Patent Application
20090214841
The current invention relates to a method of manufacturing a partially fused thermoplastic membrane that is nearly twice as wide as compared to conventionally manufactured thermoplastic membranes. The current invention also relates to methods of manufacturing tubes and bladders using thermoplastic membranes. The invention also relates to method of use of glossy thermoplastic membranes for geomembrane applications.
Thermoplastic webs have found application in many areas, for example as geomembranes to retain fluids such as water. Examples of typical uses of geomembranes are as liners in ponds, reservoirs, pits, canals and the like. Examples of such liner materials are described in U.S. Pat. No. 5,160,221 to Rohe, et. al. Additional uses for such membranes include protection from weather and the like, such as in roofing applications and other building applications. In many applications, very large sheets of thermoplastic webs are desired for use. However, the manufacturing size of the web is limited by the width of the available manufacturing equipment. For example, thermoplastic extruders are provided in widths up to 13 feet or so. As a general rule the wider the extruder, the more difficult it is provide a uniform thickness and desired quality of the web. When even larger webs than can be conveniently manufactured are needed for a particular application, separate web sections are often joined in a second step at a manufacturing facility or at the point of use in the field by adhering or welding separate sheets together. Field construction can be time consuming and challenging for many reasons, including the difficulty of handling large sections at the work site, the difficulty of keeping surfaces clean to provide good bonding, and the difficulty of providing a uniform and effective bond over long seams.
For several years, fabric mesh reinforced thermoplastic membranes have been available for use as a roofing membrane. The conventional way of making such membranes is to extrude molten thermoplastic onto one side of a fabric mesh to weld the fabric mesh to one side of the thermoplastic membrane. The resulting composite is then heated and a second layer of molten thermoplastic is extruded onto the other side of the fabric mesh to cover the fabric mesh and to weld the second thermoplastic to the first thermoplastic. U.S. Pat. No. 6,054,178 to Howells describes a method of manufacturing a fabric mesh reinforced monolithic thermoplastic membrane. The open mesh fabric is drawn into the gap between two calender rollers of a membrane extruder, a molten first thermoplastic material is extruded into the throat of the gap between the first roller and the first side of the fabric mesh, while a second molten thermoplastic material is simultaneously extruded into the throat of the gap between the second roller and the second side of the fabric mesh. The composite material is then drawn through the gap between the first and second rollers to force the molten first and second thermoplastic materials into and through the open mesh of the fabric to fuse and bond the molten first and second thermoplastic materials in and about the fabric mesh to form the fabric mesh reinforced monolithic thermoplastic membrane.
Configurations of roofing materials that are covering products comprising a membrane provided with and adhesive for adhering the covering product to a building structure are described in US Patent application Nos. 2004/0157074 and 2004/0191508 to Hubbard.
In the design of geomembranes for use in containment of fluids, such as liners for landfills, canals, ponds, and similar earthen constructions, a concern has been the tendency of material placed on top of the geomembrane to slide off of the membrane, particularly if the construction involves use of some angled berms or sidewalls as part of the containment structure. Another problem can be that the geomembrane itself slides off of the berm construction on which it is placed. Geomembranes have previously been prepared to purposefully provide one or both of the surfaces of the geomembrane with a large number of projections or recesses by embossing the geomembrane to improve the friction coefficient between the surface of the geomembrane and an adjoining surface. U.S. Pat. No. 5,728,424 describes systems and processes for providing the surface of a geomembrane with a textured surface. In this patent, systems and processes for applying particles or projections onto a surface of a geomembrane are described so as to improve the friction coefficient between the surface of the geomembrane and an adjoining surface. Similarly, methods for imparting antislip surfaces to various thermoplastic products, such as geomembrane sheets and liners, including landfill friction sheet and landscape reshaping restraints, are described in U.S. Pat. No. 6,509,084. Likewise, a geomembrane construction comprising a unitary structure fabricated by co-extrusion including a center core, a thermoplastic adhesive layer secured on one side of the center core, and a textured layer secured on the opposite side of the center core is described in U.S. Pat. No. 6,524,029.
