was irradiated with an ion beam from an ion gun 9 and thereafter a silicon thin film was deposited thereon. In the deposition, the current collector 1 successively passes through a region opposing the ion gun 9 and a region opposing the crucible 4, and thus, a surface of the current collector 1 undergoes the ion irradiation process, and a silicon thin film is deposited thereon.
A partition is provided between the region in which the ion gun 9 is provided and the region in which the crucible 4 and the electron beam gun 5 are provided, for independently controlling the pressures of the regions in which the respective processes are performed. The ion irradiation process is a process for improving the adhesion of the silicon thin film to the current collector. Argon was used for the irradiation ion species.
The evaporation source material 3 used was a single crystal silicon produced by the float-zone method. The single crystal silicon produced by the float-zone method tends to have less amounts of contaminating impurities than a single crystal silicon produced by the Czochralski method. For example, the oxygen content reduces from about 1015-1016 atoms/cm3 to about 1017-1019 atoms/cm3. When a single crystal silicon produced by the float-zone method is used for the evaporation source material 3, bumping that occurs during the silicon thin film deposition is suppressed in comparison with the case that a single crystal silicon produced by the Czochralski method is used. As the crucible 4, a water-cooled crucible made of copper was used.
The ion irradiation in the present embodiment was conducted with a pressure of 0.05 Pa and at an ion current density of 0.27 mA/cm2. The formation of the silicon thin film by electron beam evaporation was conducted with a pressure of 0.019 Pa and at an electron beam gun power of 13 kW. The transferring speed of the current collector was set at 0.35 m/min., and a 15 m region along the transfer direction of the current collector was subjected to the ion irradiation and the silicon thin film deposition.
The current collector 1 on one side of which the silicon thin film was deposited in the procedure described above was wound up around the roller 7, and then taken out of the thin-film deposition system 8 in an as-rolled state. The silicon thin film was formed only on the inner surface side of the roll of the current collector 1 taken out from the thin-film deposition system 8.
Next, the current collector 1 taken out from thin-film deposition system 8 was turned over inside out using a roll reversing apparatus, and thereafter, the current collector 1 was mounted onto the roller 6 of the thin-film deposition system 8. At this point, the silicon thin film is formed only on the outer surface side of the roll of the current collector 1. Then, the surface of the current collector 1 on which the silicon thin film was not formed was subjected to the ion irradiation and the silicon thin film deposition in the same procedure as described above.
A cross section of the current collector 1 on which the silicon thin films were deposited was observed with SEM to measure the film thickness of the silicon thin films, and it was found that the silicon thin films with a thickness of about 7 μm were deposited on the respective sides of the current collector. The deposition rate of the silicon thin film was about 2.5 μm·m/min. in the present embodiment.
Inspection of Protrusions
A 1200 cm2 region of the electrode prepared according to the above-described procedure was visually observed while being irradiated with light applied diagonally with respect to the electrode, and thereby the number and positions of protrusions formed on the electrode surface were determined. Next, using an optical microscope, the sizes (maximum dimensions along the horizontal orientation of the electrode surface) and heights of the protrusions, which were confirmed by the visual observation, were measured. The height of a protrusion was determined from the difference in the focal points between the flat surface and the peak point of the protrusion.
The number of the protrusions formed on the electrode surface was about 0.03 per 1 cm2 of the electrode area. The results of measurements of the sizes and heights of the protrusions are shown in
Pressing Process for Electrode
Using a rolling machine having 15 cm-diameter pressure rollers, a portion of the electrode that underwent the inspection of protrusions was subjected to a pressing process wherein the gap between the pressure rollers was set at 8 μm, the revolution of the rollers was 200 rpm, and the number of times that the electrode was to be passed through the rollers was two times.
Next, the electrode after the pressing process was inspected using an optical microscope, and the heights of the protrusions that had been detected before the pressing process were determined in the same manner as that used before the pressing process. The results of measurements of the heights of the protrusions before and after the pressing process are shown in
Preparation of Negative Electrode
The electrode subjected to the pressing process was cut out into a size of 3.5 cm×34 cm and current collector tabs were attached thereto, whereby negative electrodes a1, a2, and a3 were prepared. As comparative examples, negative electrodes b1 to b11 were prepared using an electrode that was not subjected to the pressing process.
Table 1 summarizes the results of measurements of heights of protrusions formed on the surfaces of the negative electrodes a1, a2, and a3. Table 1 also shows whether or not short-circuiting occurred, charge-discharge efficiency, and capacity retention ratio, which are discussed later. In the negative electrodes a1, a2, and a3, the heights of the protrusions were reduced by the pressing process, and the heights of the protrusions were 40 μm or less.
In addition, Table 2 summarizes the results of measurements of the heights of protrusions formed on the surfaces of the negative electrodes b1 to b11. Table 2 also shows whether or not short-circuiting occurred, charge-discharge efficiency, and capacity retention ratio, which are discussed later.
