Patent Application
20150307765
The present disclosure relates to a method of manufacturing a metal composite material, a metal composite material, a method of manufacturing a heat dissipating component, and a heat dissipating component.
In recent years, along with improvement in the performance and increase in the operation speed of semiconductor devices used for CPU (Central Processing Unit), GPU (Graphics Processing Unit) or the like, the amount of heat generated from the semiconductor devices have been increased year by year. The temperature of semiconductor devices is increased along with increase in the amount of generated heat, and this results in a problem such as erroneous operation.
Then, for avoiding occurrence of such a problem, various techniques for dissipating heat and cooling the semiconductor devices have been proposed. For example, there has been proposed means of attaching a heat diffusion plate (heat spreader) comprising a highly heat conductive metal to a semiconductor device and attaching a heat sink having heat dissipation fins to the heat spreader. In this case, heat generated from the semiconductor device to be cooled is once diffused to the heat spreader and then dissipated by the heat sink.
Further, there has been also proposed means of interposing, between the heat spreader and the heat sink, a heat pipe or a vapor chamber in which a working fluid is sealed in a tightly closed vessel and a capillary structure (wick) is disposed to the inner wall and dissipating heat and cooling the semiconductor devices via the heat spreader by latent heat of evaporation of the working fluid. In this case, heat generated from the semiconductor devices is once diffused to the heat spreader, the heat pipe or the vapor chamber receives the heat from the heat spreader and the working fluid is evaporated while depriving the latent heat. Then, when the vapors of the working fluid flow toward the low temperature side, the heat generated from the semiconductor devices is diffused and, as a result, the heat generating body is cooled.
Patent Documents 1 and 2 are disclosed as the related art relevant to the existent techniques described above.
In the heat dissipating component having a heat dissipating or heat conducting function as described above, highly heat conductive metals (for example, copper or aluminum) have been used as the material in order to improve the heat dissipating efficiency. Further, in the heat pipe or the vapor chamber, a wick formed of a fine copper wire braid or a wick formed of a sintered body of copper powder is used to increase the area of contact with the working fluid and improve heat dissipating efficiency. However, since such a metal has prescribed heat conductivity, the heat dissipating efficiency cannot be improved further in view of the material and still leaves a room for improvement in this respect.
Exemplary embodiments provide a method of manufacturing a metal composite material, a metal composite material and a method of manufacturing a heat dissipating component, and a heat dissipating component, which can improve the heat dissipating efficiency.
A method of manufacturing a metal composite material according to an exemplary embodiment includes:
an adhesion step of applying a mechanical impact force to a carbon material and a metal powder at such an intensity as capable of pulverizing the carbon material, thereby adhering the carbon material to a surface of the metal powder.
According to the method, a carbon material is adhered to the surface of a metal powder in an adhesion step. Since the carbon material having higher heat conductivity than the metal powder is exposed to the surface of the metal composite material, the heat conductivity of the metal composite material can be improved.
Further, in the adhesion step, at least a portion of the carbon material is pulverized and the hydrophilicity of the carbon material is improved by the pulverization. Since the carbon material improved in the hydrophilicity is exposed to the surface of the metal composite material, the hydrophilicity of the metal composite material can be improved. Accordingly, when the metal composite material is used as the wick for the heat pipe or the vapor chamber, the working fluid can be penetrated also in narrow gaps and the area of contact with the working fluid can be increased to obtain a large heat dissipating area. Thus, the heat dissipating efficiency can be improved.
A metal composite material according to an exemplary embodiment includes:
a metal powder; and
a carbon material which is activated at its surface and thereby is provided with hydrophilicity,
wherein the carbon material is adhered to the metal powder and the adhered carbon material is exposed to a portion of the surface of the metal powder.
With the constitution described above, the heat conductivity of the metal composite material can be improved by exposing the carbon material having higher heat conductivity than the metal powder to the surface of the metal composite material. Further, since the carbon material provided with hydrophilicity is exposed to the surface of the metal composite material, the hydrophilicity of the metal composite material can be improved. Accordingly, when the metal composite material is used as a wick of a heat pipe or a vapor chamber, a working fluid can be penetrated also in narrow gaps and the area of contact of the working fluid to obtain a large heat dissipating area. Thus, the heat dissipating efficiency can be improved.