It has also been noted in an article by the PVC Geomembrane Institute that
It has surprisingly been found that partially fused thermoplastic membranes can be made using conventional dual extrusion membrane extruders. The resulting partially fused membranes as produced in this process have an effective width that is nearly twice as wide as a conventional thermoplastic membrane previously delivered from factory manufacturing setting. The present method and product thus nearly doubles the effective width of thermoplastic membranes, providing unique membrane products in a highly cost effective manner.
In one aspect of the present invention, a method for manufacturing a wide, partially fused thermoplastic membrane is provided. In this method, a release liner web is drawn into a throat between parallel, spaced apart first and second nip rollers of a membrane extruder, the release liner web having first and second sides and first and second opposed edges. A molten first thermoplastic and a molten second thermoplastic that are compatible and fusible with each other are provided. The first thermoplastic is extruded between the first side of the release liner web and the first roller, and the molten second thermoplastic is extruded into the throat of the two rollers between the second side of the release liner web and the second roller, so that the resulting first and second thermoplastic membranes are wider than the release liner web and thereby fuse the first thermoplastic and the second thermoplastic proximally to the first and second edges of the release liner web to encapsulate the release liner web. One edge of the resulting thermoplastic/release liner web composite is slit to provide the first thermoplastic membrane coated on the first side of the release liner and the second thermoplastic membrane coated on the second side of the release liner, wherein the first thermoplastic membrane and the second thermoplastic membrane are fused proximally to the second edge of the release liner web. The aforementioned process can alternatively be performed using tandem calendaring systems.
A fused thermoplastic/release liner web composite is also provided, comprising a release liner web having first and second sides and first and second opposed edges, a first thermoplastic membrane coated on the first side of the release liner web, and a second thermoplastic membrane coated on the second side of the release liner web. The first thermoplastic membrane and the second thermoplastic membrane are thermoplastically fused proximally to the second edge of the release liner web.
In another aspect of the present invention, a method of simultaneously manufacturing a plurality of thermoplastic membranes is provided comprising drawing at least one release liner web into a throat between parallel, spaced apart first and second nip rollers of a membrane extruder, the release liner web having first and second sides and first and second opposed edges. Simultaneously a molten first thermoplastic and a molten second thermoplastic is extruded into the throat of the two rollers, wherein the first thermoplastic is extruded between the first side of the release liner web and the first roller, and wherein the molten second thermoplastic is extruded into the throat of the two rollers between the second side of the release liner web and the second roller, the resulting first and second thermoplastic membranes being wider than the release liner web, to form a thermoplastic/release liner web composite. Both edges of the resulting thermoplastic/release liner web composite are slit to provide the first thermoplastic membrane coated on the first side of the release liner and the second thermoplastic membrane coated on the second side of the release liner, and wherein the first thermoplastic membrane and the second thermoplastic membrane are not fused to each other. This method advantageously allows production of thermoplastic web material at twice the rate of manufacture using conventional extrusion techniques.
In another aspect of the present invention, a method of manufacturing a fused thermoplastic membrane tube is provided comprising drawing a release liner web into a throat between parallel, spaced apart first and second nip rollers of a membrane extruder, the release liner web having first and second sides and first and second opposed edges. A molten first thermoplastic and a molten second thermoplastic that are compatible and fusible with each other are simultaneously extruded into the throat of the two rollers, wherein the first thermoplastic is extruded between the first side of the release liner web and the first roller, and wherein the molten second thermoplastic is extruded into the throat of the two rollers between the second side of the release liner web and the second roller, the resulting first and second thermoplastic membranes being wider than the release liner web and thereby fusing the first thermoplastic and the second thermoplastic proximally to the first and second edges of the release liner web to encapsulate the release liner web and to form a thermoplastic/release liner web composite. The resulting thermoplastic/release liner web composite is cut in a cross machine direction to provide a thermoplastic/release liner tube.
In another aspect of the present invention, a method of manufacturing a fused thermoplastic membrane bladder is provided comprising drawing a release liner web having a predetermined length into a throat between parallel, spaced apart first and second nip rollers of a membrane extruder, the release liner web having first and second sides and first and second opposed side edges and front and back edges. A molten first thermoplastic and a molten second thermoplastic that are compatible and fusible with each other are simultaneously extruded into the throat of the two rollers, wherein the first thermoplastic is extruded between the first side of the release liner web and the first roller, and wherein the molten second thermoplastic is extruded into the throat of the two rollers between the second side of the release liner web and the second roller, the resulting first and second thermoplastic membranes being wider and longer than the release liner web. As a result, the first thermoplastic and the second thermoplastic are fused to each other proximally to the first and second side edges and the front and back edges of the release liner web to encapsulate the release liner web and to form a thermoplastic/release liner web composite. This composite is then cut in a cross machine direction at a location that does not correspond to the release liner to provide a thermoplastic/release liner bladder.
