Method of modifying the properties of a metal matrix composite body

Abstract

The present invention relates to modifying the properties of a metal matrix composite body by a post formation process treatment and/or a substantially contiguous modification treatment. The post formation process treatment may be applicable to a variety of metal matrix composite bodies produced by various techniques, and is particularly applicable to modifying the properties of a metal matrix composite body produced by a spontaneous infiltration technique. The substantially contiguous modification process may also be used primarily in conjunction with metal matrix composite bodies produced according to a spontaneous infiltration technique. Particularly, at least a portion of the matrix metal of the metal matrix composite body and/or the filler material of the metal matrix composite body is modified or altered during and/or after the formation process.

Description

FIELD OF THE INVENTION

The present invention relates to modifying the properties of a metal matrix composite body by a post formation process treatment and/or a substantially contiguous modification treatment. The post formation process treatment may be applicable to a variety of metal matrix composite bodies produced by various techniques, and is particularly applicable to modifying the properties of a metal matrix composite body produced by a spontaneous infiltration technique. The substantially contiguous modification process may also be used primarily in conjunction with metal matrix composite bodies produced according to a spontaneous infiltration technique. Particularly, at least a portion of the matrix metal of the metal matrix composite body and/or the filler material of the metal matrix composite body is modified or altered during and/or after the formation process.

BACKGROUND OF THE INVENTION

Composite products comprising a metal matrix and a strengthening or reinforcing phase such as ceramic particulates, whiskers, fibers or the like, show great promise for a variety of applications because they combine some of the stiffness and wear resistance of the reinforcing phase with the ductility and toughness of the metal matrix. Generally, a metal matrix composite will show an improvement in such properties as strength, stiffness, contact wear resistance, and elevated temperature strength retention relative to the matrix metal in monolithic form, but the degree to which any given property may be improved depends largely on the specific constituents, their volume or weight fraction, and how they are processed in forming the composite. In some instances, the composite also may be lighter in weight than the matrix metal per se. Aluminum matrix composites reinforced with ceramics such as silicon carbide in particulate, platelet, or whisker form, for example, are of interest because of their higher stiffness, wear resistance and high temperature strength relative to aluminum.

Various metallurgical processes have been described for the fabrication of aluminum matrix composites, including methods based on powder metallurgy techniques and liquid-metal infiltration techniques which make use of pressure casting, vacuum casting, stirring, and wetting agents. With powder metallurgy techniques, the metal in the form of a powder and the reinforcing material in the form of a powder, whiskers, chopped fibers, etc., are admixed and then either cold-pressed and sintered, or hot-pressed. The maximum ceramic volume fraction in silicon carbide reinforced aluminum matrix composites produced by this method has been reported to be about 25 volume percent in the case of whiskers, and about 40 volume percent in the case of particulates.

The production of metal matrix composites by powder metallurgy techniques utilizing conventional processes imposes certain limitations with respect to the characteristics of the products attainable. The volume fraction of the ceramic phase in the composite is limited typically, in the case of particulates, to about 40 percent. Also, the pressing operation poses a limit on the practical size attainable. Only relatively simple product shapes are possible without subsequent processing (e.g., forming or machining) or without resorting to complex presses. Also, nonuniform shrinkage during sintering can occur, as well as nonuniformity of microstructure due to segregation in the compacts and grain growth.

U.S Pat. No. 3,970,136, granted July 20, 1976, to J. C. Cannell et.al., describes a process for forming a metal matrix composite incorporating a fibrous reinforcement, e.g. silicon carbide or alumina whiskers, having a predetermined pattern of fiber orientation. The composite is made by placing parallel mats or felts of coplanar fibers in a mold with a reservoir of molten matrix metal, e.g., aluminum, between at least some of the mats, and applying pressure to force molten metal to penetrate the mats and surround the oriented fibers. Molten metal may be poured onto the stack of mats while being forced under pressure to flow between the mats. Loadings of up to about 50% by volume of reinforcing fibers in the composite have been reported.

The above-described infiltration process, in view of its dependence on outside pressure to force the molten matrix metal through the stack of fibrous mats, is subject to the vagaries of pressure-induced flow processes, i.e., possible non-uniformity of matrix formation, porosity, etc. Non-uniformity of properties is possible even though molten metal may be introduced at a multiplicity of sites within the fibrous array. Consequently, complicated mat/ reservoir arrays and flow pathways need to be provided to achieve adequate and uniform penetration of the stack of fiber mats. Also, the aforesaid pressure-infiltration method allows for only a relatively low reinforcement to matrix volume fraction to be achieved because of difficulty of infiltrating a large mat volume. Still further, molds are required to contain the molten metal under pressure, which adds to the expense of the process. Finally, the aforesaid process, limited to infiltrating aligned particles or fibers, is not directed to formation of aluminum metal matrix composites reinforced with materials in the form of randomly oriented particles, whiskers or fibers.

In the fabrication of aluminum matrix-alumina filled composites, aluminum does not readily wet alumina, thereby making it difficult to form a coherent product. Various solutions to this problem have been suggested. One such approach is to coat the alumina with a metal (e.g., nickel or tungsten), which is then hot-pressed along with the aluminum. In another technique, the aluminum is alloyed with lithium, and the alumina may be coated with silica. However, these composites exhibit variations in properties, or the coatings can degrade the filler, or the matrix contains lithium which can affect the matrix properties.

U.S. Pat. No. 4,232,091 to R. W. Grimshaw et.al., overcomes certain difficulties in the art which are encountered in the production of aluminum matrix-alumina composites. This patent describes applying pressures of 75-375 kg/cm.sup.2 to force molten aluminum (or molten aluminum alloy) into a fibrous or whisker mat of alumina which has been preheated to 700.degree. to 1050.degree. C. The maximum volume ratio of alumina to metal in the resulting solid casting was 0.25/1. Because of its dependency on outside force to accomplish infiltration, this process is subject to many of the same deficiencies as that of Cannell et.al.

European Patent Application Publication No. 115,742 describes making aluminum-alumina composites, especially useful as electrolytic cell components, by filling the voids of a preformed alumina matrix with molten aluminum. The application emphasizes the non-wettability of alumina by aluminum, and therefore various techniques are employed to wet the alumina throughout the preform. For example, the alumina is coated with a wetting agent of a diboride of titanium, zirconium, hafnium, or niobium, or with a metal, i.e., lithium, magnesium, calcium, titanium, chromium, iron, cobalt, nickel, zirconium, or hafnium. Inert atmospheres, such as argon, are employed to facilitate wetting. This reference also shows applying pressure to cause molten aluminum to penetrate an uncoated matrix. In this aspect, infiltration is accomplished by evacuating the pores and then applying pressure to the molten aluminum in an inert atmosphere, e.g., argon. Alternatively, the preform can be infiltrated by vapor-phase aluminum deposition to wet the surface prior to filling the voids by infiltration with molten aluminum. To assure retention of the aluminum in the pores of the preform, heat treatment, e.g., at 1400.degree. to 1800.degree. C., in either a vacuum or in argon is required. Otherwise, either exposure of the pressure infiltrated material to gas or removal of the infiltration pressure will cause loss of aluminum from the body.

The use of wetting agents to effect infiltration of an alumina component in an electrolytic cell with molten metal is also shown in European Patent Application Publication No. 94353. This publication describes production of aluminum by electrowinning with a cell having a cathodic current feeder as a cell liner or substrate. In order to protect this substrate from molten cryolite, a thin coating of a mixture of a wetting agent and solubility suppressor is applied to the alumina substrate prior to start-up of the cell or while immersed in the molten aluminum produced by the electrolytic process. Wetting agents disclosed are titanium, zirconium, hafnium, silicon, magnesium, vanadium, chromium, niobium, or calcium, and titanium is stated as the preferred agent. Compounds of boron, carbon and nitrogen are described as being useful in suppressing the solubility of the wetting agents in molten aluminum. The reference, however, does not suggest the production of metal matrix composites, nor does it suggest the formation of such a composite in, for example, a nitrogen atmosphere.

In addition to application of pressure and wetting agents, it has been disclosed that an applied vacuum will aid the penetration of molten aluminum into a porous ceramic compact. For example, U.S. Pat. No. 3,718,441, granted Feb. 27, 1973, to R. L. Landingham, reports infiltration of a ceramic compact (e.g., boron carbide, alumina and beryllia) with either molten aluminum, beryllium, magnesium, titanium, vanadium, nickel or chromium under a vacuum of less than 10.sup.-6 torr. A vacuum of 10.sup.-2 to 10.sup.-6 torr resulted in poor wetting of the ceramic by the molten metal to the extent that the metal did not flow freely into the ceramic void spaces. However, wetting was said to have improved when the vacuum was reduced to less than 10.sup.-6 torr.

