7383699
The present invention relates to a product, a process for its preparation, and the use of such product in glass. More particularly, the present invention relates to a process that produces a solid state particle that is particularly useful in the production of glass products, such as flat glass, fiberglass, container glass, lighting glass, tableware, and the like.
Processes, and materials for such processes, for the manufacture of glass have millenniums of development. In particular, glass manufacturers have been, and continue to be, concerned with the components, thermodynamics and other characteristics of the glass-making reactions in glass furnaces. The glass reaction generally involves the reaction of materials to produce a composition containing the reacted and/or dispersed components of silica (silicon dioxide from sand, quartz and the like), soda ash (sodium carbonate), and lime (calcium oxide from quicklime, hydrated lime and the like) with other optional components, generally metal oxides of lead, lithium, cerium, iron, magnesium, potassium, barium, borax and the like.
Various considerations have addressed such processes by varying the feed materials and the process schemes for the reaction of such compositions. Such considerations include, for example, reaction of a portion of the materials before creating a total glass batch. For example, one scheme is pretreatment of the batch constituents by calcining the limestone and/or dolomite constituents so as to decompose the carbonates to oxides. This calcining releases carbon dioxide from the material added to make the total glass batch. This elimination of carbon dioxide before melting begins is advantageous since it reduces the entrapping of gaseous inclusions in the glass. Other schemes involve using various components to attempt to effect the reaction's thermodynamics or quality or yield results. While advances have been made, there still exists the need for developing processes and feed materials to improve the glass-making processes.
In U.S. Pat. No. 3,082,102, heating of the batch mixture is performed prior to melting to effect reaction between silica and soda ash to produce sodium metasilicate. The temperature is limited to 820.degrees Centigrade for soda-lime-silica glass to avoid producing a molten phase that would lead to clogging of the preliminary heating apparatus.
In U.S. Pat. No. 3,682,666, a similar process of reacting the whole batch mixture to produce silicates prior to melting is disclosed in which a lowered reaction temperature between 600.degrees Centigrade and 787.degrees Centigrade. Such is made possible by the inclusion of a small amount of halide.
In U.S. Pat. No. 3,817,776, a process is disclosed to partially react preheated sand grains to sodium silicate by contact with molten caustic soda. The remainder of the batch ingredients are added subsequently. This process has the disadvantage of requiring the use of caustic soda, which is more costly than soda ash as a source of sodium for making glass. Also, the process of contacting solids with molten material is more difficult to control and more prone to plugging than a solid state reaction.
In U.S. Pat. No. 3,883,364, glass furnace dusting problems are reduced by providing a process for sintering alkaline earth carbonate to be charged to a glass furnace.
In U.S. Pat. No. 4,248,615, an energy conserving glass manufacturing process is provided in which agglomerants are preconditioned prior to supplying them to a verticle bed for glass manufacturing.
In U.S. Pat. No. 4,539,030, an example of a calcining pretreatment is disclosed. Calcining requires temperatures in excess of 1600 degrees Fahrenheit (870 degrees Centigrade), which precludes treatment of the whole batch mixture because such temperatures would cause fusion of other constituents of the batch, particularly the soda ash or other soda source.
In U.S. Pat. No. 4,920,080, silica is reacted with sodium carbonate to form sodium silicate in as a preliminary step in a glass melting process. The method preferably calcines calcium carbonate-containing batch materials separately before combining with sodium silicate as liquefying is initiated. The process materials are preheated and pre-reacted in two separate portions to optimize prior to initiation of melting.
In U.S. Pat. No. 5,004,706, a process is provided to address problems of stickiness of glass batches by pre-reaction of a portion of the glass batch.
The present invention discloses a process that includes preferentially reacting a portion of a glass batch within the total glass batch. This preferential reaction is accomplished by reacting a solid state particle containing a portion of the total glass batch thus effectively creating an inhomogeneity in the total glass batch. The components reacted in this preferential reaction are exothermic in nature and effectively lower the eutectic character of the total glass batch.
The present invention further discloses a solid state particle comprising silicon, calcium and magnesium that creates an inhomogeneity within the total glass batch. The solid state particle produced according to the process of the present invention is useful in the production of glass products, such as flat glass.
The present invention further discloses a glass composition comprising silica, soda ash, lime or limestone, a solid state particle containing silicon dioxide, calcium hydroxide, magnesium oxide, and magnesium hydroxide, and other optional metal oxides.
The solid state particle of the present invention is particularly useful in production of glass product such as flat glass, fiberglass, container glass, lighting glass, tableware, and the like.