In another aspect of the present invention, it has surprisingly been found that an amorphous or semi-crystalline thermoplastic geomembrane will exhibit exceptional interface shear resistance if one or both major surfaces of the geomembrane is provided with a surface structure that has an average gloss value that is greater than about 10 in a 20° gloss angle measurement taken in accordance with ASTM 2457-03. In another embodiment, the amorphous or semi-crystalline thermoplastic geomembrane has one or both major surfaces of the geomembrane is provided with a surface structure that has an average gloss value that is greater than about 10 in a 20° gloss angle measurement, and an average gloss value of greater than about 30 in a 60° gloss angle measurement, both sets of measurements being taken in accordance with ASTM 2457-03.
The accompanying drawings, which are incorporated in and constitute a part of this application, illustrate several aspects of the invention and together with a description of the embodiments serve to explain the principles of the invention. A brief description of the drawings is as follows:
Turning now to the drawings, wherein like numbers represent like parts,
Release liner 30 is drawn into the throat 18 under slight tension to maintain the release liner in a planar configuration. The first molten thermoplastic is extruded from the first nozzle 24 into the throat between the first side 31A of the release liner and the first roller 12. Simultaneously, the second molten thermoplastic 34 is extruded from the second nozzle 26 into the throat between the second side 31B and the second roller 14.
In one embodiment of the present invention, first roller 12 and second roller 14 are rotated at the same speed. Preferably, the rollers are maintained at the same speed that the release liner 30 is drawn into roller gap 16 between the first roller 12 and second roller 14. In an alternative embodiment of the present invention, first roller 12 and second roller 14 are rotated at different speeds with respect to each other. Preferably at least one roller is rotated at the same speed as the release liner 30 is drawn into roller gap 16 between first roller 12 and second roller 14.
In one embodiment of the present invention, release liner 30 is fed into the center of roller gap 16 with equal amounts of first and second thermoplastic being extruded into throat 18 of membrane extruder 10. In an alternative embodiment of the present invention, release liner 30 is fed into the center of roller gap 16 with a greater amount of the first thermoplastic being extruded into throat 18 than the amount of second thermoplastic being extruded into throat 18, or vice versa.
The thermoplastic/release liner web composite can optionally be prepared from two types of thermoplastic polymeric material, with one type of thermoplastic polymeric material being extruded from the first die or extruded nozzle 24 and the second thermoplastic polymeric material being extruded from the second die or extruder nozzle 26. The two thermoplastics must be compatible and must be able to fuse together to create the desired thermoplastic/release liner web composite. Preferably, the two thermoplastics will have similar thermal coefficients of expansion so that the resulting thermoplastic/release liner web composite will lie flat and not ripple.
Preferably, the first and second thermoplastics are made from materials that have similar melt indexes to facilitate fusing to each other and additionally for optional subsequent joining to additional sheets of material to form even larger continuous membranes. Preferably, the thermoplastics used in the present invention have melt indexes of 0.5 or higher, which are easier to join, e.g. by hot air welding, in the field.
The rollers are rotated as shown by the arrows to draw the release liner 30 and the extruded thermoplastic into the gap 16 between the rollers to fuse the first and second molten thermoplastic together and to encapsulate release liner 30 to form a thermoplastic/release liner web composite 38. The thermoplastic/release liner web composite 38 is preferably drawn from the gap at a speed of 4 to 8 feet per minute, although other speeds can be employed. As the thermoplastic/release liner web composite leaves the throat, the first side of the thermoplastic/release liner web composite 45A preferably is kept in contact with the surface of the first roller 12 to maintain the temperature of the thermoplastic/release liner web composite at an appropriate temperature to complete the fusing of the thermoplastic. The maintenance temperature varies for different thermoplastic melting points. The thermoplastic/release liner web composite 38 leaves the first roller and moves to the third roller 20 wherein the second side 45B of the thermoplastic/release liner web composite 38 contacts the surface of the roller 20 to additionally cool the second side and solidify it. The second and third rollers 14 and 20 are cooled with ambient temperature water. After leaving the gap and until the thermoplastic/release liner web composite leaves the nip roll set, the thermoplastic is still in a plastic or soft state, but has set, and can be imprinted with surface features if desired. More specifically, a particular finish can be applied to the thermoplastic/release liner web composite by imparting a particular finish to the surface of one or more rollers in the manufacturing process. The roller can be polished, smooth, roughened, or imprinted with a particular design, and the like, which is imparted into the side of the thermoplastic/release liner web composite when it is still in the relatively plastic state.