U.S. Pat. No. 3,864,154, granted Feb. 4, 1975, to G. E. Gazza et.al., also shows the use of vacuum to achieve infiltration. This patent describes loading a cold-pressed compact of AlB.sub.12 powder onto a bed of cold- pressed aluminum powder. Additional aluminum was then positioned on top of the AlB.sub.12 powder compact. The crucible, loaded with the AlB.sub.12 compact "sandwiched" between the layers of aluminum powder, was placed in a vacuum furnace. The furnace was evacuated to approximately 10.sup.-5 torr to permit outgassing. The temperature was subsequently raised to 1100.degree. C. and maintained for a period of 3 hours. At these conditions, the molten aluminum penetrated the porous AlB.sub.12 compact.

U.S. Pat. No. 3,364,976, granted Jan. 23, 1968, to John N. Reding et.al., discloses the concept of creating a self-generated vacuum in a body to enhance penetration of a molten metal into the body. Specifically, it is disclosed that a body, e.g., a graphite mold, a steel mold, or a porous refractory material, is entirely submerged in a molten metal. In the case of a mold, the mold cavity, which is filled with a gas reactive with the metal, communicates with the externally located molten metal through at least one orifice in the mold. When the mold is immersed into the melt, filling of the cavity occurs as the self-generated vacuum is produced from the reaction between the gas in the cavity and the molten metal. Particularly, the vacuum is a result of the formation of a solid oxidized form of the metal. Thus, Reding et. al. disclose that it is essential to induce a reaction between gas in the cavity and the molten metal. However, utilizing a mold to create a vacuum may be undesirable because of the inherent limitations associated with use of a mold. Molds must first be machined into a particular shape; then finished, machined to produce an acceptable casting surface on the mold; then assembled prior to their use; the disassembled after their use to remove the cast piece therefrom; and thereafter reclaim the mold, which most likely would include refinishing surfaces of the mold or discarding the mold if it is no longer acceptable for use. Machining of a mold into a complex shape can be very costly and time-consuming. Moreover, removal of a formed piece from a complex-shaped mold can also be difficult (i.e., cast pieces having a complex shape could be broken when removed from the mold). Still further, while there is a suggestion that a porous refractory material can be immersed directly in a molten metal without the need for a mold, the refractory material would have to be an integral piece because there is no provision for infiltrating a loose or separated porous material absent the use of a container mold (i.e., it is generally believed that the particulate material would typically disassociate or float apart when placed in a molten metal). Still further, if it was desired to infiltrate a particulate material or loosely formed preform precautions should be taken so that the infiltrating metal does not displace at least portions of the particulate or preform resulting in a non-homogeneous microstructure.

Accordingly, there has been a long felt need for a simple and reliable process to produce shaped metal matrix composites which does not rely upon the use of applied pressure or vacuum (whether externally applied or internally created), or damaging wetting agents to create a metal matrix embedding another material such as a ceramic material. Moreover, there has been a long felt need to minimize the amount of final machining operations needed to produce a metal matrix composite body. The present invention satisfies these needs by providing a spontaneous infiltration mechanism for infiltrating a material (e.g., a ceramic material), which is formed into a preform, with molten matrix metal (e.g., aluminum) in the presence of an infiltrating atmosphere (e.g., nitrogen) under normal atmospheric pressures, so long as an infiltration enhancer is present at least at some point during the process.

DESCRIPTION OF COMMONLY OWNED U.S. PATENT APPLICATIONS

The subject matter of this application is related to that of several other copending and co-owned patent applications. Particularly, these other copending patent applications describe novel methods for making metal matrix composite materials (hereinafter sometimes referred to as "Commonly Owned Metal Matrix Patent Applications").

A novel method of making a metal matrix composite material is disclosed in Commonly Owned U.S. Pat. application Ser. No. 049,171, filed May 13, 1987, in the names of White et.al., and entitled "Metal Matrix Composites", now allowed in the U.S. According to the method of the White et.al. invention, a metal matrix composite is produced by infiltrating a permeable mass of filler material (e.g., a ceramic or a ceramic-coated material) with molten aluminum containing at least about 1 percent by weight magnesium, and preferably at least about 3 percent by weight magnesium. Infiltration occurs spontaneously without the application of external pressure or vacuum. A supply of the molten metal alloy is contacted with the mass of filler material at a temperature of at least about 675.degree. C. in the presence of a gas comprising from about 10 to 100 percent, and preferably at least about 50 percent, nitrogen by volume, and a remainder of the gas, if any, being a nonoxidizing gas, e.g., argon. Under these conditions, the molten aluminum alloy infiltrates the ceramic mass under normal atmospheric pressures to form an aluminum (or aluminum alloy) matrix composite. When the desired amount of filler material has been infiltrated with the molten aluminum alloy, the temperature is lowered to solidify the alloy, thereby forming a solid metal matrix structure that embeds the reinforcing filler material. Usually, and preferably, the supply of molten alloy delivered will be sufficient to permit the infiltration to proceed essentially to the boundaries of the mass of filler material. The amount of filler material in the aluminum matrix composites produced according to the White et.al. invention may be exceedingly high. In this respect, filler to alloy volumetric ratios of greater than 1:1 may be achieved.

Under the process conditions in the aforesaid White et.al. invention, aluminum nitride can form as a discontinuous phase dispersed throughout the aluminum matrix. The amount of nitride in the aluminum matrix may vary depending on such factors as temperature, alloy composition, gas composition and filler material. Thus, by controlling one or more such factors in the system, it is possible to tailor certain properties of the composite. For some end use applications, however, it may be desirable that the composite contain little or substantially no aluminum nitride.

It has been observed that higher temperatures favor infiltration but render the process more conducive to nitride formation. The White et.al. invention allows the choice of a balance between infiltration kinetics and nitride formation.

An example of suitable barrier means for use with metal matrix composite formation is described in Commonly Owned and Copending U.S. Pat. application Ser. No. 141,642, filed Jan. 7, 1988, in the names of Michael K. Aghajanian et.al., and entitled "Method of Making Metal Matrix Composite with the use of a Barrier". According to the method of this Aghajanian et.al. invention, a barrier means (e.g., particulate titanium diboride or a graphite material such as a flexible graphite tape product sold by Union Carbide under the trade name Grafoil .RTM.) is disposed on a defined surface boundary of a filler material and matrix alloy infiltrates up to the boundary defined by the barrier means. The barrier means is used to inhibit, prevent, or terminate infiltration of the molten alloy, thereby providing net, or near net, shapes in the resultant metal matrix composite. Accordingly, the formed metal matrix composite bodies have an outer shape which substantially corresponds to the inner shape of the barrier means.

The method of U.S. Pat. application Ser. No. 049,171 was improved upon by Commonly Owned and Copending U.S. Pat. application Ser. No. 168,284, filed Mar. 15, 1988, in the names of Michael K. Aghajanian and Marc S. Newkirk and entitled "Metal Matrix Composites and Techniques for Making the Same." In accordance with the methods disclosed in this U.S. Pat. application, a matrix metal alloy is present as a first source of metal and as a reservoir of matrix metal alloy which communicates with the first source of molten metal due to, for example, gravity flow. Particularly, under the conditions described in this patent application, the first source of molten matrix alloy begins to infiltrate the mass of filler material under normal atmospheric pressures and thus begins the formation of a metal matrix composite. The first source of molten matrix metal alloy is consumed during its infiltration into the mass of filler material and, if desired, can be replenished, preferably by a continuous means, from the reservoir of molten matrix metal as the spontaneous infiltration continues. When a desired amount of permeable filler has been spontaneously infiltrated by the molten matrix alloy, the temperature is lowered to solidify the alloy, thereby forming a solid metal matrix structure that embeds the reinforcing filler material. It should be understood that the use of a reservoir of metal is simply one embodiment of the invention described in this patent application and it is not necessary to combine the reservoir embodiment with each of the alternate embodiments of the invention disclosed therein, some of which could also be beneficial to use in combination with the present invention.

The reservoir of metal can be present in an amount such that it provides for a sufficient amount of metal to infiltrate the permeable mass of filler material to a predetermined extent. Alternatively, an optional barrier means can contact the permeable mass of filler on at least one side thereof to define a surface boundary.

Moreover, while the supply of molten matrix alloy delivered should be at least sufficient to permit spontaneous infiltration to proceed essentially to the boundaries (e.g., barriers) of the permeable mass of filler material, the amount of alloy present in the reservoir could exceed such sufficient amount so that not only will there be a sufficient amount of alloy for complete infiltration, but excess molten metal alloy could remain and be attached to the metal matrix composite body. Thus, when excess molten alloy is present, the resulting body will be a complex composite body (e.g., macrocomposite), wherein an infiltrated ceramic body having a metal matrix therein will be directly bonded to excess metal remaining in the reservoir.

