Patent Application
20190278883
The present invention relates to a method of predicting a thermal fatigue life of a mold.
In a mold whose work surface is used in contact with a workpiece with a high temperature such as a die-casting mold or a hot forging mold, since heating due to contact with the workpiece and cooling with a water-soluble mold release agent and a lubricant are performed, compression and tension thermal stress is applied to the surface of the mold. Thus, in an actual operation, since this thermal stress is repeatedly applied, thermal fatigue cracks occur in the surface of the mold, and, for example, on the work surface of the mold, the cracks are transferred to the workpiece. The transfer of cracks gradually becomes severe and when the mold becomes unusable, the mold is discarded.
In particular, in a die-casting mold, cracks due to thermal fatigue are the most common reason for discarding, and it is strongly desired to improve a thermal fatigue life thereof.
In the related art, increasing the hardness of the mold and applying a mold material with improved high temperature strength were used in order to solve such problems, and the effect has actually been improved in some cases. However, since the relationships of the material properties and thermal stress load of a mold with a thermal fatigue life of the mold were unknown, it was unknown how long the life would be lengthened without actual application thereof. Therefore, the life was not lengthened as long as expected, trial and error were repeated, and time and cost were required for improvement in some cases.
Therefore, a method of predicting a thermal fatigue life of a mold according to material properties of the mold and a thermal stress distribution generated in the mold during use has been proposed (Patent Literature 1). That is, in the method, using a temperature Th and a thermal stress σh during heating at a predetermined position x on the mold obtained according to the thermal stress distribution, a yield strength σy(Th) at a predetermined mold hardness at the temperature Th of the mold material and a contraction φ(Tc) at a predetermined mold hardness at a temperature Tc during cooling, according to the formula N={C1(σy(Th)/σh)m·ln(1−φ(Tc))−1−C2}n, a thermal fatigue life N at a predetermined position x on the mold is predicted (C1, C2, m, and n are constants).
[Patent Literature 1]Japanese Patent No. 4359794
According to the method of Patent Literature 1, it is possible to efficiently find a hardness and a mold material of a mold suitable for improvement in a desired life without repeating prototyping of the mold, and thus it is possible to reduce time and cost consumed for improving a life of the mold.
However, in the case of Patent Literature 1, there is room for improvement in terms of increasing the accuracy of a predicted life of a mold with respect to an actual life of the mold.
An objective of the present invention is to provide a method of accurately predicting a thermal fatigue life of a mold.
The present invention is a method of predicting a thermal fatigue life of a mold which is made of a mold material having a hardness H and on which heating during contact with a workpiece and cooling after contact with a workpiece are repeated, which includes obtaining a temperature distribution of a mold heated during contact with a workpiece; obtaining a distribution of thermal stress occurring in the mold according to the temperature distribution; obtaining a thermal stress maximum value σh_MAX at a position x on the mold and a temperature Th at the thermal stress maximum value σh_MAX according to the thermal stress distribution; obtaining a yield strength σy(Th) at the temperature Th and a contraction φ(Tc) at a temperature Tc of the mold when it is cooled using the mold material having a hardness H; and substituting σh_MAX, σy(Th) and φ(Tc) into the following relational formula, and thereby obtaining a thermal fatigue life N at a position x on the mold:
N={C
1(σy(Th)/σh_MAX)m·ln(1−φ(Tc))−1−C2)}n
(C1, C2, m, and n are constants).
In the present invention, preferably, the temperature distribution of the mold and the distribution of thermal stress occurring in the mold are obtained whenever a use time of the mold reaches a time of 0.5 seconds or less
In addition, in the present invention, preferably, the position x on the mold is on a work surface having a corner radius of 2.0 mm or less.
According to the present invention, it is possible to predict a thermal fatigue life of a mold with accuracy.
A feature of the present invention is that, for a value of a “thermal stress σh” used for obtaining a thermal fatigue life N at any position x on a mold, “the highest value” that is extracted from a thermal stress σh generated when the mold is heated is used.
(a)<Obtaining a Temperature Distribution of a Mold (Process A)>
First, it is necessary to know a hardness H of a mold in order to obtain a yield strength and a contraction of a mold material constituting a mold to be described below. Thus, during use of a mold which is made of a mold material having the hardness H and on which heating during contact with a workpiece and cooling after contact with a workpiece are repeated, a temperature distribution of the mold that is heated during contact with a workpiece is obtained. The hardness H can be a value at room temperature. Thus, for example, in the case of a die-casting mold, the temperature distribution is a series of temperature distributions of a mold from a state in which the mold is heated by injecting a molten metal into a cavity of the die-casting mold to a state in which a die-casting part after casting is removed from the cavity and the mold is cooled. The temperature distribution can be obtained by numerical calculation, for example, a finite difference method or a finite element method. In this case, as a premise for calculating a temperature distribution, values of physical properties of a mold material such as specific heat and thermal conductivity are used as necessary.
