1. Field
The present disclosure relates to a method of manufacturing a polyvinylidene fluoride (PVDF)-based polymer and a method of manufacturing a stacked-type polymer actuators using the PVDF-based polymer.
2. Description of the Related Art
Electroactive polymers (EAP) are materials that respond mechanically to electrical stimulation. An EPA material is promising for various applications because it exhibits a far greater strain (several % to several tens of %) in response to electric stimulus than that (maximum of 0.2%) of conventional ferroelectric ceramics by several tens of times. Also, EAP may be easily manufactured in various forms, and is gaining a lot of attention because they can serve as sensors or actuators. In particular, the light-weight and flexible characteristics of EAP increase the usability of sensors or actuators as flexible electronic devices. In addition, EAP is capable of mimicking biological muscles which have high fracture toughness, large strain, high vibration damping, etc., and thus, are also referred to as artificial muscles.
EAP may be classified as an electronic EAP and an ionic EAP. Electronic EAP has a fast operation speed as force received by electrons is used under an electric field, but higher voltage is needed to drive it. Ionic EAP has a slow operation speed as deformation is generated due to movements of ions but needs a lower voltage for driving. Examples of electronic EAP actuators may include dielectric elastomer actuators and PVDF-based ferroelectric polymer actuators.
An example of electronic EAPs is a poly(vinylidene fluoride-trifluoroethylene-chlorofluoroethylene) (“P(VDF-TrFE-CFE)”), which is a relaxor ferroelectric polymer. Another example is a poly(vinylidene fluoride-trifluoroethylene-chlorotrifluoroethylene) (“P(VDF-TrFE-CTFE)”). P(VDF-TrFE-CFE) is formed of a combination of VDF, TrFE, and CFE. A thickness of an EAP layer based on a currently manufacturable PVDF is about 20 μm, and to obtain a strain of, for example, 1%, a driving voltage on the order of 600 V to 800 V is required. In order to reduce the driving voltage to a level applicable to portable electronic devices, EAP is required to have a thickness as small as about 1 μm. A stack of multiple EAP layers may be formed to obtain a desired level of power.
Provided are a method of manufacturing polyvinylidene fluoride (PVDF)-based polymers with a small thickness and a method of manufacturing stacked-type polymer actuators using the PVDF-based polymers. A polymer actuator made from the PVDF-based polymers may reduce a driving voltage.
Additional aspects will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the presented embodiments.
According to an aspect, a method of manufacturing a polyvinylidene fluoride (PVDF)-based polymer film, the method includes: applying a solution formed by dissolving a PVDF-based polymer in a solvent, on a substrate; forming a PVDF-based polymer film by evaporating the solvent; bonding a support film on the PVDF-based polymer film; reducing an adhesive force between the PVDF-based polymer film and the substrate; and separating the substrate from the PVDF-based polymer film.
The PVDF-based polymer may include P(VDF-TrEF-CTFE) (poly(vinylidene fluoride-trifluoroethylene-chloro trifluoro ethylene)) or P(VDF-TrFE-CFE) (poly(vinylidene fluoride-trifluoroethylene-chloro fluoro ethylene).
The solvent may be methyl isobutyl ketone (MIBK), methyl ethyl ketone (MEK), or dimethylformamide (DMF).
In the applying of the PVDF-based polymer solution on a substrate, an applicator or a bar-coater may be used.
The first substrate may be formed of a material coated with a hydrophilic material.
The first substrate may be formed of glass or polymer.
In the forming of a PVDF-based polymer film by evaporating the solvent, a gas flow may be introduced above the PVDF-based polymer solution. The gas flow enables a uniform evaporation of the solvent.
The gas may be an inert gas.
The support film may include a silicon elastomer or polydimethylsiloxane (PDMS).
The support film may be formed by coating a silicone elastomer or polydimethylsiloxane (PDMS) on a polyethylene terephthalate (PET) film.
In reducing an adhesive force between the PVDF-based polymer film and the first substrate, a moisturized environment may be provided to the substrate and the PVDF-based polymer film.
The moisturized environment may be formed by using water, distilled water, deionized water, or isopropyl alcohol (IPA).
An annealing operation may be further performed after the separating the first substrate from the PVDF-based polymer film.
An electrical poling operation may be further performed after the separating the first substrate from the PVDF-based polymer film.
According to another aspect, a method of manufacturing a stacked-type polymer actuator, the method includes: preparing a plurality of transfer films that are each formed of a polyvinylidene fluoride (PVDF)-based polymer film bonded on a support film; forming a first electrode layer, and transferring the PVDF-based polymer film from any one of the plurality of transfer films, on the first electrode layer; forming a second electrode layer on the transferred PVDF-based polymer film; and transferring the PVDF-based polymer film from another one of the plurality of transfer films, on the second electrode layer.
The preparing a plurality of transfer films may be performed according to the method described above.
According to another aspect, a stacked-type polymer actuator includes a plurality of electrode layers and a plurality of polyvinylidene fluoride (PVDF)-based polymer films, wherein the plurality of electrode layers and the plurality of PVDF-based polymer films are alternately stacked.
The stacked-type polymer actuator may further include a first electrode unit and a second electrode unit respectively formed with a certain distance therebetween, wherein the plurality of electrode layers are respectively alternately connected to the first electrode unit and the second electrode unit in an stacked order.
The plurality of PVDF-based polymer films may be manufactured according to the method described above.
These and/or other aspects will become apparent and more readily appreciated from the following description of the embodiments, taken in conjunction with the accompanying drawings in which:
Reference will now be made in detail to embodiments, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to like elements throughout. In this regard, the present embodiments may have different forms and should not be construed as being limited to the descriptions set forth herein. Accordingly, the embodiments are merely described below, by referring to the figures, to explain aspects of the present description.