Between the third roller 20 and the take up reel 22, the thermoplastic/release liner web composite 38 is exposed to ambient air to cool the thermoplastic/release liner web composite down to ambient temperature.
Additionally, between the third roller 20 and the take up reel 22, the thermoplastic/release liner web composite 38 passes through a slitting assembly 50 where the web is slit into trim waste 54 and thermoplastic/release liner web composite 52 that is fused on only one edge. The slitting assembly can be provided by different types of slitting arrangements, but preferably is provided by a stationary blade. Trim waste 54 is preferably collected in hopper 56 for recycling. The cooled and slit thermoplastic/release liner web composite 52 is rolled into a roll 40 for transportation and storage.
First thermoplastic membrane 25 and second thermoplastic membrane 27 are normally prepared in thicknesses of from 10 to 100 mils, although thicker membranes may be prepared and it may be possible to prepare membranes thinner than 10 mils. In preferred embodiments, the total width of the fused thermoplastic membrane (i.e. the bonded width of first thermoplastic membrane 25 in combination with second thermoplastic membrane 27 as fused) is greater than 10 feet, more preferably greater than 20 feet, and most preferably greater than 24 feet. Preferably the fused thermoplastic membrane is provided in roll form that is greater than 100 feet in length.
Web sheets 135 and 137 are normally prepared in thicknesses of from 10 to 100 mils, although thicker web sheets may be prepared and it may be possible to prepare web sheets thinner than 10 mils. In preferred embodiments, the total width of each of the web sheets 135 and 137 is greater than 5 feet, more preferably greater than 10 feet, and most preferably greater than 12 feet. Preferably the web sheets 135 and 137 are provided, either separately or together in combination with the release liner, in roll form that is greater than 100 feet in length.
Examples of polymeric release agent coatings are described in U.S. Pat. Nos. 3,957,724; 4,567,073; 4,313,988; 3,997,702; 4,614,667; 5,202,190; and 5,290,615; the disclosures of which are incorporated by reference herein. Examples of commercially available liners include Polyslik™ brand liners from Rexam Release of Oakbrook, Ill., USA and EXHERE™ brand liners from P.H. Glatfelter Company of Spring Grove, Pa., USA. Preferably the release liner is a polymer sheet having a melting point higher than the extrusion temperature of the thermoplastic membrane material.
Virtually any type of thermoplastic can be utilized in the present process. Preferably the thermoplastic has a melt index of at least 0.5 when tested at 2.14 Kg. at 190° C. Thermoplastics with higher melt indexes are less viscous when melted. Examples of thermoplastics suitable for use include thermoplastics such as: polyvinyl chloride (PVC) and thermoplastic polyolefins such as polyethylene (PE), linear polyethylene (LPE), polybutenes (PB), polypropylene (PP), co-polymers of polyolefins, ethylene-propylene rubber (EPR), ethylene-propylene copolymer (EPM), Ethylene Propylene Diene Monomer polymer (EPDM), EPDM blended with PP or PE or copolymer, acrylonitrile-butadiene-styrene (ABS) polymer, thermoplastic polyester, urethane and polyvinyl plastics and the like, or mixtures thereof. Polypropylene based thermoplastic olefin (a thermoplastic mixture of ethylene, propylene, polypropylene and EPR manufactured by Himont North America, Inc.) has been found to be very suitable because of its thermoplastic properties, its strength and its resistance to oxidation and UV.
Preferably the first and second thermoplastics are made from the same materials or substantially the same materials.