As an example, there is a method of obtaining a temperature distribution by the finite element method.
Next, heat transfer analysis of each element is performed, and a temperature distribution diagram is created from a calculation result. In this case, in order to improve the accuracy of predicting a life, it is preferable to optimize the calculation result by using the temperature that is actually measured in an actual mold for a temperature of the mold obtained in the calculation result. For example, it is possible to use a temperature that is actually measured on the surface of the actual mold. In order to measure a temperature of the surface of the actual mold, for example, a device configured to measure a temperature without contact such as an infrared thermography can be used. When the temperature of the mold obtained in the calculation result is different from the measured temperature, the heat load conditions can be re-examined and re-calculated.
(b)<Obtaining a Thermal Stress Distribution from the Temperature Distribution of the Mold Obtained in the Process A (Process B)>
Based on the temperature distribution diagram (
First, since a model of the mold 1 is divided into meshes, a constraint condition is set for this. In this constraint condition, for example, according to a fixed state from the surroundings of the mold, a constraint direction or the like can be set for each side of the split elements 2.
Then, thermal stress analysis of the split elements 2 is performed, and a thermal stress distribution diagram can be created from the calculation result.
(c)<Obtaining a Thermal Stress Maximum Value σh_MAX and a Temperature Th at the Thermal Stress Maximum Value σh_MAX at any Position x on the Mold According to the Thermal Stress Distribution Obtained in the Process B (Process C)>
The method of Patent Literature 1 is very beneficial in predicting a life of a mold and selecting a hardness and a mold material of a mold suitable for increasing a desired life of the mold. However, in the method of Patent Literature 1, at any position x on the mold, for example, using a “time at which the temperature becomes the highest” of the mold during use of the mold as a reference, a life is computed from a relationship between a pair of a temperature field and a stress field generated “at the same time” as the time at which the temperature becomes the highest. In this case, in order to improve the accuracy of predicting a life of a mold, it is effective to actually designate the thermal stress σh used for the computation as “the highest value” of thermal stress generated during heating of the mold. Thereby, in an actual mold, a time at which the temperature becomes the highest at any position x differs for each position x. In addition, the time at which the temperature becomes the highest does not necessarily match a time at which the thermal stress becomes a maximum at the position x.
As an example,
In the method of predicting a life of a mold of the present invention, a relational formula to be described below is prepared, a value such as the thermal stress σh is substituted to obtain a thermal fatigue life N, and this life N varies according to the substituting value of the thermal stress σh. Therefore, in this point, in order to improve the accuracy of predicting a life of a mold, regarding a value of the thermal stress σh occurring in the mold during use, it is desirable to correctly select a maximum value thereof. Thus, for this purpose, without simply selecting a thermal stress value σh at a time at any position x on the mold using the time at which the temperature during use of the mold becomes the highest as a reference, it is necessary to compute a series of temperature fields and stress fields during its use cycle and extract a maximum value σh_MAX of the thermal stress from a series of thermal stresses σh. Further, the above temperature is not simply set to the above highest temperature, but it is necessary that it be a temperature Th when the value of the thermal stress is a maximum value σh_MAX.
Here, for example, as shown in
(d)<Obtaining a Yield Strength σy(Th) at the Temperature Th and a Contraction φ(Tc) at a Temperature Tc of the Mold when the Mold is Cooled Using a Mold Material Having a Hardness H Constituting the Mold (Process D)>
Thus, in the method of predicting a life of a mold of the present invention, in order to obtain a thermal fatigue life N using a relational formula to be described below, the yield strength σy(Th) and the contraction φ(Tc) of the mold are required. In this case, the yield strength σy(Th) is a value at the temperature Th. In addition, the contraction φ(Tc) is a value at the temperature Tc during cooling. Values of the yield strength σy(Th) and the contraction φ(Tc) can be obtained by separately preparing a mold material having a hardness H. In this case, the hardness H can be set to a value at room temperature. Then, the values of the yield strength σy(Th) and the contraction φ(Tc) that are measured in advance at various temperatures may be stored in a mechanical property database.
Here, the temperature Tc during cooling can be a surface temperature at a position x on the mold of which a life is predicted, for example, when an upper mold and a lower mold are opened, when the molded product is removed from the mold, when the mold is cooled, or the like in a process of removing a molded product (die-cast part) from the mold. In such a case, a surface temperature of the mold can be actually measured and this actual measurement value can be used. In addition, according to the finite element method or the like, in the same manner as above, calculation results can be used.