Preparation of Positive Electrode
Li2CO3 and CoCO3 were used as starting materials, and the materials were weighed so that the atomic ratio of Li:Co was 1:1, followed by mixing them in a mortar. The resultant mixture was pressure-formed by pressing it with a stamping die with a diameter of 17 mm, and then baked at 800° C. in the air for 24 hours, to thus obtain a baked material of LiCoO2. The baked material was then pulverized in a mortar to form a powder with an average particle size of 20 μm.
Then, 90 parts by weight of the resultant LiCoO2 powder was mixed with a 5 weight % N-methylpyrrolidone solution containing 5 parts by weight of artificial graphite powder as a conductive agent and 5 parts by weight of polyvinylidene fluoride as a binder agent, to thus prepare a positive electrode mixture slurry. The resultant positive electrode mixture slurry was applied onto an aluminum foil with a thickness of 15 μm serving as a current collector. The resultant material was dried and thereafter pressure-rolled forming a positive electrode active material layer with a thickness of 65 μm, and a current collector tab was attached thereto. Thus, a positive electrode was prepared.
Preparation of Electrolyte Solution
LiPF6 was dissolved at a concentration of 1 mole/liter into a mixed solvent of 3:7 volume ratio of ethylene carbonate and diethyl carbonate to thus prepare an electrolyte solution.
Preparation of Battery
The positive electrode and each of the negative electrodes prepared in the above-described manner were overlapped facing each other with a polyethylene separator with a thickness of 16 μm interposed therebetween. Thereafter, they were wound up and pressed into a flat shape, to thus prepare an electrode assembly. In a glove box under an argon atmosphere, each electrode assembly was inserted into a battery case made of 0.11 mm-thick aluminum laminate, and the electrolyte solution was filled therein, followed by sealing the battery case.
Evaluation of Charge-Discharge Performance and Short-Circuiting
Using the batteries fabricated in accordance with the above-described manner, charge-discharge cycle performance was evaluated. The batteries were charged at 25° C. with a current of 50 mA to 4.2 V, and thereafter discharged at a current of 50 mA to 2.75 V. This process was taken as one charge-discharge cycle. This charge-discharge cycle was repeated 5 times, and the charge capacities and discharge capacities at the first cycle and the fifth cycle were evaluated. In addition, whether or not short-circuiting occurred was determined from the voltage values in the evaluation of the charge-discharge cycle performance.
The results of the evaluation for the batteries that employed the negative electrodes a1, a2, and a3 are shown in Table 1, and the results of the evaluation for the batteries that employed the negative electrodes b1 to b11 are shown in Table 2. The charge-discharge efficiencies shown in Tables 1 and 2 were calculated using the following equation 1:
(Charge-discharge efficiency)=(Discharge capacity at the first cycle)/(Charge capacity at the first cycle)×100. Eq. 1:
The capacity retention ratios shown in Tables 1 and 2 were calculated using the following equation 2:
(Capacity retention ratio)=(Discharge capacity at the fifth cycle)/(Discharge capacity at the first cycle)×100 Eq. 2:
The battery that employed the negative electrode b11 showed a voltage of 0 V immediately after the battery was fabricated, indicating that short-circuiting had occurred, so neither the charge-discharge efficiency nor capacity retention ratio could be evaluated. It is believed that because the negative electrode b11 had protrusions with a height of higher than 100 μm formed on the surface, the protrusions on the negative electrode surface penetrated the separator and came into contact with the positive electrode, causing a short-circuit failure. In the negative electrodes other than the negative electrode b11, the heights of the protrusions formed on the surface were 80 μm or less, and no short-circuiting occurred in the batteries that employed these other negative electrodes after the charge-discharge at the fifth cycle. Thus, when a height of the protrusions formed on a negative electrode surface exceeded 80 μm, the probability of short-circuit failure in the batteries increased.
The negative electrode a3 had protrusions with a height of greater than 100 μm before the pressing process, but the height of the protrusions was reduced by the pressing process to 40 μm or less. Thus, it is believed that the battery that employed the negative electrode a3 caused no short-circuit failure because the pressing process reduced the heights of the protrusions formed on the negative electrode surface.
The batteries that employed the negative electrodes a1 to a3 exhibited good charge-discharge efficiencies and capacity retention ratios comparable to those of the batteries using the negative electrodes b1 and b2. This demonstrates that the battery employing the negative electrode in which the height of the protruding portions on the negative electrode surface has been reduced by the pressing process shows a performance comparable to the battery using the negative electrode in which no protrusion is formed on the surface. Therefore, the pressing process for reducing the heights of the protrusions formed on the negative electrode surface causes no adverse effect on the charge-discharge cycle performance of the batteries fabricated. As will be understood clearly from the above-described results, the present invention makes it possible to provide a manufacturing method of batteries that are safe and excellent in productivity.
Only selected embodiments have been chosen to illustrate the present invention. To those skilled in the art, however, it will be apparent from the foregoing disclosure that various changes and modifications can be made herein without departing from the scope of the invention as defined in the appended claims. Furthermore, the foregoing description of the embodiments according to the present invention is provided for illustration only, and not for limiting the invention as defined by the appended claims and their equivalents.
This application claims priority of Japanese patent application No. 2005-096441 filed Mar. 29, 2005, which is incorporated herein by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2005-096441 | Mar 2005 | JP | national |