According to the method of manufacturing a PVDF-based polymer film of
In operation S1, a PVDF-based polymer solution in which a PVDF-based polymer is dissolved in a solvent is prepared.
Next, in operation S2, the prepared PVDF-based polymer solution is applied on a substrate, and in operation S3, the solvent is evaporated to form the PVDF-based polymer film.
Next, a support film is applied to a surface of the PVDF-based polymer film to form a laminate of the PVDF-based polymer film and the support film, in operation S4, and an adhesive force between the PVDF-based polymer film and the substrate is adjusted in operation S5. Then the substrate is separated from the PVDF-based polymer film in operation S6. In addition, an annealing operation may be performed. Alternatively, an electrical poling operation may be further performed.
Next, in operation S8, the PVDF-based polymer film may be stacked where the prepared PVDF-based polymer film is needed, using a transferring method.
As illustrated in
The PVDF-based polymer solution 123 is formed by dissolving a PVDF-based polymer in a solvent. PVDF-based polymers are known in the art, and in an embodiment, ferroelectric polymers such as PVDF, P(VDF-TrFE), and relaxor ferroelectric polymers such as poly(vinylidene fluoride-trifluoroethylene-chlorofluoroethylene) (“P(VDF-TrFE-CFE)”), poly(vinylidene fluoride-trifluoroethylene-chlorotrifluoroethylene) (“P(VDF-TrFE-CTFE)”) may be used. Examples of the solvent may include methyl isobutyl ketone (MIBK), methyl ethyl ketone (MEK), dimethylformamide (DMF).
The first substrate 110 may have at least one hydrophilic surface, which surface will be bonded to the PVDF-based polymer. For example, the first subtrate may be a glass or polymer, which may be coated with a hydrophilic material.
Referring to
Next, as illustrated in
Next, as illustrated in
Next, referring to
Next, referring to
Also, in order to increase crystallinity of the PVDF-based polymer film 120, an annealing operation may be further performed. Annealing conditions such as the temperature and duration may be determined according to the desired properties of the film. For example, by optimizing a time and temperature of the annealing operation, a driving performance of the PVDF-based polymer film 120 may be improved.
In addition, an electrical poling operation for the PVDF-based polymer film 120 may be additionally performed. In the electrical poling operation, domains of dipoles that are electrically polarized are aligned in a predetermined direction by applying a high voltage to two ends of piezoelectric materials. According to the electrical poling operation, piezoelectric characteristics of the PVDF-based polymer film 120 may be improved.
According to the above-described manufacturing method, the transfer film TF including the PVDF-based polymer film 120 having a small thickness such as several micrometers, e.g., about 0.1 μm to about 5 μm, formed on the support film 130 may be manufactured, and by using the transfer film TF, the PVDF-based polymer film 120 may be easily transferred to a needed location. The PVDF-based polymer film 120 is an electronic EAP which has a higher driving voltage than that of an ionic EAP, but when manufactured to have a single micron-scale thickness according to the above-described method, a driving voltage of the electronic EAP is significantly reduced, and thus, the electronic EAP may be applied to various electronic appliances.
In the stacked-type polymer actuator 200, the PVDF-based polymer films 120 having a small thickness such as several um are used to reduce a driving voltage V. Also, a plurality of the PVDF-based polymer films 220 may be stacked so as to generate a desired power.
The PVDF-based polymer films 120 may be manufactured according to the method described with reference to
When a voltage is applied between the first electrode unit 251 and the second electrode unit 252, each of the PVDF-based polymer films 220 is deformed, and a sum of deformation forces occurring in each of the plurality of PVDF-based polymer films 220 generates a driving force driving other electronic appliances.
When manufacturing the stacked-type polymer actuator having a structure as illustrated in
A solution casting method refers to an operation in which a PVDF-based relaxor ferroelectric polymer is melted in a solvent such as methyl isobutyl ketone (MIBK) or methyl ethyl ketone (MEK) to form a PVDF-based polymer solution in a desired form, and the solvent is volatilized to a solid. In this operation, the PVDF-based polymer solution is applied using a spin coating method or an application apparatus such as an applicator. When applying the solution casting method to a stacked-type polymer structure, a solvent may permeate into layers in the lower portion of the stacked-type polymer structure when upper layers are manufactured, and thus, the lower portion of the structure may be damaged. Referring to the microscopic image of
According to the method of manufacturing a multilayer stacked polymer actuator, according to the current embodiment of the present invention, the transfer film TF manufactured in operations described with reference to
Next, an electrode layer E is formed on the PVDF-based polymer film 120, as illustrated in
Next, as illustrated in
In
The second substrate 115 may be a portion of an electronic device to which the stacked polymer actuator 300 is to be applied, or the stacked polymer actuator 300 may be separated from the second substrate 115 and be disposed on a location where needed on an electronic device.
According to the above-described manufacturing method, a thin PVDF-based polymer film having a thickness of about 1 um may be manufactured.
When manufacturing a stacked-type polymer actuator using a method of transferring a PVDF-based polymer film as manufactured above, damages to an electrode layer such as cracks or wrinkles may be reduced.
Also, the stacked-type polymer actuator manufactured according to the embodiments as described above has a structure in which a plurality of thin PVDF-based polymer films are stacked, and thus, a driving voltage thereof may be reduced while maintaining device performance. Thus, the stacked-type polymer actuator may be used in portable electronic devices for various purposes.
It should be understood that the exemplary embodiments described therein should be considered in a descriptive sense only and not for purposes of limitation. Descriptions of features or aspects within each embodiment should typically be considered as available for other similar features or aspects in other embodiments.