Each of the above-discussed Commonly Owned Metal Matrix Patent Applications describes methods for the production of metal matrix composite bodies and novel metal matrix composite bodies which are produced therefrom. The entire disclosures of all of the foregoing Commonly Owned Metal Matrix Patent Applications are expressly incorporated herein by reference.

SUMMARY OF THE INVENTION

A metal matrix composite body can be produced by spontaneously infiltrating a permeable mass of filler material or a preform with a molten matrix metal. The matrix metal in the infiltrated filler material or preform and/or the filler material or the preform may be modified substantially contiguously with infiltration and/or may be modified by a post formation process treatment (i.e., may be modified after infiltration has been achieved). Such modification results in enhanced or improved properties (e.g., improved mechanical properties especially at high temperatures, improved corrosion resistance, improved erosion resistance, etc.) in a formed metal matrix composite. Moreover, metal matrix composites produced by methods other than a spontaneous infiltration process also may be treated in accordance with a post formation process treatment according to the present invention.

To achieve spontaneous infiltration, a permeable mass of filler material or a preform is contacted with an infiltration enhancer and/or infiltration enhancer precursor and/or infiltrating atmosphere, at least at some point during the process, which permits molten matrix metal to spontaneously infiltrate the filler material or preform. In a preferred method for achieving spontaneous infiltration, rather than supplying an infiltration enhancer precursor, an infiltration enhancer may be supplied directly to at least one of the preform and/or matrix metal and/or infiltrating atmosphere. Ultimately, at least during the spontaneous infiltration, the infiltration enhancer should be located in at least a portion of the filler material or preform.

In a preferred embodiment for modifying at least one property of a metal matrix composite, once spontaneous infiltration into the preform or filler material has been achieved, but prior to the matrix metal solidifying, the matrix metal in the metal matrix composite body is modified. Specifically, at least a portion of the matrix metal is contacted with a second, which may also be molten, and which has a composition different from that of the matrix metal. Specifically, a second metal may become interdiffused with the matrix metal, thereby resulting in, for example, the formation of desirable intermetallics due to a reaction between the matrix metal and filler with the second metal. Accordingly, in this embodiment, it may be preferable for the second metal to be miscible with (e.g., when desirable to form intermetallics) the matrix metal.

In another preferred embodiment for modifying at least one property of a metal matrix composite, prior to completing spontaneous infiltration of molten matrix metal into a permeable mass of filler material or a preform, the composition of the matrix metal which continues to infiltrate is changed by adding a second metal thereto, which has a composition which is different from the matrix metal. For example, once molten matrix metal begins to infiltrate a permeable mass of filler material or a preform, a second metal could be added to (e.g., alloyed with) the source of matrix metal (e.g., a reservoir source of matrix metal). The second metal could be any metal which, when combined with the matrix metal, does not adversely affect the spontaneous infiltration of molten matrix metal and modifies the properties of the metal matrix composite (e.g., the matrix metal in the metal matrix composite) in a desired manner.

In a further preferred embodiment for modifying at least one property of a metal matrix composite, at least one of the matrix metal and/or filler material or preform in a metal matrix composite is modified substantially contiguously with the spontaneous infiltration of molten matrix metal into a filler material or preform. In this embodiment, a second material (e.g., a powdered metal or a precursor to a metal) may be admixed at least partially with the filler material or preform, said second material being reactive with the matrix metal and/or filler material or preform. Specifically, the second material may react with molten matrix metal to form desirable intermetallics which improve, for example, the high temperature strength, corrosion resistance, erosion resistance, etc., of the metal matrix composite.

In another preferred embodiment, spontaneous infiltration is not permitted to embed completely the filler material or preform (e.g., at least some porosity is created or formed in the filler material or preform). A second metal which is different in composition from the matrix metal may then be contacted with a surface of the metal matrix composite body which has not undergone complete infiltration. The second metal then infiltrates into the porosity of the metal matrix composite, (e.g., the second metal may alloy with the infiltrated matrix metal and provide a sufficient quantity of alloyed matrix metal to fill completely the porosity in the filler material or preform). Moreover, such filling-in of the porosity should occur at a temperature at or above the liquidus temperature of the matrix metal (and/or alloy of matrix metal and second metal). Accordingly, the metal matrix composite body will be modified by the filling-in of an alloy of matrix metal and second metal into the porosity of a filler material or preform.

In another preferred embodiment, a second metal, having a composition which is different from the matrix metal that has infiltrated a filler material or preform, can be contacted with at least a portion of a substantially completely infiltrated filler material or preform, and said second metal reacts with at least one of the matrix metal and/or filler material or preform. Specifically, in a preferred method, the second metal can be transported by matrix metal to contact with filler material or preform and/or may contact the filler material or preform directly, and thereby react with the filler material or preform to form a reaction product. In this preferred method, the reaction product which is formed undergoes a volumetric expansion relative to the original filler material or preform. Such reaction product typically is formed when the matrix metal is at, above, or slightly below the liquidus temperature which results in matrix metal being displaced from the metal matrix composite body. Accordingly, depending upon the amount of reaction product formed, an overall volume percent of matrix metal in the metal matrix composite body is reduced. For example, the formation of reaction product could be limited to a surface area of the metal matrix composite, thus forming a reaction product surface in a metal matrix composite substrate. Moreover, the formation of a reaction product is not limited to metal matrix composite bodies produced according to a spontaneous infiltration technique. It is conceivable that the formation of reaction product in any system which involves a conversion of matrix metal and/or filler material or preform to a reaction product which then displaces matrix metal can produce desirable results.

It is noted that this application discusses primarily aluminum matrix metals which, at some point during the formation of the metal matrix composite body, are contacted with magnesium, which functions as the infiltration enhancer precursor, in the presence of nitrogen, which functions as the infiltrating atmosphere. Thus, the matrix metal/infiltration enhancer precursor/infiltrating atmosphere system of aluminum/magnesium/nitrogen exhibits spontaneous infiltration. However, other matrix metal/infiltration enhancer precursor/infiltrating atmosphere systems may also behave in a manner similar to the system aluminum/magnesium/nitrogen. For example, similar spontaneous infiltration behavior has been observed in the aluminum/strontium/nitrogen system; the aluminum/zinc/oxygen system; and the aluminum/calcium/nitrogen system. Accordingly, even though the aluminum/magnesium/nitrogen system is discussed primarily herein, it should be understood that other matrix metal/infiltration enhancer precursor/infiltrating atmosphere systems may behave in a similar manner and are intended to be encompassed by the invention.

When the matrix metal comprises an aluminum alloy, the aluminum alloy is contacted with a preform comprising a filler material (e.g., alumina or silicon carbide) or a filler material, said filler material or preform having admixed therewith, and/or at some point during the process being exposed to, magnesium. Moreover, in a preferred embodiment, the aluminum alloy and/or preform or filler material are contained in a nitrogen atmosphere for at least a portion of the process. The preform will be spontaneously infiltrated and the extent or rate of spontaneous infiltration and formation of metal matrix will vary with a given set of process conditions including, for example, the concentration of magnesium provided to the system (e.g., in the aluminum alloy and/or in the filler material or preform and/or in the infiltrating atmosphere), the size and/or composition of the particles in the preform or filler material, the concentration of nitrogen in the infiltrating atmosphere, the time permitted for infiltration, and/or the temperature at which infiltration occurs. Spontaneous infiltration typically occurs to an extent sufficient to embed substantially completely the preform or filler material.

DEFINITIONS

"Aluminum", as used herein, means and includes essentially pure metal (e.g., a relatively pure, commercially available unalloyed aluminum) or other grades of metal and metal alloys such as the commercially available metals having impurities and/or alloying constituents such as iron, silicon, copper, magnesium, manganese, chromium, zinc, etc., therein. An aluminum alloy for purposes of this definition is an alloy or intermetallic compound in which aluminum is the major constituent.

"Balance Non-Oxidizino Gas", as used herein, means that any gas present in addition to the primary gas comprising the infiltrating atmosphere, is either an inert gas or a reducing gas which is substantially non-reactive with the matrix metal under the process conditions. Any oxidizing gas which may be present as an impurity in the gas(es) used should be insufficient to oxidize the matrix metal to any substantial extent under the process conditions.