A method of manufacturing a heat dissipating component according to an exemplary embodiment includes:
an adhesion step of applying a mechanical impact force to a carbon material and a metal material to such an extent of intensity as capable of pulverizing the carbon material thereby forming a metal composite material where the carbon material is adhered to a surface of the metal powder; and
a sintering step of disposing the metal composite material to a surface or an inner space of a heat dissipating component and heating the heat dissipating component, thereby adhering the metal composite material to the surface or an inner wall surface of the heat dissipating component.
According to the method, a carbon material is adhered to the surface of a metal powder in an adhesion step. Since the carbon material having higher heat conductivity than the metal powder is exposed to the surface of the metal composite material, the heat conductivity of the metal composite material can be improved. Further, in the adhesion step, at least a portion of the carbon material is pulverized and the hydrophilicity of the carbon material is improved by the pulverization. Since the carbon material improved in the hydrophilicity is exposed to the surface of the metal composite material, the hydrophilicity of the metal composite material can be improved. Then, in the sintering step, such metal composite material is adhering to the surface or the inner wall surface of the heat dissipating component, the heat conductivity and the hydrophilicity of the metal composite material can be improved.
A heat dissipating component according to an exemplary embodiment includes:
a metal composite material adhered to a surface or an inner wall surface of the heat dissipating component,
where the metal composite material has a metal powder, and a carbon material which is activated at its surface and thereby is provided with hydrophilicity, and the carbon material is adhered to the metal powder, and the adhered carbon material is exposed to a portion of the surface of the metal powder.
With the constitution described above, the heat conductivity of the metal composite material can be improved by exposing the carbon material having higher heat conductivity than the metal powder to the surface of the metal composite material. Further, since the carbon material provided with hydrophilicity is exposed to the surface of the metal composite material, the hydrophilicity of the metal composite material can be improved. Furthermore, such metal composite material is adhering to the surface or the inner wall surface of the heat dissipating component, the heat conductivity and the hydrophilicity of the metal composite material can be improved.
According to the method of manufacturing a metal composite material, the metal composite material and the method of manufacturing the heat dissipating component, and the heat dissipating component, the heat dissipating efficiency can be improved.
A preferred embodiment is to be described with reference to
In a metal composite material of this embodiment, a carbon material activated at the surface and provided with hydrophilicity is adhered to a metal powder and the adhered carbon material is exposed to a portion of the surface of the metal composite material. Specifically, in the metal composite material, a carbon material pulverized by mechanical energy and a carbon material which is not pulverized yet (which will be later called as “not-yet-pulverized carbon material”) are adhered to the surface of the metal powder and just below the surface of a metal powder, and such carbon materials are exposed to a portion of the surface of the metal composite material. More specifically, in the metal composite material, the surface is formed in a concavo-convex shape with the carbon material described above and the crystal grains of the metal powder.
As the metal powder, a powder of metal, for example, copper (Cu), silver (Ag), gold (Au), aluminum (Al), lead (Pb), tin (Sn), and indium (In), or a powder of an alloy (solder, etc.) containing at least one of such metals can be used. For the metal material, metal powders of an identical kind and different grain sizes may be used in admixture. By using a metal powder of high heat conductivity, for example, a powder of Cu, Ag, Au, Al, etc., a metal composite material of higher heat conductivity can be obtained.
As the carbon material, amorphous carbon, carbon fiber, or nanocarbon can be used. As the nanocarbon, crystalline carbon materials such as carbon nanotube (CNT), graphite, graphene, fullerene, and nanodiamond can be used. The carbon materials may be used each alone or in combination of a plurality kinds of them. By using highly crystalline nanocarbon, for example, a carbon nanotube or graphite, a metal composite material of higher heat conductivity can be obtained.
The content of the carbon material based on the metal composite material is, for example, 0.1 mass % to 5 mass %. The content of the carbon material in the metal composite material can be measured by morphological observation under ultra-high resolution power FE-SEM or transmission type electron microscope or by elemental analysis or by analysis according to JIS Z 2615 “general rules for determination of carbon in metallic materials”.
A method of manufacturing a metal composite material having the constitution described above is to be described with reference to
The method of manufacturing a metal composite material includes a mixing step of mixing a metal powder and a carbon material (step S1), an adhesion step of adhering the carbon material to the metal powder (S2), a classification step of classifying to remove not-adhered particles (step S3), and a sublimation step of partially subliming a metal powder thereby exposing a portion of the carbon material to the surface (step S4). A method of manufacturing a metal composite material by using a copper powder as the metal powder and carbon nanotubes as the carbon material is to be described.