The first and second thermoplastics in one embodiment are blended composite polymers further comprising additives, such as UV screeners, UV absorbers, fire retardants, etc. to improve stability and/or weatherability. The term “UV absorber” refers to any conventional additive blended into a polymer to stabilize the adverse effects of light exposure, such as a loss of strength, degradation and decoloration. The use of a UV absorber may allow at least one layer of roofing membrane to exhibit good weathering characteristics. Examples of preferred UV absorbers additives include benzotriazole, benezophenones, hindered amine light stabilizers (HALS), non-interacting HALS (NOR-HALS), etc. The term “UV screener” refers to a conventional additive blended into a polymer to reflect ultraviolet rays. Examples of preferred UV screener additives include TiO2, carbon black, zinc oxide, etc.
When the thermoplastic/release liner web composite is to be used as liners for canals, reservoirs, pits or the like, the thermoplastic is preferably pigmented with a black pigment such as carbon black. Carbon black is an excellent UV absorber and protects the thermoplastic from atmospheric oxidation. In one of the preferred embodiments of the present invention, the thermoplastic will be pigmented with a white pigment, such as titanium dioxide, to act as a light reflectant.
In one embodiment the large webs of the present invention can optionally be joined together in the field to make even larger webs when desired for certain applications. The webs can be joined together in any appropriate manner, such as by hot air welding an overlapping exposed section of one web to an overlapped section of another web. Alternatively, a hot melt adhesive may be applied to the underside of the overlapping section or the upper side of the overlapped section by spraying or knife coating methods. In other alternative embodiments, a transfer adhesives, an solvent based adhesive, or a water based adhesive may be applied to the underside of the overlapping section or the upper side of the overlapped section by traditional adhesive coating methods. In another alternative embodiment, an overlapping section of one web may be chemically welded to an overlapped section of a second web using known techniques.
In an embodiment of the present invention, an adhesive layer may be stripe coated on the outer surface of one of the thermoplastic membranes, preferably after slitting of the waste trim, at an edge of the membrane. The adhesive preferably is covered with a release liner to provide a ready-to-adhere joint for joining webs.
In another embodiment of the present invention, it has been found that a geomembrane can be prepared from an amorphous or semi-crystalline thermoplastic sheet material that will exhibit exceptional interface shear resistance if one or both major surfaces of the geomembrane is provided with a high gloss surface structure. Containment facilities, such as ponds, landfills and other fluid retention constructions, are typically formed by first constructing a containment basin having side walls constructed to contain fluids. The side walls of these basins advantageously have a relatively steep slope to provide more volume capacity with a smaller footprint. Preferably, at least one side wall of the containment basin will have a slope of at least about 3:1 (horizontal:vertical). In a preferred embodiment, the sidewall would have a slope of at least about 2:1. This containment basin is then lined with a geomembrane. In order to protect the geomembrane, a cover soil (which can be sand, clay or other such material) is often placed on the geomembrane. Because of the steep sidewalls discussed above, the cover soil will tend to slide off of the geomembrane at the aforementioned slopes. Therefore, a more complex construction has in the past been used to help keep the cover soil in place. Typically, a geotextile which is a fabric-type construction, has been put in direct contact with the geomembrane to provide a higher friction substrate. A geonet, which is a polymer net configured to help allow liquids to flow to the bottom of the containment facility, is then placed on top of the geotextile. Another geotextile is then placed on top of the geonet to prevent any soil from clogging the geonet. Finally, the soil is placed on top of the second geotextile.
Surprisingly, because of the surface characteristics of the present geomembrane, it is possible to provide a containment facility construction with steep sidewalls that have a comfortable factor of safety in expectation that the soil will not slide down the sidewalls of the containment facility when the soil is in direct contact with the geomembrane or when a geonet is in direct contact with the geomembrane.
The conventional wisdom regarding appropriate surface structure for a geomembrane suggests that one should provide projections or a rough surface to maximize friction of materials on a geomembrane. To the contrary, it has been found that a geomembrane with high gloss provides unexpected friction in the containment facility environment.