"Barrier" or "barrier means", as used herein, means any suitable means which interferes, inhibits, prevents or terminates the migration, movement, or the like, of molten matrix metal beyond a surface boundary of a permeable mass of filler material or preform, where such surface boundary is defined by said barrier means. Suitable barrier means may be any such material, compound, element, composition, or the like, which, under the process conditions, maintains some integrity and is not substantially volatile (i.e., the barrier material does not volatilize to such an extent that it is rendered non-functional as a barrier).

Further, suitable "barrier means" includes materials which are substantially non-wettable by the migrating molten matrix metal under the process conditions employed. A barrier of this type appears to exhibit substantially little or no affinity for the molten matrix metal, and movement beyond the defined surface boundary of the mass of filler material or preform is prevented or inhibited by the barrier means. The barrier reduces any final machining or grinding that may be required and defines at least a portion of the surface of the resulting metal matrix composite product. The barrier may in certain cases be permeable or porous, or rendered permeable by, for example, drilling holes or puncturing the barrier, to permit gas to contact the molten matrix metal.

"Carcass" or "Carcass of Matrix Metal", as used herein, refers to any of the original body of matrix metal remaining which has not been consumed during formation of the metal matrix composite body, and typically, if allowed to cool, remains in at least partial contact with the metal matrix composite body which has been formed. It should be understood that the carcass may also include a second or foreign metal therein.

"Filler", as used herein, is intended to include either single constituents or mixtures of constituents which are substantially nonreactive with and/or of limited solubility in the matrix metal and may be single or multi-phase. Fillers may be provided in a wide variety of forms, such as powders, flakes, platelets, microspheres, whiskers, bubbles, etc., and may be either dense or porous. "Filler" may also include ceramic fillers, such as alumina or silicon carbide as fibers, chopped fibers, particulates, whiskers, bubbles, spheres, fiber mats, or the like, and coated fillers such as carbon fibers coated with alumina or silicon carbide to protect the carbon from attack, for example, by a molten aluminum parent metal. Fillers may also include metals.

"Infiltratinq Atmosphere", as used herein, means that atmosphere which is present which interacts with the matrix metal and/or preform (or filler material) and/or infiltration enhancer precursor and/or infiltration enhancer and permits or enhances spontaneous infiltration of the matrix metal to occur.

"Infiltration Enhancer", as used herein, means a material which promotes or assists in the spontaneous infiltration of a matrix metal into a filler material or preform. An infiltration enhancer may be formed from, for example, a reaction of an infiltration enhancer precursor with an infiltrating atmosphere to form (1) a gaseous species and/or (2) a reaction product of the infiltration enhancer precursor and the infiltrating atmosphere and/or (3) a reaction product of the infiltration enhancer precursor and the filler material or preform. Moreover, the infiltration enhancer may be supplied directly to at least one of the preform and/or matrix metal and/or infiltrating atmosphere and function in a substantially similar manner to an infiltration enhancer which has formed from a reaction between an infiltration enhancer precursor and another species. Ultimately, at least during the spontaneous infiltration, the infiltration enhancer should be located in at least a portion of the filler material or preform to achieve spontaneous infiltration.

"Infiltration Enhancer Precursor" or "Precursor to the Infiltration Enhancer", as used herein, means a material which when used in combination with the matrix metal, preform and/or infiltrating atmosphere forms an infiltration enhancer which induces or assists the matrix metal to spontaneously infiltrate the filler material or preform. Without wishing to be bound by any particular theory or explanation, it appears as though it may be necessary for the precursor to the infiltration enhancer to be capable of being positioned, located or transportable to a location which permits the infiltration enhancer precursor to interact with the infiltrating atmosphere and/or the preform or filler material and/or metal. For example, in some matrix metal/infiltration enhancer precursor/infiltrating atmosphere systems, it is desirable for the infiltration enhancer precursor to volatilize at, near, or in some cases, even somewhat above the temperature at which the matrix metal becomes molten. Such volatilization may lead to: (1) a reaction of the infiltration enhancer precursor with the infiltrating atmosphere to form a gaseous species which enhances wetting of the filler material or preform by the matrix metal; and/or (2) a reaction of the infiltration enhancer precursor with the infiltrating atmosphere to form a solid, liquid or gaseous infiltration enhancer in at least a portion of the filler material or preform which enhances wetting; and/or (3) a reaction of the infiltration enhancer precursor within the filler material or preform which forms a solid, liquid or gaseous infiltration enhancer in at least a portion of the filler material or preform which enhances wetting.

"Interdiffusion" or "Interdiffused", as used herein, means that there occurs at least partial contact or mixing of a matrix metal with a second or different metal, to result in a new desirable alloy and/or intermetallic.

"Matrix Metal", or "Matrix Metal Alloy", as used herein, means that metal which is utilized to form a metal matrix composite (e.g., before infiltration) and/or that metal which is intermingled with a filler material to form a metal matrix composite body (e.g., after infiltration). When a specified metal is mentioned as the matrix metal, it should be understood that such matrix metal includes that metal as an essentially pure metal, a commercially available metal having impurities and/or alloying constituents therein, an intermetallic compound or an alloy in which that metal is the maJor or predominant constituent.

"Matrix Metal/Infiltration Enhancer Precursor/Infiltratinq Atmosphere System" or "Spontaneous System", as used herein, refers to that combination of materials which exhibit spontaneous infiltration into a preform or filler material. It should be understood that whenever a "/" appears between an exemplary matrix metal, infiltration enhancer precursor and infiltrating atmosphere that the "/" is used to designate a system or combination of materials which, when combined in a particular manner, exhibits spontaneous infiltration into a preform or filler material.

"Metal Matrix Composite" or "MMC", as used herein, means a material comprising a two- or three-dimensionally interconnected alloy or matrix metal which has embedded a preform or filler material. The matrix metal may include various alloying elements to provide specifically desired mechanical and physical properties in the resulting composite.

A Metal "Different" from the Matrix Metal means a metal which does not contain, as a primary constituent, the same metal as the matrix metal (e.g., if the primary constituent of the matrix metal is aluminum, the "different" metal could have a primary constituent of, for example, nickel).

"Nonreactive Vessel for Housing Matrix Metal" means any vessel which can house or contain a filler material (or preform) and/or molten matrix metal under the process conditions and not react with the matrix and/or the infiltrating atmosphere and/or infiltration enhancer precursor and/or filler material or preform in a manner which would be significantly detrimental to the spontaneous infiltration mechanism.

"Preform" or "Permeable Preform", as used herein, means a porous mass of filler or filler material which is manufactured with at least one surface boundary which essentially defines a boundary for infiltrating matrix metal, such mass retaining sufficient shape integrity and green strength to provide dimensional fidelity prior to being infiltrated by the matrix metal. The mass should be sufficiently porous to accommodate spontaneous infiltration of the matrix metal thereinto. A preform typically comprises a bonded array or arrangement of filler, either homogeneous or heterogeneous, and may be comprised of any suitable material (e.g., ceramic and/or metal particulates, powders, fibers, whiskers, etc., and any combination thereof). A preform may exist either singularly or as an assemblage.

"Reaction Product", as used herein, means the product of a reaction between a second or different metal with at least one of a filler material or preform and/or a matrix metal.

"Reservoir", as used herein, means a separate body of matrix metal positioned relative to a mass of filler or a preform so that, when the metal is molten, it may flow to replenish, or in some cases to initially provide and subsequently replenish, that portion, segment or source of matrix metal which is in contact with the filler or preform.

"Spontaneous Infiltration", as used herein, means the infiltration of matrix metal into the permeable mass of filler or preform occurs without requirement for the application of pressure or vacuum (whether externally applied or internally created).

DETAILED DESCRIPTION OF THE INVENTION AND PREFERRED EMBODIMENTS

The present invention relates to forming a metal matrix composite body by spontaneously infiltrating a permeable mass of filler material or preform with molten matrix metal and during and/or subsequent to said spontaneous infiltration modifying at least a portion of the metal matrix composite body.

A metal matrix composite body can be produced by spontaneously infiltrating a permeable mass of filler material or a preform with a molten matrix metal. The matrix metal in the infiltrated filler material or preform and/or the filler material or the preform may be modified substantially contiguously with infiltration; and/or may be modified by a post formation process treatment (i.e., may be modified after infiltration has been achieved). Such modification results in enhanced or improved properties (e.g., improved mechanical properties, improved corrosion resistance, improved erosion resistance, etc.) in a formed metal matrix composite. Moreover, metal matrix composites produced by methods other than a spontaneous infiltration process also may be treated in accordance with a post formation process treatment according to the present invention.