One embodiment of the present invention is a process that includes preferentially reacting a portion of a glass batch within the total glass batch. This preferential reaction is accomplished by reacting a solid state particle containing a portion of the total glass batch thus effectively creating an inhomogeniety in the total glass batch. The components reacted in this preferential reaction are exothermic in nature and effectively lower the eutectic character of the glass batch compared to that eutectic character present without such selection. “Eutectic character” of a glass batch is defined as the temperature needed by two or more batch components in physical contact with each other to drive the glass-forming reactions as well as the path of the reaction and the impact of such on the reaction kinetics and speed. “Solid state particle” refers to a mixture of compounds such as silicon dioxide, calcium hydroxide, magnesium oxide, and magnesium hydroxide that, when heated, will initiate a solid state reaction within the particle that concludes with the production of a new compound such as calcium magnesium silicate.
In a preferred embodiment of the present invention, the solid state particle, comprising components of silicon dioxide, calcium oxide and magnesium oxide materials, creates an inhomogeniety and is located within the glass batch. The relative amount of these three components is effective to produce an exothermic reaction when heated to a reaction initiation temperature. This solid state particle is admixed with a mass containing a balance of other glass-forming materials prior to the exothermic reaction. Such other glass-forming materials may contain sodium materials and additional silicon materials as well as various other materials needed to produce the desired glass composition.
The silicon material of the solid state particle is silicon dioxide, and, more preferably, a silica flour. Preferred sources of such include sand, silica flour, nepheline syenite, and spodumene. Preferably the silicon material particle size is 90% less than 0.0075 Centimeters to promote a thermodynamic advantage towards the solid state reaction versus the standard glass reaction.
The calcium material of the solid state particle is calcium oxide and, more preferably, a calcium hydroxide. Preferred sources of such include dolomite lime, dolomitic limestone, calcite, lime, colemanite, natural diopside and wollastonite, ulexite, gypsum, fluorspar, aragonite, and feldspar. Preferably the calcium material particle size is 90% less than 0.0075 Centimeters to promote a thermodynamic advantage towards the solid state reaction versus the standard glass reaction.
The magnesium material of the solid state particle is magnesium oxide and, more preferably, a magnesium hydroxide. Preferred sources of such include dolomitic lime, dolomitic limestone, natural diopside, brucite, periclase, and epsom salt. Preferably the magnesium material particle size is 90% less than 0.0075 Centimeters to promote a thermodynamic advantage towards the solid state reaction versus the standard glass reaction.
The components of the solid state particle, the silicon material, calcium material and magnesium material are in the respective molar ratios of from about zero (0) part to about one (1) part calcium oxide and from about zero (0) part to about one (1) part magnesium oxide with respect to one (1) part silicon dioxide.
More preferably, the components of the solid state particle, the silicon material, the calcium material and the magnesium material are in the respective weight ratios of from about 0.4 parts to about 0.6 parts calcium oxide and from about 0.3 parts to about 0.4 parts magnesium oxide to one (1) part silicon dioxide.
The solid state particle size should be of a magnitude that promotes the attainment and retention of a homogenous distribution of material in the glass batch during the glass reaction. Accordingly, the solid state particle size should be of a similar magnitude of the other glass batch components, more preferably of the silicon source material, e.g. sand, used in the total glass batch. Particularly, the median size of the solid state particle material should be from about 75 percent to about 500 percent of the median size of the balancing silicon dioxide material used to produce the glass batch, even more particularly from about 85 percent to about 115 percent of the median size of the balancing silicon dioxide material.
A preferred solid state particle material is an agglomerate of minerals produced by the admixture of calcium oxide material, magnesium oxide material, silicon dioxide and water. The agglomerate is formed to a particle size which approximates the sand balance to be used in the glass batch, preferably from about 0.018 centimeters to about 0.14 centimeters, more preferably, from about 0.025 centimeters to about 0.085 centimeters.
The product of the reacted solid state particle, that occurs within the total glass batch, can be a calcium magnesium silicate having an empirical formula of (CaO)x(MgO)y(SiO2)z, wherein the weight values of x and y relative to the amount of silica is sufficient to produce an exothermic reaction. Preferably, x, y, and z have the respective ranges from about zero (0) to about three (3), from about zero (0) to about one (1), and from about one (1) to about two (2). The formed calcium magnesium silicate product and the other material in the glass batch react as a total glass batch system to produce the desired glass product. Additional energy to drive the glass-forming reaction to completion is provided to the glass batch system. Preferably, the exothermic reaction provides from about 5 percent to about 20 percent of the total energy needed to perform the total glass batch reactions to produce the desired glass product.
The following examples are intended to illustrate the present invention, but not to limit the scope of protection afforded by the claims hereafter:
A glass product is to have components of silicon, sodium, calcium, magnesium, measurable in equivalents as silica dioxide (SiO2), sodium oxide (Na2O), calcium oxide (CaO), and magnesium oxide (MgO). To supply the silicon component of the glass, a sand material is selected as a feed material. The sand has a size measurement of 30 mesh to 140 mesh. To supply the calcium and magnesium components to the glass batch, the solid state particle containing the magnesium, silica, and calcium components, agglomerated with water, dried, and screened, is added to the total glass batch. The agglomerated (solid state) particles contain silicon dioxide (SiO2), hydrated calcium oxide (Ca(OH)2), hydrated magnesium oxide (Mg(OH)2), periclase (MgO), and water. This agglomerated particle material is combined with the sand to be used in an amount to complete the total silicon value of the glass batch. Soda ash is added to supply the sodium value for the glass. Since the agglomerated particle does not contain sufficient calcium value for the glass formula, limestone will be used. The total glass batch is heated to a temperature below the glass reaction temperature but sufficient to initiate an exothermic reaction in the agglomerated particles.
