Method of mass-colouring synthetic materials

Abstract

The present invention relates to a method of mass-colouring synthetic materials, which comprises using at least one pigment dye of formula (1) wherein R and R1 together form a phenyl or heteroaryl radical and R2 is hydrogen, or R1 and R2 together form a phenyl or heteroaryl radical and R is hydrogen, and the rings A and B may each independently of the other be substituted by C1-C4?alkyl, C1-C4alkoxy, halogen, —COOR3, —CONHR4 and/or by —SR5, wherein R3, R4 and R5 are each independently of the others hydrogen, C1-C4alkyl, C6-C12aryl or heteroaryl, to synthetic materials coloured with such pigment dyes, and to novel pigment dyes of formula (3), wherein R6 is hydrogen or bromine. 1

Description

[0001] The present invention relates to a method of mass-colouring synthetic materials, as well as to novel pigment dyes based on naphthalimide.

[0002] Methods of mass-colouring synthetic materials with pigment dyes are known. It has been shown, however, that the pigment dyes used in that method do not always fully satisfy the highest demands, especially in respect of light fastness, thermostability and/or tinctorial strength, and also do not fully cover the desired range of shades. There is therefore a need for new pigment dyes that yield light-fast, thermostable, tinctorially strong colorations especially in the yellow colour range and that exhibit good allround fastness properties.

[0003] It has now been found, surprisingly, that the pigment dyes used in the method according to the invention meet the criteria given above to a considerable degree.

[0004] The present invention accordingly relates to a method of mass-colouring synthetic materials, which comprises using at least one pigment dye of formula 2

[0005] wherein

[0006] R and R1 together form a phenyl or heteroaryl radical and R2 is hydrogen, or R1 and R2 together form a phenyl or heteroaryl radical and R is hydrogen, and

[0007] the rings A and B may each independently of the other be substituted by C1-C4alkyl, C1-C4alkoxy, halogen, —COOR3, —CONHR4 and/or by —SR5, wherein R3, R4 and R5 are each independently of the others hydrogen, C1-C4alkyl, C6-C12aryl or heteroaryl.

[0008] C1-C4Alkyl as a substituent of the rings A and/or B is methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, sec-butyl or tert-butyl.

[0009] C1-C4Alkoxy as a substituent of the rings A and/or B is, for example, methoxy, ethoxy, propoxy or butoxy.

[0010] Halogen as a substituent of the rings A and/or B is, for example, fluorine, chlorine or iodine and preferably bromine.

[0011] R3, R4 and R5 as C1-C4alkyl are methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, sec-butyl or tert-butyl.

[0012] R3, R4 and R5 as C6-C12aryl are, for example, phenyl or naphthyl, which may be unsubstituted or substituted by hydroxy, halogen, C1-C4alkyl and/or by C1-C4alkoxy.

[0013] R3, R4 and R5 as heteroaryl are, for example, morpholine, piperidine, thiophene or pyrrole.

[0014] The heteroaryl radicals formed by R and R1 or by R1 and R2 are, for example, the radicals of formula 3

[0015] wherein

[0016] X is —O—, —S—, —NR6— and R6 is hydrogen, C1-C12alkyl, or phenyl that is unsubstituted or substituted by hydroxy, halogen, C1-C4alkyl and/or by C1-C4alkoxy.

[0017] X is preferably —O—.

[0018] R6 is preferably hydrogen.

[0019] The rings A and B are preferably unsubstituted.

[0020] The pigment dyes of formula (1) used in accordance with the invention are known in some cases and can be prepared according to generally known methods.

[0021] The pigment dyes of formula 4

[0022] wherein

[0023] R6 is hydrogen or bromine,

[0024] are novel, and the present invention relates also thereto.

[0025] The pigment dyes of formula (3) according to the invention are prepared, for example, by reacting a compound of formula 5

[0026] with an unsubstituted or bromo-substituted naphthalene-1,8-dicarboxylic anhydride and potassium acetate in acetic acid at elevated temperature.

[0027] The compounds of formula (50) are known or can be prepared according to known methods.

[0028] The present invention relates also to a method for the production of coloured plastics or polymeric colour particles, which comprises mixing together a high molecular weight organic material and a tinctorially effective amount of at least one pigment dye of formula (1).

[0029] The colouring of the high molecular weight organic substances with the pigment dye of formula (1) is carried out, for example, by mixing such a pigment dye into those substrates using roll mills, mixing apparatus or grinding apparatus, with the result that the pigment dye is dissolved or finely dispersed in the high molecular weight material. The high molecular weight organic material with the admixed pigment dye is then processed using processes known per se, for example calendering, compression moulding, extrusion, coating, spinning, casting or injection moulding, whereby the coloured material acquires its final form. It is also possible for the admixing of the pigment dye to be carried out immediately prior to the actual processing step, for example by continuously feeding a solid, for example pulverulent, pigment dye and, at the same time, a granulated or pulverulent high molecular weight organic material, and optionally also additional ingredients, e.g. additives, directly into the intake zone of an extruder, where mixing takes place just before processing. In general, however, it is preferable for the pigment dye to be mixed into the high molecular weight organic material beforehand, because more even coloration of the substrates can be obtained.

[0030] In order to produce non-rigid mouldings or to reduce their brittleness, it is often desirable to incorporate so-called plasticisers into the high molecular weight compounds prior to shaping. There may be used as plasticisers, for example, esters of phosphoric-acid, phthalic acid or sebacic acid. In the method according to the invention the plasticisers may be incorporated into the polymers before or after the incorporation of the colorant. It is also possible, in order to achieve different shades of colour, to add to the high molecular weight organic materials, in addition to the pigment dye of formula (1), also further pigments or other colorants in any desired amounts, optionally together with further additives, e.g. fillers or siccatives.