To achieve spontaneous infiltration, a permeable mass of filler material or a preform is contacted with an infiltration enhancer and/or infiltration enhancer precursor and/or infiltrating atmosphere, at least at some point during the process, which permits molten matrix metal to spontaneously infiltrate the filler material or preform. In a preferred method for achieving spontaneous infiltration, rather than supplying an infiltration enhancer precursor, an infiltration enhancer may be supplied directly to at least one of the preform and/or matrix metal and/or infiltrating atmosphere. Ultimately, at least during the spontaneous infiltration, the infiltration enhancer should be located in at least a portion of the filler material or preform.

In a preferred embodiment for modifying at least one property of a metal matrix composite, once spontaneous infiltration into the preform or filler material has been achieved, but prior to the matrix metal solidifying, the matrix metal in the metal matrix composite body is modified. Specifically, at least a portion of the matrix metal is contacted with a second metal which, may also be molten, and which has a composition different from that of the matrix metal. Specifically, a second metal may become interdiffused with the matrix metal, thereby resulting in, for example, the formation of desirable intermetallics due to a reaction between the matrix metal and second metal. Accordingly, in this embodiment, the second metal may be miscible with (e.g., form desirable intermetallics with) the matrix metal.

In the practice of a preferred embodiment, a stainless steel vessel comprising a container having a bottom plate sealed into position by an annular copper gasket can be utilized. The stainless steel container preferably contains a refractory support. A stainless steel can may have an alumina filler such as 90 grit, 38 Alundum supplied by Norton Co., with about 50% by volume of a powdered second metal which is different from the matrix metal. In this embodiment, the matrix metal alloy may be placed on the filler material in the stainless steel can. The matrix metal preferably comprises an aluminum alloy with about 5 percent by weight Mg. In order to spontaneously infiltrate matrix metal into the filler material, the stainless steel vessel should be heated to about 750.degree.-1100.degree. C. in an atmosphere of a nitrogen-containing gas. As the matrix metal spontaneously infiltrates into the permeable filler, it contacts the second metal contained in the filler (e.g., nickel). The aluminum in the matrix metal may react with the nickel in the filler to form an intermetallic such as a nickel aluminide in the channels through which the matrix metal passed in order to spontaneously infiltrate the filler. The degree to which any reaction occurs depends upon temperature, the length of exposure at this temperature, and/or the miscibility of the molten metals.

In another preferred embodiment for modifying at least one property of a metal matrix composite, prior to completing spontaneous infiltration of molten matrix metal into a permeable mass of filler material or a preform, the composition of the matrix metal which continues to infiltrate is changed by adding a second metal thereto, which has a composition which is different from the matrix metal. For example, once molten matrix metal begins to infiltrate a permeable mass of filler material or a preform, a second metal could be added to (e.g., alloyed with) the source of matrix metal (e.g., a reservoir source of matrix metal). The second metal could be any metal which, when combined with the matrix metal, does not adversely affect the spontaneous infiltration of molten matrix metal and modifies the properties of the metal matrix composite (e.g., the matrix metal in the metal matrix composite) in a desired manner.

In a further preferred embodiment for modifying at least one property of a metal matrix composite, at least one of the matrix metal and/or filler material or preform in a metal matrix composite is modified substantially contiguously with the spontaneous infiltration of molten matrix metal into a filler material or preform. In this embodiment, a second material (e.g., a powdered metal or a precursor to a metal) may be admixed at least partially with the filler material or preform, said second material being reactive in situ with the matrix metal and/or filler material or preform. Specifically, the second material may react with molten matrix metal to form desirable intermetallics which improve, for example, the high temperature strength, corrosion resistance, erosion resistance, etc., of the metal matrix composite.

In another preferred embodiment, spontaneous infiltration is not permitted to embed completely the filler material or preform (e.g., at least some porosity is created or formed in the filler material or preform). A second metal which is different in composition from the matrix metal may then be contacted with a surface of the metal matrix composite body which has not undergone complete infiltration. The second metal then infiltrates into the porosity of the metal matrix composite (e.g., the second metal may alloy with the infiltrated matrix metal and provide a sufficient quantity of alloyed matrix metal to fill completely the porosity in the filler material or preform). Moreover, such filling-in of the porosity should occur at a temperature at or above the liquidus temperature of the matrix metal (and/or alloy of matrix metal and second metal). Accordingly, the metal matrix composite body will be modified by the filling-in of an alloy of matrix metal and second metal into the porosity of a filler material or preform.

In another preferred embodiment, a second metal, having a composition which is different from matrix metal that has infiltrated a filler material or preform, can be contacted with at least a portion of a substantially completely infiltrated filler material or preform and said second metal reacts with at least one of the matrix metal and/or filler material or preform. Specifically, in a preferred method, the second metal can be transported by matrix metal to contact with filler material or preform, and/or may contact the filler material or preform directly, and thereby react with the filler material or preform to form a reaction product. In this preferred method, the reaction product which is formed undergoes a volumetric expansion relative to the original filler material or preform. Such reaction product typically is formed when the matrix metal is at, above, or slightly below the liquidus temperature which results in matrix metal being displaced from the metal matrix composite body. Accordingly, depending upon the amount of reaction product formed, an overall volume percent of matrix metal in the metal matrix composite body is reduced. For example, the formation of reaction product could be limited to a surface area of the metal matrix composite, thus forming a reaction product surface in a metal matrix composite substrate. Moreover, the formation of a reaction product is not limited to metal matrix composite bodies produced according to a spontaneous infiltration technique. It is conceivable that the formation of reaction product in any system which involves a conversion of matrix metal and/or filler material or preform to a reaction product then displaces the matrix metal which could produce desirable results.

This application discloses primarily methods of modifying the properties of metal matrix composite bodies produced according to a spontaneous infiltration process. However, from the text, it should be understood that some of the modification methods may also be applicable to metal matrix composites made by alternative methods.

Moreover, in any of the above discussed alteration methods, the amount or portion of metal matrix composite body and/or filler material which is to be converted or altered can be varied. Thus, each of the above-discussed processes could be limited to primarily a surface area of a metal matrix composite body, or, if conversion was permitted to occur for a sufficient amount of time, substantially complete conversion of the metal matrix composite body which was formed by spontaneous infiltration could occur. Moreover, factors such as temperature, atmospheric pressure, etc., could enhance or reduce the rate of conversion of the formed metal matrix composite body.

In a still further embodiment, a gaseous means is flowed across the surface of a formed metal matrix composite body, the gaseous means containing an element which reacts with at least a portion of a surface of formed metal matrix composite body, thereby modifying the resultant properties of the formed body.

To obtain spontaneous infiltration, an infiltration enhancer and/or infiltration enhancer precursor and/or infiltrating atmosphere are in communication with the filler material or preform, at least at some point during the process, which permits molten matrix metal to spontaneously infiltrate the filler material or preform. Specifically, in order to effect spontaneous infiltration of the matrix metal into the filler material or preform, an infiltration enhancer should be provided to the spontaneous system. An infiltration enhancer could be formed from an infiltration enhancer precursor which could be provided (1) in the matrix metal; and/or (2) in the filler material or preform; and/or (3) from the infiltrating atmosphere and/or (4)from an external source into the spontaneous system. Moreover, rather than supplying an infiltration enhancer precursor, an infiltration enhancer may be supplied directly to at least one of the filler material or preform, and/or matrix metal, and/or infiltrating atmosphere. Ultimately, at least during the spontaneous infiltration, the infiltration enhancer should be located in at least a portion of the filler material or preform.

In a preferred embodiment it is possible that the infiltration enhancer precursor can be at least partially reacted with the infiltrating atmosphere such that infiltration enhancer can be formed in at least a portion of the filler material or preform prior to or substantially contiguous with contacting the preform with molten matrix metal (e.g., if magnesium was the infiltration enhancer precursor and nitrogen was the infiltrating atmosphere, the infiltration enhancer could be magnesium nitride which would be located in at least a portion of the filler material or preform).

An example of a matrix metal/infiltration enhancer precursor/infiltrating atmosphere system is the aluminum/magnesium/nitrogen system. Specifically, an aluminum matrix metal can be embedded within a filler material which can be contained within a suitable refractory vessel which, under the process conditions, does not react with the aluminum matrix metal and/or the filler material when the aluminum is made molten. A filler material containing or being exposed to magnesium, and being exposed to, at least at some point during the processing, a nitrogen atmosphere, can be contacted with the molten aluminum matrix metal. The matrix metal will then spontaneously infiltrate the filler material or preform.