At first, in the mixing step, a copper powder and a carbon nanotube are mixed (step S1). In the step, while the mixing ratio of the copper powder and the carbon nanotube is not restricted particularly, they are mixed, for example, such that 0.1 mass % to 5 mass % of carbon nanotubes are contained in the mixture. Further, while the shape and the grain size of the particle of the copper powder are not restricted particularly, a copper powder having a grain size of 40 μm to 3 mm is used. With the mixing ratio and the grain size described above, the carbon nanotubes can be preferably adhered to the copper powder in the next adhesion step.
The carbon nanotube has a cylindrical structure comprising a graphite sheet in a hexagonal network shape (graphene). The carbon nanotube may be single-wall carbon nanotube or multi-wall carbon nanotube. Further, it may be a fullerene-incorporated carbon nanotube. A manufacturing method of the carbon nanotube is not particularly restricted and includes, for example, an arc discharge method, a laser ablation method, and a chemical vapor deposition method.
Then, in the adhesion step, mechanical impact is applied to the mixture of the copper powder and the carbon nanotubes thereby adhering the carbon nanotubes to the surface of the copper powder and in the inside just below the surface of the copper powder (S2). The method of applying the mechanical impact includes, for example, a method of using a high speed collision device 10 shown in
The high speed collision device 10 has an impact chamber 12, a rotary shaft 13 and a disk-like rotor 14. The impact chamber 12 comprises a cylindrical stator 11 and covers (not illustrated) closing both end faces of the stator 11. The disk-like rotor 14 is rotationally pivoted by the rotary shaft 13 in the impact chamber 12. A plurality of blades 15 are secured radially to the circumference of the disk of the rotor 14. Further, the high speed collision device 10 has a circulation tube 16 opened at one end to a portion of the inner wall of the stator 11 and opened at the other end to a portion of the cover thereby forming a closed circuit. A material hopper 17 for supplying a raw material is connected to the circulation tube 16 via an on-off valve 18 and a material supply chute 19. Further, the high speed collision device 10 has a discharge chute 21 which is opened and closed by a discharge valve 20 provided to a portion of the stator 11. The discharge chute 21 is connected to a powder recovery device 22 for recovering the powder after treatment.
Then, a treatment method in the adhesion step using the high speed collision device 10 having the constitution described above is to be described.
At first, in an atmosphere where carbon nanotubes are not put to oxidation combustion, for example, in an atmosphere of an inert gas (argon gas, etc.) or nitrogen gas, the copper powder and the carbon nanotubes mixed in the mixing step are supplied by the material supply chute 19 into the impact chamber 12. In this step, the rotor 14 is rotated by the rotary shaft 13 at a circumferential speed of about 50 m/s to 150 m/s for 1 to 3 minutes by driving means (not illustrated) in a state of closing the on-off valve 18 and the discharge valve 20. Thus, the copper powder and the carbon nanotubes are scattered while being rotated at a high speed in the impact chamber 12 and in this course, collide under rotation against the surface of the stator 11 and the blade 15. The copper powder and the carbon nanotubes are circulated through the circulation tube 16 opened to the stator 11 and then supplied again to the impact chamber 12. As described above, the copper powder and the carbon nanotubes are circulated by a plurality of cycles between the impact chamber 12 and the circulation tube 16 along with the rotation of the rotor 14. Due to repetitive collision against the stator 11 and the rotor 14 during the process, an intense mechanical energy is generated at the surface of the carbon nanotubes and a portion of the carbon nanotubes is pulverized. In the thus pulverized carbon nanotubes, mechanical energy of pulverization, etc. is accumulated in the state of the chemical energy at the surface and, as a result, change of the physicochemical property is induced to increase the surface activity (mechanochemical effect). By the mechanochemical effect, hydrophilicity is increased in the carbon nanotubes after pulverization.
During circulation between the impact chamber 12 and the circulation tube 16, an impact force between particles to each other is applied to the copper powder and the carbon nanotubes in addition to the impact force against the stator 11 and the blade 15 described above. Due to the mechanical impact force, the carbon nanotubes are adhered to the surface of the copper powder and, further, the carbon nanotubes adhered to the surface of the copper powder are hit by collision between the copper powder to each other and the carbon nanotubes are buried just below the surface of the copper powder. That is, the carbon nanotubes are adhered to the surface of the copper powder and just below the surface of the copper powder by the mechanical impact force given by the rotation of the rotor 14. Thus, a metal composite material 1 comprising composite carbon nanotubes and copper powder is formed, and an adhesion layer 2 where the crystal grains of the copper powder and the carbon nanotube are adhered is formed at the outermost surface of the metal composite material 1 as shown in
Then, after lapse of a predetermined time, a sample containing the metal composite material 1 after the treatment is recovered through the discharge chute 21 to the recovery device 22 by opening the discharge valve 20 shown in
In the adhesion step described above, since the carbon nanotubes are buried in the copper powder, detachment of the carbon nanotubes from the copper powder is suppressed and a homogeneous composite material can be obtained in the subsequent step (sublimation step).