In a preferred embodiment, the geomembrane is prepared from an amorphous or semi-crystalline thermoplastic sheet material and has first and second major surfaces. At least the first major surface of the geomembrane is provided with a surface structure that has an average gloss value that is greater than about 10, more preferably greater than about 30, more preferably greater than about 50, and most preferably greater than about 70 in a 20° gloss angle measurement taken in accordance with ASTM 2457-03. In a preferred embodiment, both the first major surface and the second major surface of the geomembrane is provided with a surface structure that has an average gloss value that is greater than about 10, more preferably greater than about 30, more preferably greater than about 50, and most preferably greater than about 70 in a 20° gloss angle measurement taken in accordance with ASTM 2457-03 in order to prevent slippage of both the soil on top of the geomembrane, and also of the geomembrane itself.
In another embodiment of the present invention, the gloss value of one or both major surfaces of the geomembrane as discussed above is evaluated using two measurements, and at least the first major surface of the geomembrane is provided with a surface structure that has an average gloss value that is greater than about 10, more preferably greater than about 30, more preferably greater than about 50, and most preferably greater than about 70 in a 20° gloss angle and an average gloss value of greater than about 30, more preferably greater than about 50, and most preferably greater than about 70 in a 60° gloss angle measurement, both sets of measurements being taken in accordance with ASTM 2457-03. The gloss values of the inventive geomembranes are measured in the machine direction.
Preferably, the thermoplastic sheet material is either amorphous or semi-crystalline, and is selected from the group consisting of polyvinyl chloride, polyurethane, and thermoplastic polyolefin polymer materials. Preferably the thermoplastic sheet material has a Shore A hardness of less than about 100, and more preferably less than about 95. It has been found that thermoplastic sheet materials having this degree of hardness, when provided with a glossy surface structure as described herein, exhibit exceptional performance properties as a geomembrane.
In another embodiment of the present invention, a geomembrane is prepared from an amorphous or semi-crystalline thermoplastic sheet material, the geomembrane having first and second major surfaces. At least the first major surface of the geomembrane is provided with a surface structure having sufficient gloss value that the resulting geomembrane exhibits a secant angle that is greater than about 35 when measurement is using Type III sand at a normal force of 250 psf taken in accordance with ASTM D 5321-02.
In another embodiment of the present invention, a geomembrane prepared from an amorphous or semi-crystalline thermoplastic sheet material, the geomembrane having first and second major surfaces. At least the first major surface of the geomembrane is provided with a surface structure having sufficient gloss value that the resulting geomembrane exhibits a secant angle that is greater than about 25 at a normal force of 250 psf when measurement is made using a geonet taken in accordance with ASTM D 5321-02. The geonet to be used in this evaluation is a high density polyethylene net having a fabric weight of about 135 g/m2.
The geomembrane of the present invention can be made by providing an ultrasmooth surface by formation of the geomembrane on a release liner web. More specifically, a geomembrane can be prepared by drawing a release liner web into a throat between parallel, spaced apart first and second nip rollers of a membrane extruder, the release liner web having first and second sides. A molten thermoplastic is simultaneously extruded into the throat of the two rollers, wherein the first thermoplastic is extruded between the first side of the release liner web and the first roller, thereby forming an amorphous or semi-crystalline thermoplastic sheet material having a first major surface in contact with the release liner web, wherein upon removal of the release liner web from the amorphous or semi-crystalline thermoplastic sheet material the first major surface of the thermoplastic sheet material exhibits high gloss.
In an alternative method, a geomembrane is prepared from an amorphous or semi-crystalline thermoplastic sheet material and provided with high gloss on at least one surface by extruding a molten thermoplastic into a throat between parallel, spaced apart first and second nip rollers of a membrane extruder, thereby forming an amorphous or semi-crystalline thermoplastic sheet material having a first and a second major surface and contacting at least the first major surface with a surface finishing roller under conditions to impart the first major surface of the thermoplastic sheet material with a high gloss surface. In a preferred embodiment, the surface finishing roller is a polished chrome roll.
Other methods of preparing a geomembrane from an amorphous or semi-crystalline thermoplastic sheet material and providing the sheet material with high gloss on at least one surface will now be apparent to the skilled artisan.
Because of the surprisingly high friction of the geomembrane, a method of forming a containment facility can be carried out wherein the geonet is applied directly to the geomembane. More specifically, a containment facility can be prepared by
a) constructing a containment basin having at least one side wall having a slope of at least about 3:1 (horizontal:vertical)
b) lining the containment basin with the present geomembrane, wherein the second major surface is in contact with the containment basin construction;
c) positioning a geonet directly in contact with the first major surface of geomembrane;
d) positioning a geotextile directly in contact with the geonet; and
e) applying a cover soil to the geonet.