Under the conditions employed in the method of the present invention, in the case of an aluminum/magnesium/ nitrogen spontaneous system, the filler material or preform should be sufficiently permeable to permit the nitrogen-containing gas to penetrate or permeate the filler material or preform at some point during the process and/or contact the molten matrix metal. Moreover, the permeable filler material or preform can accommodate infiltration of the molten matrix metal, thereby causing the nitrogen-permeated filler material or preform to be infiltrated spontaneously with molten matrix metal to form a metal matrix composite body and/or cause the nitrogen to react with an infiltration enhancer precursor to form infiltration enhancer in the filler material or preform and thereby resulting in spontaneous infiltration. The extent or rate of spontaneous infiltration and formation of the metal matrix composite will vary with a given set of process conditions, including magnesium content of the aluminum alloy, magnesium content of the filler material or preform, amount of magnesium nitride in the filler material or preform, the presence of additional alloying elements (e.g., silicon, iron, copper, manganese, chromium, zinc, and the like), average size of the filler material (e.g., particle diameter), surface condition and type of filler material, nitrogen concentration of the infiltrating atmosphere, time permitted for infiltration and temperature at which infiltration occurs. For example, for infiltration of the molten aluminum matrix metal to occur spontaneously, the aluminum can be alloyed with at least about 1% by weight, and preferably at least about 3% by weight, magnesium (which functions as the infiltration enhancer precursor), based on alloy weight. Auxiliary alloying elements, as discussed above, may also be included in the matrix metal to tailor specific properties thereof. Additionally, the auxiliary alloying elements may affect the minimum amount of magnesium required in the matrix aluminum metal to result in spontaneous infiltration of the filler material or preform. Loss of magnesium from the spontaneous system due to, for example, volatilization should not occur to such an extent that no magnesium was present to form infiltration enhancer. Thus, it is desirable to utilize a sufficient amount of initial alloying elements to assure that spontaneous infiltration will not be adversely affected by volatilization. Still further, the presence of magnesium in both of the filler material and matrix metal or the filler material alone may result in a reduction in the required amount of magnesium to achieve spontaneous infiltration (discussed in greater detail later herein).

The volume percent of nitrogen in the nitrogen atmosphere also affects formation rates of the metal matrix composite body. Specifically, if less than about 10 volume percent of nitrogen is present in the atmosphere, very slow or little spontaneous infiltration will occur. It has been discovered that it is preferable for at least about 50 volume percent of nitrogen to be present in the infiltrating atmosphere, thereby resulting in, for example, shorter infiltration times due to a much more rapid rate of infiltration. The infiltrating atmosphere (e.g., a nitrogen containing gas) can be supplied directly to the filler material and/or matrix metal, or it may be produced or result from a decomposition of a material.

The minimum magnesium content required for molten matrix metal to infiltrate a filler material or preform depends on one or more variables such as the processing temperature, time, the presence of auxiliary alloying elements such as silicon or zinc, the nature of the filler material, the location of the magnesium in one or more components of the spontaneous system, the nitrogen content of the atmosphere, and the rate at which the nitrogen atmosphere flows. Lower temperatures or shorter heating times can be used to obtain complete infiltration as the magnesium content of the alloy and/or filler material is increased. Also, for a given magnesium content, the addition of certain auxiliary alloying elements such as zinc permits the use of lower temperatures. For example, a magnesium content of the matrix metal at the lower end of the operable range, e.g., from about 1 to 3 weight percent, may be used in conjunction with at least one of the following: an above-minimum processing temperature, a high nitrogen concentration, or one or more auxiliary alloying elements. When no magnesium is added to the filler material, alloys containing from about 3 to 5 weight percent magnesium are preferred on the basis of their general utility over a wide variety of process conditions, with at least about 5 percent being preferred when lower temperatures and shorter times are employed. Magnesium contents in excess of about 10 percent by weight of the aluminum alloy may be employed to moderate the temperature conditions required for infiltration. The magnesium content may be reduced when used in conjunction with an auxiliary alloying element, but these elements serve an auxiliary function only and are used together with at least the above-specified minimum amount of magnesium. For example, there was substantially no infiltration of nominally pure aluminum alloyed only with 10 percent silicon at 1000.degree. C. into a bedding of 500 mesh, 39 Crystolon (99 percent pure silicon carbide from Norton Co.). However, in the presence of magnesium, silicon has been found to promote the infiltration process. As a further example, the amount of magnesium varies if it is supplied exclusively to the filler material. It has been discovered that spontaneous infiltration will occur with a lesser weight percent of magnesium supplied to the spontaneous infiltration system when at least some of the total amount of magnesium supplied is placed in the filler material. It may be desirable for a lesser amount of magnesium to be provided in order to prevent the formation of undesirable intermetallics in the metal matrix composite body. In the case of a silicon carbide preform, it has been discovered that when the preform is contacted with an aluminum matrix metal, the preform containing at least about 1% by weight magnesium and being in the presence of a substantially pure nitrogen atmosphere, the matrix metal spontaneously infiltrates the preform. In the case of an alumina preform, the amount of magnesium required to achieve acceptable spontaneous infiltration is slightly higher. Specifically, it has been found that when an alumina preform, when contacted with a similar aluminum matrix metal, at about the same temperature as the aluminum that infiltrated into the silicon carbide preform, and in the presence of the same nitrogen atmosphere, at least about 3% by weight magnesium may be required to achieve similar spontaneous infiltration to that achieved in the silicon carbide preform discussed immediately above.

Further, when infiltrating a permeable filler utilizing a aluminum/magnesium/nitrogen system a spinel (e.g., MgAl.sub.2 O.sub.4) can be formed. Thus, when a sufficient amount of magnesium is present, the magnesium can react with an alumina filler if held at a high temperature for a sufficient period of time. The formation of MgAl.sub.2 O.sub.4 results in the volumetric expansion and reduction of metal, as discussed above.

It is also noted that it is possible to supply to the spontaneous system infiltration enhancer precursor and/or infiltration enhancer on a surface of the alloy and/or on a surface of the preform or filler material and/or within the preform or filler material prior to infiltrating the matrix metal into the filler material or preform (i.e., it may not be necessary for the supplied infiltration enhancer or infiltration enhancer precursor to be alloyed with the matrix metal, but rather, simply supplied to the spontaneous system). If the magnesium was applied to a surface of the matrix metal it may be preferred that said surface should be the surface which is closest to, or preferably in contact with, the permeable mass of filler material or vice versa; or such magnesium could be mixed into at least a portion of the filler material. Still further, it is possible that some combination of surface application, alloying and placement of magnesium into at least a portion of the filler material could be used. Such combination of applying infiltration enhancer(s) and/or infiltration enhancer precursor(s) could result in a decrease in the total weight percent of magnesium needed to promote infiltration of the matrix aluminum metal into the filler material, as well as achieving lower temperatures at which infiltration can occur. Moreover, the amount of undesirable intermetallics formed due to the presence of magnesium could also be minimized.

The use of one or more auxiliary alloying elements and the concentration of nitrogen in the surrounding gas also affects the extent of nitriding of the matrix metal at a given temperature. For example, auxiliary alloying elements such as zinc or iron included in the alloy, or placed on a surface of the alloy, may be used to reduce the infiltration temperature and thereby decrease the amount of nitride formation, whereas increasing the concentration of nitrogen in the gas may be used to promote nitride formation.

The concentration of magnesium in the alloy, and/or placed onto a surface of the alloy, and/or combined in the filler or preform material, also tends to affect the extent of infiltration at a given temperature. Consequently, in some cases where little or no magnesium is contacted directly with the preform or filler material, it may be preferred that at least about three weight percent magnesium be included in the alloy. Alloy contents of less than this amount, such as one weight percent magnesium, may require higher process temperatures or an auxiliary alloying element for infiltration. The temperature required to effect the spontaneous infiltration process of this invention may be lower: (1) when the magnesium content of the alloy alone is increased, e.g. to at least about 5 weight percent; and/or (2) when alloying constituents are mixed with the permeable mass of filler material; and/or (3) when another element such as zinc or iron is present in the aluminum alloy. The temperature also may vary with different filler materials. In general, spontaneous and progressive infiltration will occur at a process temperature of at least about 675.degree. C., and preferably a process temperature of at least about 750.degree.-800.degree. C. Temperatures generally in excess of 1200.degree. C. do not appear to benefit the process, and a particularly useful temperature range has been found to be from about 675.degree. C. to about 1200.degree. C. However, as a general rule, the spontaneous infiltration temperature is a temperature which is above the melting point of the matrix metal but below the volatilization temperature of the matrix metal. Moreover, the spontaneous infiltration temperature should be below the melting point of the filler material. Still further, as temperature is increased, the tendency to form a reaction product between the matrix metal and infiltrating atmosphere increases (e.g., in the case of aluminum matrix metal and a nitrogen infiltrating atmosphere, aluminum nitride may be formed). Such reaction product may be desirable or undesirable, dependent upon the intended application of the metal matrix composite body. Additionally, electric resistance heating is typically used to achieve the infiltrating temperatures. However, any heating means which can cause the matrix metal to become molten and does not adversely affect spontaneous infiltration is acceptable for use with the invention.