As shown in
Then, in a sublimation step, the metal composite material 1 recovered by the classification step is heated to sublimate the surface of the metal composite material 1, that is, a portion of copper in the adhesion layer 2 (step 4). Specifically, the metal composite material 2 is heated in an atmosphere where the carbon nanotubes are not put to oxidative combustion (for example, in vacuum, inert gas, or nitrogen gas) under sublimation condition for copper to sublimate a portion of copper in the adhesion layer 2. More specifically, the metal composite material 1 is heated, for example, in an atmosphere at vacuum degree of 1×10−3 Pa to 1×10−4 Pa and at a temperature of 800° C. to 1100° C. in a vacuum furnace to sublimate the portion of the copper in the adhesion layer 2 and to expose the carbon nanotubes in the adhesion layer 2 to a portion of the surface of the metal composite metal 1 (for example, for about 1% to 70% of the surface area). The sublimation time is not particularly restricted and may be set such that the carbon nanotubes are exposed for 1% to 70% of the surface of the metal composite material 1. The extent of the exposure of the carbon nanotubes in the metal composite material 1 can be measured, for example, by texture observation by an ultra-high resolution power FE-SEM or an electron microscope.
As shown in
As has been described above, since the metal composite material 1A (or metal composite material 1) is excellent in the heat conductivity and the hydrophilicity, the material can be applied extensively to heat dissipating components having heat dissipating or heat conductive function such as heat pipe, vapor chamber, heat spreader, heat sink, or heat exchanger. Specific examples of applying the metal composite material 1A to such heat dissipating components are described below.
At first, description is to be made to a case of applying the metal composite material 1A described above to a heat pipe.
As the material for the heat pipe, copper is used typically. As shown in
At first, in the disposing step shown in
The sintering step described above can be performed by a known sintering method, for example, a pulsative electric current sintering method, hot press method, vacuum sintering method, gas pressure sintering method, hot isostatic pressure sintering method, etc. The sintering step is performed, preferably, in vacuum or in an inert gas atmosphere. Further, sintering conditions such as sintering temperature may be properly determined in accordance with the sintering method to be adopted, the kind of the metal powder to be used, the sublimation conditions for the metal powder to be adopted (vacuum degree, temperature, etc.).
Then, after the sintering step, the heat pipe 30 can be manufactured by injecting a working fluid into the container 31, evacuating the inside of the container 31, and sealing the end on the side of the condensation.
In the application method described above, the metal composite material 1 recovered in the classification step (S3) is disposed in the container 31. However, as shown in
As shown in
Then, in a continuous vacuum furnace, the thinned copper wire 41 is heated under the sublimation condition for copper, to sublimate a portion of copper of the copper wire 41 (specifically, the surface of the metal composite material 1 buried in the copper wire 41). Thus, a portion of the carbon nanotubes in the metal composite material 1 is exposed to a portion of the surface of the copper wire 41 and the surface of the copper wire 41 is formed into a concavo-convex shape with the carbon nanotubes and copper. That is, the metal composite material 1A is formed at the surface of the copper wire 41.
Successively, a wick member comprising a braid can be formed by braiding the thus formed copper wires 41 (fine wires) into a mesh state. Further, the copper wire 41 (fine wire) formed as described above can also be used as the wick member comprising the bundle of fine wires. The wick member comprising the braid and the wick member comprising the bundle of the fine wires can be used also as the wick member for a vapor chamber to be described below.
Then, the wick member comprising the braid or the wick member comprising the bundle of fine wires is disposed in the container sealed at one end. Successively, by heating the container, the wick member is adhered to the inner wall surface of the container. Then, a heat pipe having the wick member comprising the braid and the wick member comprising the bundle of fine wires can be manufactured by injecting a working fluid into the container and evacuating the inside of the container and sealing the other end.
