Claims
- 1. A method of manufacturing a heat resisting magnetic scale from a base composed of a non-magnetic material selected from the group consisting of non-magnetic stainless steel, copper, zinc, chrome, manganese, aluminum, their alloys and ceramics, the method comprising the steps of:
- applying a layer of magnetic material to the surface of the base,
- exposing a selected portion of the base and magnetic material to a high energy density beam to melt and mix at least a part of the magnetic material and the base portion which is disposed below the material,
- immediately and rapidly cooling the melted and mixed portion to raise the Curie point of the magnetic material to above 100.degree. C. and to solidify the mixed portion to become integrated with the base, the integrated mixed portion possessing great remanent magnetism sufficient to permit magnetic displacement detection.
- 2. The method according to claim 1 wherein the base is composed of stainless steel selected from a group consisting of non-magnetic austenitic stainless steel, ferromagnetic ferritic stainless steel and ferromagnetic, martensite stainless steel.
- 3. The method according to claim 1 wherein the magnetic material is a ferromagnetic material and the Curie point of the magnetic material is above 300.degree. C.
- 4. The method according to claim 3 wherein the ferromagnetic material is a metal that is selected from a group consisting of iron, cobalt and nickel.
- 5. The method according to claim 3 wherein the magnetic material is particulated magnetic metal selected from a group consisting of iron, cobalt, nickel, and alloys thereof.
- 6. The method according to claim 3 wherein said ferromagnetic material is a thin film that is applied to the surface of said base by means of plating or evaporation.
- 7. The method according to claim 1 wherein the magnetic material is a ferromagnetic material and the base is made of a heat resisting alloy made of elements selected from the group consisting of copper, zinc, aluminum, iron, and chrome.
- 8. A method of manufacturing a heat resisting magnetic scale suitable for use in a high temperature environment comprising:
- selecting a heat resisting base composed of a non-magnetic material selected from the group consisting of ferritic, non-magnetic stainless steel, iron, copper, zinc, chrome, manganese, molybdenum, aluminum, their alloys, and ceramics,
- placing a metallic material on a base where the metallic material has differing magnetic properties from that of the base;
- heating and cooling at graduated locations a selected portion of said metallic material and a selected portion of the base under conditions in which the portions are joined and provide integrated graduations corresponding to the graduated locations having sufficiently different magnetic characteristics than the base to permit magnetic displacement detection and having a Curie point of in excess of 100.degree. C.
- 9. The method according to claim 8 wherein the metallic material is non-magnetic chrome or molybdenum and the base is non-magnetic austenitic stainless steel.
- 10. The method according to claim 9 wherein the metallic material is a thin film applied to the surface of said base by means of plating or evaporating.
- 11. The method according to claim 8 wherein the base is non-magnetic stainless steel.
- 12. The method according to claim 8 wherein the metallic material is a powder selected from the group consisting of magnetic zinc, iron, chrome, nickel, manganese, or an alloy thereof and said base is a non-magnetic material.
- 13. A method of manufacturing a heat resisting magnetic scale suitable for use in a high temperature environment comprising:
- selecting a heat resisting base composed of a magnetic material selected from the group consisting of magnetic stainless steel, iron, nickel, cobalt, and their alloys,
- placing a metallic material on a base where the metallic material has differing magnetic properties from that of the base;
- heating and cooling at graduated locations a selected portion of said metallic material and a selected portion of the base under conditions in which the portions are joined and provide integrated graduations corresponding to the graduated locations having different magnetic characteristics than the base to permit magnetic displacement detection and having a Curie point of in excess of 100.degree. C.
- 14. The method according to claim 13 wherein said base is magnetic and said powder is non-magnetic.
- 15. The method according to claim 14 wherein the powder is copper, aluminum, or an alloy thereof.
- 16. A method of manufacturing a heat resisting magnetic scale comprising:
- heating a selected target portion of a base with a sweeping, focusable, high energy density beam, the base being composed of a metal selected from the group consisting of stainless steel, copper, zinc, chrome, manganese, aluminum, their alloys, and ceramics, the beam having a focal distance of 0 .+-.100 mm from the surface of the base and providing irradiating energy per unit length of 20-300 kJ/m and a sweeping speed of 0.1-15 m/min.
- mixing and fusing the heated target portion with the surrounding portions o the base to form an integral structure,
- by immediately and rapidly cooling the selected portion and transforming the heated and cooled portion of the base from non-magentic to magnetic, and
- increasing the Curie point of the heated portion to above 100.degree.0 C.