(e)<Obtaining a Thermal Fatigue Life N at a Position x on the Mold by Substituting Values of σh_MAX, σy(Th) and φ(Tc) into the Relational Formula
N={C
1(σy(Th)/σh_MAX)m·ln(1−p(Tc))−1−C2}n
(C1, C2, m, and n are constants) (process E)>
Then, finally, values of the thermal stress maximum value σh_MAX at a position x on the mold, the yield strength σy(Th) at the temperature Th at that time, and the contraction φ(Tc) at the temperature Tc during cooling which are obtained in the processes A to D are substituted into a relational formula of a thermal fatigue life N, material properties, and thermal stress, and a life of the mold can be obtained. In this case, as the relational formula, a formula in Patent Literature 1 can be used. However, in the present invention, since the value of the thermal stress σh in the relational formula is set as the “maximum value σh_MAX” and the value of the yield strength σy(Th) is set as the “value at the temperature Th at which the thermal stress σh_MAX is reached,” the accuracy of predicting a life of a mold is improved.
In the present invention, for example, when the hardness of the mold is variously changed and realized, a relationship between the hardness and the life of the mold can be obtained, and an “optimal hardness” for a predetermined mold can be proposed.
While an example in which a life of “one mold” is predicted under specific mold shape and use conditions is shown in an example of the present invention, it is possible to obtain a relationship between molds made of various mold materials and lifes when lifes of a “plurality of molds” made of different mold materials are predicted under specific mold shape and use conditions. In addition, when a life of one mold is predicted by changing a mold shape (for example, a curvature radius of a corner part) and a use condition (such as a temperature of a workpiece), it is also possible to obtain a relationship between a mold shape and a use condition, and a life. Thereby, it is possible to propose an “optimal mold material” for a predetermined mold shape and use condition.
The present invention is most suitable for predicting a life of a mold in which a time at which the thermal stress becomes a maximum and a time at which the temperature becomes the highest at any position on the mold during use as described above are different from each other. Thus, such a time lag may occur in, for example, a corner (corner part) of a work surface, within the stress concentration part of the mold. Thus, in the present invention, for example, a position x on the mold is preferably on a work surface having a corner radius (corner R) of 2.0 mm or less. More preferably, 1.0 mm or less is used.
Performing die-casting according to conditions in Table 1 was planned and a thermal fatigue life (the number of shots in which cracks occurred) of a mold when die-casting was actually performed was predicted. A mold used is as shown in
First, according to the above process (a), a temperature distribution of the mold in a series of casting cycles was obtained (process A). As an example of the temperature distribution diagram created from this calculation result,
Next, according to the above process (b), a distribution of thermal stress occurring in the mold was obtained from the temperature distribution (process B). As an example of the thermal stress distribution diagram created from this calculation result,
Then, according to the above process (c), according to the thermal stress distribution obtained above, as a position x on the mold, at positions of the bottom of V grooves (V1 to V5) provided on the work surface of the mold as the stress concentration part, a thermal stress maximum value σh_MAX and the temperature Th at the thermal stress maximum value σh_MAX were obtained (process C). In this case, as a comparative example, in order to perform a method of predicting a thermal fatigue life of a mold in Patent Literature 1, at positions of the bottom of V grooves, a temperature maximum value Th_MAX and the thermal stress σh at the temperature maximum value Th_MAX were obtained.
In addition, according to the above process (d), using a mold material (JIS-SKD61) having a hardness of 44 HRC at room temperature, the yield strength σy(Th) at the temperature Th and a contraction φ(Tc) at the temperature Tc of the mold that was cooled were obtained. In this case, as a numeric value used in the comparative example, a yield strength σy(Th_MAX) at the temperature Th_MAX was also obtained. The results regarding the V grooves are shown in Table 2.
Then, according to the above process (e), values of the constants C1, C2, m, and n of the relational formula of “N={C (σy(Th)/σh_MAX)m·ln(1−φ(Tc))−1−C2}n” were appropriately determined according to a level of cracks when the life was reached shown in
Then, these predicted values of the thermal fatigue life N were compared with a thermal fatigue life N (that is, a thermal fatigue life N when cracks shown in
Based on the results in Table 3, at positions of the bottom of all V grooves, in a range of 0.31 to 0.74 seconds after injection of a molten metal into the cavity was completed, the thermal stress maximum value σh_MAX and the temperature maximum value Th_MAX were confirmed. Then, according to calculation, an occurrence time of the σh_MAX and Th_MAX matched at V grooves except for V2 a time of 0.50 seconds elapsed or 0.60 seconds elapsed after injection of a molten metal was completed, and the occurrence time was shifted at V2. As a result, at V2, in the method of predicting a thermal fatigue life of a mold in the example of the present invention and the method of predicting a thermal fatigue life of a mold in the comparative example, the values of the predicted thermal fatigue life were different from each other. Thereby, the value of the thermal fatigue life obtained in the method of predicting a thermal fatigue life of a mold in the example of the present invention was close to the value of the actual thermal fatigue life.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017-058648 | Mar 2017 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2018/008922 | 3/8/2018 | WO | 00 |