Information
-
Patent Grant
-
6200837
-
Patent Number
6,200,837
-
Date Filed
Friday, June 25, 199925 years ago
-
Date Issued
Tuesday, March 13, 200123 years ago
-
Inventors
-
Original Assignees
-
Examiners
Agents
- Selitto & Associates, P.C.
-
CPC
-
US Classifications
Field of Search
US
- 438 150
- 438 166
- 438 471
- 438 476
- 438 762
- 438 764
- 438 482
- 438 486
- 438 151
- 438 692
- 438 152
- 438 301
-
International Classifications
-
Abstract
A method of manufacturing a TFT which can improve realibility by planarizing the surface of a polysilicon layer as a channel layer, is disclosed.According to the present invention, an amorphous silicon layer is formed on an insulating layer substrate and crystallized by excimer layer annealing process, to form a polysilicon layer. Next, the surface of the polysilicon layer is oxidized to form an oxide layer. At this time the sufrace of the polsyilicon under the oxide layer become smooth. Preferably, the oxide layer is formed by oxiation process using ECR (Electron Cyclon Resonator) plasma or using one selected from the group consisting of O2, O2N2, O2N2O, O2NH3 and NO. Thereafter, the oxide layer is removed to expose the polysilicon layer and then a gate insulating layer is formed on the exposed polysilicon layer. Preferably, the gate insulating layer is formed to one selected from the group consisting of a SiO2 layer, a SiN layer, a SiON layer and a TEOS oxide layer. The gate insulating layer is formed by ECR plasma oxidiation process or ECR PECVD.
Description
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method of manufacturing a thin film transistor, and more particularly to a method of manufacturing a thin film transistor using a polysilicon layer as a channel layer.
2. Description of the Related Art
In general, an active matrix type-liquid crystal display(AM-LCD) device is thin, so that it is often used in various display devices. In this AM-LCD device, one TFT is provided as a switching element for each pixel, so that individual pixel electrodes are independently driven.
In this display device, a glass substrate is used for a substrate material, for reducing cost. In this case, process must be performed at the low temperature of about 600° C., considering the softening temperature of the glass. Therefore, in case a polysilicon layer is used as a channel layer, an amorphous silicon layer is crystallized by a laser annealing capable of thermally treating at the low temperature of 600° C. or less, thereby forming the polysilicon layer. In this laser annealing, since fever is momently transmitted to the surface of the amorphous silicon layer, not to have on effect on the glass substrate, it is possible to crystallize the amorphous silicon layer without occurring the transformation of the substrate.
However, when crystallizing the amorphous silicon layer, a liquid state and a solid state coexist therein, so that the grain boundary of the polysilicon layer is projected due to the density difference of the two states, thereby generating hillock on the surface of the polysilicon layer. As a result, the surface of the polysilicon layer becomes rough, thereby deteriorating the properties of the TFT. For example, electric field is locally concentrated on the channel so layer of the TFT and leakage current occurs. Furthermore, the property of a gate insulating layer formed on the polysilicon layer is deteriorated. Accordingly, the reliability and the reproductivity are deteriorated.
SUMMARY OF THE INVENTION
It is therefore an object of the present invention to a method of manufacturing a TFT which can improve reliability by planarizing the surface of a polysilicon layer as a channel layer.
To accomplish this above object, according to the present invention, an amorphous silicon layer is formed on an insulating layer substrate and crystallized by excimer laser annealing process, to form a polysilicon layer. Next, the surface of the polysilicon layer is oxidized to form an oxide layer. At this time, the surface of the polysilicon under the oxide layer become smooth. Preferably, the oxide layer is formed by oxidation process using ECR(Electron Cyclon Resonator) plasma or using one selected from the group consisting of O
2
, O
2
N
2
, O
2
N
2
O, O
2
NH
3
and NO. Thereafter, the oxide layer is removed to expose the polysilicon layer and then a gate insulating layer is formed on the exposed polysilicon layer. Preferably, the gate insulating layer is formed to one selected from the group consisting of a SiO
2
layer, a SiN layer, a SiON layer and a TEOS oxide layer. The gate insulating layer is formed by ECR plasma oxidation process or ECR PECVD.
Additional object, advantages and novel features of the invention will be set forth in part in the description which follows, and in part will become apparent to those skilled in the art upon examination of the following or may be learned by practice of the invention. The objects and advantages of the invention may be realized and attained by means of the instrumentalities and combinations particularly pointed out in the appended claims.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1A
to
FIG. 1E
show cross sectional views for describing a method of manufacturing a TFT using a polysilicon layer as a channel layer according to an embodiment of the present invention.
DETAILED DESCRIPTION OF THE INVENTION
Hereinafter, a preferred embodiment of the present invention will be explained in more detail with reference to accompanying drawings.
Referring to
FIG. 1A
, an amorphous silicon layer
21
is formed on a transparent insulating layer
20
such as a glass. The amorphous silicon layer
21
is crystallized by an excimer laser annealing process, to form a polysilicon layer
22
. At this time, the grain boundary GB of the polysilicon layer is projected due to the density differnce of a liquid stat and a solid state, so that hillock is generated on the surface of the polysilicon layer
22
, as shown in FIG.