The exothermic reaction begins the production of calcium magnesium silicate material in the total glass batch. The temperature of the total glass batch continues to rise due to the supplied heat and the exothermic reaction heat to produce a glass reaction involving the calcium magnesium silicate material, sand, limestone, and soda ash. The exothermic reaction and glass reaction occur simultaneously for a period within the glass batch vessel until all reactions are completed producing a glass.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US01/49926 | 12/27/2001 | WO | 00 | 4/27/2004 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO03/057636 | 7/17/2003 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3082102 | Cole et al. | Mar 1963 | A |
| 3381064 | Yamaguchi | Apr 1968 | A |
| 3458331 | Kroyer | Jul 1969 | A |
| 3520705 | Shido et al. | Jul 1970 | A |
| 3682666 | Lacourrege | Aug 1972 | A |
| 3802901 | Robertson et al. | Apr 1974 | A |
| 3817776 | Gringas | Jun 1974 | A |
| 3875288 | Hoffman et al. | Apr 1975 | A |
| 3883364 | Robertson et al. | May 1975 | A |
| 3926647 | Wuhrer | Dec 1975 | A |
| 3941574 | Melkonian et al. | Mar 1976 | A |
| 3956446 | Eirich et al. | May 1976 | A |
| 3967943 | Seeley | Jul 1976 | A |
| 3969100 | Kuna et al. | Jul 1976 | A |
| 4023976 | Bauer et al. | May 1977 | A |
| 4026691 | Lovett et al. | May 1977 | A |
| 4028131 | Pons | Jun 1977 | A |
| 4110097 | Chevallier et al. | Aug 1978 | A |
| 4238217 | Stepanek et al. | Dec 1980 | A |
| 4248615 | Seng et al. | Feb 1981 | A |
| 4252754 | Nakaguchi | Feb 1981 | A |
| 4300879 | Goldmann et al. | Nov 1981 | A |
| 4474594 | Lazet | Oct 1984 | A |
| 4519814 | Demarest, Jr. | May 1985 | A |
| 4539030 | Demarest, Jr. et al. | Sep 1985 | A |
| 4576644 | Goldmann | Mar 1986 | A |
| 4612292 | Richard | Sep 1986 | A |
| 4634461 | Demarest, Jr. et al. | Jan 1987 | A |
| 4920080 | Demarest, Jr. | Apr 1990 | A |
| 5004706 | Dickinson | Apr 1991 | A |
| 5100840 | Urabe et al. | Mar 1992 | A |
| 5422320 | Adams, Jr. et al. | Jun 1995 | A |
| 5900052 | Nakajima et al. | May 1999 | A |
| 6211103 | Tomaino et al. | Apr 2001 | B1 |
| 6271159 | Fairchild et al. | Aug 2001 | B1 |
| 6287378 | Fairchild et al. | Sep 2001 | B1 |
| 6287997 | Fairchild et al. | Sep 2001 | B1 |
| 6336346 | Tomaino et al. | Jan 2002 | B2 |
| 6358870 | Szczesniewski et al. | Mar 2002 | B1 |
| 6420289 | Tomaino et al. | Jul 2002 | B1 |
| 6531421 | Hockman | Mar 2003 | B2 |
| 6569793 | Hockman et al. | May 2003 | B2 |
| 7260960 | Carty | Aug 2007 | B2 |
| 20020194873 | Hockman | Dec 2002 | A1 |
| 20020194882 | Hockman | Dec 2002 | A1 |
| 20060101855 | Pita-Sczcesniew | May 2006 | A1 |
| 20070021287 | Hockman et al. | Jan 2007 | A1 |
| Number | Date | Country |
|---|---|---|
| 141 105 | Apr 1980 | DE |
| 42 28 500 | Sep 1992 | DE |
| 1376473 | Mar 1972 | FR |
| 53-139621 | Dec 1978 | JP |
| 55 149122 | May 1979 | JP |
| 59 64563 | Apr 1984 | JP |
| 2 141454 | May 1990 | JP |
| 09 285849 | Apr 1997 | JP |
| 10 291852 | Nov 1998 | JP |
| 644 731 | Jan 1979 | SU |
| 823 285 | Apr 1981 | SU |
| 981 217 | Dec 1982 | SU |
| 340 257 | May 1983 | SU |
| Number | Date | Country | |
|---|---|---|---|
| 20040204304 A1 | Oct 2004 | US |