[0031] Preference is given to the colouring of thermoplastic plastics, especially in the form of fibres. Preferred high molecular weight organic materials to be coloured according to the invention are very generally polymers having a dielectric constant of ≧2.5, especially polyester, polycarbonate (PC), polystyrene (PS), polymethyl methacrylate (PMMA), polyamide, polyethylene, polypropylene, styrene/acrylonitrile (SAN) or acrylonitrile/butadiene/styrene (ABS). Polyester and polyamide are especially preferred. Very special preference is given to linear aromatic polyesters obtainable by polycondensation of terephthalic acid and glycols, especially ethylene glycol, or condensation products of terephthalic acid and 1,4-bis(hydroxymethyl)cyclohexane, for example polyethylene terephthalate (PET) or polybutylene terephthalate (PBTP); also polycarbonates, e.g. those from α,α-dimethyl-4,4-dihydroxy-diphenylmethane and phosgene, or polymers based on polyvinyl chloride and on polyamides, e.g. polyamide-6 or polyamide-6,6.

[0032] The pigment dyes according to the invention impart to the mentioned materials, especially polyester and polyamide materials, tinctorially strong, level yellow colour shades having very good in-use fastness properties, especially good light fastness and good thermostability.

[0033] The following Examples serve to illustrate the invention. Unless otherwise indicated, the parts are parts by weight and the percentages are percentages by weight. The temperatures are given in degrees Celsius. The relationship between parts by weight and parts by volume is the same as that between grams and cubic centimetres.

EXAMPLE 1

[0034] 20.5 parts by weight of 1,2-diaminonaphthalene sulfate together with 14.2 parts by weight of naphthalene-1,8-dicarboxylic anhydride and 23.8 parts by weight of potassium acetate are introduced into 750.0 parts by weight of acetic acid, heated to 100° C. and stirred at that temperature for 15 hours. The reaction mixture is then cooled and diluted with 1000 parts by weight of water. The precipitated product is filtered off with suction, washed with water and dried. 31 parts by weight of the pigment dye of formula 6

[0035] are obtained. The dye mass-colours polyester and polyamide in light-fast greenish yellow shades having very good thermal stability.

EXAMPLES 2 and 3

[0036] If in Example 1 the 20.5 parts by weight of 1,2-diaminonaphthalene sulfate are replaced by an equivalent amount of a diamino compound indicated in column 2 of Table 1, pigment dyes having the shades indicated in column 4 are likewise obtained.

TABLE 1
Example	Diamino compound	Pigment dye	Shade in PET
2	7	8	greenish yellow
3	9	10	greenish yellow

EXAMPLES 4-6

[0037] If in Examples 1 to 3 the 14.2 parts by weight of naphthalene-1,8-dicarboxylic anhydride are replaced by an equivalent amount of 4-bromo-naphthalene-1,8-dicarboxylic anhydride, the pigment dyes indicated in Table 2 having the shades indicated in column 4 are obtained.

TABLE 2
Example	Diamino compound	Pigment dye	Shade in PET
4	11	12	yellow
5	13	14	yellow
6	15	16	greenish yellow

DYEING EXAMPLE 1

[0038] 1200.00 g of polyester granules (PET Arnite D04-300, DSM) are pre-dried for 4 hours at 130° C. and then mixed homogeneously with 2.4 g of the pigment dye of formula 17

[0039] in a “roller rack” mixing apparatus for 15 minutes at 60 revolutions per minute.

[0040] The homogeneous mixture is extruded in an extruder (twin screw 25 mm from Collin, D85560 Ebersberg) with 6 heating zones at a maximum temperature of 275° C., cooled with water, granulated in a granulator (Turb Etuve TE 25 from MAPAG AG, CH-3001 Bern) and then dried for 4 hours at 130° C.

[0041] The resulting yellow-coloured polyester granules have good allround fastness properties, especially very good light fastness and high-temperature light fastness properties.

DYEING EXAMPLE 2

[0042] 1200.00 g of polyamide-6 granules (Ultramid B3K, BASF) are pre-dried for 4 hours at 75° C. and then mixed homogeneously with 2.4 g of the pigment dye of formula 18

[0043] in a “roller rack” mixing apparatus for 15 minutes at 60 revolutions per minute.

[0044] The homogeneous mixture is extruded in an extruder (twin screw 25 mm from Collin, D-85560 Ebersberg) with 6 heating zones at a maximum temperature of 220° C., cooled with water, granulated in a granulator (Turb Etuve TE 25 from MAPAG AG, CH-3001 Bern) and then dried for 4 hours at 75° C.

[0045] The resulting yellow-coloured polyamide granules have good allround fastness properties, especially very good light fastness and high-temperature light fastness properties.

Claims

1. A method of mass-colouring synthetic materials, which comprises incorporating at least one pigment dye of formula

2. A method according to claim 1, wherein R and R1 or R1 and R2 together form a phenyl radical.

3. A method according to claim 1, wherein the heteroaryl radicals formed by R and R1 or by R1 and R2 are the radicals of formula

4. A pigment dye according to claim 1 of formula

5. A process for the preparation of a pigment dye of formula (3) according to claim 4, which comprises reacting a compound of formula

6-7. (canceled)

8. A synthetic material coloured according to claim 1.