1
B. As a result, the surface of the polysilicon layer
22
becomes rough.
In this embodiment, to planarize the surface of the polysilicon layer
22
, an oxide layer
23
is formed thereon by oxidizing the surface thereof, as shown in FIG.
1
C. At this time, since oxidation of the polysilicon layer
22
is faster at the grain boundary GB than at the particle, the surface of the polysilicon layer
22
under the oxide layer
23
becomes smooth. Preferably, the oxide layer
23
is formed by oxiation process using ECR(Electron Cyclon Resonator) plasma or using one selected from the group consisting of O
2
, O
2
N
2
, O
2
N
2
O, O
2
NH
3
and NO.
Thereafter, the oxide layer
23
is removed by etching, to expose the polysilicon layer
22
of which the surface is smooth, as shown in
FIG. 1D. A
gate insulating layer
24
is then formed on the exposed polysilicon layer
22
, as shown in FIG.
1
E. Preferably, the gate insulating layer
24
is formed to one selected from the group consisting of a SiO
2
layer, a SiN layer, a SiON layer and a TEOS oxide layer. The gate insulating
24
is also formed by ECR plasm oxidiation process or ECR PECVD(Plasma Enhanced Chemical Vapor Deposition).
Next, as not shown in the drawings, a gate electrode and source/drain electrodes are formed, to complete a TFT.
According to the present invention, owing to the oxidation difference between the grain boundary and the partice of the polysilicon layer, the surface of the polysilicon layer under the oxide layer becomes smooth, after performing oxidation process. Therefore, it is possible to obtain the polysilicon layer of which surface is smooth after removing the oxide layer. As a result, prior problems such as local electric field concentration on a channel layer of the TFT, the vibration of threshold voltage and leakage current occurrence, due to the rough surface of the polysilicon layer are substantially prevented. Furthermore, the property of a gate insulating layer is improved. Accordingly, the realibility and the reproductivity are improved.
Although the preferred embodiment of this invention has been disclosed for illustrative purpose, those skilled in the art will appreciate that various modification, additions and substitutions are possible, without from the scope and spirit of the invention as described in the accompanyting claims.
Claims
- 1. A method of manufacturing a thin film transistor having a polysilicon layer as a channel layer, comprising the steps of:forming an amorphous silicon layer on an insulating layer; crystalizing the amorphous silicon layer to form a polysilicon layer, wherein the polysilicon layer has grain boundaries formed therein and a rough surface including first portions adjacent the grain boundaries and second portions remote from the grain boundaries; oxidizing the rough surface of the polysilicon layer to form an oxide layer, wherein the oxidizing step is performed so as to oxidize the first portions of the rough surface of the polysilicon layer at a rate faster than the rate at which the second portions of the rough surface of the polysilicon layer are oxidized such that the interface between the polysilicon layer and the oxide layer is substantially planar; and removing the oxide layer to expose the polysilicon layer having a smooth surface.
- 2. The method according to claim 1, wherein the step of the crystallizing is performed by an excimer laser annealing process.
- 3. The method according to claim 1, wherein the oxidizing step is performed by an electron cyclon resonator plasma oxidation process.
- 4. The method according to claim 1, wherein the oxidizing step is performed by an oxidation process using one selected from the group consisting of O2, O2N2, O2N2O, O2NH3 and NO.
- 5. The method according to claim 1, further comprising the step of forming a gate insulating layer on the exposed polysilicon layer.
- 6. The method according to claim 5, wherein the gate insulating layer is formed to one selected from the group consisting of a SiO2 layer, a SiN layer, a SiON layer and a TEOS oxide layer.
- 7. The method according to claim 6, wherein the gate insulating layer is formed by an electron cyclon resonator plasma oxidation process.
- 8. The method according to claim 6, wherein the gate insulating layer formed by electron cyclon resonator plasm enhanced chemical vapor deposition.
Priority Claims (1)
Number |
Date |
Country |
Kind |
98-25839 |
Jun 1998 |
KR |
|
US Referenced Citations (5)
Number |
Name |
Date |
Kind |
5550070 |
Funai et al. |
Aug 1996 |
|
5616506 |
Takemura |
Apr 1997 |
|
5849612 |
Takahashi et al. |
Dec 1998 |
|
5869363 |
Yamazaki et al. |
Feb 1999 |
|
5985740 |
Yamazaki et al. |
Nov 1999 |
|
Foreign Referenced Citations (11)
Number |
Date |
Country |
563196 |
Mar 1993 |
JP |
645607 |
Feb 1994 |
JP |
677484 |
Mar 1994 |
JP |
6252405 |
Sep 1994 |
JP |
7273347 |
Oct 1995 |
JP |
883911 |
Mar 1996 |
JP |
888172 |
Apr 1996 |
JP |
8330597 |
Dec 1996 |
JP |
9107107 |
Apr 1997 |
JP |
10200120 |
Jul 1998 |
JP |
10209460 |
Aug 1998 |
JP |