This method provides substantial savings as compared to conventional techniques in the elimination of a layer of geotextile from the containment facility construction.
In another embodiment, the geonet and both layers of geotextile can be eliminated, with the cover soil being applied directly to the geomembrane. The resulting construction provides a surprisingly functional containment facility with savings by elimination of three layers that are conventionally required.
The geomembrane having the glossy surface provided by formation of the thermoplastic sheet material with a release liner as described herein can be provided in roll form in combination with the release liner. Upon delivery of the roll to the worksite, the release liner is removed, and the geomembrane is preferably positioned with glossy side up. Optionally, the release liner is removed at the manufacturing site, and the geomembrane is provided to the worksite without the release liner. This embodiment facilitates the recycling of the release liner, reduces the weight of material to be shipped to the worksite, and additionally adds convenience at the work site in reducing the amount of material that must be removed from the worksite.
In an alternative embodiment, the geomembrane is provided in the wide fused format as described herein, where the first thermoplastic membrane is peeled away from the first side of the release liner, and the release liner is then removed from the second thermoplastic membrane, wherein the first and second thermoplastic membranes have been fused together in the manufacturing process described above. This “double-wide” geomembrane is then positioned at the worksite, preferably with glossy side up.
In an alternative embodiment, the geomembrane is provided having release liners on both major surfaces of the thermoplastic sheet material. In one aspect of this embodiment, one of the release liners is removed from the thermoplastic sheet material to expose a glossy major surface, and the other release liner stays in place to provide a more durable geomembrane construction. In another aspect of this embodiment, both of the release liners are removed from the thermoplastic sheet material to provide a geomembrane having two glossy major surfaces. This aspect is particularly preferred where the geometry or materials of the containment facility suggest that the likelihood of sliding of the geomembrane itself warrants the provision of glossy surface on both sides of the geomembrane.
The specific orientation of the glossy side or sides of a geomembrane during construction of the containment facility of course applies likewise to geomembranes prepared by surface treating the thermoplastic sheet material to provide the desired glossy surface.
Gloss value measurements of a 30 mil PVC film geomembrane of the present invention after removal of the release liner were carried out in accordance with ASTM 2457-03. As a comparison, the gloss value measurements of a conventional embossed PVC geomembrane and of a polyester film (the same film as used as the release liner in the present construction) were also carried out. The results of this evaluation are reported in TABLE I below.
Surface friction studies of a 30 mil PVC film geomembrane of the present invention with and without the removal of the release liner were carried out in accordance with ASTM D 5321-02. The results of this evaluation are reported in TABLE II below.
All patents, patent documents, and publications cited herein are incorporated by reference as if individually incorporated. Unless otherwise indicated, all parts and percentages are by weight and all molecular weights are weight average molecular weights. The foregoing detailed description has been given for clarity of understanding only. No unnecessary limitations are to be understood therefrom. The invention is not limited to the exact details shown and described, for variations obvious to one skilled in the art will be included within the invention defined by the claims.
This application claims the benefit of International Application No. PCT/US2006/023771 filed Jun. 19, 2006, entitled “METHOD OF MANUFACTURING THERMOPLASTIC MEMBRANE ARTICLES AND METHODS OF USE,” which application is incorporated herein by reference in its entirety; claims the benefit of U.S. Provisional Application Ser. No. 60/692,298 filed on Jun. 20, 2005, entitled “METHOD OF MANUFACTURING ARTICLES USING A THERMOPLASTIC MEMBRANE,” which application is incorporated herein by reference in its entirety; and claims the benefit of U.S. Provisional Application Ser. No. 60/723,528 filed Oct. 3, 2005, entitled “METHOD OF MANUFACTURING THERMOPLASTIC MEMBRANE ARTICLES AND METHODS OF USE,” which application is incorporated herein by reference in its entirety.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US2006/023771 | 6/19/2006 | WO | 00 | 2/5/2009 |
| Number | Date | Country | |
|---|---|---|---|
| 60692298 | Jun 2005 | US | |
| 60723528 | Oct 2005 | US |