As shown in
Then, in the vacuum furnace, a portion of the surface of copper in the metal composite material 1 rubbed into the grooves 50G of the copper tube 50 is sublimated and a portion of the carbon nanotubes in the metal composite material 1 is exposed to a portion of the surface of the grooves 50G. Thus, a wick of grooves comprising the metal composite material 1A where the surface is formed into a concavo-convex shape with the carbon nanotubes and copper is formed to the inner wall 50A of the copper tube 50.
The copper tube formed as described above is cut into a predetermined length, one end of the copper tube 50 is sealed, a working fluid is injected into the copper tube 50, the inside of the copper tube 50 is evacuated, and the other end of the copper tube 50 is sealed. Thus, a heat pipe having a wick of the grooves comprising the metal composite material 1A can be manufactured.
Then, description is to be made to an example of applying the metal composite material 1A described above to a vapor chamber.
As the material for the vapor chamber, copper is used typically. The vapor chamber is a flat heat pipe. Therefore, the vapor chamber has a structure substantially identical with the heat pipe that transports heat due to phase change between evaporation and condensation of a working fluid sealed in a container. The vapor chamber has a wick for promoting circulation of the working fluid in the same manner as the heat pipe. A method of manufacturing a vapor chamber having a wick comprising a sintered body of the metal composite material 1A is to be described.
At first, as shown in
Then, as shown in
In the application method described above, the metal composite material 1 recovered in the classification step (step S3) is disposed in the container parts 60, 61. However, the metal composite material 1A after the sublimation step (S4) may be disposed in the container parts 60, 61 in the same manner as the method shown in
Then, description is to be made to an example of using the metal composite material 1A described above to a heat spreader.
A heat spreader is a heat diffusing plate for releasing heat generated from the semiconductor device during operation to ambient air. At first, the structure of the heat spreader is to be described.
As shown in
The constitution shown in
Then, a method of using the metal composite material 1A to the heat spreader 70 constituted as described above is to be described.
At first, as shown in
Successively, the metal composite material 1 is rubbed into the upper surface 71A including the inside of the grooves 74 by friction stir welding to adhere the metal composite material 1 to the upper surface 71A. Then, by heating the heat spreader 70 in which the metal composite material 1 is adhered in a vacuum furnace under the sublimation condition for copper, a portion of copper in the metal composite material 1 is sublimated to expose a portion of the carbon nanotubes in the metal composite material 1 to the upper surface 71A of the heat spreader 70. Thus, the metal composite material 1A where the surface is formed into a concavo-convex shape with the carbon nanotubes and copper can be formed to the upper surface 71A of the heat spreader 70.
Then, description is to be made to an example of using the metal composite material 1A to an ambient air heat dissipating flat plate.
In the same manner as in the heat spreader described above, grooves for a depth of about 0.1 mm to 1 mm are fabricated at a predetermined pitch to the surface of a copper plate, and a metal composite material 1 is filled in the grooves. Successively, the metal composite material 1 is rubbed into the surface of the copper plate by friction stir welding to adhere the metal composite material 1 to the surface of the copper plate. Then, copper in the metal composite material 1 adhered to the copper plate is sublimated in vacuum to expose a portion of the carbon nanotubes in the metal composite material 1 to a portion of the surface of the copper plate, thereby forming a metal composite material 1A where the surface is formed into a concavo-convex shape with the carbon nanotubes and copper to the surface of the copper plate.
The metal composite material 1A may also be formed to the surface of the copper plate by laying the metal composite material 1 throughout the surface of the copper plate and hot press bonding the same by vacuum hot press. In this case, the copper plate, etc. may also be heated, for example, by supplying a high current in a pressurized state. This can improve the manufacturing efficiency.
In products where heat generation gives significant effect on the life and the reliability of products, a technique of cooling and dissipating heat more efficiently has been demanded generally. For example, by applying the metal composite materials 1, 1A to a heat sink plate provided to an LED bulb, the LED bulb can release heat and can be cooled efficiently. This can extend the life of the LED bulb.
Further, in existent small-sized projectors, since heat dissipation giving an effect on the product life cannot be effected sufficiently, they are used while suppressing the brightness. On the contrary, since heat can be dissipated sufficiently by adopting the heat dissipating components using the metal composite materials 1, 1A of this embodiment to the small-sized projectors, it is expected that suppression of the brightness is no more necessary.
Further, heat conductivity or electric conductivity can be improved also in bonding metals or alloys such as solder or indium used for jointing metals by sintering the metal composite material 1, 1A described above at a high pressure to large plane or flat plane. Therefore, it is also possible to manufacture a bonding member used for jointing metals which is improved in the heat conductivity or electric conductivity.