In the present method, for example, a permeable filler material or preform comes into contact with molten aluminum in the presence of, at least sometime during the process, a nitrogen-containing gas. The nitrogen- containing gas may be supplied by maintaining a continuous flow of gas into contact with at least one of the filler material or the preform and/or molten aluminum matrix metal. Although the flow rate of the nitrogen-containing gas is not critical, it is preferred that the flow rate be sufficient to compensate for any nitrogen lost from the atmosphere due to nitride formation in the alloy matrix, and also to prevent or inhibit the incursion of air which can have an oxidizing effect on the molten metal.

The method of forming a metal matrix composite is applicable to a wide variety of filler materials, and the choice of filler materials will depend on such factors as the matrix alloy, the process conditions, the reactivity of the molten matrix alloy with the filler material, the ability of the filler material to conform to the matrix metal and the properties sought for the final composite product. For example, when aluminum is the matrix metal, suitable filler materials include (a) oxides, e.g. alumina; (b) carbides, e.g. silicon carbide; (c) borides, e.g. aluminum dodecarboride, and (d) nitrides, e.g. aluminum nitride. If there is a tendency for the filler material to react with the molten aluminum matrix metal, this might be accommodated by minimizing the infiltration time and temperature or by providing a non-reactive coating on the filler. The filler material may comprise a substrate, such as carbon or other non-ceramic material, bearing an appropriate coating to protect the substrate from attack or degradation. Suitable ceramic coatings include oxides, carbides, borides and nitrides. Ceramics which are preferred for use in the present method include alumina and silicon carbide in the form of particles, platelets, whiskers and fibers. The fibers can be discontinuous (in chopped form) or in the form of woven mats or continuous filament, such as multifilament tows. Further, the filler material may be homogeneous or heterogeneous.

It also has been discovered that certain filler materials exhibit enhanced infiltration relative to filler materials having a similar chemical composition. For example, crushed alumina bodies made by the method disclosed in U.S. Pat. No. 4,713,360, entitled "Novel Ceramic Materials and Methods of Making Same", which issued on Dec. 15, 1987, in the names of Marc S. Newkirk et.al., exhibit desirable infiltration properties relative to commercially available alumina products. Moreover, crushed alumina bodies made by the method disclosed in Copending and Commonly Owned application Ser. No. 819,397, entitled "Composite Ceramic Articles and Methods of Making Same", in the names of Marc S. Newkirk, also exhibit desirable infiltration properties relative to commercially available aluminam products. The subject matter of each of the issued Patent and Copending Patent Application is herein expressly incorporated by reference. Specifically, it has been discovered that substantially complete infiltration of a permeable mass of a ceramic or ceramic composite material can occur at lower infiltration temperatures and/or lower infiltration times by utilizing a crushed or comminuted body produced by the method of the aforementioned U.S. Patent and Patent Application.

The size and shape of the filler material can be any that may be required to achieve the properties desired in the composite. Thus, the filler material may be in the form of particles, whiskers, platelets or fibers and mixtures thereof since infiltration is not restricted by the shape of the filler material. Other shapes such as spheres, tubules, pellets, refractory fiber cloth, and the like may be employed. In addition, the size of the material does not limit infiltration, although a higher temperature or longer time period may be needed for complete infiltration of a mass of smaller particles than for larger particles. Further, the mass of filler material (shaped into a preform) to be infiltrated should be permeable (i.e., permeable to molten matrix metal and to the infiltrating atmosphere).

The method of forming metal matrix composites according to the present invention, not being dependent on the use of pressure to force or squeeze molten matrix metal into a mass of filler material, permits the production of substantially uniform metal matrix composites having a high volume fraction of filler material and low porosity. Higher volume fractions of filler material on the order of at least about 50% may be achieved by using a lower porosity initial mass of filler material and particles of varying size. Higher volume fractions also may be achieved if the mass of filler is compacted or otherwise densified provided that the mass is not converted into either a compact with close cell porosity or into a fully dense structure that would prevent infiltration by the molten alloy.

It has been observed that for aluminum infiltration and matrix formation around a ceramic filler, wetting of the ceramic filler by the aluminum matrix metal may be an important part of the infiltration mechanism. Moreover, at low processing temperatures, a negligible or minimal amount of metal nitriding occurs resulting in a minimal discontinuous phase of aluminum nitride dispersed in the metal matrix. However, as the upper end of the temperature range is approached, nitridation of the metal is more likely to occur. Thus, the amount of the nitride phase in the metal matrix can be controlled by varying the processing temperature at which infiltration occurs. The specific process temperature at which nitride formation becomes more pronounced also varies with such factors as the matrix aluminum alloy used and its quantity relative to the volume of filler, the filler material to be infiltrated, and the nitrogen concentration of the infiltrating atmosphere. For example, the extent of aluminum nitride formation at a given process temperature is believed to increase as the ability of the alloy to wet the filler decreases and as the nitrogen concentration of the atmosphere increases.

It is therefore possible to tailor the constituency of the metal matrix during formation of the composite to impart certain characteristics to the resulting product. For a given system, the process conditions can be selected to control the nitride formation. A composite product containing an aluminum nitride phase will exhibit certain properties which can be favorable to, or improve the performance of, the product. Further, the temperature range for spontaneous infiltration with an aluminum alloy may vary with the ceramic material used. In the case of alumina as the filler material, the temperature for infiltration should preferably not exceed about 1000.degree. C. if it is desired that the ductility of the matrix not be reduced by the significant formation of nitride. However, temperatures exceeding 1000.degree. C. may be employed if it is desired to produce a composite with a less ductile and stiffer matrix. To infiltrate silicon carbide, higher temperatures of about 1200.degree. C. may be employed since the aluminum alloy nitrides to a lesser extent, relative to the use of alumina as filler, when silicon carbide is employed as a filler material.

Moreover, it is possible to use a reservoir of matrix metal to assure complete infiltration of the filler material and/or to supply a second metal which has a different composition from the first source of matrix metal. Specifically, in some cases it may be desirable to utilize a matrix metal in the reservoir which differs in composition from the first source of matrix metal. For example, if an aluminum alloy is used as the first source of matrix metal, then virtually any other metal or metal alloy which was molten at the processing temperature could be used as the reservoir metal. Molten metals frequently are very miscible with each other which would result in the reservoir metal mixing with the first source of matrix metal, so long as an adequate amount of time is given for the mixing to occur. Thus, by using a reservoir metal which is different in composition than the first source of matrix metal, it is possible to tailor the properties of the metal matrix to meet various operating requirements and thus tailor the properties of the metal matrix composite.

A barrier means may also be utilized in combination with the present invention. Specifically, the barrier means for use with this invention may be any suitable means which interferes, inhibits, prevents or terminates the migration, movement, or the like, of molten matrix alloy (e.g., an aluminum alloy) beyond the defined surface boundary of the filler material. Suitable barrier means may be any material, compound, element, composition, or the like, which, under the process conditions of this invention, maintains some integrity, is not volatile and preferably is permeable to the gas used with the process as well as being capable of locally inhibiting, stopping, interfering with, preventing, or the like, continued infiltration or any other kind of movement beyond the defined surface boundary of the filler material.

Suitable barrier means includes materials which are substantially non-wettable by the migrating molten matrix alloy under the process conditions employed. A barrier of this type appears to exhibit little or no affinity for the molten matrix alloy, and movement beyond the defined surface boundary of the filler material is prevented or inhibited by the barrier means. The barrier reduces any final machining or grinding that may be required of the metal matrix composite product. As stated above, the barrier preferably should be permeable or porous, or rendered permeable by puncturing, to permit the gas to contact the molten matrix alloy.

Suitable barriers particularly useful for aluminum matrix alloys are those containing carbon, especially the crystalline allotropic form of carbon known as graphite. Graphite is essentially non-wettable by the molten aluminum alloy under the described process conditions. A particularly preferred graphite is a graphite tape product that is sold under the trademark Grafoil.RTM., registered to Union Carbide. This graphite tape exhibits sealing characteristics that prevent the migration of molten aluminum alloy beyond the defined surface boundary of the filler material. This graphite tape is also resistant to heat and is chemically inert. Grafoil.RTM. graphite material is flexible, compatible, conformable and resilient. It can be made into a variety of shapes to fit any barrier application. However, graphite barrier means may be employed as a slurry or paste or even as a paint film around and on the boundary of the filler material. Grafoil.RTM. is particularly preferred because it is in the form of a flexible graphite sheet. In use, this paper-like graphite is simply formed around the filler material.