- 17. The method according to claim 16 wherein he heat resisting base is made of austenitic stainless steel possessing a face centered cubic crystal lattice and converting the crystal lattice to body-centered cubic.
- 18. The method according to claim 16 wherein eh stainless steel is selected from a group consisting of non-magnetic austenitic stainless steel, ferromagnetic ferritic stainless steel and ferromagnetic martensite stainless steel.
- 19. The method according to claim 16 wherein the heat resisting base is composed of a ferromagnetic material.
- 20. The method according o claim 19 wherein the ferromagnetic material is a carbon steel and further comprising the sep of hardening the target portion by heating.
- 21. The method according to claim 19 wherein he ferromagnetic material is an alloy the target portion of which is softened by heating.
- 22. The method according o claim 16 wherein the heating is conducted with electron beams having a output of 0.1-15 kW.
- 23. The method according to claim 16 wherein the heating is conducted with laser beams.
- 24. The method according to claim 16 further including the step of applying a layer of particulated material having different magentic properties form the base, on the base prior to beam heating where the particulated material is melted, mixed with and fuses to the base.
- 25. The method according to claim 24 wherein eh particulated material is selected from the group consisting of iron dust, nickel dust and cobalt dust.
- 26. A method according to claim 16 further including the step of applying a thin layer of ferromagnetic material having magentic properties measurably different from those of the base after mixing and fusing in the target portions.
- 27. The method according o claim 26 wherein said scale is suitable for use in high temperature environments, further comprising the step of applying a particulated magnetic material to the surface of the base and where the heating and cooling of the target portions is achieved by exposing selected portions to a high energy density beam to melt and mix the particulated magentic material and the base in the target portion.
- 28. A method of manufacturing a heat resisting magnetic scale comprising the steps of:
- heating at least a portion of a stainless steel base wherein the stainless steel base is selected from a group consisting of stainless steels having a lattice structure providing magnetic characteristics having a Curie point of at least 100.degree. C. and stainless steels having another lattice structure providing non-magnetic characteristics;
- immediately and rapidly cooling the portion which has been heated,
- whereby the heating and cooling steps convert the lattice structure of the heated and cooled portion from one to the other lattice structure and thereby change the portion from one to the other magnetic characteristic.
- 29. A method of manufacturing a heat resisting magnetic scale comprising the steps of:
- heating at least a portion of a heat resisting stainless steel base, the base being selected from a group consisting of stainless steels having a Curie point of less than 100.degree. C. and a first level of magnetism,
- immediately and rapidly cooling said portion which has been heated to change the Curie point of the heated portion to above 100.degree. C. and the magnetism to a second level,
- whereby the first and second levels of magnetism of said heated and cooled portion of said base are sufficiently different to permit magnetic displacement detection at temperatures in excess of 100.degree. C.
- 30. A magnetic scale produced according to the method of claim 1.
- 31. A magnetic scale produced according to the method of claim 8.
- 32. A magnetic scale produced according to the method of claim 13.
- 33. A magnetic scale produced according to the method of claim 16.
- 34. A magnetic scale produced according to the method of claim 29.
Priority Claims (3)
Number |
Date |
Country |
Kind |
62-217315 |
Aug 1987 |
JPX |
|
62-217316 |
Aug 1987 |
JPX |
|
62-33588 |
Dec 1987 |
JPX |
|
RELATED APPLICATIONS
This is a continuation-in-part application of Ser. No. 237,384 filed Sept. 29, 1988, now U.S. Pat. No. 4,935,070 issued on June 19, 1990.
US Referenced Citations (5)
Number |
Name |
Date |
Kind |
2914756 |
Heidenhain et al. |
Nov 1959 |
|
3243692 |
Heissmeier et al. |
Mar 1966 |
|
4510371 |
Nakamura et al. |
Apr 1975 |
|
4552596 |
Ichiyama et al. |
Nov 1985 |
|
4871624 |
Nakamura |
Oct 1989 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
48-10655 |
Apr 1973 |
JPX |
Non-Patent Literature Citations (2)
Entry |
Kamewaka et al., "A Magnetic Guidance Method for Automated Guided Vehicles", pp. 69-74, 12/87. |
Uemura et al., "Application and Precision of Measuring Instrument Using Magnetic Scale", vol. 20, pp. 12-19, 12/87. |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
237384 |
Sep 1988 |
|