The embodiments described above can provide the following advantageous effects.
(1) In the metal composite material 1, 1A, carbon nanotubes having heat conductivity three times or four times as high as that of copper are exposed to the surface of the metal composite material. Accordingly, heat tends to transfer on the surface of the metal composite material 1, 1A, and the heat conductivity of the metal composite material 1, 1A can be improved outstandingly compared with that of the copper powder before composition.
(2) The carbon nanotubes exposed to the surface of the metal composite material contain carbon nanotubes which are pulverized and thereby activated at the surface, that is, carbon nanotubes having high hydrophilicity. Accordingly, the hydrophilicity of the metal composite material 1, 1A can be improved greatly compared with that of the copper powder before composition. Thus, when the metal composite material 1, 1A is used, for example, to the wick of a heat pipe or a vapor chamber, the working fluid can be penetrated even in narrow gaps and a large heat receiving and heat dissipating area can be obtained. This can improve the heat receiving efficiency and the heat dissipating efficiency.
(3) The surface of the metal composite material 1A is formed into a concavo-convex shape with the carbon nanotubes and copper. Thus, since the surface area of the concavo-convex shape 1A is increased, the area of contact with the working fluid can be increased greatly when the metal composite material 1A is used to the wick of the heat pipe or the vapor chamber. Thus, the heat receiving efficiency and the heat dissipating efficiency can be improved.
(4) By laying the metal composite material 1, 1A where the carbon nanotubes are exposed at the surface throughout the ambient air heat dissipating portion, the degree of emitting ultra-red rays is increased and it is possible to easily release the heat into the ambient air.
(5) By using the metal composite material 1, 1A to various kinds of heat dissipating components, heat can be dissipated efficiently from the heat generating body. Accordingly, this can contribute to improve the reliability and extend the life of the heat generating body. Further, since the size of the heat dissipating components can be decreased, it can contribute also to the size-reduction of device.
The embodiments described above can be practiced in the following properly modified embodiments.
The embodiments described above are more specifically described with reference to examples and comparative examples.
A copper powder of 100 μm of average grain size, and carbon nanotubes having an average diameter of 10 nm to 25 nm and an average length of 2 μm to 10 μm were prepared and weighed such that the carbon nanotubes were contained by 1.0 mass % in the mixture of the copper powder and the carbon nanotubes. The mechanical impact force was applied to the mixture using the high speed collision device 10 shown in
On the other hand, the metal composite material recovered as described above was disposed in a concave portion of a heat spreader sized 30×30 mm and having 3 mm thickness for the plate portion. The heat spreader was placed in a vacuum furnace and a portion of copper was sublimated under the sublimation condition at a vacuum degree of 1×10−3 Pa and at a temperature of 900° C. to expose the carbon nanotubes by 50% for the surface.
For the heat spreader manufactured as described above, wettability to water was evaluated. The result is shown in
In ambient air, the state at the bottom of the concave portion of the heat spreader in Example 1 was observed when 20 μl of pure water was dropped to be bottom (refer to
As apparent from
On the contrary, in Example 1, dropped pure water was instantly sucked to the inside of the heat spreader and it was confirmed that the wettability to pure water, that is, the hydrophilicity was improved. This is considered that the hydrophilicity of the carbon nanotubes pulverized in the adhesion step was improved and, the carbon nanotubes were exposed at the bottom of the concave portion of the heat spreader. Further, in Example 1, deterioration of the wettability was not confirmed even when the same measurement was repeated in ambient air. That is, in Example 1, the surface of the heat spreader was not oxidized even when the surface was exposed to the ambient air. This is considered that oxidation is prevented mechanochemically by the carbon nanotubes present on the surface of the heat spreader.
A heat spreader made of copper sized 30×30 mm and having a thickness of 3 mm for the plate portion was used for the measurement.
In a state of directing the bottom of the concave portion upward and opening the upper portion to ambient air in the heat spreader of each example, 1000 μl of pure water was dropped to the bottom of the concave portion at a room temperature. Then, a heater block in contact with the surface of the heat spreader on the side opposite to the bottom of the concave portion of the heat spreader was heated by a heater (100° C.), to measure the temperature change inside the heater block.
As apparent from
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011-014183 | Jan 2011 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13315546 | Dec 2011 | US |
| Child | 14792093 | US |