Other preferred barrier(s) for aluminum metal matrix alloys in nitrogen are the transition metal borides (e.g., titanium diboride (TiB.sub.2)) which are generally non-wettable by the molten aluminum metal alloy under certain of the process conditions employed using this material. With a barrier of this type, the process temperature should not exceed about 875.degree. C., for otherwise the barrier material becomes less efficacious and, in fact, with increased temperature infiltration into the barrier will occur. The transition metal borides are typically in a particulate form (1-30 microns). The barrier materials may be applied as a slurry or paste to the boundaries of the permeable mass of ceramic filler material which preferably is preshaped as a preform.

Other useful barriers for aluminum metal matrix alloys in nitrogen include low-volatile organic compounds applied as a film or layer onto the external surface of the filler material. Upon firing in nitrogen, especially at the process conditions of this invention, the organic compound decomposes leaving a carbon soot film. The organic compound may be applied by conventional means such as painting, spraying, dipping, etc.

Moreover, finely ground particulate materials can function as a barrier so long as infiltration of the particulate material would occur at a rate which is slower than the rate of infiltration of the filler material.

Thus, the barrier means may be applied by any suitable means, such as by layering the defined surface boundary with the barrier means. Such layer of barrier means may be applied by painting, dipping, silk screening, evaporating, or otherwise applying the barrier means in liquid, slurry, or paste form, or by sputtering a vaporizable barrier means, or by simply depositing a layer of a solid particulate barrier means, or by applying a solid thin sheet or film of barrier means onto the defined surface boundary. With the barrier means in place, spontaneous infiltration substantially terminates upon reaching the defined surface boundary and contacting the barrier means.

While the preceding embodiments have been described with particularity, various modifications should be considered to be within the scope of the claims appended hereto.

Claims

1. A method for making a metal matrix composite, comprising:

providing a body comprising at least one material selected from the group consisting of a loose mass of substantially non-reactive filler and a preform comprising a shaped substantially non-reactive filler;

spontaneously infiltrating at least a portion of said body with molten matrix metal;

contacting at least a portion of said body or said matrix metal with a second metal which is different in composition from said matrix metal, thereby modifying at least one property of the infiltrated body; and

cooling said infiltrated body containing said matrix metal and second metal therein, thereby forming a metal matrix composite.

2. The method of claim 1, wherein an infiltrating atmosphere communicates with at least one of the body and the matrix metal for at least a portion of the period of infiltration.

3. The method of claim 2, wherein the infiltrating atmosphere comprises an atmosphere selected from the group consisting of oxygen and nitrogen.

4. The method of claim 2, further comprising the step of supplying at least one of an infiltration enhancer precursor and an infiltration enhancer to at least one of the matrix metal, the body and the infiltrating atmosphere.

5. The method of claim 4, wherein said at least one of said infiltration enhancer precursor and infiltration enhancer is provided in more than one of said matrix metal, said filler and said infiltrating atmosphere.

6. The method of claim 4, wherein the infiltration enhancer is formed by reacting an infiltration enhancer precursor and at least one species selected from the group consisting of the infiltrating atmosphere, a material added to the filler and the matrix metal.

7. The method of claim 6, wherein during infiltration, the infiltration enhancer precursor volatilizes.

8. The method of claim 7 wherein the volatilized infiltration enhancer precursor reacts to form a reaction product in at least a portion of the body.

9. The method of claim 8, wherein said reaction product is at least partially reducible by said molten matrix metal.

10. The method of claim 9, wherein said reaction product is formed as a coating on at least a portion of said filler.

11. The method of claim 8, wherein the reaction product comprises a nitride of magnesium.

12. The method of claim 4, wherein the infiltration enhancer precursor comprises a material selected from the group consisting of magnesium, strontium and calcium.

13. The method of claim 4, wherein said at least one of the infiltration enhancer precursor and infiltration enhancer is supplied from an external source.

14. The method of claim 4, wherein the matrix metal comprises aluminum, the infiltration enhancer precursor comprises magnesium and the infiltrating atmosphere comprises nitrogen.

15. The method of claim 4, wherein the matrix metal comprises aluminum, the infiltration enhancer precursor comprises zinc, and the infiltrating atmosphere comprises oxygen.

16. The method of claim 4, wherein said at least one of said infiltration enhancer and said infiltration enhancer precursor is provided at a boundary between said body and said matrix metal.

17. The method of claim 4, wherein the matrix metal comprises aluminum, the infiltration enhancer precursor comprises strontium and the infiltrating atmosphere comprises nitrogen.

18. The method of claim 4, wherein the matrix metal comprises aluminum, the infiltration enhancer precursor comprises calcium and the infiltrating atmosphere comprises nitrogen.

19. The method of claim 1, further comprising the step of supplying at least one of an infiltration enhancer precursor and an infiltration enhancer to at least one of the matrix metal and the body.

20. The method of claim 19, wherein said at least one of said infiltration enhancer precursor and infiltration enhancer is provided in both of said matrix metal and said filler.

21. The method of claim 1, wherein at least one of an infiltration enhancer precursor and infiltration enhancer is in contact with at least a portion of the body during at least a portion of the period of infiltration.

22. The method of claim 1, wherein the infiltration occurs within defined barrier means.

23. The method of claim 22, wherein the barrier comprises a material selected from the group consisting of carbon, graphite and titanium diboride.

24. The method of claim 22, wherein said barrier means is substantially non-wettable by said matrix metal.

25. The method of claim 22, wherein said barrier means comprises at least one material which permits communication between an infiltrating atmosphere and at least one of the matrix metal, the body, an infiltration enhancer and an infiltration enhancer precursor.

26. The method of claim 1, wherein the filler comprises at least one material selected from the group consisting of powders, flakes, platelets, microspheres, whiskers, bubbles, fibers, particulates, fiber mats, chopped fibers, spheres, pellets, tubules and refractory cloths.

27. The method of claim 1, wherein the filler is of limited solubility in the molten matrix metal.

28. The method of claim 1, wherein the filler comprises at least one ceramic material.

29. The method of claim 1, wherein an infiltration enhancer precursor is alloyed in said matrix metal.

30. The method of claim 1, wherein said matrix metal comprises aluminum and said matrix metal contains at least one alloying element selected from the group consisting of silicon, iron, copper, manganese, chromium, zinc, calcium, magnesium and strontium.

31. The method of claim 1, wherein the temperature during spontaneous infiltration is greater than the melting point of the matrix metal, but lower than the volatilization temperature of the matrix metal and the melting point of the filler.

32. The method of claim 1, wherein the matrix metal comprises aluminum and the filler comprises a material selected from the group consisting of oxides, carbides, borides and nitrides.

33. The method of claim 1, wherein said contacting comprises diffusing said second metal into a spontaneously infiltrated body.

34. The method of claim 1, wherein said contacting results in the formation of a reaction product between said second metal and at least one of the body and said matrix metal.

35. The method of claim 34, wherein said reaction product undergoes a volumetric expansion relative to the original filler material or preform.

36. The method of claim 34, wherein a volume percent of matrix metal present in the infiltrated body is reduced when said reaction product is formed.

37. The method of claim 34, wherein said reaction product is formed in only a portion of the infiltrated body.

38. The method of claim 34, wherein said reaction product is formed substantially uniformly throughout said infiltrated body.

39. A method of making a metal matrix composite comprising:

forming a permeable mass comprising at least one material selected from the group consisting of a substantially non-reactive filler and a preform comprising a shaped substantially non-reactive filler;

spontaneously infiltrating molten matrix metal into said permeable mass so that at least some porosity remains therein;

contacting a second metal with said matrix metal and thereby causing said porosity to be filled; and

cooling said infiltrated mass containing said matrix metal and second metal therein, thereby forming a metal matrix composite.

40. A method for making a metal matrix composite, comprising:

providing a body comprising at least one material selected from the group consisting of a loose mass of substantially non-reactive filler and a preform comprising a shaped substantially non-reactive filler;

spontaneously infiltrating at least a portion of said body with molten matrix metal, at least one of the matrix metal and the body being in the presence of at least one of an infiltration enhancer precursor and an infiltration enhancer for at least a portion of the period of infiltration;

contacting at least a portion of said body or said matrix metal with a second metal which is different in composition from said matrix metal, thereby modifying at least one property of the infiltrated body; and

cooling said infiltrated body containing said matrix metal and second metal therein, thereby forming a metal matrix composite.

41. A method of forming a metal matrix composite body comprising infiltrating a body of a substantially non-reactive filler with a molten matrix metal to form an infiltrated body; and after said infiltrating is substantially complete, contacting at least one second metal with said infiltrated body, said second metal having a composition which is different from said matrix metal, thereby modifying at least one property of the infiltrated body.